KR101265240B1 - Display protecting sheet and manufacturing method thereof - Google Patents

Display protecting sheet and manufacturing method thereof Download PDF

Info

Publication number
KR101265240B1
KR101265240B1 KR1020110136939A KR20110136939A KR101265240B1 KR 101265240 B1 KR101265240 B1 KR 101265240B1 KR 1020110136939 A KR1020110136939 A KR 1020110136939A KR 20110136939 A KR20110136939 A KR 20110136939A KR 101265240 B1 KR101265240 B1 KR 101265240B1
Authority
KR
South Korea
Prior art keywords
film
display
tempered glass
opening
edge reinforcement
Prior art date
Application number
KR1020110136939A
Other languages
Korean (ko)
Inventor
유원근
Original Assignee
유원근
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 유원근 filed Critical 유원근
Priority to KR1020110136939A priority Critical patent/KR101265240B1/en
Application granted granted Critical
Publication of KR101265240B1 publication Critical patent/KR101265240B1/en

Abstract

PURPOSE: A protective film for a display and a method for manufacturing the same are provided to improve the impact resistance of the border of a tempered glass and to increase a manufacturing yield rate thereof. CONSTITUTION: A protective film for a display comprises a border reinforcing film(110), a tempered glass film(120), an anti-scattering layer(130), and an optical adhesion layer. An opening is formed at the center of the border reinforcing film covering a part or the entire of a non-image part. The tempered glass film and the opening have an identical size, and the tempered glass film is fit and assembled to the opening. The anti-scattering layer integrally adheres to the lower surfaces of the border reinforcing film and a tempered glass film, and is optically transparent. The optical adhesion layer adheres to the lower surface of the anti-scattering layer and can adhere to the surface of the display.

Description

디스플레이용 보호필름 및 그 제조방법{Display protecting sheet and manufacturing method thereof}Display protective film and manufacturing method thereof

본 발명은 강화유리를 적용하여 박막의 높은 투명도를 갖는 휴대용 전자기기의 디스플레이 보호필름에 있어서 충격에 의한 파손을 방지하며, 특히 상대적으로 충격에 취약할 수 있는 강화유리의 테두리 주위에 대한 내충격성(impact resistance)을 개선할 수 있는 디스플레이용 보호필름 및 그 제조방법에 관한 것이다.
The present invention to prevent the breakage caused by impact in the display protective film of a portable electronic device having a high transparency of the thin film by applying the tempered glass, in particular impact resistance against the edge of the tempered glass that can be relatively vulnerable to impact ( It relates to a display protective film and a method for manufacturing the same that can improve impact resistance).

일반적으로, TV, 모니터, 휴대전화, PDA, 네비게이션 등과 같은 전자기기의 디스플레이 전면에는 사용 시에 지문이나 이물질 등이 묻거나 방지하기 위하여 보호필름을 부착하여 사용하게 된다.In general, a protective film is attached to a front surface of an electronic device such as a TV, a monitor, a mobile phone, a PDA, a navigation, or the like to prevent fingerprints or foreign substances from being used.

특히 최근의 휴대용 전자기기는 디스플레이를 직접 터치하여 조작이 이루어지고 있으며, 따라서 디스플레이를 직접 접촉하는 상황이 빈번하므로 오염되기 쉽고 특히 흠집이나 파손되기 쉬운 환경에 놓여 있다. 또한 최근의 휴대용 전자기기들은 화면이 커지고 두께가 얇아지므로 외부 충격에 취약할 수 있으며, 특히 휴대용 전자기기에 있어 고가의 중요 부품인 디스플레이 패널은 외부 충격에 의해 손상이 발생되기 쉽다.In particular, recently, portable electronic devices are operated by directly touching the display, and thus, the direct contact with the display is frequently performed, and therefore, the portable electronic device is easily contaminated and is particularly placed in an environment that is easily scratched or damaged. In addition, recent portable electronic devices may be vulnerable to external shock because the screen becomes larger and thinner. In particular, the display panel, which is an important important component of the portable electronic device, is easily damaged by external shock.

따라서 휴대용 전자기기의 디스플레이를 보호하기 위하여 보호필름의 기능 상, 투명도가 높고 박막구조이면서도 내충격성이 우수할 것을 요구한다.Therefore, in order to protect the display of the portable electronic device, the protective film requires a high transparency, a thin film structure and excellent impact resistance.

종래의 보호필름으로서는 투명한 플라스틱 재질의 필름이 이용되고 있으나 이러한 보호필름은 내스크래치성(anti-scratch)이 취약하여 터치패널 방식의 전자기기에서는 사용 중에 발생되는 보호필름 표면의 흠집에 의해 급격히 투명도가 저하되어 사용에 불편함이 많다.As a conventional protective film, a transparent plastic film is used, but such a protective film is weak in scratch resistance (anti-scratch), so in a touch panel type electronic device, the transparency of the protective film suddenly occurs due to scratches on the surface of the protective film generated during use. It is degraded and there are many inconveniences to use.

이러한 문제점을 해결하기 위하여 강화유리를 적용하여 내스크래치성이 우수한 보호필름을 제공하기 위한 종래기술로서, 등록실용신안 제20-0439013호(등록일자: 2008.03.10)와 등록특허 제10-1001752호(등록일자: 2010.12.09)에는 강화유리를 이용한 투명한 보호필름을 개시하고 있다.In order to solve this problem, by applying a tempered glass to provide a protective film with excellent scratch resistance, the Utility Model Registration No. 20-0439013 (Registration Date: March 10, 2008) and Patent No. 10-1001752 (Registration Date: 2010.12.09) discloses a transparent protective film using tempered glass.

그러나 이러한 종래의 강화유리를 적용한 보호필름은 투명도가 높고 내스크래치성이 우수한 장점이 있으나 충격에 의해 파손되는 경우에 유리파편이 비산되어 기기를 손상시키거나 사용자가 상해를 입을 수가 있으며, 특히 강화유리는 상대적으로 테두리 주위가 내충격성에 취약하여 쉽게 깨짐이 발생할 수가 있다.
However, the protective film using the conventional tempered glass has the advantage of high transparency and excellent scratch resistance, but in case of breakage by impact, glass fragments may scatter and damage the device or the user may be injured, especially tempered glass. Because of its relatively vulnerable to impact resistance, it is easy to break.

