KR101211687B1 - Adhesive sheet composition for bedsores preventing mat and bedsores preventing mat using it - Google Patents
Adhesive sheet composition for bedsores preventing mat and bedsores preventing mat using it Download PDFInfo
- Publication number
- KR101211687B1 KR101211687B1 KR1020120120303A KR20120120303A KR101211687B1 KR 101211687 B1 KR101211687 B1 KR 101211687B1 KR 1020120120303 A KR1020120120303 A KR 1020120120303A KR 20120120303 A KR20120120303 A KR 20120120303A KR 101211687 B1 KR101211687 B1 KR 101211687B1
- Authority
- KR
- South Korea
- Prior art keywords
- weight
- parts
- rubber
- relative
- adhesive
- Prior art date
Abstract
Description
본 발명은 거동이 불편한 환자 및 마비로 인하여 신체 이동에 장애를 가진 사람들이 휠체어 및 좌식 생활을 장시간 유지할 때 발생하는 욕창을 방지하기 위한 욕창매트 및 이 욕창매트를 제조할 때 사용되는 접착시트 고무 조성물에 관한 것으로, 다수 개의 팽창공기주머니가 일체로 연결되어 형성된 상부시트와 하부시트를 접합한 부위에서 공기가 새나가지 않도록 한, 욕창매트용 접착시트 고무 조성물 및 욕창매트에 관한 것이다.
The present invention is a pressure-sensitive bed mat and adhesive sheet rubber composition used when manufacturing the bedsore mat for preventing bedsores that occur when people with impaired behavior and people with physical disabilities due to paralysis maintain a wheelchair and sedentary life for a long time The present invention relates to a pressure-sensitive adhesive sheet rubber composition and bedsore mats for bedsore mats in which air does not leak from a portion where the upper sheet and the bottomsheet are joined by a plurality of expansion air bags.
뇌졸중과 같은 뇌신경계에 있는 의식불명환자, 노환성 질환으로 병상에 누워지네는 환자, 사고에 의해 중상을 입어 거동이 불편한 환자 등과 같이 장시간 누워서 치료해야만 하는 환자는 바닥과 접촉하는 인체부분의 혈액순환이 원활하지 못하여 욕창이 걸리기 쉽다.Patients who need to lie down for long periods of time, such as unconscious patients in the brain's nervous system such as stroke, patients lying in bed with old-fashioned diseases, or those who are seriously injured by accidents and have difficulty in moving, It is not smooth and it is easy to get bedsores.
따라서 욕창의 형성을 방지하기 위해서는 환자의 체중을 완충적으로 지지하는 동시에 환자의 바닥과 접촉하는 인체부분에 통풍이 원활해지도록 환경을 조성할 필요가 있다.Therefore, in order to prevent the formation of bedsores, it is necessary to create an environment so as to buffer the weight of the patient and to facilitate ventilation of the human body in contact with the floor of the patient.
따라서 다수의 팽창되는 주머니 구조가 방석의 좌면에 형성된 욕창방지방석이 다수 개발되었다.Therefore, a number of anti-bedsore cushions in which a plurality of expanded pocket structures are formed on the seat of the cushion have been developed.
이와 관련된 기술로, "로테이션 몰딩에 의해 성형되는 욕창방지방석 및 그 욕창방지방석의 제조방법"(한국 등록특허공보 제10-0627629호, 특허문헌 1)에는 도 1 내지 2에 도시된 바와 같이 다수의 팽창주머니들(1) 및 팽창주머니들(1) 사이의 공기소통로(4)가 형성된 연결부(5)가 형성되는 상부구조(2)를 슬러쉬 몰딩에 의해 형성하고, 상부구조(2)의 아래에 평평한 막구조인 중간부(3)가 고주파 접합을 통해 접합되어 접합부(6)가 형성된 구성이 공개되어 있다.As a related technology, "a bedsore prevention cushion molded by rotation molding and a method of manufacturing the bedsore prevention cushion" (Korea Patent Publication No. 10-0627629, Patent Document 1) as shown in Figures 1 to 2 The upper structure (2) is formed by the slush molding, the upper structure (2) formed with the connection portion (5) formed with the expansion bag (1) and the air communication path (4) between the expansion bag (1), The structure in which the intermediate |
이 기술에서 공기를 주입시에 팽창주머니들(1) 각각이 중간부(3)로부터 들뜨지 않고 중간부(3)에 고정되도록 하기 위해 각 팽창주머니들(1)의 둘레가 중간부에 접합되어 접합부(6)를 형성한다.In this technique, the circumference of each of the expansion bags 1 is joined to the middle portion so that each of the expansion bags 1 is fixed to the
상부구조(2)의 각 팽창주머니들(1)의 내부공간들을 상호간 소통시켜 공기가 욕창방지방석의 전체로 주입되도록 하는 역할을 하는 연결부(5) 내측의 공기소통로(4)는 공기소통의 기능만 수행하면되므로 5㎜이하로 형성된다.The
이러한 종래의 욕창방지방석은 슬러쉬 몰딩을 사용하여 제조한 상부구조를 중간부와 접합해서 공기가 새어나가지 않도록 했기 때문에 상부구조와 중간부를 접합하는 공정이 필수적으로 요구되었다. The conventional bedsore prevention cushion is required to join the upper structure and the intermediate part because the upper structure manufactured by using the slush molding is bonded to the intermediate part so that air does not leak.
이와 같은 별도의 접합공정 때문에 제조시간이 증가하여 생산성이 좋지 못한 문제가 있었다.Due to such a separate bonding process, the manufacturing time increases, there is a problem that the productivity is not good.
또한 접합부가 완전히 밀폐되지 않거나 접합부가 서로 떨어지게 되면 공기가 누설되어 욕창방지방석을 수지하거나 교체해야 하는 문제점이 있었다.In addition, when the joints are not completely sealed or the joints are separated from each other, there is a problem that the resin leaks or replaces the bedsore prevention cushion.
이러한 문제점을 해소하기 위하여 상기 기술에서는 로테이션 몰딩 방법에 의해 상면과 하면이 접합부분 없이 일체로 성형되도록 하였으나, 이러한 로테이션 몰딩을 위해서는 고가의 장비를 이용해야 하는 문제점이 있었다.In order to solve this problem, in the above technology, the top and bottom surfaces are integrally formed without a joint by a rotation molding method, but there is a problem in that expensive equipment is used for the rotation molding.
