KR101205916B1 - Coating composition of finishing materials for sauna booth and coating method - Google Patents
Coating composition of finishing materials for sauna booth and coating method Download PDFInfo
- Publication number
- KR101205916B1 KR101205916B1 KR1020100043304A KR20100043304A KR101205916B1 KR 101205916 B1 KR101205916 B1 KR 101205916B1 KR 1020100043304 A KR1020100043304 A KR 1020100043304A KR 20100043304 A KR20100043304 A KR 20100043304A KR 101205916 B1 KR101205916 B1 KR 101205916B1
- Authority
- KR
- South Korea
- Prior art keywords
- tourmaline
- coating composition
- liquid
- gold
- titanium dioxide
- Prior art date
Abstract
본 발명은 토르말린의 전기적 성질을 극대화한 300㎚ 이하의 액상의 토르말린과, 상기 토르말린의 음이온 흡수 및 마이너스 전극의 방출을 촉진시키기 위해 나노화 된 촉매금속물질을 1:1의 중량비로 혼합하되; 상기 촉매금속물질은 5~20㎚의 액상의 금 및 백금, 5~20㎚의 이산화티타늄 분말을 1:1:3의 중량비로 혼합하도록 구성되는 것을 특징으로 하는 사우나 부스의 마감재 코팅조성물을 제공하기 위한 것으로, 본 발명은 토르말린의 전기적 성질을 극대화하기 위해 300㎚ 이하로 제조된 액상의 토르말린과, 상기 토르말린의 음이온 흡수 및 마이너스 전극의 방출을 촉진시키기 위한 5~20㎚의 액상의 금 및 백금, 이산화티타늄 분말을 혼합한 제1 코팅조성물을 마감재에 코팅한 후, 상기 마감재에 금의 고유색상을 가지면서 제1 코팅조성물의 전기적 성질을 보완하기 위해 300㎚ 이하의 액상 토르말린에 5~20㎚의 이산화티타늄 분말과 1~5㎛의 금 분말을 혼합한 제2 코팅조성물을 코팅함으로써 사우나 내부의 온도가 35~50℃로 유지되더라도 내부에 있는 사람들은 땀을 내도록 함과 동시에 음이온과 원적외선이 다량으로 방출되는 토르말린에 의해 인체의 신진대사 및 세포활성화기능을 촉진시켜 노폐물을 분비시키고, 인체의 모세혈관을 크게 하여 혈액순환을 촉진시키며, 더불어 노화의 원인인 유해한 활성산소를 분해하고 알칼리화하여 두통, 피로회복, 신경통 등에 효과를 볼 수 있도록 하는 매우 유용한 발명인 것이다.The present invention is to mix the liquid tourmaline up to 300nm maximizing the electrical properties of tourmaline and the nano-catalyzed catalytic metal material in a weight ratio of 1: 1 to promote anion absorption and negative electrode release of the tourmaline; The catalyst metal material is 5 to 20nm of liquid gold and platinum, 5-20nm titanium dioxide powder to provide a finish coating composition of the sauna booth, characterized in that configured to mix in a weight ratio of 1: 1: 3. In order to maximize the electrical properties of the tourmaline, the present invention is a liquid tourmaline prepared to 300nm or less, and a gold and platinum of 5 ~ 20nm liquid to promote anion absorption and negative electrode release of the tourmaline, After coating the first coating composition mixed with titanium dioxide powder on the finishing material, in order to complement the electrical properties of the first coating composition while having the intrinsic color of gold on the finishing material, 5-20 nm of liquid tourmaline of 300 nm or less By coating the second coating composition, which is a mixture of titanium dioxide powder and gold powder of 1 ~ 5㎛, even if the temperature inside the sauna is maintained at 35 ~ 50 ℃, people inside can sweat. At the same time, tourmaline, which releases large amounts of negative ions and far infrared rays, promotes metabolism and cell activation of the human body to secrete waste products, enlarges the capillaries of the human body, and promotes blood circulation. It is a very useful invention that can decompose and alkalinize free radicals to have an effect on headache, fatigue, neuralgia and the like.
