KR101255735B1 - Water-absorbent paper and its preparation method - Google Patents
Water-absorbent paper and its preparation method Download PDFInfo
- Publication number
- KR101255735B1 KR101255735B1 KR1020110015248A KR20110015248A KR101255735B1 KR 101255735 B1 KR101255735 B1 KR 101255735B1 KR 1020110015248 A KR1020110015248 A KR 1020110015248A KR 20110015248 A KR20110015248 A KR 20110015248A KR 101255735 B1 KR101255735 B1 KR 101255735B1
- Authority
- KR
- South Korea
- Prior art keywords
- sheet
- absorbent
- hanji
- layer
- paraffin film
- Prior art date
Abstract
본 발명은 흡수성 한지 시트 및 이의 제조방법에 관한 것으로서, 구체적으로 나트륨 폴리아크릴레이트, 폴리아크릴아미드, 아타풀자이트를 포함하는 것을 특징으로 하는 흡수성 한지 시트가 제공되며, 특히 본 발명에서는 수분을 이용하지 않는 한지 합지 과정을 채택하고 한지 내에 특정 흡수 물질과 합지용 물질을 첨가하여 고흡수성 한지 시트를 제공함으로써, 높은 흡수성능 및 충분한 합지성능을 보일 수 있는 효과를 보인다.The present invention relates to an absorbent hanji sheet and a method of manufacturing the same, and specifically, an absorbent hanji sheet is provided comprising sodium polyacrylate, polyacrylamide, attapulgite, and in particular, the present invention does not use water. By adopting the lamination process, and adding a specific absorbent material and lamination material in the hanji to provide a superabsorbent hanji sheet, it shows an effect that can exhibit a high absorption performance and sufficient lamination performance.
Description
본 발명은 흡수성 한지 시트 및 이의 제조방법에 관한 것이다.The present invention relates to an absorbent hanji sheet and a method of manufacturing the same.
산업전분야에 걸쳐 제품의 포장지는 습기로부터 제품을 보호하고 위생을 유지하기 위한 목적으로 널리 사용되고 있으며, 그 종류도 매우 다양하다. 이 중에서 흡수성 시트는 통상적으로 수분 흡수를 목적으로 요실금 팬티나 생리대, 기저귀 등수분 흡수 목적의 제품에 부착되어 사용되며, 그 재질로는 흡수성을 갖는 견면솜이나 면의 직포 또는 부직포를 하나 이상 겹쳐 사용하고 있다.The packaging of products is widely used throughout the industry for the purpose of protecting products from moisture and maintaining hygiene. Among these, the absorbent sheet is generally used to be attached to products for moisture absorption such as urinary incontinence panties, sanitary napkins, diapers, etc. for the purpose of absorbing moisture, and one or more layers of absorbent cotton or cotton woven or nonwoven fabrics are used. Doing.
또한, 흡수제품은 피부와 접촉되는 액체 투과성의 상부시트, 이를 통과한 분비물을 흡수하여 보유하는 흡수체, 분비물이 흡수체로부터 외부로 누액되는 것을 방지하는 액체 불투과성의 배면시트를 기본적으로 포함하여 구성되며, 신체에 고정될 수 있도록 하는 체결수단을 갖게 된다. 흡수제품은 착용자에 의해 배설되는 분비물을 많이 흡수하고 사용 시 편안함을 제공하기 위해, 높은 흡수 용량과 부드러운 표면 촉감 및 내구성을 필요로 한다. In addition, the absorbent product basically includes a liquid permeable top sheet that comes into contact with the skin, an absorbent that absorbs and retains secretions that pass through it, and a liquid impermeable backsheet that prevents secretions from leaking out of the absorber to the outside. It will have a fastening means to be fixed to the body. Absorbent products require high absorption capacity, soft surface feel and durability to absorb much of the excretion excreted by the wearer and to provide comfort in use.
