CN107740103A - A kind of method for activating surface of tooth implant - Google Patents
A kind of method for activating surface of tooth implant Download PDFInfo
- Publication number
- CN107740103A CN107740103A CN201711041973.XA CN201711041973A CN107740103A CN 107740103 A CN107740103 A CN 107740103A CN 201711041973 A CN201711041973 A CN 201711041973A CN 107740103 A CN107740103 A CN 107740103A
- Authority
- CN
- China
- Prior art keywords
- tooth implant
- cleaned
- implant
- ultrasonic
- tooth
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
A kind of method for activating surface of tooth implant disclosed by the invention, tooth implant is cleaned, sandblasting, acid treatment, clean again after, dental implant surface forms bioactivity, porous structure.Present invention hydrochloric acid and sulfuric acid mixing acid treatment, it make use of corrosiveness of the mixed acid to titanium, there is provided good sandblasting dental implant surface pattern so that the characteristic of good rough surface is presented in tooth implant, further improves the interface bond strength of tooth implant bone junction.50%~75% sulfuric acid and 8%~20% concentration of hydrochloric acid proportioning acid etching effect are preferable, the acid etching step more than twice for making currently generally to use is reduced to once can just achieve the goal, and shortens processing time, improves operating efficiency, cost is reduced so as to fit in commercially producing.
Description
Technical field
The invention belongs to dentistry technical field, is related to a kind of method for activating surface of tooth implant.
Background technology
Oral implantology grows up from eighties of last century five, the sixties, popularizes very much abroad, and is sent out in China
Exhibition is horizontal relatively low.Dentistry plantation is that a plantation nail is planted at the position of patient's agomphosis, then installs corona, equivalent to growing
One new tooth, convenience attractive in appearance, is comfortable on.Will not be as installation fixed denture abrasion healthy tooth, it is not required that activity justice
The hook of tooth and the auxiliary of denture fixing device.Domestic dentistry implant market is monopolized by foreign countries substantially, and price is high.And restrict state
One key factor of production tooth implant development is exactly the process of surface treatment of planting body.Surface treatment work for tooth implant
Skill, people attempted a variety of methods, such as polishing, spraying hydroxyapatite, spraying titanium slurry etc..After in planting body implantation tooth
Be brought into close contact with dentale, Gegenbaur's cell still in chemotactic, therefore people have generally received to be processed into mat surface in implant surface, from
And planting body and synosteosis are more beneficial for certain chemotactic space to Gegenbaur's cell.It is threaded with the development of dentistry implantology
Rough surface structure planting body be more beneficial for synosteosis turn into dentistry plantation circle common recognition.Wherein with Nobled's
TUniteTM (the porous titanium oxide structure of differential arc oxidation processing) and ITI (bulky grain sandblasting-two level nest hole knot caused by acid etching
Structure) it is most representative.The surface of planting body is modified the focus for also turning into studies in China, it is desirable to improves planting body by being surface-treated
Surface bioactive, with accelerometer facial bone sedimentation rate and form firm chemical bonding.But they have technical process
Complexity, production cycle length, cost is high, the deficiencies of bioactivity difference.Experiment is much also rested on to current, domestic handling process
The room stage.
The content of the invention
It is an object of the invention to provide a kind of method for activating surface of tooth implant, solves existing dental implant surface
The problem of bioactivity difference.
The technical solution adopted in the present invention is a kind of method for activating surface of tooth implant, tooth implant is carried out clear
Wash, sandblasting, acid treatment, clean again after, dental implant surface forms bioactivity, porous structure.
The features of the present invention also resides in,
Specifically include following steps:
Step 1, tooth implant is cleaned by ultrasonic oil removing;
Step 2, blasting treatment is carried out to the dental implant surface obtained through step 1 with bulky grain diamond dust, form micron
The big pit of level, then tooth implant is sequentially placed into acetone, 75% ethanol and distilled water and is cleaned by ultrasonic, dry;
Step 3, by through the tooth implant that step 2 obtains 0.09mol/L~0.13mol/L HF and 0.07mol/L~
0.11mol/L HNO3Mixed liquor processing 5min~15min of formation, distilled water are rinsed, dried, and surface is formed submicron order
Small rut;
Step 4, the tooth implant obtained through step 4 rinsed by purified water successively, 5%NaHCO3 solution ultrasound it is clear
Wash, purified water is rinsed, Micro90 degreasers are cleaned by ultrasonic, running water rinses, purified water is rinsed, water for injection is rinsed and given birth to
The tooth implant of the active porous structure of thing.
