KR101200810B1 - Orthodontic Appliance Comprising Bracket and Wire, and Surface Treatment Method Thereof - Google Patents

Orthodontic Appliance Comprising Bracket and Wire, and Surface Treatment Method Thereof Download PDF

Info

Publication number
KR101200810B1
KR101200810B1 KR1020110003889A KR20110003889A KR101200810B1 KR 101200810 B1 KR101200810 B1 KR 101200810B1 KR 1020110003889 A KR1020110003889 A KR 1020110003889A KR 20110003889 A KR20110003889 A KR 20110003889A KR 101200810 B1 KR101200810 B1 KR 101200810B1
Authority
KR
South Korea
Prior art keywords
wire
bracket
rhodium
orthodontic appliance
treatment method
Prior art date
Application number
KR1020110003889A
Other languages
Korean (ko)
Other versions
KR20120082556A (en
Inventor
김영균
이득용
Original Assignee
(주)케라모스
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by (주)케라모스 filed Critical (주)케라모스
Priority to KR1020110003889A priority Critical patent/KR101200810B1/en
Publication of KR20120082556A publication Critical patent/KR20120082556A/en
Application granted granted Critical
Publication of KR101200810B1 publication Critical patent/KR101200810B1/en

Abstract

본 발명은 브래킷과 와이어를 포함하는 치열교정장치 및 그의 표면처리방법에 관한 것으로, 브래킷과 와이어를 포함하는 치열교정장치에 있어서, 상기 브래킷 또는 와이어의 외면에 은도금층을 형성하고 상기 은도금층 외면에 로듐도금층을 형성하여 치아와 비슷한 색상을 유지하게 되므로 사용자가 심리적으로 위축되지 않고, 내구성이 높아 변색과 마모 등이 쉬이 일어나지 않으며, 제조비용이 저렴하여 많은 사람들이 부담없이 치열을 교정할 수 있고, 인체에 무해하므로 어떤 사용자도 편히 사용할 수 있다.The present invention relates to an orthodontic appliance comprising a bracket and a wire, and a method for treating the surface thereof, wherein the orthodontic appliance comprising a bracket and a wire comprises: forming a silver plated layer on an outer surface of the bracket or wire and forming a silver plated layer on the outer surface of the silver plated layer. By forming the rhodium plated layer to maintain the color similar to the teeth, the user does not shrink psychologically, and the durability is high so that discoloration and abrasion does not occur easily, and the manufacturing cost is low, so many people can straighten the orthodontist, It is harmless to human body and can be used by any user.

Description

브래킷과 와이어를 포함하는 치열교정장치 및 그의 표면처리방법{Orthodontic Appliance Comprising Bracket and Wire, and Surface Treatment Method Thereof}Orthodontic Appliance Comprising Bracket and Wire, and Surface Treatment Method Thereof}

본 발명은 브래킷과 와이어를 포함하는 치열교정장치 및 그의 표면처리방법에 관한 것이며, 더욱 상세하게는 인체에 무해한 은도금 및 로듐도금처리하여 내구성을 향상시키고 변색과 마모를 방지하며 제품제조단가를 낮추도록 하는 브래킷과 와이어를 포함하는 치열교정장치 및 그의 표면처리방법에 관한 것이다.The present invention relates to an orthodontic appliance including a bracket and a wire, and a surface treatment method thereof, and more particularly, to silver and rhodium plating, which are harmless to a human body, to improve durability, prevent discoloration and abrasion, and lower product manufacturing costs. It relates to an orthodontic appliance comprising a bracket and a wire and a surface treatment method thereof.

일반적으로 어떤 원인에 의해 치아의 배열이 가지런하지 않거나 위 아래 맞물림의 상태가 정상의 위치를 벗어나서 심미적 또는 기능적으로 문제가 되는 교합관계를 부정교합이라고 하며, 아래위 치아의 맞물림을 좋게 해서 음식물을 골고루 잘 씹게 하고, 정확한 발음을 할 수 있게 하며, 구강 위생 상태도 향상시키기 위한이유와 심미적인 이유 등으로 입과 치아의 역할을 충분히 다할 수 있도록 부정교합을 치료하는 것이다. In general, the occlusal relationship in which teeth are not aligned due to some cause or the state of up and down engagement is out of the normal position and is aesthetic or functional problem is called malocclusion, and the food of the upper and lower teeth is improved evenly. Chemo, correct pronunciation, and oral hygiene to improve the oral hygiene state and aesthetic reasons, such as to treat the malocclusion so as to fulfill the role of the mouth.

부정교합의 치료는 원인이나 치료 시기에 따라 다양한 장치와 방법을 이용한다. 습관을 제거하도록 고안된 장치, 위아래 턱뼈의 발육을 억제하거나 증진시키는 장치, 치아를 원하는 위치로 서서히 이동시키는 장치 등이 있으며, 구강 내에 넣었다 뺐다 할 수 있는 가철성 장치와 치아에 부착한 후 치료가 끝날 때 떼어내는 고정식 장치로도 나눠 볼 수 있다. 각각의 장치는 치료 목적에 따라 단독 혹은 병행해서 사용하게 된다. Treatment of malocclusion uses a variety of devices and methods, depending on the cause and timing of treatment. Devices designed to remove habits, devices that suppress or promote the development of upper and lower jawbones, and devices that slowly move the teeth to the desired position, are removable devices that can be inserted into and removed from the mouth and attached to the teeth at the end of treatment. It can also be divided into fixed units that can be removed. Each device may be used alone or in combination depending on the purpose of treatment.

현재 가장 많이 사용되고 있는 것은 브래킷이라는 장치를 치아에 부착하고 교정용 와이어와 고무줄 등의 탄력을 사용해 치아를 이동시키는 고정식 치료법이며, 어떤 종류의 부정교합에도 흔히 사용된다.At present, the most commonly used is a fixed treatment for attaching a device called a bracket to the teeth and moving the teeth using elastic wires such as orthodontic wires and rubber bands, and is commonly used for any kind of malocclusion.

선행특허 10-0795106에서는 와이어에 은(Ag)을 도금하고 상기 표면에 고분자 화합물 혹은 테프론을 코팅하여 심미성을 구현시키는 방법이 소개되었다.In the prior patent 10-0795106, a method of plating a silver (Ag) on a wire and coating a polymer compound or teflon on the surface to implement aesthetics was introduced.

하지만 상기 선행특허에 사용되는 고분자 화합물은 사용자가 치열교정장치를 장기간 착용시 변색되거나 음식물 섭취시 치열교정장치와의 마찰로 표면이 벗겨지고, 음식물의 색상이 치열교정장치에 스며들며 내구성이 떨어지는 문제점이 있다.However, the polymer compound used in the prior patent has a problem that the user discolors when the user wears the orthodontic device for a long time, or the surface is peeled off by friction with the orthodontic device, and the color of the food penetrates the orthodontic device and the durability is poor. have.

