KR101402240B1 - Premix composition for intercepting water vein wave and preform including the same - Google Patents
Premix composition for intercepting water vein wave and preform including the same Download PDFInfo
- Publication number
- KR101402240B1 KR101402240B1 KR1020130033583A KR20130033583A KR101402240B1 KR 101402240 B1 KR101402240 B1 KR 101402240B1 KR 1020130033583 A KR1020130033583 A KR 1020130033583A KR 20130033583 A KR20130033583 A KR 20130033583A KR 101402240 B1 KR101402240 B1 KR 101402240B1
- Authority
- KR
- South Korea
- Prior art keywords
- weight
- parts
- blocking
- water
- premix composition
- Prior art date
Abstract
Description
본 발명은 수맥파를 차단할 수 있는 프리믹스 조성물 및 이를 포함하고 다양한 형태로 성형이 가능한 프리폼에 관한 것이다.The present invention relates to a premix composition capable of blocking snakes, and a preform containing the premix composition and capable of being molded into various forms.
수맥이란 폭이 좁은 지층을 따라 맥상으로 존재하는 지하수를 말한다. 습곡 운동이나 단층 작용에 의해 변형된 지형은 물의 순환작용에 의하여 지표면으로 물이 흐르면서 침식작용과 퇴적작용을 하게 되고, 자력의 자체운동 결과로 자력이 미치는 수직선상에서는 파괴 현상이 일어난다. 이때 지표 사이에 미세한 균열이 생기고 그 사이로 지상으로부터 빗물 등이 스며들어 이것에 의해 수맥은 그 생명력을 부여받을 수 있게 된다.Sucker is a groundwater that exists along a narrow creek. The topography deformed by the folding motion or the monolayer action causes the water to flow to the surface due to the circulation of the water and causes the erosion and sedimentation. And as a result of the self-motion of the magnetic force, the fracture phenomenon occurs on the vertical line. At this time, fine cracks are formed between the surfaces, and rainwater and the like penetrate from the ground therebetween, so that the water vane can be given its vitality.
수맥파(水脈波)는 수맥에서 발생하는 유해한 저주파 파동이며, 외국에서는 Harmful Radiation(해로운 지구방사선)으로 불리고 있고, 수맥파가 발생하는 지점은 Pathogenic Zone(병원성지대:病原性地帶)으로 불리고 있다. 수맥파가 생성되는 원인은 여러 가지 이론이 있으나 그 중에서도 수맥 속에 물이 흐르면서 모래나 자갈, 기타 광물질이 같이 섞여서 흐르며 강한 전기, 자기적 성질을 동반하여 흐르는데 이 전기, 자기적인 파장이 지상으로 방사되는 것으로 보는 학설과 지구 내부에서 지열(地熱)의 열원(熱原)인 자연 방사능 동위원소가 핵분열로 인하여 방사능을 자연 붕괴시키며 방사선을 발생시키는데 이때 알파(α), 베타(β), 감마(γ) 방사선 중에서 감마선이 각종 형태의 지하수를 통과하면서 그 지하수가 돋보기의 볼록렌즈 역할을 하면서 수직으로 강하게 모아지면서 파장이 짧은 전자기파로 발생하는 즉, 핵방사능의 감마(γ)선 변조파로 보는 학설과 지하수맥은 끊임없이 자신의 부족한 물을 보충하기 위하여 지상의 물을 끌어들이는데 이 힘이 탐사 된다는 학설 등이 있다. 수맥이 있다면 수맥파가 반드시 있으며 수맥의 흐름과 성질, 수맥의 량, 교차여부에 따라 변조의 강도가 다르게 된다. 즉 변조시키는 조건이 클수록 수맥은 강한 파장을 만들어내는 것이다.The waterwave is a harmful low-frequency wave that occurs in watercourses. In foreign countries, it is called Harmful Radiation. The point where the waterwave occurs is called the Pathogenic Zone (pathogenic zone). There are various theories for the creation of snakes. Among them, sand, gravel, and other minerals flow along with the water flowing in the submergence, and they flow along with strong electricity and magnetic properties. This electric and magnetic waves radiate to the ground The theory of observation and the natural radioactive isotope, which is the heat source of geothermal heat in the earth, naturally decays radioactivity due to nuclear fission and generates radiation. At this time, alpha, beta, gamma The gamma rays are transmitted through various types of groundwater, and the groundwater acts as a convex lens of the magnifying glass, while being strongly gathered vertically and generated by an electromagnetic wave having a short wavelength. That is, The theory that this force is explored in order to constantly draw water from the ground to supplement its deficient water There is. If there is a sump, the sump must be present, and the strength of the modulation depends on the flow and nature of the sump, the amount of sump, and the intersection. In other words, the larger the condition to modulate, the stronger the wavelength.
독일의 물리학자 슈만박사에 의하면 지구에서 발생하는 고유 진동 주파수는 7.83㎐이고, 이것은 지구의 자전과 공전에 의해 발생하는 고유의 진동으로서 인체에는 무해한 땅의 주파수라고 하였다. 그러나 지구 내부의 수맥이 지자기(地磁氣)의 파동성을 유동시키면서 강한 힘이 발생되어 생기는 파동이 무해한 땅의 고유 진동 주파수를 교란시키며 변조된 나쁜 증폭된 주파수가 형성되어 그 장소에 해당되는 사람과 기타 환경 물체에 나쁜 영향을 미친다고 발표하고 있다. 수맥파는 지구 안쪽에서 바깥쪽으로 수직으로 발생되는 에너지 파동으로 미치는 범위는 일반적으로 지상 15,000피트(약 1,000미터)로 알려져 있고 수맥파 위에 있는 모든 동, 식물에 해로운 영향을 미친다. 최근 수맥파와 관련하여 네델란드 지질학자인 트롬프 박사가 1986년 유네스코에 제출한 자료에 의하면, 인체는 수맥 위에서 몸 전체 반응을 느끼며 흥분을 유도하는 아드레날린 호르몬 분비를 촉진시켜 심장박동과 산소 소비의 증가, 근육긴장 등의 이상을 초래하는 것으로 나타났고, 독일 의사인 구스타프 남작이 1929년 발표한 자료에 의하면 수맥이 교차하는 강력한 유해파가 발생하고 이곳에서 장시간 잠을 잘 경우에는 암까지도 유발되는 것으로 나타났고, 독일 의학박사인 하거 박사가 발표한 자료에 의하면 1910~1932년간 5,348명의 암환자를 대상으로 주거지를 조사한 결과 98% 이상이 수맥 위에서 거주한 것으로 나타났다.According to Dr. Schumann, a physicist in Germany, the natural frequency of the earth's vibration is 7.83 Hz, which is the inherent vibration caused by earth's rotation and revolutions, which is harmless to the human body. However, as the water inside the earth circulates the vibration of geomagnetism, the strong vibration generated by the strong force disturbs the natural vibration frequency of the harmless earth and the badly amplified frequency is formed and the person And other environmental objects. Suma pampas are generally known to be 15,000 feet (1,000 meters) above ground, with an energy ripple generated vertically outward from the inside of the earth, which has a detrimental effect on all the plants and plants on the snakes. According to the data submitted to UNESCO in 1986 by the Dutch geologist Dr. Tromp, a Dutch geologist, the human body responded to the whole body on the submergence, promoting the stimulation of adrenergic hormone secretion leading to an increase in heart rate and oxygen consumption, And the German physician Gustav Baron reported in 1929 that strong suicide waves crossed the sowing and that long sleep in this place also caused cancer, According to Dr. Hagger's report, more than 98% of the 5,348 cancer patients surveyed in the years 1910-1932 were resident on the waterline.
