KR101216914B1 - Circuit breaker - Google Patents

Circuit breaker Download PDF

Info

Publication number
KR101216914B1
KR101216914B1 KR1020110025555A KR20110025555A KR101216914B1 KR 101216914 B1 KR101216914 B1 KR 101216914B1 KR 1020110025555 A KR1020110025555 A KR 1020110025555A KR 20110025555 A KR20110025555 A KR 20110025555A KR 101216914 B1 KR101216914 B1 KR 101216914B1
Authority
KR
South Korea
Prior art keywords
fixed connection
movable
contact
movable part
connection part
Prior art date
Application number
KR1020110025555A
Other languages
Korean (ko)
Other versions
KR20120107809A (en
Inventor
유원종
노만래
Original Assignee
엘에스산전 주식회사
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 엘에스산전 주식회사 filed Critical 엘에스산전 주식회사
Priority to KR1020110025555A priority Critical patent/KR101216914B1/en
Priority to CN201210068694.3A priority patent/CN102693885B/en
Publication of KR20120107809A publication Critical patent/KR20120107809A/en
Application granted granted Critical
Publication of KR101216914B1 publication Critical patent/KR101216914B1/en

Abstract

본 발명의 실시 예에 따른 배선용 차단기는 내부에 수용 공간을 형성하는 케이스와, 상기 케이스의 내부에 고정 배치되는 고정 연결부와, 상기 고정 연결부에 대해 회동 가능하게 배치되며, 전류를 유도하는 유도 고정부와 접점이 이루어지거나 이탈되는 가동부를 포함하며, 상기 고정 연결부 및 가동부 중 적어도 어느 하나는 흑연을 포함하는 조성물로 형성된 코팅층을 포함한다.The circuit breaker for wiring according to an embodiment of the present invention, a case for forming an accommodating space therein, a fixed connection part fixedly disposed in the case, and a rotatable arrangement with respect to the fixed connection part, and an induction fixed part for inducing current. And a movable part in contact with or separated from each other, wherein at least one of the fixed connection part and the movable part includes a coating layer formed of a composition including graphite.

Description

배선용 차단기{CIRCUIT BREAKER}{CIRCUIT BREAKER}

본 발명은 배선용 차단기에 관한 것으로, 특히 내구성이 향상된 배선용 차단기에 관한 것이다.The present invention relates to a circuit breaker, and more particularly, to a circuit breaker with improved durability.

일반적으로, 배선용 차단기는 배전반 등에 설치되어 무부하 상태에서는 부하측에 전원을 공급 또는 차단하는 개폐장치의 역할을 하고, 부하 사용중에는 부하 전로에 이상 현상이 발생하여 부하 전류를 초과하는 대전류가 흐를 경우 전로의 전선 및 부하 측 기기를 보호하기 위하여 전원 측으로부터 부하 측으로 공급되는 전원을 공급 또는 차단하는 차단기의 역할을 담당하게 된다.In general, wiring breakers are installed in switchboards, etc., and act as a switchgear that supplies or cuts power to the load side under no load.When a large current exceeding the load current flows when an abnormal phenomenon occurs during load load, In order to protect the wires and load-side equipment, it serves as a circuit breaker that supplies or cuts off the power supplied from the power supply to the load.

이러한 배선용 차단기는, 내부에 수용공간을 형성하는 케이스, 상기 케이스의 내부에 고정 배치되는 고정접점 및 상기 고정접점에 대해 회동 가능하게 배치되는 가동접점을 구비한다.The wiring breaker includes a case forming an accommodation space therein, a fixed contact fixedly disposed inside the case, and a movable contact disposed rotatably with respect to the fixed contact.

또한, 배선용 차단기에는, 상기 가동접점이 상기 고정접점과 접촉되어 전류를 통전하는 투입위치와, 상기 가동접점이 상기 고정접점으로부터 분리되어 전류를 차단하는 차단위치(또는 트립위치)로 구동되도록 구동력을 발생하는 기구부가 구비된다.The circuit breaker further includes a driving force such that the movable contact is in contact with the fixed contact and energizes the current, and the movable contact is driven from the fixed contact to the interruption position (or trip position) to cut off the current. A mechanism part for generating is provided.

또한, 상기 배선용 차단기에는 사고 전류 등 이상 전류를 자동으로 검출하여 상기 기구부가 상기 가동접점이 상기 고정접점으로부터 신속하게 분리되게 동작하도록 하는 트립부가 구비된다.In addition, the circuit breaker is provided with a trip part for automatically detecting an abnormal current such as an accident current so that the mechanism part is quickly detached from the fixed contact.

한편, 통상적으로 전기 기기의 고정 접점 및 가동 접점의 원재료는 동(Cu) 소재의 도체이며, 부식 방지 및 도전율 유지를 위하여 상기 동 소재 표면에 은도금으로 표면 처리를 한다.On the other hand, the raw materials of the fixed contact and the movable contact of the electrical equipment is usually a conductor of copper (Cu) material, and the surface of the copper material is surface-treated with silver plating to prevent corrosion and maintain conductivity.

그러나, 배선용 차단기를 온-오프하는 횟수가 증가하게 되면, 상기 고정 접점과 가동 접점의 접촉면에 경도, 밀착성 및 내마모성에 따른 문제가 발생하여 상기 은 도금층을 손상시키고, 이로 인해 부식 발생, 도전율 저하 및 접촉 저항 증가에 따른 과열이 발생하는 문제점이 있다.However, if the number of times of turning on / off the circuit breaker increases, a problem occurs in the contact surface between the fixed contact and the movable contact due to hardness, adhesion, and abrasion resistance, thereby damaging the silver plating layer. There is a problem that overheating occurs due to an increase in contact resistance.

