KR101341051B1 - Thermoforming dome sheet integrated with a waveguide sheet of keypad and the manufacturing method - Google Patents

Thermoforming dome sheet integrated with a waveguide sheet of keypad and the manufacturing method Download PDF

Info

Publication number
KR101341051B1
KR101341051B1 KR1020110105603A KR20110105603A KR101341051B1 KR 101341051 B1 KR101341051 B1 KR 101341051B1 KR 1020110105603 A KR1020110105603 A KR 1020110105603A KR 20110105603 A KR20110105603 A KR 20110105603A KR 101341051 B1 KR101341051 B1 KR 101341051B1
Authority
KR
South Korea
Prior art keywords
sheet
dome
metal pattern
molded
forming
Prior art date
Application number
KR1020110105603A
Other languages
Korean (ko)
Other versions
KR20130040673A (en
Inventor
정동욱
Original Assignee
주식회사 미즈바테크놀로지
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 주식회사 미즈바테크놀로지 filed Critical 주식회사 미즈바테크놀로지
Priority to KR1020110105603A priority Critical patent/KR101341051B1/en
Publication of KR20130040673A publication Critical patent/KR20130040673A/en
Application granted granted Critical
Publication of KR101341051B1 publication Critical patent/KR101341051B1/en

Abstract

본 발명은 휴대폰 키패드용 도파시트 및 돔시트에 관한 것으로서, 더 상세하게는 인쇄회로기판에 설치된 광원의 빛을 전달하는 도파시트가 돔시트와 일체형으로 구성되어서 키패드 어셈블리를 박형화할 수 있도록 한 도파시트 일체형 돔시트에 관한 것으로; 베이스시트(200b)와 도파시트(300)를 도포 또는 접착의 방법으로 일체화하여 성형시트(500b)를 형성하는 성형시트 제조단계(S1); 그 베이스시트 상면에 금속잉크를 인쇄하여 금속패턴시트(500a)를 형성하는 금속패턴 인쇄단계(S2); 상기 금속패턴 인쇄면과 일치하는 금형안에서 가열, 가압으로 열성형하여 금속패턴을 돌출시켜 금속패턴돔(200a)을 형성하는 열성형단계(S3); 상기 돌출된 성형시트가 돔형태로 고정화되어 성형돔시트(500)을 형성하는 성형돔시트 완료단계(S4); 로 이루어지는 것을 특징으로 하는 키패드용 도파시트 일체형 성형돔시트 제조에 관한 것이다.
본 발명은 금속잉크를 간단한 패턴인쇄법과 열성형 가공법으로 금속패턴 돔(Metal Pattern Dome)을 구성하는 성형돔시트를 제조하므로서, 종래 메탈돔을 수작업으로 고정화하는 복잡한 공정을 획기적으로 개선하여 제품 불량율 및 제조단가를 절감하는 장점이 있다.The present invention relates to a wave guide sheet and a dome sheet for a mobile phone keypad, and more particularly, a wave guide sheet which transmits light of a light source installed on a printed circuit board is integrally formed with a dome sheet so that the keypad assembly can be thinned. To an integral dome sheet; Forming sheet manufacturing step (S1) of forming a molded sheet (500b) by integrating the base sheet (200b) and the wave guide sheet 300 by coating or bonding; A metal pattern printing step (S2) of forming a metal pattern sheet 500a by printing a metal ink on an upper surface of the base sheet; A thermoforming step (S3) of forming a metal pattern dome (200a) by protruding the metal pattern by thermoforming by heating and pressing in a mold corresponding to the metal pattern printing surface; Forming the dome sheet (S4), wherein the protruding forming sheet is fixed in a dome shape to form a forming dome sheet 500; The present invention relates to a waveguide sheet integrated molded dome sheet for a keypad.
The present invention manufactures a molded dome sheet constituting the metal pattern dome (Metal Pattern Dome) by a simple pattern printing method and a thermoforming process of the metal ink, thereby dramatically improving the complicated process of manually fixing the conventional metal dome product defect rate and There is an advantage in reducing the manufacturing cost.