Oil removal process is cleaned in step 1 to be included:Respectively it is cleaned by ultrasonic 2 times using acetone, absolute ethyl alcohol, purified water, every time
4min~10min.
In step 2:Pressure during blasting treatment is 0.4MPa;A diameter of 10 μm~30 μm of big pit.
In step 3:A diameter of 0.2 μm~0.7 μm of small rut.
In step 4:5%NaHCO3 solution is cleaned by ultrasonic 2 times, and each time is 5min~10min.
Tooth implant is cylindricality or the threaded pure titanium implant of taper.
The device have the advantages that it is:
(1) method for activating surface of the invention, present invention hydrochloric acid and sulfuric acid mixing acid treatment, make use of mixed acid to titanium
Corrosion of metal acts on, there is provided good sandblasting dental implant surface pattern so that good rough surface is presented in tooth implant
Characteristic, further improve tooth implant bone junction interface bond strength.50%~75% sulfuric acid and 8%~20% salt
Acid concentration proportioning acid etching effect is preferable, and the acid etching step more than twice for making currently generally to use is reduced to once with regard to that can reach mesh
, shorten processing time, improve operating efficiency, reduce cost so as to fit in commercially producing;
(2) method for activating surface of the invention, without additional coating, avoiding introducing foreign substance, there may be biology danger
Evil, finds mainly to contain tetra- kinds of elements of Ti, O, C, N, no other impurities using X-ray photoelectron spectrum (XPS) analysis;And eliminate
After planting body implantation human body, risk that coating may come off.
Embodiment
With reference to embodiment, the present invention is described in detail.
A kind of method for activating surface of tooth implant of the present invention, tooth implant is cleaned, be sandblasting, acid treatment, clear again
After washing, dental implant surface forms bioactivity, porous structure.
A kind of method for activating surface of tooth implant of the present invention, specifically implements according to following steps:
Step 1, tooth implant is cleaned by ultrasonic oil removing;
Cleaning oil removal process includes:Respectively it is cleaned by ultrasonic 2 times using acetone, absolute ethyl alcohol, purified water, each 4min~
10min。
Step 2, blasting treatment is carried out to the dental implant surface obtained through step 1 with bulky grain diamond dust, form micron
The big pit of level, then tooth implant is sequentially placed into acetone, 75% ethanol and distilled water and is cleaned by ultrasonic, dry;
Pressure during blasting treatment is 0.4MPa;A diameter of 10 μm~30 μm of big pit.
Step 3, by through the tooth implant that step 2 obtains 0.09mol/L~0.13mol/L HF and 0.07mol/L~
0.11mol/L HNO3Mixed liquor processing 5min~15min of formation, distilled water are rinsed, dried, and surface is formed submicron order
Small rut, a diameter of 0.2 μm~0.7 μm of small rut.
Step 4, the tooth implant obtained through step 4 is passed through to purified water flushing successively, 5%NaHCO3 solution is cleaned by ultrasonic
2 times, each time is 5min~10min, and purified water is rinsed, and Micro90 degreasers are cleaned by ultrasonic, and running water rinses, purified water
Rinse, water for injection obtains the tooth implant of bioactivity, porous structure after rinsing.
By with upper type, method for activating surface of the invention, present invention hydrochloric acid and sulfuric acid mixing acid treatment, make use of
Corrosiveness of the mixed acid to titanium, there is provided good sandblasting dental implant surface pattern so that tooth implant presents good
Rough surface characteristic, further improve tooth implant bone junction interface bond strength.50%~75% sulfuric acid and 8%
~20% concentration of hydrochloric acid proportioning acid etching effect is preferable, and the acid etching step more than twice for making currently generally to use is reduced to once
It can just achieve the goal, shorten processing time, improve operating efficiency, reduce cost so as to fit in commercially producing;This hair
Bright method for activating surface, without additional coating, avoid introducing foreign substance there may be biology harmfulness, using X-ray photoelectricity
Son spectrum (XPS) analysis finds mainly to contain tetra- kinds of elements of Ti, O, C, N, no other impurities;And after eliminating planting body implantation human body,
The risk that coating may come off.
