KR101211762B1 - Building materials using printingfilm and manufacturing method thereof - Google Patents

Building materials using printingfilm and manufacturing method thereof Download PDF

Info

Publication number
KR101211762B1
KR101211762B1 KR1020060122360A KR20060122360A KR101211762B1 KR 101211762 B1 KR101211762 B1 KR 101211762B1 KR 1020060122360 A KR1020060122360 A KR 1020060122360A KR 20060122360 A KR20060122360 A KR 20060122360A KR 101211762 B1 KR101211762 B1 KR 101211762B1
Authority
KR
South Korea
Prior art keywords
layer
film
printing
weight
parts
Prior art date
Application number
KR1020060122360A
Other languages
Korean (ko)
Other versions
KR20080051387A (en
Inventor
정근수
강석구
Original Assignee
(주)엘지하우시스
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by (주)엘지하우시스 filed Critical (주)엘지하우시스
Priority to KR1020060122360A priority Critical patent/KR101211762B1/en
Publication of KR20080051387A publication Critical patent/KR20080051387A/en
Application granted granted Critical
Publication of KR101211762B1 publication Critical patent/KR101211762B1/en

Abstract

본 발명은 이면층인 기재시트 상에 차례로 접착제층, 인쇄층, Primer 층 및 표면층인 폴리에틸렌 텔레프탈레이트(Polyethylene terephthalate; PET) 필름층을 형성시킨 건축 내장재 및 그의 제조방법에 관한 것이다. The present invention relates to a building interior material and a method for manufacturing the same, in which an adhesive layer, a printing layer, a primer layer, and a polyethylene terephthalate (PET) film layer are formed on a base sheet which is a back layer.

본 발명에 따른 상기 건축 내장재는 PET 필름상에 인쇄적성 부여를 위한 Primer 층을 형성하고, 상기 Primer 층에 인쇄층을 형성하여 인쇄필름을 제조한 후, 별도로 MDF, HDF 등과 같은 기재시트에 접착제층을 형성하고, 상기 인쇄필름의 인쇄층과 시재시트의 접착제층을 합지시켜 제조할 수 있다. The building interior material according to the present invention forms a primer layer for imparting printability on the PET film, and after forming a printing layer on the primer layer to produce a printing film, an adhesive layer on a base sheet such as MDF, HDF, etc. Forming, and can be prepared by laminating the adhesive layer of the printing layer and the test sheet of the printing film.

본 발명에 따른 상기 건축 내장재는 표면층이 PET 필름으로 형성되어 내스크래치, 내충격성 등이 우수한 효과가 있다.The building interior material according to the present invention has a surface layer is formed of a PET film is excellent in scratch resistance, impact resistance and the like.

인쇄필름, 기재시트, 합판, MDF, HDF, 건축내장재, PET 필름 Printing film, base sheet, plywood, MDF, HDF, building interior material, PET film

Description

인쇄 필름을 이용한 건축 내장재 및 그 제조 방법{BUILDING MATERIALS USING PRINTINGFILM AND MANUFACTURING METHOD THEREOF}Building interior materials using printing film and manufacturing method thereof {BUILDING MATERIALS USING PRINTINGFILM AND MANUFACTURING METHOD THEREOF}

도 1은 종래의 건축 내장재의 단면도이다.1 is a cross-sectional view of a conventional building interior materials.

도 2는 본 발명의 일 실시예에 따른 건축 내장재의 단면도이다. 2 is a cross-sectional view of the building interior according to an embodiment of the present invention.

도 3은 본 발명의 다른 실시예에 따른 건축 내장재의 단면도이다. 3 is a cross-sectional view of the building interior according to another embodiment of the present invention.

* 도면의 주요부분에 대한 부호의 설명 *Description of the Related Art [0002]

1; 내장재 10; PET 필름 One; Interior material 10; PET film

12; Primer 처리층 14; 인쇄층 12; Primer treated layer 14; Printing layer

16; 인쇄기재층 18; UV 코팅층 16; Printing substrate layer 18; UV coating layer

20; 기재시트 22; 접착제층 20; Base sheet 22; Adhesive layer

본 발명은 기재시트 상에 차례로 접착제층, 인쇄층, Primer 처리층 및 표면층인 폴리에틸렌 테레프탈레이트 필름 (Polyethylene terephthalate film; PET film) 이 적층된 건축 내장재 및 그의 제조방법에 관한 것이다. The present invention relates to a building interior material in which a polyethylene terephthalate film (PET film), which is an adhesive layer, a printing layer, a primer treatment layer, and a surface layer, is sequentially laminated on a base sheet.