한편, 1922년 프랑스 수학자인 카탄에 의해서 발견된 토션장(Torsion field) 이론에 의하면 다양한 형태의 도형이나 기하학적 구조물과 생명체는 물론 각 재질에서도 고유의 토션장이 존재하고, 이러한 토션장은 원자나 전자 규모의 물리적 회전 방향에 의해 서로 다른 2개의 방향성을 가진 파장 중 하나의 형태로 나타난다. 예를 들어, 자석의 N극에서 발생하는 토션장은 물 분자의 회전 방향을 왼쪽으로 돌리고 이러한 파장을 좌회전파라 하며 인체에 유해한 파장인 것으로 나타났고, 자석으로 S극에서 발행하는 토션장은 물 분자의 회전 방향을 오른쪽으로 돌리고 이러한 파장을 우회전파라 하며 인체에 이로운 파장인 것으로 나타났다. 이러한 토션장에서 발생하는 파장의 방향성 및 그 강도는 통상적으로 수맥파의 발생 여부 및 강도를 측정하는 L-로드(L-rod)에 의해서도 확인이 가능한데, 예를 들어 L-로드(L-rod) 한 개를 오른손에 쥐고 파장을 측정할 때 L-로드(L-rod)가 좌측으로 회전(또는 시계 반대 방향으로 회전)하는 경우 그 파장은 유해한 파장이고 L-로드(L-rod)가 평행인 것을 기준으로 회전하는 각도가 클수록 유해한 파장의 강도는 커지는 것으로 해석될 수 있다. 반대로, L-로드(L-rod)가 우측으로 회전(또는 시계 방향으로 회전)하는 경우 그 파장은 이로운 파장이고 L-로드(L-rod)가 평행인 것을 기준으로 회전하는 각도가 클수록 이로운 파장의 강도는 커지는 것으로 해석될 수 있다. 이때, L-로드(L-rod)를 우회전시키는 우회전파는 모든 물질에 유익함을 주기 때문에 생체에 비춰졌을 때 세포의 운동성을 향상시키고 세포를 활성화시켜 건강에 유익을 주나 L-로드(L-rod)를 좌회전시키는 좌회전파는 모든 물질에 해를 끼치는 유해 에너지 파장으로서 인체의 세포 활성화를 저하시켜 건강에 해로움을 주고 더 나아가 암과 같은 질병을 유발시키는 것으로 알려져 있다.On the other hand, according to the theory of the torsion field discovered by the French mathematician Catan in 1922, there existed a unique torsion field in various shapes, geometrical structures and life forms as well as in each material, It appears as one of the wavelengths having two different directivities depending on the rotation direction. For example, the torsion field generated from the N pole of the magnet turns the direction of rotation of the water molecule to the left, and the wave turns to the left and it is harmful to the human body. Direction to the right, turning these wavelengths to the right, and showing that the wavelength is beneficial to the human body. The directionality and the intensity of the wavelength generated in such a torsion field can be confirmed by an L-rod which normally measures the occurrence and strength of the snakes. For example, one L-rod When the L-rod rotates to the left (or rotates counterclockwise) when measuring the wavelength with the right hand holding it, the wavelength is harmful and the L-rod is parallel The larger the angle of rotation is, the greater the intensity of the harmful wavelength can be interpreted to be. On the contrary, when the L-rod rotates clockwise (or clockwise), the wavelength is advantageous and the larger the angle of rotation based on the parallelism of the L-rod, Can be interpreted as increasing in strength. At this time, a right-turning wave that makes a right turn of the L-rod is beneficial to all substances, so when it is reflected to the living body, it improves the cell mobility and activates the cell, ) Is a harmful energy wave that harms all substances, and it is known that it damages the health of the human body, thereby causing illness such as cancer.
현재까지 수맥파 또는 토션장에서 발생하는 해로운 파를 차단할 수 있는 다양한 조성물이 개발되거나 판매되고 있다. 예를 들어, 구리, 니켈, 알루미늄 등의 금속류가 수맥파를 차단할 수 있는 것으로 알려져 있으며, 실제로도 수맥파가 발생하는 지점에 동판을 깔거나 구리를 코팅하여 사용하고 있다. 그러나 이러한 금속류는 무게가 무거워 벽체에 시공하거나 휴대용으로 제작하기 어려운 문제점 및 가격이 비싸다는 단점이 있다. 또한, 대한민국 등록특허공보 제0852866호에는 금, 은, 동으로 이루어진 금속성분 1~5 중량%, 게르마늄, 바이오세라믹, 황토로 이루어진 천연 광물성분 10~30 중량%, 달팽이엑기스 성분 0.05~1 중량%, 소나무뿌리 3~15 중량%, 뽕나무뿌리 15~40 중량% 및 생수 10~60 중량%을 혼합한 수맥파 차단용 조성물이 개시되어 있다. 또한, 대한민국 등록특허공보 제1172511호에는 견운모 35 내지 55 중량부, 백복령 10 내지 30 중량부, 참숯 10 내지 25 중량부, 솔잎 5 내지 15 중량부 및 구리 5 내지 15 중량부를 포함하는 수맥파 차단용 조성물이 개시되어 있다. 또한, 대한민국 등록특허공보 제0298832호에는 장석, 낙석, 도석, 견운모, 점토, 고령토, 백납석, 황토, 규석 및 운모로 이루어진 전체 원석들의 총 중량기준으로, 장석 5 중량%, 낙석 3 중량% 및 도석 5 중량%를 로(爐)속에 넣고 1200∼1300 ℃로 가열하는 가열공정과, 이를 250 메시(mesh)로 분말화 하는 1차 파쇄공정과, 상기 파쇄공정에서 얻어진 분말 30 중량%와 물 70 중량%로 혼합하고, 그 혼합물의 전체중량대비 30 중량%의 게르마늄, 갈근 또는 쑥의 분말로부터 선택된 1 종 또는 2 종 이상의 혼합분말을 투입하는 1차 혼합공정과, 전기한 혼합물을 35∼37 ℃에서 7∼9 일간 숙성하는 1차 숙성공정과, 1차 숙성물에 상기 전체 원석들의 총 중량 기준으로 견운모 60 중량%, 점토 5 중량%, 고령토 7 중량%, 백납석 4 중량%, 황토 3 중량%, 규석 5 중량%, 운모 3 중량%의 혼합분말을 혼합하는 2차 혼합공정과, 2차 혼합물을 35 ℃에서 13∼16일간 숙성시키는 2차 숙성공정과, 2차 숙성공정에 의해 얻어진 혼합물을 분말화하는 2차 파쇄공정으로 제조되는 수맥파 차단용 조성물이 개시되어 있다. 그러나, 실제 수맥파가 발생하는 지점에 상기 수맥파 차단용 조성물을 적용하는 경우 만족할 만한 수준의 수맥파 차단 효과를 얻지 못하는 것으로 나타났다.Various compositions have been developed or marketed that can block harmful waves that may occur in snakes or torsion fields. For example, metals such as copper, nickel, and aluminum are known to be able to block snakes, and copper is coated or coated with copper at the point where the snakes occur. However, such a metal has a disadvantage that it is difficult to construct the wall or to make it portable, and it is expensive because of its heavy weight. Korean Patent Publication No. 0852866 discloses that 1 to 5% by weight of a metal component consisting of gold, silver and copper, 10 to 30% by weight of a natural mineral component composed of germanium, bioceramics and loess, 0.05 to 1% by weight of a snail extract component, , 3 to 15% by weight of pine root, 15 to 40% by weight of mulberry root and 10 to 60% by weight of living water. In Korean Patent Publication No. 1172511, a composition for