KR101404019B1 - Method for varnishing with lacquer reduced allergic reaction - Google Patents
Method for varnishing with lacquer reduced allergic reaction Download PDFInfo
- Publication number
- KR101404019B1 KR101404019B1 KR1020120150150A KR20120150150A KR101404019B1 KR 101404019 B1 KR101404019 B1 KR 101404019B1 KR 1020120150150 A KR1020120150150 A KR 1020120150150A KR 20120150150 A KR20120150150 A KR 20120150150A KR 101404019 B1 KR101404019 B1 KR 101404019B1
- Authority
- KR
- South Korea
- Prior art keywords
- lacquer
- drying
- raw
- coating
- raw lacquer
- Prior art date
Abstract
Description
본 발명은 알레르기 저감을 위한 옻 도포 방법에 관한 것으로서, 더욱 상세하게는 옻을 자연 건조시켜 분말화한 후, 분말 옻을 도료나 접착제에 혼합하여 옻칠 대상부분에 도포하고, 건조후 그 위에 외피 도료를 도포하거나 또는 외피재를 부착하여 옷에 대한 알레르기를 저감시킬 수 있도록 한 알레르기 저감을 위한 옻 도포 방법에 관한 것이다.
More particularly, the present invention relates to a method for coating alluvial stones with lacquer, and more particularly, to a method for coating all or part of lacquer with a coating material or an adhesive, Or applying a covering material to reduce the allergy to clothes, and to a method of applying the varnish for reducing allergies.
종래의 옻의 알레르기 반응은 옻에 함유되어 있는 우루시올 때문이라고 알려져 있다. 식용으로 판매되는 옻은 알레르기 반응을 없애기 위해서 우루시올을 고온으로 처리하거나 화학적 반응을 시켜 우루시올을 안정화하는 방법, 추출하는 방법을 사용하여 왔다.It is known that the allergic reaction of conventional lacquer is due to urushiol contained in lacquer. In order to eliminate the allergic reaction, the lacquer sold for food use has been treated with urushiol at high temperature or by chemical reaction to stabilize urushiol and extract the urushiol.
생옻을 사용함에 있어 알레르기 반응이 일어난 예는 많이 찾아 볼 수 있다. 하다못해 옻을 다루는 작업자 또한 알레르기 반응이 일어나고 있는 것이 현실이다. 하지만, 옻을 유통하는 사람이나 옻 제품을 사용하는 사람에게 옻 알레르기가 일어나는 예는 찾아 보기 힘들다. 간혹 알레르기 반응이 일어난 사고를 보면 옻의 건조가 덜 된 상태에서 유통된 제품이거나, 다른 화합물이 첨가된 경우가 알레르기 반응을 일으킨 것으로 알려졌다.There are many examples of allergic reactions in the use of raw lacquer. In fact, it is a reality that allergic reactions are taking place in the workers who handle lacquer. However, it is difficult to find an example of lacquer allergy in people who distribute lacquer or use lacquer products. Allergic reactions occasionally seen in the case of the less dried lacquer products, or other compounds added to the product was known to cause allergic reactions.
이와 같이 생옻 상태의 옻은 알레르기 반응이 일어나지만, 기물에 칠하고 산화반응(옻의 건조과정, 20도시 온도, 80%의 습도상태에서 건조되는 과정)을 거친 옻은 안정화되어 알레르기 반응이 일어 나지 않는다. 옻으로 마감된 목기, 바루를 사용하다가 알레르기 반응이 일어난 사실은 없기에 생옻이 건조과정을 거치면서 알레르기 반응 물질이 안정화 되어 알레르기 반응이 없어짐을 알 수 있다.Thus, although allergic reaction occurs in the raw lacquer, the lacquer is stabilized and the allergic reaction occurs when it is painted and oxidized (drying process of lacquer, drying at 20 ° C, 80% humidity) Do not. Since there is no allergic reaction occurring during the use of baru, the allergic reaction material is stabilized and the allergic reaction disappears as the raw lacquer is dried.