본 발명은 표면 처리 신공법을 적용하여 배선용 차단기를 제조하여 종래 은도금 표면 처리시 발생하는 문제점을 개선할 수 있도록 한다.The present invention is to manufacture a circuit breaker by applying a surface treatment new method to improve the problems caused during conventional silver plating surface treatment.

본 발명에서 이루고자 하는 기술적 과제들은 이상에서 언급한 기술적 과제들로 제한되지 않으며, 언급되지 않은 또 다른 기술적 과제들은 아래의 기재로부터 제안되는 실시 예가 속하는 기술분야에서 통상의 지식을 가진 자에게 명확하게 이해될 수 있을 것이다. Technical problems to be achieved in the present invention are not limited to the technical problems mentioned above, and other technical problems not mentioned above are clearly understood by those skilled in the art to which the embodiments proposed from the following description belong. Could be.

본 발명의 실시 예에 따른 배선용 차단기는 내부에 수용 공간을 형성하는 케이스와, 상기 케이스의 내부에 고정 배치되는 고정 연결부와, 상기 고정 연결부에 대해 회동 가능하게 배치되며, 전류를 유도하는 유도 고정부와 접점이 이루어지거나 이탈되는 가동부를 포함하며, 상기 고정 연결부 및 가동부 중 적어도 어느 하나는 흑연을 포함하는 조성물로 형성된 코팅층을 포함한다.The circuit breaker for wiring according to an embodiment of the present invention, a case for forming an accommodating space therein, a fixed connection part fixedly disposed in the case, and a rotatable arrangement with respect to the fixed connection part, and an induction fixed part for inducing current. And a movable part in contact with or separated from each other, wherein at least one of the fixed connection part and the movable part includes a coating layer formed of a composition including graphite.

또한, 상기 고정 연결부는 상기 가동부의 일단과 결합되는 결합부를 포함하며, 상기 코팅층은 상기 고정 연결부의 결합부에 선택적으로 형성된다.In addition, the fixed connection portion includes a coupling portion coupled to one end of the movable portion, the coating layer is selectively formed on the coupling portion of the fixed connection portion.

또한, 상기 가동부는 상기 고정 연결부의 결합부와 접촉하는 접촉 면을 포함하며, 상기 코팅층은 상기 가동부의 접촉 면에 선택적으로 형성된다.In addition, the movable portion includes a contact surface in contact with the engaging portion of the fixed connection portion, the coating layer is selectively formed on the contact surface of the movable portion.

또한, 상기 고정 연결부와 가동부를 회동 가능하도록 결합시키는 가동부 핀을 더 포함하며, 상기 가동부 핀은 흑연을 포함하는 조성물에 의해 형성된 코팅층을 포함한다.The apparatus may further include a movable part pin for rotatably coupling the fixed connection part and the movable part, wherein the movable part pin includes a coating layer formed of a composition including graphite.

또한, 상기 고정 연결부 및 가동부는 은을 포함하는 도금액에 의해 형성된 은 도금층을 더 포함한다.The fixed connection part and the movable part further include a silver plating layer formed of a plating solution containing silver.

또한, 상기 은 도금층은 상기 코팅칭의 하지면을 포함하는 상기 고정 연결부 또는 가동부의 전 영역에 형성된다.In addition, the silver plating layer is formed in the entire region of the fixed connection portion or the movable portion including the base surface of the coating.

본 발명에 따른 실시 예에 의하면, 신표면 처리 공법인 흑연 코팅 공법으로 배선용 차단기의 개폐 기구부를 형성함으로써, 종래의 은 도금 공법으로 형성된 배선용 차단기가 가지는 통전 불량 및 온도 상승 문제를 개선할 수 있으며, 제품의 내구성을 향상시켜 수명을 연장할 수 있는 효과가 있다.According to the embodiment according to the present invention, by forming the opening and closing mechanism of the circuit breaker by the graphite coating method of the new surface treatment method, it is possible to improve the problem of poor current and temperature rise problems that the circuit breaker formed by the conventional silver plating method, It has the effect of extending the lifespan by improving its durability.

도 1은 본 발명의 실시 예에 따른 배선용 차단기의 주요 구성요소들을 개략적으로 나타내기 위하여 도시한 개략도이다.
도 2는 도 1에 도시된 배선용 차단기의 가동부 연결부를 도시한 조립 사시도이다.
도 3은 도 2에 도시된 가동부 연결부에 의해 조립된 배선용 차단기를 도시한 사시도이다.
도 4는 배선용 차단기의 작동 과정을 설명하기 위한 도면이다.
도 5는 본 발명의 실시 예에 따른 고정 연결부를 보다 구체적으로 나타낸 도면이다.
도 6은 본 발명의 실시 예에 따른 가동부를 보다 구체적으로 나타낸 도면이다.
도 7은 본 발명의 실시 예에 따른 배선용 차단기의 제조 방법을 단계별로 나타낸 흐름도이다.1 is a schematic view illustrating schematically the main components of a circuit breaker according to an exemplary embodiment of the present invention.
FIG. 2 is an assembled perspective view illustrating a movable part connecting part of the circuit breaker illustrated in FIG. 1.
FIG. 3 is a perspective view illustrating a circuit breaker assembled by the movable connector shown in FIG. 2.
4 is a view for explaining the operation of the circuit breaker.
5 is a view showing in more detail the fixed connection according to an embodiment of the present invention.
6 is a view showing in more detail the movable portion according to an embodiment of the present invention.
7 is a flowchart illustrating a step-by-step method of manufacturing a circuit breaker according to an exemplary embodiment of the present invention.

제안되는 실시 예에 대해서 기술하여 본다.The proposed embodiment will be described.