또, 접착제를 사용하는 경우 접착제의 유해물질로 인해 인체에 사용시 적합하지 않고 환경호르몬 발생 문제도 있었다.In addition, when using the adhesive due to the harmful substances of the adhesive is not suitable for use in the human body there was also a problem of environmental hormone generation.
또한, 욕창매트의 경우 유연성이 높음과 더불어 높은 하중을 지지하게 되는데, 이러한 환경에서 기존의 접착제는 높은 하중하에서, 또 상부시트와 하부시트의 변형시 접착 부위가 떨어지게 되는 문제점이 있었다.
In addition, the bedsore mat is high in flexibility and supports high loads. In such an environment, the conventional adhesive has a problem in that the adhesive site falls under a high load and when the top sheet and the bottom sheet are deformed.
본 발명의 욕창매트용 접착시트 고무 조성물 및 이를 이용한 욕창매트는 상기와 같은 종래 기술에서 발생하는 문제점을 해소하기 위한 것으로, 로테이션 몰딩 장치와 같은 고가의 장치를 이용하지 않으면서, 상층부와 하층부 사이에 접착시트를 설치한 채 프레스로 가압하여 상층부와 하층부를 결합하되, 접착시트가 상층부 및 하층부에 완전히 밀폐되어 떨어지지 않음으로써 공기의 누설을 최대한 방지할 수 있게 하려는 것이다.Adhesive sheet rubber composition for the bedsore mat of the present invention and the bedsore mat using the same to solve the problems caused in the prior art, between the upper layer and the lower layer, without using an expensive device such as a rotation molding device While pressing the adhesive sheet with a press to combine the upper layer and the lower layer, the adhesive sheet is to be completely sealed to the upper layer and the lower layer to prevent the leakage of air to the maximum.
보다 구체적으로, 가황고무로 이루어지는 상층부와 하층부 사이에 접착시트를 설치하여 프레스로 가압하여 일체화시키는 단순한 공정으로 접합될 수 있도록 하려는 것이다.More specifically, the adhesive sheet is installed between the upper layer portion and the lower layer portion made of vulcanized rubber so as to be bonded in a simple process of pressing and integrating with a press.
이처럼 간단한 공정으로 접합이 이루어지면서도 가류제로 디티오디모포린을 사용하여 압축영구줄음율이 적도록 하고, 접착제로 레조시놀 포름알데히드 수지와 에테르화 메틸로멜라민 수지를 특정 비로 사용하여 접착 성능을 높이는 한편, 연화제로 천연 수지인 대두유를 원료로 사용하여 유연성을 높이고, 무독성인 제품을 제공할 수 있게 하려는 것이다.In this simple process, bonding is achieved, but dicomodimorphine is used as a vulcanizing agent, so that the compressive permanent shrinkage is low. In addition, soybean oil, which is a natural resin as a softener, is used as a raw material to increase flexibility and provide a non-toxic product.
더불어, 욕창매트의 상층부와 하층부의 조성을 특정하게 한정하되, 활성제로 산화아연과 스테아린산을 특정 비율로 한정하여 동적 특성을 높이면서 스코치의 발생을 줄여 내구성을 우수하게 유지할 수 있게 하려는 것이다.
In addition, the composition of the upper and lower layers of the bedsore mat is to be specifically defined, but to limit zinc oxide and stearic acid to a specific ratio as an activator to increase the dynamic characteristics while reducing the occurrence of scorch to maintain excellent durability.
본 발명의 욕창매트용 접착시트 고무 조성물은 상기와 같은 과제를 해결하기 위하여, 고무 100 중량부와; 상기 고무 100 중량부 대비 40 ~ 70 중량부의 카본블랙과; 상기 고무 100 중량부 대비 13 ~ 21 중량부의 접착제와; 상기 고무 100 중량부 대비 5 ~ 15 중량부의 연화제와; 상기 고무 100 중량부 대비 4 ~ 7 중량부의 노화방지제와; 상기 고무 100 중량부 대비 1 ~ 3 중량부의 가류제와; 상기 고무 100 중량부 대비 1 ~ 3 중량부의 가류조제;를 포함하여 구성된다.Adhesive sheet rubber composition for bedsore mat of the present invention, in order to solve the above problems, 100 parts by weight of rubber; 40 to 70 parts by weight of carbon black relative to 100 parts by weight of the rubber; 13 to 21 parts by weight of the adhesive relative to 100 parts by weight of the rubber; 5 to 15 parts by weight of a softener relative to 100 parts by weight of the rubber; 4 to 7 parts by weight of anti-aging agent relative to 100 parts by weight of the rubber; 1 to 3 parts by weight of a vulcanizing agent relative to 100 parts by weight of the rubber; It is configured to include; 1 to 3 parts by weight of a vulcanization aid relative to 100 parts by weight of the rubber.
이때, 상기 카본블랙은 60 중량부, 접착제는 17 중량부, 연화제는 10 중량부, 노화방지제는 6 중량부, 가류제는 1.5 중량부, 가류조제는 2.5 중량부로 이루어져 있으며, 접착제는 레조시놀 포름알데히드 수지 5 중량부와, 에테르화 메틸로멜라민 수지 12 중량부로 이루어져 있고, 상기 가류제는 디티오디모포린으로 이루어져 있는 것을 특징으로 한다.At this time, the carbon black is 60 parts by weight, the adhesive is 17 parts by weight, the softener is 10 parts by weight, the anti-aging agent is 6 parts by weight, the vulcanizing agent is 1.5 parts by weight, the vulcanization aid is 2.5 parts by weight, the adhesive is resorcinol It consists of 5 parts by weight of formaldehyde resin, 12 parts by weight of etherified methylomerelamine resin, characterized in that the vulcanizing agent is composed of dithiodimorpholine.