종래의 바닥 장식재, 벽장재 또는 그 밖의 인테리어 자재와 같은 건축 내장재는 통상적인 기재상에 인쇄층이 형성된 멜라민지를 오버 레이지로 접착시켰다. 그런데 이 인테리어 자재는 촉감이 다른 소재에 비해 좋지 못하고, 종이기재 상부에 인쇄를 하여 채도가 떨어진다. 또한, 인쇄층이 형성된 폴리비닐클로라이드(PVC) 시트를 중밀도섬유판(MDF ; Medium Density Fiber Board), 고밀도섬유판(HDF ; High Density Fier Board) 또는 파티클보드(PB ; Particle Board) 와 같은 기재에 점/접착제로 부착하는 방법이 사용되고 있다. 그러나 위와 같이 제조된 벽장재 등의 인테리어 자재는 표면 강도가 약하다. 또한, 잉크층이 형성된 폴리에틸렌텔레프탈레이트(PET) 전사 필름을 기재에 열을 이용하여 전이시키는 제조방법이 있다. 그러나 그 제조 과정에서 전사된 PET 필름은 가공 후 폐기시켜 환경 문제를 유발하고 산업폐기물을 발생시키며 기재의 평활도에 따라 외관의 차이가 생긴다. 기재상에 인쇄필름을 형성하는 종래 기술의 예로서는 한국 공개 특허 제 10-2005-0121630호 및 한국 공개 특허 제 10-2006-0066819호 등을 들 수 있다. 상기 전자의 특허에서는 인쇄된 인쇄층을 HDF 기재 위에 접착을 시킬 경우 HDF의 표면 위에 오염이 되어 있으면 인쇄층 위로 전사되어 오염이 보이는 결점이 있다. Building interior materials, such as conventional floor coverings, closets, or other interior materials, have overlaid with melamine paper with printed layers formed on conventional substrates. However, this interior material is poor in touch compared to other materials, and the saturation is reduced by printing on the upper portion of the paper substrate. In addition, the polyvinyl chloride (PVC) sheet on which the print layer is formed may be applied to a substrate such as a medium density fiber board (MDF), a high density fiber board (HDF), or a particle board (PB). A method of attaching with an adhesive is used. However, interior materials such as the closet manufactured as described above has a weak surface strength. In addition, there is a manufacturing method for transferring a polyethylene terephthalate (PET) transfer film on which an ink layer is formed to a substrate using heat. However, the PET film transferred in the manufacturing process is disposed after processing, causing environmental problems, generating industrial waste, and the appearance difference according to the smoothness of the substrate. As an example of the prior art which forms a printing film on a base material, Korea Unexamined-Japanese-Patent No. 10-2005-0121630, Korea Unexamined-Japanese-Patent No. 10-2006-0066819, etc. are mentioned. In the former patent, when the printed printed layer is adhered onto the HDF substrate, if the printed layer is contaminated on the surface of the HDF, the transfer layer is transferred onto the printed layer and the contamination is seen.

또한, 상기 후자의 특허에서는 통상의 판상재의 양면 중 한 면 또는 양면에 표층을 형성시키고, 상기 표층상에 승화전사방식에 의해 인쇄층을 형성시키는 기술을 제공하고 있다. 그러나 상기 특허에 의한 승화전사 방식은 초기 인쇄 선명도는 향상되나 광 견뢰도가 떨어진다.Further, the latter patent provides a technique of forming a surface layer on one or both sides of an ordinary plate-like material and forming a printed layer on the surface layer by sublimation transfer. However, the sublimation transfer method according to the patent improves the initial print clarity but the light fastness.

한편, 기재시트 상에 인쇄층을 형성하고 그 위에 PET필름을 접착시킨 기술로서 일본국 공개특허공보 특개2001-80017(2001.03.27.공개)호 등이 개시되어 있으나, 기재시트에 인쇄층을 형성하는 경우는 기재시트의 평활도가 합성수지 필름에 비해 열악하기 때문에 인쇄 선명도 등이 떨어지는 결점이 있고, 그 평활도를 개선하기 위해서는 기재시트 상에 합성수지 코팅층을 형성해야 하는 단점이 남아있다.On the other hand, Japanese Patent Application Laid-Open No. 2001-80017 (published on March 27, 2001) and the like are disclosed as a technique of forming a printing layer on a base sheet and adhering a PET film thereon, but forming a printing layer on the base sheet. In the case of the smoothness of the base sheet compared to the synthetic film is poor, there is a disadvantage that the print clarity falls, etc., in order to improve the smoothness remains a disadvantage of forming a synthetic resin coating layer on the base sheet.

본 발명은 상기한 종래 기술의 문제점들을 해결하기 위한 것으로서 폴리에틸렌 텔레프탈레이트 필름 (Polyethylene terephthalate film; PET film)을 표면층으로 구성함으로써 산업폐기물 발생 및 환경오염을 방지하고 피착물에 접착 시 피착물의 평활도에 영향을 덜 받는 건축 내장재 및 그 제조 방법을 제공하려는 것이다. The present invention is to solve the problems of the prior art as described above by constructing a polyethylene terephthalate film (PET film) as a surface layer to prevent industrial waste generation and environmental pollution and to affect the smoothness of the adherend when adhered to the adherend It is to provide a building interior material and a method of manufacturing the less.

