JP3090774U - Optical filter for display screen - Google Patents
Optical filter for display screenInfo
- Publication number
- JP3090774U JP3090774U JP2002003649U JP2002003649U JP3090774U JP 3090774 U JP3090774 U JP 3090774U JP 2002003649 U JP2002003649 U JP 2002003649U JP 2002003649 U JP2002003649 U JP 2002003649U JP 3090774 U JP3090774 U JP 3090774U
- Authority
- JP
- Japan
- Prior art keywords
- film
- adhesive layer
- optical filter
- display screen
- adhesive
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Lifetime
Abstract
(57)【要約】
【課題】 ゴムフィルム等からなる自己粘着層を
備え、かつ光反射性その他の機能を備えた光学フィルム
であって、液晶パネル等の表示画面に対し自己粘着層の
自己粘着力で容易に貼り付けることができ、しかも連続
法で経済的に生産することが可能な光学フィルムを得
る。
【解決手段】 機能性フィルム１１の片面に第１粘着
層１２、支持フィルム１４および第２粘着層１５が順に
積層された積層体で光学フィルムをを構成し、第１粘着
層１２の初期粘着力を２０００ｍＮ／２５mm以上、第２
粘着層表面の初期粘着力を２９〜１５００ｍＮ／２５m
m、積層体の全光線透過率を４０％以上、ヘーズ値を３
０％以下に設定する。
PROBLEM TO BE SOLVED: To provide an optical film having a self-adhesive layer made of a rubber film or the like and having a light reflecting property and other functions, and the self-adhesive of the self-adhesive layer to a display screen such as a liquid crystal panel. An optical film that can be easily attached by force and economically produced by a continuous method is obtained. SOLUTION: An optical film is constituted by a laminate in which a first adhesive layer 12, a support film 14, and a second adhesive layer 15 are sequentially laminated on one surface of a functional film 11, and an initial adhesive force of the first adhesive layer 12 is provided. Over 2000mN / 25mm, 2nd
The initial adhesive strength of the adhesive layer surface is 29 to 1500 mN / 25 m
m, the total light transmittance of the laminate is 40% or more, and the haze value is 3
Set to 0% or less.
Description
【０００１】[0001]
この考案は、表示画面用光学フィルターに関し、ＣＲＴディスプレイ、液晶ディ スプレイ、プラズマディスプレイその他の各種表示装置の表示画面に対して着脱 自在で、その取付け時に表示画面を保護すると共に、表示画面に各種の機能を付 加することが可能な光学フィルターを提供する。 The present invention relates to an optical filter for a display screen, which is detachable from a display screen of a CRT display, a liquid crystal display, a plasma display, and other various display devices. Provide an optical filter to which functions can be added.
【０００２】[0002]
パソコンやコピー機、ファクシミリ等のＯＡ機器の分野に限らず、テレビや時計 、電話、工場内の制御装置その他の広い分野でＣＲＴディスプレイ、液晶ディス プレイ、プラズマ・ディスプレイ等、各種の表示装置が使用されているが、その 表示画面の損傷や汚れを防いだり、映り込みや光反射を防いだりするためのフィ ルムが表面保護用フィルムや光学フィルターの名称で市販されている。なお、表 面保護用フィルムと光学フィルターとの区別は、必ずしも明確ではないが、一般 的には、光学フィルターは表示画面の単なる保護だけでなく、映り込みや光反射 の防止その他の機能性付与も目的とし、かつ総厚みが大きい点で単なる表面保護 用フィルムと区別されている。 Various display devices such as CRT displays, liquid crystal displays, and plasma displays are used not only in the field of OA equipment such as personal computers, copiers, and facsimile machines, but also in TVs, watches, telephones, factory control devices, and other wide fields. However, films for preventing the display screen from being damaged or stained, and preventing reflection and light reflection are commercially available under the names of surface protection films and optical filters. The distinction between a surface protective film and an optical filter is not always clear, but in general, an optical filter not only protects the display screen, but also prevents reflection and reflection of light and provides other functions. It is also distinguished from a mere surface protection film in that it has a large total thickness.
【０００３】 上記の表面保護用フィルムとしては、基材フィルムの少なくとも片面にゴムフィ ルムを積層し、ゴムフィルム側を自己粘着力で表示画面に粘着させるようにした ものが知られている（特開２０００−５６６９４号公報、特開２００１−８３８ ８６号公報および実用新案登録第３０７２３６１号公報等参照）。これらの表面 保護用フィルムは、必要に応じて容易に剥離することが可能で、剥離跡に汚れが 残ることもなく、リペア性に優れている。そして、この場合は、基材フィルム側 が表面に向けられるが、従来のプラスチックフィルム単体に比べてクッション性 を有するため、汚れや傷が付き難くなり、触感もソフトに改善される。As the above-mentioned surface protection film, there is known a film in which a rubber film is laminated on at least one surface of a base film, and the rubber film side is adhered to a display screen by a self-adhesive force (Japanese Patent Laid-Open Publication No. H11-163873). 2000-56694, JP-A-2001-83886 and Utility Model Registration No. 3072361). These surface protection films can be easily peeled off as needed, and there is no stain left on the peeling marks, and they have excellent repairability. In this case, the base film side is directed to the surface, but since it has cushioning properties as compared with a conventional plastic film alone, dirt and scratches are less likely to occur, and the touch feeling is also softly improved.
【０００４】 一方、光学フィルターは、総厚みが２５０μｍ以上で、表面保護用フィルムより も厚いため、表面保護用フィルムよりも表示画面の損傷や汚れを防ぐ保護機能お よび取扱性に優れている。したがって、光学フィルターは、テレビやパソコン等 の比較的大型の表示装置に使用され、表面保護用フィルムは、携帯電話等の比較 的小型の表示装置に使用される傾向になっている。On the other hand, the optical filter has a total thickness of 250 μm or more and is thicker than a surface protection film, and thus has an excellent protection function for preventing a display screen from being damaged or stained and a better handleability than a surface protection film. Therefore, optical filters are being used for relatively large display devices such as televisions and personal computers, and surface protection films are being used for relatively small display devices such as mobile phones.