Figure 112011080625816-pat00001
Figure 112011080625816-pat00001

Description

키패드용 도파시트 일체형 성형돔시트 및 그 제조방법{Thermoforming dome sheet integrated with a waveguide sheet of keypad and the manufacturing method}Waveguide sheet integrated molding dome sheet for keypad and method for manufacturing thereof {Thermoforming dome sheet integrated with a waveguide sheet of keypad and the manufacturing method}

본 발명은 금속잉크를 직접 돔시트용 기재에 스크린 패턴인쇄하고 이를 돔형태로 열성형하므로서, 키패드의 클릭감을 제공하고, 도파시트를 돔시트 상부에 일체형으로 구비하므로서 별도의 도파시트 부착이 필요없는 제조원가 절감효과가 매우 높은 키패드용 돔시트와 그 제조방법에 관한 것이다.The present invention prints a screen pattern directly onto a substrate for a dome sheet and thermoforms it in a dome shape, thereby providing a click feeling of the keypad and providing a waveguide sheet integrally on the dome sheet so that no separate waveguide sheet is required. The present invention relates to a dome sheet for a keypad and a method of manufacturing the same having a very high manufacturing cost reduction effect.

본 발명은 키패드용 도파시트 및 돔시트에 관한 것으로서, 더 상세하게는 PCB기판에 설치된 광원의 빛을 전달하는 도파시트가 돔시트와 일체형으로 구성되어져 키패드 어셈블리를 박형화할 수 있도록 한 도파시트 일체형 돔시트에 관한 것이다. 그리고 상기 돔시트는 금속잉크를 직접 스크린 패턴인쇄하고 열성형하여 돔구조를 형성하기 때문에 종래의 메탈돔이 필요하지 않고 더불어 그 부착에 필요한 공정시간과 제조원가를 크게 절감할 수 있는, 지금까지 보고되지 않은 최초의 도파시트 일체형 성형 돔시트 제작에 관한 것이다. The present invention relates to a wave guide sheet and a dome sheet for a keypad, and more specifically, a wave guide sheet integrated dome configured to thin the keypad assembly by being integrated with the dome sheet to transmit the light of the light source installed on the PCB substrate. It is about a sheet. In addition, since the dome sheet forms a dome structure by directly screen-printing and thermally forming a metal ink, a conventional metal dome is not required, and thus the process time and manufacturing cost required for the attachment can be greatly reduced. The first waveguide sheet integrated molded dome sheet.

종래 키패드는 도 1에 도시한 바와 같이 PCB기판(10)위에 메탈돔(20a)이 백색의 절연시트(20b)에 부착되어 메탈돔시트(20)을 구성하고, 그 상부에 키패드 버튼(40a)으로 빛을 확산해주는 도파시트(30)와, 그 상부에 키패드 패널(40)이 위치한다. In the conventional keypad, as shown in FIG. 1, a metal dome 20a is attached to a white insulating sheet 20b on a PCB substrate 10 to form a metal dome sheet 20, and a keypad button 40a on the top thereof. Waveguide sheet 30 for diffusing light to the, and the keypad panel 40 is located on the top.

메탈돔은 키패드 패널의 글자나 기호의 갯수 만큼 다수의 메탈돔을 수작업으로 돔시트의 구멍(Dome Hole)속으로 삽입되어 그 상부의 투명시트(20c) 접착층에 부착되어 메탈돔시트(20)를 형성하게 된다. 메탈돔(20a)은 스테인레스 재질로 구성되므로 클릭감을 부여하는 고유 반발력이 탁월하여 널리 사용되고 있다. 또한, PCB기판에서 나오는 광원의 빛을 키패드 버튼(40a)쪽으로 전달하기 위해서는 도파시트 (30)가 추가적으로 투명시트(20c) 상면에 구비되어 진다. The metal dome is inserted into the hole of the dome sheet by hand as many metal domes as the number of letters or symbols on the keypad panel is attached to the adhesive layer on the transparent sheet 20c of the upper part to attach the metal dome sheet 20. To form. Since the metal dome 20a is made of stainless steel, it has been widely used because of its excellent repulsive force to give a feeling of clicking. In addition, the wave guide sheet 30 is additionally provided on the upper surface of the transparent sheet 20c in order to transmit the light of the light source from the PCB to the keypad button 40a.

