KR101302699B1 - The method of manufacturing stone guideboard - Google Patents

The method of manufacturing stone guideboard Download PDF

Info

Publication number
KR101302699B1
KR101302699B1 KR1020130035196A KR20130035196A KR101302699B1 KR 101302699 B1 KR101302699 B1 KR 101302699B1 KR 1020130035196 A KR1020130035196 A KR 1020130035196A KR 20130035196 A KR20130035196 A KR 20130035196A KR 101302699 B1 KR101302699 B1 KR 101302699B1
Authority
KR
South Korea
Prior art keywords
stone
silk
screen printing
plate
printing
Prior art date
Application number
KR1020130035196A
Other languages
Korean (ko)
Inventor
윤태근
Original Assignee
윤태근
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 윤태근 filed Critical 윤태근
Priority to KR1020130035196A priority Critical patent/KR101302699B1/en
Application granted granted Critical
Publication of KR101302699B1 publication Critical patent/KR101302699B1/en

Abstract

PURPOSE: A stone guideboard is provided to be used semi-permanently as a printing on the stone is not discolored or damaged. CONSTITUTION: A manufacturing method of a stone guideboard (100) comprises the following steps. 97wt% of sericol 22 liquid 97, as an emulsion for silkscreen printing, and 3wt% of a sensitizer are mixed and aged for 5 hours. After fixing silk net having 420 mesh on an aluminum graving plate for silk printing, the aged emulsion is coated thereon for once, and then, a drawing-printed film including road guiding phrases and road markings is attached to the silk net. The silk net is placed 1.5 m in front of an arc lamp for transmitting light of 5 kw for 110 seconds, and then water is sprayed thereon to complete a graving plate for silk screen printing. 50wt% of a coloring powder and 50wt% of colorless screen printing oil are mixed to prepare ink for silk screen printing. The graving plate for silk screen printing is placed on a stone board and printing is performed by using the ink for silk screen printing, and the printing on the stone board is air dried at a temperature of 40°C for 30 minutes. The air dried stone board is put into a pottery kiln and primarily plasticized at a temperature of 700°C for 24 hours. Then, the primarily plasticized stone board is put into a pottery kiln again and heated at a temperature of 800°C for 24 hours to manufacture the stone guideboard.

Description

석재 안내판의 제조방법{THE METHOD OF MANUFACTURING STONE GUIDEBOARD}Manufacturing method of stone guide plate {THE METHOD OF MANUFACTURING STONE GUIDEBOARD}

본 발명은 보행자가 걷게 되는 보행자 도로의 바닥에 QR코드나 각종 안내정보가 표시된 석재 안내판을 설치함으로써 보행자가 바닥에 설치된 석재 안내판을 보고 주변 정보를 쉽게 인지할 수 있도록 하되 상기 석재 안내판의 표면에 인쇄되는 각종 정보가 반영구적으로 보존될 수 있도록 하는 석재 안내판의 제조방법에 관한 것이다.The present invention by installing a stone guide plate on the floor of the pedestrian walk pedestrian walk QR code or various guide information is displayed so that the pedestrian can easily recognize the surrounding information by looking at the stone guide plate installed on the floor, but printed on the surface of the stone guide plate It relates to a method of manufacturing a stone guide plate so that the various information is semi-permanently preserved.

국립공원이나 관광유적지 등의 출입구에는 공원과 유적지 등을 안내하는 안내판이 입식으로 설치되어 있기는 하나 이는 안내판이 목재로 된 합판이나 스테인레스 금속판으로 제작되어 있어 눈, 비에 쉽게 부식이 되고 탈, 변색이 되므로 해서 설치 후 1~2년 만에 안내판을 교체해 주어야 하는 비경제적인 문제점이 있었고, 부식이 쉽게 되고 탈 변색이 되어 훼손된 안내판으로 인하여 관광지를 찾는 관광객들은 안내판의 안내도를 보고 가고자하는 지점을 쉽게 찾아갈 수가 없는 문제점이 있었다.At the entrances of national parks and tourist sites, guide boards that guide parks and historic sites are installed by standing, but the guide boards are made of plywood or stainless metal plates, which are easily corroded to snow and rain. As a result, there was an uneconomical problem that the information board had to be replaced within one or two years after installation, and tourists looking for tourist attractions due to the information signs easily damaged due to deterioration and discoloration could easily find the point where they wanted to go. There was a problem that can not go.

즉, 보행자에게 각종 지리 정보나 안내 정보를 주기 위해서는 입간판 형태로 안내판을 설치하거나 안내도를 그려서 벽면에 설치하는 등의 방법을 사용하는 관계로 보행자의 시야가 입식 안내판에 의하여 가려지게 되는 문제와 함께 설치비용이 많이 드는 문제가 있다.In other words, in order to give pedestrians various geographic information or guide information, the guideline is installed in the form of a signboard or draws a guide map and installs it on the wall. There is a costly problem.

