KR101273194B1 - Film for protecting screen of display panel - Google Patents

Film for protecting screen of display panel Download PDF

Info

Publication number
KR101273194B1
KR101273194B1 KR1020110023917A KR20110023917A KR101273194B1 KR 101273194 B1 KR101273194 B1 KR 101273194B1 KR 1020110023917 A KR1020110023917 A KR 1020110023917A KR 20110023917 A KR20110023917 A KR 20110023917A KR 101273194 B1 KR101273194 B1 KR 101273194B1
Authority
KR
South Korea
Prior art keywords
pressure
sensitive adhesive
film
base film
panel
Prior art date
Application number
KR1020110023917A
Other languages
Korean (ko)
Other versions
KR20120106068A (en
Inventor
강한준
윤성환
전승환
이은구
Original Assignee
율촌화학 주식회사
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 율촌화학 주식회사 filed Critical 율촌화학 주식회사
Priority to KR1020110023917A priority Critical patent/KR101273194B1/en
Publication of KR20120106068A publication Critical patent/KR20120106068A/en
Application granted granted Critical
Publication of KR101273194B1 publication Critical patent/KR101273194B1/en

Abstract

본 발명은 LCD 패널 등의 디스플레이 패널의 화면 보호 필름에 관한 것으로서, 기재 필름 상에 형성된 점착제 코팅부와 점착제 비코팅부를 포함하되, 상기 점착제 코팅부는 기재 필름의 가장자리에 형성되어 디스플레이 패널의 프레임에 부착되며, 상기 점착제 비코팅부는 디스플레이 패널의 표시부에 위치되고 상기 표시부의 면적보다 크거나 같은 화면 보호 필름을 제공한다.　 본 발명에 따르면, 점착제가 패널의 화면에 접촉되지 않도록 기재 필름의 가장자리 영역에 부분 코팅되어, 점착제의 전사에 따른 액정 폴(Pol) 얼룩 등의 화면 오염이 방지된다. The present invention relates to a screen protection film of a display panel, such as an LCD panel, including an adhesive coating and an adhesive non-coating formed on a base film, wherein the adhesive coating is formed on the edge of the base film is attached to the frame of the display panel The adhesive uncoated portion is provided on the display unit of the display panel and provides a screen protection film that is larger than or equal to the area of the display unit. According to the present invention, the adhesive is partially coated on the edge region of the base film so that the adhesive does not contact the screen of the panel, thereby preventing screen contamination such as liquid crystal pollen due to transfer of the adhesive.

Description

디스플레이 패널의 화면 보호 필름{FILM FOR PROTECTING SCREEN OF DISPLAY PANEL}Screen protection film of display panel {FILM FOR PROTECTING SCREEN OF DISPLAY PANEL}

본 발명은 디스플레이 패널의 화면 보호 필름에 관한 것으로, 보다 상세하게는 기재 필름 상에 점착제를 코팅하되, 점착제를 패널의 화면에 접촉되지 않도록 기재 필름의 가장자리 영역에 부분 코팅함으로써, 점착제의 전사에 따른 화면의 오염을 방지한 디스플레이 패널의 화면 보호 필름에 관한 것이다.
The present invention relates to a screen protection film of a display panel, and more particularly, by coating the pressure-sensitive adhesive on the base film, by partially coating the pressure-sensitive adhesive on the edge region of the base film so as not to contact the screen of the panel, The screen protection film of the display panel which prevented the contamination of the screen.

디스플레이 패널(Display Panel), 예를 들어 LCD 패널(Liquid Crystal Display Panel), PDP(Plasma Display Panel) 등의 디스플레이 패널은 컴퓨터 모니터, TV 및 각종 광고판 등의 표시 장치로 유용하게 사용된다.　　　 A display panel such as a liquid crystal display panel (LCD), a plasma display panel (PDP), or the like is usefully used as a display device such as a computer monitor, a TV, and various advertisement boards.

도 1은 디스플레이 패널의 일반적인 모습을 보인 정면도이다.　 도 1에 보인 바와 같이, 디스플레이 패널(P)은 영상 등이 표시되는 화면으로서의 표시부(10)와, 상기 표시부(10)의 측면에 형성되어 표시부(10)를 지지하는 지지체로서의 프레임(20)을 갖는다.　 1 is a front view illustrating a general view of a display panel. As shown in FIG. 1, the display panel P includes a display unit 10 as a screen on which an image or the like is displayed, and a frame 20 formed on the side of the display unit 10 to support the display unit 10. Have

디스플레이 패널(P)은 일반적으로 그의 정면(앞면)에, 즉 표시부(10)의 표면에 화면 보호 필름이 부착된 상태로 소비자에게 유통, 보급되고 있다.　 화면 보호 필름은 통상적으로 접착 테이프(tape)에 의해 패널(P)에 부착, 고정되었다.　 화면 보호 필름은 패널(P)의 화면, 즉 패널(P)의 표시부(10)를 외력이나 오염으로부터 보호한다.　 이러한 화면 보호 필름으로는 폴리에틸렌테레프탈레이트(PET) 필름 등이 주로 사용되어 왔다.　 상기 PET 필름은 내오염성 및 내마모성 등이 우수한 장점이 있다.　 그러나 화면 보호 필름을 패널(P)에 접착 테이프(tape)로 부착한 경우, 화면 보호 필름과 패널(P) 사이의 빈 공간으로 이물질이 혼입되어 스크래치(scratch)나 오염이 발생되었다. The display panel P is generally distributed and distributed to consumers in the state where the screen protection film is attached to the front (front) thereof, that is, the surface of the display unit 10. The screen protection film was normally attached to and fixed to the panel P by an adhesive tape. The screen protective film protects the screen of the panel P, that is, the display portion 10 of the panel P from external force or contamination. As such screen protection films, polyethylene terephthalate (PET) films and the like have been mainly used. The PET film has advantages such as pollution resistance and wear resistance. However, when the screen protection film is attached to the panel P with an adhesive tape, foreign matters are mixed into the empty space between the screen protection film and the panel P, resulting in scratches or contamination.

이를 방지하기 위해, 화면 보호 필름에는 일반적으로 패널(P)과의 부착성(밀착성) 개선을 위한 점착제가 코팅되고 있다.　 구체적으로, 화면 보호 필름은 기재 필름과, 상기 기재 필름에 코팅된 점착제층을 포함하여 구성되고 있다.　 상기 기재 필름은 전술한 바와 같은 PET 필름 등이 주로 사용되고, 점착제층은 주로 아크릴계 점착제가 코팅되어 형성된다.　 이때, 점착제층은 기재 필름의 표면 전체 영역에 코팅된다.　 이에 따라, 점착제층이 패널(P)의 표시부(10)에 부착되어, 필름과 패널(P)의 부착력 개선으로 이물질의 혼입이 방지된다. In order to prevent this, the screen protection film is generally coated with an adhesive for improving adhesion (adhesiveness) with the panel P. Specifically, the screen protection film is comprised including the base film and the adhesive layer coated on the said base film. The base film is mainly used as the PET film as described above, the pressure-sensitive adhesive layer is mainly formed by coating an acrylic pressure-sensitive adhesive. At this time, the pressure-sensitive adhesive layer is coated on the entire surface area of the base film. Accordingly, the pressure-sensitive adhesive layer is attached to the display portion 10 of the panel P, and the mixing of the foreign matter is prevented by improving the adhesion between the film and the panel P.