이하에서는 본 발명의 구체적인 실시 예를 도면과 함께 상세히 설명하도록 한다. 그러나, 본 발명의 사상이 제시되는 실시 예에 제한된다고 할 수 없으며, 또 다른 구성요소의 추가, 변경, 삭제 등에 의해서 퇴보 적인 다른 발명이나, 본 발명 사상의 범위 내에 포함되는 다른 실시 예를 용이하게 제안할 수 있다.Hereinafter, specific embodiments of the present invention will be described in detail with reference to the drawings. However, the spirit of the present invention is not limited to the embodiments presented, and other inventions which are further deteriorated by addition, change, deletion, etc. of other components, or other embodiments included within the scope of the present invention can be easily made. I can suggest.

본 발명에서 사용되는 용어는 가능한 현재 널리 사용되는 일반적인 용어를 선택하였으나, 특정한 경우는 출원인이 임의로 선정한 용어도 있으며, 이 경우 해당되는 발명의 설명 부분에서 상세히 그 의미를 기재하였으므로, 단순한 용어의 명칭이 아닌 용어가 가지는 의미로서 본 발명을 파악하여야 함을 밝혀 두고자 한다.The term used in the present invention was selected as a general term widely used as possible, but in some cases, the term is arbitrarily selected by the applicant, in which case the meaning is described in detail in the description of the invention, the name of a simple term It should be clear that the present invention is to be understood as a meaning of terms.

즉, 이하의 설명에 있어서, 단어 '포함하는'은 열거된 것과 다른 구성요소들 또는 단계들의 존재를 배제하지 않는다.In other words, in the following description, the word 'comprising' does not exclude the presence of other elements or steps than those listed.

도 1은 본 발명의 실시 예에 따른 배선용 차단기의 주요 구성요소들을 개략적으로 나타내기 위하여 도시한 개략도이다.1 is a schematic view illustrating schematically the main components of a circuit breaker according to an exemplary embodiment of the present invention.

도 1을 참조하면, 배선용 차단기(20)는 전류가 배선용 차단기(20)의 내측으로 유도되어 흐를 수 있도록 도체로 이루어진 내부 유도 고정부(1)와, 상기 내부 유도 고정부(1)를 통해 흐르는 전류를 개폐 기구부(2)의 기구적 동작으로 상기 내부 유도 고정부(1)와 선택적으로 접점을 이루는 가동부(3)와, 상기 가동부(3)와 내부 유도 고정부(1)의 접점 간에 발생하는 아크(arc)를 소멸시켜주는 소호부(4)와, 상기 가동부(3)의 일단과 결합되는 고정 연결부(5)와, 상기 고정 연결부(5)에 연결되어 흐르는 전류를 외부로 유도시키는 도체로 이루어진 외부 유도 고정부(6)와, 이상 전류 및 사고 전류의 발생시 이를 검출하여 상기 개폐 기구부(2)를 작동시키는 트립부(7) 및 상기 개폐 기구부(2)를 수동으로 작동시키는 핸들(8)과, 상기 가동부(3)와 고정 연결부(5)를 결합시키는 가동부 연결부(10)로 구성된다.Referring to FIG. 1, the circuit breaker 20 flows through an internal induction fixing part 1 made of a conductor so that a current flows into the wiring breaker 20 and flows through the internal induction fixing part 1. The mechanical part of the opening / closing mechanism part 2 generates a current between the movable part 3 and the contact part of the movable part 3 and the internal induction fixing part 1. A arc extinguisher (4) for extinguishing an arc, a fixed connection part (5) coupled to one end of the movable part (3), and a conductor connected to the current connected to the fixed connection part (5) to guide the outside The external induction fixing unit 6, the trip unit 7 for operating the opening and closing mechanism unit 2 by detecting the occurrence of abnormal current and accident current and the handle 8 for manually operating the opening and closing mechanism unit 2 And, to couple the movable portion 3 and the fixed connection portion 5 It consists of a connection part (10).

도 2는 도 1에 도시된 배선용 차단기의 가동부 연결부를 도시한 조립 사시도이고, 도 3은 가동부 연결부에 의해 조립된 배선용 차단기를 도시한 사시도이다.FIG. 2 is an assembled perspective view illustrating a movable part connecting part of the wiring breaker illustrated in FIG. 1, and FIG. 3 is a perspective view illustrating a wiring breaker assembled by the movable part connecting part.

도 2 및 도 3을 참조하면, 가동부 연결부(10)는 가동부(3)의 일단부가 고정 연결부(5)에 가동부 핀(11)과 함께 한 쌍의 접촉 스프링(12)에 의해서 회동 가능하도록 결합된다.2 and 3, the movable portion connecting portion 10 is rotatably coupled to one end of the movable portion 3 by a pair of contact springs 12 together with the movable portion pin 11 on the fixed connection portion 5. .

또한, 상기 가동부(3)는 그 일단부의 소정 부위에 상기 가동부 핀(11)이 삽입될 수 있도록 삽입 홀(3a)이 형성되어 있고, 상기 고정 연결부(5)는 상기 가동부(3)의 일단부가 끼워져 가동부(3)의 일단부의 양 측면이 각각의 내측면에 접촉될 수 있도록 수직으로 대향하여 돌출되어 있는 접촉 측면부(5a)와, 상기 접촉 측면부(5a)의 소정 부위에 상기 가동부(3)가 삽입되어, 상기 가동부(3)의 삽입 홀(3a)과 연통될 수 있도록 형성되어 있는 삽입 홀(5b)과, 상기 각각의 접촉 측면부(5a)의 하부에서 수직 하부로 연장되어 소정 곡률로 수평으로 연장되고 다시 소정 곡률로 수직 하부로 연장되어 있는 지지부(5c) 및 상기 지지부(5c)의 단부가 그 양 측면부 위에 부착되어 있는 바닥부(5d)로 구성되어 있다.In addition, the movable portion 3 has an insertion hole 3a formed so that the movable portion pin 11 can be inserted into a predetermined portion of one end thereof, and the fixed connection portion 5 has one end portion of the movable portion 3. The movable side 3 is provided at a contact side portion 5a which is inserted and protrudes vertically to face both sides of one end of the movable portion 3 so as to be in contact with each inner side thereof, and at a predetermined portion of the contact side portion 5a. An insertion hole 5b which is inserted and is formed to be in communication with an insertion hole 3a of the movable portion 3, and extends vertically downward from a lower portion of each of the contact side portions 5a and horizontally with a predetermined curvature. It consists of a supporting portion 5c that extends and extends vertically downward again with a predetermined curvature, and a bottom portion 5d having an end portion of the supporting portion 5c attached on both side portions thereof.

