KR102075243B1 - Manufacturing method for body massage composition containing functional mixed powder, body massage composition and massage on body method thereof - Google Patents

Abstract

The present invention relates to a method for preparing a composition for whole body massage containing a functional mixed powder, a composition for whole body massage containing a functional mixed powder prepared by the same, and a method for whole body massage using the same. In the method, preparing the ocher powder, illite powder, tourmaline powder and CMC (carboxymethyl cellulose) powder of the same particle size in the 900-1100 mesh particle size range, the ocher powder, illite powder of the same particle size, Preparing a functional mixed powder capable of forming a plurality of pores by mixing tourmaline powder and CMC (carboxymethyl cellulose) powder and mixing the same weight of distilled water with the functional mixed powder and stirring to prepare a composition for whole body massage. In the process of drying in a range of 36-40 degrees Celsius, similar to human body temperature. When a large number of pores are formed, the specific far-infrared radiation is maximized in the range of 36-40 degrees Celsius, which is similar to human body temperature, thereby increasing the concentration of NO (Nitric Oxide) in the human body and in large quantities at 37 degrees Celsius, which is similar to human body temperature. Specific far infrared rays increase the concentration of NO (Nitric Oxide) in the human body, maintain optimal blood circulation, protect the vascular endothelial, produce powerful antioxidants, promote the activation of functions of the circulatory system, immune system, nervous system, and maintain the homeostasis of the human body Has

Description

MANUFACTURING METHOD FOR BODY MASSAGE COMPOSITION CONTAINING FUNCTIONAL MIXED POWDER, BODY MASSAGE COMPOSITION AND MASSAGE ON BODY METHOD THEREOF}

The present invention relates to a method for preparing a composition for whole body massage containing a functional mixed powder, to a composition for whole body massage containing a functional mixed powder prepared by the same, and to a method for whole body massage using the same. Method of producing a composition for whole body massage having a very beneficial effect on the human body by increasing the concentration of NO (Nitric Oxide) in the human body through a massage using a composition for the whole body massage containing a functional mixture powder having a specific composition and specific particle size And it relates to a composition for whole body massage containing the functional mixed powder prepared by this and a method for whole body massage using the same.

Skin is the body's primary protective barrier and has a unique function of protecting the organs of the body from changes in temperature and humidity, and stimulation of the external environment such as ultraviolet rays and pollutants. Like everything in nature, skin has a homeostasis to balance itself. However, skin has its homeostasis broken down by internal and external factors. Specifically, with age, the secretion of various hormones that regulate metabolism internally decreases, and the function and function of cells of immune cells is reduced, thereby reducing the biosynthesis of immune proteins and bioconstituent proteins necessary for the living body. . In addition, due to the destruction of the ozone layer, the ultraviolet ray content increases in the sun's rays, and as the environmental pollution becomes more severe, free radicals and free radicals increase, resulting in excessive physical and chemical irritation and stress. By itself, it can make the skin unstable and break the homeostasis of the skin. Skin that loses homeostasis loses its balance, and its rhythm is disturbed, causing skin troubles such as skin dryness, loss of elasticity, pigmentation, trouble, and unbalanced secretion of sebum. Will be generated.

Edema (Ederma) refers to the state of tissue fluid between the tissue cells in the body, simply swelling symptoms. This can result from heart disease, kidney disease, or a disorder of blood circulation in any part of the body. Legs are particularly distant from the heart, and the effects of gravity are so great that blood flow to the kidneys is reduced, resulting in edema. In addition, in women, edema occurs during normal pregnancy or during pregnancy addiction, edema may occur temporarily if you drink too much water or salt, or when you are not tired or have a good night's sleep. When the permeability of capillaries increases, local edema also occurs, for example, in the case of burns, trauma, local inflammation, and allergic reactions.

When edema develops, your body swells, you gain weight, and when you sleep and wake up, your eyes are swollen, your fingers ring tight, and your shoes are smaller. Pressing a finger on the tibia and tibia may cause recessed edema (hamedoedema).

Conventional massage compositions include ingredients that serve to provide nutrients to the skin, and the most common one is to use grains, natural extracts or powders mixed with liquid materials. Such a conventional massage composition is commonly attached to the skin to perform a role of supplying a functional main ingredient and nutrients and oil and moisture components at a time. However, there is no research on the composition for the whole body massage containing the functional mixed powder to reduce the edema by increasing the NO (Nitric Oxide) concentration in the human body.

Looking at the prior literature related to the present invention, Korean Patent Publication No. 10-2018-0009367 discloses a composition comprising a natural extract. The composition of the prior literature contains anti-inflammatory effect, including the extract of honey, licorice, yulpi and ginseng as an active ingredient, as well as the anti-inflammatory effect, and thus has the effect of inhibiting or delaying oxidation and inhibiting or alleviating edema. It relates to a composition comprising an extract. However, the preceding document is also effective by the temporary supply of nutrients and oil and moisture components, the composition for whole body massage containing a functional mixed powder to reduce the edema through increasing the concentration of NO (Nitric Oxide) in the present invention This is different from the study.

Republic of Korea Patent Publication No. 10-2018-0009367

The present invention has been made to solve the above problems of the prior art, the object of the present invention is that when a plurality of voids are formed in the process of drying the composition for whole body massage in the range of 36-40 ℃ similar to human body temperature, Method for preparing a composition for whole body massage containing functional mixture powder which increases the emission of specific far infrared rays in the range of 36-40 ℃ similar to human body temperature to increase NO (Nitric Oxide) in human body and functional mixture produced by It is to provide a composition for body massage containing powder and a method for whole body massage using the same.