그러나 종래 기술에 따른 화면 보호 필름은 점착제의 코팅에 의해 이물질의 혼입은 방지되고 있으나, 오히려 점착제에 의해 얼룩 등의 오염이 발생되는 문제점이 있다.　 구체적으로, 점착제가 패널(P)의 표시부(10), 즉 화면에 전사되어 액정 폴(Pol) 얼룩 등의 오염이 발생되는 문제점이 있다.
However, the screen protection film according to the prior art is prevented from mixing of foreign matter by the coating of the adhesive, but rather there is a problem that contamination such as stains are generated by the adhesive. Specifically, there is a problem that the adhesive is transferred to the display unit 10 of the panel P, that is, the screen, such that contamination such as liquid crystal pollen stains occurs.

이에, 본 발명은 기재 필름 상에 점착제를 코팅하되, 점착제를 패널의 화면에 접촉되지 않도록 기재 필름의 가장자리 영역에 부분 코팅함으로써, 이물질의 혼입을 방지함은 물론, 점착제의 전사에 따른 액정 폴(Pol) 얼룩 등의 화면 오염을 방지한 디스플레이 패널의 화면 보호 필름을 제공하는 데에 그 목적이 있다.
Accordingly, the present invention is coated with an adhesive on the base film, but by partially coating the adhesive on the edge region of the base film so as not to contact the screen of the panel, to prevent the mixing of foreign matters, as well as the liquid crystal pole according to the transfer of the adhesive ( Pol) The object is to provide a screen protection film of a display panel which prevents screen contamination such as staining.

상기 목적을 달성하기 위하여 본 발명은, The present invention to achieve the above object,

표시부와 프레임을 가지는 디스플레이 패널의 화면 보호 필름으로서, As a screen protection film of the display panel which has a display part and a frame,

기재 필름; A base film;

상기 기재 필름 상에 형성된 점착제 코팅부와 점착제 비코팅부를 포함하고, It includes a pressure-sensitive adhesive coating and a pressure-sensitive adhesive uncoated portion formed on the base film,

상기 점착제 코팅부는 기재 필름의 가장자리에 형성되어 디스플레이 패널의 프레임에 부착되며, The adhesive coating is formed on the edge of the base film is attached to the frame of the display panel,

상기 점착제 비코팅부는 디스플레이 패널의 표시부에 위치되고, 상기 표시부의 면적보다 크거나 같은 디스플레이 패널의 화면 보호 필름을 제공한다. The pressure-sensitive adhesive uncoated portion is positioned on a display portion of the display panel and provides a screen protection film of the display panel that is larger than or equal to the area of the display portion.

이때, 상기 점착제 코팅부는 프레임의 측면 및 배면 중에서 선택된 하나 이상에 부착되는 것이 바람직하다.　 또한, 상기 점착제 코팅부와 점착제 비코팅부의 경계선에 꺾임부가 형성된 것이 좋다.　 At this time, the pressure-sensitive adhesive coating is preferably attached to one or more selected from the side and back of the frame. In addition, the bent portion is formed on the boundary line of the pressure-sensitive adhesive coating and the pressure-sensitive adhesive uncoated portion.

바람직한 구현예에 따라서, 상기 기재 필름은 프레임의 측면에 밀착되도록 꺾어지는 제1꺾임부와, 프레임의 배면에 밀착되도록 꺾어지는 제2꺾임부가 형성되고, 상기 점착제 코팅부는 제2꺾임부에서 꺾어져 프레임의 배면에 부착되는 것이 좋다.　
According to a preferred embodiment, the base film is formed with a first bent to be in close contact with the side of the frame, a second bent to be in close contact with the back of the frame, the pressure-sensitive adhesive coating is bent at the second bent It is advisable to be attached to the back of the frame.

본 발명에 따르면, 점착제가 패널의 화면에 접촉되지 않도록 기재 필름의 가장자리 영역에 부분 코팅되어, 점착제의 전사에 따른 액정 폴(Pol) 얼룩 등의 화면 오염이 방지되는 효과를 갖는다.　　　
According to the present invention, the pressure-sensitive adhesive is partially coated on the edge region of the base film so as not to contact the screen of the panel, thereby preventing screen contamination such as liquid crystal pollen due to transfer of the pressure-sensitive adhesive.

도 1은 디스플레이 패널의 일반적인 모습을 보인 정면도이다.
도 2는 본 발명의 제1구현예에 따른 화면 보호 필름의 평면 구성도이다.
도 3은 상기 도 2에 보인 화면 보호 필름의 종단면도이다.
도 4는 본 발명의 제2구현예에 따른 화면 보호 필름의 평면 구성도이다.
도 5는 상기 도 4에 보인 화면 보호 필름의 종단면도이다.
도 6은 본 발명의 제3구현예에 따른 화면 보호 필름의 평면 구성도이다.
도 7은 상기 도 6에 보인 화면 보호 필름의 종단면도이다.
도 8은 본 발명의 제4구현예에 따른 화면 보호 필름의 평면 구성도이다. 1 is a front view illustrating a general view of a display panel.
2 is a plan view illustrating the screen protection film according to the first embodiment of the present invention.
3 is a longitudinal cross-sectional view of the screen protection film shown in FIG.
4 is a plan view illustrating a screen protection film according to a second embodiment of the present invention.
5 is a longitudinal cross-sectional view of the screen protection film shown in FIG.
6 is a plan view illustrating a screen protection film according to a third embodiment of the present invention.
FIG. 7 is a longitudinal cross-sectional view of the screen protection film shown in FIG. 6.
8 is a plan view illustrating a screen protection film according to a fourth embodiment of the present invention.

이하, 첨부된 도면을 참조하여 본 발명을 상세히 설명한다. Hereinafter, with reference to the accompanying drawings will be described in detail the present invention.

도 2는 본 발명의 제1구현예에 따른 화면 보호 필름(100)의 평면 구성도이고, 도 3은 상기 도 2에 보인 화면 보호 필름(100)의 종단면도이다.　　 도 2 및 도 3에는 본 발명에 따른 화면 보호 필름(100)과 디스플레이 패널(P)이 함께 도시되어 있다.　 이때, 도 3은 디스플레이 패널(P)에 본 발명에 따른 화면 보호 필름(100)이 부착되는 모습을 도시한 것이다.　　　 2 is a plan configuration diagram of the screen protection film 100 according to the first embodiment of the present invention, Figure 3 is a longitudinal cross-sectional view of the screen protection film 100 shown in FIG. 2 and 3 illustrate the screen protection film 100 and the display panel P according to the present invention. In this case, Figure 3 shows a state in which the screen protection film 100 according to the present invention is attached to the display panel (P).

상기 디스플레이 패널(P)은, 영상 등이 표시되는 화면으로서의 표시부(10)와, 상기 표시부(10)의 측면에 형성되어 표시부(10)를 지지하는 지지체로서의 프레임(20)을 갖는다.　 이러한 디스플레이 패널(P)은 제한되지 않는다.　 디스플레이 패널(P)은, 예를 들어 LCD 패널(Liquid Crystal Display Panel) 및 PDP(Plasma Display Panel) 등으로부터 선택될 수 있으며, 표시부(10)와 프레임(20)을 가지는 것이면 좋다.　 상기 표시부(10)는 유리 또는 투명 필름 등으로 구성될 수 있으며, 상기 프레임(20)은 금속재, 플라스틱재, 석재(대리석 등) 또는 세라믹재 등으로 구성될 수 있다.　 또한, 프레임(20)은 상기 금속재, 플라스틱재 등의 표면에 수지가 코팅된 형태이어도 좋다. The display panel P has a display portion 10 as a screen on which an image or the like is displayed, and a frame 20 formed on the side of the display portion 10 to support the display portion 10. This display panel P is not limited. The display panel P may be selected from, for example, an LCD panel (Liquid Crystal Display Panel), a plasma display panel (PDP), or the like, and may have the display unit 10 and the frame 20. The display unit 10 may be made of glass, transparent film, or the like, and the frame 20 may be made of metal, plastic, stone (marble, etc.) or ceramic material. In addition, the frame 20 may be in the form of a resin coated on the surface of the metal, plastic, or the like.

