KR101147337B1 - Algenate Impression Material Composition - Google Patents
Algenate Impression Material Composition Download PDFInfo
- Publication number
- KR101147337B1 KR101147337B1 KR1020050035315A KR20050035315A KR101147337B1 KR 101147337 B1 KR101147337 B1 KR 101147337B1 KR 1020050035315 A KR1020050035315 A KR 1020050035315A KR 20050035315 A KR20050035315 A KR 20050035315A KR 101147337 B1 KR101147337 B1 KR 101147337B1
- Authority
- KR
- South Korea
- Prior art keywords
- impression material
- alginate
- composition
- peo
- weight
- Prior art date
Abstract
본 발명은 알지네이트 인상재 분말에 폴리에틸렌 옥사이드-폴리프로필렌 옥사이드-폴리에텔렌 옥사이드(이하, "PEO-PPO-PEO"라 함) 블록 공중합체를 첨가하여, 알지네이트 인상재가 갖추어야 할 물성에는 영향을 미치지 않으면서, 인상재 분말과 물의 혼합 시에 기포 발생을 억제하여 정교한 인상채득이 가능한 알지네이트 인상재 조성물을 제공한다. 또한, 본 발명은 상기 PEO-PPO-PEO 블록 공중합체 이외에 트리클로산, 자일리톨 등을 첨가함으로써 인상채득 후의 이차감염이나 교차감염을 예방하고 인상재에 청량감을 부여하는 알지네이트 인상재 조성물을 제공한다.The present invention adds a block copolymer of polyethylene oxide-polypropylene oxide-polyethylene oxide (hereinafter referred to as "PEO-PPO-PEO") to the alginate impression material powder, without affecting the physical properties of the alginate impression material It provides an alginate impression material composition which can suppress the occurrence of bubbles during mixing of impression material powder and water to enable a sophisticated impression acquisition. In addition, the present invention provides an alginate impression material composition that prevents secondary infection or cross-infection after impression taking and gives a refreshing feeling to the impression material by adding triclosan, xylitol, and the like in addition to the PEO-PPO-PEO block copolymer.
Description
본 발명은 알지네이트 인상재 조성물에 관한 것으로, 더욱 상세하게는 알지네이트 인상재 분말에 폴리에틸렌 옥사이드-폴리프로필렌 옥사이드-폴리에텔렌 옥사이드(이하, "PEO-PPO-PEO"라 함) 블록 공중합체를 첨가하여, 알지네이트 인상재가 갖추어야 할 물성에는 영향을 미치지 않으면서, 인상재 분말과 물의 혼합 시에 기포 발생을 억제하여 정교한 인상채득이 가능한 알지네이트 인상재 조성물, 더욱 바람직하게는 상기 PEO-PPO-PEO 블록 공중합체 이외에 트리클로산, 자일리톨 등을 더 첨가함으로써 인상채득 후의 이차감염이나 교차감염을 예방하고 인상재에 청량감을 부여하는 알지네이트 인상재 조성물에 관한 것이다.The present invention relates to an alginate impression material composition, and more particularly, to an alginate impression material powder by adding a polyethylene oxide-polypropylene oxide-polyethylene oxide (hereinafter referred to as "PEO-PPO-PEO") block copolymer, Alginate impression material composition capable of suppressing bubble generation during mixing of impression material powder and water without affecting the physical properties of the impression material, more preferably triclosan and xylitol in addition to the PEO-PPO-PEO block copolymer The present invention relates to an alginate impression material composition which prevents secondary infection or cross-infection after taking impressions and imparts a refreshing feeling to the impression material.
본 발명에 따른 알지네이트 인상재 조성물은 인상재가 일반적으로 사용되는 모든 용도에 이용될 수 있으며, 본 명세서에서는 특히 치과용 인상재에 대하여 서술하지만 이로 한정되는 것은 아니다. The alginate impression material composition according to the present invention can be used in all applications in which the impression material is generally used, and in this specification, the dental impression material is described in particular, but is not limited thereto.