a saxane blocking composition comprising 35 to 55 parts by weight of a sericite, 10 to 30 parts by weight of Baekbok-gil, 10 to 25 parts by weight of charcoal, 5 to 15 parts by weight of pine needle and 5 to 15 parts by weight of copper . In addition, Korean Patent Publication No. 0298832 discloses that 5 wt% of feldspar, 3 wt% of feldspar, and 3 wt% of feldspar are contained, based on the total weight of the total of the ores consisting of feldspar, rock, dolomite, sericite, clay, kaolin, A heating step of heating 5% by weight of stearic acid into a furnace and heating the mixture to 1200 to 1300 DEG C, a primary crushing step of pulverizing the same to 250 mesh, a step of mixing 30% by weight of the powder obtained in the crushing step with 70% By weight, and a mixture of one or more mixed powders selected from the group consisting of 30% by weight of germanium, powder of Pueraria or Artemisia, is added to the total weight of the mixture, In a first aging step for aging for 7 to 9 days in a first aging step; and a second aging step of aging for 7 to 9 days in a first aging step; %, 5% by weight of silica and 3% by weight of mica And a secondary crushing step of pulverizing the mixture obtained by the secondary aging step and a secondary crushing step of pulverizing the mixture obtained by the secondary aging step, Lt; / RTI > However, it has been found that when the composition for blocking the sulfamox is applied at the point where the actual sulfamoic acid occurs, a satisfactory level of the sulfamoide blocking effect is not obtained.
본 발명은 이러한 배경하에 도출된 것으로서, 본 발명의 목적은 수맥파를 효과적으로 차단하거나 수맥파를 인체에 이로운 파장으로 변환시킬 수 있는 성형재의 프리폼 및 상기 프리폼의 제조에 적합한 프리믹스 조성물을 제공하는데에 있다.SUMMARY OF THE INVENTION The present invention has been made under these circumstances, and an object of the present invention is to provide a preform of a molding material and a premix composition suitable for manufacturing the preform, which can effectively cut off the snakes or convert the snakes into the human body.
상기 목적을 해결하기 위해서, 본 발명은 도석, 규석, 활석, 장석, 토석 및 백토로 이루어진 군에서 선택된 1종 이상으로 구성되는 천연 광물질, 운석(meteor), 황토 및 점토를 포함하는 조성물로서, 상기 운석의 함량은 조성물 전체 중량을 기준으로 5-40 중량%인 것을 특징으로 하는 수맥파 차단용 프리믹스 조성물을 제공한다.In order to solve the above object, the present invention provides a composition comprising natural minerals, meteor, clay and clay, which is composed of at least one selected from the group consisting of stonite, silica, talc, feldspar, Wherein the content of meteorite is 5-40 wt% based on the total weight of the composition.
또한, 본 발명은 프리믹스 조성물과 물의 혼합물로 이루어진 수맥파 차단용 프리폼을 제공한다.Further, the present invention provides a pre-foam for blocking a water-repellent material comprising a mixture of a premix composition and water.
본 발명에 따른 수맥파 차단용 프리폼을 특정 형태로 성형하여 귀걸이 같은 장신구, 휴대폰 걸이, 건축용 피복재, 실내 바닥재, 내장재, 벽재, 장판, 매트, 이불, 베게 또는 의류 등에 부착하는 경우 수맥파를 효과적으로 차단하거나 수맥파를 인체에 이로운 파장으로 전환 시킬 수 있다. 또한, 본 발명에 따른 수맥파 차단용 프리믹스 조성물 및 프리폼은 도석, 규석, 활석, 장석, 토석 또는 백토와 같은 통상적인 수맥파 차단용 물질과 운석(meteor)의 조합에 의해 수맥파의 차단 효과 또는 수맥파를 인체에 이로운 파장으로 전환하는 효과를 극대화시킬 수 있다.When the pre-foam for blocking a sumaucer according to the present invention is molded into a specific shape, it can effectively block the squeeze wave when it is attached to an ornamental jewelry such as earrings, a mobile phone hook, a building cover material, an indoor floor material, an interior material, a wall material, To a wavelength advantageous to the human body. The premix composition and preform according to the present invention can also be used in combination with conventional marsupial blocking substances such as stonite, silica, talc, feldspar, It is possible to maximize the effect of switching to a useful wavelength.
도 1은 L-로드(L-rod)를 잡은 손과 L-로드(L-rod)가 평행할 때를 기준점으로 하였을 때, L-로드(L-rod)가 바깥쪽으로 소정의 각도 θ만큼 회전한 상태를 나타낸 것이다.FIG. 1 is a cross-sectional view showing a state in which the L-rod is rotated outward by a predetermined angle? When the L-rod is parallel to the hand holding the L-rod, .
이하, 본 발명을 구체적으로 설명한다.Hereinafter, the present invention will be described in detail.
본 발명의 일 측면은 수맥파 차단용 프리폼을 간편하게 제조하는데 이용될 수 있는 수맥파 차단용 프리믹스 조성물에 관한 것이다. 이때, 수맥파 차단용 프리폼은 다양한 모양의 성형품으로 성형될 수 있는 반고체 상태의 혼합물을 의미한다. 본 발명에 따른 수맥파 차단용 프리믹스 조성물은 특정 성분으로 구성된 천연 광물질, 운석(meteor), 황토 및 점토를 포함한다. 이하, 본 발명에 따른 수맥파 차단용 프리믹스 조성물을 구성성분 별로 나누어 설명한다.One aspect of the present invention relates to a premix composition for smack-breaking that can be used to conveniently produce a pre-foam for blocking a smack. At this time, the sump-blocking preform refers to a semi-solid mixture that can be molded into various shaped articles. The premix compositions for smack blocking according to the present invention include natural minerals, meteor, loess and clay composed of specific components. Hereinafter, the present invention will be described by dividing the premix compositions for the smack parts by constituents.