본 발명에 따른 화면 보호 필름(100)은 위와 같은 디스플레이 패널(P)에 부착되어 패널(P)의 표면을 보호한다.　 본 발명에 따른 화면 보호 필름(100)은 패널(P)의 표시부(10)를 포함하는 전면(정면)을 보호하며, 패널(P)의 전면(정면)은 물론 측면 및/또는 배면을 보호하여도 좋다.　 Screen protection film 100 according to the present invention is attached to the display panel (P) as described above to protect the surface of the panel (P). The screen protection film 100 according to the present invention protects the front surface (front) including the display unit 10 of the panel P, and protects the front surface (front) of the panel P as well as the side and / or the rear surface. Also good.

본 발명에 따른 화면 보호 필름(100)은 기재 필름(110)을 포함한다.　 그리고 상기 기재 필름(110)의 어느 한 면에는 점착제가 코팅되어 있다.　 이때, 상기 점착제는 기재 필름(110)의 표면 전체에 코팅되지 않고, 기재 필름(110) 표면의 일부 영역에 부분 코팅되어 있다.　 구체적으로, 도 2를 참조하면, 본 발명에 따른 화면 보호 필름(100)은 기재 필름(110)과, 상기 기재 필름(110) 상에 형성된 점착제 코팅부(120)와 점착제 비코팅부(130)를 포함한다.　 Screen protective film 100 according to the present invention includes a base film (110). And one side of the base film 110 is coated with an adhesive. In this case, the pressure-sensitive adhesive is not coated on the entire surface of the base film 110, but partially coated on a portion of the surface of the base film 110. Specifically, referring to FIG. 2, the screen protection film 100 according to the present invention includes a base film 110, an adhesive coating part 120 and an adhesive non-coating part 130 formed on the base film 110. It includes.

상기 점착제 코팅부(120)는 점착제가 코팅된 부분으로서, 여기에는 구체적으로 점착제층(125)이 형성되어 있다.　 이때, 도 2에 보인 바와 같이, 상기 점착제 코팅부(120)는 기재 필름(110)의 가장자리 영역에 형성된다.　 구체적으로, 점착제 코팅부(120)는 기재 필름(110)의 중앙 영역을 제외한 주변부(테두리)에 점착제층(125)이 코팅되어 형성된다.　 이때, 점착제 코팅부(120)는 x-y 평면에서 x 방향(가로 방향) 또는 y 방향(세로 방향)으로 형성되거나, x 및 y 방향 모두에 형성될 수 있다.　 도 2에는 x 방향(가로 방향)으로 형성된 모습을 예시한 것이다.　 그리고 첨부된 도 8에서는 x 및 y 방향 모두에 형성된 모습을 예시한 것이다.　 보다 구체적으로, 상기 점착제 코팅부(120)는 기재 필름(110)의 가장자리 영역에 형성되되, 도 2에 도시된 방향을 기준으로 기재 필름(110)의 x 방향의 상하측, y 방향의 좌우측 또는 상하좌우측 모두에 형성될 수 있다.　 도 2는 상하측에 형성된 모습을 예시한 것이다.　 그리고 도 8은 상하좌우측 모두에 형성된 것으로서, 기재 필름(110)의 주변부를 따라 가장자리 전체 역역에 형성된 모습을 예시한 것이다.　　 The pressure-sensitive adhesive coating 120 is a portion coated with an adhesive, in which the pressure-sensitive adhesive layer 125 is formed. At this time, as shown in Figure 2, the pressure-sensitive adhesive coating 120 is formed in the edge region of the base film (110). Specifically, the pressure-sensitive adhesive coating 120 is formed by coating the pressure-sensitive adhesive layer 125 on the peripheral portion (border) except for the central region of the base film 110. In this case, the pressure-sensitive adhesive coating 120 may be formed in the x-direction (horizontal direction) or the y-direction (vertical direction) in the x-y plane, or may be formed in both the x and y directions. 2 illustrates a state formed in the x direction (horizontal direction). And attached to Figure 8 illustrates the appearance formed in both the x and y direction. More specifically, the pressure-sensitive adhesive coating 120 is formed in the edge region of the base film 110, based on the direction shown in FIG. 2, the upper and lower sides of the base film 110, the left and right sides of the y direction or It can be formed in both up, down, left and right. Figure 2 illustrates the appearance formed on the upper and lower sides. And Figure 8 is formed on both the upper, lower, left and right side, illustrating the state formed in the entire area of the edge along the periphery of the base film 110.

또한, 상기 점착제층(125)은 코팅부(120)의 전체 면적에 대해 전면(全面) 코팅되거나, 점 코팅(dot coating) 또는 그리드(grid) 형상으로 코팅될 수 있다.　 도 2는 전면 코팅된 모습을 예시한 것이다.　 아울러, 도 4 및 도 5에 예시한 바와 같이, 상기 점착제층(125)은 코팅부(120)에 라인(Line) 형상으로 코팅될 수 있다.　 도 4 및 도 5는 점착제층(125)이 라인 형상으로서, x 방향으로 상하측에 2줄씩 형성된 모습을 예시한 것이다. In addition, the pressure-sensitive adhesive layer 125 may be coated on the entire surface of the coating part 120 or may be coated in a dot coating or grid shape. 2 illustrates a front coated appearance. In addition, as illustrated in FIGS. 4 and 5, the pressure-sensitive adhesive layer 125 may be coated in a line shape on the coating part 120. 4 and 5 illustrate a state in which the pressure-sensitive adhesive layer 125 is formed in a line shape, two lines on the upper and lower sides in the x direction.

도 3을 참조하면, 패널(P)에 부착 시, 상기 점착제 코팅부(120)가 패널(P)의 프레임(20)에 부착된다.　 즉, 점착제 코팅부(120)에 형성된 점착제층(125)이 프레임(20)에 부착되어, 본 발명에 따른 화면 보호 필름(100)과 패널(P) 간의 부착력이 도모된다.　 이때, 도 3에서는 기재 필름(110)과 표시부(10)의 계면에 공간이 형성된 모습으로 도시되어 있지만, 이들은 실제로는 밀착된다.　 Referring to FIG. 3, when attaching to the panel P, the pressure-sensitive adhesive coating 120 is attached to the frame 20 of the panel P. Referring to FIG. That is, the pressure-sensitive adhesive layer 125 formed on the pressure-sensitive adhesive coating portion 120 is attached to the frame 20, and thus the adhesive force between the screen protection film 100 and the panel P according to the present invention is promoted. In this case, although the space is formed in the interface between the base film 110 and the display unit 10 in FIG. 3, they are in close contact with each other.