본 발명은 표면층인 상기 폴리에틸렌 텔레프탈레이트 필름 (Polyethylene terephthalate film; PET film)상에 직접 인쇄층을 형성함으로써 인쇄 선명도가 우수한 건축 내장재 및 그 제조 방법을 제공하려는 것이다.An object of the present invention is to provide a building interior material having excellent printing clarity and a manufacturing method thereof by forming a printing layer directly on the polyethylene terephthalate film (PET film) as a surface layer.

본 발명의 다른 목적은 표면층을 PET 필름으로 구성함으로써 내스크래치, 내충격성 등 표면 물성이 우수한 건축 내장재 및 그 제조방법을 제공하려는 것이다.Another object of the present invention is to provide a building interior material having excellent surface properties such as scratch resistance, impact resistance, and the manufacturing method by configuring the surface layer of a PET film.

본 발명의 또 다른 목적은 표면층을 구성하는 PET 필름의 일면에 프라이머 처리층을 형성시킴으로써 인쇄 적성을 향상시킨 건축 내장재 및 그 제조방법을 제공하려는 것이다.Still another object of the present invention is to provide a building interior material and a method for manufacturing the same, which improve printability by forming a primer treatment layer on one surface of a PET film constituting the surface layer.

본 발명에 따른 인쇄 필름을 이용한 건축 내장재는 이면층인 기재시트 상에 차례로 접착제층, 인쇄층, Primer 처리층 및 표면층인 폴리에틸렌 텔레프탈레이트(Polyethylene terephthalate; PET) 필름으로 구성되는 것을 특징으로 한다.The building interior material using the printing film according to the present invention is characterized by consisting of a polyethylene terephthalate (PET) film, which is an adhesive layer, a printing layer, a primer treatment layer, and a surface layer on a base sheet which is a back layer.

본 발명에 따른 상기 건축내장재는 폴리에틸렌 텔레프탈레이트(Polyethylene terephthalate; PET) 필름의 일면에 인쇄적성을 부여하기 위한 Primer처리층을 형성하고, 상기 Primer 처리층 위에 인쇄층을 형성하여 인쇄필름을 제조한 다음, 별도로 준비된 기재시트의 일면에 접착제층을 형성하고, 상기 접착제층과 상기 인쇄필름의 인쇄층이 접하도록 합지시켜 제조할 수 있다. The building interior material according to the present invention forms a primer treatment layer for imparting printability on one surface of a polyethylene terephthalate (PET) film, and forms a printing layer on the primer treatment layer to produce a printing film. The adhesive layer may be formed on one surface of the separately prepared base sheet, and may be manufactured by laminating the adhesive layer and the printing layer of the printing film.

본 발명은 통상 전사필름의 캐리어 필름으로서 전사 후에는 벗겨내어 폐기되는 폴리에틸렌 텔레프탈레이트(Polyethylene terephthalate; PET) 필름을 건축 내장재의 표면층으로 구성한 것을 특징으로 한다.The present invention is characterized in that a polyethylene terephthalate (PET) film, which is peeled off and discarded after transfer as a carrier film of a transfer film, is composed of a surface layer of a building interior material.

또한, 본 발명은 PET 필름의 인쇄 적성 및 부착력을 향상시키기 위하여 PET 필름의 일면에 Primer처리층을 형성시킨 것을 특징으로 한다. In addition, the present invention is characterized in that the primer treatment layer is formed on one surface of the PET film in order to improve the printability and adhesion of the PET film.

상기 Primer처리층은 PET 필름의 일면에 코팅되는 수지조성물의 코팅층 및/또는 PET 필름의 일면을 코로나 방전 처리한 처리층일 수 있다. 상기 수지조성물은 아크릴계 혹은 폴리우레탄(Polyurethane)계의 합성수지로 이루어지는 조성물이 사용될 수 있다. 이는 인쇄층의 잉크와 표면층과의 접착력과, 표면층과 접착제 층과의 접착력을 고려해야 하기 때문이다. The primer treatment layer may be a coating layer of a resin composition coated on one surface of the PET film and / or a treatment layer obtained by corona discharge treatment of one surface of the PET film. The resin composition may be a composition consisting of an acrylic resin or a polyurethane (polyurethane) synthetic resin. This is because the adhesion between the ink and the surface layer of the printing layer and the adhesion between the surface layer and the adhesive layer should be taken into account.