아울러, 본 발명의 욕창매트는, 다수의 팽창주머니가 형성되어 있고, 각각의 팽창주머니가 연결부를 통해 서로 연통되도록 형성되어 있는 상층부와; 상기 상층부와 동일한 재질로 이루어져 있으며, 상층부의 하부에 형성되어 있는 하층부와; 상기 상층부와 하층부 사이에 형성되어 있고, 상층부와 하층부 사이에 삽입된 채 프레스에 의해 가압되어 상층부와 하층부를 결합시키는 접착시트;로 구성되어 있되, 상기 상층부 및 하층부는, 고무 100 중량부와; 상기 고무 100 중량부 대비 보강제 20 ~ 30 중량부와; 상기 고무 100 중량부 대비 연화제 0.3 ~ 1 중량부와; 상기 고무 100 중량부 대비 5 ~ 9 중량부의 활성제와; 상기 고무 100 중량부 대비 노화방지제 3 ~ 5 중량부와; 상기 고무 100 중량부 대비 가황제 1 ~ 3 중량부와; 상기 고무 100 중량부 대비 가류조제 1 ~ 3 중량부를 포함하여 구성되어 있고, 상기 접착시트는, 고무 100 중량부와; 상기 고무 100 중량부 대비 40 ~ 70 중량부의 카본블랙과; 상기 고무 100 중량부 대비 13 ~ 21 중량부의 접착제와; 상기 고무 100 중량부 대비 5 ~ 15 중량부의 연화제와; 상기 고무 100 중량부 대비 4 ~ 7 중량부의 노화방지제와; 상기 고무 100 중량부 대비 1 ~ 3 중량부의 가류제와; 상기 고무 100 중량부 대비 1 ~ 3 중량부의 가류조제;를 포함하여 구성된 것을 특징으로 한다.In addition, the bedsore mat of the present invention, a plurality of expansion bags are formed, each of the expansion bag is formed so as to communicate with each other through the connection portion; A lower layer part formed of the same material as the upper layer part and formed under the upper layer part; An adhesive sheet formed between the upper layer and the lower layer, and pressed by a press while being inserted between the upper layer and the lower layer, wherein the upper and lower layers comprise 100 parts by weight of rubber; 20 to 30 parts by weight of the reinforcing agent with respect to 100 parts by weight of the rubber; 0.3 to 1 part by weight of the softener relative to 100 parts by weight of the rubber; 5 to 9 parts by weight of the active agent relative to 100 parts by weight of the rubber; 3 to 5 parts by weight of anti-aging agent relative to 100 parts by weight of the rubber; 1 to 3 parts by weight of the vulcanizing agent relative to 100 parts by weight of the rubber; It comprises a 1 to 3 parts by weight of vulcanization aid relative to 100 parts by weight of the rubber, wherein the adhesive sheet, 100 parts by weight of rubber; 40 to 70 parts by weight of carbon black relative to 100 parts by weight of the rubber; 13 to 21 parts by weight of the adhesive relative to 100 parts by weight of the rubber; 5 to 15 parts by weight of a softener relative to 100 parts by weight of the rubber; 4 to 7 parts by weight of anti-aging agent relative to 100 parts by weight of the rubber; 1 to 3 parts by weight of a vulcanizing agent relative to 100 parts by weight of the rubber; Characterized in that it comprises a; 1 to 3 parts by weight of a vulcanization aid relative to 100 parts by weight of the rubber.
이때, 상기 접착시트는, 카본블랙은 60 중량부, 접착제는 17 중량부, 연화제는 10 중량부, 노화방지제는 6 중량부, 가류제는 1.5 중량부, 가류조제는 2.5 중량부로 이루어져 있으며, 접착제는 레조시놀 포름알데히드 수지 5 중량부와, 에테르화 메틸로멜라민 수지 12 중량부로 이루어져 있고, 상기 가류제는 디티오디모포린으로 이루어져 있는 것을 특징으로 한다.At this time, the adhesive sheet, carbon black is 60 parts by weight, adhesive is 17 parts by weight, softener is 10 parts by weight, anti-aging agent is 6 parts by weight, vulcanizing agent is 1.5 parts by weight, vulcanization aid is composed of 2.5 parts by weight, adhesive Is composed of 5 parts by weight of resorcinol formaldehyde resin and 12 parts by weight of etherified methylolomelamine resin, wherein the vulcanizing agent is composed of dithiodimorpholine.
아울러, 상기 활성제는 산화아연 6 중량부와, 스테아린산 1.2 중량부인 것을 특징으로 한다.
In addition, the active agent is characterized in that 6 parts by weight of zinc oxide and 1.2 parts by weight of stearic acid.
본 발명에 의해, 로테이션 몰딩 장치와 같은 고가의 장치를 이용하지 않으면서, 상층부와 하층부 사이에 접착시트를 설치한 채 프레스로 가압하여 상층부와 하층부를 결합하되, 접착시트가 상층부 및 하층부에 완전히 밀폐되어 떨어지지 않음으로써 공기의 누설을 최대한 방지할 수 있게 된다.According to the present invention, without using an expensive device, such as a rotation molding device, while pressing the adhesive sheet between the upper layer and the lower layer by pressing with a press to combine the upper layer and the lower layer, the adhesive sheet is completely sealed in the upper layer and the lower layer By not falling off, air leakage can be prevented as much as possible.
보다 구체적으로, 가황고무로 이루어지는 상층부와 하층부 사이에 접착시트를 설치하여 프레스로 가압하여 일체화시키는 단순한 공정으로 접합될 수 있게 된다.More specifically, the adhesive sheet is installed between the upper layer portion and the lower layer portion made of vulcanized rubber, and can be joined by a simple process of pressing and integrating with a press.
이처럼 간단한 공정으로 접합이 이루어지면서도 가류제로 디티오디모포린을 사용하여 압축영구줄음율이 적도록 하고, 접착제로 레조시놀 포름알데히드 수지와 에테르화 메틸로멜라민 수지를 특정 비로 사용하여 접착 성능을 높이는 한편, 연화제로 천연 수지인 대두유를 원료로 사용하여 유연성을 높이고, 무독성인 제품을 제공할 수 있게 된다.In this simple process, bonding is achieved, but dicomodimorphine is used as a vulcanizing agent, so that the compressive permanent shrinkage is low. On the other hand, soybean oil, a natural resin as a softener, can be used as a raw material to increase flexibility and provide a non-toxic product.
더불어, 욕창매트의 상층부와 하층부의 조성을 특정하게 한정하되, 활성제로 산화아연과 스테아린산을 특정 비율로 한정하여 동적 특성을 높이면서 스코치의 발생을 줄여 내구성을 우수하게 유지할 수 있게 된다.
In addition, the composition of the upper and lower layers of the bedsore mat is specifically limited, and zinc oxide and stearic acid are limited to a specific ratio as an activator to increase the dynamic characteristics, thereby reducing the occurrence of scotch and maintaining excellent durability.
도 1은 종래의 욕창방지방석을 나타낸 사시도.
도 2는 종래 욕창방지방석의 단면을 나타낸 단면도.