상기 점착제 비코팅부(130)는 점착제가 코팅되지 않은 부분으로서, 이는 점착제 코팅부(120)를 제외한 영역이다.　 패널(P)에 부착 시, 상기 점착제 비코팅부(130)는 패널(P)의 표시부(10)에 위치된다.　 이때, 점착제 비코팅부(130)는 표시부(10)의 면적보다 크거나 같다.　 구체적으로, 도 2를 참조하면, 상기 점착제 비코팅부(130)의 면적(S130)과 상기 표시부(10)의 면적(S10)은 S130 ≥ S10을 만족한다.　 따라서 패널(P)에 부착 시, 영상이 표시되는 화면, 즉 패널(P)의 표시부(10)는 점착제층(125)과 접촉되지 않아 점착제가 전사되지 않는다.　 The pressure-sensitive adhesive uncoated portion 130 is a portion not coated with the pressure-sensitive adhesive, which is an area excluding the pressure-sensitive adhesive coating 120. When attaching to the panel P, the adhesive uncoated portion 130 is positioned on the display portion 10 of the panel (P). At this time, the adhesive uncoated portion 130 is greater than or equal to the area of the display portion 10. Specifically, 2, the area (S 10) of the area (S 130) and the display unit 10 of the adhesive non-coated portion 130 satisfies S 130 S ≥ 10. Therefore, when attached to the panel P, the screen on which the image is displayed, that is, the display portion 10 of the panel P is not in contact with the pressure-sensitive adhesive layer 125 so that the pressure-sensitive adhesive is not transferred.

따라서 본 발명에 따른 화면 보호 필름(100)은 패널(P)에 부착 시, 점착제 코팅부(120)가 프레임(20)에 부착되어 패널(P)과의 부착력이 도모되고, 점착제가 코팅되지 않은 점착제 비코팅부(130)는 패널(P)의 표시부(10)에 위치되어 점착제가 패널(P)의 표시부(10)에 전사되지 않는다. 이에 따라, 종래와 같이 점착제 전사에 따른 액정 폴(Pol) 얼룩 등의 오염 발생이 방지된다. Therefore, when the screen protection film 100 according to the present invention is attached to the panel (P), the adhesive coating portion 120 is attached to the frame 20 to promote adhesion with the panel (P), the adhesive is not coated The adhesive uncoated portion 130 is positioned on the display portion 10 of the panel P so that the adhesive is not transferred to the display portion 10 of the panel P. As a result, contamination such as liquid crystal pollen (Pol) staining due to adhesive transfer is prevented as in the related art.

한편, 상기 점착제 코팅부(120)는 전술한 바와 같이 패널(P)의 프레임(20)에 부착되는데, 이때 상기 점착제 코팅부(120)는 프레임(20)의 전면(21), 측면(22) 및/또는 배면(23)에 부착될 수 있다.　 도 2 및 도 3은 본 발명의 제1구현예로서, 점착제 코팅부(120)가 프레임(20)의 전면(21)에 부착되는 형태를 예시한 것이다.　 바람직한 구현예에 따라서, 상기 점착제 코팅부(120)는 프레임(20)의 측면(22) 및 배면(23) 중에서 선택된 하나 이상에 부착되는 것이 좋으며, 이를 도 4 내지 도 7을 참조하여 설명한다. On the other hand, the pressure-sensitive adhesive coating 120 is attached to the frame 20 of the panel (P) as described above, wherein the pressure-sensitive adhesive coating 120 is the front surface 21, side 22 of the frame 20 And / or to the back 23. 2 and 3 illustrate a form in which the pressure-sensitive adhesive coating 120 is attached to the front surface 21 of the frame 20 as a first embodiment of the present invention. According to a preferred embodiment, the pressure-sensitive adhesive coating 120 is preferably attached to at least one selected from the side 22 and the back 23 of the frame 20, which will be described with reference to FIGS.

도 4 및 도 5는 본 발명의 제2구현예에 따른 화면 보호 필름(100)을 도시한 것이고, 도 6 및 도 7은 본 발명의 제3구현예에 따른 화면 보호 필름(100)을 도시한 것이다.　 도 4 내지 도 7에는 패널(P)이 함께 도시되어 있다. 4 and 5 show a screen protection film 100 according to a second embodiment of the present invention, Figures 6 and 7 show a screen protection film 100 according to a third embodiment of the present invention. will be. 4 to 7 show panel P together.

먼저, 도 4 및 도 5를 참조하면, 상기 점착제 코팅부(120)는 프레임(20)의 측면(22)에 부착될 수 있는데, 이때 기재 필름(110)은 패널(P)의 측면(22)까지 덮을 수 있는 크기(넓이)를 갖는다.　 도 5에 도시한 바와 같이, 점착제 코팅부(120)는 점착제 비코팅부(130)와의 경계선에서 꺾어져 프레임(20)의 측면(22)에 부착된다.　 이때, 점착제 코팅부(120)의 꺾임이 용이하도록 상기 경계선에는 꺾임부(112)가 형성되는 것이 바람직하다.　 구체적으로, 점착제 코팅부(120)와 점착제 비코팅부(130)의 경계선에는 점착제 코팅부(120)의 꺾임을 용이하게 하는 꺾임부(112)가 형성되는 것이 바람직하다.　 상기 꺾임부(112)는 코팅부(120)의 꺾임을 용이하게 할 수 있는 것이면 제한되지 않는다.　 상기 꺾임부(112)는 기재 필름(110)에, 즉 코팅부(120)와 비코팅부(130)의 경계선이 위치하는 기재 필름(110)에 칼집 또는 미세 구멍의 천공에 의해 형성될 수 있다.　 다른 예를 들어, 상기 꺾임부(112)는 레이저 조사 등의 방법으로 주위보다 상기 경계선의 두께가 얇아지도록 식각되어 형성되거나, 또는 상기 경계선의 연질화 등을 통해 구현될 수 있으나, 이에 한정되는 것은 아니다. First, referring to FIGS. 4 and 5, the pressure-sensitive adhesive coating 120 may be attached to the side surface 22 of the frame 20, wherein the base film 110 has a side surface 22 of the panel P. FIG. It has a size (width) to cover up to. As shown in FIG. 5, the pressure-sensitive adhesive coating part 120 is bent at a boundary line with the pressure-sensitive adhesive uncoated part 130 and attached to the side surface 22 of the frame 20. At this time, it is preferable that the bent portion 112 is formed at the boundary line so that the pressure-sensitive adhesive coating portion 120 can be easily bent. Specifically, it is preferable that the bent portion 112 that facilitates the bending of the pressure-sensitive adhesive coating portion 120 is formed at the boundary between the pressure-sensitive adhesive coating portion 120 and the pressure-sensitive adhesive non-coating portion 130. The bending portion 112 is not limited as long as it can facilitate bending of the coating portion 120. The bent portion 112 may be formed by perforation of the cut or micro holes in the base film 110, that is, the base film 110 in which the boundary between the coating part 120 and the non-coating part 130 is located. . For example, the bent portion 112 may be formed by etching the thickness of the boundary line to be thinner than the surroundings by a method such as laser irradiation, or may be implemented by softening the boundary line, but is not limited thereto. no.