【０００５】 しかしながら、従来の光学フィルターは、表示画面に対する固定手段として、粘 着テープや固定治具を用いており、前者の場合は剥離が困難で、剥離した際に粘 着テープの跡が残り、後者の場合は固定治具のためのスペースを必要とするとい う問題があった。そして、光学フィルターは、前記の表面保護用フィルムのよう に自己粘着層を設けようとしても、基材フィルムの総厚みが大きくてロール状で 巻き取ることができないため、基材フィルムをロール状で入手することができず 、そのため光学フィルターを連続法で生産することができず、経済的に不利にな っていた。However, the conventional optical filter uses an adhesive tape or a fixing jig as a fixing means for the display screen. In the former case, it is difficult to peel off the adhesive tape, and when the adhesive is peeled off, a trace of the adhesive tape remains. However, in the latter case, there is a problem that a space for a fixing jig is required. And, even if the optical filter attempts to provide a self-adhesive layer like the above-mentioned surface protection film, the total thickness of the base film is too large to be wound up in a roll shape. They were not available, which made it impossible to produce optical filters in a continuous process, which was economically disadvantageous.
【０００６】[0006]
この考案は、上記のゴムフィルムからなる自己粘着層を備えた光学フィルムであ って、しかも連続法で経済的に生産することが可能な光学フィルムを提供するも のである。 The present invention provides an optical film having a self-adhesive layer made of the above-mentioned rubber film, which can be economically produced by a continuous method.
【０００７】[0007]
この考案に係る表示画面用光学フィルターは、機能性フィルムの片面に第１粘着 層、支持フィルムおよび第２粘着層が順に積層された積層体からなり、上記第１ 粘着層の初期粘着力が２０００ｍＮ／２５mm以上、上記第２粘着層表面の初期粘 着力が２９〜１５００ｍＮ／２５mm、上記積層体の全光線透過率が４０％以上、 ヘーズ値が３０％以下であることを特徴とする。 The optical filter for a display screen according to the present invention comprises a laminate in which a first adhesive layer, a support film, and a second adhesive layer are sequentially laminated on one surface of a functional film, and the first adhesive layer has an initial adhesive force of 2,000 mN. / 25 mm or more, the initial adhesive force of the surface of the second adhesive layer is 29 to 1500 mN / 25 mm, the total light transmittance of the laminate is 40% or more, and the haze value is 30% or less.
【０００８】 上記の表示画面用光学フィルターは、第１粘着層の初期粘着力が２０００ｍＮ／ ２５mm以上に設定されているため、この光学フィルターを表示画面に対して着脱 する際および使用中に機能性フィルムが支持フィルムから容易に剥離されること がなく、一体性を保持する。In the above-mentioned optical filter for a display screen, the initial adhesive strength of the first adhesive layer is set to 2000 mN / 25 mm or more. The film is not easily peeled from the support film and retains its integrity.
【０００９】 一方、上記支持フィルムの反対側に積層された第２粘着層の表面は、その初期粘 着力が２９〜１５００ｍＮ／２５mmに設定され、自己粘着層を構成するので、表 示画面に対して接触させることにより、上記の光学フィルターを容易に固定する ことができ、しかもいったん固定した光学フィルターを交換したい等の理由で外 す場合は、その一端から手で容易に剥離することができ、その剥離跡に粘着剤等 が付着して表示画面が汚れることもなく、施工性およびリペア性に優れている。 ただし、上記の初期粘着力が２９ｍＮ／２５mm未満では、使用中に脱落し易く、 反対に１５００ｍＮ／２５mmを超えると、上記の剥離が困難になる。なお、上記 の第２粘着層には、易剥離性のカバーフィルムを積層しておき、使用の際に剥離 することが好ましい。On the other hand, the surface of the second adhesive layer laminated on the opposite side of the support film has an initial adhesive force of 29 to 1500 mN / 25 mm and constitutes a self-adhesive layer. The above optical filter can be easily fixed by contacting the optical filter.In addition, when the optical filter once fixed is removed for reasons such as replacement, it can be easily peeled off from one end by hand. The display screen is not stained by the adhesion of adhesive or the like to the peeling marks, and the workability and repairability are excellent. However, if the initial adhesive strength is less than 29 mN / 25 mm, the adhesive tends to fall off during use, and if it exceeds 1500 mN / 25 mm, the peeling becomes difficult. In addition, it is preferable that an easily peelable cover film is laminated on the second adhesive layer, and the second adhesive layer is peeled off at the time of use.
【００１０】 また、上記の光学フィルターは、全光線透過率が４０％以上、ヘーズ値が３０％ 以下であるため、その使用中は表示画面の画像の視認性が高く、鮮明度は光学フ ィルターの貼着前と同程度以上となる。ただし、全光線透過率が４０％未満であ ったり、ヘーズ値が３０％を超えたりした場合は、画像の視認性が低下する。な お、上記の全光線透過率およびヘーズ値は、機能性フィルム、支持フィルムおよ び第１、第２の粘着層に透明性の高い材料を選び、光線を遮る添加剤を添加した り、機能性フィルムの表面に光線調整層を積層する等の手段で付与することがで きる。In addition, the above optical filter has a total light transmittance of 40% or more and a haze value of 30% or less, so that the visibility of an image on a display screen is high during use and the sharpness of the optical filter is high. Before attachment. However, if the total light transmittance is less than 40% or the haze value exceeds 30%, the visibility of the image is reduced. The above total light transmittance and haze value can be determined by selecting a highly transparent material for the functional film, the support film, and the first and second adhesive layers, and adding an additive that blocks light, It can be provided by means such as laminating a light beam adjusting layer on the surface of the functional film.