Another object of the present invention is to increase the concentration of NO (Nitric Oxide) in the human body by releasing a large amount of infrared rays at a temperature similar to human body temperature at 37 ℃, maintaining optimal blood circulation, vascular endothelial protection, strong antioxidant production, circulatory system, immune system , To promote the activation of the function of the nervous system, and to prepare a composition for the whole body massage composition containing a functional mixed powder that maintains the homeostasis of the human body, a composition for a whole body massage containing the functional mixed powder prepared thereby and a whole body massage method using the same To provide.

Another object of the present invention is to prepare a composition for the whole body massage composition containing a functional mixed powder that promotes lymph circulation by increasing the concentration of NO (Nitric Oxide) in the human body and removes waste products to remove the swelling of the skin and thereby produced It is to provide a composition for whole body massage containing the functional mixture powder and a method for whole body massage using the same.

Another object of the present invention is to promote blood circulation by increasing the concentration of NO (Nitric Oxide) in the human body to supply nutrients and moisture and to remove waste products to increase skin elasticity and to recover fatigue containing whole body containing functional powder It is to provide a method for producing a composition for massage, and a composition for whole body massage containing the functional mixed powder produced thereby and a method for whole body massage using the same.

In order to achieve the above object, the present invention provides a method for preparing a composition for whole-body massage, comprising ocher powder, illite powder, tourmaline powder and CMC (carboxymethyl cellulose) powder of the same particle size in the 900-1100 mesh particle size range. A step of preparing, preparing a functional mixed powder capable of forming a plurality of pores by mixing the ocher powder, illite powder, tourmaline powder and CMC (carboxymethyl cellulose) powder of the same particle size and the same weight to the functional mixed powder It provides a method for producing a composition for whole body massage containing a functional mixed powder comprising the step of mixing and stirring distilled water to prepare a composition for whole body massage.

The present invention provides a composition for whole body massage containing a functional mixed powder prepared by a method for preparing a composition for whole body massage containing a functional mixed powder to achieve the above object.

The present invention is to prepare a loess powder, illite powder, tourmaline powder and CMC (carboxymethyl cellulose) powder of the same particle size in the range of 900-1100 mesh particle size to achieve the above object, the loess of the same particle size A powder, an illite powder, a tourmaline powder, and a CMC (carboxymethyl cellulose) powder are mixed to prepare a functional mixed powder capable of forming a plurality of pores, and mixed with a distilled water of the same weight to the functional mixed powder and stirred for whole body massage. Preparing a composition, applying the composition for whole body massage to the target skin surface of the human body to form a first composition layer, covering 70 μm-90 μm thick paper soaked in water on the first composition layer Forming a layer, wherein the second composition layer is formed by reapplying the whole body massage composition on the Hanji layer. And wherein the method provides a full-body massage using the composition for the cover 2 the foil on the layer containing the functional mixture powder comprising the step of forming the foil layer body massage composition.

The present invention is a method for producing a composition for whole body massage containing a functional mixed powder, a composition for whole body massage containing a functional mixed powder prepared by the present invention and a whole body massage method using the same is a process of drying in a 36-40 ℃ similar to the human body temperature When a large number of pores are formed in, the emission of a particular far infrared rays is maximized in the range of 36-40 ℃ similar to the human body temperature has the effect of increasing the concentration of NO (Nitric Oxide) in the human body.

In the present invention, a method for preparing a composition for whole body massage containing a functional mixed powder, a composition for whole body massage containing a functional mixed powder prepared by the same, and a whole body massage method using the same, within the range of 900-1100 mesh (MESH) particle size When whole-body massage is performed using functional mixture powders of ocher powder, illite powder, tourmaline powder and CMC (carboxymethyl cellulose) powder of the size, many specific size pores are formed due to the same particle size, and human body temperature It is rich in the emission of specific far infrared rays in the range of 36-40 ℃ similar to that of having the effect of increasing NO (Nitric Oxide) concentration in human body. Furthermore, when shredded hanji with a length range of 10 μm-15 μm is added, fibrin keeps strong inter-particle bonds in the particles and blocks all pores while the ocher is not dry at first, and during the time when the loess loses moisture and dries, The volume of fibrin is reduced, making the micropore while maintaining the bond. In addition, 1000 mesh particle size and 13 μm in length are mixed when 13 μm long crushed Hanji powder is mixed with ocher powder, illite powder, tourmaline powder and CMC (carboxymethyl cellulose) powder of 1000 mesh particle size. Since the values are approximate to each other, microvoids are most likely to occur, and the specific infrared radiation is emitted the most in the range of 36-40 ℃ similar to the human body temperature, thereby increasing the NO (Nitric Oxide) concentration in the human body. Has .

The method for producing a composition for whole body massage containing the functional mixed powder of the present invention, the composition for whole body massage containing the functional mixed powder prepared by the same, and the method for whole body massage using the same are applied to a specific far-infrared ray which is released in a large amount at 37 ° C. similar to the human body temperature By increasing the NO (Nitric Oxide) concentration in the human body, and maintains the optimal blood circulation, vascular endothelial protection, strong antioxidants produced, promoting the activation of functions of the circulatory system, immune system, nervous system, etc. has a unique effect of maintaining the homeostasis of the human body.

The present invention provides a method for preparing a composition for whole body massage containing a functional mixed powder, a composition for whole body massage containing a functional mixed powder prepared by the same, and a method for whole body massage using the same according to an increase in NO (Nitric Oxide) concentration in the human lymph circulation. This promotes and removes wastes and has an effect of removing swelling of the skin.