도 3 및 도 4는 본 발명에 따른 욕창매트의 일 실시예를 나타낸 사진.1 is a perspective view showing a conventional bed sock cushion.
Figure 2 is a sectional view showing a cross section of the conventional bedsore prevention cushion.
3 and 4 are photographs showing one embodiment of the bedsore mat in accordance with the present invention.
이하 본 발명의 욕창매트용 접착시트 고무 조성물 및 욕창매트에 대하여 상세히 설명하기로 한다.
Hereinafter, the adhesive sheet rubber composition and the bedsore mat for the bedsore mat of the present invention will be described in detail.
먼저, 본 발명의 욕창매트용 접착시트 고무 조성물은 상기와 같은 과제를 해결하기 위하여, 고무 100 중량부와; 상기 고무 100 중량부 대비 40 ~ 70 중량부의 카본블랙과; 상기 고무 100 중량부 대비 13 ~ 21 중량부의 접착제와; 상기 고무 100 중량부 대비 5 ~ 15 중량부의 연화제와; 상기 고무 100 중량부 대비 4 ~ 7 중량부의 노화방지제와; 상기 고무 100 중량부 대비 1 ~ 3 중량부의 가류제와; 상기 고무 100 중량부 대비 1 ~ 3 중량부의 가류조제;를 포함하여 구성된다.First, the pressure-sensitive adhesive sheet rubber composition for mattresses of the present invention, in order to solve the above problems, 100 parts by weight of rubber; 40 to 70 parts by weight of carbon black relative to 100 parts by weight of the rubber; 13 to 21 parts by weight of the adhesive relative to 100 parts by weight of the rubber; 5 to 15 parts by weight of a softener relative to 100 parts by weight of the rubber; 4 to 7 parts by weight of anti-aging agent relative to 100 parts by weight of the rubber; 1 to 3 parts by weight of a vulcanizing agent relative to 100 parts by weight of the rubber; It is configured to include; 1 to 3 parts by weight of a vulcanization aid relative to 100 parts by weight of the rubber.
이때, 상기 카본블랙은 60 중량부, 접착제는 17 중량부, 연화제는 10 중량부, 노화방지제는 6 중량부, 가류제는 1.5 중량부, 가류조제는 2.5 중량부로 이루어져 있으며, 접착제는 레조시놀 포름알데히드 수지 5 중량부와, 에테르화 메틸로멜라민 수지 12 중량부로 이루어져 있고, 상기 가류제는 디티오디모포린으로 이루어져 있는 것을 특징으로 한다.
At this time, the carbon black is 60 parts by weight, the adhesive is 17 parts by weight, the softener is 10 parts by weight, the anti-aging agent is 6 parts by weight, the vulcanizing agent is 1.5 parts by weight, the vulcanization aid is 2.5 parts by weight, the adhesive is resorcinol It consists of 5 parts by weight of formaldehyde resin, 12 parts by weight of etherified methylomerelamine resin, characterized in that the vulcanizing agent is composed of dithiodimorpholine.
본 발명 욕창매트용 접착시트 고무 조성물의 구성요소인 고무는 여러 천연고무나 합성고무를 사용할 수 있으나, 이 둘을 배합하여 사용하는 것이 바람직하며, 그 배합비는 천연고무와 합성고무가 8 : 2 내지 2 : 8의 배합으로 적절히 혼합하여 사용하는 것이 바람직하다.Rubber, which is a component of the adhesive sheet rubber composition for the bedsores of the present invention, may use various natural rubbers or synthetic rubbers. It is preferable to mix and use suitably by the mixture of 2: 8.
이때, 합성고무는 IR과 CIIR을 혼합하거나 단독으로 사용하는 것이 바람직하다.At this time, the synthetic rubber is preferably mixed with IR or CIIR or used alone.
본 발명 욕창매트용 접착시트 고무 조성물의 구성요소인 카본블랙은 고무 100 중량부 대비 40 ~ 70 중량부의 범위로 구성됨이 바람직하며, 가장 바람직하기로는 60 중량부로 구성됨이 좋다.Carbon black which is a component of the adhesive sheet rubber composition for the bedsores of the present invention is preferably composed of 40 to 70 parts by weight relative to 100 parts by weight of rubber, most preferably 60 parts by weight.
이러한 카본블랙을 상기 중량부 미만일 경우 인장강도나 전단계수 등 기계적 물성이 충분치 않아 바람직하지 않고, 상기 중량부 초과할 경우에는 고무 제조 과정상의 가공성이 저하되어 바람직하지 않을 뿐만 아니라 오히려 역가황에 의해 기계적 물성이 열화될 수도 있다.When the carbon black is less than the weight part, it is not preferable because the mechanical properties such as tensile strength or shear strength are not sufficient. If the carbon black is more than the weight part, the workability in the rubber manufacturing process is lowered, which is not preferable, but rather mechanically caused by reverse vulcanization. Physical properties may deteriorate.
이러한 카본블랙은 욕창매트에 적용할 수 있는 고무조성물에 적합하게 사용될 수 있는 것이라면 어떠한 것이라도 사용할 수 있으나, 가장 바람직하기로는 HAF(High Abrasion Furnace)와 ISAF(Intermediate Super Abrasion Furnace)가 1 : 1의 중량비로 사용됨이 바람직하다.The carbon black may be used as long as it can be used for rubber compositions applicable to bedsore mats, but most preferably HAF (High Abrasion Furnace) and ISAF (Intermediate Super Abrasion Furnace) are 1: 1. It is preferably used in weight ratio.
이는 HAF의 경우 보강성 및 마모성이 좋고, 인장강도의 상승에 좋으며, ISAF의 경우 회전성 제품에 좋으므로 이 둘의 장점을 살리고자 함이다.This is because HAF has good reinforcement and abrasion property, is good for increasing tensile strength, and ISAF is good for rotatable product.
본 발명 욕창매트용 접착시트 고무 조성물의 구성요소인 접착제는 고무 100 중량부 대비 13 ~ 21 중량부의 범위로 사용됨이 바람직하고, 가장 바람직하기로는 17 중량부가 사용됨이 바람직하다.The adhesive that is a component of the adhesive sheet rubber composition for the bedsore mat of the present invention is preferably used in the range of 13 to 21 parts by weight relative to 100 parts by weight of rubber, and most preferably 17 parts by weight.