또한, 상기 가동부(3)가 상기 고정 연결부(5)의 접촉 측면부(5a) 사이에 삽입된 상태에서 상기 가동부 핀(11)을 연결 접촉부(5)의 삽입 홀(5b)과 가동부(3)의 삽입 홀(3a)을 통과시키면, 상기 가동부 핀(11)의 양 단부가 상기 고정 연결부(5)의 측면으로부터 돌출된다. 이때 상기 접촉 스프링(12)을 가동부 핀(11)에 끼워서 접촉 스프링(12)의 단부를 가동부 핀(11)에 고정하면 상기 접촉 스프링(12)은 접촉 측면부(5a)를 밀게 되고 이에 접촉 측면부(5a)의 내측면과 가동부(3)의 외측면은 일정한 접촉력에 의해 접촉이 이루어진다.In addition, the movable part pin 11 is inserted between the insertion hole 5b of the connecting contact part 5 and the movable part 3 while the movable part 3 is inserted between the contact side parts 5a of the fixed connection part 5. When the insertion hole 3a is passed through, both ends of the movable part pin 11 protrude from the side surface of the fixed connection part 5. At this time, when the contact spring 12 is inserted into the movable pin 11 to fix the end of the contact spring 12 to the movable pin 11, the contact spring 12 pushes the contact side portion 5a and thus the contact side portion ( The inner surface of 5a) and the outer surface of movable part 3 are contacted by a constant contact force.

도 4는 배선용 차단기의 작동 과정을 설명하기 위한 도면이다.4 is a view for explaining the operation of the circuit breaker.

도 4를 참조하여, 상기 배선용 차단기의 작동 과정을 정격 전류가 흐를 경우와, 단락 전류가 흐를 경우로 나누어 설명하기로 한다.Referring to FIG. 4, the operation of the circuit breaker will be described by dividing the case when the rated current flows and the short circuit current flows.

먼저, 정격 전류가 흐를 경우에는 내부 유도 고정부(1)와 가동부(3)가 접점이 이루어지면, 전류는 내부 유도 고정부(1)에서 가동부(3)로 흐르게 된다. 이때, 가동부(3)를 흐르는 전류는 고정 연결부(5)의 양쪽의 접촉 측면부(5a)로 분기되어 흐르게 되고, 상기 지지부(5c)와 바닥부(5d)를 통해서 바닥부(5d)와 연결되어 있는 외부 유도 고정부(6)를 통해 정상적으로 흘러가게 된다.First, when the rated current flows, when the internal induction fixing part 1 and the movable part 3 make contact, the current flows from the internal induction fixing part 1 to the movable part 3. At this time, the current flowing through the movable portion 3 is branched to the contact side portion 5a of both sides of the fixed connection portion 5, and is connected to the bottom portion 5d through the support portion 5c and the bottom portion 5d. It flows normally through the external induction fixture (6).

다음으로, 단락 전류가 흐를 경우에는 내부 유도 고정부(1), 가동부(3) 및 고정 연결부(5)의 접촉 측면부(5a)로 분기된 상태에서, 정격 전류보다 단락 전류가 월등히 크기 때문에, 접촉 측면부(5a)와 지지부(5c) 사이에는 서로 끌어당기는 인력이 작용하여 가동부(3)와 고정 연결부(5) 사이의 접촉력을 증가시킨다.Next, when a short circuit current flows, since a short circuit current is much larger than a rated current in the state branched to the contact side part 5a of the internal induction fixed part 1, the movable part 3, and the fixed connection part 5, it contacts Attracting force between the side portion 5a and the support portion 5c acts to increase the contact force between the movable portion 3 and the fixed connection portion 5.

이때, 상기 가동부(3)와 고정 연결부(5) 사이의 접촉력이 증가함에 따라 상기 가동부(3)가 상방으로 회동하면서 전로를 개방하여 상기 단락 전류가 흐름으로 인해 발생될 수 있는 화재 등의 사고를 예방한다.At this time, as the contact force between the movable part 3 and the fixed connection part 5 increases, the movable part 3 rotates upwards to open a converter and cause an accident such as a fire that may occur due to the flow of the short circuit current. Prevent.

도 5는 본 발명의 실시 예에 따른 고정 연결부(5)를 보다 구체적으로 나타낸 도면이고, 도 6은 본 발명의 실시 예에 따른 가동부(3)를 보다 구체적으로 나타낸 도면이다.5 is a view showing in more detail the fixed connection part 5 according to an embodiment of the present invention, Figure 6 is a view showing in more detail the movable part 3 according to an embodiment of the present invention.

상기 고정 연결부(5)는 은을 포함하는 도금액에 의해 은 도금 표면 처리된 제 1 영역(A)과, 흑연을 포함하는 조성물에 의해 표면 처리된 제 2 영역(B)을 포함한다.The fixed connection part 5 includes a first region A surface-treated with a plating solution containing silver and a second region B surface-treated with a composition containing graphite.