본 발명에 따른 상기 건축내장재는 표면층인 PET 필름 위에 인쇄층 및 표면 층 보호를 위한 통상적인 자외선 (UV)경화 수지 코팅층이 더 형성될 수 있다.The building interior material according to the present invention may be further formed with a conventional UV (UV) cured resin coating layer for protecting the print layer and the surface layer on the PET film surface layer.

또한, 본 발명에 따른 상기 건축내장재는 기재층의 이면에 점ㆍ접착제층이 형성된 이형지가 더 적층될 수 있다.In addition, the building interior material according to the present invention may further be laminated with a release paper having a point, the adhesive layer formed on the back surface of the base layer.

이하, 본 발명은 첨부한 도면을 참조하여 구체적으로 설명한다. Hereinafter, the present invention will be described in detail with reference to the accompanying drawings.

도 1은 종래의 건축 내장재의 적층구조의 단면도이고, 도 2는 본 발명의 일 실시예에 따른 건축 내장재의 적층구조의 단면도이며, 도 3은 본 발명의 다른 실시예에 따른 건축 내장재의 적층구조의 단면도를 나타낸 것이다. 1 is a cross-sectional view of a laminated structure of a conventional building interior material, Figure 2 is a cross-sectional view of a laminated structure of a building interior material according to an embodiment of the present invention, Figure 3 is a laminated structure of a building interior material according to another embodiment of the present invention It shows a cross-sectional view of the.

도1을 참조하면, 종래의 건축 내장재 중, 마루바닥재의 일예로서 맨 하부의 기재층(20)으로부터 접착제층(22), 인쇄기재층(24), 인쇄층(14) 및 표면층(또는 표면보호층)(10)이 차례로 적층된 구조를 나타낸 것이다.Referring to Fig. 1, as an example of the floor covering material, the adhesive layer 22, the printing substrate layer 24, the printing layer 14 and the surface layer (or surface protection) from the base substrate layer 20 at the bottom of the conventional building interior materials. Layer) 10 is shown stacked in sequence.

상기 종래의 마루바닥재는 크게 기재층과 표면시트층(인쇄기재층, 인쇄층 및 표면층) 그리고 상기 두 층을 결합시키는 접착제층으로 구성된 것으로서, 상기 기재층과 상기 표면시트층의 이면을 접착제로 접착시켜 제조된다.The conventional floorboard material is composed of a substrate layer and a surface sheet layer (printing substrate layer, printing layer and surface layer) and an adhesive layer that combines the two layers, and adheres the back surface of the substrate layer and the surface sheet layer with an adhesive. Are prepared.

상기 기재층(20)은 합판, 집성목, 중밀도파이버보드(Midium Density Fiberboard;MDF), 고밀도파이버보드(High Density Fiberboard; HDF), WPC(Wood Plastic Composite), 파티클보드 등과 같은 통상의 판상재로 이루어지고, 상기 기재시트와 표면시트는 에폭시계 또는 폴리우레탄계 접착제로 접착되며, 상기 인쇄층은 열가소성 합성수지를 원료로 하여 성형한 인쇄 기재층 위에 그라비아 인쇄, 전사인쇄, 승화인쇄, 실크스크린인쇄, 프린터를 이용한 실사인쇄 등을 통하여 형성되 고, 상기 표면층(또는 표면보호층)은 상기 인쇄층을 보호하면서 표면물성을 제공하는 기능층으로서 인쇄층의 인쇄무늬가 보이도록 투명 내지 반투명으로 PVC, PE, PP, PET 등과 같은 합성수지 조성물로 형성된다. The base layer 20 may be formed of a conventional plate material such as plywood, laminated wood, medium density fiberboard (MDF), high density fiberboard (HDF), wood plastic composite (WPC), particle board, or the like. Wherein, the base sheet and the surface sheet is bonded with an epoxy or polyurethane adhesive, the printing layer is gravure printing, transfer printing, sublimation printing, silk screen printing, printer on the printing substrate layer molded from thermoplastic synthetic resin as a raw material The surface layer (or surface protective layer) is formed through a live-printing using, and is a functional layer that provides surface properties while protecting the printed layer, and is transparent, translucent, transparent or translucent so that the printed pattern of the printed layer is visible. It is formed of a synthetic resin composition, such as PET.

도2을 참조하면, 본 발명의 바람직한 일 실시예에 따른 판상 건축내장재의 적층구조를 나타낸 단면도로서 이면층인 기재시트(20) 상에 차례로 접착제층(22), 인쇄층(14), Primer 처리층(12) 및 표면층인 폴리에틸렌 텔레프탈레이트(Polyethylene terephthalate; PET) 필름(10)이 적층된 구조를 보여주고 있다. Referring to Figure 2, a cross-sectional view showing a laminated structure of a plate-like building interior according to an embodiment of the present invention, the adhesive layer 22, the printing layer 14, Primer treatment in order on the backing sheet substrate 20 A layer 12 and a surface of a polyethylene terephthalate (PET) film 10, which is a surface layer, are stacked.