본 발명은 종래기술의 문제점을 해결하고자 하는 것으로, 강화유리를 적용하여 박막의 높은 투명도를 갖는 휴대용 전자기기의 디스플레이 보호필름에 있어서 충격에 위한 파손을 방지하며, 특히 상대적으로 충격에 취약할 수 있는 강화유리의 테두리 주위에 대한 내충격성(impact resistance)을 개선할 수 있는 디스플레이용 보호필름 및 그 제조방법을 제공하고자 한다.The present invention is to solve the problems of the prior art, by applying a tempered glass in the display protective film of a portable electronic device having a high transparency of a thin film to prevent breakage for impact, in particular can be relatively vulnerable to impact An object of the present invention is to provide a protective film for a display and a method of manufacturing the same, which can improve impact resistance around the edge of tempered glass.

또한, 본 발명은 디스플레이용 보호필름을 제조함에 있어서, 제조 수율을 향상시킬 수 있으며, 생산성을 높일 수 있는 디스플레이용 보호필름 제조방법을 제공하고자 한다.
In addition, the present invention to improve the production yield in manufacturing the protective film for display, and to provide a method for manufacturing a protective film for display that can increase the productivity.

상기 목적을 달성하기 위한 본 발명에 따른 디스플레이용 보호필름은 영상 정보를 출력하는 화상부와, 이 화상부의 테두리를 감싸는 비화상부가 디스플레이 전면부를 구성하게 되는 전자기기의 디스플레이용 보호필름에 있어서, 중앙에 개구부를 가지며 상기 비화상부의 전부 또는 일부를 덮도록 마련되는 테두리 보강필름과; 상기 개구부와 동일한 사이즈를 갖고 상기 개구부에 끼워 조립되는 강화유리필름과; 상기 테두리 보강필름과 강화유리필름의 저면에 일체로 접착되는 광학적으로 투명한 비산방지층과; 상기 비산방지층의 하면에 점착되어 전자기기의 디스플레이 표면에 점착이 가능한 광학점착층에 의해 달성된다.In the protective film for a display according to the present invention for achieving the above object is a display portion for outputting image information, and a non-image portion surrounding the edge of the image portion constitutes the display front portion of the display of the electronic device in the center, An edge reinforcement film having an opening and covering all or part of the non-image part; A tempered glass film having the same size as the opening and fitted into the opening; An optically transparent scattering prevention layer integrally bonded to the bottom of the edge reinforcement film and the tempered glass film; It is achieved by an optical adhesive layer that is adhered to the lower surface of the anti-scattering layer and is able to adhere to the display surface of the electronic device.

바람직하게는 본 발명에 있어서, 상기 개구부는 화상부와 동일한 사이즈를 갖는 것을 특징으로 하며, 보다 바람직하게는 상기 화상부와 동일한 사이즈의 개구부를 갖는 테두리 보강필름에는 디스플레이 전면부에 구비되는 버튼 또는 스피커가 바깥으로 노출되도록 천공홀을 갖는 것을 특징으로 한다.Preferably, in the present invention, the opening is characterized in that it has the same size as the image portion, and more preferably, the edge reinforcement film having an opening of the same size as the image portion is provided with a button or speaker provided on the front display portion It characterized in that it has a perforation hole to be exposed to the outside.

바람직하게는 본 발명에 있어서, 상기 테두리 보강필름에는 무선인식태그가 추가로 구비될 수 있으며, 또는 상기 광학점착층은 실리콘 또는 우레탄계열의 점착제인 것을 특징으로 하며, 또는 상기 테두리 보강필름과 강화유리필름의 모서리는 모따기되거나 곡면인 것을 특징으로 한다.Preferably, in the present invention, the edge reinforcement film may be further provided with a wireless recognition tag, or the optical adhesive layer is characterized in that the silicone or urethane-based adhesive, or the edge reinforcement film and tempered glass The edges of the film are characterized by being chamfered or curved.

다음으로, 상기 목적을 달성하기 위한 본 발명에 따른 디스플레이용 보호필름의 제조방법은, 하기의 제2공정에서 제작되는 테두리 보강필름 유니트의 개구부 사이즈와 동일한 사이즈를 갖도록 마련된 박막의 강화유리 표면에 기능성 박막층을 형성하여 강화유리필름 유니트를 제작하는 제1공정과; 대상 전자기기의 디스플레이 전면의 사이즈와 대응되도록 마련된 보강필름에 개구부를 갖도록 테두리 보강필름 유니트를 제작하는 제2공정과; 상기 테두리 보강필름 유니트의 외곽 사이즈와 대응되는 사이즈를 갖는 고투명도의 PET필름에 광학적으로 투명한 광학점착제를 도포하여 비산방지필름 유니트를 제작하는 제3공정과; 상기 제1공정, 제2공정, 제3공정에서 각각 제작된 강화유리필름 유니트, 테두리 보강필름 유니트 및 비산방지필름 유니트를 합지하는 제4공정에 의해 달성될 수 있다.Next, the manufacturing method of the protective film for display according to the present invention for achieving the above object, the functionality on the surface of the tempered glass of the thin film provided to have the same size as the opening size of the edge reinforcement film unit produced in the second step Forming a thin film layer to produce a tempered glass film unit; A second step of manufacturing an edge reinforcement film unit to have an opening in the reinforcement film provided to correspond to the size of the front surface of the display of the target electronic device; A third step of manufacturing an anti-scattering film unit by applying an optically transparent optical adhesive to a high transparency PET film having a size corresponding to the outer size of the edge reinforcing film unit; It can be achieved by a fourth process of laminating the tempered glass film unit, the edge reinforcement film unit and the shatterproof film unit produced in each of the first step, the second step, and the third step.

바람직하게는 본 발명에 있어서, 상기 제1공정에서 상기 기능성 박막층은 방오 코팅층일 수 있으며, 보다 바람직하게는 상기 개구부의 사이즈는 대상 전자기기의 디스플레이 전면 화상부의 사이즈와 동일한 것을 특징으로 한다.
Preferably, in the first step, the functional thin film layer may be an antifouling coating layer, and more preferably, the size of the opening is the same as that of the display front image of the target electronic device.