한편, 닥나무 껍질을 원료로 하는 한지는 천연 재료로 만들어지므로 자연이 가지는 질감을 그대로 가지고 있으며, 원료가 저피로 매우 질기며 그 수명도 양지나 천보다도 내구성이 우수하다. 또한, 한지는 양지에 비해 습기 흡수성과 습기조절이 우수하며, 섬유 사이에 적당한 공간을 가지고 있어서 공기를 소통시키는 통기성이 있고, 햇빛을 투과시키는 특성을 가지고 있을 뿐만 아니라, 냄새를 제거하는 소취성과 항균성 및 원적외선 방사의 특성을 가지고 있다.On the other hand, Hanji, which is made from the bark of bark, is made of natural materials, so it has the texture of nature. In addition, Hanji has excellent moisture absorption and moisture control compared to sunny, has a suitable space between the fibers, it is breathable to communicate air, has the property of transmitting sunlight, deodorant and antibacterial to remove odor and It has the characteristics of far-infrared radiation.
이와 같은 우수성에도 불구하고, 한지 그 자체만으로는 흡수성 제품에 사용할 정도의 흡수성능을 보이기는 어려워서, 한지만으로는 해당 제품에 사용하기에 어려움이 있다. 뿐만 아니라, 한지의 합지 과정에 그동안 필수적으로 사용되던 수분으로 인해서, 한지 내에 흡수성 물질을 포함시켜 한지를 제조하는 것 역시 큰 제한이 따른다.In spite of such superiority, it is difficult to show the absorbent performance enough to be used in absorbent products by itself, but it is difficult to use in the product alone. In addition, due to the moisture that has been used essentially during the papermaking process of Hanji, it is also a big limitation to manufacture hanji by including an absorbent material in the hanji.
이와 같은 종래의 어려움을 극복하고자, 본 발명에서는 수분을 이용하지 않는 한지 합지 과정을 채택하고 한지 내에 특정 흡수 물질과 합지용 물질을 첨가하여 고흡수성 한지 시트를 제공함으로써, 높은 흡수성능 및 충분한 합지성능을 보일 수 있는 고흡수성 한지 시트 및 이의 제조방법을 제공하고자 한다.In order to overcome such conventional difficulties, the present invention adopts a paper lamination process without using moisture and adds a specific absorbent material and a paper lamination material into the paper to provide a superabsorbent paper sheet, thereby providing high absorption performance and sufficient lamination performance. It is intended to provide a super absorbent Hanji sheet and a method for manufacturing the same.
본 발명의 일 측면에 따르면, 나트륨 폴리아크릴레이트, 폴리아크릴아미드, 아타풀자이트를 포함하는 것을 특징으로 하는 흡수성 한지 시트가 제공된다.According to one aspect of the invention, there is provided an absorbent hanji sheet comprising sodium polyacrylate, polyacrylamide, attapulgite.
본 발명의 다른 측면에 따르면, (a) 제1 한지 시트층, (b) 상기 제1 한지 시트층 위의 제1 파라핀 필름층, (c) 상기 제1 파라핀 필름층 위의 흡수성 물질층, (d) 상기 흡수성 물질층 위의 제2 파라핀 필름층, (e) 상기 제2 파라핀 필름층 위의 제2 한지 시트층을 포함하는 흡수성 합지 시트가 제공된다.According to another aspect of the invention, (a) a first Hanji sheet layer, (b) a first paraffin film layer on the first hanji sheet layer, (c) an absorbent material layer on the first paraffin film layer, ( and d) a second paraffin film layer over the absorbent material layer, and (e) a second paper sheet sheet over the second paraffin film layer.
일 구현예에 따르면, 상기 흡수성 물질은 나트륨 폴리아크릴레이트, 폴리아크릴아미드, 아타풀자이트을 포함하는 것을 특징으로 하는 흡수성 합지 시트가 제공된다.According to one embodiment, the absorbent material is provided with an absorbent laminated sheet, characterized in that it comprises sodium polyacrylate, polyacrylamide, attapulgite.