상기에서 '인상재(impression material)'라 함은, 구강내 치아 및 조직 등을 복제하기 위해 사용되는 재료로서, 음형(오목형태)의 인기를 인상(impression)이라 하고, 상기 인상재로 인상을 채득한 후, 상기 음형의 인기에 석고산물을 부어 양형(볼록형태)의 모형을 복제함으로써, 구강내 치아 및 조직을 구강 밖에서 관찰할 수 있도록 하는 역할을 한다. In the above description, 'impression material' refers to a material used for replicating teeth and tissues in the oral cavity, and the popularity of the negative shape (concave shape) is called an impression, and the impression is taken with the impression material. Later, by pouring a gypsum product on the popularity of the negative type to duplicate the model of the positive (convex), it plays a role to observe the teeth and tissues in the oral cavity outside the oral cavity.
알지네이트 인상재는 사용이 간편하고 양호한 정밀성을 가지고 있으며 인상채득 부위에 습기가 있어도 부정확한 인상의 원인이 되지 않는 등의 장점을 가지고 있어 가장 많이 사용되는 인상재 중의 하나이다. 또한, 치과용 알지네이트 인상재는 구강내의 치관 주위나 함몰부위를 원래의 형태대로 정확히 재현해 낼 수 있어 유치악, 무치악 등 모든 경우의 인상채득에 효과적이며, 화학반응에 의해 졸(Sol)에서 겔(Gel)로 변화하는 비가역성 탄성 인상재로서 그 취급이 용이하고 가격이 저렴하다는 장점이 있다.Alginate impression material is one of the most used impression materials because it is easy to use, has good precision and does not cause inaccurate impression even if there is moisture in the impression acquisition area. In addition, dental alginate impression material can accurately reproduce the oral crown or depression in the oral cavity as it is in its original form, and is effective for taking impressions in all cases such as dental teeth, dental teeth, etc. It is an irreversible elastic impression material that changes to Gel), and its advantages are easy to handle and low cost.
알지네이트 인상재는 분말의 형태로 공급되므로 물과 혼합하여 사용하며, 인상재를 물과 혼합하는 방법에는 기계적인 혼합과 손으로 혼합하는 방법이 있다. 기계적인 혼합은 그 이용이 편리하고 공기유입이 적어 균질한 혼합물을 얻을 수 있다는 장점이 있지만 경화시간이 빨라지고 비용이 증가하므로 치과에서는 손으로 혼합하는 방법이 보다 일반적으로 사용되고 있다. 따라서, 필연적으로 공기의 유입이 발생하게 되고, 이렇게 유입된 공기에 의해 기포가 발생하여 인상채득이 부정확하게 되는 원인이 될 뿐만 아니라, 인상재 강도를 보강하기 위해 사용된 작은 분말의 충진제 입자가 작업자에게 호흡기 질환을 유발할 수 있는 문제점이 있다. Since the alginate impression material is supplied in the form of a powder, it is used by mixing with water, and the method of mixing the impression material with water includes mechanical mixing and hand mixing. Mechanical mixing has the advantage of obtaining a homogeneous mixture because of its ease of use and low inflow of air, but the method of mixing by hand is more commonly used in dentistry because of faster curing time and increased cost. Therefore, the inflow of air inevitably occurs, and air bubbles are generated by the inflowed air, which causes inaccurate impression gain, and the small powder filler particles used to reinforce the impression material strength to the operator. There is a problem that can cause respiratory diseases.
따라서, 여러 분진 방지제를 사용하는 저분진형 알지네이트 개발에 관한 연구가 활발히 이루어졌으며, 그러한 예로, 미국특허 제5,698,610호에서는 일정량의 라놀린을 첨가함으로써 알지네이트 인상재의 분진의 문제점을 해결하였다.Therefore, researches on the development of low-dust alginate using various anti-dust agents have been actively conducted. For example, US Pat. No. 5,698,610 solves the problem of dust of the alginate impression material by adding a certain amount of lanolin.
그러나, 알지네이트 인상재 사용시의 기포발생 문제는 여전히 해결해야 할 과제로 남아있으며, 더불어 구강 미생물에 대한 항균성이 증대된 인상재에 대한 요청도 높은 실정이다.However, the bubble generation problem when using the alginate impression material remains a problem to be solved, and there is also a high demand for the impression material with increased antimicrobial resistance to oral microorganisms.
따라서, 본 발명은 이러한 종래의 기술의 문제점과 과거로부터 요청되어온 기술적 과제를 해결하는 것을 목적으로 한다.Accordingly, an object of the present invention is to solve the problems of the prior art and the technical problems that have been requested from the past.