본 발명에 따른 디스플레이용 보호필름은 중앙에 개구부를 가지며 전자기기 디스플레이의 비화상부의 전부 또는 일부를 덮도록 마련되는 테두리 보강필름과; 상기 개구부와 동일한 사이즈를 갖고 상기 개구부에 끼워 조립되는 강화유리필름과; 상기 테두리 보강필름과 강화유리필름의 저면에 일체로 접착되는 광학적으로 투명한 비산방지층과; 상기 비산방지층의 하면에 점착되어 전자기기의 디스플레이 표면에 점착이 가능한 광학점착층으로 구성됨으로써, 보호필름으로 강화유리를 적용하여 박막의 높은 투명도를 가지면서도 충격에 위한 파손을 방지하며, 특히 상대적으로 충격에 취약할 수 있는 강화유리의 테두리에 대한 내충격성을 개선할 수가 있다.The protective film for a display according to the present invention includes an edge reinforcement film having an opening in the center and provided to cover all or a portion of the non-image portion of the electronic device display; A tempered glass film having the same size as the opening and fitted into the opening; An optically transparent scattering prevention layer integrally bonded to the bottom of the edge reinforcement film and the tempered glass film; It is adhered to the lower surface of the anti-scattering layer is composed of an optical adhesive layer that can be attached to the display surface of the electronic device, by applying a tempered glass as a protective film to prevent damage to the impact while having a high transparency of the thin film, in particular relatively It can improve the impact resistance to the edge of the tempered glass which can be vulnerable to impact.

또한 본 발명에 따른 디스플레이용 보호필름 및 그 제조방법은 디스플레이 전면부의 비화상부에 마련되는 버튼 또는 스피커가 바깥으로 노출되기 위한 천공홀을 강화유리필름보다는 상대적으로 가공이 용이한 테두리 보강필름에 마련함으로써 제작이 용이하며 제조 단가를 낮출 수 있는 효과가 있다.In addition, the protective film for a display according to the present invention and a method for manufacturing the same by providing a perforated hole for exposing the outside of the button or speaker provided on the non-image portion of the display front in the edge reinforcement film that is relatively easy to process rather than tempered glass film It is easy to manufacture and has the effect of lowering the manufacturing cost.

다음으로 본 발명에 따른 디스플레이용 보호필름은 무선인식태그가 마련됨으로써 통신카드나 ID카드 등으로 활용도를 높일 수 있는 효과가 있다.Next, the protective film for display according to the present invention has an effect of increasing the utilization of the communication card or ID card by providing a wireless recognition tag.

다음으로 본 발명에 따른 디스플레이용 보호필름의 제조방법은, 보호필름을 구성하는 각 필름 유니트를 별도의 공정에 의해 제조하여 최종적으로 각 필름 유니트를 합지하는 공정을 통해 보호필름을 제작하게 되므로, 제조 수율을 향상시킬 수 있으며, 생산성을 높일 수 있는 효과가 있다.
Next, the manufacturing method of the protective film for a display according to the present invention, by manufacturing the film unit constituting the protective film by a separate process and finally to produce a protective film through the process of laminating each film unit, Yield can be improved, and productivity can be increased.

도 1 본 발명의 디스플레이용 보호필름이 부착된 휴대폰을 보여주는 도면,
도 2는 본 발명의 디스플레이용 보호필름의 분해 사시도,
도 3은 도 1의 A-A 선의 단면도,
도 4의 (a)(b)(c)는 본 발명의 디스플레이용 보호필름에 있어서, 테두리 보강필름과 강화유리필름(120)의 조립단면에 대한 다양한 변형예를 보여주는 도면,
도 5는 본 발명의 디스플레이용 보호필름의 다른 실시예를 보여주는 도면,
도 6은 본 발명의 실시예에 따른 디스플레이용 보호필름의 제조공정을 보여주는 흐름도.1 is a view showing a mobile phone with a protective film for display of the present invention,
Figure 2 is an exploded perspective view of the protective film for display of the present invention,
3 is a cross-sectional view taken along line AA of FIG.
Figure 4 (a) (b) (c) is a view showing various modifications to the assembly cross-section of the edge reinforcement film and tempered glass film 120 in the display protective film of the present invention,
5 is a view showing another embodiment of the protective film for a display of the present invention,
6 is a flow chart showing a manufacturing process of the protective film for a display according to an embodiment of the present invention.

이하, 본 발명의 실시예를 첨부 도면을 참고하여 상세히 설명하면 다음과 같다. Hereinafter, embodiments of the present invention will be described in detail with reference to the accompanying drawings.

도 1 내지 도 3을 참고하면, 본 실시예에서 휴대용 전자기기로서 터치패널이 적용된 휴대폰을 보여주고 있으며, 휴대폰(1)의 디스플레이 전면부는 영상 정보를 출력하는 화상부(10)와, 이 화상부(10)의 테두리를 감싸는 비화상부(20)로 구성된다. 1 to 3, in this embodiment, a mobile phone to which a touch panel is applied as a portable electronic device is shown. The display front part of the mobile phone 1 includes an image part 10 for outputting image information, and the image part. It consists of a non-image portion 20 surrounding the edge of the (10).

화상부(10)의 주요 기능은 영상 정보를 출력하게 되며, 터치패널이 적용된 휴대폰은 화상부(10)를 터치하여 입력수단으로도 사용될 수가 있다.The main function of the image unit 10 is to output image information, and a mobile phone to which a touch panel is applied can also be used as an input means by touching the image unit 10.

비화상부(20)는 화상부(10)의 테두리 외곽을 구성하는 것으로 휴대폰의 전원 또는 기능을 조작하기 위한 버튼(21)과 음향 출력을 위한 스피커(22) 등이 마련될 수 있으며, 버튼의 종류나 위치는 다양할 수가 있다.
The non-picture unit 20 constitutes an outer periphery of the image unit 10 and may include a button 21 for operating a power or function of a mobile phone and a speaker 22 for sound output. My location can vary.

본 발명의 디스플레이용 보호필름은 테두리 보강필름(110), 강화유리필름(120) 및 비산방지층(130)을 주요 구성요소로 하는 것이다.The display protective film of the present invention is to include the edge reinforcement film 110, the tempered glass film 120 and the scattering prevention layer 130 as the main components.

테두리 보강필름(110)은 화상부(10)와 동일한 사이즈의 개구부(111)를 가지며 비화상부(20)를 덮도록 마련되며, 알루미늄 등의 금속재질 또는 PC, 아크릴, ABS 등의 수지나 유리섬유 등의 다양한 소재가 이용될 수가 있다. 이러한 테두리 보강필름(110)은 강화유리필름(120)의 테두리 외곽을 보호하여 보호필름의 내구성을 크게 개선시킬 수 있다.The edge reinforcement film 110 has an opening 111 having the same size as the image portion 10 and is provided to cover the non-image portion 20, and is made of metal such as aluminum or resin or glass fiber such as PC, acrylic, or ABS. Various materials such as can be used. The edge reinforcement film 110 may greatly improve the durability of the protective film by protecting the outer edge of the tempered glass film 120.