Embodiment 1
Step 1, tooth implant is respectively cleaned by ultrasonic 2 times, each 4min by using acetone, absolute ethyl alcohol, purified water, with
Remove the greasy dirt of dental implant surface;
Step 2, with bulky grain diamond dust sandblasting is carried out to the dental implant surface obtained through step 1 with 0.4MPa pressure
Processing, forms a diameter of 10 μm of the big pit of micron order, then tooth implant is sequentially placed into acetone, 75% ethanol and distilled water
It is cleaned by ultrasonic, dries;
Step 3, by through the tooth implant that step 2 obtains in 0.09mol/L HF and 0.07mol/L HNO3The mixing of formation
Liquid handles 5min, and distilled water rinses, and dries, the submicron order small rut for making surface form a diameter of 0.2 μm;
Step 4, the tooth implant obtained through step 4 is passed through to purified water flushing successively, 5%NaHCO3 solution is cleaned by ultrasonic
2 times, each time is 5min, and purified water is rinsed, and Micro90 degreasers are cleaned by ultrasonic, and running water rinses, and purified water is rinsed, note
Penetrate after being rinsed with water and obtain the tooth implant of bioactivity, porous structure.
Embodiment 2
Step 1, tooth implant is respectively cleaned by ultrasonic 2 times, each 5min by using acetone, absolute ethyl alcohol, purified water, with
Remove the greasy dirt of dental implant surface;
Step 2, with bulky grain diamond dust sandblasting is carried out to the dental implant surface obtained through step 1 with 0.4MPa pressure
Processing, forms a diameter of 12 μm of the big pit of micron order, then tooth implant is sequentially placed into acetone, 75% ethanol and distilled water
It is cleaned by ultrasonic, dries;
Step 3, by through the tooth implant that step 2 obtains in 0.1mol/L HF and 0.09mol/L HNO3The mixing of formation
Liquid handles 6min, and distilled water rinses, and dries, the submicron order small rut for making surface form a diameter of 0.3 μm;
Step 4, the tooth implant obtained through step 4 is passed through to purified water flushing successively, 5%NaHCO3 solution is cleaned by ultrasonic
2 times, each time is 6min, and purified water is rinsed, and Micro90 degreasers are cleaned by ultrasonic, and running water rinses, and purified water is rinsed, note
Penetrate after being rinsed with water and obtain the tooth implant of bioactivity, porous structure;
Embodiment 3
Step 1, tooth implant is respectively cleaned by ultrasonic 2 times, each 7min by using acetone, absolute ethyl alcohol, purified water, with
Remove the greasy dirt of dental implant surface;
Step 2, with bulky grain diamond dust sandblasting is carried out to the dental implant surface obtained through step 1 with 0.4MPa pressure
Processing, forms a diameter of 15 μm of the big pit of micron order, then tooth implant is sequentially placed into acetone, 75% ethanol and distilled water
It is cleaned by ultrasonic, dries;
Step 3, by through the tooth implant that step 2 obtains in 0.11mol/L HF and 0.1mol/L HNO3The mixing of formation
Liquid handles 8min, and distilled water rinses, and dries, the submicron order small rut for making surface form a diameter of 0.6 μm;
Step 4, the tooth implant obtained through step 4 is passed through to purified water flushing successively, 5%NaHCO3 solution is cleaned by ultrasonic
2 times, each time is 8min, and purified water is rinsed, and Micro90 degreasers are cleaned by ultrasonic, and running water rinses, and purified water is rinsed, note
Penetrate after being rinsed with water and obtain the tooth implant of bioactivity, porous structure.