다른 구현예에 따르면, 상기 흡수성 물질은, 상기 제1 한지 시트 10 cm × 10 cm 크기 기준으로, 나트륨 폴리아크릴레이트 1-3 g, 아타풀자이트 0.5-1 g, 폴리아크릴레이트 0.5-1 g의 혼합물인 것을 특징으로 하는 흡수성 합지 시트가 제공된다.According to another embodiment, the absorbent material may include 1-3 g of sodium polyacrylate, 0.5-1 g of attapulgite, and 0.5-1 g of polyacrylate, based on a size of 10 cm × 10 cm of the first sheet of paper. An absorbent laminated sheet is provided which is a mixture.
본 발명의 또 다른 측면에 따르면, (A) 제1 한지 시트층 위에 제1 파라핀 필름층을 위치시키는 단계, (B) 상기 제1 파라핀 필름층 위에 흡수성 물질층을 위치시키는 단계, (C) 상기 흡수성 물질층 위에 제2 파라핀 필름층을 위치시키는 단계, (D) 상기 제2 파라핀 필름층 위에 제2 한지 시트층을 위치시켜 흡수성 한지 복합층을 형성시키는 단계, (E) 상기 흡수성 한지 복합층을 압착하는 단계를 포함하는 흡수성 합지 시트 제조방법가 제공된다.According to another aspect of the invention, (A) positioning the first paraffin film layer on the first sheet of Hanji sheet, (B) positioning the absorbent material layer on the first paraffin film layer, (C) the Positioning a second paraffin film layer on the absorbent material layer, (D) placing a second hanji sheet layer on the second paraffin film layer to form an absorbent hanji composite layer, (E) the absorbent hanji composite layer Provided is a method for producing an absorbent laminated sheet comprising the step of pressing.
일 구현예에 따르면, 상기 흡수성 물질은 나트륨 폴리아크릴레이트, 폴리아크릴아미드, 아타풀자이트을 포함하는 것을 특징으로 하는 흡수성 합지 시트 제조방법이 제공된다.According to one embodiment, the absorbent material is provided with a method for producing an absorbent laminated sheet characterized in that it comprises sodium polyacrylate, polyacrylamide, attapulgite.
다른 구현예에 따르면, 상기 흡수성 물질은, 상기 제1 한지 시트 10 cm × 10 cm 크기 기준으로, 나트륨 폴리아크릴레이트 1-3 g, 아타풀자이트 0.5-1 g, 폴리아크릴레이트 0.5-1 g의 혼합물인 것을 특징으로 하는 흡수성 합지 시트 제조방법이 제공된다.According to another embodiment, the absorbent material may include 1-3 g of sodium polyacrylate, 0.5-1 g of attapulgite, and 0.5-1 g of polyacrylate, based on a size of 10 cm × 10 cm of the first sheet of paper. Provided is a method for producing an absorbent laminated sheet, which is a mixture.
본 발명에 의하여 개발된 흡수체는 장시간 분비물이 방치될 수 있고 양이 많을 수도 있는 상황 및 피부에 민감한 신체와 위생적인 측면 등을 고려하여, 기존의 흡수체 시트보다 훨씬 높은 흡수성과 부드러운 질감 및 통기성을 갖는 시트를 얻을 수 있다. 이에 위생성 및 흡수제품의 다양한 용도에 적용이 가능하고, 분비물이 외부로 누액 되는 문제를 해결할 수 있다.The absorbent developed by the present invention has much higher absorbency and softer texture and breathability than the existing absorbent sheet in consideration of a situation in which secretion may be left for a long time and may be quantitative, and a skin-sensitive body and hygienic aspects. A sheet can be obtained. This can be applied to various uses of hygiene and absorbent products, and can solve the problem of leakage of secretion to the outside.