【００１１】 そして、上記の光学フィルターは、機能性フィルム、第１粘着層、支持フィルム および第２粘着層の４層構造であり、従来の単なる表面保護用フィルムが基材フ ィルムおよび自己粘着層の２層構造であるのと比べると、従来の基材フィルムに 相当する部分が機能性フィルム、第１粘着層および支持フィルムの３層で構成さ れるため、機能性フィルムおよび支持フィルムの合計厚みを従来の基材のフィル ムの２倍程度にしても、個々の厚みは従来の基材フィルムと同程度となる。した がって、機能性フィルムおよび支持フィルムをそれぞれロール状で入手すること ができ、単なる表面保護用フィルムよりも厚みの大きい光学フィルターを連続方 式で生産することが可能になる。The optical filter has a four-layer structure of a functional film, a first adhesive layer, a support film, and a second adhesive layer. A conventional simple surface protection film is composed of a base film and a self-adhesive layer. Compared to the two-layer structure, the portion corresponding to the conventional base film is composed of the functional film, the first adhesive layer and the support film, and thus the total thickness of the functional film and the support film Even if the thickness is about twice as large as the film of the conventional base material, the individual thickness is almost the same as that of the conventional base film. Therefore, the functional film and the support film can be obtained in the form of a roll, respectively, and it becomes possible to produce an optical filter thicker than a mere surface protection film in a continuous manner.
【００１２】 上記機能性フィルムの材質は、強度に優れ、光学フィルターを構成した状態で前 記の全光線透過率およびヘーズ値が得られるものであれば、任意であり、例えば ポリエステル、ポリアミド、ポリオレフィン、ポリカーボネート、アクリル樹脂 、フッ素樹脂、トリアセチルセルローズ樹脂等があげられる。特に、ポリエステ ルフィルムは、透明性、寸法安定性および経済性の点で好適である。そして、こ の機能性フィルムは、単層構造に限るものではなく、前記の支持フィルムとは別 の基材フィルムで裏打ちされた２層構造とすることもできる。The material of the functional film is arbitrary as long as it is excellent in strength and can obtain the above-mentioned total light transmittance and haze value in a state where the optical filter is formed. Examples of the material include polyester, polyamide, and polyolefin. , Polycarbonate, acrylic resin, fluorine resin, triacetyl cellulose resin and the like. In particular, polyester films are suitable in terms of transparency, dimensional stability and economy. The functional film is not limited to a single-layer structure, and may have a two-layer structure lined with a base film different from the above-described support film.
【００１３】 上記の機能性フィルムは、光学フィルターとしての価値を高めるための機能を具 備する必要があり、かかる機能としては、表示画面の単なる表面保護以外に、鉛 筆硬度で１Ｈ以上の耐スクラッチ性、または映り込み防止性、光線の反射防止性 、透明導電性、抗菌性および赤外線遮断性があげられ、本考案の機能性フィルム は、これらの機能のいずれか１以上を具備することが好ましい。なお、これらの 機能は、機能性フィルムの表面に上記の機能を有する機能剤を塗工法等のウエッ ト法または蒸着法（スパッタリングを含む）等のドライ法で積層したり、上記フ ィルム中に機能剤を含有したりする等、任意の手段で付与することができる。The above-mentioned functional film needs to be provided with a function for enhancing the value as an optical filter. Such a function includes, in addition to mere surface protection of a display screen, a resistance of 1H or more in lead brush hardness. Scratch property, anti-reflection property, anti-reflection property of light rays, transparent conductivity, antibacterial property and infrared ray blocking property are given, and the functional film of the present invention may have at least one of these functions. preferable. These functions can be achieved by laminating a functional agent having the above functions on the surface of the functional film by a wet method such as a coating method or a dry method such as a vapor deposition method (including sputtering), or in the above-mentioned film. It can be provided by any means such as containing a functional agent.
【００１４】 上記機能性フィルムの厚みは、特に限定されないが、機能性フィルムと支持フィ ルムとの合計厚みが２５０〜１０００μｍになることが取扱い性の点で好ましい 。ただし、機能性フィルムと支持フィルムの厚みの差が大きいと、光学フィルタ ーにカールが発生するので、機能性フィルムの厚みを１２５〜５００μｍに設定 し、支持フィルムとの厚み差を小さくすることが好ましい。The thickness of the functional film is not particularly limited, but the total thickness of the functional film and the supporting film is preferably 250 to 1000 μm from the viewpoint of handleability. However, if the difference in thickness between the functional film and the support film is large, curling occurs in the optical filter. Therefore, the thickness of the functional film should be set to 125 to 500 μm to reduce the difference in thickness from the support film. preferable.
【００１５】 この考案で用いる支持フィルムは、光線透過率や強度に優れたものであって、光 学フィルターを構成した状態で光線透過率とヘーズ値が前記の要件を満たすもの であれば、特に限定されない。例えば、ポリエステル、ポリアミド、ポリオレフ ィン、ポリカーボネート、アクリル系樹脂、フッ素樹脂、トリアセチルセルロー ズ樹脂等からなるフィルムが使用可能である。特に、ポリエステルフィルムは、 透明性、寸法安定性および経済性等の点で好適である。なお、厚みは、前記の機 能性フィルムと同じ理由で１２５〜５００μｍが好ましい。The support film used in the present invention is excellent in light transmittance and strength, as long as the light transmittance and the haze value satisfy the above requirements in the state where the optical filter is formed. Not limited. For example, a film made of polyester, polyamide, polyolefin, polycarbonate, acrylic resin, fluororesin, triacetyl cellulose resin, or the like can be used. In particular, a polyester film is suitable in terms of transparency, dimensional stability, economy, and the like. In addition, the thickness is preferably 125 to 500 μm for the same reason as the above-mentioned functional film.