이 같이 구조물을 이용한 안내를 하지 않고 보행자 도로에 안내판을 설치하여 안내 정보나 지리 정보를 제공하는 방법이 있으나, 이는 대부분 투명 플라스틱이나 강화 유리를 이용하여 문자나 그림 및 도형 등이 훼손되지 않도록 하고 있음에도 불구하고, 장시간에 걸쳐 많은 사람이 밟게 되면 표시정보가 훼손되어 보행자가 원하는 정보를 인식할 수 없는 경우가 발생하게 되고, 이러한 방식의 안내판은 입식 안내판 보다 많은 설치비용을 초래하는 한편 유지보수가 쉽지 않다.As such, there is a method of providing guide information or geographic information by installing a guide plate on a pedestrian road without guiding the structure, but most of them use transparent plastic or tempered glass to prevent letters, pictures, and figures from being damaged. Nevertheless, if many people step on it for a long time, the display information is damaged and pedestrians cannot recognize the desired information, and this type of signage incurs more installation costs than the standing signage and is easier to maintain. not.

그리고, 저렴하게 설치할 수 있는 것이 점자 블록과 같이 이동 방향이나 특정의 장소로 인도할 수 있는 정도의 유도블록을 사용할 수 있으나, 이러한 방식은 보행자의 이동 경로를 유도할 뿐이고 주변의 관광 정보나 위치 정보 등의 다양한 정보를 줄 수 없는 문제가 있다.In addition, inexpensive installation may use a guide block such as a braille block that can lead to a moving direction or a specific place, but this method only induces a pedestrian's moving path, and the surrounding tourist information or location information. There is a problem that can not give a variety of information.

대한민국 특허 등록 10-1043695호(2011.06.16 등록)Republic of Korea Patent Registration No. 10-1043695 (Registered June 16, 2011) 대한민국 특허 공개 10-2005-0045056호(2005.05.17 공개)Republic of Korea Patent Publication 10-2005-0045056 (published May 17, 2005) 대한민국 실용신안 등록 20-0168860호(1999.11.15 등록)Korea Utility Model Registration 20-0168860 (Registered Nov. 15, 1999) 대한민국 실용신안 등록 20-0340178호(2004.01.16 등록)Registered Korean Utility Model No. 20-0340178 (Registered Jan. 16, 2004) 대한민국 특허 등록 10-0928740호(2009.11.19 등록)Republic of Korea Patent Registration No. 10-0928740 (Registered Nov. 19, 2009)

본 발명은 공원 안내판, 문화재 안내판, 사찰 안내판, 관광유적지 안내판 등의 각종 안내판에 안내 정보와 위치정보 등의 각종 정보를 표시하기 위하여 입식 안내판을 설치할 때 발생되는 주변 시야를 가리고 경관을 해치는 문제와 함께 안내판의 수명이 짧아 자주 교체해 주어야 하는 문제를 해결하기 위한 것으로, 내부식성과 내모성 및 자연 친화적인 특성을 갖는 석재 안내판을 보행자 도로에 설치하되 석재판의 표면에 각종 안내 정보와 지리 정보 등의 다양한 정보를 인쇄하여 표시할 수 있도록 함으로써 시야를 가리고 경관을 해치는 문제를 해결하는 한편 상기 석재판의 표면에 유리질 유약을 피복시켜 석재판에 실크 스크린 인쇄된 안내정보의 손상이 발생하지 않도록 함으로써 자주 교체하고 수리하여야 하는 문제를 해결하는 것이다.The present invention obstructs the surrounding view generated by installing a standing guide plate to display various information such as guide information and location information on various guide boards such as a park guide plate, a cultural property guide plate, a temple guide plate, a tourist site guide plate, etc. To solve the problem of frequent replacement of the guide plate due to the short life of the guide plate, install a stone guide plate on the pedestrian road with corrosion resistance, abrasion resistance, and nature-friendly characteristics, and provide various guide information and geographic information on the surface of the stone plate. It solves the problem of obstructing the view and harming the landscape by printing and displaying the information, and by frequently replacing the glaze glaze on the surface of the stone plate so as not to damage the silk screen printed guide information on the stone plate. It is to solve the problem that needs to be repaired.