이때, 상기 제 1 영역(A)은 상기 고정 연결부(5)의 전 영역에 대응된다 할 수 있다. 즉, 상기 고정 연결부(5)의 전 영역(A)은 부식 방지 및 도전율 향상을 위해 은 도금액으로 표면 처리된다.In this case, the first area A may correspond to the entire area of the fixed connection part 5. That is, the entire area A of the fixed connection part 5 is surface treated with a silver plating solution to prevent corrosion and improve conductivity.

상기 은 도금액은 은(Ag)을 포함하며, 여기에 팔라듐(Pd), 흑연(C) 및 로듐(Rh) 중 적어도 어느 하나 이상을 더 포함할 수 있다. 이와 같이 상기 은에 팔라듐 및 로듐을 첨가한 은 도금액을 이용하여 표면처리를 수행할 경우, 전류의 흐름과 윤활성인 미끄럼이 좋으며, 은만을 사용할 때와 대비하여 경도가 보완되어 내식성과 하지 도금의 마모를 방지할 수 있다.The silver plating solution includes silver (Ag), and may further include at least one of palladium (Pd), graphite (C), and rhodium (Rh). As described above, when surface treatment is performed using a silver plating solution in which palladium and rhodium are added to the silver, the flow of current and lubrication are good. Can be prevented.

다시 말해서, 상기 팔라듐은 상기 은보다 경도가 높아 내식성이 강화되며, 상기 로듐은 하지 도금의 마모성을 방지하고 윤활성을 보완하여 동작, 접촉 및 통전 동작 등을 강화하여 전기기기의 신뢰성을 향상시킨다. In other words, the palladium has a higher hardness than the silver, so that the corrosion resistance is enhanced, and the rhodium prevents abrasion of the underlying plating and supplements lubricity to enhance operation, contact, and energization, thereby improving reliability of the electric device.

또한, 상기 고정 연결부(5)는 흑연을 포함하는 조성물에 의해 표면 처리된 제 2 영역(B)을 포함하는데, 상기 제 2 영역(B)은 상기 제 1 영역(A)의 일 영역이며, 이는 상기 가동부(3)의 일단과 접촉하는 접촉 측면부(5a)에 대응된다.In addition, the fixed connection part 5 includes a second region B surface-treated with a composition comprising graphite, which is a region of the first region A, which is It corresponds to the contact side part 5a which contacts the one end of the said movable part 3.

즉, 상기 고정 연결부(5)를 상기 은 도금액을 이용한 표면처리만을 수행할 경우, 상기 가동부(3)의 회동에 의해 상기 가동부(3)와 접촉되는 은 도금면이 손상되게 된다.That is, when only the surface treatment using the silver plating solution is performed on the fixed connection part 5, the silver plated surface in contact with the movable part 3 is damaged by the rotation of the movable part 3.

이에 따라, 본 발명에 따른 실시 예에서는 상기 가동부(3)와 접촉하는 상기 고정 연결부(5)의 접촉 측면부(5a)를 흑연을 포함하는 조성물로 표면 처리하여, 상기 가동부(3)의 내마모성을 향상시킨다.Accordingly, in the embodiment according to the present invention, the contact side portion 5a of the fixed connection portion 5 in contact with the movable portion 3 is surface treated with a composition containing graphite, thereby improving wear resistance of the movable portion 3. Let's do it.

이때, 상기 흑연 표면 처리는 코팅 공법을 적용하여 실시한다.At this time, the graphite surface treatment is carried out by applying a coating method.

상기 코팅 공법은 도금 공법에 비해 공정이 단순하고, 수세 처리가 필요하지 않으므로, 물 사용이 필요없는 친환경적인 공법이며, 침착 및 건조로가 필요한 비교적 간단한 설비만이 필요한 공법이므로, 도금 공법에 비해 제조 비용을 감소시킬 수 있음과 동시에 환경 보전에 이바지할 수 있다.Since the coating method is simpler than the plating method and does not require washing, it is an environmentally friendly method that does not require the use of water, and it is a method requiring only a relatively simple facility requiring deposition and drying furnaces. In addition to reducing the risk, it can also contribute to environmental conservation.

상기에서, 상기 고정 연결부(5)의 접촉 측면부(5a)에만 선택적으로 흑연 표면 처리를 수행한다 하였지만, 제품의 신뢰성을 위해 상기 접촉 측면부(5a)에 연장되는 영역에도 선택적으로 상기 흑연 표면 처리를 수행할 수도 있다.In the above, although the graphite surface treatment is selectively performed only on the contact side portions 5a of the fixed connection portion 5, the graphite surface treatment is selectively performed on the region extending to the contact side portions 5a for the reliability of the product. You may.

상기와 같이, 상기 고정 연결부(5)에만 흑연 표면 처리를 수행한다 하더라도 배선용 차단기(20)의 내구성을 향상시킬 수 있지만, 본 발명에서는 가동부(3)에도 흑연 표면 처리를 적용하여 상기 배선용 차단기(20)의 내구성을 더욱 향상시킬 수 있도록 한다.As described above, even if the graphite surface treatment is performed only on the fixed connection portion 5, the durability of the circuit breaker 20 can be improved. However, in the present invention, the graphite circuit treatment is also applied to the movable portion 3 to provide the circuit breaker 20. ) To further improve durability.

즉, 도 6을 참조하면 상기 가동부(3)는 은 도금액에 의해 표면처리된 제 1 영역(A)과 흑연을 포함하는 조성물에 의해 표면 처리된 제 2 영역(B)을 포함한다.That is, referring to FIG. 6, the movable part 3 includes a first region A surface treated with a silver plating solution and a second region B surface treated with a composition containing graphite.

이때, 상기 제 2 영역(B)은 상기 고정 연결부(5)의 접촉 측면부(5a) 내부에 삽입되어, 상기 접촉 측면부(5a)의 내측면과 접촉하는 접촉 부위에 대응된다.In this case, the second region B is inserted into the contact side portion 5a of the fixed connection portion 5 and corresponds to the contact portion contacting the inner side surface of the contact side portion 5a.