Description
본 발명은 사우나 부스의 마감재 코팅조성물 및 그 코팅방법에 관한 것으로, 더욱 상세하게는 토르말린의 전기적 성질을 극대화한 300㎚ 이하의 토르말린에 은폐력이 크고 열에 안정적인 이산화티타늄, 전기 및 열의 양도체인 금, 전성 및 연성의 성질을 갖는 백금을 각각 5~20㎚의 크기로 각각 혼합한 제1 코팅조성물을 1차로 코팅하여 마감재에 상기 토르말린의 기능을 부가하고, 금 1~5㎛의 분말에 300㎚ 이하의 토르말린, 5~20㎚의 이산화티타늄을 혼합한 제2 코팅조성물을 2차로 코팅하여 상기 마감재에 금의 고유한 색상을 부가하도록 하는 사우나 부스의 마감재 코팅조성물 및 그 코팅방법에 관한 것이다.
The present invention relates to a coating composition of the finishing material of the sauna booth and a coating method thereof, and more particularly, to a tourmaline of 300 nm or less, which maximizes the electrical properties of tourmaline, a concealable and heat-stable titanium dioxide, a good conductor of electricity and heat, gold, and electrical And a first coating composition in which platinum having ductile properties, respectively, is mixed in a size of 5 to 20 nm. The first coating composition is added to add a function of the tourmaline to a finish, and 300 nm or less to powder of 1 to 5 μm gold. The present invention relates to a finish coating composition of a sauna booth for coating a second coating composition mixed with tourmaline and 5 to 20 nm of titanium dioxide to add a unique color of gold to the finish, and a coating method thereof.
일반적으로 사우나는 인체 내에 축적된 노폐물 등을 땀을 통해 체외로 배출시켜 인체의 신진대사를 원활하게 하기 위한 시설로, 좀처럼 시간을 내기 어려운 현대인은 땀과 더불어 체내의 노폐물을 배출시키기 위해 사우나를 즐겨 찾고 있는 실정이다.In general, the sauna is a facility for smoothing the metabolism of the human body by discharging wastes accumulated in the human body through sweat, and modern people who have difficulty in spending time enjoy saunas to discharge wastes in the body together with sweat. I'm looking for a situation.
이러한 사우나는 원적외선을 이용하는 황토를 비롯하여 예로부터 조상의 지혜로 전해져 내려오는 쑥, 숯, 소금 등의 효능을 이용한 사우나, 그 밖에 어느 정도 효능이 과학적으로 입증된 옥이나 은을 이용한 사우나, 각종 한약재를 이용한 사우나 등이 널리 알려지고 있다.These saunas use loess using far-infrared rays, saunas using wormwood, charcoal, salt, etc., which have been handed down to the wisdom of ancestors since ancient times, and other saunas using jade or silver, which have been scientifically proven to some extent. Used saunas are widely known.
그러나 상기한 종래의 사우나는 실내의 온도가 대략 70~120℃의 고온으로 유지되는 건식사우나로, 한약재 등의 성분이 증기를 통해 인체의 피부 속으로 스며들기보다는 고온 증기의 피부접촉에 따른 화상, 호흡곤란, 현기증, 두통 등의 장애를 일으키는 문제점이 있었다.However, the conventional sauna is a dry sauna in which the temperature of the room is maintained at a high temperature of approximately 70 to 120 ° C., and components such as herbal medicines are burned according to skin contact of hot steam rather than penetrating into human skin through steam. Difficulty in breathing, dizziness, headache and other problems.
또한, 사람의 체질에 따라 땀의 분비는 각각 다르다 할 것인데, 상기와 같이 고온 다습한 환경의 사우나를 이용할지라도 땀의 분비가 잘 되지않는 사람이나 땀의 분비가 느린 사람은 땀을 체외로 배출하기 어려우며, 특히 여성의 경우 사우나의 고온 증기는 피부를 자극하여 손상시킬 우려가 크고, 노약자나 어린이는 고온 다습한 환경에 의해 사우나를 이용하기 어려운 문제점이 있었다.In addition, the secretion of sweat will be different depending on the constitution of the person, even if you use a sauna in a high temperature and high humidity environment as described above, those who do not secret sweat well or slow sweat secretion to discharge the sweat to the body It is difficult, especially in the case of women, high temperature steam of the sauna is likely to irritate and damage the skin, the elderly and children were difficult to use the sauna due to the high temperature and high humidity environment.