The present invention provides a method for producing a composition for whole body massage containing a functional mixed powder, a composition for whole body massage containing a functional mixed powder prepared by the same, and a method for whole body massage using the same according to an increase in the concentration of NO (Nitric Oxide) in the human body This promotes the supply of nutrients and moisture, and removes waste products, increasing skin elasticity and restoring fatigue.

1 is a flow chart of a method for producing a composition for whole body massage containing the functional mixed powder of the present invention.
Figure 2 is a flow chart of the whole body massage method using a composition for whole body massage containing a functional powder mixed.
Figure 3a is a photograph showing the appearance of the massage and the formation of the voids according to the whole body massage method using the composition for whole body massage containing the functional powder mixed.
Figure 3b is ocher powder, illite powder in a functional mixed powder consisting of 30 parts by weight of ocher powder, 170 parts by weight of illite powder, 6 parts by weight of tourmaline powder, 5 parts by weight of CMC (carboxymethyl cellulose) powder and 5 parts by weight of fiber. , Tourmaline powder and CMC (carboxymethyl cellulose) powder are photographs showing that many pores are formed when the fiber size is 13 μm in length with the same particle size of 1000 mesh.
Figure 4 is a reference picture showing the color change according to the concentration of NO (Nitric Oxide) in the human body of Neogenis Test Strips.
5 is a photograph comparing the color of Neogenis Test Strips in which the saliva (acupuncture) of the test subjects were buried before and after the whole-body massage method was performed using the whole-body massage composition containing the functional mixed powder.
FIG. 6 shows Neogenis Test Strips coated with saliva (acupuncture) of the test subjects after whole-body massage using powder mixed with ocher powder, illite powder, tourmaline powder and CMC (carboxymethyl cellulose) powder of different particle sizes. Salivary powder (acupuncture needle) after whole body massage was performed by using a functional mixture powder capable of forming a large number of pores by mixing ocher powder, illite powder, tourmaline powder and CMC (carboxymethyl cellulose) powder having the same particle color as the color. ) Is a photo comparing the colors of Neogenis Test Strips with the.

Hereinafter, the present invention will be described in detail with reference to the accompanying drawings so that those skilled in the art can easily implement the present invention.

1 is a flow chart of a method for producing a composition for whole body massage containing the functional mixed powder of the present invention. According to Figure 1 is a method for producing a composition for body massage containing the functional powder of the present inventors in the range of 900-1100 mesh particle size ocher powder, illite powder, tourmaline powder and CMC (carboxymethyl cellulose) powder of the same particle size A step of preparing, preparing a functional mixed powder capable of forming a plurality of pores by mixing the ocher powder, illite powder, tourmaline powder and CMC (carboxymethyl cellulose) powder of the same particle size and the same weight to the functional mixed powder Mixing and stirring distilled water to prepare a composition for whole body massage.

When a large number of voids are formed in the process of drying the composition for the whole body massage containing the present inventors functional mixture powder in the range of 36-40 ℃ similar to human body temperature, a large amount of specific far infrared rays in the range of 36-40 ℃ similar to human body temperature When NADPH is oxidized to NADP ⁺ by stimulation of specific far infrared rays in endothelial cells in human body, L-Arginine binds to oxygen (O ₂ ) and L-Citrulline (L). -Citrulline, and nitrogen monoxide (NO) is produced in the body. First, by the composition for the whole body massage containing the functional mixed powder of the present invention, a large amount of nitric oxide (NO) is generated in vascular endothelial cells, nitric oxide (NO) generated from vascular endothelial cells expands blood vessels and removes waste products It has the effect of preventing aging. By the composition for the whole-body massage containing the functional mixed powder of the present invention, the second generation of nitric oxide (NO) also in the nerve cells of the brain, the nitric oxide (NO) generated in the nerve cells of the brain to strengthen the brain blood flow dementia I have the effect of preventing Alzheimer's. Third, by the composition for the whole-body massage containing the functional powder of the present invention, a lot of nitrogen monoxide (NO) is also generated in the lungs, nitrogen monoxide (NO) generated in the lungs has the effect of expanding the airways to enable comfortable breathing Have Fourth by the composition for the whole body massage containing the functional powder of the present inventors, a lot of nitrogen monoxide (NO) is also generated in the white blood cells, nitrogen monoxide (NO) generated in the white blood cells enhance the phagocytosis effect to amplify the anti-cancer effect Have Fifth, the monoxide (NO) is generated in the genitals by the composition for the whole body massage containing the functional mixed powder of the present inventors, the nitrogen monoxide (NO) generated in the genitals has the effect of strengthening the erection capacity by expanding blood vessels. ,

Ocher has a distinctive far infrared rays that are wavelengthd in the yellow soil, and such far infrared rays are known to be very beneficial to the health of the human body. In addition, the loess has been recognized from the East and West to revitalize the cells, and has the effect of delaying skin aging, antimicrobial properties, removing bacteria, and adsorption, and at the same time removing the waste accumulated in the skin when used for massage. . In the present invention, the ocher powder uses a particle size of 900-1100 mesh. If the particle size of the ocher powder is less than 900 mesh, it may cause difficulty in attaching the composition for whole body massage to the skin of the subject subjected to the whole body massage method, and there is a possibility of a wound on the skin of the subject. In addition, when the particle size of the ocher powder exceeds 1100 mesh, the manufacturing cost increases, which may cause economic problems. Furthermore, if the ocher powder is out of the range of 900-1100 mesh particle size, a large number of pores may not be formed during the drying process in the range of 36-40 ° C similar to human body temperature, and in the range of 36-40 ° C similar to human body temperature. The emission of certain far infrared rays may be reduced, so that the effect of increasing the concentration of nitric oxide (NO) in the human body may not occur.