본 발명에 따른 상기 건축내장재는 PET 필름(10)의 일면에 인쇄적성을 부여하기 위한 Primer처리층(12)을 형성하고, 상기 Primer 처리층 위에 다양한 무늬나 문자 등을 인쇄한 인쇄층(14)을 형성하여 인쇄필름을 제조한 다음, 별도로 준비된 기재시트(20)의 일면에 접착제층(22)을 형성하고, 상기 기재시트(20)의 접착제층(22)과 상기 인쇄필름의 인쇄층(14)이 접하도록 기재시트(20)와 인쇄필름을 합지(합판)시켜 제조할 수 있다.The building interior material according to the present invention forms a primer treatment layer 12 for imparting printability on one surface of the PET film 10, and the printed layer 14 printed various patterns or characters on the primer treatment layer To form a printing film, and then to form an adhesive layer 22 on one surface of the substrate sheet 20 prepared separately, the adhesive layer 22 of the substrate sheet 20 and the printing layer 14 of the printing film. ) May be manufactured by laminating (plywood) the base sheet 20 and the printing film so as to contact each other.

본 발명에 따른 상기 기재시트(20)의 접착제층(22)과 합지되는 인쇄필름은 PET 필름(10)의 일면에 직접 다양한 무늬나 문자 등을 인쇄한 인쇄층(14)을 형성하여 제조할 수도 있다. The printing film laminated with the adhesive layer 22 of the base sheet 20 according to the present invention may be prepared by forming a printing layer 14 printed various patterns or letters directly on one surface of the PET film 10. have.

본 발명에서 상기 기재시트(20)와 인쇄필름을 합지(합판)시키는 접착제는 특별히 한정되지는 않지만, 상기 기재시트와 인쇄층의 접착이 용이하고, 장기간 접착력이 유지될 수 있는 접착제가 바람직하다. 이러한 접착제로서 예를 들면, 폴리 비닐아세테이트 (Polyvinylacetate; PVAc)계, 폴리올레핀(Polyolefin)계, 폴리우레탄(Polyurethane)계, 아크릴(Acryl)계, 폴리아미드(Polyamide)계, 폴리에스테르(Polyester)계, 에폭시(Epoxy)계 등의 접착제 중에서 선택, 사용할 수 있다. In the present invention, the adhesive for laminating (plywood) the substrate sheet 20 and the printing film is not particularly limited, but an adhesive capable of easily adhering the substrate sheet and the printing layer and maintaining adhesive strength for a long time is preferable. As such an adhesive, for example, polyvinylacetate (PVAc) -based, polyolefin-based, polyurethane (polyurethane), acrylic (Acryl), polyamide (polyester), polyester (Polyester), It can select and use from adhesives, such as an epoxy system.

본 발명에서 상기 폴리에틸렌 텔레프탈레이트(Polyethylene terephthalate; PET) 필름(10)은 전사필름의 캐리어필름으로 사용되는 통상적인 PET 필름으로서 본 발명의 표면층을 구성한다. 본 발명에서 표면층을 PET 필름으로 구성함으로써 산업 폐기물의 발생을 줄이고, 건축 내장재의 내마모성, 내스크래치, 내충격성 등 표면 물성을 크게 향상시킬 수 있다. 본 발명에서 PET 필름의 두께는 특별히 한정되지는 않지만 내구성이나 Primer처리층의 형성 등을 감암하면 20 내지 150 마이크론미터(㎛) 범위의 것이 바람직하다.In the present invention, the polyethylene terephthalate (PET) film 10 constitutes the surface layer of the present invention as a conventional PET film used as a carrier film of a transfer film. In the present invention, by forming the surface layer of PET film, it is possible to reduce the generation of industrial waste and to greatly improve the surface properties such as wear resistance, scratch resistance, impact resistance, and the like of building interior materials. In the present invention, the thickness of the PET film is not particularly limited, but the thickness of the PET film is preferably in the range of 20 to 150 micrometers (µm) in view of the durability and the formation of the primer treatment layer.