또한, 원적외선을 방출하기 위해 다다미, 면, 부직포 등의 마감재에 황토를 코팅한 사우나 부스도 있으나, 상기 황토에서 방사되는 원적외선은 방향성을 가지고 있으므로 몸 전체에 골고루 원적외선이 도달하지 못하여 가열장치를 사우나 부스 내에 돌출시켜 설치할 수밖에 없어 불편하고 실내를 효과적으로 사용할 수 없는 문제점이 있었다.
In addition, there is also a sauna booth coated with ocher to finish materials such as tatami, cotton, nonwoven fabric to emit far infrared rays, but since the far infrared rays emitted from the loess have directivity, the heating device does not reach evenly the whole infrared sauna booth. There is a problem that can not only be installed to protrude in the inside and can not use the interior effectively.
따라서 본 발명은 상기와 같은 문제점을 해결하기 위해, 토르말린의 전기적 성질에 의해 사우나 내부의 온도가 35~50℃로 유지되더라도 내부에 있는 사람들은 땀을 내도록 하는 토르말린을 함유한 사우나 부스의 마감재 코팅조성물 및 그 코팅방법을 제공하는데 그 목적이 있다.Therefore, in order to solve the above problems, the finish coating composition of the sauna booth containing tourmaline to make people sweat even if the temperature inside the sauna is maintained at 35 ~ 50 ℃ by the electrical properties of the tourmaline And its coating method.
즉 본 발명은 토르말린의 전기적 성질을 극대화한 300㎚ 이하의 액상 토르말린에 전기 및 열의 양도체인 액상의 금과, 전성 및 연성의 성질을 갖는 액상의 백금과, 은폐력이 크고 열에 안정적인 이산화티타늄 분말을 5~20㎚의 크기로 각각 혼합한 제1 코팅조성물을 마감재에 코팅하여 토르말린의 기능을 부가하고, 상기 제1 코팅조성물이 코팅된 마감재의 표면에 금 1~5㎛의 분말에 300㎚ 이하의 액상 토르말린, 5~20㎚의 이산화티타늄 분말을 혼합한 제2 코팅조성물을 코팅하여 마감재의 표면에 금의 고유한 색상을 부가하도록 하는 사우나 부스의 마감재 코팅조성물 및 그 코팅방법에 관한 것이다.
In other words, the present invention is a liquid tourmaline up to 300nm maximizing the electrical properties of tourmaline liquid gold, liquid and platinum, a liquid and a malleable and malleable nature of the good conductors of electricity and heat, and a high hiding power and stable titanium dioxide powder 5 The first coating composition mixed in the size of ˜20 nm is coated on the finish material to add the function of tourmaline, and the first coating composition is 300 μm or less in a powder of 1-5 μm gold on the surface of the finish material coated with the first coating composition. It relates to a finish coating composition of a sauna booth for coating a second coating composition mixed with tourmaline, titanium dioxide powder of 5 ~ 20nm to add a unique color of gold to the surface of the finish material and a coating method thereof.
상기한 목적을 달성하기 위한 본 발명에 따른 사우나 부스의 마감재 코팅조성물은, 토르말린의 전기적 성질을 극대화한 300㎚ 이하의 액상의 토르말린과, 상기 토르말린의 음이온 흡수 및 마이너스 전극의 방출을 촉진시키기 위해 나노화 된 촉매금속물질을 1:1의 중량비로 혼합하되; 상기 촉매금속물질은 5~20㎚의 액상의 금 및 백금, 5~20㎚의 이산화티타늄 분말을 1:1:3의 중량비로 혼합하도록 구성되는 것을 특징으로 한다.The finish coating composition of the sauna booth according to the present invention for achieving the above object is nano-structured to promote the absorption of negative ion and negative electrode of the tourmaline of 300nm or less liquid maximized the electrical properties of the tourmaline and the tourmaline Mixed catalyst metal material in a weight ratio of 1: 1; The catalytic metal material is characterized in that it is configured to mix the liquid gold and platinum of 5 ~ 20nm, titanium dioxide powder of 5 ~ 20nm in a weight ratio of 1: 1: 3.