피부와 미용에 대한 소비자의 관심이 높아짐에 따라 제품의 다양한 기능성 및 용도에 맞는 제품을 선택하는 경향성이 늘고 있다. 또한 생리적, 위생적 기능성 제품을 선택할 때 소비자들이 더욱 제품의 본래의 기능과 부가적인 측면도 생각하여 제품의 종류가 다각화되는 양상이다.As consumers' interest in skin and beauty increases, there is an increasing tendency to select products for various functions and uses of the products. In addition, when selecting a physiological and hygiene functional product, consumers are more diversified in consideration of the original function and additional aspects of the product.
상술한 바와 같이 본 발명은 피부에 부드러운 촉감을 제공하며 습도조절 및 통기성이 좋고 세균에 대한 항균성이 우수한 한지를 시트로 적용하여, 양이 많거나 자주 갈아주지 못하는 소비자의 욕구를 본 발명의 고흡수성 한지 시트로 제품의 적용시 이를 해결할 수 있다.As described above, the present invention provides a soft touch to the skin, and applies a Hanji sheet as a sheet for controlling humidity and breathability and having excellent antimicrobial properties against bacteria, thereby absorbing a large amount of the consumer's desire to change or not frequently absorbing the present invention. Hanji sheet can solve this problem.
본 발명에 의해 제조된 고 흡수성 한지 시트를 제조시 흡수성이 높아 기존의 흡수체보다 적은 양으로도 그 이상의 흡수력을 얻을 수 있고, 이를 통해 경제적 절감의 효과를 기대해 볼 수 있다.High absorbency when manufacturing a high-absorbent Hanji sheet produced by the present invention can be obtained even more absorbent power in a smaller amount than the existing absorbent, through which the effect of economic savings can be expected.
물질 입수처Substance
PAPSS (폴리아크릴산 나트륨 부분 염 또는 나트륨 폴리아크릴레이트)은 Sigma-Aldrich에서 구매하여 사용하였고(CAS#.76774-25-9), 아타풀자이트는 BASF에서 구매하여 사용하였으며(상품명 Attagel, CAS#.12174-11-7), 폴리아크릴아미드는 Kento Chemical에서 구매하여 사용하였다(CAS#.9003-05-8).PAPSS (sodium polyacrylate partial salt or sodium polyacrylate) was purchased from Sigma-Aldrich (CAS # .76774-25-9) and attapulgite was purchased from BASF (trade names Attagel, CAS # .12174). -11-7), polyacrylamide was purchased from Kento Chemical and used (CAS # .9003-05-8).
제조예Manufacturing example : 한지 시트 제조: Hanji sheet manufacture
1% 농도의 지료를 만들기 위해 백피(수입닥) 350 g과 물 350 L를 장섬유 고해기인 칼비터(대일기공, DM-822-1)에 넣고 30 분 동안 고해하였다. 이 지료를 298 mm × 298 mm의 사각 수초지기(대일기공, DM-831)를 이용하여 시편을 제작한 후, 흡취지(250 g/㎡) 2 장을 습지 위에 올려놓았다. 그리고 나서, 쿠우치 플레이트(102 mm)를 깔고, 쿠우치 롤(13 kg)을 이용하여 중앙으로부터 전후로 움직여 플레이트의 끝에서 6 mm 곳까지 5 회에 걸쳐 압착시켰다. 한지에 남아있는 수분을 제거하기 위해서 시트 프레스(대일기공, DM-837)로 340 kPa의 압력으로 압착을 시킨 후, 회전형 건조기(대일기공, DM-839)를 이용하여 120 ℃로 건조를 시킴으로써, 한지 시트를 제작하였다.In order to make a 1% feedstock, 350 g of Baekpi (Imported Soup) and 350 L of water were placed in a long fiber aviator Calbitter (Daeilong, DM-822-1) and beaten for 30 minutes. After the specimens were prepared using a 298 mm × 298 mm square weeding machine (Daeil Pore, DM-831), two sheets of suction paper (250 g / m 2) were placed on the wetland. Then, the couch plate (102 mm) was laid and it was moved back and forth from the center using the couch roll (13 kg) and crimped five times from the end of the plate to 6 mm. In order to remove the moisture remaining in the paper, press the sheet press (Daeil pore, DM-837) at a pressure of 340 kPa, and then dry it at 120 ° C using a rotary dryer (Daeil pore, DM-839). , Hanji sheet was produced.