본 발명에 따른 수맥파 차단용 프리믹스 조성물은 일 구성성분으로 운석(metero)을 포함한다. 운석(meteor)은 우주공간으로부터 지구에 진입한 암석이 지구 대기와의 마찰에 타고 남아 지표면에서 발견된 것으로서 별똥별로도 불리운다. 운석(meteor)은 일반적으로 환원 환경, 낮은 압력, 건조한 조건에서 생성되었기 때문에 지구의 암석에 비해 산화철이 금속 철의 형태로 산출되는 경우가 흔하며, 충돌에 의해 형성된 경우를 제외하고는 높은 압력에서 형성된 광물이 거의 없고, 함수 광물의 함량이 적다. 많은 종류의 운석(meteor)은 철과 니켈의 합금을 포함하고 있으므로, 지구상의 암석에 비해 밀도가 높고 자성을 띤다. 운석은 구성 성분에 따라 크게 세 종류로 분류할 수 있는데, 예를 들어 운석이 주로 규산염 광물로 이루어져 있는 경우 이를 석질 운석(stony meteorites)이라고 부르고, 운석이 주로 금속 철과 니켈의 합금으로 이루어져 있다면 이를 철질 운석(iron meteorites)이라 부르고, 금속 상태의 철질 성분과 규산염 성분이 약 절반씩 섞여있는 운석은 석철질 운석(stony-iron meteorites)으로 분류한다. 또한, 운석(meteor)의 종류에 따라 지구상의 암석에서는 볼 수 없는 독특한 내부구조를 볼 수 있다. 철질 운석의 경우는 비드만스태튼 무늬라고 하는 빗살무늬를 볼 수 있는데 철과 니켈이 고체상태에서 확산에 의한 분화과정을 거쳐 형성된 것으로 매우 오랜시간이 필요해 지구상의 다른 암석에서는 볼 수 없다. 또한, 석질 운석의 경우에는 콘드률이라 부르는 전형적인 구조가 있는데 이는 우주 공간에서 녹았던 암석이 액체가 되었을때 물방울 모양으로 둥글게 식은 것이다. 이것들이 뭉쳐있는 암석을 콘드라이트라 한다. 석철질 운석의 경우는 철질과 석질이 섞여있어 매우 아름다운 모양을 띄는데 이를 팔라사이트라 한다.The premix composition for smack blocking according to the present invention contains meteol as a constituent. A meteor is a rock that has entered the earth from outer space and has been found on the surface of the earth in rubbing with the Earth's atmosphere and is also called a star. Since meteorites are generally produced under reducing conditions, low pressure and dry conditions, iron oxides are often produced in the form of metallic iron as compared to earth rocks. Except when formed by collision, minerals formed at high pressure And the content of minerals is small. Many types of meteorite contain iron and nickel alloys, so they are more dense and magnetic than earth rocks. For example, if meteorites are mainly composed of silicate minerals, they are called stony meteorites. If meteorites are mainly composed of metal iron and nickel alloys, Iron meteorites are called meteorites (iron meteorites), and the metal components are mixed with about half of the silicate component is classified as stony-iron meteorites (stony-iron meteorites). In addition, depending on the type of meteor, you can see a unique internal structure that can not be seen on Earth's rocks. In the case of iron meteorite, we can see a comb stripe called Beadmann stathen pattern. Iron and nickel are formed by diffusion process in solid state. It takes very long time and can not be seen in other rocks on earth. Also, in the case of a stone-like meteorite, there is a typical structure called a conduction rate, which means that the rocks melted in outer space are rounded in droplets when they become liquids. These rocks are called conidia. In the case of stonemal meteorite, it is called palaceite because it is a mixture of iron and stone.
본 발명에 따른 수맥파 차단용 프리믹스 조성물에 사용되는 운석(meteor)의 종류는 크게 제한되지 않으며, 경제성 등을 고려할 때 석질 운석인 것이 바람직하다. 또한, 본 발명에 따른 수맥파 차단용 프리믹스 조성물에 사용되는 운석(meteor)은 다른 성분과의 혼용성을 고려할 때 분말 형태인 것이 바람직하고, 이때, 운석 분말의 입도는 100~1000 메시(mesh)인 것이 바람직하고, 300~800 메시(mesh)인 것이 더 바람직하다. 또한, 본 발명에 따른 수맥파 차단용 프리믹스 조성물에서 운석(meteor)의 함량은 조성물 전체 중량을 기준으로 5~40 중량%인 것이 바람직하고, 운석의 첨가에 따른 수맥파 차단 효과 및 수맥파를 이로운 파장으로 전환 시키는 효과를 고려할 때 5~35 중량%인 것이 더 바람직하며, 10~30 중량%인 것이 가장 바람직하다. 운석의 함량이 조성물 전체 중량을 기준으로 5 중량% 미만인 경우 운석의 첨가에 따른 수맥파 차단 효과 및 수맥파를 이로운 파장으로 전환 시키는 효과가 미비할 염려가 있고, 40 중량%를 초과하면 초과에 따른 효과의 상승이 크지 않고 반고체 상태의 프리폼을 제조하는 것이 원활하지 않을 수 있다.The type of meteor used in the squeeze-screening premix composition according to the present invention is not particularly limited, and it is preferable that the meteorite is a meteorite in consideration of economical efficiency and the like. The meteorite used in the present invention is preferably in the form of a powder in consideration of compatibility with other components. In this case, the particle size of the meteor powder is 100 to 1000 mesh And more preferably 300 to 800 meshes. In addition, the meteoric content in the premix compositions for squeeze-screening according to the present invention is preferably 5 to 40% by weight based on the total weight of the composition, and the meteoric effect More preferably from 5 to 35% by weight, most preferably from 10 to 30% by weight. When the content of the meteorite is less than 5% by weight based on the total weight of the composition, there is a fear that the effect of blocking the snakes with the addition of meteorite and the effect of converting the snakes into the beneficial wavelength are insufficient. It may not be smooth to produce a preform in a semi-solid state without a large rise.
또한, 본 발명에 따른 수맥파 차단용 프리믹스 조성물은 일 구성성분으로 황토를 포함한다. 본 발명에 따른 수맥파 차단용 프리믹스 조성물에서 황토는 다른 성분과의 혼용성을 고려할 때 분말 형태인 것이 바람직하고, 이때, 황토 분말의 입도는 100~1000 메시(mesh)인 것이 바람직하고, 300~800 메시(mesh)인 것이 더 바람직하다. 또한, 본 발명에 따른 수맥파 차단용 프리믹스 조성물에서 황토의 함량은 크게 제한되지 않으며, 다른 성분들의 함량 관계를 고려할 때 운석(meteor) 100 중량부당 15~200 중량부인인 것이 바람직하고, 20-150 중량부인 것이 더 바람직하며, 25~100 중량부인 것이 가장 바람직하다.In addition, the premix composition for smack blocking according to the present invention includes yellow loess as one component. It is preferable that the loess is in the form of powder in consideration of compatibility with other components in the premix composition for blocking saumma wave according to the present invention. In this case, the loess powder preferably has a particle size of 100 to 1000 mesh, More preferably, it is a mesh. In addition, the content of the loess is not limited in the premix composition for snakes blocking according to the present invention, and it is preferably 15 to 200 parts by weight per 100 parts by weight of meteor in consideration of content of other components, More preferably 25 to 100 parts by weight.