이때, 접착제는 레조시놀 포름알데히드 수지 5 중량부와, 에테르화 메틸로멜라민 수지 12 중량부가 각각 사용됨이 가장 바람직하다.At this time, the adhesive is most preferably used 5 parts by weight of resorcinol formaldehyde resin, and 12 parts by weight of etherified methyllomelamine resin.
상기 재료들은 레조시놀 포름알데히드 수지는 내흡습성, 내증발성이 우수하고, 고무와의 상용성이 좋으며, 내 블루밍성이 우수하다.Resorcinol formaldehyde resin is excellent in hygroscopic resistance, evaporation resistance, good compatibility with rubber, and excellent blooming resistance.
이에 따라 상기 재료들은 고무끼리의 접착에 우수한 접착성능을 갖게 된다.As a result, the materials have excellent adhesion to rubber to each other.
본 발명 욕창매트용 접착시트 고무 조성물의 구성요소인 연화제는 상기 고무 100 중량부 대비 5 ~ 15 중량부의 범위로 사용됨이 바람직하고, 가장 바람직하기로는 10 중량부가 사용됨이 바람직하다.The softener which is a component of the adhesive sheet rubber composition for the bedsore mat of the present invention is preferably used in the range of 5 to 15 parts by weight with respect to 100 parts by weight of the rubber, and most preferably 10 parts by weight.
연화제는 물질의 증발을 늦추고 고무 조성물에 이형성 및 윤활성을 부여하여 제품의 가공 안정성을 높이기 위한 것으로, 본 발명에서는 "CIZER E-03"과 같이 천연수지인 대두유를 원료로 제조된 것이 바람직하며, 이는 무독성 첨가제로서 의료용이나 식품 저장용 등으로 주로 사용되는데, 본 발명에서 사용한 결과 기존의 광물류 연화제에 비해 무독성을 가져 신체 접촉시 무해해질 수 있게 된다.Softener is to increase the process stability of the product by delaying evaporation of the material and imparting releasability and lubricity to the rubber composition, in the present invention, it is preferable that the soybean oil, which is a natural resin such as "CIZER E-03", is used as a raw material. As a non-toxic additive, it is mainly used for medical use or food storage. As a result of the present invention, the non-toxic additive is non-toxic compared to conventional mineral softeners, and thus may be harmless in contact with the body.
본 발명 욕창매트용 접착시트 고무 조성물의 구성요소인 노화방지제는 상기 고무 100 중량부 대비 4 ~ 7 중량부의 범위로 사용됨이 바람직하고, 가장 바람직하기로는 6 중량부가 사용됨이 바람직하다.Anti-aging agent that is a component of the adhesive sheet rubber composition for the bedsores of the present invention is preferably used in the range of 4 to 7 parts by weight relative to 100 parts by weight of the rubber, most preferably 6 parts by weight.
노화방지제는 고무의 내열성, 내굴곡성, 내산화성을 향상시키는 역할을 하는데, 예를 들어 N-페닐-N'-이소프로필-p-페닐렌디아민(N-phenyl-N'-isopropyl-p-phenylenediamine), 아세톤(acetone), p-아미노디페닐아민(paminodiphenylamine), 스티렌네이티드 페놀(styrenated phenol), 스티렌(styrene), 페놀(phenol), 2-머캅토벤즈이미다졸(2-mercaptobenzimidazole) 중에서 하나 또는 둘 이상을 선택하여 혼합한 것을 사용할 수 있다.Anti-aging agents play a role in improving the heat resistance, flex resistance and oxidation resistance of rubber, for example N-phenyl-N'-isopropyl-p-phenylenediamine ), Acetone, p-aminodiphenylamine, styrenated phenol, styrene, phenol, 2-mercaptobenzimidazole Or two or more selected and mixed can be used.
본 발명 욕창매트용 접착시트 고무 조성물의 구성요소인 가류제는 상기 고무 100 중량부 대비 1 ~ 3 중량부의 범위로 사용됨이 바람직하고, 가장 바람직하기로는 1.5 중량부가 사용됨이 바람직하다.The vulcanizing agent as a component of the adhesive sheet rubber composition for the bedsore mat of the present invention is preferably used in the range of 1 to 3 parts by weight, and most preferably 1.5 parts by weight based on 100 parts by weight of the rubber.
가류제는 공지의 다양한 원료를 사용할 수도 있으나, 디티오디모포린(4,4' - dithiodimorpholinr;Vulnoc-R)을 사용하는 것이 가장 바람직하다.Although a vulcanizing agent may use various well-known raw materials, it is most preferable to use dithiodimorpholine (4,4'- dithiodimorpholinr; Vulnoc-R).
상기 재료는 설퍼 블룸(sulfur bloom)이 없고, 압축영구줄음율이 적은 고무를 만들 수 있게 해주는 역할을 해주게 된다.The material serves to make rubber free of sulfur bloom and low compression set.
본 발명 욕창매트용 접착시트 고무 조성물의 구성요소인 가류조제는 상기 고무 100 중량부 대비 1 ~ 3 중량부의 범위로 사용됨이 바람직하고, 가장 바람직하기로는 2.5 중량부가 사용됨이 바람직하다.The vulcanization aid as a component of the adhesive sheet rubber composition for the bedsore mat of the present invention is preferably used in the range of 1 to 3 parts by weight, and most preferably 2.5 parts by weight, based on 100 parts by weight of the rubber.
가류조제는 폴리머의 가교 속도를 증가시키는 한편 측쇄(side chain) 반응을 방지하여 가교 밀도를 증가시키기위한 것으로, 공지의 다양한 가류조제를 사용할 수 있다.
The vulcanization aid is intended to increase the crosslinking speed of the polymer and to increase the crosslinking density by preventing side chain reaction, and various known vulcanization aids can be used.