비교예Comparative example 1: 한지 시트 제조 1: Hanji sheet manufacturer
제조예에서 제조한 한지 시트를 10 cm × 10 cm 크기로 자른 후, 히팅 프레스용 스테인레스 시트에 위에 놓고, 그 위에 파라핀 필름(Para film, Whatman)을 덮은 후, 한지를 다시 덮고, 스테인레스 시트로 덮었다. 한지 시트를 합지시키기 위해 히팅 프레스(오션 사이언스, MH-20)에 넣고 20 MPa의 압력과, 70 ℃로 10 분간 압착시켰다. 압착하고 10 분 후 다시 동일 조건으로 압착을 반복하였다.The Hanji sheet prepared in Preparation Example was cut into a size of 10 cm × 10 cm, placed on a stainless sheet for heating press, covered with a paraffin film (Para film, Whatman), and then covered with Hanji, and covered with a stainless sheet. . In order to laminate the Hanji sheet, it was put into a heating press (Ocean Science, MH-20) and pressed for 10 minutes at a pressure of 20 MPa and 70 ° C. After pressing, 10 minutes later, the pressing was repeated under the same conditions.
실시예Example 1: One: 고흡수성Superabsorbent 한지 시트 제조 Hanji sheet manufacturer
제조예에서 제조한 한지 시트를 10 cm × 10 cm 크기로 자른 후, 히팅 프레스용 스테인레스 시트에 위에 놓고, 그 위에 파라핀 필름(Para film, Whatman)을 덮었다. 파라핀 필름 위에 PAPSS 1.5 g, 아타풀자이트 0.75 g, 폴리아크릴아미드 0.75 g을 도포한 후, 그 위에 다시 파라핀 필름을 놓고 한지를 덮었다. 그 후 합지시키기 위하여, 스테인레스 시트로 덮고, 히팅 프레스(오션 사이언스, MH-20)에 놓고 20 MPa, 70 ℃로 10 분 동안 압착시켰다. 압착하고 10 분 후, 다시 동일한 조건으로 압착을 1회 반복하였다.The Hanji sheet prepared in Preparation Example was cut to a size of 10 cm × 10 cm, placed on a stainless sheet for heating press, and covered with a paraffin film (Whatman). After applying PAPSS 1.5 g, attapulgite 0.75 g, and polyacrylamide 0.75 g on the paraffin film, the paraffin film was put on it again and the hanji was covered. Then, for lamination, it was covered with a stainless sheet, placed on a heating press (Ocean Science, MH-20) and pressed at 20 MPa, 70 ° C. for 10 minutes. After 10 minutes of pressing, the pressing was repeated once under the same conditions.
시험예Test Example 1: 흡수성 테스트 1: absorbency test
비교예 1 및 실시예 1에서 제작된 한지 시트의 가운데 부분을 3 cm × 3 cm 크기로 절단하였다. 그리고 2개의 페트리 디쉬(Petri Dish)에 40 g의 물을 넣은 후, 절단된 한지 시트를 침지시킨 후 30 분 및 1 시간 경과 후의 흡수량을 측정하였다. 시편 각 중량(g)은 전자 저울(SARTORIUS, CP224S)로 측정하였으며, 그 결과를 아래 표 1로 나타내었다.The center part of the Hanji sheets produced in Comparative Example 1 and Example 1 was cut to a size of 3 cm × 3 cm. Then, 40 g of water was added to two Petri dishes, and the absorbed amount was measured after 30 minutes and 1 hour after immersing the cut Hanji sheet. Each weight (g) of the specimen was measured by an electronic balance (SARTORIUS, CP224S), the results are shown in Table 1 below.