선행기술문헌 : 한국특허출원 10-2007-0010323, KR100620874 B1
Prior Art Documents: Korean Patent Application 10-2007-0010323, KR100620874 B1
옻을 사용함에 있어 알레르기 반응은 꼭 해결해야만 하는 과제이다. 알레르기 반응으로 인해 옻을 사용하고자 하는 많은 분야에서 회피하는 이유이기 때문이다. 옻이 가진 많은 장점도 옻을 사용함에 있어 나타나는 알레르기 반응으로 많은 제한이 따르기 때문이다.Allergic reactions are a problem that must be solved in using lacquer. This is because they are avoided in many areas where they want to use lacquer because of allergic reactions. Many of the benefits of lacquer are due to the many limitations associated with allergic reactions in using lacquer.
따라서 본 발명은 옻의 알레르기 반응을 없애기 위하여 기존에 사용하는 방법인 고온가열 방식, 우루시올을 추출하거나, 화학적으로 안정화 시키는 방법을 배제하고, 자연건조방식을 취함으로써 비용이 절감되고 인위적인 화학가공에 첨가되는 화합물을 배제하고 고온가열 방식에서 오는 성분변화를 줄일 수 있도록 한 알레르기 저감을 위한 옻 도포방법을 제공하기 위한 것이다.
Accordingly, the present invention eliminates the method of high temperature heating, urushiol extraction or chemical stabilization, which is a conventional method for eliminating the allergic reaction of lacquer, and the cost is reduced by taking the natural drying method and added to artificial chemical processing And to provide a method of applying the varnish for reducing allergies so as to reduce changes in components coming from the high temperature heating method.
본 발명에 의한 옻 도포 방법은,According to the present invention,
액상의 생옻을 교반기를 이용하여 교반시키는 교반단계와;Agitating the raw lacquer in a liquid state using a stirrer;
상기 교반단계에서 교반된 액상의 생옻을 평판 용기에 미리 설정된 범위의 두께로 담는 평탄화단계와;A planarizing step of placing the liquid raw silk agitated in the stirring step in a predetermined range of thickness on a flat plate container;
상기 평탄화단계에서 평판용기에 담긴 생옻을 건조시키는 건조단계와;Drying the green lacquer contained in the flat plate container in the flattening step;
상기 건조단계에서 건조된 옻을 분쇄기로 분쇄하여 분말로 만드는 분말화 단계와;A pulverizing step of pulverizing the dried lacquer in the drying step into a powder;
상기 분말화 단계에서 분말화된 옻 분말을 도료 또는 접착제에 혼합하여 옻칠 대상부위에 도포하는 도포단계를 수행하는 것을 특징으로 한다.And the coating step of applying the powdered lacquer powder to the lacquer to be mixed with the paint or the adhesive in the powdering step.
본 발명은 상기 분말옻에 접착제를 혼합하여 도포한후, 자연 건조시키고 옻분말 도포층 위에 외장지 또는 외장 도장을 하여 마감하는 것을 특징으로 한다.The present invention is characterized in that the above-mentioned powdered lacquer is mixed with an adhesive, followed by natural drying, and then covered with an external paper or an exterior coating on the lacquer powder coated layer.
본 발명은 상기 교반단계에서 교반된 생옻을 걸름망을 통해 걸러서 평판 용기에 담는 걸름 단계를 더 포함하는 것을 특징으로 한다.The present invention is further characterized in that the agitating step of stirring the agar agar agitated in the agitating step is carried out through a squeezing net to be contained in a flat plate container.
상기 건조단계는, 직사광선이 없는 그늘에서 자연 건조 경화시키는 것을 특징으로 한다.The drying step is characterized by natural drying and curing in a shade without direct sunlight.
상기 건조단계는, 건조실의 온도를 15 ~ 25도로, 습도를 60 ~ 80%로 유지시켜 자연 건조 경화시키는 것을 특징으로 한다.The drying step is characterized in that the temperature of the drying chamber is maintained at 15 to 25 degrees and the humidity is maintained at 60 to 80% to naturally dry and cure.