특히 본 발명에 있어서, 테두리 보강필름(110)에는 무선인식태그(RF Tag)(112)가 추가로 구비될 수가 있다. 무선인식태그(112)는 RFID 시스템에서 근거리의 무선 전달 정보를 포함하는 중계칩으로서 통신카드나 ID카드, 교통카드, 선불카드 등으로 사용될 수가 있다.In particular, in the present invention, the edge reinforcement film 110 may be further provided with a radio tag (RF Tag) (112). The radio tag 112 may be used as a communication card, an ID card, a traffic card, or a prepaid card as a relay chip including near field wireless transmission information in an RFID system.

또한 테두리 보강필름(110)은 주지의 항균 물질을 포함할 수 있으며, 다양한 칼라가 사용되거나 로고나 도형 문형 등이 인쇄되어 외관미를 높일 수 있다.In addition, the edge reinforcement film 110 may include a known antimicrobial material, and various colors may be used, or a logo or a figure sentence pattern may be printed to enhance appearance.

도면부호 113과 114는 각각 비화상부(20)에 마련되는 버튼(21)과 스피커(22)가 바깥으로 노출되도록 하기 위하여 테두리 보강필름(110)에 형성된 천공홀이며, 이러한 천공홀은 전자기기에 따라서 비화상부(20)에 마련되는 기능 버튼들이나 스피커의 위치나 사이즈에 따라서 결정된다.Reference numerals 113 and 114 are perforated holes formed in the edge reinforcement film 110 to expose the buttons 21 and the speakers 22 provided in the non-image portion 20 to the outside, respectively, and the perforated holes are formed in the electronic apparatus. Therefore, it is determined according to the position or size of the function buttons or the speaker provided in the non-image unit 20.

이와 같이 디스플레이 전면부에 배치되는 기능 버튼이나 스피커를 바깥으로 노출시키기 위한 천공홀을 테두리 보강필름에 배치되도록 함으로써 상대적으로 강화유리필름에 홀가공을 하는 것과 비교하여 가공이 용이하며 제조 단가를 낮출 수 있다.
In this way, the perforated hole for exposing the function button or the speaker placed on the front of the display to the outside is placed on the edge reinforcement film, which is easier to process and lower the manufacturing cost compared to the hole processing on the tempered glass film. have.

강화유리필름(120)은 테두리 보강필름(110)의 개구부(111)와 대응되는 사이즈를 갖는 박판화된 강화유리로써 테두리 보강필름(110)의 개구부(111)에 끼워 고정되어 보호필름의 상부층을 구성한다.Tempered glass film 120 is a laminated tempered glass having a size corresponding to the opening 111 of the edge reinforcement film 110 is fixed to the opening 111 of the edge reinforcement film 110 to form an upper layer of the protective film. do.

강화유리필름(120)은 박판화된 유리를 강화 가공하여 얻게 되며, 본 발명에서는 공지의 유리강화 방법으로 이용되는 물리강화법 또는 화학강화법이 이용될 수가 있다. The tempered glass film 120 is obtained by reinforcing the laminated glass, and in the present invention, a physical strengthening method or a chemical strengthening method used by a known glass strengthening method may be used.

물리강화법은 통상 두께 5.0㎜ 이상의 유리를 550℃ 내지 700℃ 사이의 온도로 가열한 후에 급랭시켜 유리의 내부 강도를 강화하는 방식이나 이러한 고온에 의한 물리강화는 유리 표면층과 중심층 사이의 온도 구배가 거의 없는 3.0㎜ 이하의 박판유리에는 적용이 불가능하며, 따라서 3.0㎜ 이하의 박판유리에서는 화학강화법이 주로 이용된다. In general, the physical strengthening method is to heat a glass having a thickness of 5.0 mm or more to a temperature between 550 ° C. and 700 ° C. and then quench the glass to strengthen the internal strength of the glass. It is not applicable to thin glass having a thickness of 3.0 mm or less, so that chemical strengthening is mainly used in thin glass of 3.0 mm or less.

화학강화법은 박판유리를 질산칼륨 등의 용액이 담긴 열처리로에서 3시간 이상 침지시킴에 따라 유리에 포함된 이온 반경이 작은 나트륨 이온과 질산칼륨 용액의 이온 반경이 큰 칼륨 이온을 서로 치환시켜 유리 표면층에 압축응력을 발생시켜 유리를 강화시킨다.In chemical strengthening, thin glass is immersed in a heat treatment furnace containing a solution of potassium nitrate for at least 3 hours, so that sodium ions having a small ionic radius and potassium ions having a large ionic radius of a glass are replaced with each other. The compressive stress is generated to strengthen the glass.

따라서 본 발명에 따라서는 박판유리의 두께에 따라서 물리강화법 또는 화학강화법이 모두 적용이 가능하나, 보다 얇은 박판유리에 적합한 화학강화법이 선호되어 사용될 수가 있다.Therefore, according to the present invention, both physical strengthening and chemical strengthening may be applied depending on the thickness of the thin glass, but a chemical strengthening method suitable for thinner thin glass may be preferably used.

강화유리필름(110)에는 방오 코팅층(미도시)이 상부면에 코팅되어 오염물질에 의하여 표면이 오염되는 것을 방지할 수 있다. 이러한 방오 코팅층은 지문에 의한 오염을 방지하기 위한 AF(Anti-finger)코팅, 내스크래치성을 갖는 AS(Anti-Scratch)코팅, 또는 내식성을 갖는 AC(Anti-Corrosion)코팅 등 다른 기능성 혼합물로 구성된 코팅층에 의해 제공될 수 있다.The tempered glass film 110 may be coated on the upper surface of the antifouling coating layer (not shown) to prevent the surface from being contaminated by contaminants. This antifouling coating layer is composed of other functional mixtures such as anti-finger coating to prevent fingerprint contamination, anti-scratch coating with scratch resistance, or anti-corrosion coating with corrosion resistance. It may be provided by a coating layer.

비산방지층(130)은 광학적으로 투명한 재질로서 테두리 보강필름(110)과 강화유리필름(120)의 하면에 광학접착제에 의해 접착이 이루어지는 것으로, 휴대폰(1)에 충격이 가해져 강화유리필름(110)이 깨지더라도 조각이나 파편이 비산되는 것을 방지하는 기능을 한다.The anti-scattering layer 130 is an optically transparent material that is bonded to the lower surface of the edge reinforcement film 110 and the tempered glass film 120 by an optical adhesive, and the cell phone 1 is applied to the tempered glass film 110. Even if it is broken, it prevents fragments or debris from scattering.