【００１６】 前記の第１粘着層は、初期粘着力が２０００ｍＮ／２５mm以上であり、かつ光線 透過率に優れ、光学フィルターを構成した状態で光線透過率４０％以上およびヘ ーズ値３０％以下を満足するものであればよく、例えばアクリル系やシリコーン 系のものがあげられる。なお、この第１粘着層は、ロールコーター、リバースコ ーター、コンマコーター、リップコーター、ダイコーター等を用いた塗工によっ て積層することができ、その厚みは、上記の初期粘着力が得られる限り任意であ り、一般的には１〜１００μｍ、好ましくは５〜５０μｍに設定される。The first adhesive layer has an initial adhesive force of 2,000 mN / 25 mm or more, has excellent light transmittance, and has a light transmittance of 40% or more and a haze value of 30% or less when an optical filter is formed. Any material that satisfies the above conditions may be used, for example, acrylic or silicone-based materials. The first adhesive layer can be laminated by coating using a roll coater, a reverse coater, a comma coater, a lip coater, a die coater, or the like, and the thickness is such that the above initial adhesive strength is obtained. As long as it is arbitrary, it is generally set to 1 to 100 μm, preferably 5 to 50 μm.
【００１７】 また、第２粘着層は、支持フィルム表面に積層されるが、その積層後の表面にお ける初期粘着力が前記の要件を満たし、光学フィルターを構成した状態で、光線 透過率およびヘーズ値が前記の要件を満たすものであれば、特に限定されない。 例えば、特開２０００−５６６９４号公報や特開２００１−８３８８６号公報に 記載されたゴムフィルムおよび実用新案登録第３０７２３６１号公報に記載され た再剥離性の粘着剤が使用可能である。この第２粘着層は、第１粘着層と同様の 塗工によって積層することができ、その厚みは、上記の初期粘着力が得られる限 り、任意であり、一般的には１〜１００μｍ、好ましくは５〜５０μｍに設定さ れる。Further, the second adhesive layer is laminated on the surface of the support film, and the initial adhesive force on the surface after the lamination satisfies the requirements described above, and the light transmittance and the light transmittance of the optical filter are formed. There is no particular limitation as long as the haze value satisfies the above requirements. For example, a rubber film described in JP-A-2000-56694 or JP-A-2001-83886 and a removable adhesive described in Utility Model Registration No. 3072361 can be used. The second pressure-sensitive adhesive layer can be laminated by the same coating as the first pressure-sensitive adhesive layer, and its thickness is arbitrary as long as the above-mentioned initial pressure-sensitive adhesive force is obtained. Preferably, it is set to 5 to 50 μm.
【００１８】 この考案に係る表示画面用光学フィルターは、支持フィルムの片面に第２粘着層 およびカバーフィルムを順に積層し、次いで上記支持フィルムの他面に第１粘着 層および機能性フィルムを順に積層して生産することができる。また、上記のと おり支持フィルムの片面に第２粘着層およびカバーフィルムを順に積層する一方 、機能性フィルムの片面に第１粘着層を積層し、しかるのち両者を重ねて生産す ることができる。また、上記支持フィルムの片面に第１粘着層を、他面に第２粘 着層をそれぞれ積層し、しかるのち第１粘着層に機能性フィルムを積層すること もできる。In the optical filter for a display screen according to the present invention, the second adhesive layer and the cover film are sequentially laminated on one surface of the support film, and then the first adhesive layer and the functional film are sequentially laminated on the other surface of the support film. Can be produced. In addition, as described above, the second adhesive layer and the cover film are sequentially laminated on one side of the support film, while the first adhesive layer is laminated on one side of the functional film, and thereafter, both can be laminated and produced. . Further, the first adhesive layer may be laminated on one side of the support film and the second adhesive layer may be laminated on the other side, and then the functional film may be laminated on the first adhesive layer.
【００１９】[0019]
実施形態１ 図１において、１０は表示画面用光学フィルターであり、機能性フィルム１１の 下面に第１粘着層１２を介して支持フィルム１４が接着され、この支持フィルム １４の下面に第２粘着層１５が積層され、この第２粘着層１５の下面にカバーフ ィルム１６が着脱自在に積層されている。なお、機能性フィルム１１は、図２に 示すように、基材フィルム１１ａの上面に耐スクラッチ性のハード加工層１１ｂ を複合して作ることができる。 Embodiment 1 In FIG. 1, reference numeral 10 denotes an optical filter for a display screen. A support film 14 is adhered to a lower surface of a functional film 11 via a first adhesive layer 12, and a second adhesive layer is attached to a lower surface of the support film 14. The cover film 16 is detachably laminated on the lower surface of the second adhesive layer 15. In addition, as shown in FIG. 2, the functional film 11 can be made by combining a scratch-resistant hard working layer 11b on the upper surface of the base film 11a.
【００２０】 上記の機能性フィルム１１は、合成樹脂、好ましくはポリエステルからなる厚み ２５〜５００μｍの透明フィルムであり、前記の機能を備えている。機能性フィ ルム１１の下面には、透明な粘着剤を塗布、乾燥して厚み１〜１００μｍ、好ま しくは５〜５０μｍ、表面の初期粘着力２０００ｍＮ／２５mm以上の第１粘着層 １２を形成し、この第１粘着層１２の表面を、好ましくは離型フィルム１３（図 ２参照）で保護する。The functional film 11 is a transparent film made of a synthetic resin, preferably polyester and having a thickness of 25 to 500 μm, and has the functions described above. On the lower surface of the functional film 11, a transparent adhesive is applied and dried to form a first adhesive layer 12 having a thickness of 1 to 100 µm, preferably 5 to 50 µm, and an initial surface adhesive force of 2000 mN / 25 mm or more. The surface of the first adhesive layer 12 is preferably protected by a release film 13 (see FIG. 2).