또한 치열교정용 브래킷과 와이어는 일반적으로 금속으로 형성되어 교정치료기간 동안 타인의 눈에 잘 띄는 단점이 있어 사용자는 심리적으로 위축되기 쉽고, 알러지가 유발되거나, 제품의 제조비용이 상당한 문제점이 있다.In addition, orthodontic brackets and wires are generally made of metal, so there is a noticeable disadvantage of others during orthodontic treatment period, so that the user is likely to shrink psychologically, cause allergies, or there is a significant problem in manufacturing cost of the product.

본 발명은 상기한 바와 같은 종래의 문제점을 해결하기 위한 것으로써, 본 발명의 목적은 치열교정용 브래킷과 와이어에 은도금과 로듐도금을 하여 심미성을 갖고 제조비용이 저렴하며 내구성이 뛰어나고 인체에 무해한 치열교정장치 및 그의 표면처리방법을 제공하는 것이다.The present invention is to solve the conventional problems as described above, the object of the present invention is to provide aesthetics by the silver plating and rhodium plating on the orthodontic bracket and wire, low manufacturing cost, excellent durability and harmless to human body It is to provide a calibration apparatus and its surface treatment method.

상기한 바와 같은 본 발명의 목적을 달성하기 위하여, 본 발명에 따른 브래킷과 와이어를 포함하는 치열교정장치에 있어서, 상기 브래킷은 외면에 형성되어 브래킷의 표면산화를 방지하는 은도금층과; 상기 은도금층 외면에 형성되어 변색과 마모를 방지하는 로듐도금층;을 포함하는 것을 특징으로 한다.In order to achieve the object of the present invention as described above, in the orthodontic appliance comprising the bracket and the wire according to the present invention, the bracket is formed on the outer surface to prevent the surface oxidation of the bracket; And a rhodium plating layer formed on the outer surface of the silver plating layer to prevent discoloration and abrasion.

상기한 바와 같은 본 발명의 목적을 달성하기 위하여, 본 발명에 따른 브래킷과 와이어를 포함하는 치열교정장치에 있어서, 상기 와이어는 외면에 형성되어 와이어의 표면산화를 방지하는 은도금층과; 상기 은도금층 외면에 형성되어 변색과 마모를 방지하는 로듐도금층;을 포함하는 것을 특징으로 한다.In order to achieve the object of the present invention as described above, in the orthodontic appliance comprising a bracket and a wire according to the present invention, the wire is formed on the outer surface to prevent the surface oxidation of the wire; And a rhodium plating layer formed on the outer surface of the silver plating layer to prevent discoloration and abrasion.

본 발명에 따른 브래킷과 와이어를 포함하는 치열교정장치에 있어서, 상기 은도금층은 브래킷 또는 와이어에 전류밀도 20㎃/dm2 ~ 35㎃/dm2로 20초 내지 30초 동안 시안화은(AgCN)과 시안화칼륨(KCN)의 혼합물을 도포하는 전해도금으로 형성된 것을 특징으로 한다.In the orthodontic appliance including a bracket and a wire according to the present invention, the silver plated layer has a current density 20㎃ / dm 2 ~ 35㎃ / 20 seconds to 30 seconds sianhwaeun (AgCN) with cyanide for a dm 2 in the bracket or wire It is characterized in that formed by electroplating to apply a mixture of potassium (KCN).

본 발명에 따른 브래킷과 와이어를 포함하는 치열교정장치에 있어서, 상기 로듐도금층은 로듐 1 ~ 2g/ℓ와 96 부피％인 황산 40㎖/ℓ으로 조성된 황산로듐 도금액, 또는 로듐 1 ~ 2g/ℓ와 85 부피％인 인산 60㎖/ℓ으로 조성된 인상로듐 도금액 중 어느 하나에서 형성된 것을 특징으로 한다.In the orthodontic appliance including the bracket and the wire according to the present invention, the rhodium plating layer is a rhodium sulfate plating solution composed of rhodium 1 to 2 g / l and 96 vol% sulfuric acid 40 ml / l, or rhodium 1 to 2 g / l And 85% by volume of an impression rhodium plating solution composed of 60 ml / l phosphoric acid.

본 발명에 따른 브래킷과 와이어를 포함하는 치열교정장치에 있어서, 상기 로듐도금층의 두께는 0.4 ~ 0.5㎛인 것을 특징으로 한다.In the orthodontic appliance including the bracket and the wire according to the present invention, the rhodium plating layer is characterized in that the thickness of 0.4 ~ 0.5㎛.

상기한 바와 같은 본 발명의 목적을 달성하기 위하여, 본 발명에 따른 브래킷과 와이어를 포함하는 치열교정장치의 표면처리방법에 있어서, 상기 브래킷의 표면처리방법은 연마석과 에틸알콜 및 PVA(Polyvinyl Alcohol)를 혼합한 액상을 브래킷에 분사하여 연마하는 연마단계와; 상기 연마된 브래킷을 초음파로 세척하는 제1세척단계; 및 상기 초음파로 세척 후 건조된 브래킷 표면에 0.4 ~ 0.5㎛ 두께로 로듐도금을 하는 로듐도금단계;로 이루어지는 것을 특징으로 한다.In order to achieve the object of the present invention as described above, in the surface treatment method of the orthodontic appliance comprising a bracket and a wire according to the present invention, the surface treatment method of the bracket is abrasive stone, ethyl alcohol and PVA (Polyvinyl Alcohol) Polishing step of polishing by spraying the mixed liquid to the bracket; A first washing step of ultrasonically washing the polished bracket; And a rhodium plating step of rhodium plating to a thickness of 0.4 to 0.5 μm on the surface of the dried bracket after washing with ultrasonic waves.

상기한 바와 같은 본 발명의 목적을 달성하기 위하여, 본 발명에 따른 브래킷과 와이어를 포함하는 치열교정장치의 표면처리방법에 있어서, 상기 와이어의 표면처리방법은 연마석과 에틸알콜 및 PVA(Polyvinyl Alcohol)를 혼합한 액상을 와이어에 분사하여 연마하는 연마단계와; 상기 연마된 와이어를 초음파로 세척하는 제1세척단계; 및 상기 초음파로 세척 후 건조된 와이어 표면에 0.4 ~ 0.5㎛ 두께로 로듐도금을 하는 로듐도금단계;로 이루어지는 것을 특징으로 한다.In order to achieve the object of the present invention as described above, in the surface treatment method of the orthodontic appliance comprising the bracket and the wire according to the present invention, the surface treatment method of the wire is polished stone, ethyl alcohol and PVA (Polyvinyl Alcohol) Polishing step of polishing by spraying the mixed liquid to the wire; A first washing step of ultrasonically washing the polished wire; And a rhodium plating step of plating rhodium with a thickness of 0.4 to 0.5 μm on the dried wire surface after washing with ultrasonic waves.

브래킷과 와이어를 포함하는 치열교정장치의 표면처리방법에 있어서, 상기 제1세척단계와 로듐도금단계 사이에는 상기 초음파로 세척된 브래킷 또는 와이어 표면에 은도금을 하는 은도금단계와; 상기 은도금된 브래킷 또는 와이어를 증류수에 세정 후 건조하는 제2세척단계;를 더 포함하여 이루어지는 것을 특징으로 한다.A surface treatment method of an orthodontic appliance comprising a bracket and a wire, comprising: a silver plating step of silver plating the surface of the ultrasonically cleaned bracket or wire between the first washing step and the rhodium plating step; And a second washing step of washing and then drying the silver plated bracket or wire in distilled water.

