KR101399328B1 - Removal method of free formalin - Google Patents
Removal method of free formalin Download PDFInfo
- Publication number
- KR101399328B1 KR101399328B1 KR1020130136995A KR20130136995A KR101399328B1 KR 101399328 B1 KR101399328 B1 KR 101399328B1 KR 1020130136995 A KR1020130136995 A KR 1020130136995A KR 20130136995 A KR20130136995 A KR 20130136995A KR 101399328 B1 KR101399328 B1 KR 101399328B1
- Authority
- KR
- South Korea
- Prior art keywords
- mam
- acrylic emulsion
- present
- formalin
- free formalin
- Prior art date
Abstract
Description
본 발명은 프리 포르말린 제거방법 및 이에 의하여 제조되는 아크릴계 에멀젼에 관한 것으로서, 더욱 상세하게는 프리 포르말린(Free Formalin)을 에틸렌 우레아(Ethylene Urea, EU)와 반응시켜 제거하는 프리 포르말린 제거방법 및 이에 의하여 프리 포르말린(Free Formalin)이 제거되어 제조되는 것을 특징으로 하는 아크릴계 에멀젼에 관한 것이다.
The present invention relates to a method for removing formaldehyde and an acrylic emulsion produced thereby. More particularly, the present invention relates to a method for removing formaldehyde by reacting free formalin with ethylene urea (EU) The present invention relates to an acrylic emulsion in which free formalin is removed.
N-메티롤아크릴아미드(N-Methylolacrylamide, N-MAM)는 응용범위가 매우 넓은 정밀화학제품이다. 분자구조에 두 개 이상의 활성중심을 가지고 있기에 가교성 모노머(架橋性 모노머, crosslinking monomer)의 특성을 가지고 있으며 섬유 개질, 수지가공, 도료, 플라스틱, 접착제, 토양개량제 등 많은 영역에 활용되고 있다.
N-Methylolacrylamide (N-MAM) is a fine chemical product with a very wide application range. Because it has two or more active centers in its molecular structure, it has properties of crosslinking monomer (crosslinking monomer) and is used in many fields such as fiber modification, resin processing, paint, plastic, adhesive, soil improvement agent.
특히, 아크릴 수지의 합성과정에서 수성이나 유성을 막론하고 광범위하게 이용되고 있지만, 프리 포르말린(Free Formalin)의 검출 문제로 인하여 친환경화 되지 못하고 있다. 아크릴 에멀젼의 견뢰도를 향상하기 위한 수단으로서 N-MAM의 대용 가교제로서 AAEM, HEAA, TMPTMA, GMA, DAAM, PETA 등 원료 자체나 가교반응 과정에 전혀 프리 포르말린(Free Formalin)이 검출되지 않는 다수의 친환경 가교제들이 이용되고 있지만 아직까지 N-MAM의 가교 성능을 초월하는 범용 가교제가 개발되지 못하고 있는 실정이다.
Particularly, it is widely used regardless of whether it is aqueous or oily in the process of synthesizing acrylic resin, but it is not eco-friendly due to detection problem of free formalin. As a means for improving the fastness of an acrylic emulsion, a large number of eco-friendly materials such as AAEM, HEAA, TMPTMA, GMA, DAAM, and PETA, which are free of formalin Although cross-linking agents have been used, a universal cross-linking agent exceeding the crosslinking ability of N-MAM has not yet been developed.
본 발명은 상기한 바와 같은 종래 기술의 문제점을 해결하기 위하여 안출된 것으로서, 본 발명은 프리 포르말린(Free Formalin)을 제거하는 방법을 제공하는 것을 발명의 목적으로 한다.
SUMMARY OF THE INVENTION The present invention has been made in order to solve the problems of the prior art as described above, and it is an object of the present invention to provide a method for removing free formalin.
또한, 본 발명은 아크릴계 에멀젼에서 사용되는 가교성 모노머(Monomer)로 사용되는 N-MAM에서 제기되어 온 프리 포르말린(Free Formalin) 관련 문제점을 해결하는 것을 발명의 목적으로 한다.
It is another object of the present invention to solve the problems associated with free formalin which has been proposed in N-MAM used as a crosslinkable monomer used in an acrylic emulsion.
또한, 본 발명은 EU를 이용하여 아크릴계 에멀젼의 가교성 모노머(Monomer)로 사용되는 N-MAM 자체에서 발생하는 프리 포르말린을 제거하는 방법을 제공하는 것을 발명의 다른 목적으로 한다.