또한, 본 발명에 따른 수맥파 차단용 프리믹스 조성물은 일 구성성분으로 점토를 포함한다. 상기 점토는 수맥파 차단용 프리믹스 조성물에 물을 첨가하고 반죽하여 수맥파 차단용 프리폼을 제조할 때 바인더 역할을 주로 담당한다. 본 발명에 따른 수맥파 차단용 프리믹스 조성물에서 점토는 다른 성분과의 혼용성을 고려할 때 분말 형태인 것이 바람직하고, 이때, 점토 분말의 입도는 100~1000 메시(mesh)인 것이 바람직하고, 300~800 메시(mesh)인 것이 더 바람직하다. 또한, 본 발명에 따른 수맥파 차단용 프리믹스 조성물에서 점토의 함량은 크게 제한되지 않으나, 프리폼 제조 과정에서 다른 성분들을 원활하게 접착시키는 역할을 고려할 때 운석(meteor) 100 중량부당 30~200 중량부인 것이 바람직하고, 50~150 중량부인 것이 더 바람직하며, 50~100 중량부인 것이 가장 바람직하다.In addition, the premix composition for smack blocking according to the present invention includes clay as one constituent. The clay mainly serves as a binder when water is added to the pre-mix composition for blocking the water drops and kneaded to prepare a pre-foam for blocking the water drops. The clay is preferably in the form of a powder in consideration of compatibility with other components in the premix composition for smackwash according to the present invention. The particle size of the clay powder is preferably 100 mesh to 1000 mesh, More preferably, it is a mesh. In addition, the content of clay in the premix composition for smackwash according to the present invention is not limited, but it is preferably 30 to 200 parts by weight per 100 parts by weight of meteor, considering the role of smoothly adhering other components in the preform manufacturing process More preferably 50 to 150 parts by weight, most preferably 50 to 100 parts by weight.
또한, 본 발명에 따른 수맥파 차단용 프리믹스 조성물은 구성성분으로 천연 광물질을 포함한다. 본 발명에 따른 천연 광물질은 운석과 조합하여 수맥파를 차단하는 효과 또는 수맥파를 이로운 파장으로 변환시키는 효과를 상승시킬 수 있는 것이라면 그 종류가 크게 제한되지 않으며, 예를 들어 도석, 규석, 활석, 장석, 토석 또는 백토 등에서 선택되는 1종 이상으로 구성될 수 있다. 본 발명에 따른 수맥파 차단용 프리믹스 조성물에서 천연 광물질은 다른 성분과의 혼용성을 고려할 때 분말 형태인 것이 바람직하고, 이때 천연 광물질의 입도는 100~1000 메시(mesh)인 것이 바람직하고, 300~800 메시(mesh)인 것이 더 바람직하다. 또한, 본 발명에 따른 수맥파 차단용 프리믹스 조성물에서 천연 광물질의 함량은 크게 제한되지 않으나, 운석과의 조합에 의한 수맥파 차단 효과 또는 수맥파를 이로운 파장으로 전환하는 효과를 고려할 때 운석(meteor) 100 중량부당 100~1000 중량부인 것이 바람직하고, 더 바람직하게는 150~700 중량부인 것이 더 바람직하며 150~500 중량부인 것이 가장 바람직하다. 한편, 본 발명에서 천연 광물질은 운석과의 조합에 의해 수맥파를 차단하는 효과 또는 수맥파를 이로운 파장으로 변환시키는 효과를 상승시키는데, 상기 상승 효과를 극대화하는 관점에서 도석, 규석 및 활석으로 구성되는 것이 바람직하다. 이때, 상기 도석:규석:활석의 중량비는 1:0.5:0.5 내지 1:3:3인 것이 더 바람직하다.
In addition, the premix composition for smack blocking according to the present invention comprises natural minerals as a constituent. The natural minerals according to the present invention are not limited in their kind insofar as they can increase the effect of blocking the snakes in combination with meteorites or the effect of converting the snakes into advantageous wavelengths. For example, Earth stone, clay or the like. It is preferable that the natural minerals in the premix compositions for smackwash according to the present invention are in the form of powder in consideration of compatibility with other components, and the particle size of the natural minerals is preferably 100 to 1000 mesh, More preferably, it is a mesh. In addition, the content of natural minerals in the premix composition for screening of the present invention is not limited. However, considering the effect of blocking snakes by combining with meteorites or converting snakes into advantageous wavelengths, More preferably 150 to 700 parts by weight, most preferably 150 to 500 parts by weight. On the other hand, in the present invention, natural minerals increase the effect of cutting off the snakes by combining with meteorites or converting the snakes into advantageous wavelengths. From the viewpoint of maximizing the synergy effect, it is preferable that the natural minerals consist of stones, Do. At this time, it is more preferable that the weight ratio of the stones: silica: talc is 1: 0.5: 0.5 to 1: 3: 3.
본 발명의 다른 측면은 수맥파 차단용 프리폼에 관한 것이다. 이때, 수맥파 차단용 프리폼은 다양한 모양의 성형품으로 성형될 수 있는 반고체 상태의 혼합물을 의미한다. 본 발명에서 수맥파 차단용 프리폼은 전술한 수맥파 차단용 프리믹스 조성물과 물의 혼합물로 이루어진다. 구체적으로, 전술한 수맥파 차단용 프리믹스 조성물에 소정의 물을 첨가하고 균일하게 반죽하여 반고체 상태의 수맥파 차단용 프리폼을 제조할 수 있다. 이때, 상기 수맥파 차단용 프리믹스 조성물 대 물의 혼합 중량비는 반고체 상태의 반죽을 형성하는 범위에서 선택될 수 있으며, 예를 들어 1:0.4 내지 1:0.7인 것이 바람직하고, 1:0.4 내지 1:0.6인 것이 더 바람직하며, 1:0.45 내지 1:0.55인 것이 가장 바람직하다.
Another aspect of the present invention relates to a pre-foam for smackers. At this time, the sump-blocking preform refers to a semi-solid mixture that can be molded into various shaped articles. In the present invention, the pre-foam for blocking the samp mantle is composed of a mixture of the premix composition for samp-mask protection and water described above. Specifically, predetermined water is added to the above-mentioned premix compositions for squeeze-screening and uniformly kneaded to prepare a semi-solid state preform for smack stoppage. In this case, the mixing ratio by weight of the premix composition for smacker blocking to water may be selected from the range of 1: 0.4 to 1: 0.7, preferably 1: 0.4 to 1: 0.6 More preferably 1: 0.45 to 1: 0.55.
이하, 본 발명을 실시예를 통하여 보다 구체적으로 설명한다. 다만, 하기 실시예는 본 발명의 기술적 특징을 명확하게 예시하기 위한 것일 뿐, 본 발명의 보호범위를 한정하는 것은 아니다.