본 발명의 석재 안내판은 안내 문구와 도로 표시 등의 각종 정보를 석재판에 실크스크린 인쇄를 한 후 도자기 가마에서 700oC로 한번 구운 다음 800oC의 고열로 소성을 하여 제작함으로써 이루어지는 것으로, 석재 안내판의 훼손이 발생하지 않아 장시간 안정적으로 사용할 수 있고, 또한 보행자 도로에 설치하되 미끄럼이 방지되게 함으로써 시야를 가리지 않고 설치할 수 있으며, 유리질을 피복시켜 밟고 다녀도 인쇄된 각종 정보가 훼손되는 경우를 없애게 된다.The stone guide plate of the present invention is made by silkscreen printing various kinds of information such as guide text and road markings and then baking them at 700 o C in a ceramic kiln and then baking them at a high temperature of 800 o C. It can be used stably for a long time without any damage to the information board, and it can be installed on the pedestrian road to prevent slippage, and can be installed without covering the field of view, and eliminates the case where various printed information is damaged even if it is covered with glass. do.

본 발명은 각종공원이나 사찰, 관광유적지의 안내판을 목재로 된 합판이나 스테인레스 금속판이 아닌 석재판에 위치 정보 및 안내 정보 등의 각종 정보를 칼라스크린 인쇄를 하여 안내판을 제조하는 것으로, 석재에 유리질 유약을 피복시켜 석재의 강인성과 유리의 내식성 및 청결성을 겸비하는 것이다.The present invention is to produce a guide plate by color screen printing a variety of information, such as location information and guide information on the stone plate rather than wood plywood or stainless metal plate of the guide plate of various parks, temples, tourist sites, glass glaze on the stone It is to combine the toughness of stone and corrosion resistance and cleanliness of glass.

이러한 본 발명은 박테리아의 성장을 억제하고 청소가 용이한 비침투성 표면으로써 매우 위생적이고, 장기간 사용을 해도 표면이 닳거나 칼, 못 등에도 긁히지 않으며, 화학제품에 의해 손상되지 않고, 표면이 녹슬지 않으며, 불에 타지 않고, 유리질을 고온에서 용해하여 석재 표면에 융착한 것이므로 색상이 변하지 않으며, 완전 무기질의 비독성으로서 자연친화적인 효과가 있다.The present invention is a non-invasive surface that inhibits the growth of bacteria and is easy to clean, is very hygienic, does not scratch or scratch the surface even after prolonged use, is not damaged by chemicals, and the surface is not rusted. Because it is melted on the stone surface by melting glass at high temperature without burning, it does not change color and has a natural friendly effect as a completely nontoxic of minerals.

이와 같이 본 발명은 지리정보나 위치정보 등의 각종 안내 정보가 인쇄된 석재 안내판을 구비하되 상기 인쇄물의 탈 변색과 훼손이 되지 않아 반영구적으로 사용할 수 있는 것으로, 입식으로 석재 안내판을 설치하거나 보행자 도로에 보도 블록과 같이 설치하여 사용이 가능한 것이다.As described above, the present invention has a stone guide plate on which various guide information such as geographic information and location information is printed, but can be used semi-permanently because it does not become discolored and damaged in the printed matter. It can be installed and used like a sidewalk block.

도 1은 본 발명에 의해 제조된 안내판의 실시예 사시도
도 2는 본 발명에 의해 제조된 안내판의 다른 실시예 정면도
도 3은 본 발명에 의해 제조된 안내판에 QR코드를 표시한 상태의 사시도
도 4는 본 발명에 의해 제조된 안내판의 배면도1 is a perspective view of an embodiment of a guide plate produced by the present invention
2 is a front view of another embodiment of a guide plate produced by the present invention;
Figure 3 is a perspective view of a state displaying a QR code on the guide plate produced by the present invention
Figure 4 is a rear view of the guide plate produced by the present invention

본 발명은 보행자 도로에 QR코드나 각종 안내정보를 석재판에 인쇄한 안내판을 설치하여 보행자가 안내판을 보고 주변 정보를 손쉽게 획득할 수 있도록 하는 것으로, 도로가에 각종 안내판을 설치하여 주변경관을 가리지 않게 된다.The present invention is to install a guide plate printed with a QR code or various guide information on the stone plate on the pedestrian road so that pedestrians can easily see the guide plate and obtain the surrounding information, install various guide plates on the roadside to cover the surrounding landscape Will not.

본 발명은 실크스크린 인쇄용 제판을 제작하는 과정과, 석재판에 실크스크린 인쇄용 제판을 대고 실크 인쇄를 하는 과정과, 인쇄가 완료된 석재판을 소성하는 과정과, 1차 소성된 석재판을 2차 소성시키는 2차 소성과정을 수행함으로써 세워 놓거나 걸어 놓은 상태로 사용하는 석재 안내판을 제공한다.The present invention provides a process for producing a silk-screen printing plate, a silk-printing the silk-screen printing plate on the stone plate, the process of firing the stone plate is printed, and the secondary fired stone plate It provides a stone guide plate to be used upright or hanged by performing a secondary firing process.