상기 건조단계는, 15 ~ 25도의 온도와 60 ~ 80% 습도를 갖는 공기를 상기 평판 용기의 상면으로 강제 송풍시켜 건조 경화시키는 것을 특징으로 한다.In the drying step, air having a temperature of 15 to 25 degrees and a humidity of 60 to 80% is forcibly blown to the upper surface of the flat plate container to dry and cure the air.
따라서 옻을 자연적으로 건조시킨 후 분말화 하여 다시 사용한다면 알레르기 반응을 없앨 수 있다. Therefore, it is possible to eliminate the allergic reaction if the lacquer is dried naturally and then powdered again.
옻의 알레르기 반응을 없애기 위하여 기본에 사용하는 방법인 고온가열 방식, 우루시올을 추출하거나, 화학적으로 안정화 시키는 방법에 비하여 자연건조방식을 취함으로써 비용이 절감되고 인위적인 화학가공에 첨가되는 화합물을 배제하고 고온가열 방식에서 오는 성분변화를 줄일 수 있다.
In order to eliminate the allergic reaction of lacquer, the natural drying method is adopted in comparison with the method of high temperature heating method, urushiol extraction or chemical stabilization, which is a method used in the basic process, thereby eliminating the compounds added to artificial chemical processing, It is possible to reduce the variation of components coming from the heating method.
도 1은 본 발명에 의한 알레르기 저감을 위한 옻 도포 방법 흐름도.BRIEF DESCRIPTION OF THE DRAWINGS FIG. 1 is a flow chart of a method for applying an alum varnish for alleviating allergies according to the present invention. FIG.
이하, 본 발명의 실시 예를 첨부된 도면을 참조해서 상세히 설명하면 다음과 같다.Hereinafter, embodiments of the present invention will be described in detail with reference to the accompanying drawings.
도 1은 본 발명에 의한 알레르기 저감을 위한 옻 도포 방법 흐름도이다.BRIEF DESCRIPTION OF THE DRAWINGS Fig. 1 is a flow chart of a method of applying rubrene for reducing allergies according to the present invention.
이에 도시된 바와 같이,As shown therein,
액상의 생옻을 교반기를 이용하여 교반시키는 교반단계(S10)와;Agitating the raw lacquer in a liquid state using a stirrer (S10);
상기 교반단계(S10)에서 교반된 액상의 생옻을 평판 용기에 미리 설정된 범위의 두께로 담는 평탄화단계(S20)와;(S20) of placing the liquid raw stalks stirred in the stirring step (S10) in a predetermined range of thickness in a flat plate container;
상기 평탄화단계(S20)에서 평판용기에 담긴 생옻을 건조시키는 건조단계(S30)와;A drying step (S30) of drying the green lacquer contained in the flat plate container in the flattening step (S20);
상기 건조단계(S30)에서 건조된 옻을 분쇄기로 분쇄하여 분말로 만드는 분말화 단계(S40)와;A powdering step (S40) of pulverizing the dried lacquer in the drying step (S30) with a pulverizer to form a powder;
상기 분말화 단계(S40)에서 분말화된 옻 분말을 도료 또는 접착제에 혼합하여 옻칠 대상부분에 도포하는 도포단계(S50)를 수행하는 것을 특징으로 한다.(S50) of applying the powdered lacquer powder to the portion to be lacquered by mixing the powdered lacquer powder with the paint or the adhesive in the powdering step (S40).
본 발명은 상기 분말옻에 도료 또는 접착제를 혼합하여 도포한 후, 자연 건조시키고 옻분말 도포층 위에 외장지 또는 외장 도장을 하여 마감하는 외장 마감단계(S60)를 더 포함하는 것을 특징으로 한다.The present invention is characterized by further comprising an external finishing step (S60) in which the powdery lacquer is coated with a paint or an adhesive, applied to the lacquer, dried naturally, and then covered with external or external coating on the lacquer powder coated layer.
본 발명은 상기 교반단계(S10)에서 교반된 생옻을 걸름망을 통해 걸러서 평판 용기에 담는 걸름 단계를 더 포함하는 것을 특징으로 한다.The present invention is further characterized in that the step of mixing the raw lacquer agitated in the stirring step (S10) through a filter net is carried out in a flat plate container.