브래킷과 와이어를 포함하는 치열교정장치의 표면처리방법에 있어서, 상기 은도금단계에서 은도금은 브래킷과 와이어에 전류밀도 20㎃/dm2 ~ 35㎃/dm2로 20초 내지 30초 동안 시안화은(AgCN)과 시안화칼륨(KCN)의 혼합물을 도포하는 전해도금인 것을 특징으로 한다.In the method for surface treatment of orthodontic appliance including a bracket and a wire, sianhwaeun (AgCN) in the silver plating step the silver plated is a current density 20㎃ / dm 2 ~ 35㎃ / dm 2 to the brackets and wires for 20 seconds to 30 seconds It is characterized in that the electroplating to apply a mixture of potassium cyanide (KCN).

브래킷과 와이어를 포함하는 치열교정장치의 표면처리방법에 있어서, 상기 로듐도금단계이후에는 상기 로듐도금된 와이어를 잔류 응력을 풀어주는 진공열처리 단계를 더 포함하여 이루어지는 것을 특징으로 한다.In the surface treatment method of the orthodontic appliance comprising a bracket and a wire, after the rhodium plating step, characterized in that it further comprises a vacuum heat treatment step of releasing the residual stress of the rhodium plated wire.

브래킷과 와이어를 포함하는 치열교정장치의 표면처리방법에 있어서, 상기 진공열처리 단계에서는 120℃의 10-6㎩에서 3시간 동안 풀림처리를 실시하는 것을 특징으로 하는 특징으로 한다.In the surface treatment method of the orthodontic appliance comprising a bracket and a wire, the vacuum heat treatment step is characterized in that the annealing treatment for 3 hours at 10 -6 kPa of 120 ℃.

브래킷과 와이어를 포함하는 치열교정장치의 표면처리방법에 있어서, 상기 연마단계에서는 연마석 30 중량％와 에틸알콜 70 중량％가 혼합된 액상이 브래킷 또는 와이어에 분사하여 연마되는 것을 특징으로 한다.In the surface treatment method of the orthodontic appliance including the bracket and the wire, the polishing step is characterized in that the liquid mixed with 30% by weight of abrasive stone and 70% by weight of ethyl alcohol is sprayed on the bracket or wire to be polished.

브래킷과 와이어를 포함하는 치열교정장치의 표면처리방법에 있어서, 상기 연마단계에서는 연마석 30 중량％와 에틸알콜 65 중량％ 및 5 중량%의 PVA수용액 5 중량%가 혼합된 액상이 브래킷 또는 와이어에 분사되어 연마되는 것을 특징으로 한다.In the surface treatment method of the orthodontic appliance including the bracket and the wire, in the polishing step, a liquid mixed with 30% by weight of abrasive stone, 65% by weight of ethyl alcohol and 5% by weight of 5% by weight of PVA aqueous solution is sprayed onto the bracket or wire. It is characterized in that the polishing.

브래킷과 와이어를 포함하는 치열교정장치의 표면처리방법에 있어서, 상기 연마단계에서 상기 연마석은 금강사, 탄화규소, 질화규소, 산화알루미늄 중 어느 하나인 것을 특징으로 한다.In the surface treatment method of the orthodontic appliance comprising a bracket and a wire, in the polishing step, the abrasive stone is characterized in that any one of diamond steel, silicon carbide, silicon nitride, aluminum oxide.

브래킷과 와이어를 포함하는 치열교정장치의 표면처리방법에 있어서, 상기 연마단계에서 상기 연마석은 65 ~ 104㎛ 입상인 것을 특징으로 한다.In the surface treatment method of the orthodontic appliance comprising a bracket and a wire, in the polishing step, the abrasive stone is characterized in that the granule of 65 ~ 104㎛.

브래킷과 와이어를 포함하는 치열교정장치의 표면처리방법에 있어서, 상기 로듐도금단계에서는 25 ~ 30℃의 로듐도금액에서 전류밀도 2A/dm2로 2 ~ 10분 동안 브래킷 또는 와이어에 도금되는 것을 특징으로 한다.In the surface treatment method of the orthodontic appliance comprising a bracket and a wire, in the rhodium plating step, the bracket or wire is plated on the bracket or wire for 2 to 10 minutes at a current density of 2A / dm 2 in a rhodium plating solution at 25 to 30 ° C. It is done.

브래킷과 와이어를 포함하는 치열교정장치의 표면처리방법에 있어서, 상기 로듐도금단계에서 로듐도금은 로듐 1 ~ 2g/ℓ와 96 부피％인 황산 40㎖/ℓ으로 조성된 황산로듐 도금액 또는 로듐 1 ~ 2g/ℓ와 85 부피％인 인산 60㎖/ℓ으로 조성된 인상로듐 도금액 중 어느 하나에서 실시되는 것을 특징으로 한다.In the surface treatment method of the orthodontic appliance comprising a bracket and a wire, the rhodium plating in the rhodium plating step is a rhodium sulfate plating solution or rhodium 1 ~ 2 g / l and 96 vol% sulfuric acid 40ml / l It is characterized in that it is carried out in any one of the impression rhodium plating solution composed of 2g / l and 85% by volume of 60ml / l phosphoric acid.

본 발명에 따르면, 치열교정용 와이어와 브래킷에 은도금과 로듐도금을 하므로 치아와 비슷한 색상을 유지하게 되어 사용자가 심리적으로 위축되지 않고, 내구성이 높아 변색과 마모 등이 쉬이 일어나지 않으며, 제조비용이 저렴하여 많은 사람들이 부담없이 치열을 교정할 수 있고, 인체에 무해하므로 어떤 사용자도 편히 사용할 수 있다.According to the present invention, silver plating and rhodium plating are performed on the orthodontic wire and the bracket, so that the color similar to the tooth is maintained, so that the user is not psychologically shrunk, the durability is high, discoloration and wear do not occur easily, and the manufacturing cost is low. Many people feel free to straighten the orthodontic, harmless to the human body, so any user can use comfortably.

도 1은 종래의 브래킷과 와이어를 포함하는 치열교정장치를 나타낸 브래킷과 와이어의 사시도.
도 2는 본 발명의 실시예에 따른 브래킷과 와이어를 포함하는 치열교정장치의 사용상태를 나타낸 측단면도.
도 3은 본 발명의 실시예에 따른 브래킷과 와이어를 포함하는 치열교정장치의 표면처리방법을 나타낸 플로차트.1 is a perspective view of a bracket and wire showing an orthodontic appliance comprising a conventional bracket and wire.
Figure 2 is a side cross-sectional view showing a state of use of the orthodontic appliance comprising a bracket and a wire according to an embodiment of the present invention.
Figure 3 is a flow chart showing a surface treatment method of the orthodontic appliance comprising a bracket and a wire according to an embodiment of the present invention.