또한 본 발명은 실크스크린 인쇄용 제판을 제작하는 과정과, 석재판에 실크스크린 인쇄용 제판을 대고 실크 인쇄를 하는 과정과, 인쇄가 완료된 석재판을 소성하는 과정과, 1차 소성된 석재판에 미끄럼 방지 잉크를 실크스크린 인쇄를 하는 과정과, 미끄럼 방지 인쇄된 석재판을 소성시키는 2차 소성과정을 수행함으로써 보행자 도로에 깔아 놓고 사용할 수 있도록 하는 것으로, 시야를 가리지 않고 바닥에 각종 안내판의 설치가 가능하게 된다.In addition, the present invention is a process for producing a silk-screen printing plate, a silk-printing the silk-screen printing plate on the stone plate, a process of firing the stone plate is printed, and the anti-slip on the primary fired stone plate Silkscreen printing of ink and secondary firing process of firing non-slip printed stone plates can be used on the pedestrian road, allowing various guide plates to be installed on the floor. do.

여기서, 석재판은 자연석 또는 인조석을 모두 사용할 수 있다.Here, the stone plate may be used both natural stone or artificial stone.

이러한 본 발명은 영국에서 생산되는 실크스크린 인쇄용 감광유제인 세리콜22유제와 노광시간을 조절하는 유제복합제인 감광제를 혼합하여 30분간 골고루 저은 다음 암실에서 48시간 경과 후 420메쉬 정도의 실크스크린 인쇄용 망사에 암실에서 감광유제 도포작업을 하고 도포작업 후 드라이어로 말린 후 노광작업을 한 다음 살수작업을 하여 석재판 표면에 안내표지판을 인쇄한 후에 700oC로 한번(24시간) 구운 다음 특수 코팅 한 것을 다시 800oC로 도자기 가마에 다시 소성(24시간)하게 되는 것으로, 물리적으로나 화학적으로 훼손되지 않는 석재 안내판을 얻게 된다.The present invention is a mixture of petroleum petroleum emulsion silk sensitizer for silk-screen printing produced in the United Kingdom and a photosensitive agent for the emulsion complex to control the exposure time, evenly mixed for 30 minutes and then in the dark room after about 48 hours in a silk screen printing mesh of about 420 mesh Apply photo emulsion in the darkroom, dry it with a dryer, apply exposure, spray water, print the guide plate on the surface of the stone plate, bake it at 700 o C (24 hours), and then apply special coating again. By firing again (24 hours) in a ceramic kiln at 800 o C, you get a stone guide that is not physically or chemically damaged.

이러한 석재 안내판을 보행자 도로에 깔아서 사용하기 위해서는 표면에 미끄럼 방지 코팅을 하여야 하는 것으로, 1차 소성이 완료된 석재판의 표면에 미끄럼 방지코팅을 하게 된다.In order to use such a stone guide plate on the pedestrian road, it is necessary to apply a non-slip coating on the surface, and the anti-slip coating is performed on the surface of the stone plate where the primary firing is completed.

본 발명에서 1차 소성을 마친 석재판에 미끄럼방지(논슬립 코팅)을 하기위해 후럭스가루(Flux) 40중량%에 알루미나가루(ALUMINIUM OXIDE) 10중량%를 희석한 후에 오일(Colourless Screen Printing Oil) 50 중량%를 희석한 잉크를 180메쉬공판에 희석된 잉크를 사용하여 석재판에 직접 실크스크린 인쇄를 한 후 30분간 40oC의 온도에서 열풍기 바람으로 건조한 후 2차 소성에 들어가 가마에서 24시간 소성시켜 완성된 석재 안내판은 칼, 못, 화공약품 등 어떠한 것으로도 손상되지 않고 보행자가 편리하게 주변 정보를 알 수 있다.In the present invention, after diluting 10% by weight of alumina powder (ALUMINIUM OXIDE) to 40% by weight of Flux powder to prevent slippage (non-slip coating) on the finished stone plate, the oil (Colourless Screen Printing Oil) Ink diluted 50% by weight was directly silk-screen printed on stone plate using ink diluted in 180 mesh plate, dried by hot air wind at 40 o C for 30 minutes, and then subjected to secondary firing, The stone guide plate completed by firing is not damaged by any knife, nail, chemicals, etc., and pedestrians can conveniently know the surrounding information.

이하 본 발명을 세워서 설치하게 되는 안내판에 적용시키는 실시예에 대하여 상세히 설명하면 다음과 같다.Hereinafter will be described in detail with respect to the embodiment to be applied to the guide plate to be installed in the present invention.