즉, 본 발명의 목적은 알지네이트 인상재가 갖추어야 할 물성에는 영향을 미치지 않으면서, 인상재 분말과 물의 혼합 시에 기포 발생을 억제하여 정교한 인상채득이 가능한 알지네이트 인상재 조성물을 제공하는 것이다.That is, an object of the present invention is to provide an alginate impression material composition capable of precise impression acquisition by suppressing bubble generation during mixing of impression material powder and water, without affecting the physical properties of the alginate impression material.
본 발명의 또다른 목적은 사이 기포발생 억제와 더불어 항균성 및 청량감을 부여하는 알지네이트 인상재 조성물을 제공하는 것이다. It is still another object of the present invention to provide an alginate impression material composition which provides antibacterial and refreshing feelings together with suppression of bubbling.
이러한 목적을 달성하기 위한 본 발명에 따른 알지네이트 인상재 조성물은, 알지네이트, 겔화제, 겔화조절제 및 충진제로 이루어진 알지네이트 인상재 분말 100 중량부에 대하여 PEO-PPO-PEO 블록 공중합체 0.1 내지 5 중량부를 포함하는 것으로 구성되어 있다. Alginate impression material composition according to the present invention for achieving this object is to include 0.1 to 5 parts by weight of PEO-PPO-PEO block copolymer with respect to 100 parts by weight of the alginate impression material powder consisting of alginate, gelling agent, gelling regulator and filler. Consists of.
상기 조성에서, 알지네이트는 알긴산의 수용성 염으로서, 예를 들어, 알긴산 나트륨(sodium alginate), 알긴산 칼륨(potassium alginate), 알긴산 암모늄(ammonium alginate) 등을 사용할 수 있으며, 경우에 따라서는 이들의 둘 이상의 조합이 사용될 수도 있다. 상기 겔화제로는 2가 또는 그 이상의 비가용성 금속염을 가진, 예를 들어, 황산 칼슘(calcium sulfate), 이수화물(dihydrate), 또는 1/2수화물(hemihydrate) 등을 사용할 수 있으며, 경우에 따라서는 이들의 둘 이상의 조합이 사용될 수도 있다. 상기 겔화 조절제로는 나트륨(sodium) 또는 칼륨(potassium)의 적어도 하나의 인산염(phosphate), 규산염(silicate) 및 탄산염(carbonate)으로서, 예를 들어, 인산나트륨(sodium phosphate) 등을 사용할 수 있다. 상기 충진제로는 규조토(diatomaceous earth), 규산 무수물(silicic acid anhydride), 탈크(talc), 탄산칼슘(calcium cabonate), 카올린 등을 사용할 수 있으며, 경우에 따라서는 이들의 둘 이상의 조합이 사용될 수도 있다. 그러나, 이들 성분들 중의 일부가 제외된 알지네이트 인상재 분말도 경우에 따라서는 최소한의 물성을 제공할 수 있으므로, 본 발명은 이러한 다양한 알지네이트 인상재 분말 조성에 모두 적용될 수 있음은 물론이다.In the above composition, alginate may be used as a water-soluble salt of alginic acid, for example, sodium alginate, potassium alginate, ammonium alginate, and the like, in some cases two or more of them. Combinations may be used. As the gelling agent, for example, calcium sulfate, dihydrate, hemihydrate, or the like having a divalent or higher insoluble metal salt may be used. Combinations of two or more thereof may be used. As the gelling regulator, for example, sodium phosphate may be used as at least one of phosphate, silicate and carbonate of sodium or potassium. The filler may be diatomaceous earth, silicic acid anhydride, talc, calcium carbonate, kaolin, and the like, and in some cases, a combination of two or more thereof may be used. . However, alginate impression material powder, in which some of these components are excluded, may in some cases provide minimal physical properties, so that the present invention can be applied to all of these various alginate impression material powder compositions.