또한, 본 발명에 따른 사우나 부스의 마감재 코팅방법은, 상기 마감재에 토르말린의 전기적 성질을 극대화한 300㎚ 이하의 액상의 토르말린과, 상기 토르말린의 음이온 흡수 및 마이너스 전극의 방출을 촉진시키기 위해 나노화 된 촉매금속물질을 1:1의 중량비로 혼합하되; 상기 촉매금속물질은 5~20㎚의 액상의 금 및 백금, 5~20㎚의 이산화티타늄 분말을 1:1:3의 중량비로 혼합한 제1 코팅조성물을 1차 코팅한 후, 상기 제1 코팅조성물이 1차 코팅된 마감재의 표면에 300㎚ 이하의 액상의 토르말린 10~30중량%; 5~20㎚의 이산화티타늄 30~70중량%; 1~5㎛의 금 분말 20~40중량%;로 혼합된 제2 코팅조성물을 2차 코팅하도록 구성되는 것을 특징으로 한다.
In addition, the finish coating method of the sauna booth according to the present invention, the nano-catalyst to promote the absorption of negative ion and negative electrode of the tourmaline of 300nm or less liquid maximized the electrical properties of the tourmaline to the finish material Mixing the metal materials in a weight ratio of 1: 1; The catalytic metal material is the first coating composition after mixing the first coating composition of 5 to 20nm liquid gold and platinum, and 5 to 20nm titanium dioxide powder in a weight ratio of 1: 1: 3, and then the first coating 10 to 30% by weight of the liquid tourmaline of 300 nm or less on the surface of the finish coating the composition; 30-70 weight% of titanium dioxide of 5-20 nm; It is characterized in that it is configured to secondary coating the second coating composition mixed with 20 to 40% by weight of gold powder of 1 ~ 5㎛.
이처럼 본 발명은 토르말린의 전기적 성질을 극대화하기 위해 300㎚ 이하로 제조된 액상의 토르말린과, 상기 토르말린의 음이온 흡수 및 마이너스 전극의 방출을 촉진시키기 위한 5~20㎚의 액상의 금 및 백금, 이산화티타늄 분말을 혼합한 제1 코팅조성물을 마감재에 코팅한 후, 상기 마감재에 금의 고유색상을 가지면서 제1 코팅조성물의 전기적 성질을 보완하기 위해 300㎚ 이하의 액상 토르말린에 5~20㎚의 이산화티타늄 분말과 1~5㎛의 금 분말을 혼합한 제2 코팅조성물을 코팅함으로써 사우나 내부의 온도가 35~50℃로 유지되더라도 내부에 있는 사람들은 땀을 내도록 함과 동시에 음이온과 원적외선이 다량으로 방출되는 토르말린에 의해 인체의 신진대사 및 세포활성화기능을 촉진시켜 노폐물을 분비시키고, 인체의 모세혈관을 크게 하여 혈액순환을 촉진시키며, 더불어 노화의 원인인 유해한 활성산소를 분해하고 알칼리화하여 두통, 피로회복, 신경통 등에 효과를 볼 수 있도록 하는 매우 유용한 발명인 것이다.
As described above, the present invention is a liquid tourmaline prepared at 300 nm or less to maximize the electrical properties of tourmaline, and 5-20 nm of liquid gold, platinum, and titanium dioxide to promote anion absorption and negative electrode release of the tourmaline. After coating the first coating composition mixed with the powder on the finishing material, in order to complement the electrical properties of the first coating composition while having a unique color of gold on the finishing material, 5-20 nm of titanium dioxide in liquid tourmaline of 300 nm or less By coating the second coating composition mixed with powder and gold powder of 1 ~ 5㎛, even though the temperature inside the sauna is maintained at 35 ~ 50 ℃, people inside can sweat and at the same time a large amount of negative ions and far infrared rays are released. Tourmaline stimulates the body's metabolism and cell activation, releasing waste products, and enlarges capillaries in the body to promote blood circulation Sikimyeo, with very useful inventors that by decomposing and alkalizing the cause of harmful free radicals in the aging to be effective such as headache, fatigue, neuralgia.
상기한 목적 및 효과를 달성하기 위한 본 발명을 바람직한 실시예를 통해 상세히 설명하면 다음과 같다.
The present invention for achieving the above objects and effects are described in detail through the preferred embodiments as follows.
본 발명에 따른 사우나 부스의 마감재 코팅조성물은, 토르말린의 전기적 성질을 극대화한 300㎚ 이하의 액상의 토르말린과, 상기 토르말린의 음이온 흡수 및 마이너스 전극의 방출을 촉진시키기 위해 나노화 된 촉매금속물질을 1:1의 중량비로 혼합하되; 상기 촉매금속물질은 5~20㎚의 액상의 금 및 백금, 5~20㎚의 이산화티타늄 분말을 1:1:3의 중량비로 혼합하도록 구성되는 것을 특징으로 한다.