상기 건조단계(S30)는, 직사광선이 없는 그늘에서 자연 건조 경화시키는 것을 특징으로 한다.The drying step (S30) is characterized by natural drying and curing in a shade without direct sunlight.
상기 건조단계(S30)는, 건조실의 온도를 15 ~ 25도로, 습도를 60 ~ 80%로 유지시켜 자연 건조 경화시키는 것을 특징으로 한다.The drying step (S30) is characterized in that the temperature of the drying chamber is kept at 15 to 25 degrees and the humidity is maintained at 60 to 80%, followed by natural drying and curing.
상기 건조단계(S30)는, 15 ~ 25도의 온도와 60 ~ 80% 습도를 갖는 공기를 상기 평판 용기의 상면으로 강제 송풍시켜 건조 경화시키는 것을 특징으로 한다.The drying step (S30) is characterized in that air having a temperature of 15 to 25 degrees and air having a humidity of 60 to 80% is forcibly blown to the upper surface of the flat plate container to dry and cure.
이와 같이 본 발명은, 생옻을 건조시켜 분말화하고 분말 옻을 도료나 접착제에 혼합하여 도포하며, 도포된 분말 옻을 건조후, 도포층 위에 외장 도료를 도장하거나 외장재를 부착하여 마감처리하도록 하는 것을 특징으로 한다.As described above, according to the present invention, it is possible to dry the powdered green lacquer to powder, mix the powdered lacquer with the coating material or the adhesive agent, dry the applied powdered lacquer, and then coat the exterior layer with the coating layer or with the exterior material, .
교반단계(S10)는, 생옻은 일부 덩어리들이 포함될 수 있으므로 교반기를 통해서 교반한다. 교반기는 단순히 회전날개를 갖는 교반기를 이용하여 회전날개의 회전에 의해 생옻을 교반시키는 방법을 사용할 수 있다.In the stirring step (S10), raw lacquer may be agglomerated through a stirrer because some agglomerates may be contained therein. The agitator may be a method of agitating the raw lacquer by the rotation of a rotating blade using a stirrer having a rotating blade.
한편, 생옻의 상태에 따라 두 개의 롤러 사이를 통과시켜 롤러의 압착으로 생옻의 덩어리를 잘게 부수고, 이를 교반기를 통해 교반시켜 좀더 고른 입자 분포를 갖는 생옻으로 추출할 수 있다.On the other hand, according to the state of raw silk, it is passed between two rollers to crush the raw lacquer by crushing the roller, and the raw silk is agitated through a stirrer to extract raw silk having a more uniform particle distribution.
평탄화 단계(S20)는, 교반된 생옻을 일반 용기에 담아 건조시키게 되면 건조시간이 너무 길어지므로, 본 발명에서는 평판 용기에 교반된 생옻을 얇게 펼쳐서 평탄화 시킨다. 이는 미리 실험적으로 구해진 두께 범위(예; 1mm ~ 5mm)로 평탄화시킨다. 이는 용기에 교반된 옻을 부어놓고 일정한 간격이 유지되게 평탄화 부재를 생옻 상면에서 밀어서 일정한 두께 미만으로 옻을 얇게 펴서 평탄화 시킨다.In the planarizing step S20, if the aged green lacquer is dried in a general container, drying time becomes too long. Therefore, in the present invention, the aged green lacquer stirred in the flat plate is flattened by thinly spreading. This is planarized to a thickness range (for example, 1 mm to 5 mm) obtained in advance experimentally. This is accomplished by pouring the aged lacquer into the container and flattening it by spreading the planarizing member on the surface of the surface of the raw lacquer to a predetermined distance so as to maintain a constant interval.
건조단계(S30)는, 기본적인 건조방법으로는 그늘에서 24시간 ~ 36시간 정도 건조시키는 자연건조 방식을 사용한다.In the drying step (S30), a natural drying method in which the substrate is dried for 24 hours to 36 hours in the shade is used as a basic drying method.