It is another object of the present invention to provide a method for removing a preformalin generated in N-MAM itself which is used as a crosslinkable monomer of an acrylic emulsion by using EU.
또한, 본 발명은 EU를 이용하여 아크릴계 에멀젼의 가교성 모노머(Monomer)로 사용되는 N-MAM으로부터 가교 반응 중에 발생하는 프리 포르말린을 제거하는 방법을 제공하는 것을 발명의 또 다른 목적으로 한다.
It is another object of the present invention to provide a method for removing formaldehyde generated during a crosslinking reaction from N-MAM used as a crosslinkable monomer of an acrylic emulsion using EU.
또한, 본 발명은 가교성 모노머(Monomer)로서 N-MAM을 사용하는 아크릴계 에멀젼을 친환경화 시키는 제조방법 및 이에 의하여 제조되는 친환경 아크릴계 에멀젼을 제공하는 것을 발명의 또 다른 목적으로 한다.
It is another object of the present invention to provide a process for producing an eco-friendly emulsion of an acrylic emulsion using N-MAM as a crosslinkable monomer and an eco-friendly acrylic emulsion produced thereby.
본 발명의 해결하고자 하는 과제는 이상에서 언급한 것들에 한정되지 않으며, 언급되지 아니한 다른 해결하고자 하는 과제들은 아래의 기재로부터 당업자에게 명확하게 이해되어질 수 있을 것이다.
The problems to be solved by the present invention are not limited to those mentioned above, and other problems to be solved can be clearly understood by those skilled in the art from the following description.
상기와 같은 목적을 달성하기 위하여 본 발명에 따른 프리 포르말린의 제거방법은, 프리 포르말린(Free Formalin)을 에틸렌 우레아(Ethylene Urea, EU)와 반응시켜 제거하는 것을 특징으로 한다.
In order to accomplish the above object, the present invention provides a method for removing formaldehyde, which comprises removing free formalin by reacting with ethylene urea (EU).
또한, 본 발명에 따른 프리 포르말린의 제거방법은, 상기 프리 포르말린(Free Formalin)이 아마이드와 포르말린의 하이드록시메틸화 반응에 의하여 N-메티롤아크릴아미드(N-Methylolacrylamide, N-MAM)로부터 발생한 프리 포르말린(Free Formalin)인 것을 특징으로 한다.
The method for removing formaldehyde according to the present invention is a method for removing formaldehyde generated from N-Methylolacrylamide (N-MAM) by hydroxymethylation reaction of amide and formalin, (Free Formalin).
또한, 본 발명에 따른 프리 포르말린의 제거방법은, 상기 프리 포르말린(Free Formalin)이 가교성 모노머로서 N-메티롤아크릴아미드(N-Methylolacrylamide, N-MAM)를 포함하는 아크릴계 에멀젼의 제조방법에 있어서, 아크릴계 에멀젼의 열처리 과정에서 가교 반응에 의하여 상기 N-MAM으로부터 발생하는 프리 포르말린(Free Formalin)인 것을 특징으로 한다.
The present invention also provides a method for preparing an acrylic emulsion, wherein the free formalin comprises N-methylolacrylamide (N-MAM) as a crosslinking monomer, And free formalin generated from the N-MAM by a crosslinking reaction in the heat treatment process of the acrylic emulsion.
또한, 본 발명에 따른 프리 포르말린의 제거방법은, 상기 N-MAM과 EU의 반응은 아크릴계 에멀젼의 합성 과정 또는 합성 후에 이루어지는 것을 특징으로 한다.
The method for removing formaldehyde according to the present invention is characterized in that the reaction between the N-MAM and the EU is performed after the synthesis or synthesis of the acrylic emulsion.
한편, 본 발명에 따른 아크릴계 에멀젼은 상기 본 발명에 따른 프리 포르말린의 제거방법에 의하여 프리 포르말린(Free Formalin)이 제거되어 제조되는 것을 특징으로 한다.
Meanwhile, the acrylic emulsion according to the present invention is characterized in that the free formalin is removed by removing the preformalin according to the present invention.
이상과 같은 구성의 본 발명에 따른 프리 포르말린의 제거방법에 의하면, EU를 이용하여 프리 포르말린(Free Formalin)을 제거하는 방법을 제공할 수 있다.
According to the method of removing formaldehyde according to the present invention having the above-described structure, a method of removing free formalin using EU can be provided.