도면부호 131과 132는 각각 비화상부(20)에 마련되는 버튼(21)과 스피커(22)가 바깥으로 노출되도록 하기 위하여 비산방지층(130)에 형성되는 천공홀이며, 이러한 천공홀은 전자기기에 따라서 비화상부(20)에 마련되는 기능 버튼들이나 스피커의 위치나 크기에 따라서 결정된다.Reference numerals 131 and 132 are perforation holes formed in the anti-scattering layer 130 so that the buttons 21 and the speakers 22 provided in the non-image portion 20 are exposed to the outside. Therefore, it is determined according to the position or size of the function buttons or the speaker provided in the non-image portion 20.

이러한 비산방지층(130)으로는 기계적 강도가 우수하고 투명도가 높은 범용 수지인 PET(polyethylene terephthalate) 필름 또는 PC(polycarbonate) 필름에 의해 제공될 수가 있으며, 바람직하게는 고투명도의 PET 필름이 이용될 수가 있다.The anti-scattering layer 130 may be provided by a polyethylene terephthalate (PET) film or a PC (polycarbonate) film, which is a general-purpose resin having excellent mechanical strength and high transparency, and preferably, a high transparency PET film may be used. have.

이러한 비산방지층(130)은 광학(가시광선)적으로 투명한 광학접착제(133)에 의해 테두리 보강필름(110)과 강화유리필름(120)과 접착이 이루어질 수 있다.The scattering prevention layer 130 may be bonded to the edge reinforcement film 110 and the tempered glass film 120 by an optical (visible light) optically transparent adhesive 133.

본 발명에서 광학접착제는 아크릴 또는 실리콘계열의 점착제에 의해 제공될 수가 있으며, 바람직하게는 아크릴 공중합체(acrylic coplymer) 약 22.0 중량%와 아세트산에틸(ethyl acetate) 42~51 중량%를 주재료로 하는 접착제에 의해 제공될 수 있으며, 투명도를 80~90%이상 유지하며, 그 두께는 30마이크로미터 이하로 실시하는 것이 바람직할 것이다.In the present invention, the optical adhesive may be provided by an acrylic or silicone-based adhesive, preferably an adhesive based on an acrylic copolymer of about 22.0 wt% and ethyl acetate 42 to 51 wt% It may be provided by the, it is preferable to maintain the transparency of 80 to 90% or more, the thickness of less than 30 micrometers.

광학점착층(140)은 비산방지층(130)의 하면에 점착되어 전자기기의 디스플레이 표면에 점착이 가능하다.The optical adhesive layer 140 is adhered to the lower surface of the scattering prevention layer 130 to enable adhesion to the display surface of the electronic device.

광학점착층(140)은 비산방지층(130)의 하면에 마련되어 디스플레이 전면에 점착이 가능하도록 하기 위한 것으로, 가시광선에 대해 광학적으로 투명한 점착제에 의해 제공될 수 있다.The optical adhesive layer 140 is provided on the lower surface of the anti-scattering layer 130 to enable adhesion to the front surface of the display, and may be provided by an optically transparent adhesive to visible light.

광학점착층은 실리콘 또는 우레탄계열의 점착제에 의해 제공될 수 있으며, 바람직하게는 xylene(ortho, meta, para) 30 ~ 60 중량%, Dimethyl siloxane, dimethyl-vinyl 20 ~ 30 중량%를 주재료로 하는 점착제에 의해 제공될 수 있다.The optical adhesive layer may be provided by a silicone or urethane-based adhesive, preferably an adhesive based on 30 to 60 wt% of xylene (ortho, meta, para), 20 to 30 wt% of dimethyl siloxane, dimethyl-vinyl May be provided by

이러한 광학점착층은 기포가 발생하지 않으며, 여러 차례 반복하여 사용하여도 80% 이상의 점착력이 유지되는 특성을 가지며, 그 두께는 50마이크로미터 이하로 실시하는 것이 바람직할 것이다.Such an optical adhesive layer does not generate bubbles and has a property of maintaining adhesive strength of 80% or more even after repeated use, and its thickness may be preferably performed at 50 micrometers or less.

광학점착층(140)은 디스플레이 표면에 반복하여 탈부착이 가능한 반면에, 비산방지층(130)과, 테두리 보강필름(110) 및 강화유리필름(120) 사이를 접착하게 되는 광학접착제는 비산방지역할을 하기 위하여 광학점착층(140) 보다는 큰 접착력을 갖는 것이 바람직하다.
While the optical adhesive layer 140 may be repeatedly attached to and detached from the display surface, the optical adhesive agent for bonding the scattering prevention layer 130 and the edge reinforcement film 110 and the tempered glass film 120 may be scattered. In order to have a greater adhesive force than the optical adhesive layer 140 in order to.

이러한 본 발명의 디스플레이용 보호필름은 테두리 보강필름(110)의 개구부(111)에 강화유리필름(120)이 끼워 조립이 이루어지며, 강화유리필름(120)과 테두리 보강필름(110) 사이에는 틈이 없도록 조립되는 것이 바람직할 것이다.The protective film for display of the present invention is assembled by the tempered glass film 120 is inserted into the opening 111 of the edge reinforcement film 110, the gap between the tempered glass film 120 and the edge reinforcement film 110. It would be desirable to be assembled without this.

구체적으로 도 4는 테두리 보강필름과 강화유리필름의 조립단면에 대한 다양한 변형예를 보여주는 도면이다.Specifically, Figure 4 is a view showing a variety of modifications to the assembly cross-section of the edge reinforcement film and tempered glass film.

도 4의 (a)는 테두리 보강필름(211)은 상단부에 개구부 안쪽으로 돌출 형성된 돌기(211a)가 마련되어 강화유리필름(221)과 조립될 수 있으며, 이때 강화유리필름(221)과 테두리 보강필름(211)의 하측 개구부를 통해 상방으로 끼워 조립되어 강화유리필름(221)은 테두리 보강필름(211) 상단의 돌기(211a)에 의해 지지될 수 있다. 한편, 돌기(211a)는 수평 방향으로만 돌출 형성되어 테두리 보강필름(211)과 강화유리필름(221)은 이음새 부위에 돌출된 구조를 갖지 않도록 하는 것이 바람직하다.4 (a) is the edge reinforcement film 211 is provided with a projection (211a) protruding into the opening in the upper end may be assembled with the tempered glass film 221, wherein the tempered glass film 221 and the edge reinforcement film Assembled upward through the lower opening of the 211, the tempered glass film 221 may be supported by the projection (211a) of the upper edge of the edge reinforcement film (211). On the other hand, the projection (211a) is formed to protrude only in the horizontal direction so that the edge reinforcement film 211 and the tempered glass film 221 preferably do not have a structure protruding in the seam.