Hereinafter, the present invention will be described in more detail with reference to examples. However, the following examples are intended to clearly illustrate the technical features of the present invention, and do not limit the scope of protection of the present invention.
1. One.
수맥파Smack
차단용 For blocking
프리믹스Premix
조성물 및 Composition and
프리폼(Preform)의Preform
제조 Produce
제조예 1.Production Example 1
운석(meteor) 50 중량부, 황토 100 중량부, 점토 100 중량부 및 도석 500 중량부를 혼합기에 넣고 입자 크기가 약 300~800 (mesh)가 되도록 미세 분말화하여 수맥파 차단용 프리믹스 조성물을 제조하였다. 이후, 상기 수맥파 차단용 프리믹스 조성물 100 중량부에 물 38 중량부를 첨가하고 반죽하여 반고체 상태의 수맥파 차단용 프리폼을 제조하였다.
50 parts by weight of meteor, 100 parts by weight of yellow clay, 100 parts by weight of clay and 500 parts by weight of stearic acid were put into a mixer and finely pulverized into particles having a particle size of about 300 to 800 mesh to prepare a premix composition for blocking the sapphire. Thereafter, 38 parts by weight of water was added to 100 parts by weight of the premix composition for blocking spheric wax, and the mixture was kneaded to prepare a semisolid pre-foam for blocking the water.
제조예 2.Production Example 2
수맥파 차단용 프리믹스 조성물의 일 구성 성분으로 도석 500 중량부 대신 규석 500 중량부를 사용한 점을 제외하고는 제조예 1과 동일한 조건 및 동일한 방법으로 수맥파 차단용 프리믹스 조성물 및 수맥파 차단용 프리폼을 제조하였다.
A pre-mix composition for blocking the water-shed wave and a pre-foam for blocking the water-shed wave were prepared under the same conditions and in the same manner as in Preparation Example 1, except that 500 parts by weight of silica was used instead of 500 parts by weight of stearic acid as one component of the pre-
제조예 3.Production Example 3
수맥파 차단용 프리믹스 조성물의 일 구성 성분으로 도석 500 중량부 대신 활석 500 중량부를 사용한 점을 제외하고는 제조예 1과 동일한 조건 및 동일한 방법으로 수맥파 차단용 프리믹스 조성물 및 수맥파 차단용 프리폼을 제조하였다.
A pre-mix composition for blocking a water-shock wave and a pre-foam for blocking a water-shock wave were prepared under the same conditions and in the same manner as in Preparation Example 1, except that 500 parts by weight of talc was used instead of 500 parts by weight of talc as one component of the pre-
제조예 4.Production Example 4
운석(meteor) 300 중량부, 황토 50 중량부, 점토 100 중량부 및 도석 300 중량부를 혼합기에 넣고 입자 크기가 약 300~800 (mesh)가 되도록 미세 분말화하여 수맥파 차단용 프리믹스 조성물을 제조하였다. 이후, 상기 수맥파 차단용 프리믹스 조성물 100 중량부에 물 40 중량부를 첨가하고 반죽하여 반고체 상태의 수맥파 차단용 프리폼을 제조하였다.
300 parts by weight of meteor, 50 parts by weight of yellow clay, 100 parts by weight of clay and 300 parts by weight of stearic acid were put into a mixer and finely pulverized into particles having a particle size of about 300 to 800 mesh to prepare a premix composition for blocking insecticide. Then, 40 parts by weight of water was added to 100 parts by weight of the premix composition for blocking the water-shed-mask, and the mixture was kneaded to prepare a semisolid pre-foam for blocking the water.
제조예 5.Production Example 5
수맥파 차단용 프리믹스 조성물의 일 구성 성분으로 도석 300 중량부 대신 규석 300 중량부를 사용한 점을 제외하고는 제조예 4와 동일한 조건 및 동일한 방법으로 수맥파 차단용 프리믹스 조성물 및 수맥파 차단용 프리폼을 제조하였다.
The pre-mix composition for blocking the water drops and the pre-foam for blocking the water drops were prepared under the same conditions and in the same manner as in Preparation Example 4, except that 300 parts by weight of silica was used instead of 300 parts by weight of stearic acid as one component of the premix composition for blocking the water drops.
제조예 6.Production Example 6
수맥파 차단용 프리믹스 조성물의 일 구성 성분으로 도석 300 중량부 대신 활석 300 중량부를 사용한 점을 제외하고는 제조예 4와 동일한 조건 및 동일한 방법으로 수맥파 차단용 프리믹스 조성물 및 수맥파 차단용 프리폼을 제조하였다.
A pre-mix composition for blocking a water-shock wave and a pre-foam for blocking a water-shock wave were prepared under the same conditions and in the same manner as in Preparation Example 4, except that 300 parts by weight of talc was used instead of 300 parts by weight of talc as one component of the pre-
제조예 7.Production Example 7
운석(meteor) 50 중량부, 황토 100 중량부, 점토 100 중량부, 도석 250 중량부 및 규석 250 중량부를 혼합기에 넣고 입자 크기가 약 300~800 (mesh)가 되도록 미세 분말화하여 수맥파 차단용 프리믹스 조성물을 제조하였다. 이후, 상기 수맥파 차단용 프리믹스 조성물 100 중량부에 물 38 중량부를 첨가하고 반죽하여 반고체 상태의 수맥파 차단용 프리폼을 제조하였다.
50 parts by weight of meteor, 100 parts by weight of loess, 100 parts by weight of clay, 250 parts by weight of stones and 250 parts by weight of silicate were added to a mixer and finely pulverized to a particle size of about 300 to 800 mesh, A composition was prepared. Thereafter, 38 parts by weight of water was added to 100 parts by weight of the premix composition for blocking spheric wax, and the mixture was kneaded to prepare a semisolid pre-foam for blocking the water.
제조예 8.Production Example 8
운석(meteor) 50 중량부, 황토 100 중량부, 점토 100 중량부, 도석 150 중량부, 규석 150 중량부 및 활석 200 중량부를 혼합기에 넣고 입자 크기가 약 300~800 (mesh)가 되도록 미세 분말화하여 수맥파 차단용 프리믹스 조성물을 제조하였다. 이후, 상기 수맥파 차단용 프리믹스 조성물 100 중량부에 물 38 중량부를 첨가하고 반죽하여 반고체 상태의 수맥파 차단용 프리폼을 제조하였다
50 parts by weight of meteor, 100 parts by weight of loess, 100 parts by weight of clay, 150 parts by weight of stones, 150 parts by weight of zeolite and 200 parts by weight of talc were put into a mixer and finely pulverized to a particle size of about 300 to 800 mesh To prepare a premix composition for blocking samsam. Thereafter, 38 parts by weight of water was added to 100 parts by weight of the premix composition for blocking the spheric wax, and the mixture was kneaded to prepare a semi-solid,
제조예 9.Production Example 9
운석(meteor) 300 중량부, 황토 50 중량부, 점토 100 중량부, 도석 100 중량부, 규석 100 중량부 및 활석 100 중량부를 혼합기에 넣고 입자 크기가 약 300~800 (mesh)가 되도록 미세 분말화하여 수맥파 차단용 프리믹스 조성물을 제조하였다. 이후, 상기 수맥파 차단용 프리믹스 조성물 100 중량부에 물 40 중량부를 첨가하고 반죽하여 반고체 상태의 수맥파 차단용 프리폼을 제조하였다.