The illite (chemical composition: (K, H ₃ O) Al ₂ (Si, Al) ₄ O ₁₀ (H ₂ O, OH) ₂ ) is a mica mineral belonging to monoclinic system. Hardness 1-2, specific gravity 2.6-2.9, streak color white. Illite, which has a chemical composition and crystal structure, is a mineral that emits soft far-infrared rays and is safe for the skin. The illite powder uses 900-1100 mesh particle size. If the particle size of the illite powder is less than 900 mesh, it may be difficult to attach the composition for the whole body massage to the skin of the subject subjected to the whole body massage method, there is a possibility that the wound on the skin of the subject. In addition, if the particle size of the illite powder exceeds 1100 mesh, the manufacturing cost increases, there is a possibility that problems in economic efficiency. Furthermore, when the illite powder is out of the 900-1100 mesh particle size range, a large number of pores may not be formed during the drying process at 36-40 ° C., which is similar to human body temperature, and 36-40 ° C., which is similar to human body temperature. In particular, the emission of certain far infrared rays may be reduced, so the effect of increasing the concentration of nitric oxide (NO) in the human body may not occur.

The chemical composition of tourmaline is a complex borosilicate of iron, magnesium, alkali metals and aluminum. Usually consists of hexagonal or hexahedral, sometimes triangular, columnar, minerals belonging to the hexagonal system with crystal structure. Tourmaline promotes skin circulation. Tourmaline anion and a weak electric current come into contact with the skin and have a synergistic effect, which is very effective for skin care. In addition, by activating the skin by emitting far infrared rays, it is excellent for maintaining beauty and skin health. Tourmaline powder uses a 900-1100 mesh particle size. If the particle size of the tourmaline powder is less than 900 mesh, it may cause difficulty in attaching the composition for the whole body massage to the skin of the subject subjected to the whole body massage method, and there is a possibility that a wound occurs in the skin of the subject. In addition, if the particle size of the tourmaline powder exceeds 1100 mesh, there is a possibility that the production cost increases, causing problems in economic efficiency. Furthermore, if the tourmaline powder is out of the 900-1100 mesh particle size, a number of pores may not be formed during the drying process in the range of 36-40 ° C similar to human body temperature, and in the range of 36-40 ° C similar to human body temperature. The emission of certain far infrared rays may be reduced, so that the effect of increasing the concentration of nitric oxide (NO) in the human body may not occur.

CMC (carboxymethyl cellulose) powder is a natural binder and forms a large number of voids during the massage process using the composition for whole body massage to maximize the emission of specific far infrared rays and is nontoxic and harmless to the human body. CMC (carboxymethyl cellulose) powder uses a 900-1100 mesh particle size. If the particle size of the CMC (carboxymethyl cellulose) powder is less than 900 mesh, it may cause difficulty in attaching the composition for whole body massage to the skin of the subject subjected to the whole body massage method. In addition, when the particle size of the CMC (carboxymethyl cellulose) powder exceeds 1100 mesh, the manufacturing cost increases, which may cause economic problems. Furthermore, if the CMC (carboxymethyl cellulose) powder is out of the 900-1100 mesh particle size, a number of pores may not be formed in the process of drying in the range of 36-40 ℃ similar to the human body temperature, 36 similar to the human body temperature In the range of -40 ℃, the emission of certain far infrared rays may be reduced, so that the effect of increasing the concentration of nitric oxide (NO) in the human body may not occur.

In order to form a large number of specific size pores when performing whole-body massage using functional mixture powder prepared by mixing ocher powder, illite powder, tourmaline powder and CMC (carboxymethyl cellulose) powder, 900-1100 mesh particle size It should have the same particle size within the range. When the whole body massage is performed using a mixed powder prepared by mixing ocher powder, illite powder, tourmaline powder and CMC (carboxymethyl cellulose) powder of different particle size but not the same particle size, a large number of specific size pore formation In the range of 36-40 ° C, which is difficult and similar to human body temperature, the emission of certain far-infrared rays is reduced so that the effect of increasing NO (Nitric Oxide) concentration in the human body does not occur.

In the step of preparing the functional mixed powder may be further mixed with a fiber called crushed Hanji water of 10㎛-15㎛ length. By adding crushed Korean paper called water to the functional mixed powder, the soft touch improves contact with the skin, and the natural ingredients of 10 ㎛-15 ㎛ long crushed Korean paper called water during the massage process The pores of the skin are alive and breathed, and the absorption of good active ingredients on the skin is quick and moisturizing. Fibrin called crushed Korean paper should have a length of 10 μm-15 μm. When the length of the crushed Hanji-fiber called water exceeds 10㎛-15㎛, many pores are not formed in the process of drying in the range of 36-40 ℃ which is similar to human body temperature. In the range of 40 ℃, the emission of certain far infrared rays is reduced, so that the effect of increasing the concentration of NO (Nitric Oxide) in the human body does not occur. The fibrils crushed Hanji in water retained strong inter-particle bonds in the particles when the initial functional mixed powder did not dry out, and blocked all pores, but the fibrils crushed Hanji in water during the time that the ocher lost moisture and dried Its volume decreases, creating fine pores while maintaining bonding. These micropores correspond to the pores produced by the reduction of fibrils called crushed Korean paper. The most common length of micropores is when 13 micrometers of crushed Korean paper is mixed with fibrils called water in an ocher powder, an illite powder, a tourmaline powder and a CMC (carboxymethyl cellulose) powder having a particle size of 1000 mesh. Since the 1000 mesh particle size and the length of 13 μm are approximate to each other, the result of generating the most micropores is generated.