The finish coating composition of the sauna booth according to the present invention, a liquid tourmaline of 300 nm or less that maximizes the electrical properties of tourmaline, and the catalyst metal material nanonized to promote anion absorption and negative electrode release of the tourmaline 1: Mixed at a weight ratio of 1; The catalytic metal material is characterized in that it is configured to mix the liquid gold and platinum of 5 ~ 20nm, titanium dioxide powder of 5 ~ 20nm in a weight ratio of 1: 1: 3.
상기 토르말린은 300㎚ 이하의 액상상태로 나노화 되는데, 이는 아래의 그림에서 확인되는 바와 같이 토르말린을 300㎚ 이하로 나노화 하였을 때 전기적 성질이 극대화되고 있음을 확인할 수 있다.The tourmaline is nanonized in a liquid state of less than 300nm, which can be seen that the electrical properties are maximized when the tourmaline is nanonized to 300nm or less as shown in the figure below.
이처럼 상기 토르말린은 결정 구조 자체에 끊임없이 전기를 띄는 특성이 있으며, 결정의 양단에 플러스 전극과 마이너스 전극이 자연적이고 영구적으로 유지되는 특성이 있다. 이때 상기 토르말린의 플러스 전극은 대기 중의 음이온을 흡수하고 모인 음이온은 토르말린 내부에 쌓이며 상기 음이온이 마이너스 전극으로 방출되면서 0.06㎃의 미약한 전류가 영구적으로 발생하는 것이다.As such, tourmaline has a characteristic of constantly displaying electricity in the crystal structure itself, and the positive and negative electrodes are naturally and permanently maintained at both ends of the crystal. At this time, the positive electrode of the tourmaline absorbs negative ions in the air, and the negative ions collected in the tourmaline are accumulated inside the tourmaline, and a weak current of 0.06 mA is permanently generated as the negative ions are released to the negative electrode.
그리고 상기 토르말린이 방출하는 전기는 아주 미약한 전류이긴 하나, 아무리 방전을 해도 전기를 지속적으로 내고 온도가 상승하는 경우에는 그 효과가 배가 되며, 잘게 부수어도 그 성질은 바뀌지 않고, 나노입자 1개가 모두 정전기를 발생하기 때문에 같은 양의 토르말린이라면 잘게 부순, 즉 위의 그림처럼 토르말린을 300㎚ 이하로 나노화 한 경우 정전기 발생량이 많고 전압이 높아지는 것이다.And the tourmaline emits electricity is very weak current, but even if discharged, even if the discharge of electricity continuously and the temperature rises, the effect is doubled, even if broken finely, the properties do not change, all one nanoparticle Since the same amount of tourmaline is generated because of the static electricity, that is, when the tourmaline is nanoscaled to 300nm or less as shown in the figure above, the amount of static electricity generated and the voltage increase.
그리고 상기 토르말린은 물에 접촉할 때 효과가 극대화되는데, 이는 토르말린의 마이너스 전극에 축적된 전자는 물에 접촉하는 순간에 방전되고 물은 수소 이온과 수산 이온으로 전기분해되며, 상기 수소 이온은 토르말린이 방출한 마이너스 전자와 결합하여 수소 원자가 되어 방출되고, 상기 수산 이온은 물 분자와 결합하여 히드록실이라고도 하는 계면 활성 물질, 즉 음이온을 발생시키기 때문이다.The tourmaline is maximized when it comes into contact with water. The electrons accumulated in the negative electrode of the tourmaline are discharged at the moment of contact with water, and the water is electrolyzed into hydrogen ions and hydroxyl ions. This is because the hydroxyl ions combine with the released negative electrons to form hydrogen atoms, and the hydroxyl ions combine with water molecules to generate a surface-active substance called a hydroxyl, that is, an anion.