본 발명은 석재 안내판(100)을 제작하여 매달아 놓거나 세워서 설치하는데 사용하는 것으로, 표면에 흠집만 나지 않으면 될 뿐 굳이 미끄럼 방지 기능까지는 요구하지 않는다.The present invention is to use to install the stone guide plate 100 to hung or installed upright, it does not require the anti-slip function only if the surface only scratches.

본 발명의 실시예 1은 실크스크린인쇄용 제판을 제작하는 과정과, 석재판에 실크스크린인쇄용 제판을 대고 실크 인쇄를 하는 과정과, 인쇄가 완료된 석재판을 1차 소성하는 과정과, 1차 소성된 석재판을 2차 소성시키는 2차 소성과정을 거쳐 석재 안내판(100)을 얻어내게 된다.Example 1 of the present invention is a process for producing a silk-screen printing plate, a silk-printing the silk-screen printing plate on the stone plate, a process of first firing the stone plate is completed, and the first fired The stone guide plate 100 is obtained through a secondary firing process of secondaryly firing the stone plate.

이러한 본 발명의 실시예 1에서 각각의 과정에 대하여 구체적으로 살펴본다.In the first embodiment of the present invention will be described in detail for each process.

1. 실크스크린 인쇄용 제판을 제작하는 과정1. The process of making silkscreen printing

①. 실크스크린 인쇄용으로 시중에서 구입할 수 있는 영국제품인 인쇄용 감광유제인 세리콜22 액체 97중량%에 감광제 3중량%의 비율로 혼합시킨 후 5시간 숙성을 시킨다.①. It is mixed with 97% by weight of liquid 3% by weight of a photosensitive emulsion, Cericol 22, a British printing emulsion, commercially available for silk screen printing, and then aged for 5 hours.

②. 420메쉬(mesh)의 실크망사를 실크인쇄용 알루미늄 제판에 고정시킨 후 상기에서 숙성된 감광유제를 1회 도포한다.②. After fixing 420 mesh of silk mesh to the aluminum plate for silk printing, the photosensitive emulsion aged above is applied once.

③. 감광유제를 도포한 후 도로안내 문구와 도로표시 그림 등의 각종 안내 정보가 표시된 인쇄도면 필름을 상기 실크망사에 부착한 후 5kw의 아크등으로 1.5m앞에서 110초간 빛을 투과시킨 이후 인쇄도면 필름을 떼어낸다.③. After applying a photosensitive emulsion, a printed drawing film showing various guide information such as road guide text and road marking picture was attached to the silk mesh, and after transmitting light for 110 seconds at a distance of 1.5m with an arc lamp of 5kw, the printed drawing film was applied. Remove it.

④. 인쇄도면 필름을 떼어낸 후 콤프레서로 물을 분사시켜 주어 실크스크린 인쇄용 제판을 완성한다.④. After removing the printed drawing film, spray water with a compressor to complete the silkscreen printing.

2. 실크 인쇄를 하는 과정2. Silk printing process

①. 칼라색소분말 50중량%에 점도조절용 오일(Colourless Screen Printing Oil) 50중량%의 비율로 혼합 하여 실크스크린인쇄용 잉크를 만든다.①. Silk-screen printing ink is prepared by mixing 50% by weight of color pigment powder in 50% by weight of Colorless Printing Oil.

②. 석재판에 실크스크린 인쇄용 제판을 대고 상기 실크스크린인쇄용 잉크로 칼라인쇄를 한 후 40℃ 의 온도에서 30분간 자연 건조시킨다.②. A silk screen printing plate is placed on the stone plate, and color printing is performed with the silk screen printing ink, followed by natural drying at a temperature of 40 ° C. for 30 minutes.

3. 1차 소성과정3. First firing process

①. 실크스크린 인쇄된 석재판을 도자기 가마에 넣고 700oC로 24시간 동안 가열을 시킨다.①. Silkscreen printed stone plates are placed in a ceramic kiln and heated to 700 o C for 24 hours.

②. 가열 과정에서 실크스크린인쇄용 잉크는 450oC에서 녹으며 제거되고, 석재판에는 도로안내 문구와 도로표시 등의 각종 안내정보를 나타내는 그림과 글자 및 기호 등이 칼라로 소성된 석재 안내판(100)이 1차 완성된다.②. In the heating process, the silk screen printing ink is melted and removed at 450 ° C. The stone plate includes a stone guide plate 100 calcined with colors, pictures, letters, and symbols representing various guide information such as road guide text and road markings. 1st complete.

4. 2차 소성과정4. Secondary firing process

1차 소성된 석재판을 가마에 넣어 800℃의 고온으로 24시간 가열을 시켜 표면에 단단한 유리질 코팅을 하여 석재 안내판(100)을 얻게 된다.The first calcined stone plate is put into a kiln and heated at a high temperature of 800 ° C. for 24 hours to give a hard glass coating on the surface to obtain a stone guide plate 100.