Functional mixture powder is 20-40 parts by weight of the ocher powder, 150-190 parts by weight of the illite powder, 5-7 parts by weight of the tourmaline powder, 4-6 parts by weight of the CMC (carboxymethyl cellulose) powder and the fiber 4- 6 parts by weight may be mixed.

 The ocher powder is preferably mixed 20-40 parts by weight. If the ocher powder is less than 20 parts by weight, there is a problem in adhesion during the massage process, and there is a possibility of crumbs in the drying process. When the clay powder exceeds 40 parts by weight, the number of pores decreases and the far infrared emission is reduced in the range of 36-40 ° C. similar to the human body temperature, so that the effect of increasing the concentration of NO (Nitric Oxide) in the human body does not occur. Can be. Even more preferably, the clay powder may be mixed in 30 parts by weight.

The illite powder is preferably mixed at 150-190 parts by weight. If the illite powder is less than 150 parts by weight, the number of voids may be reduced, and far infrared emission may be reduced in the range of 36-40 ° C. similar to human body temperature. If the illite powder exceeds 190 parts by weight, there is a problem in adhesion and cracking or chipping may occur during the massage process. Furthermore, when the illite powder is out of the above range, the specific far-infrared emission in the range of 36-40 ° C. similar to the human body temperature is relatively reduced, so that the effect of increasing the NO (nitric oxide) concentration in the human body does not occur. You can do it. Even more preferably, the illite powder may be mixed in an amount of 170 parts by weight.

The tourmaline powder is preferably 5-7 parts by weight mixed. If the tourmaline powder is out of the above range, the specific far-infrared emission in the range of 36-40 ℃ similar to the human body temperature is relatively reduced, which causes the problem that the effect of increasing the NO (Nitric Oxide) concentration in the human body does not occur. Can be. Even more preferably, the tourmaline powder may be mixed in 6 parts by weight.

The CMC (carboxymethyl cellulose) powder preferably has a structure containing 4-6 parts by weight. If the CMC (carboxymethyl cellulose) powder is less than 4 parts by weight, the bonding strength between the components is weakened may cause problems such as chipping or cracking during the massage process. When the CMC (carboxymethyl cellulose) powder exceeds 6 parts by weight, the bonding force between the components is so strong that the excessive stickiness and difficulty in the application process for the massage may occur. In addition, when the CMC (carboxymethyl cellulose) powder is out of the above range, the specific far-infrared emission in the range of 36-40 ° C. similar to the human body temperature is relatively decreased, so that the effect of increasing NO (Nitric Oxide) concentration in the human body does not occur. Problems may arise. CMC (carboxymethyl cellulose) powder maintains strong bonding between particles and closes pores when the initial functional mixed powder is not dry, but retains the bond due to the volume of functional mixed powder losing its moisture and drying time. While making a micro void. These fine pores correspond to pores caused by a decrease in the volume of CMC (carboxymethyl cellulose). Even more preferably, 5 parts by weight of the CMC (carboxymethyl cellulose) powder may be mixed.

 The fibrin, which is called crushed Korean paper, preferably has 4-6 parts by weight. Less than 4 parts by weight of the crushed Hanji fibrils in water may weaken the bonding force between the components may cause problems such as chipping or cracking during the massage process. When more than 6 parts by weight of fibrils called crushed Hanji in water is relatively reduced in certain far-infrared emission in the range of 36-40 ° C similar to human body temperature, the effect of increasing NO (Nitric Oxide) concentration in the human body does not occur. Problems may arise. Even more preferably, 5 parts by weight of the fibrous soaked crushed Korean paper may be mixed.

The functional mixture powder is mixed with a distilled water of the same weight and stirred to prepare a composition for whole body massage. When distilled water of less than the same weight is mixed, the viscosity is too high, excessive stickiness and difficulty in the process of applying for massage. When distilled water of a weight greater than the same weight is mixed, the viscosity may be too low, causing a difficulty in the process of applying for massage, such as a drop occurs. Furthermore, if the same weight of distilled water is not mixed, the specific far-infrared emission in the range of 36-40 ° C similar to the human body temperature is relatively reduced, so that the effect of increasing NO (Nitric Oxide) concentration in the human body does not occur. Problems may arise.

Overall, when the particle size or weight of the components is outside of the specified ranges, a number of specific size micropores are not formed, thereby relatively reducing the specific far-infrared emission in the range of 36-40 ° C, which is similar to human body temperature, and reducing NO in the human body. Problems may arise with the effect of increasing nitric oxide concentration.

Figure 2 is a flow chart of the whole body massage method using a composition for whole body massage containing a functional powder mixed. According to Figure 2 the whole body massage method using the composition for the whole-body massage containing the functional powder of the present inventors in the range of 900-1100 mesh particle size ocher powder, illite powder, tourmaline powder and CMC (carboxymethyl cellulose) of the same particle size Preparing a powder, preparing a functional mixture powder capable of forming a plurality of pores by mixing the same particle size of ocher powder, illite powder, tourmaline powder, and CMC (carboxymethyl cellulose) powder; Mixing and stirring the same weight of distilled water to prepare a composition for whole body massage, applying the composition for whole body massage to the target skin surface of the human body to form a first composition layer, and in water on the first composition layer Covering the wet paper 70㎛-90㎛ thick paper to form a hanji layer, the whole body on the Hanji layer By re-applying the composition for the limbs cover the first step of forming a second layer composed of aluminum foil and on the second composition layer comprises the step of forming the aluminum foil layer.