또한, 본 발명에 따른 프리 포르말린의 제거방법에 의하면, EU를 이용하여 아크릴계 에멀젼에서 사용되는 가교성 모노머(Monomer)로 사용되는 N-MAM에서 제기되어 온 프리 포르말린(Free Formalin) 관련 문제점을 해결할 수 있는 효과를 제공한다.
Further, according to the method of removing the formalin according to the present invention, it is possible to solve the problem related to the free formalin which has been proposed in the N-MAM used as a crosslinkable monomer used in the acrylic emulsion by using the EU Provides an effect.
또한, 본 발명에 따른 아크릴계 에멀젼의 프리 포르말린 제거방법에 의하면, EU를 이용하여 아크릴계 에멀젼의 가교성 모노머(Monomer)로 사용되는 N-MAM 자체에서 발생하는 프리 포르말린을 제거할 수 있는 효과를 제공한다.
Also, according to the method of removing formaldehyde from acrylic emulsion according to the present invention, it is possible to remove the preformalin generated in N-MAM itself used as a crosslinkable monomer of an acrylic emulsion by using EU .
또한, 본 발명에 따른 아크릴계 에멀젼의 프리 포르말린 제거방법에 의하면, EU를 이용하여 아크릴계 에멀젼의 가교성 모노머(Monomer)로 사용되는 N-MAM으로부터 가교 반응 중에 발생하는 프리 포르말린을 제거할 수 있는 효과를 제공한다.
Further, according to the method of removing formaldehyde from acrylic emulsion according to the present invention, it is possible to remove the preformalin generated during crosslinking reaction from N-MAM used as a crosslinkable monomer of acrylic emulsion by using EU to provide.
또한, 본 발명에 따른 아크릴계 에멀젼에 의하면, 가교성 모노머(Monomer)로서 N-MAM을 사용하는 아크릴계 에멀젼을 친환경화 시킬 수 있는 효과를 제공한다.
Further, according to the acrylic emulsion according to the present invention, an acrylic emulsion using N-MAM as a crosslinkable monomer can be eco-friendly.
본 발명의 효과는 이상에서 언급한 것들에 한정되지 않으며, 언급되지 아니한 다른 효과들은 아래의 기재로부터 당업자에게 명확하게 이해되어질 수 있을 것이다.
The effects of the present invention are not limited to those mentioned above, and other effects not mentioned can be clearly understood by those skilled in the art from the following description.
도 1a 내지 1b는 본 발명에 따른 아크릴계 에멀젼의 프리 포르말린 제거방법에서 프리 포르말린의 발생 메카니즘을 보여주는 화학반응식.
도 2는 본 발명에 따른 아크릴계 에멀젼의 프리 포르말린 제거방법에서 프리 포르말린의 제거 메카니즘을 보여주는 화학반응식.FIGS. 1A to 1B are chemical schemes showing the mechanism of the formation of preformalin in the method of removing formalin from acrylic emulsion according to the present invention.
2 is a chemical reaction formula showing the removal mechanism of the formalin in the method for removing formalin in the acrylic emulsion according to the present invention.
이하, 후술되어 있는 내용을 참조하여 본 발명의 바람직한 실시예들을 상세히 설명한다. 그러나, 본 발명은 여기서 설명되는 실시예들에 한정되지 않고 다른 형태로 구체화될 수도 있다. 오히려, 여기서 소개되는 실시예들은 개시된 내용이 철저하고 완전해질 수 있도록 그리고 당업자에게 본 발명의 기술적 사상이 충분히 전달될 수 있도록 하기 위해 제공 되어지는 것이다. 본 명세서 전체에 걸쳐서 동일한 부호들은 동일한 구성요소들을 나타낸다.
Hereinafter, preferred embodiments of the present invention will be described in detail with reference to the following description. However, the present invention is not limited to the embodiments described herein but may be embodied in other forms. Rather, the embodiments disclosed herein are provided so that this disclosure will be thorough and complete, and will fully convey the scope of the invention to those skilled in the art. Like numbers refer to like elements throughout.
도 1a 내지 1b는 본 발명에 따른 아크릴계 에멀젼의 프리 포르말린 제거방법에서 프리 포르말린의 발생 메카니즘을 보여주는 화학반응식이고, 도 2는 본 발명에 따른 아크릴계 에멀젼의 프리 포르말린 제거방법에서 프리 포르말린의 제거 메카니즘을 보여주는 화학반응식이다.
1A and 1B are chemical reaction formulas showing the mechanism of the formation of preformalin in the method of removing formalin in the acrylic emulsion according to the present invention, and FIG. 2 is a view showing a mechanism of removing formaldehyde in the method of removing formalin in the acrylic emulsion according to the present invention. It is a chemical reaction formula.