이하, 본 발명의 실시예가 첨부된 도면을 참조하여 더욱 상세하게 설명한다.Hereinafter, with reference to the accompanying drawings an embodiment of the present invention will be described in more detail.

도 1은 종래의 브래킷과 와이어를 나타낸 사시도로써, 치열교정장치는 브래킷(10)과 와이어(20)를 포함한다.1 is a perspective view showing a conventional bracket and wire, the orthodontic appliance includes a bracket 10 and a wire 20.

도 2는 본 발명의 실시예에 따른 브래킷과 와이어를 포함하는 치열교정장치의 사용상태를 나타낸 측단면도를 나타낸다.Figure 2 shows a side cross-sectional view showing a state of use of the orthodontic appliance comprising a bracket and a wire according to an embodiment of the present invention.

브래킷과 와이어를 포함하는 치열교정장치에 있어서, 상기 브래킷(10)은, 외면에 형성되어 브래킷(10)의 표면산화를 방지하는 은도금층(11)과 상기 은도금층(11) 외면에 형성되어 변색과 마모를 방지하는 로듐도금층(12)을 포함한다.In the orthodontic appliance comprising a bracket and a wire, the bracket 10 is formed on the outer surface to prevent surface oxidation of the bracket 10 and the silver plating layer 11 formed on the outer surface of the silver plating layer 11 is discolored And a rhodium plated layer 12 for preventing abrasion.

또한 브래킷과 와이어를 포함하는 치열교정장치에 있어서, 상기 와이어(20)는, 외면에 형성되어 와이어(20)의 표면산화를 방지하는 은도금층(21)과 상기 은도금층(21) 외면에 형성되어 변색과 마모를 방지하는 로듐도금층(22)을 포함한다.In the orthodontic appliance including the bracket and the wire, the wire 20 is formed on the outer surface and formed on the outer surface of the silver plating layer 21 and the outer surface of the silver plating layer 21 to prevent surface oxidation of the wire 20. Rhodium plating layer 22 to prevent discoloration and wear.

상기 와이어(20)는 형상기억합금이 사용되어 사용자가 치열교정장치를 착용하였을 때 상기 와이어(20)가 탄성으로 치열을 교정시킨다.The wire 20 is a shape memory alloy used when the user wears the orthodontic device to the wire 20 to elastically correct the teeth.

본 발명에서는 상기 브래킷(10) 또는 와이어(20)의 재질로 Ni-Ti 합금의 사용이 바람직하나 이에 한정하지 않는다.In the present invention, the use of the Ni-Ti alloy is preferable as the material of the bracket 10 or the wire 20, but is not limited thereto.

상기 은도금층(11, 21)은 브래킷(10) 또는 와이어(20) 표면에 형성되어있다.The silver plating layers 11 and 21 are formed on the surface of the bracket 10 or the wire 20.

상기 은도금층(11, 21)은 전해도금으로 형성된 것으로, 상온(바람직하게는 18 ~ 25℃)에서 브래킷(10)과 와이어(20)에 전류밀도 20 ~ 35㎃/dm2(가장 바람직하게는 20㎃/dm2)로 20 ~ 30초(가장 바람직하게는 20초)동안 시안화은(AgCN)과 시안화칼륨(KCN)의 혼합물이 도포되는 것이 바람직하다.The silver plating layers 11 and 21 are formed by electroplating, and the current density is 20 to 35 mA / dm 2 (most preferably at room temperature (preferably 18 to 25 ° C.)) at the bracket 10 and the wire 20. 20 cc / dm 2 ), a mixture of silver cyanide (AgCN) and potassium cyanide (KCN) is preferably applied for 20-30 seconds (most preferably 20 seconds).

상기 로듐도금층(12, 22)을 형성하는데 사용되는 도금액은 로듐 1 ~ 2g/ℓ와 96 부피％인 황산 40㎖/ℓ으로 조성된 황산로듐인 도금액 또는 로듐 1 ~ 2g/ℓ와 85 부피％인 인산 60㎖/ℓ으로 조성된 인상로듐인 도금액 중 어느 하나가 사용됨이 바람직하다.The plating solution used to form the rhodium plated layers 12 and 22 may be rhodium sulfate or rhodium 1 to 2 g / l and 85 vol. It is preferable that any one of the plating liquids which are impression rhodium formed with 60 mL / L phosphoric acid is used.

상기 로듐도금층(12, 22)의 두께는 0.4 ~ 0.5㎛인 것이 바람직하다.The rhodium plating layers 12 and 22 preferably have a thickness of 0.4 to 0.5 µm.

도 3은 본 발명의 실시예에 따른 브래킷과 와이어를 포함한 치열교정장치의 표면처리방법을 나타낸 플로차트이다.3 is a flowchart illustrating a surface treatment method of an orthodontic appliance including a bracket and a wire according to an embodiment of the present invention.

도 3을 참조하면 상기 브래킷의 표면처리방법은 연마단계(S10)와, 제1세척단계(S20) 및 로듐도금단계(S30)로 이루어지며 상기 제1세척단계(S20)와 로듐도금단계(S30) 사이에 은도금단계(S22)와 제2세척단계(S24)가 포함될 수 있다.Referring to FIG. 3, the surface treatment method of the bracket includes a polishing step S10, a first washing step S20, and a rhodium plating step S30, and the first washing step S20 and rhodium plating step S30. ) May include a silver plating step (S22) and the second washing step (S24).

또한 상기 와이어(20)의 표면처리방법은 연마단계(S10)와, 제1세척단계(S20) 및 로듐도금단계(S30)로 이루어지며 상기 제1세척단계(S20)와 로듐도금단계(S30) 사이에 은도금단계(S22)와 제2세척단계(S24)가 포함될 수 있다.In addition, the surface treatment method of the wire 20 is composed of a polishing step (S10), a first washing step (S20) and a rhodium plating step (S30) and the first washing step (S20) and rhodium plating step (S30). The silver plating step (S22) and the second washing step (S24) may be included between.

상기 브래킷(10) 또는 와이어(20)의 연마단계(S10)는 연마석과 에틸알콜 및 PVA(Polyvinyl Alcohol)를 혼합하여 제조한 액상을 브래킷(10) 또는 와이어(20)에 분사하여 연마한다.In the polishing step S10 of the bracket 10 or the wire 20, the liquid prepared by mixing the abrasive stone with ethyl alcohol and PVA (Polyvinyl Alcohol) is sprayed onto the bracket 10 or the wire 20 to polish.

상기 연마단계(S10)에서 사용되는 혼합액상은 연마석 30 중량％와 에틸알콜 70 중량％가 혼합된 액상, 또는 연마석 30 중량％와 에틸알콜 65 중량％ 및 5 중량％의 PVA수용액 5 중량％가 혼합된 액상이 사용될 수 있다.The mixed liquid phase used in the polishing step (S10) is a liquid in which 30% by weight of abrasive stone and 70% by weight of ethyl alcohol are mixed, or 30% by weight of abrasive stone and 65% by weight of ethyl alcohol and 5% by weight of 5% by weight of PVA aqueous solution are mixed. Liquid phase can be used.