결론적으로, 본 발명에 따른 실시 예에서는 상기 가동부(3)의 일단과 접촉하는 고정 연결부(5)의 일 영역과, 상기 고정 연결부(5)와 접촉하는 상기 가동부(3)의 일 영역은 흑연 코팅 공법으로 표면 처리를 수행하여 상기 배선용 차단기(20)의 내구성을 향상시킬 수 있도록 한다.In conclusion, in the embodiment according to the present invention, one area of the fixed connection part 5 in contact with one end of the movable part 3 and one area of the movable part 3 in contact with the fixed connection part 5 are graphite coated. Surface treatment may be performed by a method to improve durability of the circuit breaker 20.

이에 더하여, 본 발명에 따른 실시 예에서는 상기 가동부(3)의 삽입 홀(3a)과 고정 연결부(5)의 삽입 홀(5b)에 삽입되는 가동부 핀(11)에도 상기와 같은 흑연 코팅 공법을 적용하여 표면 처리를 수행하여, 상기 가동부(3)와 고정 연결부(5) 간의 결합력을 향상시킬 수 있도록 한다.In addition, in the embodiment according to the present invention, the graphite coating method is applied to the movable part pin 11 inserted into the insertion hole 3a of the movable part 3 and the insertion hole 5b of the fixed connection part 5b. Surface treatment to improve the bonding force between the movable portion 3 and the fixed connection portion 5.

상기와 같은 본 발명의 실시 예에 따른 배선용 차단기(20)에 의하면, 신표면 처리 공법인 흑연 코팅 공법으로 배선용 차단기의 가동부와 고정 연결부를 제조함으로써, 종래의 은 도금 공법으로 형성된 배선용 차단기가 가지는 통전 불량 및 온도 상승 문제를 개선할 수 있음과 동시에 제품의 내구성을 향상시켜 수명을 연장할 수 있다.According to the wiring breaker 20 according to the embodiment of the present invention as described above, by manufacturing the movable portion and the fixed connection portion of the circuit breaker by the graphite coating method of the new surface treatment method, the conduction failure of the wiring breaker formed by the conventional silver plating method And it is possible to improve the temperature rise problem and at the same time improve the durability of the product can be extended life.

도 7은 본 발명의 실시 예에 따른 배선용 차단기의 제조 방법을 단계별로 나타낸 흐름도이다.7 is a flowchart illustrating a step-by-step method of manufacturing a circuit breaker according to an exemplary embodiment of the present invention.

도 7을 참조하면, 우선적으로 가동부(3)와 고정 연결부(5)를 준비한다(1단계).Referring to FIG. 7, first, the movable part 3 and the fixed connection part 5 are prepared (step 1).

상기 가동부(3)와 고정 연결부(5)는 동(Cu)으로 제조되며, 가동부(3)의 형상에 대응되는 틀과, 고정 연결부(5)의 형상에 대응되는 틀을 이용하여 제조할 수 있다.The movable part 3 and the fixed connection part 5 are made of copper Cu, and may be manufactured using a mold corresponding to the shape of the movable part 3 and a mold corresponding to the shape of the fixed connection part 5. .

다음으로, 은을 포함하는 합금으로 이루어진 도금액으로 상기 준비된 가동부(3)와 고정 연결부(5)를 도금하여 상기 가동부(3)와 고정 연결부(5)를 표면 처리한다(2단계).Next, the movable part 3 and the fixed connection part 5 are plated with a plating solution made of an alloy containing silver to surface-treat the movable part 3 and the fixed connection part 5 (step 2).

상기 도금액은 은(Ag)을 포함하며, 팔라듐(Pd), 로듐(Rh) 및 흑연(C)을 더 포함할 수 있다. 상기 은(Ag)은 상기 가동부(3)와 고정 연결부(5)에 보다 높은 도전율을 제공하며, 상기 팔라듐(Pd)은 보다 높은 경도를 제공하며, 상기 로듐(Rh)은 도금층의 마모성을 방지한다. The plating liquid may include silver (Ag), and may further include palladium (Pd), rhodium (Rh), and graphite (C). The silver (Ag) provides higher conductivity to the movable portion (3) and the fixed connection portion (5), the palladium (Pd) provides a higher hardness, and the rhodium (Rh) prevents wear of the plating layer. .

다음으로, 상기 은을 포함하는 합금으로 이루어진 도금액에 의해 도금된 가동부(3)와 고정 연결부(5)를 건조시킨다(3단계).Next, the movable part 3 and the fixed connection part 5 which are plated by the plating liquid which consists of the said alloy containing silver are dried (3 step).

상기 건조 공정(3단계)은 25℃~30℃ 범위를 만족하는 온도에서 약 10분간 실시하는 것이 바람직하다. 이는, 상기 도금 표면 처리에 의해 상기 가동부(3)와 고정 연결부(5)에 발생한 수분(흡습)을 제거하기 위한 것으로, 상온에서 약 10분간 실시하도록 한다.The drying step (step 3) is preferably carried out for about 10 minutes at a temperature satisfying the range of 25 ℃ ~ 30 ℃. This is to remove moisture (hygroscopicity) generated in the movable part 3 and the fixed connection part 5 by the plating surface treatment, and it is performed for about 10 minutes at room temperature.

또한, 주위 환경에 따라 상기 건조 시간은 변경될 수 있을 것이다. 즉, 눈이나 비가 올 때에는 상기 건조 시간을 증가시켜 상기 건조 공정을 진행하는 것이 바람직하다.In addition, the drying time may vary depending on the surrounding environment. That is, when it is snowing or raining, it is preferable to advance the drying process by increasing the drying time.