본 발명은 프리 포르말린(Free Formalin)을 에틸렌 우레아(Ethylene Urea, EU)와 반응시켜 제거하는 프리 포르말린의 제거방법에 관한 것이다. 특히, 가교성 모노머로서 N-메티롤아크릴아미드(N-Methylolacrylamide, N-MAM)를 포함하는 아크릴계 에멀젼의 제조방법에 있어서, N-MAM 원료 자체에서 발생하는 프리 포르말린(Free Formalin)과 열처리 과정의 가교 반응 중에 발생되는 프리 포르말린(Free Formalin)을 제거하는 방법에 관한 것이다.
The present invention relates to a method for removing free formalin by reacting free formalin with ethylene urea (EU). Particularly, in the process for producing an acrylic emulsion containing N-methylolacrylamide (N-MAM) as a crosslinkable monomer, the free formalin generated in the N-MAM raw material itself and the heat- And to a method for removing free formalin generated during a crosslinking reaction.
아크릴 접착제는 아크릴산에틸, 아크릴산부틸, 아크릴산-2-에틸헥실 등을 주체로 하며, 이것과 메타크릴산에스테르, 스티렌, 아크릴로니트릴, 아세트산비닐 등과의 공중합물이다. 섬유용으로 사용되는 열경화 아크릴 에멀젼은 N-메티롤아크릴아미드나 글리시딜메타크릴레이트 등을 공중합하며, 플록(floc) 가공이나 직물 접착과 같이 고점도를 필요로 하는 에멀젼은 아크릴산이나 메타크릴산을 공중합하여 사용 전에 알칼리를 첨가하여 점도를 증가시키는 방법을 취하고 있다.
Acrylic adhesives mainly consist of ethyl acrylate, butyl acrylate, 2-ethylhexyl acrylate, etc., and copolymers thereof with methacrylate esters, styrene, acrylonitrile, and vinyl acetate. The thermosetting acrylic emulsion used for the fiber is copolymerized with N-methylol acrylamide or glycidyl methacrylate. Emulsions requiring high viscosity, such as floc processing or fabric adhesion, are made of acrylic acid or methacrylic acid Is copolymerized and alkali is added before use to increase the viscosity.
아크릴계 에멀젼에서 프리 포르말린(Free Formalin)은 주로 자기가교형 모노머인 N-메티롤아크릴아미드(N-Methylolacrylamide, N-MAM)에서 석출된다. 이와 같은 아크릴계 에멀젼에서 프리 포르말린의 발생원인 내지 루트는 다음의 두 가지 요인으로 볼 수 있다.
In the acrylic emulsion, Free Formalin is mainly precipitated from N-Methylolacrylamide (N-MAM), which is a self-crosslinking monomer. The cause and route of the formalin in the acrylic emulsion can be considered as the following two factors.
하나는, 아마이드와 프리 포르말린의 하이드록시메틸(Hydroxymethyl)화 반응은 가역반응이므로 하이드록시메틸화된 N-MAM은 프리 포르말린을 석출한다. N-MAM 원료 중 0.5 중량% 미만이 함유되어 있는 것으로 알려져 있으며, 도 1a에서 도시한 바와 같이 그 발생 메카니즘(Mechaism)은 아래 화학반응식과 같다.One is that the hydroxymethylation reaction of amide and formaldehyde is a reversible reaction, so the hydroxymethylated N-MAM precipitates the formalin. It is known that less than 0.5% by weight of the raw material of N-MAM is contained. As shown in FIG. 1A, the mechanism of the mechanism is represented by the following chemical reaction formula.
다른 하나는, 아크릴 수지의 열처리 과정에서 가교 반응에 의하여 프리 포르말린(Free Formalin)이 석출되며, 구체적인 석출량은 N-MAM의 함량에 따라 다르다. 도 1b에서 도시한 바와 같이 그 발생 메카니즘(Mechaism)은 아래 화학반응식과 같다.The other is that free formalin is precipitated by the crosslinking reaction during the heat treatment of the acrylic resin, and the specific precipitation amount differs depending on the content of N-MAM. As shown in FIG. 1B, its mechanism of occurrence (Mechaism) is shown in the following chemical reaction formula.