그리고 상기 토르말린은 공기 중에 있는 수분이나 몸에서 증발하는 땀과 반응하면 음이온이 발생하여 체내에 흡수되며, 몸으로부터 항상 방출되고 있는 열에너지를 토르말린이 흡수하고 음이온과 원적외선으로 변환하여 다시 체내에 되돌리는 역할을 하게 된다. 이때 상기 원적외선은 인체 세포를 따뜻하게 하고 혈액순환을 좋게 하여 신진대사를 활발히 하고 세포를 활성화하는 온열 효과를 내게 되므로, 사우나 내부의 온도가 35~50℃로 유지되더라도 내부에 있는 사람들은 땀을 내도록 상기 토르말린의 성질에 의해 땀을 낼 수 있는 것이다.When the tourmaline reacts with moisture in the air or sweat evaporating from the body, anion is generated and absorbed into the body, and the tourmaline absorbs thermal energy that is always released from the body, converts it into anion and far infrared rays, and returns it back to the body. Will be At this time, the far infrared warms human cells and improves blood circulation, thereby promoting a metabolic activity and activating the cells. Therefore, even if the temperature inside the sauna is maintained at 35 to 50 ° C., the people inside may sweat. You can sweat by the nature of tourmaline.
즉 상기 토르말린으로부터 방출되는 음이온과 원적외선에 의해 인체의 신진대사 및 세포활성화기능을 촉진시켜 노폐물을 분비시키고, 인체의 모세혈관을 크게 하여 혈액순환을 촉진시키며, 노화의 원인인 유해한 활성산소를 분해하고 알칼리화하여 두통, 피로회복, 신경통에 효과를 볼 수 있는 것이다.
That is, by promoting the metabolism and cell activation function of the human body by the anion and far infrared rays emitted from the tourmaline to secrete waste products, increase the capillary blood vessels of the human body to promote blood circulation, decompose harmful free radicals that cause aging and Alkali can be effective for headache, fatigue, neuralgia.
이처럼 상기 토르말린의 전기적 성질을 극대화한 300㎚ 이하의 액상의 토르말린에 상기 토르말린의 음이온 흡수 및 마이너스 전극의 방출을 촉진시키기 위해 나노화 된 촉매금속물질을 1:1의 중량비로 혼합하게 되는데, 이때 상기 토르말린과 촉매금속물질을 1:1의 중량비로 혼합하는 것은 상기 토르말린의 양이 많은 경우에는 촉매금속물질의 양이 적고 상기 토르말린의 양이 적은 경우에는 촉매금속물질의 양이 많아 상기 토르말린의 전기발생을 극대화하기 어렵기 때문이다. 즉 상기 토르말린과 촉매금속물질의 가장 바람직한 1:1의 중량비에 의해 상기 토르말린의 전기발생을 최적화할 수 있는 것이다.
As such, nano-catalyzed catalyst metal materials are mixed in a weight ratio of 1: 1 in order to promote anion absorption and negative electrode release of the tourmaline into a liquid tourmaline of 300 nm or less, which maximizes the electrical properties of the tourmaline. Mixing the catalyst metal material in a weight ratio of 1: 1 means that the amount of the catalyst metal material is small when the amount of tourmaline is high and the amount of the catalyst metal material is high when the amount of the tourmaline is low, thereby generating electricity of the tourmaline. This is because it is difficult to maximize. In other words, the generation of the tourmaline can be optimized by the weight ratio of the most preferable 1: 1 of the tourmaline and the catalytic metal material.
그리고 상기 촉매금속물질은 5~20㎚의 액상의 금 및 백금, 5~20㎚의 이산화티타늄 분말을 1:1:3의 중량비로 혼합하도록 구성되는데, 이때 상기 촉매금속물질은 상술한 바와 같이 상기 토르말린의 음이온 흡수 및 마이너스 전극의 방출을 촉진시키기 위한 것으로 5~20㎚의 액상의 금 및 백금, 5~20㎚의 이산화티타늄 분말을 1:1:3의 중량비로 혼합하는 것이 가장 바람직하다.The catalytic metal material is configured to mix 5 to 20 nm of liquid gold and platinum, and 5 to 20 nm of titanium dioxide powder in a weight ratio of 1: 1: 3, wherein the catalytic metal material is as described above. It is most preferable to mix 5 to 20 nm of liquid gold and platinum and 5 to 20 nm of titanium dioxide powder in a weight ratio of 1: 1: 3 to promote anion absorption of tourmaline and release of negative electrode.