또한 상기 연마단계(S10)에서 연마석은 금강사, 탄화규소, 질화규소, 산화알루미늄 중 어느 하나가 사용됨이 바람직하나 이에 한정하지 않고 그 외 재질의 연마석을 사용하는 것도 가능하다.In addition, the polishing stone in the polishing step (S10) is preferably any one of gold steel, silicon carbide, silicon nitride, aluminum oxide, but is not limited to this, it is also possible to use a polished stone of other materials.

상기 연마단계(S10)에서 상기 연마석은 65 ~ 104㎛ 입상인 것이 바람직하다.In the polishing step (S10), the abrasive stone is preferably 65 ~ 104㎛ granular.

상기 연마단계(S10)에서는 상기 혼합액상을 2 ~ 5㎏/㎠의 압력으로 상기 브래킷(10) 또는 와이어(20)와 30㎝의 거리만큼 떨어진 상태에서 10 ~ 20초(가장 바람직하게는 브래킷(10)에는 20초, 와이어(20)에는 10초) 동안 공기와 함께 분사하는 것이 바람직하다.In the polishing step (S10) is 10 to 20 seconds (most preferably the bracket (a) in the state separated from the bracket 10 or the wire 20 by a distance of 30 cm at a pressure of 2 ~ 5㎏ / ㎠ 10) for 20 seconds, the wire 20 is preferably sprayed with air for 10 seconds).

상기 혼합액상을 분사하는 압력으로는 브래킷(10)에는 5㎏/㎠가, 와이어(20)에는 3㎏/㎠의 압력이 가장 바람직하다.The pressure for spraying the mixed liquid phase is most preferably 5 kg / cm 2 for the bracket 10 and 3 kg / cm 2 for the wire 20.

또한 상기 혼합액상을 상기 와이어(20)에 분사함에 있어 일정간격 요철이 형성되도록 한다.In addition, the spraying the mixed liquid phase to the wire 20 to form a predetermined interval irregularities.

상기 와이어(20)는 Ni-Ti 합금으로 제작하는 것이 바람직하지만 이에 한정하지는 않는다.The wire 20 is preferably made of Ni-Ti alloy, but is not limited thereto.

상기 Ni-Ti 합금은 형상기억효과와 초탄성효과로 인해 상변환이 일어나므로 물리적인 샌딩으로 표면 개질을 할 경우 와이어의 특성이 변하기 때문에, 본 발명에서는 이러한 연마석 입자를 에틸알콜과 혼합하여 2 ~ 5㎏/㎠의 압력으로 공기와 함께 와이어 표면에 분사한다.Since the Ni-Ti alloy has phase transformation due to shape memory effect and superelastic effect, the surface properties are changed when the surface is modified by physical sanding, so that the abrasive grains are mixed with ethyl alcohol in the present invention. Spray to the wire surface with air at a pressure of 5 kg / ㎠.

상기 제1세척단계(S20)에서는 상기 연마된 브래킷(10) 또는 와이어(20)를 초음파로 세척한다.In the first washing step S20, the polished bracket 10 or the wire 20 is cleaned by ultrasonic waves.

상기 은도금단계(S22)에서는 상기 초음파로 세척된 상기 브래킷(10) 또는 와이어(20)의 표면산화를 방지하기 위해 브래킷(10) 또는 와이어(20) 표면에 은도금을 한다.In the silver plating step (S22) to the surface of the bracket 10 or the wire 20 to prevent the surface oxidation of the bracket 10 or the wire 20 cleaned by the ultrasonic wave.

상기 은도금단계(S22)에서 은도금은 전해도금으로, 상온(바람직하게는 18 ~ 25℃)에서 브래킷(10)과 와이어(20)에 전류밀도 20 ~ 35㎃/dm2(가장 바람직하게는 20㎃/dm2)로 20 ~ 30초(가장 바람직하게는 20초)동안 시안화은(AgCN)과 시안화칼륨(KCN)의 혼합물을 도포하는 것이 바람직하다.In the silver plating step (S22), the silver plating is an electroplating, current density of 20 ~ 35 ㎃ / dm 2 (most preferably 20 ㎃) to the bracket 10 and the wire 20 at room temperature (preferably 18 ~ 25 ℃) / dm 2 ), it is preferred to apply a mixture of silver cyanide (AgCN) and potassium cyanide (KCN) for 20 to 30 seconds (most preferably 20 seconds).

상기 제2세척단계(S24)에서는 상기 은도금된 브래킷(10) 또는 와이어(20)를 증류수에 세정 후 건조한다.In the second washing step S24, the silver plated bracket 10 or the wire 20 is washed with distilled water and dried.

상기 로듐도금단계(S30)에서는 상기 초음파로 세척 후 건조된 브래킷(10) 또는 와이어(20) 표면에 0.4 ~ 0.5㎛ 두께로 로듐도금을 한다.In the rhodium plating step (S30) is rhodium plating to a thickness of 0.4 ~ 0.5㎛ on the surface of the bracket 10 or the wire 20 dried after the ultrasonic cleaning.

상기 로듐도금단계(S30)에서 로듐도금은 로듐 1 ~ 2g/ℓ와 96 부피％인 황산 40㎖/ℓ으로 조성된 황산로듐인 도금액이 사용될 수 있고, 또는 로듐 1 ~ 2g/ℓ와 85 부피％인 인산 60㎖/ℓ으로 조성된 인상로듐인 도금액에서 실시될 수 있다.In the rhodium plating step (S30), rhodium plating may be used a plating solution of rhodium sulfate composed of rhodium 1 to 2 g / l and 96 vol% sulfuric acid 40 ml / l, or rhodium 1 to 2 g / l and 85 vol% It can be carried out in a plating solution of impression rhodium phosphorus composed of 60 mL / L phosphoric acid.

상기 로듐도금단계(S30)에서는 25 ~ 30℃의 로듐도금액에서 전류밀도 2A/dm2로 2 ~ 10분(가장 바람직하게는 10분)동안 브래킷(10) 또는 와이어(20)에 도금된다.In the rhodium plating step (S30) is plated on the bracket 10 or the wire 20 for 2 to 10 minutes (most preferably 10 minutes) at a current density of 2A / dm 2 in a rhodium plating solution of 25 ~ 30 ℃.

상기 로듐도금단계(S30) 이후 상기 로듐도금된 와이어(20)를 잔류 응력을 풀어주는 진공열처리 단계(S40)를 포함하여 이루어진다.After the rhodium plating step (S30) comprises a vacuum heat treatment step (S40) for releasing the residual stress of the rhodium plated wire (20).

상기 진공열처리 단계(S40)에서는 120℃의 10-6㎩에서 3시간 동안 풀림처리를 실시하는 것이 바람직하다.In the vacuum heat treatment step (S40) it is preferable to perform the annealing treatment for 3 hours at 10 -6 kPa of 120 ℃.

본 발명에 따른 브래킷, 와이어(20) 및 그의 표면처리방법는 다음과 같이 제작?사용된다.The bracket, the wire 20 and the surface treatment method according to the present invention are manufactured and used as follows.