이러한 본 발명의 석재 안내판(100)은 위치정보나 안내 정보 등의 각종 안내정보가 칼라로 표시된 상태에서 물리적으로나 화학적으로 훼손되지 않는 것이어서, 장시간 안정적으로 사용할 수 있다.The stone guide plate 100 of the present invention is not damaged physically or chemically in a state where various guide information such as position information and guide information is displayed in color, it can be used stably for a long time.

본 발명은 석재 안내판(200)을 제작하여 보행자도로에 설치함으로써 보행자가 보행자도로에 설치된 것을 보고, 위치정보나 안내 정보 등의 각종 정보를 쉽게 확인할 수 있도록 하는 한편 보행 시 문제가 되지 않도록 표면에 미끄럼을 방지하는 한편 흠집이 발생하지 않도록 한다.The present invention by making the stone guide plate 200 is installed on the pedestrian road to see that the pedestrian is installed on the pedestrian road, it is easy to check a variety of information, such as location information and guide information, while slipping on the surface to avoid problems when walking Prevents scratches and prevents scratches.

본 발명의 실시예 2는 실크스크린인쇄용 제판을 제작하는 과정과, 석재판에 실크스크린인쇄용 제판을 대고 실크 인쇄를 하는 과정과, 인쇄가 완료된 석재판을 1차 소성하는 과정과, 1차 소성된 석재판에 미끄럼 방지 잉크로 실크스크린 인쇄를 하는 과정과, 미끄럼 방지 인쇄된 석재판을 소성시키는 2차 소성과정을 수행함으로써 석재 안내판(200)을 얻게 된다.Example 2 of the present invention is a process for producing a silk-screen printing plate, a silk-printing the silk-screen printing plate on the stone plate, a process of first firing the stone plate is printed, and the first fired The stone guide plate 200 is obtained by performing a silkscreen printing process using a non-slip ink on the stone plate and a secondary baking process of firing the non-slip printed stone plate.

이러한 본 발명의 실시예 2에서 각각의 과정에 대하여 구체적으로 살펴본다.In the second embodiment of the present invention will be described in detail for each process.

1. 실크스크린 인쇄용 제판을 제작하는 과정1. The process of making silkscreen printing

①. 실크스크린 인쇄용으로 시중에서 구입할 수 있는 영국제품인 인쇄용 감광유제인 세리콜22 액체 97중량%에 감광제 3중량%의 비율로 혼합시킨 후 5시간 숙성을 시킨다.①. It is mixed with 97% by weight of liquid 3% by weight of a photosensitive emulsion, Cericol 22, a British printing emulsion, commercially available for silk screen printing, and then aged for 5 hours.

②. 420메쉬(mesh)의 실크망사를 실크인쇄용 알루미늄 제판에 고정시킨 후 상기에서 숙성된 감광유제를 1회 도포한다.②. After fixing a 420 mesh silk mesh to an aluminum plate for silk printing, the photosensitive emulsion aged above is applied once.

③. 감광유제를 도포한 후 도로안내 문구와 도로표시 그림 등의 각종 안내 정보가 표시된 인쇄도면 필름을 상기 실크망사에 부착한 후 5kw의 아크등으로 1.5m앞에서 110초간 빛을 투과시킨 이후 인쇄도면 필름을 떼어낸다.③. After applying a photosensitive emulsion, a printed drawing film showing various guide information such as road guide text and road marking picture was attached to the silk mesh, and after transmitting light for 110 seconds at a distance of 1.5m with an arc lamp of 5kw, the printed drawing film was applied. Remove it.

④. 인쇄도면 필름을 떼어낸 후 콤프레서로 물을 분사시켜 주어 실크스크린 인쇄용 제판을 완성한다.④. After removing the printed drawing film, spray water with a compressor to complete the silkscreen printing.

2. 실크 인쇄를 하는 과정2. Silk printing process

①. 칼라색소분말 50중량%에 점도조절용 오일(Colourless Screen Printing Oil) 50중량%의 비율로 혼합 하여 실크스크린인쇄용 잉크를 만든다.①. Silk-screen printing ink is prepared by mixing 50% by weight of color pigment powder in 50% by weight of Colorless Printing Oil.

②. 석재판에 실크스크린 인쇄용 제판을 대고 상기 실크스크린인쇄용 잉크로 칼라인쇄를 한 후 40℃ 의 온도에서 30분간 자연 건조시킨다.②. A silk screen printing plate is placed on the stone plate, and color printing is performed with the silk screen printing ink, followed by natural drying at a temperature of 40 ° C. for 30 minutes.