【００２１】 一方、支持フィルム１４は、合成樹脂、好ましくはポリエステルからなる厚みが １２５〜５００μｍの透明フィルムであり、その両面にあらかじめ易接着性処理 が施されている。そして、その片面（図２の下面）に接着性改良剤が配合された 透明なゴムまたは樹脂からなる厚み１〜１００μｍ、好ましくは５〜５０μｍの 第２粘着層１５を積層し、その表面にカバーフィルム１６を積層する。このカバ ーフィルム１６は、片面が易剥離性処理された平滑な厚み３〜１２５μｍのポリ エステルフィルムであり、その易剥離性処理をされた平滑面が上記の第２粘着層 １５に重ねられる。On the other hand, the support film 14 is a transparent film made of a synthetic resin, preferably polyester and having a thickness of 125 to 500 μm, and both surfaces of which are previously subjected to an easy adhesion treatment. Then, on one surface (the lower surface in FIG. 2), a second adhesive layer 15 having a thickness of 1 to 100 μm, preferably 5 to 50 μm, made of a transparent rubber or resin mixed with an adhesiveness improving agent is laminated, and a cover is formed on the surface. The film 16 is laminated. The cover film 16 is a smooth polyester film having a smooth thickness of 3 to 125 μm on one side, and the smooth surface subjected to the easy release is laminated on the second adhesive layer 15.
【００２２】 そして、前記の機能性フィルム１１、第１粘着層１２および離型フィルム１３か らなる積層体の離型フィルム１３を剥離しながら、第１粘着層１２を、上記の支 持フィルム１４、第２粘着層１５およびカバーフィルム１６からなる積層体の支 持フィルム１４に重ねて挟圧することにより、図１に示す機能性フィルム１１、 第１粘着層１２、支持フィルム１４、第２粘着層１５およびカバーフィルム１６ からなる表示画面用光学フィルター１０を得る。Then, while peeling off the release film 13 of the laminate composed of the functional film 11, the first adhesive layer 12 and the release film 13, the first adhesive layer 12 is attached to the support film 14. The functional film 11, the first adhesive layer 12, the support film 14, and the second adhesive layer shown in FIG. 1 are sandwiched and pressed on the support film 14 of the laminate including the second adhesive layer 15 and the cover film 16. An optical filter 10 for a display screen comprising a cover film 15 and a cover film 16 is obtained.
【００２３】 上記の表示画面用光学フィルター１０は、カバーフィルム１６を剥離して第２粘 着層１５を液晶パネル等の表示画面に合わせると、第２粘着層１５の自己粘着力 で貼付けることができる。この第２粘着層１５の表面は、初期粘着力が適度にコ ントロールされているため、表示画面に貼り付ける際の施工性が良好で、空気を 介在させずに、きれいに貼着でき、仮に空気が入っても、貼着が自己粘着性によ るので、時間の経過にしたがって上記の空気が排出される。また、貼着後の剥離 性も良好であり、かつ剥離跡に粘着剤による汚れが残ることもない。そして、こ の貼着と剥離は、繰返しが可能であり、リペアー性に優れている。一方、第１粘 着層１２は、粘着力が高いので、その界面で剥離の生じることがない。更に、全 光線透過率およびヘーズ値が適度であるため、画面の視認性が高くなる。When the cover film 16 is peeled off and the second adhesive layer 15 is fitted to a display screen such as a liquid crystal panel, the optical filter 10 for a display screen is attached by the self-adhesive force of the second adhesive layer 15. Can be. Since the surface of the second adhesive layer 15 has an adequately controlled initial adhesive force, it has good workability when attached to a display screen, and can be adhered cleanly without intervening air. , The air is discharged over time because the sticking is self-adhesive. In addition, the peelability after sticking is good, and no dirt due to the adhesive remains on the trace of peeling. This attachment and detachment can be repeated, and is excellent in repairability. On the other hand, since the first adhesive layer 12 has a high adhesive strength, no peeling occurs at the interface. Further, since the total light transmittance and the haze value are appropriate, the visibility of the screen is improved.
【００２４】[0024]
種々の表示画面用光学フィルターを試作し、その性能を比較した。なお、初期粘 着力、全光線透過率、ヘーズ値および鉛筆硬度の測定は、下記により行った。 １．初期粘着力：ＪＩＳ−Ｚ−０２３７に準拠し、ステンレス鋼板に貼り合わせ 、その２０分後に剥離角度１８０度、引張り速度３００mm／分で測定した。 ２．全光線透過率およびヘーズ値：濁度計（日本電色工業株式会社製「ＮＤＨ− １００１ＤＨ型」）を用いて測定した。 ３．鉛筆硬度：ＪＩＳ−Ｋ−５４００に準拠して測定した。 Various optical filters for display screens were prototyped, and their performances were compared. The initial adhesive force, total light transmittance, haze value and pencil hardness were measured as described below. 1. Initial adhesive strength: It was adhered to a stainless steel plate according to JIS-Z-0237, and after 20 minutes, measured at a peel angle of 180 ° and a pulling speed of 300 mm / min. 2. Total light transmittance and haze value: Measured using a turbidity meter (“NDH-1001DH type” manufactured by Nippon Denshoku Industries Co., Ltd.). 3. Pencil hardness: Measured according to JIS-K-5400.