300 parts by weight of meteor, 50 parts by weight of loess, 100 parts by weight of clay, 100 parts by weight of stearic acid, 100 parts by weight of zirconium and 100 parts by weight of talc were put into a mixer and finely pulverized to a particle size of about 300 to 800 To prepare a premix composition for blocking samsam. Then, 40 parts by weight of water was added to 100 parts by weight of the premix composition for blocking the water-shed-mask, and the mixture was kneaded to prepare a semisolid pre-foam for blocking the water.
비교제조예 1.Comparative Production Example 1
황토 50 중량부, 점토 100 중량부 및 도석 600 중량부를 혼합기에 넣고 입자 크기가 약 300~800 (mesh)가 되도록 미세 분말화하여 수맥파 차단용 프리믹스 조성물을 제조하였다. 이후, 상기 수맥파 차단용 프리믹스 조성물 100 중량부에 물 40 중량부를 첨가하고 반죽하여 반고체 상태의 수맥파 차단용 프리폼을 제조하였다.
50 parts by weight of yellow clay, 100 parts by weight of clay and 600 parts by weight of stearic acid were put into a mixer and finely pulverized into particles having a particle size of about 300 to 800 mesh to prepare a premix composition for blocking the water. Then, 40 parts by weight of water was added to 100 parts by weight of the premix composition for blocking the water-shed-mask, and the mixture was kneaded to prepare a semisolid pre-foam for blocking the water.
비교제조예 2.Comparative Preparation Example 2
황토 50 중량부, 점토 100 중량부 및 규석 600 중량부를 혼합기에 넣고 입자 크기가 약 300~800 (mesh)가 되도록 미세 분말화하여 수맥파 차단용 프리믹스 조성물을 제조하였다. 이후, 상기 수맥파 차단용 프리믹스 조성물 100 중량부에 물 40 중량부를 첨가하고 반죽하여 반고체 상태의 수맥파 차단용 프리폼을 제조하였다.
50 parts by weight of yellow clay, 100 parts by weight of clay and 600 parts by weight of silicate were added to a mixer and finely pulverized into particles having a particle size of about 300 to 800 mesh to prepare a premix composition for smack wave shielding. Then, 40 parts by weight of water was added to 100 parts by weight of the premix composition for blocking the water-shed-mask, and the mixture was kneaded to prepare a semisolid pre-foam for blocking the water.
비교제조예 3.Comparative Preparation Example 3
황토 50 중량부, 점토 100 중량부 및 활석 600 중량부를 혼합기에 넣고 입자 크기가 약 300~800 (mesh)가 되도록 미세 분말화하여 수맥파 차단용 프리믹스 조성물을 제조하였다. 이후, 상기 수맥파 차단용 프리믹스 조성물 100 중량부에 물 40 중량부를 첨가하고 반죽하여 반고체 상태의 수맥파 차단용 프리폼을 제조하였다.
50 parts by weight of loess, 100 parts by weight of clay, and 600 parts by weight of talc were added to a mixer and finely pulverized into particles having a particle size of about 300 to 800 mesh to prepare a premix composition for blocking the water. Then, 40 parts by weight of water was added to 100 parts by weight of the premix composition for blocking the water-shed-mask, and the mixture was kneaded to prepare a semisolid pre-foam for blocking the water.
비교제조예 4.Comparative Preparation Example 4
참숯 300 중량부, 황토 50 중량부, 점토 100 중량부, 도석 100 중량부, 규석 100 중량부 및 활석 100 중량부를 혼합기에 넣고 입자 크기가 약 300~800 (mesh)가 되도록 미세 분말화하여 수맥파 차단용 프리믹스 조성물을 제조하였다. 이후, 상기 수맥파 차단용 프리믹스 조성물 100 중량부에 물 40 중량부를 첨가하고 반죽하여 반고체 상태의 수맥파 차단용 프리폼을 제조하였다.
300 parts by weight of charcoal, 50 parts by weight of loess, 100 parts by weight of clay, 100 parts by weight of stones, 100 parts by weight of zircon, and 100 parts by weight of talc were put into a mixer and finely pulverized to a particle size of about 300 to 800 (mesh) Lt; / RTI > Then, 40 parts by weight of water was added to 100 parts by weight of the premix composition for blocking the water-shed-mask, and the mixture was kneaded to prepare a semisolid pre-foam for blocking the water.
비교제조예 5.Comparative Preparation Example 5
견운모 300 중량부, 황토 50 중량부, 점토 100 중량부, 도석 100 중량부, 규석 100 중량부 및 활석 100 중량부를 혼합기에 넣고 입자 크기가 약 300~800 (mesh)가 되도록 미세 분말화하여 수맥파 차단용 프리믹스 조성물을 제조하였다. 이후, 상기 수맥파 차단용 프리믹스 조성물 100 중량부에 물 40 중량부를 첨가하고 반죽하여 반고체 상태의 수맥파 차단용 프리폼을 제조하였다.
300 weight parts of the sericite, 50 weight parts of the loess, 100 weight parts of the clay, 100 weight parts of the stones, 100 weight parts of the stones and 100 weight parts of the talc were put into a mixer and finely pulverized to a particle size of about 300 to 800 mesh, Lt; / RTI > Then, 40 parts by weight of water was added to 100 parts by weight of the premix composition for blocking the water-shed-mask, and the mixture was kneaded to prepare a semisolid pre-foam for blocking the water.
비교제조예 6.Comparative Preparation Example 6
옻나무 300 중량부, 황토 50 중량부, 점토 100 중량부, 도석 100 중량부, 규석 100 중량부 및 활석 100 중량부를 혼합기에 넣고 입자 크기가 약 300~800 (mesh)가 되도록 미세 분말화하여 수맥파 차단용 프리믹스 조성물을 제조하였다. 이후, 상기 수맥파 차단용 프리믹스 조성물 100 중량부에 물 40 중량부를 첨가하고 반죽하여 반고체 상태의 수맥파 차단용 프리폼을 제조하였다.
300 parts by weight of lacquer, 50 parts by weight of loess, 100 parts by weight of clay, 100 parts by weight of stones, 100 parts by weight of silicate and 100 parts by weight of talc were added to a mixer and finely pulverized to a particle size of about 300 to 800 mesh, Lt; / RTI > Then, 40 parts by weight of water was added to 100 parts by weight of the premix composition for blocking the water-shed-mask, and the mixture was kneaded to prepare a semisolid pre-foam for blocking the water.
비교제조예 7.Comparative Preparation Example 7
솔잎 300 중량부, 황토 50 중량부, 점토 100 중량부, 도석 100 중량부, 규석 100 중량부 및 활석 100 중량부를 혼합기에 넣고 입자 크기가 약 300~800 (mesh)가 되도록 미세 분말화하여 수맥파 차단용 프리믹스 조성물을 제조하였다. 이후, 상기 수맥파 차단용 프리믹스 조성물 100 중량부에 물 40 중량부를 첨가하고 반죽하여 반고체 상태의 수맥파 차단용 프리폼을 제조하였다.