본 발명은, 아크릴계 에멀젼에서 상기한 바와 같은 발생 메카니즘에 의하여 N-MAM 원료 자체에서 발생하는 프리 포르말린(Free Formalin)과 열처리 과정의 가교 반응 중에 발생되는 프리 포르말린(Free Formalin)을 에틸렌 우레아(Ethylene Urea, EU, 
상기한 바와 같은 프리 포르말린(Free Formalin)과 EU의 반응은 아크릴계 에멀젼의 합성 과정 중에 이루어지도록 가교성 모노머로서 N-MAM을 사용하는 공지의 아크릴계 에멀젼 합성 과정(합성온도 60 ~ 70℃) 중에 EU를 N-MAM의 1.2 내지 1.5 배의 당량비로 혼합함으로써 달성할 수 있다.
The reaction between free formalin and EU as described above is carried out in a known acrylic emulsion synthesis process (at a synthesis temperature of 60 to 70 ° C) using N-MAM as a crosslinkable monomer so as to be carried out during the synthesis of an acrylic emulsion, At an equivalent ratio of 1.2 to 1.5 times that of N-MAM.
또한, 아크릴 에멀젼의 합성 종료 후에 상온에서 합성 종료된 아크릴 에멀젼에 EU를 N-MAM의 1.2 내지 1.5 배의 당량비로 단순 혼합하여 구성할 수 있다.
Further, after completion of the synthesis of the acrylic emulsion, EU can be simply mixed with the acrylic emulsion synthesized at room temperature at an equivalent ratio of 1.2 to 1.5 times of N-MAM.
한편, 본 발명에 따른 아크릴계 에멀젼은, 상기 본 발명에 따른 아크릴계 에멀젼의 프리 포르말린 제거방법에 의하여 프리 포르말린이 제거되어 제조되는 것을 특징으로 한다.
Meanwhile, the acrylic emulsion according to the present invention is characterized in that the formal emulsion is removed by removing the formalin in the acrylic emulsion according to the present invention.
한편, 본 발명의 EU를 이용한 프리 포르말린(Free Formalin)의 제거 방법은 본 발명과 같이 N-MAM을 가교성 모노머로 사용하는 아크릴계 에멀젼에서 발생되는 프리 포르말린(Free Formalin)의 제거에만 한정되는 것이 아니다. 즉, 프리 포르말린(Free Formalin)을 제거하는 방법으로 일반화할 수 있음은 당업자에게 자명하다고 할 것이다.
Meanwhile, the method of removing free formalin using the EU of the present invention is not limited to the removal of free formalin generated in an acrylic emulsion using N-MAM as a crosslinking monomer as in the present invention . That is, it will be apparent to those skilled in the art that the method can be generalized by removing free formalin.
이하, 본 발명의 실시예를 통하여 더욱 상세히 설명한다. 그러나 이들 실시예는 본 발명을 예시하기 위한 것이며, 본 발명이 이들 실시예에 의해 한정되는 것은 아니다.
Hereinafter, embodiments of the present invention will be described in more detail. However, these examples are for illustrating the present invention, and the present invention is not limited by these examples.
[실시예 1][Example 1]
상기한 바와 같은 공지의 아크릴계 에멀젼의 제조방법에 의하여 가교성 모노머로서 N-MAM을 사용하여 아크릴계 에멀젼을 합성하되, 합성반응 중에 EU를 첨가하여 프리 포르말린(Free Formalin)을 제거한 아크릴계 에멀젼을 제조하였다.An acrylic emulsion was prepared using N-MAM as a crosslinkable monomer by the above-mentioned known method for producing an acrylic emulsion, and an acrylic emulsion was prepared by adding EU during the synthesis reaction to remove free formalin.
N-MAM 원료 중 포르말린(Formalin)기의 함량은 약 28중량%이였으며, N-MAM의 사용량은 전체 합성 원료의 1.5중량%로 하였으며, EU의 첨가량은 N-MAM의 사용량의 66.7중량%로 하였으며, 공중합 합성온도는 60 ~ 70℃로 하였다.
The content of formalin in the N-MAM raw material was about 28% by weight, the amount of N-MAM used was 1.5% by weight of the total starting material, the amount of EU was 66.7% by weight of N-MAM, And the copolymerization temperature was 60 to 70 ° C.
[실시예 2][Example 2]
EU를 아크릴 에멀젼의 합성 종료 후에 첨가한 것 외에는 실시예 1과 동일하게 실시하였다.
The procedure of Example 1 was repeated except that the EU was added after completion of the synthesis of the acrylic emulsion.
[비교예 1][Comparative Example 1]
공지의 제조방법에 의하여 가교성 모노머로서 N-MAM을 사용하여 아크릴계 에멀젼을 합성하였다.