먼저 Ni-Ti합금으로 형성된 브래킷(10)과 와이어(20)를 65 ~ 104㎛ 입상인 연마석 30 중량％와 에틸알콜 70 중량％가 혼합된 액상, 또는 65 ~ 104㎛ 입상인 연마석 30 중량％와 에틸알콜 65 중량％ 및 5 중량％의 PVA수용액 5 중량％가 혼합된 액상으로 연마한다.First, the bracket 10 and the wire 20 formed of a Ni-Ti alloy were mixed with 30 wt% of abrasive grains having a granularity of 65 to 104 μm and 30 wt% of abrasive grains of 65 to 104 μm granules and 70 wt% of ethyl alcohol. Grind to a mixed liquid of 65% by weight ethyl alcohol and 5% by weight aqueous PVA solution.

상기 연마석은 금강사, 탄화규소, 질화규소, 산화알루미늄 중 어느 하나가 사용됨이 바람직하나 그 외 재질의 연마석을 사용하는 것도 가능하다.As the abrasive stone, any one of gold steel, silicon carbide, silicon nitride, and aluminum oxide is preferably used, but it is also possible to use abrasive stone of other materials.

상기 브래킷(10)을 연마할 때는 혼합액상을 5㎏/㎠의 압력으로 분사하고, 상기 와이어(20)를 연마할 때는 혼합액상을 3㎏/㎠의 압력으로 분사한다.When the bracket 10 is polished, the mixed liquid phase is sprayed at a pressure of 5 kg / cm 2, and when the wire 20 is polished, the mixed liquid phase is sprayed at a pressure of 3 kg / cm 2.

상기 혼합액상을 2 ~ 5㎏/㎠의 압력으로 상기 브래킷(10) 또는 와이어(20)와 30㎝의 거리만큼 떨어진 상태에서 10 ~ 20초(가장 바람직하게는 브래킷(10)에는 20초, 와이어(20)에는 10초) 동안 공기와 함께 분사하는 것이 바람직하다.10 to 20 seconds (most preferably 20 seconds to the bracket 10) in a state in which the mixed liquid phase is separated from the bracket 10 or the wire 20 by a distance of 30 cm at a pressure of 2 to 5 kg / cm 2. 20 is preferably sprayed with air for 10 seconds).

상기 혼합액상을 분사하면서 상기 와이어(20)의 표면에 일부 요철이 형성되도록 연마한다.While spraying the mixed liquid phase, the surface of the wire 20 is polished to form some irregularities.

상기 요철은 빛의 난반사를 일으켜 광택을 줄임으로써 사용자의 심리적인 위축감을 덜어주어 타인의 눈에 덜 띄도록 하고, 또한 비표면적을 넓혀 도금과정에서 도금층의 형성이 쉽도록 한다.The irregularities cause diffuse reflection of light to reduce gloss, thereby reducing the psychological atrophy of the user, making it less noticeable to others, and widening the specific surface area to facilitate the formation of a plating layer in the plating process.

다음으로 상기 연마된 브래킷(10) 또는 와이어(20)를 초음파로 세척한다.Next, the polished bracket 10 or the wire 20 is cleaned ultrasonically.

그리고 상기 초음파로 세척된 브래킷(10) 또는 와이어(20) 표면에 은도금을 한다.Then, silver plating is performed on the surface of the ultrasonically cleaned bracket 10 or wire 20.

상기 은도금은 상기 브래킷(10) 또는 와이어(20)의 표면이 산화되는 것을 방지한다.The silver plating prevents the surface of the bracket 10 or the wire 20 from being oxidized.

상기 은도금은 전해도금으로, 18 ~ 25℃에서 브래킷(10)과 와이어(20)에 전류밀도 20㎃/dm2로 20초동안 시안화은(AgCN)과 시안화칼륨(KCN)의 혼합물을 도포한다.The silver plating is electroplating, and a mixture of silver cyanide (AgCN) and potassium cyanide (KCN) is applied to the bracket 10 and the wire 20 at a current density of 20 mA / dm 2 for 20 seconds at 18 to 25 ° C.

상기 시안화은은 이온의 공급원으로 작용하고, 시안화칼륨은 금속의 착이온을 만드는데 이용되며, 상기 혼합물은 전류밀도를 높여서 도금이 가능하므로 도금속도를 향상시키는 역할을 한다.The silver cyanide acts as a source of silver ions, and potassium cyanide is used to make a complex ion of the metal, and the mixture serves to improve the plating speed since plating is possible by increasing the current density.

그 후 상기 은도금된 브래킷(10) 또는 와이어(20)를 증류수에 세정 후 건조한다.Thereafter, the silver plated bracket 10 or the wire 20 is washed with distilled water and dried.

상기 증류수로 세정 후 건조된 브래킷(10) 또는 와이어(20) 표면에 0.4 ~ 0.5㎛ 두께로 로듐도금을 한다.After rinsing with distilled water, rhodium is plated to a thickness of 0.4 to 0.5 μm on the surface of the dried bracket 10 or wire 20.

상기 로듐도금에는 황산로듐 도금액과 인산로듐 도금액이 사용되며, 황산로듐도금은 로듐 1 ~ 2g/ℓ와 96 부피％인 황산 40㎖/ℓ으로 조성된 도금액을 사용하고, 인산로듐도금은 로듐 1 ~ 2g/ℓ와 85 부피％인 인산 60㎖/ℓ으로 조성된 도금액을 사용한다.A rhodium sulfate plating solution and a rhodium phosphate plating solution are used for the rhodium plating, and a rhodium sulfate plating solution uses a plating solution composed of rhodium 1 to 2 g / l and 96 ml of sulfuric acid 40 ml / l, and rhodium phosphate plating to rhodium 1 to A plating solution composed of 2 g / l and 60 ml / l phosphoric acid at 85% by volume is used.

상기 로듐도금은 내구성이 뛰어나고 마모에 강하므로 상기 브래킷(10) 또는 와이어(20)의 변색과 마모를 방지하며, 치아색깔과 큰 차이가 없도록 실시되어 사용자의 심리적인 위축감을 덜어줄 수 있다.The rhodium plating is excellent in durability and resistant to abrasion, thereby preventing discoloration and abrasion of the bracket 10 or the wire 20, and being performed so as not to be significantly different from the color of the tooth, thereby reducing the psychological atrophy of the user.

또한 25 ~ 30℃의 황산로듐과 인산로듐의 도금액에서 전류밀도 2A/dm2로 10분 동안 브래킷(10) 또는 와이어(20)에 도금한다.In addition, the plate 10 or the wire 20 is plated for 10 minutes at a current density of 2 A / dm 2 in a plating solution of rhodium sulfate and rhodium phosphate at 25 to 30 ° C.

상기 로듐도금된 와이어(20)는 120℃의 10-6㎩에서 3시간 동안 풀림처리를 실시하는 진공열처리를 거치도록 한다.The rhodium plated wire 20 is subjected to a vacuum heat treatment for performing an annealing treatment for 3 hours at 10 -6 kPa of 120 ° C.