다음으로, 상기 건조된 가동부(3)와 고정 연결부(5)의 특정 영역에 흑연을 포함하는 공법을 적용하여 표면 처리를 수행한다. 상기 특정 영역은 상기 가동부(3)와 고정 연결부(5) 사이의 접촉 부위에 대응되는 영역임이 바람직하다.Next, a surface treatment is performed by applying a method including graphite to a specific region of the dried movable part 3 and the fixed connection part 5. The specific area is preferably an area corresponding to the contact portion between the movable part 3 and the fixed connection part 5.

상기 흑연 표면 처리는 흑연으로 이루어진 CRC 액상에 상기 가동부(3)와 고정 연결부(5)의 특정 영역을 함침시키는 코팅 공법에 의해 수행된다. The graphite surface treatment is performed by a coating method of impregnating a specific region of the movable portion 3 and the fixed connection portion 5 in a CRC liquid phase made of graphite.

상기 흑연 표면 처리는 흑연 입자가 소재에 붙을 수 있는 시간인 10초가 바람직하고, 액상 농도의 변화에 대비하여 상기 액상을 지속적으로 저어주거나, 추가 보충해주는 것이 바람직하다.The graphite surface treatment is preferably 10 seconds, which is the time that the graphite particles can adhere to the material, it is preferable to continuously stir or supplement the liquid phase in preparation for the change in the liquid phase concentration.

또한, 상기 흑연 표면 처리시 상기 흑연 표면 처리 영역에 기포나 상처 등이 발생하지 않도록 한다.In addition, bubbles or scratches are not generated in the graphite surface treatment region during the graphite surface treatment.

상기 흑연 표면 처리를 수행한 이후에는 상기 흑연 표면 처리된 가동부(3)와 고정 연결부(5)를 건조시킨다(5단계).After the graphite surface treatment is performed, the movable surface 3 and the fixed connection portion 5 which are treated with the graphite surface are dried (step 5).

상기 건조 공정(5단계)은 통풍이 양호한 상온에서 자연 건조로 진행함이 바람직하다. 즉 상기 흑연 표면 처리된 가동부(3)와 고정 연결부(5)를 강제 건조할 경우, 상기 흑연 코팅 면이 갈라지는 현상이 발생하므로, 상기 흑연 표면 처리된 가동부(3)와 고정 연결부(5)를 자연 건조시킨다.The drying step (step 5) is preferably proceeded to natural drying at room temperature with good ventilation. That is, when the graphite surface-treated movable part 3 and the fixed connection part 5 are forcibly dried, the graphite coating surface is cracked, so that the graphite surface-treated movable part 3 and the fixed connection part 5 are naturally formed. To dry.

이후, 상기 건조된 가동부(3)와 고정 연결부(5)에 대해 재 흑연 표면 처리를 수행한다(6단계).Subsequently, ash graphite surface treatment is performed on the dried movable part 3 and the fixed connection part 5 (step 6).

즉, 본 발명에 따른 실시 예에서는 일정 시간 간격을 두고 복수 회 나누어 상기 가동부(3)와 고정 연결부(5)의 흑연 표면 처리를 수행한다.That is, in the embodiment according to the present invention, the graphite surface treatment of the movable part 3 and the fixed connection part 5 is performed by dividing a plurality of times at predetermined time intervals.

이때, 상기 흑연 표면 처리 수행 시간을 증가시켜, 상기 흑연 표면 처리 공정을 1회만 진행할 수도 있지만, 상기 흑연 표면 처리를 1회 진행하는 경우에는 균일한 두께의 흑연 코팅면을 확보할 수 없으며, 건조시 상기 흑연 코팅면이 갈라지게 되므로, 상기 흑연 표면 처리는 복수 회로 나누어 실시한다.At this time, the graphite surface treatment time may be increased to increase the graphite surface treatment process only once, but when the graphite surface treatment is performed once, the graphite coating surface having a uniform thickness may not be secured. Since the graphite coated surface is divided, the graphite surface treatment is performed in a plurality of circuits.

다음으로, 상기 재 흑연 표면 처리된 가동부(3)와 고정 연결부(5)를 건조시킨다(7단계).Next, the movable graphite 3 treated with the ash graphite surface and the fixed connection portion 5 are dried (step 7).

이때, 상기 건조 공정(7단계)은 2단계로 나누어 실시될 수 있다.At this time, the drying process (7 steps) may be carried out divided into two steps.

즉, 우선적으로 상기 재 흑연 표면 처리된 가동부(3)와 고정 연결부(5)를 통풍이 양호한 상온에서 자연 건조시킨다. 이때, 상기 자연 건조 조건은 25℃~30℃ 범위를 만족하도록 한다.That is, the movable graphite 3 and the fixed connection part 5 which are first treated with the ash graphite surface are naturally dried at room temperature with good ventilation. At this time, the natural drying conditions to satisfy the range of 25 ℃ ~ 30 ℃.

그리고, 상기 자연 건조된 가동부(3)와 고정 연결부(5)를 강제 건조시켜 상기 흑연 표면 처리된 코팅면의 밀착성을 확보한다.Then, the naturally dried movable part 3 and the fixed connection part 5 are forcibly dried to secure the adhesion of the graphite surface-treated coating surface.

이때, 상기 강제 건조 조건은 260℃~300℃ 범위의 온도에서 약 10분간 진행하는 것이 바람직하다. 또한 상기 온도 조건에 따라 상기 코팅면의 밀착성이 결정되므로, 상기 온도 조건을 벗어나지 않도록 함과 동시에 균일한 온도에서 상기 가동부(3)와 고정 연결부(5)가 건조되도록 관리하는 것이 바람직하다.At this time, the forced drying condition is preferably performed for about 10 minutes at a temperature of 260 ℃ ~ 300 ℃ range. In addition, since the adhesion of the coating surface is determined according to the temperature conditions, it is preferable not to deviate from the temperature conditions and to manage the movable part 3 and the fixed connection part 5 to dry at a uniform temperature.