The whole body massage composition is applied to the target skin surface of the human body by mixing the same particle size of ocher powder, illite powder, tourmaline powder and CMC (carboxymethyl cellulose) powder in the 900-1100 mesh particle size range. The first composition layer is formed. Preferably, the first composition layer has a thickness of 0.5-2 cm. If the first composition layer is less than 0.5 cm, the amount of specific far-infrared radiation in the range of 36-40 ° C., which is similar to the human body temperature, is relatively small, and thus the effect of increasing the concentration of NO (Nitric Oxide) in the human body is insufficient. If the composition layer exceeds 2cm, there is a difficulty in forming micropores of a specific size, the subject complains of frustration, and the problem of excessive time required for the procedure may occur.

A paper layer is formed on the first composition layer by covering a 70 μm-90 μm thick Korean paper soaked in water. The formation of a Hanji layer has the effect of improving skin moisturizing. If the Hanji layer is less than 70 μm, there is a problem that the Hanji layer is easily torn, and many specific size micropores are not formed, which is similar to human body temperature in the range of 36-40 ° C. The specific far-infrared emission at Rs is relatively reduced, which may cause the problem that the effect of increasing the concentration of nitric oxide (NO) in the human body does not occur. If the Hanji layer exceeds 90 μm, the Hanji layer is too thick to complain of the subject's frustration, and many specific sized micro-pores are not formed, so that specific far-infrared emission in the range of 36-40 ° C similar to human body temperature is relatively This may cause a problem that the effect of increasing the concentration of NO (Nitric Oxide) in the human body does not occur.

Applying the whole body massage composition comprising the same weight of distilled water mixed with ocher powder, illite powder, tourmaline powder and CMC (carboxymethyl cellulose) powder in the 900-1100 mesh particle size range on the Hanji layer second To form a composition layer. Preferably, the second composition layer has a thickness of 0.5-2 cm. If the second composition layer is less than 0.5 cm, the amount of specific far-infrared radiation in the range of 36-40 ° C., which is similar to the human body temperature, is relatively small, so that the effect of increasing the concentration of NO (Nitric Oxide) in the human body is insufficient. If the composition layer exceeds 2cm, there is a difficulty in forming the micro voids, complains that the subject is frustrated, and may cause a problem that the time required for the procedure is excessive.

The silver foil layer is covered on the second composition layer to form a silver foil layer. By forming the silver foil layer, the specific far infrared rays emitted in the range of 36-40 ° C. similar to the human body temperature by a plurality of specific size micropores are not emitted to the outside, but are reflected by the silver foil layer and irradiated to the target skin surface of the human body. In particular, the specific far-infrared rays irradiated to the target skin surface are relatively increased, and the increase of NO (Nitric Oxide) concentration in the human body is amplified.

Figure 3a is a photograph showing the appearance of the massage and the formation of the voids according to the whole body massage method using the composition for the whole-body massage containing the functional mixed powder.

According to Figure 3a, a drying time of 10-20 minutes is applied after the first composition layer, the Hanji layer and the second composition layer is formed. That is, a time interval of 10-20 minutes exists between forming the second composition layer and forming the silver foil layer. Distilled water evaporates during a time interval of 10-20 minutes, forming a number of specific size micropores and relatively high specific infrared radiation emission in the range of 36-40 ° C, similar to human body temperature. The effect of increasing the concentration is generated. According to FIG. 3A, pores are formed by drying, and a plurality of pores are formed as time passes. After the step of forming the silver foil layer there is a holding time of 10-20 minutes. Specific far-infrared radiation in the range of 36-40 ° C., similar to human body temperature caused by a number of specific size micropores for 10-20 minutes of retention time, is irradiated to the target skin surface of the human body and the concentration of NO (Nitric Oxide) in the human body An increase of is generated.

Figure 3b is ocher powder, illite powder in a functional mixed powder consisting of 30 parts by weight of ocher powder, 170 parts by weight of illite powder, 6 parts by weight of tourmaline powder, 5 parts by weight of CMC (carboxymethyl cellulose) powder and 5 parts by weight of fiber. , Tourmaline powder and CMC (carboxymethyl cellulose) powder are photographs showing that many pores are formed when the fiber size is 13 μm in length with the same particle size of 1000 mesh. According to FIG. 3b, immediately after the formation of the second composition layer using a functional mixed powder containing 13 µm-thick fiber pulverized paper in water, after 1 minute, after 3 minutes, after 5 minutes, 10 Comparing the photographs after the passage of minutes, it was confirmed that a large number of voids were formed by 13 μm-length fibers of crushed Hanji in water. In other words, when 13 μm-long fibrils called crushed Hanji are added to water, when the initial functional mixed powder is not dry, the interparticles are strongly maintained and the pores are blocked to hold all the pores in the particles. During the loss and drying time, the volume of crushed Korean paper reduced the volume of fibrin soaked water. Furthermore, comparing FIG. 3A and FIG. 3B, it can be seen that the number of fine pores produced by addition of 13 µm-long fibrils called crushed Hanji in water increases.

Figure 4 is a reference picture showing the color change according to the concentration of NO (Nitric Oxide) in the human body of Neogenis Test Strips.

5 is a photograph comparing the color of Neogenis Test Strips in which the saliva (acupuncture) of the test subjects were buried before and after the whole-body massage method was performed using the whole-body massage composition containing the functional mixed powder. According to FIG. 5, a 23-year-old woman conducted an experiment on an empty stomach, and showed a difference in NO (Nitric Oxide) concentration in the human body before and after the whole body massage method. According to FIG. 5, a 23-year-old female subject had a NO (Nitric Oxide) concentration in the human body of 25-100 (Ч) before the whole body massage method was performed using the composition for whole body massage containing the inventor's functional mixed powder in a fasting state. It was in the Low (lack) state in the mol / L) range. However, the whole body massage method using the composition for the whole body massage containing the functional mixed powder is performed, and after 10 minutes have elapsed the concentration of NO (Nitric Oxide) in the human body is in the range of 100-300 (Чmol / L) It rose to the normal state.