한국특허 등록 제10-0851658호에는 상기에 언급된 투명시트(20c)를 생략하고키패드를 간단하게 박형화할 수 있는 방법으로 도파시트(30)에 접착의 방법으로 메탈돔이 부착된 도파시트를 구비한 메탈돔시트를 게시하였다. 그러나, 상기 발명에는 여전히 메탈돔을 부착하는 번거로운 공정이 수반된다. Korean Patent Registration No. 10-0851658 is provided with a waveguide with a metal dome attached to the waveguide 30 by a method of simply thinning the keypad and omitting the transparent sheet 20c mentioned above. Posted a metal dome sheet. However, the invention still involves a cumbersome process of attaching a metal dome.

이러한 다수의 메탈돔을 수작업으로 투명시트(20c) 접착면에 부착하는 공정은 도파시트를 설치하는 후공정과 더불어 전체적으로 키패드 어셈블리를 생산하는 조립과정에서 수율을 낮추고, 제조원가가 상승하는 문제점이 있다.
The process of attaching the plurality of metal domes to the transparent sheet 20c adhesive surface by hand has a problem of lowering the yield and increasing the manufacturing cost in the assembly process of producing the keypad assembly as well as the post-installation process of the waveguide sheet.

따라서, 본 발명은 이러한 문제점을 해결하기 위하여 창출된 것으로서, 도파시트와 돔시트를 합지공정으로 일체화하고 그 한면에 패턴인쇄법(Pattern Printing)으로 금속잉크를 도포하여 전도성을 부여하고, 그 금속패턴 부위를 돔형태로 열성형하므로서, 키패드 클릭감을 부여할 수 있는 도광시트를 일체형으로 구비한 성형돔시트를 제공함이 주목적이다. 이러한 본 발명의 도파시트 일체형 성형돔시트는 키패트 조립공정이 매우 간소화되어 제조원가 및 제품 불량율을 크게 줄일수 있는 잇점이 있다. Therefore, the present invention was created to solve this problem, the waveguide sheet and the dome sheet is integrated into a lamination process, and one side is coated with a metal ink by pattern printing to impart conductivity, and the metal pattern It is a main object to provide a molded dome sheet integrally provided with a light guide sheet capable of imparting a keypad click feeling by thermoforming a portion in a dome shape. The dopa sheet-integrated molded dome sheet of the present invention has the advantage that the keypad assembly process is greatly simplified, greatly reducing the manufacturing cost and product defect rate.

상기한 목적을 달성하고자 본 발명의 구성은, 베이스시트(200b)와 도파시트(300)를 도포 또는 접착의 방법으로 일체화하여 성형시트(500b)를 형성하는 성형시트 제조단계(S1); 그 베이스시트 상면에 금속잉크를 인쇄하여 금속패턴시트(500a)를 형성하는 금속패턴 인쇄단계(S2); 상기 금속패턴 인쇄면과 일치하는 금형안에서 가열, 가압으로 열성형하여 금속패턴을 돌출시켜 금속패턴돔(200a)을 형성하는 열성형단계(S3); 상기 돌출된 성형시트(500b)가 돔형태로 고정화되어 성형돔시트(500)을 형성하는 성형돔시트 완료단계(S4); 로 구비되어 도파시트와 돔시트가 일체화되어 이루어지는 것을 특징으로 한다.To achieve the above object, the configuration of the present invention comprises a molding sheet manufacturing step (S1) of forming a molding sheet (500b) by integrating the base sheet (200b) and the waveguide sheet 300 by coating or bonding; A metal pattern printing step (S2) of forming a metal pattern sheet 500a by printing a metal ink on an upper surface of the base sheet; A thermoforming step (S3) of forming a metal pattern dome (200a) by protruding the metal pattern by thermoforming by heating and pressing in a mold corresponding to the metal pattern printing surface; A molding dome sheet completing step S4 of forming the molded dome sheet 500 by fixing the protruding molding sheet 500b in a dome shape; It is provided as characterized in that the wave guide sheet and the dome sheet is made integral.