또한, 도 6 및 도 7을 참조하면, 점착제 코팅부(120)는 상기한 바와 같이 프레임(20)의 배면(23)에 부착될 수 있는데, 이때 기재 필름(110)은 패널(P)의 배면(23)까지 덮을 수 있는 크기(넓이)를 갖는다.　 이와 같이, 점착제 코팅부(120)가 프레임(20)의 배면(23)에 부착되는 경우, 도 7에 도시한 바와 같이 기재 필름(110)은 두 군데의 꺾임부(113)(114)가 형성되는 것이 바람직하다.　　 보다 구체적으로, 도 7에 도시한 바와 같이 상기 기재 필름(110)은 프레임(20)의 측면(22)에 밀착되도록 꺾어지는 제1꺾임부(114)와, 프레임(20)의 배면(23)에 밀착되도록 꺾어지는 제2꺾임부(112)가 형성되는 것이 바람직하다.　 이때, 상기 제1꺾임부(114)는 패널(P)에 부착 시, 프레임(20)의 모서리에 위치되는 지점에 형성되며, 이러한 제1꺾임부(114)에서 꺾어진 측면 밀착부(113)는 프레임(20)의 측면(22)에 밀착된다.　 또한, 상기 제2꺾임부(112)는 측면 밀착부(113)와 점착제 코팅부(120)의 사이에 형성되며, 이러한 제2꺾임부(112)에서 꺾어진 점착제 코팅부(120)는 프레임(20)의 배면(23)에 부착된다.　 상기 제1꺾임부(114) 및 제2꺾임부(112)의 형성 방법은 전술한 바와 같다.　 6 and 7, the pressure-sensitive adhesive coating 120 may be attached to the rear surface 23 of the frame 20 as described above, wherein the base film 110 is the rear surface of the panel P. It has a size (width) that can cover up to (23). As such, when the pressure-sensitive adhesive coating 120 is attached to the rear surface 23 of the frame 20, as shown in FIG. 7, the base film 110 has two bent portions 113 and 114 formed therein. It is preferable to be. More specifically, as shown in FIG. 7, the base film 110 may include a first bent portion 114 that is bent to be in close contact with the side surface 22 of the frame 20, and a rear surface 23 of the frame 20. It is preferable that the second bent portion 112 bent to be in close contact therewith. In this case, when the first bent portion 114 is attached to the panel P, the first bent portion 114 is formed at a point located at the corner of the frame 20, and the side contact portion 113 bent at the first bent portion 114 is formed. It is in close contact with the side surface 22 of the frame 20. In addition, the second bent portion 112 is formed between the side contact portion 113 and the pressure-sensitive adhesive coating portion 120, the pressure-sensitive adhesive coating portion 120 bent in the second bent portion 112 is a frame 20 It is attached to the back surface 23). The method of forming the first bent portion 114 and the second bent portion 112 is as described above.

아울러, 다른 구현예에 따라서, 상기 측면 밀착부(113)에 점착제층이 형성되어, 프레임(20)의 배면(23)에서는 물론 프레임(20)의 측면(22)에서도 부착력이 도모될 수 있다.　 구체적으로, 프레임(20)의 배면(23)에는 점착제 코팅부(120)가 부착되고, 프레임(20)의 측면(22)에는 점착제가 코팅된 측면 밀착부(113)가 부착될 수 있다. In addition, according to another embodiment, the pressure-sensitive adhesive layer is formed on the side contact portion 113, the adhesion may be promoted on the back surface 23 of the frame 20 as well as the side surface 22 of the frame 20. Specifically, the adhesive coating part 120 may be attached to the rear surface 23 of the frame 20, and the side contact part 113 coated with the adhesive may be attached to the side surface 22 of the frame 20.

도 4 내지 도 7을 참조하여 설명한 바와 같이, 점착제 코팅부(120)가 프레임(20)의 측면(22) 및/또는 배면(23)에 부착되는 경우, 이물질 혼입 방지성이 더 향상된다.　 구체적으로, 기재 필름(110)이 패널(P)의 전면(前面)을 감싼 다음, 프레임(20)의 측면(22)에 부착되거나, 패널(P)의 전면(前面)은 물론 측면(22)까지 감싼 다음, 프레임(20)의 측면(23)에 부착되어 패널(P)의 표시부(10)로 이물질이 유입되는 것을 효과적으로 방지한다.　 이때, 상기 점착제 코팅부(120)가 프레임(20)의 측면(22) 및/또는 배면(23)에 부착될 수 있도록, 상기 기재 필름(110)은 패널(P)의 측면(22) 및/또는 배면(23)까지 덮을 수 있는 크기(넓이)를 갖는다.　 As described with reference to FIGS. 4 to 7, when the adhesive coating part 120 is attached to the side surface 22 and / or the rear surface 23 of the frame 20, the foreign matter mixing prevention property is further improved. Specifically, the base film 110 surrounds the front surface of the panel P and is then attached to the side surface 22 of the frame 20, or the front surface of the panel P as well as the side surface 22. After wrapping up, it is attached to the side surface 23 of the frame 20 to effectively prevent foreign matter from entering the display unit 10 of the panel (P). In this case, the base film 110 may be attached to the side surface 22 and / or the rear surface 23 of the frame 20 so that the pressure-sensitive adhesive coating 120 may be attached to the side surface 22 and / or the panel P. Or it has a size (width) which can cover up to the back surface 23.

또한, 도 8은 본 발명의 제4구현예에 따른 화면 보호 필름(100)의 평면 구성도로서, 이는 상기한 바와 같이 점착제 코팅부(120)가 x 및 y 방향으로 기재 필름(110)의 가장자리 상하좌우측 모두에 형성된 모습을 보인 것이다.　 즉, 기재 필름(110)의 주변부를 따라 가장자리 전체 역역에 형성된 모습을 예시한 것이다. In addition, Figure 8 is a plan view of the screen protection film 100 according to a fourth embodiment of the present invention, which is the adhesive coating 120 as described above the edge of the base film 110 in the x and y direction It is shown on the top, bottom, left and right sides. That is, it illustrates the state formed in the entire area of the edge along the periphery of the base film 110.

한편, 본 발명에서 상기 기재 필름(110)은 투명, 반투명 및 불투명을 포함하며, 바람직하게는 투명 또는 반투명이다.　 또한, 기재 필름(110)은 1층 또는 2층 이상의 다층이 될 수 있다.　 구체적으로, 기재 필름(110)은 1개의 수지 필름으로 구성되거나, 2개 이상의 수지 필름이 합지된 것이어도 좋다.　 아울러, 기재 필름(110)은 1종의 수지 또는 서로 다른 2종 이상의 수지가 혼합된 복합 재질이어도 좋다.　 기재 필름(110)은 예를 들어 폴리에틸렌테레프탈레이트(PET), 폴리카보네이트(PC), 폴리염화비닐(PVC), 폴리올레핀(예를 들어 폴리에틸렌(PE), 폴리프로필렌(PP) 등) 및 이들의 공중합체 등으로부터 선택된 하나 이상의 수지를 포함하는 필름, 또는 상기 필름이 2개 이상 합지된 적층체로 구성될 수 있다.　 On the other hand, in the present invention, the base film 110 includes a transparent, translucent and opaque, preferably transparent or translucent. In addition, the base film 110 may be a single layer or a multilayer of two or more layers. Specifically, the base film 110 may be composed of one resin film, or two or more resin films may be laminated. In addition, the base film 110 may be a composite material in which one kind of resin or two or more kinds of different resins are mixed. The base film 110 is, for example, polyethylene terephthalate (PET), polycarbonate (PC), polyvinyl chloride (PVC), polyolefin (for example polyethylene (PE), polypropylene (PP), etc.) and their air It may be composed of a film comprising at least one resin selected from coalescing or the like, or a laminate in which two or more films are laminated.