상기 진공열처리는 상기 와이어(20)의 잔류 응력을 풀어주는 효과가 있다.The vacuum heat treatment has an effect of releasing residual stress of the wire 20.

이상에서 설명한 바와 같이 본 발명에 따른 브래킷과 와이어를 포함하는 치열교정장치 및 그의 표면처리방법은 실시예에 불과한 것으로서, 본 발명은 상기한 실시예에 한정되지 않고, 이하 특허청구범위에서 청구하는 본 발명의 요지를 벗어남이 없이 본 발명이 속하는 분야에서 통상의 지식을 가진 자라면 누구든지 다양하게 변경하여 실시할 수 있는 범위까지 본 발명의 기술적 정신이 있다고 할 것이다.As described above, the orthodontic appliance including the bracket and the wire according to the present invention and its surface treatment method are just examples, and the present invention is not limited to the above-described embodiment, but the present invention claims in the following claims. Without departing from the gist of the invention, those skilled in the art to which the present invention pertains to the technical spirit of the present invention to the extent that can be changed in various ways.

10 : 브래킷 20 : 와이어
11, 21 : 은도금층 12, 22 : 로듐도금층
S10: 연마단계 S20: 제1세척단계
S22: 은도금단계 S24: 제2세척단계
S30: 로듐도금단계 S40: 진공열처리단계10: bracket 20: wire
11, 21: silver plating layer 12, 22: rhodium plating layer
S10: polishing step S20: first washing step
S22: silver plating step S24: second washing step
S30: rhodium plating step S40: vacuum heat treatment step

Claims (17)