본 발명은 금속잉크를 간단한 패턴인쇄법과 열성형 가공법으로 금속패턴 돔(Metal Pattern Dome)을 구성하는 성형돔시트를 제조하므로서, 종래 메탈돔을 수작업으로 고정화하는 복잡한 공정을 획기적으로 개선하여 제품 불량율 및 제조단가를 절감하는 효과를 갖는다.The present invention manufactures a molded dome sheet constituting the metal pattern dome (Metal Pattern Dome) by a simple pattern printing method and a thermoforming process of the metal ink, thereby dramatically improving the complicated process of manually fixing the conventional metal dome product defect rate and It has the effect of reducing the manufacturing cost.

또한, 상기 성형시트 제조단계에서 도파시트를 접착방법으로 돔시트위에 일체화하여 구비되어지므로서, 종래 도파시트를 돔시트 상면에 부가적으로 설치하는 과정이 생략되어, 키패드의 조립공정이 크게 간소화되고 생산성이 증대되는 효과를 갖는다.In addition, since the waveguide sheet is integrally provided on the dome sheet by the bonding method in the forming sheet manufacturing step, the process of additionally installing the waveguide sheet on the upper surface of the dome sheet is omitted, thereby greatly simplifying the assembly process of the keypad. The productivity is increased.

도 1은 종래 기술에 의한 메탈돔시트와 도파시트를 나타내는 도면.
도 2는 본 발명에 의한 키패드용 도파시트 일체형 성형돔시트를 나타내는 도면.
도 3은 본 발명에 의한 성형시트를 나타내는 도면.
도 4는 본 발명에 의한 금속패턴시트를 나타내는 도면.
도 5는 본 발명에 의한 도파시트 일체형 성형돔시트를 나타내는 도면.
도 6은 본 발명에 의한 키패드용 도파시트 일체형 성형돔시트를 제조하는 순서도.1 is a view showing a metal dome sheet and a wave guide sheet according to the prior art.
Figure 2 is a view showing a waveguide sheet integral molded dome sheet for a keypad according to the present invention.
3 is a view showing a molded sheet according to the present invention.
4 is a view showing a metal pattern sheet according to the present invention.
5 is a view showing a waveguide integrated sheet formed dome sheet according to the present invention.
Figure 6 is a flow chart for manufacturing a waveguide sheet integrated molded dome sheet for a keypad according to the present invention.

본 발명에 의한 키패드용 도파시트 일체형 성형돔시트 및 그 제조방법을 도 2부터 도 6을 기초로 상세하게 설명한다.Keypad waveguide integrated molded dome sheet and a method for manufacturing the same according to the present invention will be described in detail with reference to Figs.

도 2에는 본 발명의 실시예에 따른 키패드용 도파시트 일체형 성형돔시트의 구조를 나타내는 단면도이고, 도 3 ~ 5는 본 발명의 그 실시예에 따른 각 단계별로성형시트와 금속패턴시트와, 그리고 그 금속패턴으로 성형된 성형돔시트를 나타낸다. 도 6은 키패드용 도파시트 일체형 성형돔시트를 제조하는 전체 공정을 나타내는 순서도이다.2 is a cross-sectional view showing the structure of a waveguide sheet integrated molded dome sheet for a keypad according to an embodiment of the present invention, and FIGS. 3 to 5 are each forming sheet and a metal pattern sheet according to the embodiment of the present invention, and The molded dome sheet molded by the metal pattern is shown. 6 is a flow chart showing the overall process of manufacturing the waveguide sheet integrally formed dome sheet for keypad.

도 2에 도시한 바와 같이, 본 발명의 키패드용 도파시트 일체형 성형 돔시트(500)는 금속패턴돔(200a)과 베이스시트(200b)와 도파시트(300)로 이루어진다.As shown in FIG. 2, the waveguide sheet integrated molded dome sheet 500 for a keypad of the present invention includes a metal pattern dome 200a, a base sheet 200b, and a waveguide sheet 300.

하기에 도 2 ~ 도 5의 도면을 기초로 키패드용 도파시트 일체형 성형돔시트에 관한 그 제조공정을 상세히 설명한다.Hereinafter, the manufacturing process of the waveguide sheet integrated molded dome sheet for a keypad will be described in detail based on the drawings of FIGS. 2 to 5.