또한 건조 시간을 단축시키기 위하여 온도 및 습도 조절이 가능한 건조실을 구비하고, 건조실의 온도를 15 ~ 25도로, 습도를 60 ~ 80%로 유지시켜 건조 경화시킬 수 있다. In addition, a drying chamber capable of controlling temperature and humidity can be provided to shorten the drying time, and the drying and curing can be performed by maintaining the temperature of the drying chamber at 15 to 25 degrees and the humidity at 60 to 80%.
또한, 상기 건조단계(S30)는, 15 ~ 25도의 온도와 60 ~ 80% 습도를 갖는 공기를 상기 평판 용기의 상면으로 강제 송풍시켜 건조 경화시킬 수 있다.Also, in the drying step (S30), air having a temperature of 15 to 25 degrees and a humidity of 60 to 80% can be forcedly blown to the upper surface of the flat plate container to dry and cure.
건조실을 구비하여 온도 및 습도를 조정하고 송풍을 하게 되면 일반 자연건조보다 건조시간을 대폭 줄일 수 있게 된다. 다만 가열등의 방법을 사용한다면 더욱 건조시간을 단축시킬 수 있으나, 생옻의 화학적 성질변화등이 발생될 수 있어서 가열방식을 사용하지 않는 것이 바람직하다.If a drying chamber is provided and the temperature and humidity are adjusted and the air is blown, the drying time can be significantly reduced compared to the normal natural drying. However, if the method such as heating is used, the drying time can be shortened further, but it is preferable not to use the heating method because the chemical properties of the raw lacquer may be changed.
분말화 단계(S40)는, 상기와 같이 건조된 옻을 분쇄기를 이용하여 분쇄하여 분말화 하는데, 분쇄기의 종류나 분쇄기의 조정에 의해 분말의 크기를 다양하게 만들수 있다. 이는 옻칠 대상물이나 옻칠 대상 부분에 따라 분말 입자의 크기를 다르게 사용할 수 있게 한다.In the pulverizing step (S40), the dried lacquer is pulverized using a pulverizer to be pulverized. The size of the pulverized powder can be varied by adjusting the kind of the pulverizer or the pulverizer. This makes it possible to use powder particles differently depending on the object to be lacquered or the portion to be lacquered.
도포 단계(S50)는, 분말 옻에 도료 또는 접착제를 혼합하여 옻칠 대상부분에 도포한다. 물론 도포 방법은 붓 칠이나 롤러 칠을 할 수도 있고, 대형 벽면 같은 곳에는 스프레이 분사방식을 이용할 수도 있다. 그리고 1회의 도포만 하는 것은 아니고 용도나 대상에 따라 건조 후 덧칠하여 옻칠의 성능을 높일 수 있다.In the coating step (S50), a paint or an adhesive is mixed with the powdered lacquer and applied to the part to be lacquered. Of course, the application method may be brushing or roller coating, or spraying method may be used on a large wall surface. It is not only one application but also it can be applied after drying depending on the application or subject, thereby enhancing the performance of lacquer.
상기와 같이 분말 옻을 도포한 후 자연 건조시켜 마감처리하게 되면, 옻칠이 최종 외피막을 형성하게 된다. 이는 옻칠의 색감이나 무늬감등을 살리기 위한 용도로 옻칠 외피막으로 마감할 수 있다.When the powdery lacquer is applied as described above and is then dried naturally, the lacquer forms the final covering film. It can be finished with a lacquer outer coating for the purpose of saving color and texture of lacquer.
한편, 옻칠 알레르기에 민감한 사람들을 위해서 분말 옻칠의 위에 외피막을 더 형성하는 마감단계(S60)더 포함한다. 이는 도장 도료를 외피막으로 칠하거나, 벽지등과 같은 외피재를 부착하여 마감처리한다. 따라서, 외피막 내부에 옻칠막이 형성되어 있으므로, 항균성등의 옻칠 효과는 그대로 얻을 수 있다.Meanwhile, for those who are sensitive to lacquer allergy, it further includes a finishing step (S60) for further forming an outer covering film on the powder lacquer. This is done by painting the painting material with an outer coating or by applying a covering material such as wallpaper or the like. Therefore, since the lacquer film is formed inside the outer coating film, the lacquer effect such as antibacterial property can be obtained as it is.