【００２５】 実施例１ 図２の表示画面用光学フィルター１０において、機能性フィルム１１は、ポリエ ステルからなる厚み２５０μｍの基材フィルム１１ａの上面に、マット調のハー ド加工層（厚み：１０μｍ：鉛筆硬度：４Ｈ）１１ｂを複合したものであり、こ のハード加工層１１ｂは、光散乱性の粒子の配合による映り込み防止機能を備え た市販品である。この機能性フィルム１１をコンマコーターに供給し、その下面 に市販のアクリル系強粘着剤を塗布、乾燥して厚み２５μｍの第１粘着層１２を 形成し、その表面にポリエステルからなる市販の離型フィルム（厚み：３８μｍ ）１３のシリコーン処理面を重ねて着脱自在に積層した。なお、上記第１粘着層 １２の初期粘着力は、１３５００／２５mmであった。Example 1 In the optical filter 10 for a display screen of FIG. 2, the functional film 11 is formed by matting a hardened layer (thickness: 10 μm) on the upper surface of a 250 μm thick base film 11 a made of polyester. Pencil hardness: 4H) 11b is compounded, and the hard processed layer 11b is a commercially available product having a reflection preventing function by blending light scattering particles. This functional film 11 is supplied to a comma coater, a commercially available acrylic adhesive is applied to the lower surface thereof, and dried to form a first adhesive layer 12 having a thickness of 25 μm. The silicone-treated surfaces of the film (thickness: 38 μm) 13 were superposed and detachably laminated. The initial adhesive strength of the first adhesive layer 12 was 13,500 / 25 mm.
【００２６】 支持フィルム１４として、両面が易接着性処理をされた市販のポリエステルフィ ルム（厚み：２５０μｍ）を、またカバーフィルム１６として、片面が易剥離処 理をされた市販のポリエステルフィルム（厚み：２５μｍ）をそれぞれ準備した 。一方、市販の高透明型シリコーンゴム組成物（ゴム硬度：１０度）をトルエン に溶解し、これに支持フィルム１４に対する接着性を上げるための接着性改良剤 を添加して塗工液とし、この塗工液を上記支持フィルム１４の表面に乾燥後厚み が５０μｍとなるように塗布、乾燥し、そのゴム層表面に上記カバーフィルム１ ６の易接着処理面を重ね、この積層体を電子線照射装置に導入して上記のゴム層 を架橋して第２粘着層１５を形成し、かつ支持フィルム１４と結合した。この第 ２粘着層１５におけるカバーフィルム１６の剥離面の初期粘着力は、７０ｍＮ／ ２５mmであった。As the supporting film 14, a commercially available polyester film (thickness: 250 μm) having both surfaces subjected to an easy adhesion treatment, and as the cover film 16, a commercially available polyester film having one surface subjected to an easy peeling treatment (thickness: 250 μm) : 25 μm). On the other hand, a commercially available highly transparent silicone rubber composition (rubber hardness: 10 degrees) is dissolved in toluene, and an adhesion improver for increasing the adhesion to the support film 14 is added thereto to form a coating liquid. The coating liquid is applied to the surface of the support film 14 after drying so as to have a thickness of 50 μm, and dried. The surface of the rubber layer is covered with the easily adhesively treated surface of the cover film 16, and the laminate is irradiated with an electron beam. The rubber layer was crosslinked by introduction into an apparatus to form a second adhesive layer 15 and bonded to the support film 14. The initial adhesive strength of the peeled surface of the cover film 16 in the second adhesive layer 15 was 70 mN / 25 mm.
【００２７】 上記機能性フィルム１１の積層体と支持フィルム１４の積層体とをラミネーター に供給し、機能性フィルム１１側の離型フィルム１３を剥離しながら、第１粘着 層１２を介して機能性フィルム１１と支持フィルム１４とを貼り合わせ、得られ た機能性フィルム１１と支持フィルム１４の積層体をカバーフィルム１６と共に 所定の大きさに打抜き、表示画面用光学フィルター１０を得た。この実施例１の 表示画面用光学フィルター１０の特性を後掲の表１に示す。The laminate of the functional film 11 and the laminate of the support film 14 are supplied to a laminator, and the release film 13 on the side of the functional film 11 is peeled off while the functionality is interposed through the first adhesive layer 12. The film 11 and the support film 14 were bonded together, and the obtained laminate of the functional film 11 and the support film 14 was punched together with the cover film 16 into a predetermined size to obtain an optical filter 10 for a display screen. The characteristics of the display screen optical filter 10 of Example 1 are shown in Table 1 below.
【００２８】 この実施例１の表示画面用光学フィルター１０は、第２粘着層１５の存在により リペアー性に優れる一方、第１粘着層１２の粘着力が高いので、機能性フィルム １１および支持フィルム１４が界面で剥離することがなく、かつ視認性が高い。 また、総厚みが大きいので、取扱いが容易であり、かつ表示画面の保護機能に優 れ、大型画面の保護用に好適である。そして、機能性フィルム１１の表面にマッ ト加工層１１ｂを有するので、傷や指紋が着き難く、更に光の反射防止機能を有 するので、画面の鮮明性が向上する。The optical filter 10 for a display screen of Example 1 has excellent repairability due to the presence of the second adhesive layer 15, but has high adhesive strength of the first adhesive layer 12, so that the functional film 11 and the support film 14 are provided. Does not peel off at the interface and has high visibility. Further, since the total thickness is large, it is easy to handle and has an excellent function of protecting the display screen, which is suitable for protecting a large screen. Further, since the surface of the functional film 11 has the matte processing layer 11b, scratches and fingerprints are hardly attached thereto, and furthermore, since it has a function of preventing light reflection, the sharpness of the screen is improved.