상기 조성 이외에도 첨가제로서 산화아연(zinc oxide), 산화마그네슘(magnesium oxide), 불화티타네이트 칼륨(potassium fluoro titanate), 분진방지제, 색소 등이 선택적으로 또는 모두 첨가할 수 있다. 상기 분진방지제로는, 예를 들어, 폴리에틸렌글리콜, 폴리프로필렌글리콜, 글리세린, 미네랄오일을 사용할 수 있다. 상기 색소로는, 예를 들어, 식용색소 청색 1호 알루미늄레이크, 식용색소 청색 2호 알루미늄레이크, 식용색소 적색 2호 알루미늄레이크, 식용색소 적색 40호 알루미늄레이크를 사용할 수 있다. In addition to the above composition, zinc oxide, magnesium oxide, potassium fluoro titanate, an anti-dust agent, a pigment, and the like may be selectively or all added as an additive. As the anti-dust agent, for example, polyethylene glycol, polypropylene glycol, glycerin, mineral oil can be used. As said pigment | dye, food coloring blue No. 1 aluminum lake, food coloring blue No. 2 aluminum lake, food coloring red No. 2 aluminum lake, food coloring red No. 40 aluminum lake can be used, for example.
상기 알지네이트 인상재 분말의 하나의 예시적인 바람직한 조성은 하기 표 1에 나타낸 바와 같다.One exemplary preferred composition of the alginate impression material powder is shown in Table 1 below.
치과용 알지네이트 인상재의 기준규격을 요약하면 다음과 같다. The standard of dental alginate impression material is summarized as follows.
ⅰ) 육안으로 관찰할 때 분말이 균일하여야 하며, 불순물을 함유하지 않아야 한다.Iii) When visually observed, the powder should be homogeneous and contain no impurities.
ⅱ) 혼합물은 제조자가 제시한 방법으로 혼합한 후 육안으로 관찰하였을 때 균질하여야 하며 덩어리가 남아 있거나 뭉쳐있어서는 안되고 인상체의 표면이 매끄러워야 한다.Ii) The mixture shall be homogeneous when visually observed after mixing by the method suggested by the manufacturer, and shall not have any lumps or agglomerations and the surface of the impression body should be smooth.
ⅲ) 충분히 혼합하는데 걸리는 시간은 60 초 이내가 되도록 한다.V) The time required for sufficient mixing shall be within 60 seconds.
ⅳ) 혼합을 시작하여 경화가 될 때까지의 시간으로 작업시간 시험방법으로 시험할 때 제조자가 제시한 시간 이후에 평균투과율은 0.25 mm를 넘어서는 안 된다.Ⅳ) The time from the start of mixing to hardening, when tested by the working time test method, shall not exceed 0.25 mm after the time given by the manufacturer.
ⅴ) 석고와의 친화성 및 미세 부위의 재현성 시험방법에 따라 시험할 때, 추천하는 석고로 제작한 석고모형과 깨끗하게 분리되어야 하고 표면은 매끄러워야 하며 인상에 주입한 석고모형은 50 ㎛의 선을 끊김 없이 재현하여야 한다.시험) When tested according to the test method of affinity with gypsum and reproducibility of fine parts, the gypsum model made of the recommended gypsum should be separated cleanly, the surface should be smooth, and the gypsum model injected into the impression should have a 50 ㎛ line. It must be reproduced without interruption.
ⅵ) 영구변형 시험에 따라 시험할 때 영구변형은 3.0 % 이하이어야 한다.Ⅵ) When tested according to the permanent deformation test, the permanent deformation shall not be more than 3.0%.
ⅶ) 압축응력 시험에 따라 시험할 때 압축응력(strain in compression)은 5 내지 20 %를 가져야 한다.V) When tested according to the compressive stress test, the strain in compression shall be between 5 and 20%.
ⅷ) 압축강도 시험에 따라 시험할 때, 압축강도는 적어도 0.35 Mpa 이상이어야 한다.I) When tested according to the compressive strength test, the compressive strength shall be at least 0.35 Mpa.
본 발명은 상기한 조건을 만족시키는 인상재 분말을 채택하고, 여기에 PEO-PPO-PEO 블록 공중합체를 첨가함으로써, 알지네이트 인상재가 갖추어야 할 물성에는 영향을 미치지 않으면서, 인상재 분말과 물의 혼합 시에 기포 발생을 억제하여 정교한 인상채득이 가능한 알지네이트 인상재 조성물을 제공한다.The present invention adopts an impression material powder that satisfies the above conditions, and by adding a PEO-PPO-PEO block copolymer thereto, bubbles are produced at the time of mixing the impression material powder and water without affecting the physical properties of the alginate impression material. It provides an alginate impression material composition capable of suppressing the occurrence of fine impression acquisition.