즉 상기 5~20㎚의 액상의 금 및 백금이 상기한 중량비 미만으로 혼합되는 경우에는 전기 및 열의 양도체인 금과 전성 및 연성이 있는 백금의 성질을 기대할 수 없고, 상기 5~20㎚의 액상의 금 및 백금이 상기한 중량비 초과로 혼합되는 경우에는 바인더 역할을 하는 이산화티타늄의 양이 상대적으로 줄어들게 되므로 마감재에 코팅이 원활하게 이루어지지 않을뿐더러 상기 이산화티타늄에 비해 상대적으로 비싼 금 및 백금의 가격에 의해 경제성이 떨어지기 때문이다. 또 상기 5~20㎚의 이산화티타늄 분말이 상기한 중량비 미만으로 혼합되는 경우에는 상기 이산화티타늄의 은폐력이 크고 열에 안정적인 성질을 기대하기 어렵고, 상기 5~20㎚의 이산화티타늄 분말이 상기한 중량비 초과로 혼합되는 경우에는 상기 금 및 백금의 양이 상대적으로 줄어들게 되어 상기 금 및 백금의 성질을 기대하기 어렵기 때문이다.
That is, when the 5 to 20 nm liquid gold and platinum are mixed at the weight ratios below, the properties of gold and the malleable and ductile platinum, which are good conductors of electricity and heat, cannot be expected. When gold and platinum are mixed in excess of the above weight ratio, the amount of titanium dioxide acting as a binder is relatively reduced, so that the coating is not smoothly applied to the finishing material, and the price of gold and platinum is relatively expensive compared to the titanium dioxide. This is because the economy is falling. In addition, when the titanium dioxide powder of 5 ~ 20nm is mixed below the above weight ratio, the hiding power of the titanium dioxide is large and it is difficult to expect heat stable properties, the titanium dioxide powder of 5 ~ 20nm in excess of the above weight ratio This is because the amount of the gold and platinum is relatively reduced when it is mixed, it is difficult to expect the properties of the gold and platinum.
또한, 본 발명에 따른 사우나 부스의 마감재 코팅방법은, 상기 마감재에 토르말린의 전기적 성질을 극대화한 300㎚ 이하의 액상의 토르말린과, 상기 토르말린의 음이온 흡수 및 마이너스 전극의 방출을 촉진시키기 위해 나노화 된 촉매금속물질을 1:1의 중량비로 혼합하되; 상기 촉매금속물질은 5~20㎚의 액상의 금 및 백금, 5~20㎚의 이산화티타늄 분말을 1:1:3의 중량비로 혼합한 제1 코팅조성물을 1차 코팅한 후, 상기 제1 코팅조성물이 1차 코팅된 마감재의 표면에 300㎚ 이하의 액상의 토르말린 10~30중량%; 5~20㎚의 이산화티타늄 30~70중량%; 1~5㎛의 금 분말 20~40중량%;로 혼합된 제2 코팅조성물을 2차 코팅하도록 구성되는 것을 특징으로 한다.
In addition, the finishing material coating method of the sauna booth according to the present invention, the nano-catalyst to promote the absorption of negative ion and negative electrode of the tourmaline of 300nm or less liquid maximized the electrical properties of the tourmaline to the finish material Mixing the metal materials in a weight ratio of 1: 1; The catalytic metal material is the first coating composition after mixing the first coating composition of 5 to 20nm liquid gold and platinum, and 5 to 20nm titanium dioxide powder in a weight ratio of 1: 1: 3, and then the first coating 10 to 30% by weight of the liquid tourmaline of 300 nm or less on the surface of the finish coating the composition; 30-70 weight% of titanium dioxide of 5-20 nm; It is characterized in that it is configured to secondary coating the second coating composition mixed with 20 to 40% by weight of gold powder of 1 ~ 5㎛.
상기 제1 코팅조성물이 코팅된 마감재의 표면에 상기 액상의 토르말린, 이산화티타늄 분말, 금 분말을 코팅하는 것은 상기 마감재에 금의 고유색상을 가지면서 제1 코팅조성물의 전기적 성질을 보완하기 위함이다.Coating the liquid tourmaline, titanium dioxide powder and gold powder on the surface of the finishing material coated with the first coating composition is to supplement the electrical properties of the first coating composition while having the intrinsic color of gold on the finishing material.