도 4의 (b)와 같이, 테두리 보강필름(231)과 강화유리필름(241)은 각각 모따기되어 경사면(211a)(221a)에 의한 홈이 형성될 수 있으며, 이와 같이 테두리 보강필름(231)과 강화유리필름(241)이 접하여 형성된 홈 내에는 수지 또는 금속 재료에 의해 충전되어 테두리 보강필름(231)과 강화유리필름(241) 사이에 틈새를 없앨 수 있다.As shown in (b) of FIG. 4, the edge reinforcement film 231 and the tempered glass film 241 may be chamfered to form grooves formed by the inclined surfaces 211 a and 221 a, respectively. In the groove formed in contact with the tempered glass film 241, the gap between the edge reinforcement film 231 and the tempered glass film 241 may be filled with a resin or a metal material.

한편 도 4의 (c)에는 강화유리필름(271)보다 높게 돌출 되어 형성된 테두리 보강필름(261) 상단부가 개구부 안쪽으로 돌출 형성된 돌기(261a)가 마련되어 강화유리필름(271)과 조립될 수 있음을 보여주고 있다.On the other hand, Figure 4 (c) is provided with a protrusion (261a) formed in the upper end of the edge reinforcement film 261 formed to protrude higher than the tempered glass film 271 to the inside of the opening can be assembled with the tempered glass film 271. Is showing.

이와 같은 테두리 보강필름과 강화유리필름 사이의 조립단면 구조는 테두리 보강필름이 강화유리필름의 테두리를 보호하면서도 틈새 사이에 이물질 등이 끼는 것을 최소화할 수 있는 범위 내에서 테두리 보강필름의 재질 강도나 특성에 따라서 다양하게 결정될 수 있다.
The assembly cross-sectional structure between the edge reinforcement film and the tempered glass film is such that the edge reinforcement film protects the edges of the tempered glass film while minimizing foreign substances between the gaps. It can be determined variously according to.

도 5는 본 발명의 디스플레이용 보호필름의 다른 실시예를 보여주는 도면으로, 5 is a view showing another embodiment of the protective film for a display of the present invention,

본 실시예에서 테두리 보강필름(310)이 강화유리필름(330) 테두리 외곽을 감싸서 구성됨은 앞서의 실시예와 동일하며, 휴대폰(1)의 비화상부(20)에 마련되는 버튼(21)과 스피커(22)가 바깥으로 노출되도록 하기 위한 천공홀(321)(322)이 테두리 보강필름(310)이 아닌 강화유리필름(330)에 마련됨에 차이가 있다.In the present embodiment, the edge reinforcement film 310 is formed to surround the outer edge of the tempered glass film 330, and the same as the previous embodiment, and the button 21 and the speaker provided in the non-image part 20 of the mobile phone 1 are provided. There is a difference in that the perforation holes 321 and 322 for exposing the 22 to the outside are provided in the tempered glass film 330 instead of the edge reinforcement film 310.

따라서 본 실시예에서 테두리 보강필름(310)은 비화상부(20)의 일부만을 덮게 되며, 강화유리필름(320)은 테두리 보강필름(310)의 개구부(311)에 끼워 조립되어 화상부(20)와 함께 비화상부(10)의 일부를 덮게 된다.
Therefore, in the present embodiment, the edge reinforcement film 310 covers only a part of the non-image portion 20, and the tempered glass film 320 is assembled to the opening 311 of the edge reinforcement film 310 to be assembled to the image portion 20. A portion of the non-image portion 10 is covered together.

이와 같은 구성을 갖는 본 발명의 디스플레이용 보호필름은 적층구조에 따라서 순차적인 공정에 의해 제조가 이루어질 수가 있으나, 각 필름 유니트에 따라서 별도의 제조공정으로 분리하여 제조된 후에 각 필름 유니트를 합지하는 공정에 의해 제조됨이 바람직할 것이다.The display protective film of the present invention having such a configuration may be manufactured by a sequential process according to the laminated structure, but the process of laminating each film unit after being manufactured separately by a separate manufacturing process according to each film unit It will be preferred to make.

이하에서 구체적으로 살펴보겠으나, 본 발명의 보호필름의 제조에 있어서 테두리 보강필름 유니트, 강화유리필름 유니트와 비산방지필름 제조공정은 크게 다르며, 따라서 순차적인 일괄 공정으로 제조하는 경우에는 과다한 설비투자비와 생산성, 수율의 저하로 인하여 채산성이 현저히 저하된다.As will be described in detail below, in the manufacturing of the protective film of the present invention, the manufacturing process of the edge reinforcement film unit, the tempered glass film unit and the shatterproof film is greatly different. Due to the decrease in productivity and yield, profitability is significantly reduced.

따라서 본 발명의 보호필름 제조방법은 각 필름 유니트를 별도로 제조하여 최종적으로 각 필름 유니트를 합지하여 제조하는 것을 특징으로 한다.Therefore, the method for manufacturing a protective film of the present invention is characterized by manufacturing each film unit separately and finally manufacturing each film unit by lamination.

구체적으로 도 6을 참고하면, 본 발명에 따른 디스플레이용 보호필름의 제조방법은, 박막의 강화유리 표면에 기능성 박막층을 형성하여 강화유리필름 유니트를 제작하는 제1공정(S10)과; 대상 전자기기의 디스플레이 전면의 사이즈와 대응되도록 마련된 보강필름에 개구부를 갖도록 테두리 보강필름 유니트를 제작하는 제2공정(S20)과; 상기 테두리 보강필름 유니트의 외곽 사이즈와 대응되는 사이즈를 갖는 고투명도의 PET필름에 광학적으로 투명한 광학점착제를 도포하여 비산방지필름 유니트를 제작하는 제3공정(S30)과; 상기 제1공정, 제2공정, 제3공정에서 각각 제작된 강화유리필름 유니트, 테두리 보강필름 유니트 및 비산방지필름 유니트를 합지하는 제4공정(S40)을 포함한다.
Specifically, referring to Figure 6, the manufacturing method of the protective film for a display according to the present invention, the first step (S10) to form a functional thin film layer on the surface of the tempered glass of the thin film to produce a tempered glass film unit; A second step S20 of manufacturing an edge reinforcement film unit to have an opening in the reinforcement film provided to correspond to the size of the front surface of the display of the target electronic device; A third step (S30) of manufacturing an anti-scattering film unit by applying an optically transparent optical adhesive to a high transparency PET film having a size corresponding to the outer size of the edge reinforcement film unit; And a fourth step S40 of laminating the tempered glass film unit, the edge reinforcement film unit, and the shatterproof film unit produced in the first step, the second step, and the third step, respectively.