【００２９】 比較例１ 上記の実施例１において、第１粘着層１２および第２粘着層１５の成分を入れ替 える以外は、実施例１と同様にして比較例１の表示画面用光学フィルターを作っ た。その特性を表１に示す。この比較例１は、第２粘着層１５の初期粘着力が高 いので、表示画面に取付ける際の施工性が劣り、第２粘着層１５と表示画面との 間に空気が入り易く、また剥離しようとすると、第１粘着層１２の部分で剥離が 発生して、支持フィルム１４が表示画面上に残る結果となり、かつ無理に剥離す ると、表示画面に粘着剤が汚れとして残り、実用性に欠けていた。Comparative Example 1 An optical filter for a display screen of Comparative Example 1 was prepared in the same manner as in Example 1 except that the components of the first adhesive layer 12 and the second adhesive layer 15 were replaced. Was. The characteristics are shown in Table 1. In Comparative Example 1, since the initial adhesive strength of the second adhesive layer 15 was high, the workability at the time of attaching to the display screen was inferior, air easily entered between the second adhesive layer 15 and the display screen, and the second adhesive layer 15 was peeled off. If this is attempted, peeling will occur at the portion of the first adhesive layer 12 and the support film 14 will remain on the display screen, and if it is forcibly peeled off, the adhesive will remain on the display screen as stains, and Was lacking.
【００３０】 比較例２ 前記の実施例１において、第１粘着層１２および第２粘着層１５の両者をアクリ ル系強粘着剤で形成し、その他は実施例１と同様にして比較例２の表示画面用光 学フィルターを試作した。その特性を表１に示す。この比較例２は、第１粘着層 １２の界面での剥離は防ぐことができたが、第２粘着層１５の初期粘着力が高い ので、比較例１と同様に施工性および剥離性が劣り、実用性に欠けていた。Comparative Example 2 In Example 1, both the first pressure-sensitive adhesive layer 12 and the second pressure-sensitive adhesive layer 15 were formed of an acryl-based strong pressure-sensitive adhesive. An optical filter for a display screen was prototyped. The characteristics are shown in Table 1. In Comparative Example 2, peeling at the interface of the first adhesive layer 12 could be prevented, but since the initial adhesive force of the second adhesive layer 15 was high, workability and peelability were inferior as in Comparative Example 1. , Lacked practicality.
【００３１】 比較例３ 前記の実施例１において、第１粘着層１２および第２粘着層１５の両者を架橋シ リコーンゴム層（自己粘着層）で形成し、その他は実施例１と同様にして比較例 ３の表示画面用光学フィルターを得た。その特性を表１に示す。この比較例３は 、表示画面に対する貼着時の施工性およびリペア性は、実施例１と同等であった が、第１粘着層１２の初期粘着力が低いので、機能性フィルム１１に対して支持 フィルム１４が容易に剥離し、実用性に劣るものであった。Comparative Example 3 In Example 1, both the first adhesive layer 12 and the second adhesive layer 15 were formed of a crosslinked silicone rubber layer (self-adhesive layer), and the other conditions were the same as in Example 1. An optical filter for a display screen of Example 3 was obtained. The characteristics are shown in Table 1. In Comparative Example 3, the workability and the repairability at the time of sticking to the display screen were the same as those in Example 1, but the initial adhesive force of the first adhesive layer 12 was low. The support film 14 was easily peeled off, and was inferior in practical use.
【００３２】 実施例２ 実施例１において、機能性フィルム１１および支持フィルム１４の厚みをそれぞ れ１８８μｍとする以外は、実施例１と同様にして実施例２の表示画面用光学フ ィルターを得た。その特性は、表１に示すとおりであり、実施例１と同様の実用 性を備えていた。Example 2 An optical filter for a display screen of Example 2 was obtained in the same manner as in Example 1, except that the thicknesses of the functional film 11 and the support film 14 were each 188 μm. Was. The characteristics were as shown in Table 1, and the same practicality as in Example 1 was provided.
【００３３】 実施例３ 実施例１において、その第２粘着層１５の成分をアクリルゲル系の自己粘着剤に 変更し、かつ電子線照射処理を取り止める以外は、実施例１と同様にして実施例 ３の表示画面用光学フィルターを得た。その特性は、表２に示すとおりであり、 実施例１と同様に実用性に優れていた。Example 3 An example was performed in the same manner as in Example 1 except that the component of the second adhesive layer 15 was changed to an acrylic gel-based self-adhesive and the electron beam irradiation treatment was stopped. 3 was obtained. The characteristics are as shown in Table 2, and were excellent in practicality as in Example 1.
【００３４】 実施例４ 実施例３において、第２粘着層１５の成分を、アクリル酸をグラフト重合した共 重合ポリエステルとアクリル系粘着剤との混合系自己粘着剤に変更し、その他は 実施例３と同様にして実施例４の表示画面用光学フィルターを得た。その特性は 、表２に示すとおりであり、実施例３と同様に実用性の高いものであった。Example 4 In Example 3, the component of the second adhesive layer 15 was changed to a mixed self-adhesive of a copolymerized polyester obtained by graft polymerization of acrylic acid and an acrylic adhesive. In the same manner as in Example 4, an optical filter for a display screen of Example 4 was obtained. The characteristics are as shown in Table 2 and were high in practicality as in Example 3.
【００３５】 実施例５ 実施例３において、第１粘着層１２の成分を自己粘着性のポリウレタン系粘着剤 に変更する以外は、実施例３と同様にして実施例５の表示画面用光学フィルター を得た。その特性は、表２に示すとおりであり、実用性は実施例３と同様に優れ ていた。Example 5 The display screen optical filter of Example 5 was prepared in the same manner as in Example 3, except that the component of the first adhesive layer 12 was changed to a self-adhesive polyurethane-based adhesive. Obtained. The characteristics are as shown in Table 2, and the practicality was excellent as in Example 3.
【００３６】 実施例６〜９ 前記の実施例１において、機能性フィルム１１の具備する機能を、表１に示す機 能に変更し、その他は実施例１と同様にして実施例６〜９の表示画面用光学フィ ルターを得た。その特性は、表３に示すとおりであり、実施例１と同様に優れた 実用性を備えていた。Examples 6 to 9 In the above-mentioned Example 1, the functions of the functional film 11 were changed to the functions shown in Table 1, and the others were the same as in Example 1 to obtain the functions of Examples 6 to 9. An optical filter for a display screen was obtained. The characteristics are as shown in Table 3, and as in Example 1, it had excellent practicality.