3. 1차 소성과정3. First firing process

①. 실크스크린 인쇄된 석재판을 도자기 가마에 넣고 700oC로 24시간 동안 가열을 시킨다.①. Silkscreen printed stone plates are placed in a ceramic kiln and heated to 700 o C for 24 hours.

②. 가열 과정에서 실크스크린인쇄용 잉크는 450oC에서 녹으며 제거되고, 석재판에는 도로안내 문구와 도로표시 등의 각종 안내정보를 나타내는 그림과 글자 및 기호 등이 칼라로 소성된 석재 안내판(200)이 1차 완성된다.②. In the heating process, the silk screen printing ink is melted and removed at 450 o C, and the stone plate includes a stone guide plate 200 which is burned in color with pictures, letters, and symbols indicating various guide information such as road guide text and road markings. 1st complete.

4. 미끄럼 방지 인쇄과정4. Anti-skid printing process

①. 후럭스 가루(Flux) 40중량%에 알루미나가루(ALUMINIUM OXIDE) 10중량%를 혼합한 후에 오일(Colourless Screen Printing Oil) 50중량%의 비율로 혼합하여 미끄럼 방지 실크스크린인쇄용 잉크를 만든다.①. 10% by weight of alumina powder (ALUMINIUM OXIDE) is mixed with 40% by weight of flux powder (Flux) and then mixed at a rate of 50% by weight of oil (Colourless Screen Printing Oil) to make an anti-slip silk screen printing ink.

②. 미끄럼 방지 실크스크린인쇄용 잉크를 180 메쉬공판에 희석된 잉크를 사용하여 1차 소성된 석재판에 직접 실크스크린 인쇄를 한 후 40℃의 온도에서 30분간 자연 건조시킨다.②. The non-slip silk screen printing ink was directly silkscreen printed on the first calcined stone board using ink diluted in a 180 mesh slab and then naturally dried at a temperature of 40 ° C. for 30 minutes.

5. 2차 소성과정5. Secondary firing process

미끄럼방지 실크스크린인쇄용 잉크로 실크스크린 인쇄된 석재판은 가마에 넣어 800℃의 고온으로 24시간 가열을 시켜 보행자 도로에 설치하는 석재 안내판(200)을 완성하게 된다.The stone plate silk-screen printed with the non-slip silk screen printing ink is put into the kiln to be heated at a high temperature of 800 ℃ 24 hours to complete the stone guide plate 200 to be installed on the pedestrian road.

여기서, 석재판에 인쇄된 미끄럼방지 실크스크린인쇄용 오일은 400℃의 온도에서 녹아 제거된다.Here, the non-slip silk screen printing oil printed on the stone plate is removed by melting at a temperature of 400 ℃.

이러한 본 발명의 석재 안내판(200)은 보행자도로에 깔려있는 상태에서 위치정보나 안내 정보 등의 각종 안내정보를 확인하게 되므로, 시야를 가리지 않으면서도 정보 제공이 가능하고, 또한 석재 안내판(200)은 칼라로 표시된 상태에서 물리적으로나 화학적으로 훼손되지 않는 것이어서, 장시간 안정적으로 사용할 수 있다.Since the stone guide plate 200 of the present invention checks various guide information such as location information and guide information while being laid on a pedestrian road, information can be provided without obscuring the field of view, and the stone guide plate 200 is It is not physically or chemically damaged in the state indicated by the color, so it can be used stably for a long time.

100, 200 : 석재 안내판100, 200: stone guide plate

Claims (2)