이와 같이 본 발명은 생옻을 건조후 분말화하고, 분말 ?을 도료나, 접착제에 첨가하여 저 알레르기 옻 도료나. 접착제로 사용하며, 건축물 내장공사에서 도배지 장판지를 시공함에 있어 건조된 옻을 분말화 하여 첨가 사용한다.
As described above, the present invention relates to a method for producing a low-allergic rust lacquer, which comprises drying and pulverizing raw lacquer, and adding powder to the coating material or the adhesive. It is used as an adhesive, and in the construction of the building, the dried lacquer is added in powder form in the construction of the platform paper.
S10 : 교반단계 S20 : 평탄화 단계
S30 : 건조단계 S40 : 분말화 단계
S50 : 도포단계 S60 : 마감 단계S10: Stirring step S20: Flattening step
S30: Drying step S40: Powdering step
S50: Application step S60: Finishing step
Claims (6)
액상의 생옻을 교반기를 이용하여 교반시키는 교반단계(S10)와;
상기 교반단계(S10)에서 교반된 액상의 생옻을 걸름망을 통해 걸러서 평판 용기에 미리 설정된 범위의 두께로 담는 평탄화단계(S20)와;
상기 평탄화단계(S20)에서 평판용기에 담긴 생옻을 건조시키는 건조단계(S30)와;
상기 건조단계(S30)에서 건조된 옻을 분쇄기로 분쇄하여 분말로 만드는 분말화 단계(S40)와;
상기 분말화 단계(S40)에서 분말화된 옻 분말을 도료 또는 접착제에 혼합하여 옻칠 대상부분에 도포하는 도포단계(S50)를 수행하는 것을 특징으로 하는 알레르기 저감을 위한 옻 도포 방법.In a method for applying an oak to reduce allergies,
Agitating the raw lacquer in a liquid state using a stirrer (S10);
(S20) of filtering out the liquid raw stalks in a stirred state in the stirring step (S10) and filtering the raw lacquer in a predetermined range of thickness in the flat plate container;
A drying step (S30) of drying the green lacquer contained in the flat plate container in the flattening step (S20);
A powdering step (S40) of pulverizing the dried lacquer in the drying step (S30) with a pulverizer to form a powder;
Wherein the coating step (S50) of applying the powdered lacquer powder to the part to be lacquered by mixing the powdered lacquer powder with the paint or the adhesive is performed in the powdering step (S40).
상기 분말옻에 도료 또는 접착제를 혼합하여 도포한 후, 자연 건조시키고 옻분말 도포층 위에 외장지 부착 또는 외장 도장을 하여 마감하는 외장 마감단계(S60)를 더 포함하는 것을 특징으로 하는 알레르기 저감을 위한 옻 도포 방법.[2] The method for coating allergens according to claim 1,
Further comprising an external finishing step (S60) of coating the powdered lacquer with a paint or an adhesive, naturally drying the coated lacquer, and applying an exterior paper or coat on the lacquer powder coated layer to finish the coating. Method of applying varnish.
직사광선이 없는 그늘에서 자연 건조 경화시키는 것을 특징으로 하는 알레르기 저감을 위한 옻 도포 방법.The method according to claim 1, wherein the drying step (S30)
And drying and curing in a shade without direct sunlight.
건조실의 온도를 15 ~ 25도로, 습도를 60 ~ 80%로 유지시켜 자연 건조 경화시키는 것을 특징으로 하는 알레르기 저감을 위한 옻 도포 방법.The method according to claim 1, wherein the drying step (S30)
Characterized in that the temperature of the drying chamber is maintained at 15 to 25 degrees and the humidity is maintained at 60 to 80%, thereby naturally drying and curing.
15 ~ 25도의 온도와 60 ~ 80% 습도를 갖는 공기를 상기 평판 용기의 상면으로 강제 송풍시켜 건조 경화시키는 것을 특징으로 하는 알레르기 저감을 위한 옻 도포 방법.The method according to claim 1, wherein the drying step (S30)
Wherein air having a temperature of 15 to 25 degrees and a humidity of 60 to 80% is forcibly blown to the upper surface of the flat plate container to dry and cure the coating.