상기 PEO-PPO-PEO 블록 공중합체는 적은 수의 산화 에틸렌기를 갖는 것이 기포 제거에 더욱 효과적이다. 즉, 이러한 적은 수의 산화 에틸렌기를 갖는 PEO-PPO-PEO 블록 공중합체를 상기 인상재 분말에 첨가함으로써 인상재 분말과 물이 혼합될 때 기포가 발생하는 것을 억제하여 정확한 인상채득이 가능할 수 있도록 한다. 따라서, PEO-PPO-PEO 블록 공중합체는 산화 에틸렌기의 수가 공중합체를 기준으로 5 ~ 30%인 것이 바람직하다. 또한, 분자량(수평균 분자량)이 1000 ~ 5000인 것이 바람직하다. 상기 PEO-PPO-PEO 블록 공중합체는 앞서 정의한 바와 같이 인상재 분말 100 중량부를 기준으로 0.1 내지 5 중량부의 함량으로 포함되며, 너무 적으면 첨가에 따른 효과를 발휘하기 어렵고, 반대로 너무 많으면 인상재의 물성을 저하시키는 문제점이 발생할 수 있다.The PEO-PPO-PEO block copolymer having a small number of ethylene oxide groups is more effective in removing bubbles. That is, by adding the PEO-PPO-PEO block copolymer having such a small number of ethylene oxide groups to the impression material powder, it is possible to suppress the generation of bubbles when the impression material powder and water are mixed to enable accurate impression acquisition. Accordingly, the PEO-PPO-PEO block copolymer preferably has 5 to 30% of the number of ethylene oxide groups based on the copolymer. Moreover, it is preferable that molecular weight (number average molecular weight) is 1000-5000. The PEO-PPO-PEO block copolymer is included in the content of 0.1 to 5 parts by weight based on 100 parts by weight of the impression material powder as defined above, if too small it is difficult to exert the effect of the addition, on the contrary, too much if the physical properties of the impression material Degrading problems may occur.
하나의 바람직한 예에서, 본 발명에 따른 조성물에는 인상재 분말 100 중량부를 기준으로, 트리클로산 0.1 내지 5 중량부 및/또는 자일리톨 0.1 내지 5 중량부가 더 포함됨으로써, 인상채득 과정에 항균효과, 청량감 등을 부여할 수 있다. In one preferred embodiment, the composition according to the present invention further comprises 0.1 to 5 parts by weight of triclosan and / or 0.1 to 5 parts by weight of xylitol, based on 100 parts by weight of the impression material powder, thereby imparting antibacterial effect, refreshing feeling, etc. to the impression taking process. can do.
상기 트리클로산으로 사용되는 화합물은 디페닐 에테르(diphenyl ether) 유도체로서, 강력한 항균 및 항진균 작용을 나타내고 인체에는 비교적 무해한 2,4,4'-트리클로로-2'-하이드록시디페닐 에테르(2,4,4'-trichloro-2'-hydroxydiphenyl ether)가 특히 바람직하다. 인상재 분말에 첨가된 상기 화합물은 인상채득 과정의 항균, 항진균 작용에 관여하며, 이로 인하여 인상채득 후에 치면과 치은 및 상피의 미생물 수가 줄여 치과 종사자의 이차 감염 및 교차 감염을 방지하는 효과가 있다. 상기 트리클로산은 앞서 정의한 바와 같이 인상재 분말 100 중량부를 기준으로 0.1 내지 5 중량부의 함량으로 포함되며, 너무 적으면 첨가에 따른 효과를 발휘하기 어렵고, 반대로 너무 많으면 인상재의 물성을 저하시키는 문제점이 발생할 수 있다.The compound used as the triclosan is a diphenyl ether derivative, a 2,4,4'-trichloro-2'-hydroxydiphenyl ether (2,4) that exhibits strong antibacterial and antifungal action and is relatively harmless to the human body. , 4'-trichloro-2'-hydroxydiphenyl ether) is particularly preferred. The compound added to the impression material powder is involved in the antibacterial and antifungal action of the impression acquisition process, thereby reducing the number of microorganisms in the dental gingival, gingival and epithelium after the impression acquisition has the effect of preventing secondary infection and cross infection of dental workers. The triclosan is included in an amount of 0.1 to 5 parts by weight based on 100 parts by weight of the impression material powder as defined above, if too small it is difficult to exert the effect of the addition, on the contrary too much may cause a problem of lowering the physical properties of the impression material .