다음으로, 내부 수용 공간을 형성하는 케이스에 상기 고정 연결부(5)를 배치하고, 가동부 핀(11)을 이용하여 상기 고정 연결부(5)에 가동부(3)를 결합시킨다(8단계).Next, the fixed connection part 5 is disposed in the case forming the inner accommodating space, and the movable part 3 is coupled to the fixed connection part 5 using the movable part pin 11 (step 8).

이때, 상기 고정 연결부(5)와 가동부(3)를 결합시키는 가동부 핀(11)도 상기 고정 연결부(5)와 가동부(3)와 함께 흑연 표면 처리를 수행하여, 상기 고정 연결부(5)와 가동부(3)의 결합력을 향상시키도록 함이 바람직하다.At this time, the movable part pin 11 which couples the fixed connection part 5 and the movable part 3 also performs graphite surface treatment together with the fixed connection part 5 and the movable part 3, so that the fixed connection part 5 and the movable part are provided. It is preferable to improve the bonding force of (3).

상기와 같은 본 발명의 실시 예에 따른 배선용 차단기(20)의 제조 방법에 의하면, 신표면 처리 공법인 흑연 코팅 공법으로 배선용 차단기의 가동부와 고정 연결부를 제조함으로써, 종래의 은 도금 공법으로 형성된 배선용 차단기가 가지는 통전 불량 및 온도 상승 문제를 개선할 수 있음과 동시에 제품의 내구성을 향상시켜 수명을 연장할 수 있다.According to the manufacturing method of the wiring breaker 20 according to the embodiment of the present invention as described above, by manufacturing the movable portion and the fixed connection of the circuit breaker by the graphite coating method of the new surface treatment method, the wiring breaker formed by the conventional silver plating method Eggplant can improve the problem of poor current and temperature rise, while improving the durability of the product can be extended.

또한, 본 발명의 실시 예들을 설명하였으나, 이 실시 예들에 의해 본 발명의 범위가 제한되지 않으며, 본 발명의 범위는 특허청구범위의 해석에 의해 정해진다. 전술한 실시 예들에 대해서는 다양한 변형이 가능하고 이들 변형 예들도 본 발명의 범위에 모두 포함된다.In addition, although embodiments of the present invention have been described, the scope of the present invention is not limited by these embodiments, and the scope of the present invention is defined by the interpretation of the claims. Various modifications are possible to the above-described embodiments, and these modifications are all included in the scope of the present invention.

20: 배선용 차단기
1: 내부 유도 고정부 2: 개폐 기구부
3: 가동부 4: 소호부
5: 고정 연결부 6: 외부 유도 고정부
7. 트립부 8: 핸들
10: 가동부 연결부20: circuit breaker
1: internal guide fixing part 2: opening and closing mechanism part
3: movable part 4: extinguishing part
5: fixed connection 6: external induction fixing
7. Trip section 8: handle
10: movable part connection

Claims (6)

내부에 수용 공간을 형성하는 케이스;
상기 케이스의 내부에 고정 배치되고, 제 1 삽입 홀이 형성되어 있으며, 흑연을 포함하는 조성물로 코팅된 제 1 코팅층을 포함하는 고정 연결부;
상기 고정 연결부에 대해 회동 가능하게 배치되어 전류를 유도하는 유도 고정부와 접점이 이루어지거나 이탈되고, 상기 제 1 삽입 홀과 연통하는 제 2 삽입 홀이 형성되어 있으며, 흑연을 포함하는 조성물로 코팅된 제 2 코팅층을 포함하는 가동부; 및
상기 제 1 및 2 삽입 홀에 삽입되어 상기 고정 연결부와 가동부를 회동 가능하도록 결합시키며, 흑연을 포함하는 조성물로 코팅된 가동부 핀을 포함하며,
상기 고정 연결부는 상기 가동부의 일단과 결합되는 결합부를 포함하고,
상기 가동부는 상기 고정 연결부의 결합부와 접촉하는 접촉면을 포함하며,
상기 제 1 코팅층은,
상기 가동부의 결합부에만 형성되고,
상기 제 2 코팅층은,
상기 가동부의 접촉면에만 형성되는
배선용 차단기.A case defining an accommodation space therein;
A fixed connection part fixedly disposed in the case, having a first insertion hole, and including a first coating layer coated with a composition including graphite;
A second insertion hole formed in contact with the induction fixing part which is rotatably disposed with respect to the fixed connection part and induces a current and communicates with the first insertion hole, and is coated with a composition including graphite A movable part including a second coating layer; And
A movable part pin inserted into the first and second insertion holes to rotatably couple the fixed connection part and the movable part and coated with a composition including graphite;
The fixed connection portion includes a coupling portion coupled to one end of the movable portion,
The movable portion includes a contact surface in contact with the engaging portion of the fixed connection portion,
The first coating layer,
Is formed only in the coupling portion of the movable portion,
The second coating layer,
It is formed only on the contact surface of the movable part
Circuit breakers. 삭제delete 삭제delete 삭제delete 제 1항에 있어서,
상기 고정 연결부 및 가동부는 은을 포함하는 도금액에 의해 형성된 은 도금층을 더 포함하는 배선용 차단기. The method of claim 1,
The fixed connection part and the movable part circuit breaker further comprises a silver plating layer formed by a plating liquid containing silver. 제 5항에 있어서,
상기 은 도금층은 상기 제 1 및 2 코팅층의 하지층을 포함하는 상기 고정 연결부 및 가동부의 전 영역에 형성되는 배선용 차단기.6. The method of claim 5,
The silver plating layer is a circuit breaker is formed in the entire area of the fixed connecting portion and the movable portion including the base layer of the first and second coating layer.
KR1020110025555A 2011-03-22 2011-03-22 Circuit breaker KR101216914B1 (en)