본 발명에서 상기 Primer처리층(12)은 인쇄적성 부여를 위한 처리층으로서 상기 표면층을 구성하는 PET 필름의 이면에 형성된다. 상기 Primer처리층(12)은 코로나 방전 처리층 및/또는 합성수지 조성물이 코팅된 투명코팅층이 될 수 있다. 상기 합성수지 조성물은 폴리우레탄(Polyurethane)계 또는 아크릴계 합성수지를 주재료로 이루어지는 조성물이 사용될 수 있다. 상기 우레탄계 수지 조성물로서 예를 들면, HMDI수지 35 중량부, 폴리올 45 중량부, 에폭시 수지 10 중량부, 멜라민 수지 10 중량부으로 구성될 수 있고, 아크릴계 수지 조성물로서는 메타크릴레이트(Methacrylate), 메틸메타크릴레이트(Methymethacrylate), 메타크릴산(Methacrylic Acid) 중에서 선택되는 1종 이상 50~55 중량부, 에틸아크릴레이트(Ethylacrylate), 부틸아크릴레이트(Buthylacrylate) 중에서 선택되는 1종 이상 40~45 중량부, 그 외 첨가제 5~10 중량부로 구성되어 있을 수 있다. In the present invention, the primer treatment layer 12 is formed on the back surface of the PET film constituting the surface layer as a treatment layer for imparting printability. The primer treatment layer 12 may be a transparent coating layer coated with a corona discharge treatment layer and / or a synthetic resin composition. The synthetic resin composition may be a composition consisting of polyurethane (polyurethane) or acrylic synthetic resin as a main material. As the urethane-based resin composition, for example, 35 parts by weight of HMDI resin, 45 parts by weight of polyol, 10 parts by weight of epoxy resin, 10 parts by weight of melamine resin, and the acrylic resin composition as methacrylate (Methacrylate), methyl meth At least 50 to 55 parts by weight selected from methacrylate and methacrylic acid, at least 40 to 45 parts by weight selected from ethyl acrylate and butyl acrylate; Other additives may be composed of 5 to 10 parts by weight.

본 발명에서 상기 인쇄층은 통상적인 점착시트의 인쇄층과 같은 것으로서 그라비아 인쇄, 오프셋인쇄, 스크린 인쇄 등과 같은 공지의 인쇄방법에 의해 형성된다.In the present invention, the printed layer is formed by a known printing method such as gravure printing, offset printing, screen printing, and the like as a printing layer of a conventional adhesive sheet.

본 발명에서 상기 기재시트(20)는 예를 들면, 합판, 집성목, 중밀도 파이버보드(Midium Density Fiberboard;MDF), 고밀도파이버보드(High Density Fiberboard; HDF), WPC(Wood Plastic Composite), 파티클보드 등과 같은 통상의 판상 시트 또는 합성수지 시트(필름)로 구성할 수 있다. 상기 기재시트(20)로 사용되는 합성수지 시트나 필름은 착색된 것이거나 투명 또는 반투명이어도 무방하다. In the present invention, the base sheet 20 is, for example, plywood, laminated wood, medium density fiberboard (MDF), high density fiberboard (High Density Fiberboard; HDF), WPC (Wood Plastic Composite), particle board It can comprise with normal plate-like sheets or synthetic resin sheets (film), such as these. The synthetic resin sheet or film used as the base sheet 20 may be colored, or may be transparent or translucent.

본 발명에 따른 상기 건축내장재의 제조방법은 PET 필름의 일면에 인쇄적성부여를 위한 Primer처리층을 형성하는 단계; 상기 Primer 처리층 위에 인쇄층을 형성하는 단계;를 포함하는 인쇄필름을 제조하는 단계;와, 기재시트를 준비하는 단계; 상기 기재시트의 일면에 접착제층을 형성하는 단계; 및 상기 기재시트에 형성된 접착제층과 상기 인쇄필름에 형성된 인쇄층이 접하도록 기재시트와 인쇄필름을 합지(합판)시키는 단계를 포함하여 제조되는 것을 특징으로 한다.Method for producing a building interior material according to the present invention comprises the steps of forming a primer treatment layer for imparting printability on one surface of the PET film; Forming a printing layer on the primer treatment layer; preparing a printing film comprising; and preparing a base sheet; Forming an adhesive layer on one surface of the base sheet; And laminating the base sheet and the print film such that the adhesive layer formed on the base sheet and the print layer formed on the print film are in contact with each other.

본 발명의 상기 건축내장재는 상기 PET 필름의 외표면에 자외선(UV) 경화 수지 코팅층을 형성하는 단계가 더 포함될 수 있다. PET 필름의 외표면에 UV코팅층을 형성하는 경우에는 공지의 자외선 경화 코팅조성물을 사용하여 통상적인 방법으로 형성할 수 있다. The building interior material of the present invention may further comprise forming an ultraviolet (UV) cured resin coating layer on the outer surface of the PET film. When forming the UV coating layer on the outer surface of the PET film can be formed by a conventional method using a known UV curing coating composition.

또한, 본 발명의 상기 건축내장재는 상기 기재시트의 이면에 점(접)착제가 코팅된 통상적인 이형지를 합판하는 단계가 더 포함될 수 있다.In addition, the building interior of the present invention may further comprise the step of plywood conventional release paper coated with a adhesive (glue) on the back of the base sheet.