상기 자일리톨은 천연의 당알콜계 감미료로서, 충치예방에 효과가 있는 5 탄당 구조로 되어있다. 일반적으로 충치는 충치균인 뮤탄스균이나 소르비누스균이 음식물에 들어 있는 포도당 및 과당 등을 먹고 배출하는 젖산이 치아의 표면을 부식시키는 현상으로, 충치균은 6 탄당은 쉽게 분해하지만 5 탄당인 자일리톨은 분해하지 못한다. 이로 인해 충치의 원인인 산이 발생하지 않게 되면 영양소를 섭취하지 못한 충치균은 결국 치아 표면에서 떨어져 나가게 된다. 뿐만 아니라, 자일리톨은 입안을 시원하게 해주는 쿨링 이펙트(Cooling Effect)까지 있어서 이를 상기 인상재 분말에 첨가하면, 항균효과와 더불어 쿨링 이펙트로 인해 인상채득 시 환자에게 청량감을 줄 수 있다. 상기 자일리톨은 앞서 정의한 바와 같이 인상재 분말 100 중량부를 기준으로 0.1 내지 5 중량부의 함량으로 포함되며, 너무 적으면 첨가에 따른 효과를 발휘하기 어렵고, 반대로 너무 많으면 인상재의 물성을 저하시키는 문제점이 발생할 수 있다.The xylitol is a natural sugar alcohol-based sweetener and has a five-sugar structure that is effective in preventing tooth decay. In general, tooth decay is a phenomenon in which caries, such as mutans or sorbin, eat and release glucose and fructose in foods, which corrode the surface of teeth. can not do. As a result, when acid, which is the cause of tooth decay, does not occur, cavities that do not consume nutrients eventually fall off the tooth surface. In addition, xylitol also has a cooling effect (Cooling Effect) to cool the mouth, when added to the impression material powder, due to the antibacterial effect and cooling effect can give the patient a refreshing feeling when taking the impression. The xylitol is included in an amount of 0.1 to 5 parts by weight based on 100 parts by weight of the impression material powder, as defined above, if too small it is difficult to exert the effect of the addition, on the contrary too much may cause a problem of lowering the physical properties of the impression material .
경우에 따라서는, 본 발명의 효과를 저해하지 않는 범위내에서 당업계에 공지되어 있는 기타의 물질들이 선택적으로 더 포함될 수 있다.In some cases, other materials known in the art may optionally be further included within the scope of not impairing the effects of the present invention.
이하 실시예 및 비교예를 통해 본 발명의 내용을 더욱 구체적으로 설명하지만, 본 발명의 범주가 그것에 의해 한정되는 것은 아니다.Hereinafter, the content of the present invention will be described in more detail with reference to Examples and Comparative Examples, but the scope of the present invention is not limited thereto.
[실시예 1]Example 1
하기 표 2에 따른 조성으로 해당 물질들을 브렌더에 넣고 혼수비는 분말 12.8 g에 물 32.5 ml로 하여 혼합함으로써 인상재 조성물을 제조하였다.The impression material composition was prepared by mixing the materials according to the composition according to Table 2 in a blender by mixing 32.5 ml of water to 12.8 g of a coma powder.
[실시예 2][Example 2]
하기 표 3의 조성을 따른 것을 제외하고는 실시예 1과 동일한 방법으로 혼합하여 조성물을 제조하였다.A composition was prepared by mixing in the same manner as in Example 1 except for following the composition of Table 3.
[실시예 3][Example 3]
하기 표 4의 조성을 따른 것을 제외하고는 실시예 1과 동일한 방법으로 혼합하여 조성물을 제조하였다.To prepare a composition by mixing in the same manner as in Example 1 except for following the composition of Table 4.
[실시예 4]Example 4
하기 표 5의 조성을 따른 것을 제외하고는 실시예 1과 동일한 방법으로 혼합하여 조성물을 제조하였다.A composition was prepared by mixing in the same manner as in Example 1 except for following the composition of Table 5.
[실시예 5][Example 5]
하기 표 6의 조성을 따른 것을 제외하고는 실시예 1과 동일한 방법으로 혼합하여 조성물을 제조하였다.To prepare a composition by mixing in the same manner as in Example 1 except for following the composition of Table 6.
[비교예 1]Comparative Example 1
하기 표 7의 조성을 따른 것을 제외하고는 실시예 1과 동일한 방법으로 혼합하여 조성물을 제조하였다.To prepare a composition by mixing in the same manner as in Example 1 except for following the composition of Table 7.