이때 상기 금을 나노화 된 액상물질이 아닌 1~5㎛으로 분쇄된 미세한 분말로 코팅하는 것은 마감재의 표면에 금 고유의 색상을 입히기 위한 것이다.At this time, the coating of the gold with a fine powder pulverized to 1 ~ 5㎛ not a nanonized liquid material is to coat the color of the gold on the surface of the finish.
또 상기 액상의 토르말린은 분말상태의 이산화티타늄과 금을 결합시키기 위한 결합재의 역할을 할 뿐더러 제1 코팅조성물의 전기적 성질을 보완하기 위한 역할을 하게 된다. 그리고 상기 이산화티타늄은 제1 코팅조성물 및 제2 코팅조성물을 마감재에 고착시키기 위한 역할과 함께 토르말린의 음이온 흡수 및 마이너스 전극의 방출을 촉진하기 위한 촉매제로의 역할을 하게 되는데, 이때 가장 바람직하게는 제2 코팅조성물의 전체중량에 대해 30~70중량%로 혼합하는 것이 바람직하다. 이는 상기 이산화티타늄의 양이 분말상태의 금과 나노화 된 액상의 토르말린에 비해 상대적으로 적거나 많은 경우 이산화티타늄, 금, 토르말린의 각각의 효과를 기대하기 어렵기 때문이다.
In addition, the liquid tourmaline serves as a binder for bonding the titanium dioxide and gold in the powder form, and also serves to supplement the electrical properties of the first coating composition. In addition, the titanium dioxide serves to fix the first coating composition and the second coating composition to the finishing material, and serves as a catalyst for promoting anion absorption of the tourmaline and release of the negative electrode. 2 It is preferable to mix at 30 to 70 weight% with respect to the total weight of a coating composition. This is because when the amount of titanium dioxide is relatively small or large compared to powdered gold and nano-ized liquid tourmaline, it is difficult to expect the respective effects of titanium dioxide, gold and tourmaline.
이처럼 본 발명은 비록 한정된 실시예에 의해 설명되었으나, 본 발명은 이것에 한정되지 않으며 본 발명이 속하는 기술분야에서 통상의 지식을 가진 자에 의해 본 발명의 기술사상과 아래에 기재될 특허청구범위의 균등범위 내에서 다양한 수정 및 변형이 가능하다 할 것이다.As described above, the present invention has been described by means of a limited embodiment, but the present invention is not limited thereto and is intended by those skilled in the art to which the present invention pertains to the technical spirit of the present invention and claims to be described below. Various modifications and variations are possible within the scope of equivalents.
Claims (2)
상기 토르말린과 촉매금속물질은 1:1의 중량비로 혼합되되, 상기 토르말린은 300㎚ 이하의 액상이고;
상기 촉매금속물질은 5~20㎚의 액상의 금 및 백금, 5~20㎚의 이산화티타늄 분말을 1:1:3의 중량비로 혼합하도록; 구성되는 것을 특징으로 하는 사우나 부스의 마감재 코팅조성물.
In the finish coating composition of the sauna booth consisting of nano-ized tourmaline mixed with nano-catalyzed catalytic metal material to promote anion absorption and negative electrode release of the tourmaline,
The tourmaline and the catalytic metal material are mixed in a weight ratio of 1: 1, and the tourmaline is in a liquid phase of 300 nm or less;
The catalytic metal material is 5 to 20nm liquid gold and platinum, 5-20nm titanium dioxide powder to mix in a weight ratio of 1: 1: 3; Finishing coating composition of the sauna booth, characterized in that configured.
상기 제1 코팅조성물이 1차 코팅된 마감재의 표면에 300㎚ 이하의 액상의 토르말린 10~30중량%과, 5~20㎚의 이산화티타늄 분말 30~70중량%과, 1~5㎛의 금 분말 20~40중량%로 혼합된 제2 코팅조성물;을 2차 코팅하도록 구성되는 것을 특징으로 하는 사우나 부스의 마감재 코팅방법.After coating the first coating composition of claim 1 on the finishing material,
10 to 30% by weight of liquid tourmaline of 300 nm or less, 30 to 70% by weight of titanium dioxide powder of 5 to 20 nm, and 1 to 5 μm of gold powder on the surface of the first coating composition coated with the first coating composition Second coating composition mixed with 20 to 40% by weight; Finish coating method of the sauna booth, characterized in that configured to coat the second.