【００３７】 実施例１０ 実施例１において、第１粘着層１２に青色、赤色および黒色の顔料を配合して波 長４５０〜８００ｎｍの領域で光線透過率が５６〜７０％となるように着色し、 その他は実施例１と同様にして実施例１０の表示画面用光学フィルターを得た。 その特性は、表３に示すように、実施例１と同様に実用性に優れ、しかも光線透 過率を特定値に限定しているため、画面における画像のコントラストが良好であ り、目の疲れを軽減する機能が認められた。Example 10 In Example 1, the first adhesive layer 12 was mixed with blue, red and black pigments and colored so that the light transmittance was 56 to 70% in the wavelength range of 450 to 800 nm. The optical filter for a display screen of Example 10 was obtained in the same manner as in Example 1 except for the above. As shown in Table 3, the characteristics are excellent in practicality as in Example 1, and the light transmittance is limited to a specific value. A function to reduce fatigue was recognized.
【００３８】[0038]
【表１】 [Table 1]
【００３９】[0039]
【表２】 [Table 2]
【００４０】[0040]
【表３】 [Table 3]
【００４１】[0041]
上記のとおり、この考案に係る表示画面用光学フィルターは、機能性フィルムが 支持フィルムから容易に剥離することがなく、一体性を保持する一方、支持フィ ルムの反対側の第２粘着層が自己粘着層を構成するので、表示画面に対する着脱 が容易で、施工性およびリペア性に優れており、使用中は表示画面の画像の視認 性が高い。しかも、機能性フィルムおよび支持フィルムをそれぞれロール状で入 手することができ、単なる表面保護用フィルムよりも厚みの大きい光学フィルタ ーを連続方式で生産することが可能になり、取扱いが容易になる。 As described above, in the optical filter for a display screen according to the present invention, the functional film does not easily peel off from the support film and maintains the integrity, while the second adhesive layer on the opposite side of the support film is self-supporting. Since the adhesive layer is used, it can be easily attached to and detached from the display screen, has excellent workability and repairability, and has high visibility of the image on the display screen during use. In addition, the functional film and the support film can be obtained in roll form respectively, making it possible to produce an optical filter thicker than a mere surface protection film in a continuous manner, which facilitates handling. .
【００４２】 特に請求項２に係る考案は、第２粘着層を使用直前までカバーフィルムで保護す ることができる。また、請求項３に係る考案は、機能性フィルムおよび支持フィ ルムの合計厚みが従来の単なる保護用フィルムに比べて大きいので、表示画面の 保護機能が向上し、取扱いも容易になる。また、請求項４に係る考案は、耐スク ラッチ性、映り込み防止性、反射防止性、透明導電性、抗菌性および赤外線遮断 性のいずれか１以上の機能を有する機能性フィルムが得られる。In particular, according to the present invention, the second adhesive layer can be protected by the cover film until immediately before use. In the invention according to claim 3, since the total thickness of the functional film and the supporting film is larger than that of the conventional simple protective film, the protective function of the display screen is improved and the handling is easy. Further, according to the invention of claim 4, a functional film having at least one of scratch resistance, anti-glare property, anti-reflection property, transparent conductivity, antibacterial property and infrared shielding property can be obtained.
【図１】実施形態の断面図である。FIG. 1 is a sectional view of an embodiment.
【図２】製造工程の説明図である。FIG. 2 is an explanatory diagram of a manufacturing process.
１０：表示画面用光学フィルター １１：機能性フィルム、１１ａ：基材フィルム、１１
ｂ：ハード加工層 １２：第１粘着層 １３：離型フィルム １４：支持フィルム １５：第２粘着層 １６：カバーフィルム10: Optical filter for display screen 11: Functional film, 11a: Base film, 11
b: Hard working layer 12: First adhesive layer 13: Release film 14: Support film 15: Second adhesive layer 16: Cover film
Claims (4)
持フィルムおよび第２粘着層が順に積層された積層体か
らなり、上記第１粘着層の初期粘着力が２０００ｍＮ／
２５mm以上、上記第２粘着層表面の初期粘着力が２９〜
１５００ｍＮ／２５mm、上記積層体の全光線透過率が４
０％以上、ヘーズ値が３０％以下であることを特徴とす
る表示画面用光学フィルター。1. A functional film comprising a laminate in which a first adhesive layer, a support film, and a second adhesive layer are sequentially laminated on one surface of a functional film, and the first adhesive layer has an initial adhesive force of 2,000 mN /
25 mm or more, the initial adhesive strength of the second adhesive layer surface is 29 to
1500 mN / 25 mm, the total light transmittance of the laminate is 4
An optical filter for a display screen, wherein the haze value is 0% or more and the haze value is 30% or less.
脱自在に積層された請求項１記載の表示画面用光学フィ
ルター。2. The optical filter for a display screen according to claim 1, wherein a cover film is removably laminated on the surface of the second adhesive layer.
計厚みが２５０〜１０００μｍである請求項１または２
に記載の表示画面用光学フィルター。3. The functional film and the supporting film have a total thickness of 250 to 1000 μm.
An optical filter for a display screen according to item 1.
耐スクラッチ性、映り込み防止性、光線の反射防止性、
透明導電性、抗菌性および赤外線遮断性のいずれか１以
上の機能を具備する請求項１〜３のいずれかに記載の表
示画面用光学フィルター。4. The functional film has scratch resistance of 1H or more in pencil hardness, anti-glare property, anti-reflection property of light rays,
The optical filter for a display screen according to any one of claims 1 to 3, wherein the optical filter has at least one function of transparent conductivity, antibacterial property, and infrared blocking property.