실크스크린 인쇄용 감광유제인 세리콜22액체 97중량%에 감광제 3중량%의 비율로 혼합시킨 후 5시간 숙성을 시키고, 420매시(mesh)의 실크망사를 실크인쇄용 알루미늄 제판에 고정시킨 후 상기 숙성된 감광유제를 1회 도포한 다음 도로안내 문구와 도로표시 그림이 형성된 인쇄도면 필름을 실크망사에 부착한 후 5kw의 아크등으로1.5m앞에서 110초간 빛을 투과시킨 이후 콤프레서로 물을 분사시켜 실크스크린인쇄용 제판을 완성하고,
칼라색소분말 50중량%에 점도조절용 오일(Colourless Screen Printing Oil) 50중량%의 비율로 혼합하여 실크스크린인쇄용 잉크를 만든 다음 석재판에 실크스크린인쇄용 제판을 대고 상기 실크스크린인쇄용 잉크로 인쇄를 한 후 40℃의 온도에서 30분간 자연 건조시키며,
자연 건조된 석재판은 도자기 가마에 넣고 700℃로 24시간 구워 1차 소성을 하고,
1차 소성된 석재판을 도자기 가마에 넣고 다시 800℃로 24시간 가열시켜 석재 안내판을 제조하는 것을 특징으로 하는 석재 안내판의 제조방법.97% by weight of a photosensitive emulsion, ceric 22 liquid for silk screen printing, was mixed at a ratio of 3% by weight of a photosensitive agent, followed by aging for 5 hours, and after fixing 420 mesh silk mesh to an aluminum plate for silk printing, the aged After applying the emulsion once, attach the printed drawing film formed with road guidance text and road marking pictures to the silk mesh, transmit light for 1.5 seconds in front of 1.5m with 5kw arc lamp, and then spray water with the compressor for silk screen printing. To finish the engraving,
After mixing 50% by weight of color pigment powder with 50% by weight of viscosity control oil (Colourless Screen Printing Oil) to make a silk screen printing ink, and then put the silk screen printing plate on the stone plate and print with the silk screen printing ink. Air-dried for 30 minutes at a temperature of 40 ℃,
The naturally dried stone board is placed in a ceramic kiln and baked at 700 ° C for 24 hours for the first firing.
Put the first fired stone plate in a ceramic kiln and again heated to 800 ℃ for 24 hours to produce a stone guide plate, characterized in that for producing a stone guide plate. 실크스크린 인쇄용 감광유제인 세리콜22액체 97중량%에 감광제 3중량%의 비율로 혼합시킨 후 5시간 숙성을 시키고, 420매시(mesh)의 실크망사를 실크인쇄용 알루미늄 제판에 고정시킨 후 상기 숙성된 감광유제를 1회 도포한 다음 도로안내 문구와 도로표시 그림 또는 QR코드가 표시된 인쇄도면 필름을 실크망사에 부착한 후 5kw의 아크등으로1.5m앞에서 110초간 빛을 투과시킨 이후 콤프레서로 물을 분사시켜 실크스크린인쇄용 제판을 완성하고,
칼라색소분말 50중량%에 점도조절용 오일(Colourless Screen Printing Oil) 50중량%의 비율로 혼합하여 실크스크린인쇄용 잉크를 만든 다음 석재판에 실크스크린인쇄용 제판을 대고 상기 실크스크린인쇄용 잉크로 인쇄를 한 후 40℃의 온도에서 30분간 자연 건조시키며,
자연 건조된 석재판은 도자기 가마에 넣고 700℃로 24시간 구워 1차 소성을 하고,
상기 1차 소성된 석재판에 미끄럼 방지를 위하여 후럭스가루(Flux) 40중량%에 알루미나가루(ALUMINIUM OXIDE) 10중량%를 희석한 후에 오일(Colourless Screen Printing Oil) 50중량%를 희석한 잉크를 180메쉬공판에 희석된 잉크를 사용하여 직접 실크스크린인쇄를 한 후 30분간 40℃의 온도에서 열풍기 바람으로 건조하며,
상기 미끄럼방지 실크스크인 인쇄를 한 석재판을 도자기 가마에 넣고 다시 800℃로 24시간 가열시켜 석재 안내판을 제조하는 것을 특징으로 하는 석재 안내판의 제조방법.97% by weight of a photosensitive emulsion, ceric 22 liquid for silk screen printing, was mixed at a ratio of 3% by weight of a photosensitive agent, followed by aging for 5 hours, and after fixing 420 mesh silk mesh to an aluminum plate for silk printing, the aged After applying the emulsion once, attach the road guide text, the road marking picture or the printed drawing film marked with the QR code to the silk mesh, and then transmit the light through the compressor for 110 seconds at 1.5m with a 5kw arc lamp. Finish the silk screen printing plate,
After mixing 50% by weight of color pigment powder with 50% by weight of viscosity control oil (Colourless Screen Printing Oil) to make a silk screen printing ink, and then put the silk screen printing plate on the stone plate and print with the silk screen printing ink. Air-dried for 30 minutes at a temperature of 40 ℃,
The naturally dried stone board is placed in a ceramic kiln and baked at 700 ° C for 24 hours for the first firing.
The first calcined stone plate was diluted with 10% by weight of alumina powder (ALUMINIUM OXIDE) to 40% by weight of flux powder (Flux) to prevent slipping, and then ink containing 50% by weight of oil (Colourless Screen Printing Oil) was diluted. After silkscreen printing using ink diluted in 180 mesh plate, dry by hot air wind at 40 ℃ for 30 minutes,
The method of producing a stone guide plate characterized in that the non-slip silk-sk printing stone plate is put in a ceramic kiln and again heated to 800 ℃ 24 hours to produce a stone guide plate.
KR1020130035196A 2013-04-01 2013-04-01 The method of manufacturing stone guideboard KR101302699B1 (en)