본 발명에 따른 상기 건축내장재는 내장재의 기재시트의 이면이나 또는 피착물의 표면에 접(점)착제를 도포시켜 피착물에 부착, 사용하거나, 기재시트의 이면에 점(접)착제가 코팅된 이형층이 형성된 경우에는 이형지를 제거한 다음, 이를 피착물의 표면에 부착시켜 사용할 수 있다.The building interior material according to the present invention is applied to the adherend by applying a adhesive on the back of the base sheet or the surface of the substrate of the interior material, or use a release adhesive coated on the back of the substrate sheet If a layer is formed, the release paper can be removed and then attached to the surface of the adherend to be used.

따라서, 상기 구성에 따른 본 발명은 환경 문제를 해결하고 산업폐기물 발생을 감소시키며 피착물에 접착 시 피착물의 평활도에 영향을 덜 받는 효과가 있다. 본 발명의 인쇄 필름을 이용한 건축 내장재는 표면층을 PET 필름으로 구성함으로써 내스크래치, 내충격성 등 표면 물성이 우수한 효과가 있다.Therefore, the present invention according to the above configuration has the effect of solving environmental problems, reducing industrial waste generation, and less affected by the smoothness of the adherend when adhered to the adherend. Building interior materials using the printing film of the present invention has an excellent surface properties such as scratch resistance, impact resistance by configuring the surface layer of a PET film.

본 발명에 따른 인쇄 필름을 이용한 건축 내장재 및 그 제조 방법은 피이티(PET)필름에 비해 평활도가 떨어지는 기재시트에 직접 인쇄층을 형성시키는 것에 비해 인쇄 선명도 등 인쇄층이 우수할 뿐만 아니라, 기재시트의 평활도 개선을 위 한 합성수지 코팅공정을 생략할 수 있는 효과가 있다. Building interior materials using the printing film and the manufacturing method using the printing film according to the present invention is not only excellent in the print layer, such as print sharpness, but also the substrate sheet compared to forming a printed layer directly on the substrate sheet is less smooth than the PET film (PET) film There is an effect that can omit the synthetic resin coating process to improve the smoothness of.

또한, 표면이 약하여 각종 용제로 3～4회만 닦아도 인쇄된 무늬가 쉽게 지워지고 미세한 긁힘에도 쉽게 생채기가 발생하는 종래 일반 전사지 필름의 단점을 개선하여 내마모성, 내스크래치, 내충격성 등의 표면 강도를 향상시킨 내구성이 우수한 인테리어 자재로 인쇄 필름을 이용한 건축 내장재 및 그 제조 방법을 제공할 수 있다.In addition, the surface is weak to improve the surface strength, such as wear resistance, scratch resistance, impact resistance, etc. by improving the disadvantages of conventional transfer paper film that the printed pattern is easily erased even if wiped only three to four times with various solvents and the scratches easily occur even fine scratches It is possible to provide a building interior material using a printing film and a method of manufacturing the same as interior materials having excellent durability.

Claims (12)