FIG. 6 shows Neogenis Test Strips coated with saliva (acupuncture) of the test subjects after whole-body massage using powder mixed with ocher powder, illite powder, tourmaline powder and CMC (carboxymethyl cellulose) powder of different particle sizes. Salivary powder (acupuncture needle) after whole body massage was performed by using a functional mixture powder capable of forming a large number of pores by mixing ocher powder, illite powder, tourmaline powder and CMC (carboxymethyl cellulose) powder having the same particle color as the color. ) Is a photo comparing the colors of Neogenis Test Strips with the. According to Figure 6 when the whole body massage was carried out using a functional mixed powder of a mixture of ocher powder, illite powder, tourmaline powder and CMC (carboxymethyl cellulose) powder of the same particle size and 20 minutes have elapsed, In the range of 36-40 ℃, which is similar to human body temperature, the formation of pores maximizes the emission of specific far infrared rays and increases the concentration of NO (Nitric Oxide) in the human body, whereas ocher powder, illite powder, When the whole body massage is performed using a mixed powder of tourmaline powder and CMC (carboxymethyl cellulose) powder, and after 20 minutes, a large number of pores are not formed and the temperature is in the range of 36-40 ° C. similar to the human body temperature. The emission of certain far infrared rays is reduced and there is no effect of increasing the concentration of NO (Nitric Oxide) in the human body.

Referring to Figure 6 in detail, using a functional mixture of a mixture of ocher powder, illite powder, tourmaline powder and CMC (carboxymethyl cellulose) powder of the same particle size massage for women aged 23 and 38 years on an empty stomach As a result of conducting the experiment and performing the whole body massage method, the increase of NO (Nitric Oxide) concentration in the human body appeared after 20 minutes. According to FIG. 6, both the 23-year-old and the 38-year-old female subjects had a NO (Nitric Oxide) concentration of 25 in the human body before the whole body massage method was performed using the composition for whole body massage containing the present inventors' functional mixture powder in a fasting state. It was in the low state in the range of -100 (Чmol / L). However, the whole body massage method using the composition for the whole body massage containing the functional mixed powder was performed, and after 20 minutes, both the 23 and 38 year old female subjects had a concentration of 300 (NO) in the human body. It rose to the range exceeding (Чmol / L), and became Optimal state.

The porosity is the ratio of the porosity to the total volume of the solid. In general, the smaller and higher the particle size, the larger the porosity. In the present invention, a plurality of pores are formed when a mixture of distilled water is mixed and stirred in a functional mixture powder of ocher powder, illite powder, tourmaline powder and CMC (carboxymethyl cellulose) powder of the same particle size in the 900-1100 mesh particle size range. The color of the Neogenis Test Strips that formed, and only when these numerous voids were formed, resulted in far-infrared emission in the range of 36-40 ° C similar to human body temperature, soaking the saliva (acupuncture) of the subject after performing a full body massage. It can be seen that the concentration of NO (Nitric Oxide) in the human body is increased. On the contrary, when distilled water is mixed and mixed with a mixture of ocher powder, illite powder, tourmaline powder and CMC (carboxymethyl cellulose) powder of different particle sizes, and stirred and dried, a large number of pores are not formed. Far-infrared emission was reduced in the range of -40 ° C, and the color of Neogenis Test Strips with saliva (acupuncture) of the subject after the whole body massage showed no increase of NO (Nitric Oxide) concentration in the human body.

As described above, when the whole body massage method is performed by using the composition for whole body massage containing the functional powder mixed with ocher powder, illite powder, tourmaline powder and CMC (carboxymethyl cellulose) powder of the same particle size of the present invention At 37 ℃ -40 ℃, which is similar to human body temperature, certain far-infrared rays are released, which raises NO (Nitric Oxide) concentration in human body, thus maintaining optimal blood circulation, protecting vascular endothelial, producing strong antioxidants, and circulatory system , Immune system, nervous system and other functions, such as promoting the activation of the body will have a unique effect of maintaining homeostasis. Furthermore, the present invention contains a functional mixed powder of crushed Hanji, which has a length similar to that of a functional mixed powder of ocher powder, illite powder, tourmaline powder and CMC (carboxymethyl cellulose) powder of the same particle size added to the present invention. When the whole body massage method is performed using the whole body massage composition, specific far infrared rays are released at 37 ° C.-40 ° C., which is similar to the human body temperature, thereby increasing the concentration of nitric oxide (NO) in the human body. The unique effects of maintaining optimal blood circulation, protecting vascular endothelial, producing powerful antioxidants, promoting the activation of functions of the circulatory system, immune system, nervous system, and maintaining the homeostasis of the human body will be further enhanced.

Example 1

A functional mixed powder was prepared by mixing 30 g of ocher powder of 1000 mesh, 170 g of illite powder, 6 g of tourmaline powder, and 5 g of CMC (carboxymethyl cellulose) powder and 5 g of 13 µm long fiber. 216 g of distilled water was mixed with 216 g of the functional mixed powder and stirred to prepare a composition for whole body massage. The composition for whole body massage was applied to the target skin surface of the human body to form a first composition layer, and a paper layer was formed on the cover of 70 μm-90 μm thick paper soaked in water. Thereafter, the composition for applying the whole body massage layer was again applied to form a second composition layer, and a silver foil layer was formed by covering silver foil on the second composition layer at a time interval of 20 minutes. Thereafter a 20 minute hold time.