비교예Comparative example 2: 고흡수성 한지 시트 제조 2: manufacture of super absorbent Hanji sheet
제조예에서 제조한 한지 시트를 10 cm × 10 cm 크기로 자른 후, 히팅 프레스용 스테인레스 시트에 위에 놓고, 그 위에 파라핀 필름(Para film, Whatman)을 덮었다. 파라핀 필름 위에 PAPSS 0.5 g, 아타풀자이트 1.25 g, 폴리아크릴아미드 1.25 g을 도포한 후, 그 위에 다시 파라핀 필름을 놓고 한지를 덮었다. 그 후 합지시키기 위하여, 스테인레스 시트로 덮고, 히팅 프레스(오션 사이언스, MH-20)에 놓고 20 MPa, 70 ℃로 10 분 동안 압착시켰다. 압착하고 10 분 후, 다시 동일한 조건으로 압착을 1회 반복하였다.The Hanji sheet prepared in Preparation Example was cut to a size of 10 cm × 10 cm, placed on a stainless sheet for heating press, and covered with a paraffin film (Whatman). 0.5 g of PAPSS, 1.25 g of attapulgite, and 1.25 g of polyacrylamide were applied on the paraffin film, and then the paraffin film was placed on it again to cover the paper. Then, for lamination, it was covered with a stainless sheet, placed on a heating press (Ocean Science, MH-20) and pressed at 20 MPa, 70 ° C. for 10 minutes. After 10 minutes of pressing, the pressing was repeated once under the same conditions.
시험예Test Example 2: 접착력 테스트 2: adhesion test
실시예 1 및 비교예 2에서 제작된 한지 시트의 가운데 부분을 3 cm × 3 cm 크기로 절단하였다. 그리고 2개의 페트리 디쉬(Petri Dish)에 40 g의 물을 넣은 후, 절단된 한지 시트를 침지시킨 후, 100 시간 경과 후 합지된 부위의 접착력을 육안으로 평가하여 비교하였다. 그 결과, 실시예 1에서 제조된 합지 시트의 경우 제작 초기와 큰 외관상의 차이를 찾아볼 수 없는 반면, 비교예 2에서 제작된 합지 시트의 경우에는 네 귀퉁이 합지 부분이 부분적으로 벌어져 있음을 확인하였다.The center part of the Hanji sheets produced in Example 1 and Comparative Example 2 was cut to a size of 3 cm × 3 cm. 40 g of water was added to two Petri dishes, and the cut sheet of paper was immersed, and after 100 hours, the adhesion of the laminated parts was visually evaluated and compared. As a result, in the case of the laminated sheet produced in Example 1 was not found a significant difference in appearance and the initial production, in the case of the laminated sheet produced in Comparative Example 2 it was confirmed that the four corners of the laminated portion partially open. .
Claims (7)
(B) 상기 제1 파라핀 필름층 위에 흡수성 물질층을 위치시키는 단계,
(C) 상기 흡수성 물질층 위에 제2 파라핀 필름층을 위치시키는 단계,
(D) 상기 제2 파라핀 필름층 위에 제2 한지 시트층을 위치시켜 흡수성 한지 복합층을 형성시키는 단계,
(E) 상기 흡수성 한지 복합층을 압착하는 단계를 포함하는 흡수성 합지 시트 제조방법.(A) placing a first paraffin film layer on the first Hanji sheet layer,
(B) placing a layer of absorbent material on the first paraffin film layer,
(C) placing a second paraffin film layer over the absorbent material layer,
(D) placing a second hanji sheet layer on the second paraffin film layer to form an absorbent hanji composite layer,
(E) absorbent paper sheet manufacturing method comprising the step of compressing the absorbent Hanji composite layer.