300 parts by weight of pine needle, 50 parts by weight of loess, 100 parts by weight of clay, 100 parts by weight of stearic acid, 100 parts by weight of zeolite and 100 parts by weight of talc were put into a mixer and finely pulverized to a particle size of about 300 to 800 mesh, Lt; / RTI > Then, 40 parts by weight of water was added to 100 parts by weight of the premix composition for blocking the water-shed-mask, and the mixture was kneaded to prepare a semisolid pre-foam for blocking the water.
2. 2. 수맥파Smack 차단용 For blocking 프리폼으로By preform 성형한 판재의 Of the molded plate 수맥파Smack 차단 효과 평가 Evaluation of blocking effect
한국수맥학회에서 제작한 L-로드(L-rod) 2개를 사용하여 약 40평형의 아파트에서 수맥이 지나가는 자리를 조사하였고, 총 5개의 수맥이 흐르는 지점을 발견하였으며, 그 중 수맥파 발생 강도가 가장 큰 지점을 시험 지점으로 선택하였다. 즉, 2개의 L-로드(L-rod)를 평행하게 양손에 1개씩 잡고 수맥이 흐르는 지점 즉, 수맥파가 존재하는 지점에 도달하면 2개의 L-로드(L-rod)는 안쪽으로 회전하고 수맥파가 존재하지 않으면 평행하거나 바깥쪽으로 회전한다. 이때, L-로드(L-rod)를 잡은 손과 L-로드(L-rod)가 평행할 때를 기준점, 즉 0°로 하여 L-로드(L-rod)가 안쪽 또는 바깥쪽으로 회전할 때 기준점과 이루는 각을 θ로 정의하였다. L-로드(L-rod)가 안쪽으로 회전하고 그때의 θ값이 커질수록 수맥파의 발생 강도가 커짐을 의하고, L-로드(L-rod)가 바깥쪽으로 회전하고 그때의 θ값이 커질수록 수맥파가 완전히 차단되고 오히려 인체에 유익한 파장으로 전환됨을 의미한다. 도 1은 L-로드(L-rod)를 잡은 손과 L-로드(L-rod)가 평행할 때를 기준점으로 하였을 때, L-로드(L-rod)가 바깥쪽으로 소정의 각도 θ만큼 회전한 상태를 나타낸 것이다.Using two L-rods manufactured by the Korean Society of Veterinary Medicine, we surveyed the passage of water in a 40-pyeong apartment, and found a total of five water-shedding points. Among them, The largest point was chosen as the test point. That is, when two L-rods are held in parallel to each other and one of the L-rods reaches the point where the snakes flow, that is, where the snakes are present, the two L-rods rotate inward, If it does not exist, it will be parallel or outward. At this time, when the L-rod rotates inward or outward at a reference point, that is, when the L-rod is in parallel with the hand holding the L-rod, The angle formed with the reference point is defined as?. As the L-rod rotates inward and the θ value at that time increases, the generation strength of the squeak wave increases. When the L-rod rotates outward and the θ value at that time increases, Is completely blocked and converted into a wavelength that is beneficial to the human body. FIG. 1 is a cross-sectional view showing a state in which the L-rod is rotated outward by a predetermined angle? When the L-rod is parallel to the hand holding the L-rod, .
상기 제조예 1 내지 9 및 비교제조예 1 내지 7에서 제조한 수맥파 차단용 프리폼을 각각 가로 2m, 세로 2m 및 두께 2㎜의 크기로 성형한 후 약 12시간 동안 건조하여 수맥파 차단용 판재를 제조하였다. 이후, 수맥이 흐르는 시험 지점의 바닥에 수맥파 차단용 판재를 부착한 후 한국수맥학회에서 제작한 L-로드(L-rod) 2개를 사용하여 수맥파 차단 여부를 측정하였다. 수맥이 흐르는 동일한 시험 지점에 수맥파 차단용 판재를 바꾸어 가면서 총 16번의 시험을 진행하였다.Each of the pre-forms for blocking the smack pawls prepared in Preparation Examples 1 to 9 and Comparative Preparations 1 to 7 was formed into a size of 2 m in length, 2 m in length and 2 mm in thickness and dried for about 12 hours to prepare a plate for blocking saw- . Subsequently, a plate for blocking the snakes was attached to the bottom of the test point where the snakes were running, and then the two L-rods manufactured by the Korean Society of Zoology were used to measure the snakes. A total of 16 tests were carried out while changing the sheet metal for blocking the submachine at the same test point where the sump flows.
하기 표 1은 수맥이 흐르는 시험 지점의 바닥에 수맥파 차단용 판재를 부착한 후 L-로드(L-rod) 2개로 수맥파 차단 여부를 측정한 결과를 나타낸 것이다.Table 1 below shows the result of measuring the number of L-rods by using two L-rods after inserting the saucer-blocking plate on the bottom of the test point where the sump flows.
이상에서와 같이 본 발명을 상기의 실시예를 통해 설명하였지만 본 발명이 반드시 여기에만 한정되는 것은 아니며 본 발명의 범주와 사상을 벗어나지 않는 범위 내에서 다양한 변형실시가 가능함은 물론이다. 따라서, 본 발명의 보호범위는 최상의 양식으로서 개시된 특정 실시 태양으로 국한되는 것이 아니며, 본 발명에 첨부된 특허청구의 범위에 속하는 모든 실시 태양을 포함하는 것으로 해석되어야 한다.While the present invention has been particularly shown and described with reference to exemplary embodiments thereof, it is to be understood that the invention is not limited to the disclosed exemplary embodiments, but, on the contrary, is intended to cover various modifications and equivalent arrangements included within the spirit and scope of the appended claims. Accordingly, the scope of protection of the present invention should not be construed as limited to the specific embodiments disclosed as the best mode, but should be construed as including all embodiments falling within the scope of the appended claims.
Claims (8)
상기 천연 광물질은 도석, 규석 및 활석으로 구성되고,
상기 운석의 함량은 조성물 전체 중량을 기준으로 5~40 중량%인 것을 특징으로 하는 수맥파 차단용 프리믹스 조성물.
A composition comprising natural minerals, meteorites, loess and clay,
The natural minerals are composed of stoneware, silica and talc,
Wherein the meteorite content is 5 to 40 wt% based on the total weight of the composition.
The premix composition of claim 1, wherein the content of the loess is 15 to 200 parts by weight per 100 parts by weight of meteor.
The premix composition of claim 1, wherein the content of the clay is 30-200 parts by weight per 100 parts by weight of meteor.
The premix composition of claim 1, wherein the natural mineral content is 100-1000 parts by weight per 100 parts by weight of meteor.
The premix composition of claim 1, wherein the weight ratio of stonite: silica: talc is 1: 0.5: 0.5 to 1: 3: 3.
A pre-foam for blocking water of Sulfur-containing water comprising a premix composition according to any one of claims 1 to 4 and water.