제1공정(S10)은 강화유리필름 유니트를 제조하는 공정으로, 앞서도 설명한 바와 같이 유리를 박판 형태의 강화유리필름으로 가공하는 공정(S11)과, 가공이 완료된 강화유리필름의 일면에 방오 코팅층을 코팅하는 공정(S12)으로 구성되어 강화유리필름 유니트를 제작하며, 이때 강화유리필름의 사이즈는 제2공정에서 제작되는 테두리 보강필름 유니트의 개구부 사이즈와 동일한 사이즈를 갖도록 제작된다.The first step (S10) is a step of manufacturing a tempered glass film unit, as described above, the process of processing the glass into a thin tempered glass film (S11), and the antifouling coating layer on one surface of the finished tempered glass film It is composed of a coating process (S12) to produce a tempered glass film unit, wherein the size of the tempered glass film is manufactured to have the same size as the opening size of the edge reinforcement film unit produced in the second process.

제2공정(S20)은 중앙에 개구부를 갖는 테두리 보강필름 유니트를 제작하는 공정으로, 테두리 보강필름 유니트의 재질에 따라서 적절한 가공 방법에 의해 제작될 수 있다.The second step (S20) is a step of manufacturing the edge reinforcement film unit having an opening in the center, it can be produced by a suitable processing method according to the material of the edge reinforcement film unit.

예를 들어, 금속재질의 테두리 보강필름 유니트인 경우에는 금속 판재를 주지의 프레스 금형 공정을 통해 제작할 수 있으며, 또는 수지 재질의 테두리 보강필름 유니트에서는 주지의 사출금형 공정또는 프레스 금형을 통하여 제작이 이루어질 수 있다.For example, in the case of a metal frame reinforcement film unit, the metal plate may be manufactured through a known press mold process, or a resin frame reinforcement film unit may be manufactured through a known injection mold process or a press mold. Can be.

바람직하게는, 테두리 보강필름 유니트에 형성되는 개구부는 대상 전자기기의 디스플레이 전면 화상부의 사이즈와 동일한 사이즈를 갖도록 제작하며, 이때 대상 전자기기의 비화상부에 마련되는 버튼 또는 스피커의 위치에 따라서 천공홀이 형성될 수 있다.Preferably, the opening formed in the edge reinforcement film unit is manufactured to have the same size as the size of the image on the front surface of the display of the target electronic device, wherein the perforation hole is formed according to the position of the button or speaker provided in the non-image portion of the target electronic device. Can be formed.

한편 테두리 보강필름 유니트의 제조 공정 중에는 주지의 항균물질이 포함되는 공정이 추가될 수 있다.Meanwhile, during the manufacturing process of the edge reinforcement film unit, a process including a known antibacterial material may be added.

제3공정(S30)은 비산방지필름 유니트를 제조하는 공정으로 고투명도를 갖는 PET 필름 기재의 양면에 점착제를 도포하는 공정으로 이루어지며, 이때 비산방비필름 유니트의 사이즈는 테두리 보강필름 유니트의 외곽 사이즈와 동일한 사이즈를 갖는다.The third step (S30) is a process for manufacturing a shatterproof film unit is a process of applying a pressure-sensitive adhesive on both sides of the PET film base material having a high transparency, wherein the size of the scattering film unit is the outer size of the edge reinforcement film unit Have the same size as.

한편, 비산방지필름 유니트의 제조 공정 시에는 대상 전자기기의 비화상부에 마련되는 버튼 또는 스피커의 위치에 따라서 천공홀이 형성될 수 있음은 자명할 것이다.On the other hand, in the manufacturing process of the shatterproof film unit it will be apparent that the perforation hole may be formed according to the position of the button or the speaker provided in the non-image portion of the target electronic device.

다른 한편으로, PET 필름 기재의 양면에 도포되는 접착제는 구분되어 도포될 수 있다.On the other hand, the adhesive applied to both sides of the PET film substrate may be applied separately.

예를 들어, 비산방지필름 유니트에서 강화유리필름 유니트 및 테두리 보강필름 유니트와 접합되는 접착제는 견고히 접착이 이루어질 수 있도록 강한 접착력을 갖는 광학접착제가 사용될 수 있으며, 이러한 광학접착제로는 아크릴 또는 실리콘계열의 광학접착제가 사용될 수 있다. 한편, 디스플레이 전면에 부착을 위해 사용되는 광학점착제는 기포가 발생하지 않으면서 여러 차례 반복하여 사용되어도 점착력이 지속될 수 있도록 가시광 영역에 대해 광학적으로 투명한 광학점착제가 이용될 수 있으며, 광학점착제로는 실리콘 또는 우레탄계열의 점착제에 의해 제공될 수가 있다.For example, the adhesive bonded to the tempered glass film unit and the edge reinforcement film unit in the anti-scattering film unit may be used an optical adhesive having a strong adhesive force to be firmly bonded, such an optical adhesive is acrylic or silicone-based Optical adhesives can be used. On the other hand, the optical adhesive used for adhesion to the front of the display may be used an optically transparent optical adhesive for the visible region so that the adhesive force can be maintained even if repeated use without repeated bubbles, the silicone as an optical adhesive Or it may be provided by a urethane-based adhesive.

이와 같이 제조되는 비산방지필름 유니트는 다음의 합지 공정까지 오염물에 의해 오염되는 것을 방지하고 비산방지필름 유니트 표면을 보호하기 위하여 이형지가 추가로 접합될 수가 있다.The shatterproof film unit manufactured as described above may be further bonded with release paper to prevent contamination by contaminants until the next lamination process and to protect the surface of the shatterproof film unit.

제4공정(S40)은 제1,2,3공정에서 제작된 각각의 필름 유니트를 합지하는 공정으로, 이형지가 부착된 비산방지필름 유니트에서 이형지를 제거하고 강화유리필름 유니트와 테두리 보강필름 유니트를 합지하여 보호필름으로 제작이 이루어진다.The fourth step (S40) is a step of laminating the respective film units produced in the first, second, and third processes, removing the release paper from the scattering prevention film unit to which the release paper is attached, and removing the tempered glass film unit and the edge reinforcement film unit. It is made of laminated protective film.