Embodiment 4
Step 1, tooth implant is respectively cleaned by ultrasonic 2 times, each 7min by using acetone, absolute ethyl alcohol, purified water, with
Remove the greasy dirt of dental implant surface;
Step 2, with bulky grain diamond dust sandblasting is carried out to the dental implant surface obtained through step 1 with 0.4MPa pressure
Processing, forms a diameter of 25 μm of the big pit of micron order, then tooth implant is sequentially placed into acetone, 75% ethanol and distilled water
It is cleaned by ultrasonic, dries;
Step 3, by through the tooth implant that step 2 obtains 0.09mol/L~0.13mol/L HF and 0.07mol/L~
0.11mol/L HNO3The mixed liquor processing 10min of formation, distilled water are rinsed, dried, the Asia for making surface form a diameter of 0.5 μm
Micron order small rut;
Step 4, the tooth implant obtained through step 4 is passed through to purified water flushing successively, 5%NaHCO3 solution is cleaned by ultrasonic
2 times, each time is 7min, and purified water is rinsed, and Micro90 degreasers are cleaned by ultrasonic, and running water rinses, and purified water is rinsed, note
Penetrate after being rinsed with water and obtain the tooth implant of bioactivity, porous structure.
Embodiment 5
Step 1, tooth implant is respectively cleaned by ultrasonic 2 times, each 10min by using acetone, absolute ethyl alcohol, purified water,
To remove the greasy dirt of dental implant surface;
Step 2, with bulky grain diamond dust sandblasting is carried out to the dental implant surface obtained through step 1 with 0.4MPa pressure
Processing, forms a diameter of 30 μm of the big pit of micron order, then tooth implant is sequentially placed into acetone, 75% ethanol and distilled water
It is cleaned by ultrasonic, dries;
Step 3, by through the tooth implant that step 2 obtains 0.09mol/L~0.13mol/L HF and 0.07mol/L~
0.11mol/L HNO3The mixed liquor processing 15min of formation, distilled water are rinsed, dried, the Asia for making surface form a diameter of 0.7 μm
Micron order small rut;
Step 4, the tooth implant obtained through step 4 is passed through to purified water flushing successively, 5%NaHCO3 solution is cleaned by ultrasonic
2 times, each time is 10min, and purified water is rinsed, and Micro90 degreasers are cleaned by ultrasonic, and running water rinses, and purified water is rinsed, note
Penetrate after being rinsed with water and obtain the tooth implant of bioactivity, porous structure.
Claims (7)
- A kind of 1. method for activating surface of tooth implant, it is characterised in that tooth implant is cleaned, sandblasting, acid treatment, again After cleaning, dental implant surface forms bioactivity, porous structure.
- 2. a kind of method for activating surface of tooth implant as claimed in claim 1, it is characterised in that specifically include following step Suddenly:Step 1, tooth implant is cleaned by ultrasonic oil removing;Step 2, blasting treatment is carried out to the dental implant surface obtained through step 1 with bulky grain diamond dust, formed micron-sized Big pit, then tooth implant is sequentially placed into acetone, 75% ethanol and distilled water and is cleaned by ultrasonic, dry;Step 3, by through the tooth implant that step 2 obtains 0.09mol/L~0.13mol/L HF and 0.07mol/L~ 0.11mol/L HNO3Mixed liquor processing 5min~15min of formation, distilled water are rinsed, dried, and surface is formed submicron order Small rut;Step 4, by the tooth implant obtained through step 4 successively by purified water rinse, 5%NaHCO3 solution be cleaned by ultrasonic, it is pure Change water flushing, Micro90 degreasers are cleaned by ultrasonic, running water rinses, purified water is rinsed, water for injection rinses to obtain bioactivity The tooth implant of loose structure.
- 3. a kind of method for activating surface of tooth implant as claimed in claim 2, it is characterised in that cleaned in the step 1 Oil removal process includes:Respectively it is cleaned by ultrasonic 2 times using acetone, absolute ethyl alcohol, purified water, each 4min~10min.
- 4. a kind of method for activating surface of tooth implant as claimed in claim 2, it is characterised in that in the step 2:Sandblasting Pressure in processing procedure is 0.4MPa;A diameter of 10 μm~30 μm of big pit.
- 5. a kind of method for activating surface of tooth implant as claimed in claim 2, it is characterised in that in the step 3:It is small recessed A diameter of 0.2 μm~0.7 μm of hole.
- 6. a kind of method for activating surface of tooth implant as claimed in claim 2, it is characterised in that in the step 4:5% NaHCO3 solution is cleaned by ultrasonic 2 times, and each time is 5min~10min.
- A kind of 7. method for activating surface of tooth implant as claimed in any one of claims 1 to 6, it is characterised in that the tooth Planting body is cylindricality or the threaded pure titanium implant of taper.