도 3에서 도시한 바와 같이, 상기 베이스시트(200b)는 1차적으로 열성형이 용이한 백색의 합성필름을 단독 또는 합지(Lamination)하여 구성되어지며, 이 베이스시트(200b)는 성형시트 제조단계(S1)에서 도파시트(300)로 사용되는 합성필름(주로 폴리카보네이트)과 접착방법으로 일체화되어 금속잉크 패턴인쇄 및 열성형이 가능한 도파시트 일체형 성형시트(500b)로 구성되어진다. As shown in FIG. 3, the base sheet 200b is primarily composed of a single or laminated white composite film that is easily thermoformed, and the base sheet 200b is formed of a molded sheet. In (S1), the composite film (mainly polycarbonate) used as the waveguide 300 is composed of a waveguide sheet integrated molding sheet 500b which is integrated by an adhesive method and enables metal ink pattern printing and thermoforming.

또한, 상기 베이스시트(200b)가 일체화된 도파시트를 통하여 광원의 빛이 확산될 때에 효과적으로 그 빛을 난반사하여 키버튼으로 전달하는 기능을 제공함은 당연하다. In addition, when the light of the light source is diffused through the waveguide integrated with the base sheet 200b, it is natural to provide a function of diffusely reflecting the light to the key button.

베이스시트(200b)의 원단으로는 100oC 이상 온도로 가열된 금형안에서 가압으로 열성형이 용이한 백색의 열성형(Thermoforming) 필름이 적합하다. 그 예로는 이축연신 가공된 백색 폴리에스테르필름 또는 그 이축연신 백색 폴리에스테르필름을 아몰포스 폴리에스테르필름 또는 폴리올레핀 성형필름과의 합지로 이루어진 적층필름이 있다. 그외에 가압하에 열성형이 가능한 어떠한 백색의 베이스시트용 필름류도 본 발명의 목적에 맞게 사용되어진다.As a fabric of the base sheet 200b, a white thermoforming film which is easily thermoformed by pressurization in a mold heated to a temperature of 100 ° C. or higher is suitable. For example, a biaxially stretched white polyester film or a biaxially stretched white polyester film is laminated with an amorphous polyester film or a polyolefin molded film. In addition, any white basesheet films capable of thermoforming under pressure may be used for the purpose of the present invention.

도 4에서는 도 6에 의한 패턴인쇄단계(S2)로서, 상기 도 3에서 구비되어진 성형시트(500b)를 패턴인쇄법으로 인쇄회로기판의 전도성 고정접점에 통전할 수 있는 금속잉크를 도포하고 건조하여, 도파시트 일체형 금속패턴시트(500a)을 구성하게 된다. 통상의 패턴인쇄법으로는 스크린인쇄법, 롤투롤(Roll to Roll)법, 스탬프법, 그라비아 옵셋(Gravure Offset) 등이 있으며, 이중에서 선택되어지는 한 방법으로 패턴인쇄가 이루어진다.In FIG. 4, as the pattern printing step (S2) of FIG. 6, a metal sheet capable of applying electricity to a conductive fixed contact of a printed circuit board by applying the molding sheet 500b provided in FIG. The waveguide integrated metal pattern sheet 500a is configured. Conventional pattern printing methods include screen printing, roll to roll, stamping, gravure offset, and the like. Pattern printing is performed by one method selected from among them.

금속잉크는 나노입자로 고루 분산된 은페이스트를 특정 인쇄방법에 맞도록 레올로지를 조절하여 두께는 약 1 ~ 20 micrometer 범위이내로 도포되어 진다. 또한 다음 단계에서 준비되어지는 열성형 가공시에 금속도막의 박리나 깨짐이 전혀 없도록 내구성이 강한 금속잉크 조성물로 물성 조절이 필수적이다. The metal ink is applied to the thickness of about 1 to 20 micrometers by adjusting the rheology of silver paste evenly dispersed with nanoparticles according to specific printing method. In addition, during the thermoforming process to be prepared in the next step, it is essential to control physical properties with a durable metal ink composition so that there is no peeling or cracking of the metal coating film.