한편, 본 발명의 욕창매트는 도 4 및 도 5에 도시되어 있는 바와 같이 다수의 팽창주머니가 형성되어 있고, 각각의 팽창주머니가 연결부를 통해 서로 연통되도록 형성되어 있는 상층부(1)와; 상기 상층부와 동일한 재질로 이루어져 있으며, 상층부(10)의 하부에 형성되어 있는 하층부(20)와; 상기 상층부(10)와 하층부(20) 사이에 형성되어 있고, 상층부(10)와 하층부(20) 사이에 삽입된 채 프레스에 의해 가압되어 상층부(10)와 하층부(20)를 결합시키는 접착시트(30);로 구성되어 있다.On the other hand, the bedsore mat of the present invention is a plurality of expansion bags are formed, as shown in Figure 4 and 5, each of the expansion bag is formed so that each of the expansion bag is in communication with each other through the connection portion; A
이때, 접착시트(30)는 앞서 설명한 조성으로 이루어져 있다.At this time, the
즉, 고무 100 중량부와; 상기 고무 100 중량부 대비 40 ~ 70 중량부의 카본블랙과; 상기 고무 100 중량부 대비 13 ~ 21 중량부의 접착제와; 상기 고무 100 중량부 대비 5 ~ 15 중량부의 연화제와; 상기 고무 100 중량부 대비 4 ~ 7 중량부의 노화방지제와; 상기 고무 100 중량부 대비 1 ~ 3 중량부의 가류제와; 상기 고무 100 중량부 대비 1 ~ 3 중량부의 가류조제;를 포함하여 구성된 것을 특징으로 한다.That is, 100 parts by weight of rubber; 40 to 70 parts by weight of carbon black relative to 100 parts by weight of the rubber; 13 to 21 parts by weight of the adhesive relative to 100 parts by weight of the rubber; 5 to 15 parts by weight of a softener relative to 100 parts by weight of the rubber; 4 to 7 parts by weight of anti-aging agent relative to 100 parts by weight of the rubber; 1 to 3 parts by weight of a vulcanizing agent relative to 100 parts by weight of the rubber; Characterized in that it comprises a; 1 to 3 parts by weight of a vulcanization aid relative to 100 parts by weight of the rubber.
이때, 상기 접착시트는, 카본블랙은 60 중량부, 접착제는 17 중량부, 연화제는 10 중량부, 노화방지제는 6 중량부, 가류제는 1.5 중량부, 가류조제는 2.5 중량부로 이루어져 있으며, 접착제는 레조시놀 포름알데히드 수지 5 중량부와, 에테르화 메틸로멜라민 수지 12 중량부로 이루어져 있고, 상기 가류제는 디티오디모포린으로 이루어짐이 보다 바람직하다.At this time, the adhesive sheet, carbon black is 60 parts by weight, adhesive is 17 parts by weight, softener is 10 parts by weight, anti-aging agent is 6 parts by weight, vulcanizing agent is 1.5 parts by weight, vulcanization aid is composed of 2.5 parts by weight, adhesive Is composed of 5 parts by weight of resorcinol formaldehyde resin and 12 parts by weight of etherified methylomerelamine resin, and the vulcanizing agent is more preferably made of dithiodimorpholine.
한편, 상층부 및 하층부는 별도로 각각 제조되는데, 그 조성을 살펴보면 다음과 같다.On the other hand, the upper and lower layers are separately prepared, looking at the composition as follows.
구체적으로, 고무 100 중량부와; Specifically, 100 parts by weight of rubber;
상기 고무 100 중량부 대비 보강제 20 ~ 30 중량부와; 20 to 30 parts by weight of the reinforcing agent with respect to 100 parts by weight of the rubber;
상기 고무 100 중량부 대비 연화제 0.3 ~ 1 중량부와; 0.3 to 1 part by weight of the softener relative to 100 parts by weight of the rubber;
상기 고무 100 중량부 대비 5 ~ 9 중량부의 활성제와; 5 to 9 parts by weight of the active agent relative to 100 parts by weight of the rubber;
상기 고무 100 중량부 대비 노화방지제 3 ~ 5 중량부와; 3 to 5 parts by weight of anti-aging agent relative to 100 parts by weight of the rubber;
상기 고무 100 중량부 대비 가황제 1 ~ 3 중량부와; 1 to 3 parts by weight of the vulcanizing agent relative to 100 parts by weight of the rubber;
상기 고무 100 중량부 대비 가류조제 1 ~ 3 중량부를 포함하여 구성된다.It comprises a 1 to 3 parts by weight of vulcanization aid relative to 100 parts by weight of the rubber.
상술한 구성에서 보강제는 22 중량부, 연화제는 0.5 중량부, 활성제는 7.2 중량부, 노화방지제는 3 중량부, 가황제는 1.5 중량부, 가류조제는 2.3 중량부로 이루어짐이 가장 바람직하다.In the above-described configuration, the reinforcing agent is 22 parts by weight, the softening agent is 0.5 parts by weight, the active agent is 7.2 parts by weight, the antioxidant is 3 parts by weight, the vulcanizing agent is 1.5 parts by weight, the vulcanization aid is most preferably composed of 2.3 parts by weight.
또, 이때 보강제는 마그네슘 카보네이트(BTT)가 바람직하며, 연화제는 파라핀계 배합유로 P-2를 사용하는 것이 바람직하다.In this case, the reinforcing agent is preferably magnesium carbonate (BTT), and it is preferable to use P-2 as the paraffin compounding oil.
활성제는 고무의 동적특성(dynamic characteristics)과 가공성이 우수해지도록 하고, 내열성 또한 개선될 수 있도록 하는 역할을 한다.The active agent serves to improve the dynamic characteristics and processability of the rubber and to improve the heat resistance.
활성제는 공지의 다양한 제품을 사용할 수 있으나, 본 발명에서는 산화아연(zinc oxide)과 스테아린산(Stearic acid)이 5 : 1의 중량비율이 되도록 하여 사용하는 것이 바람직하다.The active agent may use a variety of known products, but in the present invention, zinc oxide and stearic acid are preferably used in a weight ratio of 5: 1.
즉, 활성제는 산화아연 6 중량부와, 스테아린산 1.2 중량부로 이루어짐이 가장 바람직하다.That is, the active agent is most preferably composed of 6 parts by weight of zinc oxide and 1.2 parts by weight of stearic acid.
이러한 비율로 두 종류를 사용하는 것은, 상기 중량부 미만으로 과소 배합할 경우 가황속도의 활성화가 약해지고, 과잉배합할 경우에는 가황 속도 활성화가 커져서 스코치가 발생되어 고무의 성질이 약해지는 문제가 발생할 수 있다.The use of two types at such a ratio may result in weak activation of the vulcanization rate when under-mixed at less than the weight part, and in the case of over-mixing, the activation of the vulcanization rate is increased, resulting in scorch generation and weakening of rubber properties. have.
매트에서 노화방지제 및 가황제, 가류조제는 공지의 제품을 다양한 조합으로 사용할 수 있되, 상기 조성을 유지함이 바람직하다.
Anti-aging agent, vulcanizing agent, vulcanization aid in the mat can be used in various combinations of known products, it is preferable to maintain the composition.