Experimental Example 1

In order to determine the edema reduction effect according to Example 1 prepared in the above, the whole body massage method using the whole body massage composition containing the functional mixed powder of Example 1 to eight women in 20-30 Calf thickness before and after was compared. Measuring the calf thickness of the test subject before the whole body massage method using the composition for whole body massage containing the functional mixed powder of Example 1, using the composition for whole body massage containing the functional mixed powder of Example 1 The calf circumference was measured after the retention time of 20 minutes after the whole body massage method.

Table 1 shows the whole body massage method using the whole body massage composition containing the functional circumference of the calf and the present invention before the whole body massage method using the whole body massage composition containing the functional mixed powder of Example 1 It shows the rate of decrease in the circumference of the calf after the trial.

Subject
(Women in their 20s and 30s) Calf circumference length (cm) before full body massage Calf circumference length (cm) after full body massage method Reduction rate
(%) One 34.50 32.80 4.93 2 32.45 31.25 3.70 3 35.30 32.45 8.07 4 37.25 34.50 7.38 5 31.85 29.90 6.12 6 29.90 28.75 3.85 7 32.10 31.35 2.34 8 30.85 28.95 6.16 Average 32.88 31.24 5.39

According to Table 1, the average calf circumference was decreased by an average of 5.39% before and after the whole body massage method using the whole body massage composition containing the functional powder of Example 1. Therefore, it was confirmed that the whole-body massage method using the composition for the whole-body massage containing the functional mixed powder of the present invention has an edema reduction effect.

As described above, although the present invention has been described by way of limited embodiments, the present invention is not limited to the above-described embodiments, which can be variously modified and modified by those skilled in the art to which the present invention pertains. Modifications are possible. Therefore, the spirit of the present invention should be grasped only by the claims described below, and all equivalent or equivalent modifications thereof will belong to the scope of the present invention.

Claims (10)

In the method for producing a composition for whole body massage,
Preparing an ocher powder, an illite powder, a tourmaline powder, and a CMC (carboxymethyl cellulose) powder having the same particle size in a 900-1100 mesh particle size range;
The formation of a plurality of pores by mixing the same particle size ocher powder, illite powder, tourmaline powder and CMC (carboxymethyl cellulose) powder, and further mixed with fibrils called water of 10㎛-15㎛ long shredded Hanji Preparing a possible functional mixed powder; And
Preparing a composition for whole body massage by mixing and stirring distilled water of the same weight in the functional powder;
Method for producing a composition for whole body massage containing a functional mixed powder comprising a.
delete The method of claim 1,
The functional mixed powder is 20-40 parts by weight of the ocher powder, 150-190 parts by weight of the illite powder, 5-7 parts by weight of the tourmaline powder, 4-6 parts by weight of the CMC (carboxymethyl cellulose) powder and the fiber 4 -6 parts by weight of a method for producing a composition for whole body massage containing a functional mixed powder, characterized in that the mixture.
The method of claim 3,
The functional mixed powder is made of 30 parts by weight of the ocher powder, 170 parts by weight of the illite powder, 6 parts by weight of the tourmaline powder, 5 parts by weight of the CMC (carboxymethyl cellulose) powder and 5 parts by weight of the fiber, The ocher powder, the illite powder, the tourmaline powder and the CMC (carboxymethyl cellulose) powder all have the same particle size of 1000 mesh and the fibrin has a 13 μm length. Method for producing a composition for use.
A composition for whole body massage containing a functional mixed powder prepared by the method of any one of claims 1, 3 and 4.
Preparing an ocher powder, an illite powder, a tourmaline powder, and a CMC (carboxymethyl cellulose) powder having the same particle size in a 900-1100 mesh particle size range;
The formation of a plurality of pores by mixing the same particle size ocher powder, illite powder, tourmaline powder and CMC (carboxymethyl cellulose) powder, and further mixed with fibrils called water of 10㎛-15㎛ long shredded Hanji Preparing a possible functional mixed powder;
Preparing a composition for whole body massage by mixing and stirring distilled water of the same weight in the functional powder;
Applying the whole body massage composition to a target skin surface of a human body to form a first composition layer;
Forming a hanji layer on the first composition layer by covering a 70 μm-90 μm thick paper soaked with water;
Re-coating the whole body massage composition on the Hanji layer to form a second composition layer; And
Forming a silver foil layer by covering the silver foil on the second composition layer;
Systemic massage method using a composition for whole body massage containing a functional mixed powder comprising a.
delete The method of claim 6,
The functional mixed powder is 20-40 parts by weight of the ocher powder, 150-190 parts by weight of the illite powder, 5-7 parts by weight of the tourmaline powder, 4-6 parts by weight of the CMC (carboxymethyl cellulose) powder and the fiber 4 -6 parts by weight of the whole body massage method using a composition for full body massage containing the functional powder mixed, characterized in that the mixture.
The method of claim 8,
The functional mixed powder is 30 parts by weight of the ocher powder, 170 parts by weight of the illite powder, 6 parts by weight of the tourmaline powder, 5 parts by weight of the CMC (carboxymethyl cellulose) powder and 5 parts by weight of the fiber The ocher powder, the illite powder, the tourmaline powder and the CMC (carboxymethyl cellulose) powder all have a 1000 mesh particle size, and the cellulose has a 13 μm length. Whole body massage method using the composition for whole body massage.
The method according to any one of claims 6, 8 and 9,
There is a time interval of 10-20 minutes between the step of forming the second composition layer and the step of forming the silver foil layer, the retention time of 10-20 minutes after the step of forming the silver foil layer. Full-body massage method using a composition for full-body massage containing the functional powder mixed.