도 5는 도 6에 의한 열성형단계(S3)로서, 도 4에서 제공되어진 금속패턴시트(500a)가 클릭감을 갖을수 있도록 금속패턴면을 열성형하여 돔형태로 돌출시키므로서 최종적으로 도파시트 일체형 성형돔시트(500)가 형성되어진다. 이때, 돔형태로 이루어지는 금속패턴층(200c)면이 열성형 과정에서 박리(delamination)되는 등의 문제점을 방지하기 위하여, 금속패턴(200c)을 인쇄하기 전에, 금속잉크와 강한 접착력을 갖는 코팅제를 사용하여, 베이스시트(200b)면에 전처리제 코팅(primer coating)하는 것이 바람직하다. 본 발명에 의한 성형돔은 스테인레스로 구성된 종래 메탈돔과 달리 필름재질에 금속입자가 도포되어진 재질로서 원활한 클릭감을 부여하기 위해서는 0.5 ~ 2mm 범위의 두께가 적당하다.5 is a thermoforming step (S3) of FIG. 6, in which the metal pattern sheet 500a provided in FIG. 4 is thermally molded to protrude in a dome shape so as to have a click feeling, and finally, the waveguide sheet is integrally formed. Forming dome sheet 500 is formed. At this time, in order to prevent a problem such that the surface of the metal pattern layer 200c having a dome shape is delaminated during the thermoforming process, before printing the metal pattern 200c, a coating agent having strong adhesion with the metal ink is applied. It is preferable to use a primer coating on the surface of the base sheet 200b. Unlike the conventional metal dome made of stainless steel, the molded dome according to the present invention has a thickness in the range of 0.5 to 2 mm in order to provide a smooth click feeling as a material to which metal particles are applied to the film material.

상기 도 5의 도파시트 일체형 성형돔시트(500)의 베이스시트(200b) 하부면에 접착제를 도포하고 이형지를 부착하여 보관하고, 키패드 어셈블리를 조립할 때는 그 이형지를 제거하여, 인쇄회로기판(100) 위에 본 발명의 성형돔시트(500) 을 부착하고 그 위에 키패드 패널을 올려놓고 조립하면 완성된다. The adhesive is applied to the bottom surface of the base sheet 200b of the waveguide integrated molded dome sheet 500 of FIG. 5, and the release paper is attached and stored. When the keypad assembly is assembled, the release paper is removed to remove the printed circuit board 100. Attached to the molded dome sheet 500 of the present invention on top of the keypad panel on the assembly is completed.

본 발명은 도면에 도시된 한 실시예를 참고로 설명하였으나 이는 예시적인 것에 불과하며, 당해 분야에서 통상의 기술자라면 본 발명의 기술적 사상내에서 다른 변형된 실시가 있을수 있음은 명백한 사실이다.
Although the present invention has been described with reference to one embodiment shown in the drawings, this is merely exemplary, and it is obvious that a person skilled in the art may have other modified embodiments within the spirit of the present invention.

100: 인쇄회로기판 100a: 전도성 고정접점
200a: 금속패턴돔 200b: 베이스시트
200c: 금속패턴 300: 도파시트
400: 키패드 패널 400a: 키버튼
500a: 도파시트 일체형 금속패턴시트 500b: 도파시트 일체형 성형시트
500: 도파시트 일체형 성형돔시트100: printed circuit board 100a: conductive fixed contact
200a: metal pattern dome 200b: base sheet
200c: metal pattern 300: waveguide
400: keypad panel 400a: key button
500a: integrated waveguide sheet metal pattern sheet 500b: integrated waveguide sheet integral sheet
500: waveguide integrated molded dome sheet

Claims (8)