이하, 실시예를 통하여 본 발명을 더욱 상세하게 설명한다. Hereinafter, the present invention will be described in more detail by way of examples.
그러나 하기 실시예는 본 발명을 예시하기 위한 것으로서 본 발명은 하기 실시예에 의하여 한정되지 않고 다양하게 수정 및 변경될 수 있다 할 것이다.
However, the following examples are provided to illustrate the present invention, and the present invention is not limited to the following examples and may be variously modified and changed.
< 실시예> 실시예 1의 시편 제조(접착시트)EXAMPLES Preparation of Specimen of Example 1 (Adhesive Sheet)
표 1과 같이 실시예 1의 시험용 고무 시편을 제작하였다.A test rubber specimen of Example 1 was prepared as shown in Table 1.
시편의 제작 공정은 다음과 같다.The fabrication process of the specimen is as follows.
1단계 : 원료 마스켓 숙성(밀폐식 혼합기)Step 1: ripening the raw material mask (sealed mixer)
2단계 : 혼합(밀폐식 혼합기)Stage 2: Mixing (Enclosed Mixer)
3단계 : 믹싱(오픈롤)Step 3: Mixing (Open Roll)
4단계 : 촉진제 투입Step 4: Add Accelerator
5단계 : 혼련작업(오픈롤)Step 5: kneading work (open roll)
6단계 : 카렌더 시트 작업
Step 6: Work with Calendar Sheets
< 실시예 2> 실시예 2의 시편 제조(욕창매트의 상층부 및 하층부)Example 2 Preparation of Specimen of Example 2 (Upper and Lower Layers of a Bathtub Mat)
표 2와 같이 실시예 2의 시험용 고무 시편을 제작하였다.A test rubber specimen of Example 2 was prepared as shown in Table 2.
시편의 제작 공정은 다음과 같다.The fabrication process of the specimen is as follows.
1단계 : 원료 마스켓 숙성(밀폐식 혼합기)Step 1: ripening the raw material mask (sealed mixer)
2단계 : 혼합(밀폐식 혼합기)Stage 2: Mixing (Enclosed Mixer)
3단계 : 믹싱(오픈롤)Step 3: Mixing (Open Roll)
4단계 : 촉진제 투입Step 4: Add Accelerator
5단계 : 혼련작업(오픈롤)Step 5: kneading work (open roll)
6단계 : 카렌더 시트 작업
Step 6: Work with Calendar Sheets
< 실시예 3> 실시예 3의 시편 제조(욕창매트)Example 3 Preparation of Specimen of Example 3 (Bath Sore Mat)
실시예1의 시편을 두 개 준비하고, 그 사이에 실시예 2의 시편을 사이에 설치한 후 열을 가하면서 프레스기로 압력을 가해 실시예3의 욕창매트 시편을 제작하였다.Two specimens of Example 1 were prepared, and the specimens of Example 2 were interposed therebetween, and pressure was applied with a press while applying heat to prepare the bedsore mat specimens of Example 3.
이 시편은 프레스하는 환경에서 가류하지 않은 것을 특징으로 한다.
This specimen is characterized in that it is not vulcanized in the press environment.
<실험예 1> 박리강도 실험Experimental Example 1 Peel Strength
실시예 3의 시편에 대해 ASTM D 1876-01에 의거하여 박리강도 시험을 실시하였다.The specimen of Example 3 was subjected to peel strength test in accordance with ASTM D 1876-01.
이 실험은 실시예2의 시편 외측의 두 실시예1의 시편을 떼어내는 데 걸리는 저항 값을 나타낸 것으로, 최초 박리가 시작되는 부분에서 최소 127mm까지 박리시켜 분리되는 시편 폭 당 평균 하중을 나타낸다.This experiment shows the value of resistance it takes to remove two specimens of Example 1 outside of the specimen of Example 2, and shows the average load per specimen width separated by peeling at least 127mm from the beginning of the initial peeling.
박리강도를 측정하기 위해서 Instron 4467을 사용하였으며, 254mm/min의 cross-head speed로 시험을 실시하였다.Instron 4467 was used to measure the peel strength, and the test was carried out at a cross-head speed of 254 mm / min.
그 결과 실시예 3의 시편은 박리강도가 130 Mpa가 나와 우수한 접착성을 갖는 것을 알 수 있었다.
As a result, it was found that the specimen of Example 3 had a peel strength of 130 Mpa and had excellent adhesion.
<실험예 2> 기계적 물성Experimental Example 2 Mechanical Properties
상기 실시예 3 시편의 기계적 물성을 측정하여 아래 표 3에 나타냈다.Example 3 The mechanical properties of the specimens were measured and shown in Table 3 below.
경도 KS M 6518에 준하여 TECLOCK 사의 스프링A Type 경도기로 측정
Tensile strength, elongation and tear strength are measured according to KS M 6518, and static shear modulus is measured by Sejong Hi-Tech tensile and elongation tester according to KS M 6785.
Hardness measured by TECLOCK spring A type hardness tester according to KS M 6518
648
5.9
상기 실험예에 나타난 바와 같이 본 발명에 따른 실시예의 고무시편은 비교적 안정된 인장강도, 신장율 및 인열강도가 기준을 모두 상회하는 것으로 나타났다.
As shown in the experimental example, the rubber specimens of the examples according to the present invention were found to be relatively stable in tensile strength, elongation rate and tear strength.
이에 따라 본 발명에 따른 욕창매트는 우수한 성질을 갖는 접착시트를 사용함으로써 접착 성능이 우수하여 박리가 잘 일어나지 않고 기타 기계적 물성이 우수하다 할 것이다.
Accordingly, the bedsore mat according to the present invention will have excellent adhesion performance by using an adhesive sheet having excellent properties, so that peeling does not occur well and other mechanical properties will be excellent.
Claims (5)
고무 100 중량부와;
상기 고무 100 중량부 대비 40 ~ 70 중량부의 카본블랙과;
상기 고무 100 중량부 대비 13 ~ 21 중량부의 접착제와;
상기 고무 100 중량부 대비 5 ~ 15 중량부의 연화제와;
상기 고무 100 중량부 대비 4 ~ 7 중량부의 노화방지제와;
상기 고무 100 중량부 대비 1 ~ 3 중량부의 가류제와;
상기 고무 100 중량부 대비 1 ~ 3 중량부의 가류조제;를 포함하여 구성된,
욕창매트용 접착시트 고무 조성물.