상기 기재 필름(110)은 미연신 또는 연신 필름일 수 있으며, 보다 구체적인 예를 들어 PET 필름, PC 필름, PVC 필름 및 폴리올레핀 필름 등으로부터 선택된 하나 또는 2이상이 합지된 적층체로 구성될 수 있다. 이때, 상기 폴리올레핀 필름은 PE 및 PP 필름 등을 예로 들 수 있으며, 상기 PP 필름은 OPP 필름(Oriented Polypropylene film, 연신 PP 필름) 및 CPP 필름(Cast Polypropylene film, 미연신 PP 필름) 등을 포함한다. 아울러, 상기 PE 필름의 경우 복합 PE 필름이 좋으며, 구체적으로 LDPE(Low Density Polyethylene) 및 HDPE(High Density Polyethylene)가　2층 또는 3층 이상으로 적층 합지된 복합 PE 필름이 좋다.　 일례로, LDPE/HDPE/LDPE이 적층 합지된 3층 복합 PE 필름을 사용할 수 있다. The base film 110 may be an unstretched or stretched film, and may be composed of a laminate in which one or two or more selected from, for example, PET film, PC film, PVC film, and polyolefin film are laminated. In this case, the polyolefin film may be an example of PE and PP film, and the PP film includes an OPP film (Oriented Polypropylene film, stretched PP film) and CPP film (Cast Polypropylene film, unstretched PP film). In addition, the PE film is preferably a composite PE film, specifically, a low density polyethylene (LDPE) and HDPE (High Density Polyethylene) is a composite PE film laminated laminated in two or three or more layers. For example, a three-layer composite PE film in which LDPE / HDPE / LDPE is laminated and laminated may be used.

아울러, 상기 기재 필름(110)은 컬링(Curling) 현상이 없으며, 투습 방지능이 우수한 것이 좋다.　 기재 필름(110)은, 바람직하게는 필름의 강성(경도 등)을 나타내는 척도인 Stiffness(빳빳함 정도)가 우수한 것이 좋다. Stiffness가 우수한 경우, 패널(P)에 부착 시 취급성 및 밀착성이 좋은 장점이 있다. 기재 필름(110)은, 바람직하게는 Stiffness가 TD(길이 방향) 및 MD(폭 방향) 5 ~ 50gf/5mm인 것이 좋으며, 더욱 바람직하게는 15 ~ 50gf/5mm인 것이 좋다.　 상기 Stiffness 값은 통상적인 필름의 Stiffness 측정방법(예, Loop Stiffness 측정방법)에 준하는 측정치로서, 기재 필름(110)이 상기 범위의 Stiffness를 가지는 경우, 패널(P)에 부착 시 훌렁거림이 없어 취급성이 좋고, 컬링(Curling) 현상이 없어 패널(P)과의 밀착력이 좋다.　 In addition, the base film 110 does not have a curling (Curling) phenomenon, it is good that the moisture permeability excellent. The base film 110 preferably has excellent stiffness, which is a measure of the rigidity (hardness, etc.) of the film. If the stiffness is excellent, there is an advantage in handling and adhesion when attached to the panel (P). Preferably, the base film 110 has a stiffness of 5 to 50 gf / 5 mm in TD (length direction) and MD (width direction), and more preferably 15 to 50 gf / 5 mm. The stiffness value is a measurement value corresponding to a stiffness measuring method (for example, loop stiffness measuring method) of a conventional film. When the base film 110 has the stiffness in the above range, there is no fluffing when attached to the panel P. Good property, no curling phenomenon, good adhesion to the panel (P).

보다 바람직하게는, 상기 기재 필름(110)은 PC 필름, PVC 필름 및 폴리올레핀 필름(PE 필름 및 PP 필름 등)으로부터 선택되고, Stiffness가 15 ~ 50gf/5mm인 것, 더욱 바람직하게는 25 ~ 50gf/5mm인 것을 사용하면 좋다.　 이러한 필름은, PET 필름보다 가격이 저렴하고, 적정 Stiffness 값을 가져 패널(P)에 부착 시 취급성 및 밀착성이 좋으며, 내마모성 등의 물성이 우수하여 본 발명에 유용하게 적용될 수 있다. More preferably, the base film 110 is selected from PC film, PVC film and polyolefin film (PE film and PP film, etc.), the stiffness is 15 ~ 50gf / 5mm, more preferably 25 ~ 50gf / It is good to use 5mm. Such a film has a lower price than a PET film, has a proper stiffness value, has good handleability and adhesion when attached to the panel P, and has excellent physical properties such as wear resistance, and thus may be usefully applied to the present invention.

또한, 상기 점착제 코팅부(120)에 형성된 점착제층(125)은 아크릴계 점착제를 사용하는 것이 좋다.　 이때, 상기 점착제층(125)은, 점착제 조성물 전체 100중량부 기준으로 아크릴레이트 18 ~ 60중량부, 반응성 경화제 0.1 ~ 10 중량부, 및 용매 35 ~ 80중량부를 포함하는 아크릴계 점착제 조성물이 코팅되어 형성되는 것이 좋다.　 이러한 성분 및 함량으로 조성된 아크릴계 점착제는 100gf(gram force) 이상의 양호한 점착 강도를 갖는다. In addition, the pressure-sensitive adhesive layer 125 formed on the pressure-sensitive adhesive coating 120 may use an acrylic pressure-sensitive adhesive. At this time, the pressure-sensitive adhesive layer 125 is formed by coating an acrylic pressure-sensitive adhesive composition including 18 to 60 parts by weight of acrylate, 0.1 to 10 parts by weight of reactive curing agent, and 35 to 80 parts by weight of solvent based on 100 parts by weight of the entire pressure-sensitive adhesive composition. It is good to be. Acrylic pressure-sensitive adhesives composed of such components and contents have good adhesive strength of 100 gf (gram force) or more.

이때, 상기 아크릴레이트의 함량이 18중량부 미만이면 점착강도가 미미하고, 60중량부를 초과하면 조성물의 점도가 높아져 작업성 및 생산성이 떨어질 수 있다. 즉, 점도가 높아진 경우, 코팅 시 점착제 파이버(fiber)의 발생에 의해 작업 환경이 좋지 않고 코팅속도를 증가시킬 수 없어 생산성이 저하될 수 있다. 또한, 상기 반응성 경화제는, 바람직하게는 아소시아네이트계 등을 사용할 수 있으며, 이러한 반응성 경화제의 함량이 0.1중량부 미만이면 경화가 미미할 수 있고, 10중량부를 초과하면 점착 강도를 저하시킬 수 있다. 아울러, 상기 용매는 에틸아세테이트, 알코올류 및 케톤류 등의 유기 용제를 사용할 수 있으며, 이는 코팅성을 고려하여 상기 범위에서 적절히 조절한다. In this case, when the content of the acrylate is less than 18 parts by weight, the adhesive strength is insignificant, and when the content of the acrylate exceeds 60 parts by weight, the viscosity of the composition may be increased, thereby reducing workability and productivity. That is, when the viscosity is high, the work environment is not good due to the generation of pressure-sensitive adhesive fibers (fiber) during coating and the coating speed can not be increased, productivity can be reduced. In addition, the reactive curing agent may be preferably an isocyanate-based or the like, and if the content of the reactive curing agent is less than 0.1 parts by weight, the curing may be insignificant, and if it exceeds 10 parts by weight, the adhesive strength may be lowered. In addition, the solvent may be used an organic solvent such as ethyl acetate, alcohols and ketones, which is appropriately adjusted in the above range in consideration of coating properties.