베이스시트(200b)와 도파시트(300)를 도포 또는 접착의 방법으로 일체화하여 성형시트(500b)를 형성하는 성형시트 제조단계(S1); 그 베이스시트 상면에 금속잉크를 인쇄하여 금속패턴시트(500a)를 형성하는 금속패턴 인쇄단계(S2); 상기 금속패턴 인쇄면과 일치하는 금형안에서 가열, 가압으로 열성형하여 금속패턴을 돌출시켜 금속패턴돔(200a)을 형성하는 열성형단계(S3); 상기 돌출된 성형시트가 돔형태로 고정화되어 성형돔시트(500)을 형성하는 성형돔시트 완료단계(S4); 로 이루어지는 것을 특징으로 하는 키패드용 도파시트 일체형 성형돔시트의 제조방법.Forming sheet manufacturing step (S1) of forming a molded sheet (500b) by integrating the base sheet (200b) and the wave guide sheet 300 by coating or bonding; A metal pattern printing step (S2) of forming a metal pattern sheet 500a by printing a metal ink on an upper surface of the base sheet; A thermoforming step (S3) of forming a metal pattern dome (200a) by protruding the metal pattern by thermoforming by heating and pressing in a mold corresponding to the metal pattern printing surface; Forming the dome sheet (S4) to form the molded dome sheet 500 by fixing the protruding molding sheet into a dome shape; Method for producing a waveguide sheet integrated molded dome sheet for a keypad comprising a. 제 1항에 있어서, 베이스시트(200b)는 아몰포스 폴리에스테르필름과 백색 이축연신 폴리에스테르필름으로 합지된 적층필름으로 구성되어지는 것을 특징으로 하는 키패드용 도파시트 일체형 성형돔시트의 제조방법.The method according to claim 1, wherein the base sheet (200b) is composed of a laminated film laminated with an amorphous polyester film and a white biaxially stretched polyester film. 제 1항에 있어서, 베이스시트(200b)는 폴리올레핀 성형필름과 백색 이축연신 폴리에스테르필름으로 합지된 적층필름으로 구성되어지는 것을 특징으로 하는 키패드용 도파시트 일체형 성형돔시트의 제조방법.       The method of claim 1, wherein the base sheet (200b) is composed of a laminated film laminated with a polyolefin molded film and a white biaxially stretched polyester film. 제 1항에 있어서, 성형시트(500b)는 폴리카보네이트필름과 상기 베이스시트(200b)로 합지된 적층필름으로 구성되어지는 것을 특징으로 하는 키패드용 도파시트 일체형 성형돔시트의 제조방법. The method of claim 1, wherein the molded sheet (500b) is composed of a polycarbonate film and a laminated film laminated with the base sheet (200b). 청구항 4에 있어서, 성형시트(500b)의 베이스시트(200b)면에 패턴인쇄법으로 금속잉크를 도포하여 금속패턴층을 형성하는 것을 특징으로 하는 키패드용 도파시트 일체형 성형돔시트의 제조방법.The method according to claim 4, wherein the metal sheet is formed by applying a metal ink on the surface of the base sheet (200b) of the molded sheet (500b) by a pattern printing method. 청구항 5에 있어서, 금속패턴인쇄된 성형시트(500b)가 금형(Mold)안에서 가열, 가압으로 금속패턴층이 돔형태 구조로 열성형되는 것을 특징으로 하는 키패드용 도파시트 일체형 성형돔시트의 제조방법.The method according to claim 5, wherein the metal pattern printed molded sheet 500b is heated and pressed in a mold to heat-form the metal pattern layer into a dome-shaped structure. . 청구항 5에 있어서, 성형시트(500b)의 베이스시트(200b)면에 금속패턴인쇄는 스크린인쇄, 롤투롤법, 스탬프법, 그라비아 옵셋 등에서 선택되어지는 인쇄법으로 형성되어지는 것을 특징으로 하는 키패드용 도파시트 일체형 성형돔시트의 제조방법.The method according to claim 5, wherein the metal pattern printing on the surface of the base sheet 200b of the molded sheet 500b is formed by a printing method selected from screen printing, roll-to-roll method, stamp method, gravure offset, etc. Method for manufacturing sheet integrated molded dome sheet. 청구항 5에 있어서, 성형시트(500b)의 베이스시트(200b)면에 금속잉크 접착성을 강화하기 위해 전처리 코팅하는 것을 특징으로 하는 키패드용 도파시트 일체형 성형돔시트의 제조방법.


The method according to claim 5, wherein the method for manufacturing a waveguide sheet integrated molded dome sheet for a keypad, characterized in that the pre-treatment coating to strengthen the metal ink adhesion to the base sheet (200b) surface of the molded sheet (500b).


KR1020110105603A 2011-10-15 2011-10-15 Thermoforming dome sheet integrated with a waveguide sheet of keypad and the manufacturing method KR101341051B1 (en)