이면층인 기재시트 상에 차례로 접착제층, 인쇄층 및 표면층으로 이루어지는 건축내장재에 있어서, 상기 표면층은 폴리에틸렌 텔레프탈레이트(Polyethylene terephthalate; PET) 필름이며, 상기 표면층이 인쇄층과 접하는 면에, 우레탄계 수지 조성물 또는 아크릴계 수지 조성물의 코팅층인 프라이머 처리층을 형성하되, 상기 우레탄계 수지 조성물은 HMDI수지 35 중량부, 폴리올 45 중량부, 에폭시 수지 10 중량부, 멜라민 수지 10 중량부로 구성되고, 상기 아크릴계 수지 조성물은 메타크릴레이트(Methacrylate), 메틸메타크릴레이트(Methymethacrylate), 메타크릴산(Methacrylic Acid) 중 하나 이상 선택된 것 50~55 중량부, 에틸아크릴레이트(Ethylacrylate), 부틸아크릴레이트(Buthylacrylate) 중 하나 이상 선택된 것 40~45 중량부, 그외 첨가제 5~10 중량부로 구성되는 것을 특징으로 하는 인쇄 필름을 이용한 건축 내장재. In a building interior material consisting of an adhesive layer, a printing layer, and a surface layer on a base sheet, which is a back layer, the surface layer is a polyethylene terephthalate (PET) film, and a urethane-based resin composition on a surface where the surface layer is in contact with the printing layer. Or a primer treatment layer which is a coating layer of an acrylic resin composition, wherein the urethane resin composition is composed of 35 parts by weight of HMDI resin, 45 parts by weight of polyol, 10 parts by weight of epoxy resin, and 10 parts by weight of melamine resin, and the acrylic resin composition is meta At least one selected from methacrylate, methyl methacrylate, and methacrylic acid 50 to 55 parts by weight, at least one selected from ethyl acrylate and butyl acrylate Print, characterized in that composed of 40 to 45 parts by weight, other additives 5 to 10 parts by weight Architectural interior materials using film. 삭제delete 삭제delete 삭제delete 제 1항에 있어서, The method of claim 1, 상기 표면층의 외표면에 자외선(UV)경화 수지코팅층이 더 형성된 것을 특징으로 하는 인쇄 필름을 이용한 건축 내장재.Building interior material using a printing film, characterized in that the ultraviolet (UV) cured resin coating layer is further formed on the outer surface of the surface layer. 제 1항에 있어서,The method of claim 1, 상기 기재시트의 이면에 점(접)착제가 코팅된 이형지가 합판된 것을 특징으로 하는 인쇄 필름을 이용한 건축 내장재.Building interior material using a printing film, characterized in that the release paper coated with a point (adhesive) adhesive on the back surface of the base sheet. 제 6항에 있어서,The method according to claim 6, 상기 표면층의 외표면에 자외선(UV)경화 수지코팅층이 더 형성된 것을 특징으로 하는 인쇄 필름을 이용한 건축 내장재.Building interior material using a printing film, characterized in that the ultraviolet (UV) cured resin coating layer is further formed on the outer surface of the surface layer. 폴리에틸렌 텔레프탈레이트(Polyethylene terephthalate; PET) 필름의 일면에 인쇄적성부여를 위한 우레탄계 수지 조성물 또는 아크릴계 수지 조성물을 코팅하여 프라이머 처리층을 형성한 다음, 상기 프라이머 처리층에 인쇄층을 형성하여 인쇄필름을 제조한 다음, 기재시트의 일면에 접착제층을 형성한 후, 상기 기재시트에 형성된 접착제층과 상기 인쇄필름에 형성된 인쇄층이 접하도록 기재시트와 인쇄필름을 합지(합판)시키는 단계를 포함하여 제조하되, 상기 우레탄계 수지 조성물은 HMDI수지 35 중량부, 폴리올 45 중량부, 에폭시 수지 10 중량부, 멜라민 수지 10 중량부로 구성되고, 상기 아크릴계 수지 조성물은 메타크릴레이트(Methacrylate), 메틸메타크릴레이트(Methymethacrylate), 메타크릴산(Methacrylic Acid) 중 하나 이상 선택된 것 50~55 중량부, 에틸아크릴레이트(Ethylacrylate), 부틸아크릴레이트(Buthylacrylate) 중 하나 이상 선택된 것 40~45 중량부, 그외 첨가제 5~10 중량부로 구성되는 것을 특징으로 인쇄 필름을 이용한 건축 내장재의 제조방법.Coating a urethane-based resin composition or an acrylic resin composition for printing aptitude on one side of the polyethylene terephthalate (PET) film to form a primer treatment layer, and then formed a printing layer on the primer treatment layer to produce a printed film Then, after the adhesive layer is formed on one side of the base sheet, the adhesive layer formed on the base sheet and the printing layer formed on the printing film, including the step of laminating (plywood) the base sheet and the print film to be in contact with The urethane resin composition includes 35 parts by weight of HMDI resin, 45 parts by weight of polyol, 10 parts by weight of epoxy resin, and 10 parts by weight of melamine resin, and the acrylic resin composition includes methacrylate and methyl methacrylate. , At least one selected from methacrylic acid 50 to 55 parts by weight, ethyl acrylate (E thylacrylate), butyl acrylate (Buthylacrylate) at least one selected from 40 to 45 parts by weight, and other additives 5 to 10 parts by weight of the manufacturing method of a building interior material using a printing film. 삭제delete 제 8항에 있어서,9. The method of claim 8, 상기 PET 필름의 외표면에 자외선(UV)경화 수지코팅층을 형성하는 단계가 더 포함된 것을 특징으로 인쇄 필름을 이용한 건축 내장재의 제조방법.Method for manufacturing a building interior material using a printing film, characterized in that it further comprises the step of forming an ultraviolet (UV) cured resin coating layer on the outer surface of the PET film. 제 8항에 있어서,9. The method of claim 8, 상기 기재시트의 이면에 점(접)착제가 코팅된 이형지를 합판하는 단계가 더 포함된 특징으로 인쇄 필름을 이용한 건축 내장재의 제조방법.Method of manufacturing a building interior material using a printing film, characterized in that further comprising the step of plywood the release paper coated with a point (adhesive) adhesive on the back of the base sheet. 제 10항에 있어서,The method of claim 10, 상기 기재시트의 이면에 점(접)착제가 코팅된 이형지를 합판하는 단계가 더 포함된 특징으로 인쇄 필름을 이용한 건축 내장재의 제조방법.Method of manufacturing a building interior material using a printing film, characterized in that further comprising the step of plywood the release paper coated with a point (adhesive) adhesive on the back of the base sheet.
KR1020060122360A 2006-12-05 2006-12-05 Building materials using printingfilm and manufacturing method thereof KR101211762B1 (en)