바람직하게는, 상기 반응성 경화제의 경우 점착제 조성물 전체 100중량부 기준으로 0.2 ~ 5중량부로 포함된 것이 좋다. 이와 같이, 반응성 경화제가 0.2 중량부 이상으로 포함된 경우 프레임(20)에 점착제가 전사되는 것을 방지할 수 있다. 보다 바람직하게는, 상기 점착제층(125)은, 점착제 조성물 전체 100중량부 기준으로 아크릴레이트 20 ~ 60중량부, 반응성 경화제 0.2 ~ 5 중량부, 및 용매 35 ~ 80중량부를 포함하는 아크릴계 점착제 조성물이 코팅되어 형성되는 것이 좋다. 이러한 성분 및 함량으로 조성된 아크릴계 점착제는 프레임(20)에 전사되지 않아, 패널(P)로부터 필름(100)의 제거 시 깨끗한 표면성을 유지시키면서, 프레임(20)이 플라스틱재는 물론 석재나 금속재로 구성된 경우 프레임(20)과의 점착력이 우수하여 본 발명에 바람직하다.Preferably, in the case of the reactive curing agent, it is preferably included in 0.2 to 5 parts by weight based on 100 parts by weight of the entire pressure-sensitive adhesive composition. As such, when the reactive curing agent is included in an amount of 0.2 parts by weight or more, the adhesive may be prevented from being transferred to the frame 20. More preferably, the pressure-sensitive adhesive layer 125, the acrylic pressure-sensitive adhesive composition comprising 20 to 60 parts by weight of acrylate, 0.2 to 5 parts by weight of reactive curing agent, and 35 to 80 parts by weight of solvent based on 100 parts by weight of the total pressure-sensitive adhesive composition It is preferably formed by coating. The acrylic pressure-sensitive adhesive composed of such a component and content is not transferred to the frame 20, so that the frame 20 is formed of a stone or a metal material as well as a plastic material while maintaining a clean surface property when the film 100 is removed from the panel P. When configured, the adhesive force with the frame 20 is excellent and is preferable to the present invention.

이상에서 설명한 본 발명에 따른 화면 보호 필름(100)은 이물질의 혼입을 방지하여 이물질의 혼입에 따른 스크래치나 오염을 방지한다.　 특히, 상기한 바와 같이 점착제 코팅부(120)가 프레임(20)의 측면(22) 및/또는 배면(23)에 부착된 경우, 패널(P)의 표시부(10)로 이물질이 유입되는 것을 효과적으로 방지한다.　 또한, 본 발명에 따르면, 점착제가 패널(P)의 표시부(10)에, 즉 영상이 표시되는 화면에 접촉되지 않아 점착제의 전사에 따른 액정 폴(Pol) 얼룩 등의 화면 오염이 방지된다.　
Screen protection film 100 according to the present invention described above to prevent the mixing of foreign matter to prevent scratches or contamination due to the mixing of foreign matter. In particular, when the pressure-sensitive adhesive coating portion 120 is attached to the side surface 22 and / or rear surface 23 of the frame 20 as described above, it is effective to introduce foreign matter into the display portion 10 of the panel P. prevent. In addition, according to the present invention, the adhesive is not in contact with the display unit 10 of the panel P, that is, the screen on which the image is displayed, and thus screen contamination such as liquid crystal pollen due to transfer of the adhesive is prevented.

이하, 본 발명의 실시예를 예시한다.　 하기의 실시예는 본 발명의 이해를 돕도록 하기 위해 제공되는 것일 뿐, 이에 의해 본 발명의 기술적 범위가 한정되는 것은 아니다.　 하기의 실시예는 점착제의 조성에 따른 점착 강도와 전사 여부를 알아보기 위한 실험예를 예시한 것이다.
Hereinafter, embodiments of the present invention will be exemplified. The following examples are merely provided to aid the understanding of the present invention, whereby the technical scope of the present invention is not limited. The following examples illustrate the experimental example for determining the adhesive strength and the transfer or not according to the composition of the pressure-sensitive adhesive.

[실시예][Example]

하기 [표 1] 및 [표 2]에 보인 바와 같이, 각 실시예에 따라 점착제의 성분 및 함량을 달리하여 제조하였다.　 이때, [표 1]에서와 같이, 실시예 1 ~ 5의 경우에는 점착제의 주제인 아크릴레이트의 함량을 달리하였다.　 그리고 [표 2]에서와 같이, 실시예 6 ~ 10의 경우에는 반응성 경화제(이소시아네이트)의 함량을 달리하였다.
As shown in the following [Table 1] and [Table 2], it was prepared by varying the components and content of the pressure-sensitive adhesive according to each embodiment. In this case, as shown in Table 1, in Examples 1 to 5, the content of the acrylate, which is the subject of the pressure-sensitive adhesive, was changed. As shown in Table 2, in Examples 6 to 10, the content of the reactive curing agent (isocyanate) was different.

< 실시예 1 ~ 5에 따른 점착제의 조성, 단위 : 중량부 ><Composition of the pressure sensitive adhesive according to Examples 1 to 5, unit: parts by weight> 비 고
Remarks
실시예 1Example 1 실시예 2Example 2 실시예 3Example 3 실시예 4Example 4 실시예 5Example 5 아크릴레이트
Acrylate
1515 2020 3030 4040 5050 반응성경화제
(이소시아네이트계)Reactive curing agent
(Isocyanate) 1One 1One 1One 1One 1One 에틸아세테이트
Ethyl acetate
8484 7979 6969 5959 4949 합 계
Sum
100100 100100 100100 100100 100100

< 실시예 6 ~ 10에 따른 점착제의 조성, 단위 : 중량부 > <Composition of the pressure sensitive adhesive according to Examples 6 to 10, unit: parts by weight> 비 고
Remarks
실시예 6Example 6 실시예 7Example 7 실시예 8Example 8 실시예 9Example 9 실시예 10Example 10 아크릴레이트
Acrylate
3030 3030 3030 3030 3030 반응성경화제
(이소시아네이트계)Reactive curing agent
(Isocyanate) 0.10.1 0.20.2 1One 33 55 에틸아세테이트
Ethyl acetate
69.969.9 69.869.8 6969 6767 6565 합 계
Sum
100100 100100 100100 100100 100100

상기 각 실시예에 따른 점착제에 대해 점착 강도와 점착제 전사 여부를 평가하였다.　 점착 강도는 강도 시험기를 이용하여 180도 박리각으로 측정하였으며, 점착제 전사 여부는 Al 금속판에 대한 전사 여부를 관찰하여 평가하였다.　 이상의 결과를 하기 [표 3]에 나타내었다.
The pressure-sensitive adhesive strength and whether or not the pressure-sensitive adhesive transfer was evaluated for the pressure-sensitive adhesives according to the above Examples. Adhesive strength was measured at a 180 degree peel angle using a strength tester, and the adhesive transfer was evaluated by observing the transfer to the Al metal plate. The above results are shown in the following [Table 3].

< 점착 강도 및 점착제 전사 여부 평가 결과 ><Evaluation result of adhesive strength and adhesive transfer> 비 고Remarks 실시예　Example 1One 22 33 44 55 66 77 88 99 1010 점착 강도
(gf)Adhesive strength
(gf) 3030 140140 350350 470470 600600 850850 680680 350350 210210 110110 점착제　
전사 여부adhesive
Warrior XX XX XX XX XX OO XX XX XX XX

상기 [표 3]에 나타난 바와 같이, 실시예 1 ~ 5에서 점착 주제인 아크릴레이트 함량이 증가할수록 점착 강도가 증가함을 알 수 있다.　 그리고 20중량부 이상에서 100gf 이상의 점착 강도를 가짐을 알 수 있다.　 아울러, 아크릴레이트의 함량이 5너무 높은 경우 점도 증가로 코팅성이 떨어짐을 알 수 있었다.　 또한, 실시예 6 ~ 10에서 알 수 있듯이, 반응성 경화제의 함량이 증가할수록 점착 강도가 떨어짐을 알 수 있다.　 그리고 실시예 6에서와 같이 반응성 경화제의 함량이 극히 낮을 경우 점착 주제인 아크릴레이트 미반응분 발생에 의해 점착 강도는 증가하지만, 이로 인하여 점착제의 전사가 발생되었다.　 아울러, 반응성 경화제의 함량이 5중량부를 초과하여 너무 많은 경우, 점착 강도가 100gf 이하로 떨어질 수 있음을 알 수 있었다.　 As shown in Table 3, it can be seen that in Examples 1 to 5, the adhesive strength increases as the acrylate content of the adhesive main ingredient increases. And it can be seen that the adhesive strength of 100gf or more at 20 parts by weight or more. In addition, it was found that when the content of the acrylate is too high, the coating property is reduced due to the increase in viscosity. In addition, as can be seen in Examples 6 to 10, it can be seen that the adhesive strength decreases as the content of the reactive curing agent increases. And when the content of the reactive curing agent is extremely low as in Example 6, the adhesive strength is increased by the generation of acrylate unreacted powder, which is the adhesive subject, but this caused the transfer of the adhesive. In addition, it was found that when the content of the reactive curing agent is more than 5 parts by weight, the adhesive strength may drop below 100 gf.