An acrylic emulsion was synthesized using N-MAM as a crosslinkable monomer by a known production method.
[시험예][Test Example]
상기한 실시예 1 내지 2 및 비교예 1에 의하여 제조된 각각의 아크릴계 에멀젼에 대하여 잔존하는 프리 포르말린(Free Formalin)의 함량을 분석하여 그 결과를 표 1에 나타내었다.The content of free formalin remaining in each of the acrylic emulsions prepared in Examples 1 to 2 and Comparative Example 1 was analyzed and the results are shown in Table 1.
(Free Formalin)Preformulin
(Free Formalin)
상기 시험예의 표 1에 의하면, 비교예 1의 경우 프리 포르말린(Free Formalin)의 함량이 약 300 ppm으로서 매우 높은 수치로 잔존하고 있는 반면에, 본 발명에 따른 실시예 1 내지 2의 경우 가교성 모노머로서 N-MAM을 사용한 아크릴계 에멀젼의 경우에 그동안 문제가 되어 왔던 프리 포르말린(Free Formalin)의 함량이 각각 0 ppm 및 0 ppm으로서 프리 포르말린(Free Formalin)이 각각 합성반응 중 및 합성종료 후 EU와의 반응에 의하여 제거되어 거의 잔존하지 않음을 확인할 수 있다.According to Table 1 of the above test example, in Comparative Example 1, the content of free formalin remained at a very high value of about 300 ppm, whereas in Examples 1 and 2 according to the present invention, the crosslinkable monomer In the case of acrylic emulsion using N-MAM, free formalin content was 0 ppm and 0 ppm, respectively, which had been a problem in the meantime, and free formalin was used in the reaction And it is confirmed that almost no residue is left.
이상에서 설명된 본 발명은 예시적인 것에 불과하며, 본 발명이 속한 기술분야의 통상의 지식을 가진 자라면 이로부터 다양한 변형 및 균등한 타 실시예가 가능하다는 점을 잘 알 수 있을 것이다. 그러므로 본 발명은 상기의 상세한 설명에서 언급되는 형태로만 한정되는 것은 아님을 잘 이해할 수 있을 것이다. 따라서 본 발명의 진정한 기술적 보호 범위는 첨부된 특허청구범위의 기술적 사상에 의해 정해져야 할 것이다. 또한, 본 발명은 첨부된 청구범위에 의해 정의되는 본 발명의 정신 그 범위 내에 있는 모든 변형물과 균등물 및 대체물을 포함하는 것으로 이해되어야 한다.While the present invention has been particularly shown and described with reference to exemplary embodiments thereof, it is to be understood that the invention is not limited to the disclosed exemplary embodiments, but, on the contrary, is intended to cover various modifications and equivalent arrangements included within the spirit and scope of the invention. Therefore, it is to be understood that the present invention is not limited to the above-described embodiments. Accordingly, the true scope of the present invention should be determined by the technical idea of the appended claims. It is also to be understood that the invention is to cover all modifications, equivalents, and alternatives falling within the spirit and scope of the invention as defined by the appended claims.
Claims (5)
아크릴계 에멀젼의 열처리 과정에서 가교 반응에 의하여 상기 N-MAM으로부터 발생하는 프리 포르말린(Free Formalin) 및 아마이드와 포르말린의 하이드록시메틸화 반응에 의하여 상기 N-MAM으로부터 발생하는 프리 포르말린(Free Formalin)을 에틸렌 우레아(Ethylene Urea, EU)와 반응시켜 제거하며,
상기 N-MAM과 EU의 반응은 아크릴계 에멀젼의 합성 후에 상온에서 합성 종료된 상기 아크릴 에멀젼에 EU를 상기 N-MAM의 1.2 ~ 1.5 배의 당량비로 혼합하여 이루어지는 것을 특징으로 하는 프리 포르말린의 제거방법.A process for producing an acrylic emulsion for an adhesive comprising N-Methylolacrylamide (N-MAM) as a crosslinkable monomer,
Free formalin generated from the N-MAM by hydroxymethylation reaction of amide and formalin generated by the crosslinking reaction in the heat treatment process of the acrylic emulsion is reacted with ethylene urea (Ethylene Urea, EU)
Wherein the reaction between the N-MAM and the EU is performed by mixing EU with the acrylic emulsion, which has been synthesized at room temperature after synthesis of the acrylic emulsion, at an equivalent ratio of 1.2 to 1.5 times the N-MAM.