이후 검수 등의 후공정(S50)을 거쳐서 최종 제품으로 생산이 이루어질 수 있다.
Thereafter, the production may be made as a final product through a post-process such as inspection (S50).

이상에서 설명한 본 발명은 전술한 실시예 및 첨부된 도면에 의해 한정되는 것이 아니고, 본 발명의 기술적 사상을 벗어나지 않는 범위 내에서 여러 가지 치환, 변형 및 변경이 가능함은 본 발명이 속하는 기술분야에서 통상의 지식을 가진 자에게 명백할 것이다.
The present invention described above is not limited to the above-described embodiment and the accompanying drawings, and various substitutions, modifications, and changes are possible within the scope without departing from the technical spirit of the present invention. It will be evident to those who have knowledge of.

1 : 휴대폰 10 : 화상부
20 : 비화상부 110 : 테두리 보강필름
111 : 개구부 112 : 무선인식태그
120 : 강화유리필름 130 : 비산방지층
140 : 광학점착층1 cell phone 10 burn part
20: non-image portion 110: edge reinforcement film
111: opening 112: radio recognition tag
120: tempered glass film 130: shatterproof layer
140: optical adhesive layer

Claims (9)

영상 정보를 출력하는 화상부와, 이 화상부의 테두리를 감싸는 비화상부가 디스플레이 전면부를 구성하게 되는 전자기기의 디스플레이용 보호필름에 있어서,
중앙에 개구부를 가지며 상기 비화상부의 전부 또는 일부를 덮도록 마련되는 테두리 보강필름과;
상기 개구부와 동일한 사이즈를 갖고 상기 개구부에 끼워 조립되는 강화유리필름과;
상기 테두리 보강필름과 강화유리필름의 저면에 일체로 접착되는 광학적으로 투명한 비산방지층과;
상기 비산방지층의 하면에 점착되어 전자기기의 디스플레이 표면에 점착이 가능한 광학점착층을 포함하는 디스플레이용 보호필름.In the protective film for display of an electronic device, the image portion for outputting the image information and the non-image portion surrounding the edge of the image portion constitutes the front surface of the display,
An edge reinforcement film having an opening at a center thereof and covering all or part of the non-image portion;
A tempered glass film having the same size as the opening and fitted into the opening;
An optically transparent scattering prevention layer integrally bonded to the bottom of the edge reinforcement film and the tempered glass film;
A protective film for a display comprising an optical adhesive layer that is adhered to the lower surface of the scattering prevention layer and is capable of adhesion to the display surface of the electronic device. 제1항에 있어서, 상기 개구부는 화상부와 동일한 사이즈를 갖는 것을 특징으로 하는 디스플레이용 보호필름.The protective film for display of claim 1, wherein the opening has the same size as the image part. 제2항에 있어서, 상기 화상부와 동일한 사이즈의 개구부를 갖는 테두리 보강필름에는 디스플레이 전면부에 구비되는 버튼 또는 스피커가 바깥으로 노출되도록 천공홀을 갖는 것을 특징으로 하는 디스플레이용 보호필름.The display protective film of claim 2, wherein the edge reinforcement film having an opening having the same size as the image part has a perforation hole so that a button or a speaker provided on the front surface of the display is exposed to the outside. 제1항에 있어서, 상기 테두리 보강필름에는 무선인식태그가 추가로 구비되는 것을 특징으로 하는 디스플레이용 보호필름.The protective film for display of claim 1, wherein the edge reinforcement film is additionally provided with a wireless recognition tag. 제1항에 있어서, 상기 광학점착층은 실리콘 또는 우레탄계열의 점착제인 것을 특징으로 하는 디스플레이용 보호필름.According to claim 1, wherein the optical adhesive layer is a protective film for display, characterized in that the adhesive of silicone or urethane series. 제1항에 있어서, 상기 테두리 보강필름과 강화유리필름의 모서리는 모따기되거나 곡면인 것을 특징으로 하는 디스플레이용 보호필름.According to claim 1, wherein the edge of the edge reinforcement film and the tempered glass film is a protective film for display, characterized in that the chamfered or curved surface. 하기의 제2공정에서 제작되는 테두리 보강필름 유니트의 개구부 사이즈와 동일한 사이즈를 갖도록 마련된 박막의 강화유리 표면에 기능성 박막층을 형성하여 강화유리필름 유니트를 제작하는 제1공정과;
대상 전자기기의 디스플레이 전면의 사이즈와 대응되도록 마련된 보강필름에 개구부를 갖도록 테두리 보강필름 유니트를 제작하는 제2공정과;
상기 테두리 보강필름 유니트의 외곽 사이즈와 대응되는 사이즈를 갖는 고투명도의 PET필름에 광학적으로 투명한 광학점착제를 도포하여 비산방지필름 유니트를 제작하는 제3공정과;
상기 제1공정, 제2공정, 제3공정에서 각각 제작된 강화유리필름 유니트, 테두리 보강필름 유니트 및 비산방지필름 유니트를 합지하는 제4공정을 포함하는 디스플레이용 보호필름의 제조방법.A first step of manufacturing a tempered glass film unit by forming a functional thin film layer on the surface of the tempered glass of the thin film provided to have the same size as the opening size of the edge reinforcement film unit produced in the second step;
A second step of manufacturing an edge reinforcement film unit to have an opening in the reinforcement film provided to correspond to the size of the front surface of the display of the target electronic device;
A third step of manufacturing an anti-scattering film unit by applying an optically transparent optical adhesive to a high transparency PET film having a size corresponding to the outer size of the edge reinforcing film unit;
And a fourth step of laminating the tempered glass film unit, the edge reinforcement film unit, and the shatterproof film unit produced in the first step, the second step, and the third step, respectively. 제7항에 있어서, 상기 제1공정에서 상기 기능성 박막층은 방오 코팅층인 것을 특징으로 하는 디스플레이 보호필름의 제조방법.The method of claim 7, wherein the functional thin film layer is an antifouling coating layer in the first process. 제7항에 있어서, 상기 개구부의 사이즈는 대상 전자기기의 디스플레이 전면 화상부의 사이즈와 동일한 것을 특징으로 하는 디스플레이 보호필름의 제조방법.The method of claim 7, wherein the size of the opening is the same as the size of the image on the front surface of the display of the target electronic device.
KR1020110136939A 2011-12-19 2011-12-19 Display protecting sheet and manufacturing method thereof KR101265240B1 (en)