따라서 양호한 점착 강도를 가지면서 점착제 전사가 없도록 하기 위해서는, 점착 주제(아크릴레이트)의 경우에는 20중량부 이상, 반응성 경화제의 경우에는 0.2중량부 이상의 범위에서 조성하는 것이 적합함을 알 수 있다.
Therefore, in order to prevent adhesive transfer while having favorable adhesive strength, it can be seen that it is suitable to make it in the range of 20 weight part or more in the case of an adhesive main body (acrylate), and 0.2 weight part or more in the case of a reactive hardening | curing agent.

10 : 표시부 20 : 프레임
100 : 화면 보호 필름 110 : 기재 필름
112, 114 : 꺾임부 120 : 점착제 코팅부
125 : 점착제층 130 : 점착제 비코팅부
P : 패널 10: display unit 20: frame
100: screen protection film 110: base film
112, 114: bent portion 120: pressure-sensitive adhesive coating
125: pressure-sensitive adhesive layer 130: pressure-sensitive adhesive uncoated portion
P: Panel

Claims (9)

삭제delete 표시부와 프레임을 가지는 디스플레이 패널의 화면 보호 필름으로서,
기재 필름;
상기 기재 필름 상에 형성된 점착제 코팅부와 점착제 비코팅부를 포함하되,
상기 점착제 코팅부는 기재 필름의 가장자리에 형성되어 디스플레이 패널의 프레임에 부착되며,
상기 점착제 비코팅부는 디스플레이 패널의 표시부에 위치되고, 상기 표시부의 면적보다 크거나 같으며,
상기 점착제 코팅부는 프레임의 측면 및 배면 중에서 선택된 하나 이상에 부착되고,
상기 기재 필름은, Stiffness가 5 ~ 50gf/5mm인 것을 특징으로 하는 디스플레이 패널의 화면 보호 필름.
As a screen protection film of the display panel which has a display part and a frame,
A base film;
Including the pressure-sensitive adhesive coating and pressure-sensitive adhesive uncoated portion formed on the base film,
The adhesive coating is formed on the edge of the base film is attached to the frame of the display panel,
The pressure-sensitive adhesive uncoated portion is positioned on a display portion of the display panel, and is greater than or equal to an area of the display portion.
The adhesive coating is attached to at least one selected from the side and back of the frame,
The base film has a stiffness of 5 ~ 50gf / 5mm, the screen protection film of the display panel.
제2항에 있어서,
상기 점착제 코팅부와 점착제 비코팅부의 경계선에 꺾임부가 형성된 것을 특징으로 하는 디스플레이 패널의 화면 보호 필름.
The method of claim 2,
Screen protective film of the display panel, characterized in that the bent portion formed on the boundary line of the pressure-sensitive adhesive coating and the pressure-sensitive adhesive uncoated portion.
제2항에 있어서,
상기 기재 필름은 프레임의 측면에 밀착되도록 꺾어지는 제1꺾임부와, 프레임의 배면에 밀착되도록 꺾어지는 제2꺾임부가 형성되고,
상기 점착제 코팅부는 제2꺾임부에서 꺾어져 프레임의 배면에 부착되는 것을 특징으로 하는 디스플레이 패널의 화면 보호 필름.
The method of claim 2,
The base film is formed with a first bent portion to be in close contact with the side of the frame, and a second bent portion is bent in close contact with the back of the frame,
The pressure-sensitive adhesive coating is bent at the second bent portion is a screen protection film of the display panel, characterized in that attached to the back of the frame.
제2항 내지 제4항 중 어느 하나의 항에 있어서,
상기 기재 필름은 폴리에틸렌테레프탈레이트(PET), 폴리카보네이트(PC), 폴리염화비닐(PVC) 및 폴리올레핀 필름으로부터 선택된 하나 또는 2 이상의 적층체인 것을 특징으로 하는 디스플레이 패널의 화면 보호 필름.
The method according to any one of claims 2 to 4,
The base film is one or two or more laminates selected from polyethylene terephthalate (PET), polycarbonate (PC), polyvinyl chloride (PVC) and polyolefin film.
제2항 내지 제4항 중 어느 하나의 항에 있어서,
상기 기재 필름은, Stiffness가 15 ~ 50gf/5mm인 것을 특징으로 하는 디스플레이 패널의 화면 보호 필름.
The method according to any one of claims 2 to 4,
The base film has a stiffness of 15 ~ 50gf / 5mm, the screen protection film of the display panel.
제2항 내지 제4항 중 어느 하나의 항에 있어서,
상기 기재 필름은 폴리카보네이트(PC), 폴리염화비닐(PVC) 및 폴리올레핀 필름으로부터 선택되고, Stiffness가 15 ~ 50gf/5mm인 것을 특징으로 하는 디스플레이 패널의 화면 보호 필름.
The method according to any one of claims 2 to 4,
The base film is selected from polycarbonate (PC), polyvinyl chloride (PVC) and polyolefin film, the screen protection film of a display panel, characterized in that the stiffness is 15 ~ 50gf / 5mm.
제2항 내지 제4항 중 어느 하나의 항에 있어서,
상기 점착제 코팅부는, 점착제 조성물 전체 100중량부 기준으로 아크릴레이트 18 ~ 60중량부, 반응성 경화제 0.1 ~ 10중량부, 및 용매 35 ~ 80중량부를 포함하는 아크릴계 점착제 조성물이 코팅되어 형성된 것을 특징으로 하는 디스플레이 패널의 화면 보호 필름.
The method according to any one of claims 2 to 4,
The pressure-sensitive adhesive coating is a display, characterized in that formed by coating an acrylic pressure-sensitive adhesive composition comprising 18 to 60 parts by weight of acrylate, 0.1 to 10 parts by weight of reactive curing agent, and 35 to 80 parts by weight of solvent based on 100 parts by weight of the total pressure-sensitive adhesive composition. Screen protection film of the panel.
제2항 내지 제4항 중 어느 하나의 항에 있어서,
상기 점착제 코팅부는, 점착제 조성물 전체 100중량부 기준으로 아크릴레이트 20 ~ 60중량부, 반응성 경화제 0.2 ~ 5 중량부, 및 용매 35 ~ 80중량부를 포함하는 아크릴계 점착제 조성물이 코팅되어 형성된 것을 특징으로 하는 디스플레이 패널의 화면 보호 필름. The method according to any one of claims 2 to 4,
The pressure-sensitive adhesive coating is a display, characterized in that formed by coating an acrylic pressure-sensitive adhesive composition comprising 20 to 60 parts by weight of acrylate, 0.2 to 5 parts by weight of reactive curing agent, and 35 to 80 parts by weight of solvent based on 100 parts by weight of the pressure-sensitive adhesive composition. Screen protection film of the panel.
KR1020110023917A 2011-03-17 2011-03-17 Film for protecting screen of display panel KR101273194B1 (en)