브래킷과 와이어를 포함하는 치열교정장치에 있어서, 상기 브래킷은
외면에 형성되어 브래킷(10)의 표면산화를 방지하는 은도금층(11)과;
상기 은도금층(11) 외면에 형성되어 변색과 마모를 방지하는 로듐도금층(12);
을 포함하며,
상기 은도금층(11, 21)은 브래킷(10) 또는 와이어(20)에 전류밀도 20㎃/dm2 ~ 35㎃/dm2로 20초 내지 30초 동안 시안화은(AgCN)과 시안화칼륨(KCN)의 혼합물을 도포하는 전해도금으로 형성된 것을 특징으로 하는 치열교정장치.In an orthodontic appliance comprising a bracket and a wire, the bracket
A silver plating layer 11 formed on an outer surface to prevent surface oxidation of the bracket 10;
A rhodium plating layer 12 formed on an outer surface of the silver plating layer 11 to prevent discoloration and abrasion;
/ RTI >
The silver plating layers 11 and 21 may be formed of silver cyanide (AgCN) and potassium cyanide (KCN) for 20 seconds to 30 seconds at a current density of 20 mA / dm 2 to 35 mA / dm 2 on the bracket 10 or the wire 20. Orthodontic device characterized in that formed by electroplating to apply the mixture. 브래킷과 와이어를 포함하는 치열교정장치에 있어서, 상기 와이어는,
외면에 형성되어 와이어(20)의 표면산화를 방지하는 은도금층(21)과;
상기 은도금층(21) 외면에 형성되어 변색과 마모를 방지하는 로듐도금층(22);
을 포함하며,
상기 은도금층(11, 21)은 브래킷(10) 또는 와이어(20)에 전류밀도 20㎃/dm2 ~ 35㎃/dm2로 20초 내지 30초 동안 시안화은(AgCN)과 시안화칼륨(KCN)의 혼합물을 도포하는 전해도금으로 형성된 것을 특징으로 하는 치열교정장치.In the orthodontic appliance comprising a bracket and a wire, the wire,
A silver plating layer 21 formed on an outer surface to prevent surface oxidation of the wire 20;
A rhodium plating layer 22 formed on an outer surface of the silver plating layer 21 to prevent discoloration and abrasion;
/ RTI >
The silver plating layers 11 and 21 may be formed of silver cyanide (AgCN) and potassium cyanide (KCN) for 20 seconds to 30 seconds at a current density of 20 mA / dm 2 to 35 mA / dm 2 on the bracket 10 or the wire 20. Orthodontic device characterized in that formed by electroplating to apply the mixture. 삭제delete 제 1 항 또는 제 2 항에 있어서, 상기 로듐도금층(12, 22)은 로듐 1 ~ 2g/ℓ와 96 부피％인 황산 40㎖/ℓ으로 조성된 황산로듐 도금액, 또는 로듐 1 ~ 2g/ℓ와 85 부피％인 인산 60㎖/ℓ으로 조성된 인상로듐 도금액 중 어느 하나에서 형성된 것을 특징으로 하는 치열교정장치.The rhodium plating layer (12, 22) according to claim 1 or 2, wherein the rhodium plating layer (12, 22) is a rhodium sulfate plating solution composed of rhodium sulfate 1 ~ 2g / l and 96% of sulfuric acid 40ml / l, or rhodium 1 ~ 2g / l and An orthodontic appliance, characterized in that formed in any one of the impression rhodium plating solution composed of 60 vol / l phosphoric acid of 85% by volume. 제 1 항 또는 제 2 항에 있어서, 상기 로듐도금층(12, 22)의 두께는 0.4 ~ 0.5㎛인 것을 특징으로 하는 치열교정장치.The orthodontic appliance according to claim 1 or 2, wherein the rhodium plated layers (12, 22) have a thickness of 0.4 to 0.5 mu m. 브래킷과 와이어를 포함하는 치열교정장치의 표면처리방법에 있어서, 상기 브래킷의 표면처리방법은
연마석과 에틸알콜 및 PVA(Polyvinyl Alcohol)를 혼합한 액상을 브래킷(10)에 분사하여 연마하는 연마단계(S10)와;
상기 연마된 브래킷(10)을 초음파로 세척하는 제1세척단계(S20); 및
상기 초음파로 세척 후 건조된 브래킷(10) 표면에 0.4 ~ 0.5㎛ 두께로 로듐도금을 하는 로듐도금단계(S30);
로 이루어지는 것을 특징으로 하는 치열교정장치의 표면처리방법.In the surface treatment method of the orthodontic appliance comprising a bracket and a wire, the surface treatment method of the bracket
A polishing step (S10) of polishing by spraying a liquid mixture of abrasive stone, ethyl alcohol and polyvinyl alcohol (PVA) onto the bracket 10;
A first washing step (S20) of washing the polished bracket 10 with ultrasonic waves; And
Rhodium plating step (S30) for rhodium plating to a thickness of 0.4 ~ 0.5㎛ on the surface of the bracket 10 dried after washing with ultrasonic;
Surface treatment method of the orthodontic appliance, characterized in that consisting of. 브래킷과 와이어를 포함하는 치열교정장치의 표면처리방법에 있어서, 상기 와이어의 표면처리방법은
연마석과 에틸알콜 및 PVA(Polyvinyl Alcohol)를 혼합한 액상을 와이어(20)에 분사하여 연마하는 연마단계(S10)와;
상기 연마된 와이어(20)를 초음파로 세척하는 제1세척단계(S20); 및
상기 초음파로 세척 후 건조된 와이어(20) 표면에 0.4 ~ 0.5㎛ 두께로 로듐도금을 하는 로듐도금단계(S30);
로 이루어지는 것을 특징으로 하는 치열교정장치의 표면처리방법.In the surface treatment method of the orthodontic appliance comprising a bracket and a wire, the surface treatment method of the wire
A polishing step (S10) of polishing by spraying a liquid mixture of abrasive stone, ethyl alcohol and polyvinyl alcohol (PVA) onto the wire 20;
A first washing step (S20) of washing the polished wire 20 by ultrasonic waves; And
Rhodium plating step (S30) for rhodium plating to a thickness of 0.4 ~ 0.5㎛ on the surface of the dried wire 20 after washing with ultrasonic waves;
Surface treatment method of the orthodontic appliance, characterized in that consisting of. 제 6 항 또는 제 7 항에 있어서, 상기 제1세척단계(S20)와 로듐도금단계(S50) 사이에는
상기 초음파로 세척된 브래킷(10) 또는 와이어(20) 표면에 은도금을 하는 은도금단계(S22)와;
상기 은도금된 브래킷(10) 또는 와이어(20)를 증류수에 세정 후 건조하는 제2세척단계(S24);
를 더 포함하여 이루어지는 것을 특징으로 하는 치열교정장치의 표면처리방법.The method of claim 6 or 7, wherein the first washing step (S20) and rhodium plating step (S50) between
A silver plating step (S22) for silver plating the surface of the bracket 10 or the wire 20 cleaned by ultrasonic waves;
A second washing step (S24) of washing and drying the silver plated bracket 10 or wire 20 in distilled water;
Surface treatment method of the orthodontic appliance characterized in that it further comprises. 제 8 항에 있어서, 상기 은도금단계(S22)에서 은도금은 브래킷(10)과 와이어(20)에 전류밀도 20㎃/dm2 ~ 35㎃/dm2로 20초 내지 30초 동안 시안화은(AgCN)과 시안화칼륨(KCN)의 혼합물을 도포하는 전해도금인 것을 특징으로 하는 치열교정장치의 표면처리방법.10. The method of claim 8, wherein in said silver plating step (S22) is silver-plated bracket 10 and the wire 20 to the current density 20㎃ / dm 2 ~ 35㎃ / dm 2 to 20 seconds to 30 seconds sianhwaeun (AgCN), and for A surface treatment method of an orthodontic appliance characterized in that it is electroplating to apply a mixture of potassium cyanide (KCN). 제 7 항에 있어서, 상기 로듐도금단계(S30)이후에는
상기 로듐도금된 와이어(20)를 잔류 응력을 풀어주는 진공열처리 단계(S40)를 더 포함하여 이루어지는 것을 특징으로 하는 치열교정장치의 표면처리방법.According to claim 7, After the rhodium plating step (S30)
And a vacuum heat treatment step (S40) of releasing the residual stress in the rhodium plated wire (20). 제 10 항에 있어서, 상기 진공열처리 단계(S40)에서는 120℃의 10-6㎩에서 3시간 동안 풀림처리를 실시하는 것을 특징으로 하는 치열교정장치의 표면처리방법.The surface treatment method of the orthodontic appliance according to claim 10, wherein in the vacuum heat treatment step (S40), an annealing treatment is performed at 10 -6 kPa for 120 hours. 제 6 항 또는 제 7 항에 있어서, 상기 연마단계(S10)에서는 연마석 30 중량％와 에틸알콜 70 중량％가 혼합된 액상이 브래킷(10) 또는 와이어(20)에 분사하여 연마되는 것을 특징으로 하는 치열교정장치의 표면처리방법.According to claim 6 or 7, wherein in the polishing step (S10) is characterized in that the liquid mixed with 30% by weight of abrasive stone and 70% by weight of ethyl alcohol is sprayed on the bracket 10 or the wire 20 to be polished. Surface treatment method of orthodontic appliance. 제 6 항 또는 제 7 항에 있어서, 상기 연마단계(S10)에서는 연마석 30 중량％와 에틸알콜 65 중량％ 및 5 중량%의 PVA수용액 5 중량%가 혼합된 액상이 브래킷(10) 또는 와이어(20)에 분사되어 연마되는 것을 특징으로 하는 치열교정장치의 표면처리방법.According to claim 6 or 7, wherein the polishing step (S10) is a liquid mixed with 30% by weight of abrasive stone, 65% by weight of ethyl alcohol and 5% by weight of 5% by weight of PVA aqueous solution bracket 10 or wire (20) The surface treatment method of the orthodontic appliance characterized in that the sprayed on). 제 6 항 또는 제 7 항에 있어서, 상기 연마단계(S10)에서 상기 연마석은 금강사, 탄화규소, 질화규소, 산화알루미늄 중 어느 하나인 것을 특징으로 하는 치열교정장치의 표면처리방법.The surface treatment method of an orthodontic appliance according to claim 6 or 7, wherein the abrasive stone is any one of gold steel, silicon carbide, silicon nitride, and aluminum oxide in the polishing step (S10). 제 6 항 또는 제 7 항에 있어서, 상기 연마단계(S10)에서 상기 연마석은 65 ~ 104㎛ 입상인 것을 특징으로 하는 치열교정장치의 표면처리방법.8. The surface treatment method of the orthodontic appliance according to claim 6 or 7, wherein the polishing stone is in the form of 65 to 104 µm in the polishing step (S10). 제 6 항 또는 제 7 항에 있어서, 상기 로듐도금단계(S30)에서는 25 ~ 30℃의 로듐도금액에서 전류밀도 2A/dm2로 2 ~ 10분 동안 브래킷(10) 또는 와이어(20)에 도금되는 것을 특징으로 하는 치열교정장치의 표면처리방법.According to claim 6 or 7, in the rhodium plating step (S30) is plated on the bracket 10 or the wire 20 for 2 to 10 minutes at a current density of 2A / dm 2 in a rhodium plating solution of 25 ~ 30 ℃ Surface treatment method of orthodontic appliance characterized in that. 제 6 항 또는 제 7 항에 있어서, 상기 로듐도금단계(S30)에서 로듐도금은 로듐 1 ~ 2g/ℓ와 96 부피％인 황산 40㎖/ℓ으로 조성된 황산로듐 도금액 또는 로듐 1 ~ 2g/ℓ와 85 부피％인 인산 60㎖/ℓ으로 조성된 인상로듐 도금액 중 어느 하나에서 실시되는 것을 특징으로 하는 치열교정장치의 표면처리방법.According to claim 6 or 7, wherein the rhodium plating in the rhodium plating step (S30) is a rhodium sulfate plating solution or rhodium 1 ~ 2g / L composed of rhodium 1 ~ 2g / L and 96mL of sulfuric acid 40mL / L And 85% by volume of an impression rhodium plating solution composed of 60 ml / l phosphoric acid.
KR1020110003889A 2011-01-14 2011-01-14 Orthodontic Appliance Comprising Bracket and Wire, and Surface Treatment Method Thereof KR101200810B1 (en)