In the adhesive sheet rubber composition for bedsore mats,
100 parts by weight of rubber;
40 to 70 parts by weight of carbon black relative to 100 parts by weight of the rubber;
13 to 21 parts by weight of the adhesive relative to 100 parts by weight of the rubber;
5 to 15 parts by weight of a softener relative to 100 parts by weight of the rubber;
4 to 7 parts by weight of anti-aging agent relative to 100 parts by weight of the rubber;
1 to 3 parts by weight of a vulcanizing agent relative to 100 parts by weight of the rubber;
Comprising 1 to 3 parts by weight of a vulcanization aid relative to 100 parts by weight of the rubber;
Adhesive sheet rubber composition for bedsore mats.
상기 카본블랙은 60 중량부, 접착제는 17 중량부, 연화제는 10 중량부, 노화방지제는 6 중량부, 가류제는 1.5 중량부, 가류조제는 2.5 중량부로 이루어져 있으며,
접착제는 레조시놀 포름알데히드 수지 5 중량부와, 에테르화 메틸로멜라민 수지 12 중량부로 이루어져 있고,
상기 가류제는 디티오디모포린으로 이루어져 있는 것을 특징으로 하는,
욕창매트용 접착시트 고무 조성물.
The method of claim 1,
60 parts by weight of carbon black, 17 parts by weight of adhesive, 10 parts by weight of softener, 6 parts by weight of anti-aging agent, 1.5 parts by weight of vulcanizing agent, 2.5 parts by weight of vulcanization aid,
The adhesive consists of 5 parts by weight of resorcinol formaldehyde resin and 12 parts by weight of etherified methylommelamine resin,
The vulcanizing agent is characterized in that consisting of dithiodimorpholine,
Adhesive sheet rubber composition for bedsore mats.
다수의 팽창주머니가 형성되어 있고, 각각의 팽창주머니가 연결부를 통해 서로 연통되도록 형성되어 있는 상층부와;
상기 상층부와 동일한 재질로 이루어져 있으며, 상층부의 하부에 형성되어 있는 하층부와;
상기 상층부와 하층부 사이에 형성되어 있고, 상층부와 하층부 사이에 삽입된 채 프레스에 의해 가압되어 상층부와 하층부를 결합시키는 접착시트;로 구성되어 있으며,
상기 상층부 및 하층부는,
고무 100 중량부와; 상기 고무 100 중량부 대비 보강제 20 ~ 30 중량부와; 상기 고무 100 중량부 대비 연화제 0.3 ~ 1 중량부와; 상기 고무 100 중량부 대비 5 ~ 9 중량부의 활성제와; 상기 고무 100 중량부 대비 노화방지제 3 ~ 5 중량부와; 상기 고무 100 중량부 대비 가황제 1 ~ 3 중량부와; 상기 고무 100 중량부 대비 가류조제 1 ~ 3 중량부를 포함하여 구성되어 있고,
상기 접착시트는,
고무 100 중량부와; 상기 고무 100 중량부 대비 40 ~ 70 중량부의 카본블랙과; 상기 고무 100 중량부 대비 13 ~ 21 중량부의 접착제와; 상기 고무 100 중량부 대비 5 ~ 15 중량부의 연화제와; 상기 고무 100 중량부 대비 4 ~ 7 중량부의 노화방지제와; 상기 고무 100 중량부 대비 1 ~ 3 중량부의 가류제와; 상기 고무 100 중량부 대비 1 ~ 3 중량부의 가류조제;를 포함하여 구성된 것을 특징으로 하는,
욕창매트.
In bedsore mats,
A plurality of expansion bags are formed, and each expansion bag is formed so as to communicate with each other through a connection portion;
A lower layer part formed of the same material as the upper layer part and formed under the upper layer part;
It is formed between the upper layer and the lower layer, and is inserted between the upper layer and the lower layer is pressed by a press to bond the upper layer and the lower layer; consisting of;
The upper and lower layers,
100 parts by weight of rubber; 20 to 30 parts by weight of the reinforcing agent with respect to 100 parts by weight of the rubber; 0.3 to 1 part by weight of the softener relative to 100 parts by weight of the rubber; 5 to 9 parts by weight of the active agent relative to 100 parts by weight of the rubber; 3 to 5 parts by weight of anti-aging agent relative to 100 parts by weight of the rubber; 1 to 3 parts by weight of the vulcanizing agent relative to 100 parts by weight of the rubber; Consists of 1 to 3 parts by weight of vulcanization aid relative to 100 parts by weight of rubber,
The adhesive sheet,
100 parts by weight of rubber; 40 to 70 parts by weight of carbon black relative to 100 parts by weight of the rubber; 13 to 21 parts by weight of the adhesive relative to 100 parts by weight of the rubber; 5 to 15 parts by weight of a softener relative to 100 parts by weight of the rubber; 4 to 7 parts by weight of anti-aging agent relative to 100 parts by weight of the rubber; 1 to 3 parts by weight of a vulcanizing agent relative to 100 parts by weight of the rubber; Characterized in that it comprises a; 1 to 3 parts by weight of vulcanization aid relative to 100 parts by weight of the rubber,
Bed sores mat.
상기 접착시트는,
카본블랙은 60 중량부, 접착제는 17 중량부, 연화제는 10 중량부, 노화방지제는 6 중량부, 가류제는 1.5 중량부, 가류조제는 2.5 중량부로 이루어져 있으며,
접착제는 레조시놀 포름알데히드 수지 5 중량부와, 에테르화 메틸로멜라민 수지 12 중량부로 이루어져 있고,
상기 가류제는 디티오디모포린으로 이루어져 있는 것을 특징으로 하는,
욕창매트.
The method of claim 3,
The adhesive sheet,
60 parts by weight of carbon black, 17 parts by weight of adhesive, 10 parts by weight of softener, 6 parts by weight of anti-aging agent, 1.5 parts by weight of vulcanizer, 2.5 parts by weight of vulcanization aid,
The adhesive consists of 5 parts by weight of resorcinol formaldehyde resin and 12 parts by weight of etherified methylommelamine resin,
The vulcanizing agent is characterized in that consisting of dithiodimorpholine,
Bed sores mat.
상기 활성제는
산화아연 6 중량부와, 스테아린산 1.2 중량부인 것을 특징으로 하는,
욕창매트.5. The method of claim 4,
The active agent
6 parts by weight of zinc oxide and 1.2 parts by weight of stearic acid,
Bed sores mat.