[비교예 2] Comparative Example 2
하기 표 8의 조성을 따른 것을 제외하고는 실시예 1과 동일한 방법으로 혼합하여 조성물을 제조하였다.A composition was prepared by mixing in the same manner as in Example 1 except for following the composition of Table 8.
[실험예][Experimental Example]
상기 실시예 1 ~ 5와 비교예 1 및 2에서 각각 제조된 인상재 조성물의 기포발생 여부와 항균성 및 청량감을 확인하였다. The foaming and antibacterial and refreshing feeling of the impression material composition prepared in Examples 1 to 5 and Comparative Examples 1 and 2, respectively.
우선, 기포발생 여부는 블렌더에서 혼합된 조성물을 투명 용기에 담고 육안으로 기포의 발생 여부를 확인하였다.First, whether the bubble is generated in the transparent container containing the composition mixed in the blender was confirmed whether the bubble is generated visually.
항균성은, 알지네이트 인상재의 시편을 제작하여 균을 접종한 후, 일정시간 간격으로 균을 채취하여 영양배지에 접종하고, 12 시간 배양 후 균의 성장정도를 비교하는 방법으로 확인하였다. 사용한 균주는 E-coli, Streptococcus mutans 및 Aspergillus nizer이었다.The antimicrobial properties were prepared by inoculating the specimens of the alginate impression material and inoculating the bacteria, and then, the bacteria were collected at regular time intervals and inoculated in the nutrient medium, and then confirmed by the method of comparing the growth of the bacteria after 12 hours of incubation. The strains used were E-coli, Streptococcus mutans and Aspergillus nizer.
청량감은 관능검사 방법으로 확인하였다. 구체적으로, 관능검사법의 하나인 차이 식별법 중 시료간 전체적 차이를 검사하는 종합적 차이검사법으로, 다양한 검사원을 대상으로 자일리톨을 넣은 인상재와 넣지 않은 인상재를 가지고 검사원들의 인상을 채득하는 과정에서 두 인상재간에 청량감의 차이가 있는지에 대해 평가하게 하였다. Cooling was confirmed by the sensory test method. Specifically, it is a comprehensive difference test that examines the overall difference among samples among the difference identification methods, which is one of the sensory test methods, and the refreshment feeling between the two impression materials in the process of acquiring the impressions of the inspectors with the impression material with or without xylitol for various testers. Evaluate whether there is a difference.
실험 결과, 실시예 1 ~ 5의 조성물 모두에서 기포가 발생하지 않은 것으로 확인되었다. 또한, 트리클로산을 포함하고 있는 실시예 1 및 3 ~ 5의 조성물로부터 얻어진 인상재는 우수한 항균성을 갖는 것으로 확인되었고, 자일리톨을 포함하고 있는 실시예 2 ~ 5의 조성물로부터 얻어진 인상재는 청량감을 발휘하는 것으로 확인되었다. 반면에, 본 발명에 따른 PEO-PPO-PEO 블록 공중합체를 포함하지 않은 비교예 1 및 2의 조성물은 기포가 발생하는 것으로 확인되었다. 또한, 이들 비교예의 조성물로 얻어진 인상재는 항균성과 청량감도 떨어지는 것으로 확인되었다.As a result of the experiment, it was confirmed that no bubbles were generated in all of the compositions of Examples 1 to 5. In addition, the impression material obtained from the compositions of Examples 1 and 3 to 5 containing triclosan was confirmed to have excellent antimicrobial properties, and the impression material obtained from the compositions of Examples 2 to 5 containing xylitol was confirmed to exhibit a refreshing feeling. It became. On the other hand, the compositions of Comparative Examples 1 and 2, which do not contain the PEO-PPO-PEO block copolymer according to the present invention, were found to generate bubbles. Moreover, it was confirmed that the impression material obtained by the composition of these comparative examples is also inferior to antibacterial property and a refreshing feeling.
본 발명이 속한 분야에서 통상의 지식을 가진 자라면 상기 내용을 바탕으로 본 발명의 범주내에서 다양한 응용 및 변형을 행하는 것이 가능할 것이다.Those skilled in the art to which the present invention pertains will be able to perform various applications and modifications within the scope of the present invention based on the above contents.
이상의 설명과 같이, 본 발명의 알지네이트 인상재 조성물은 알지네이트 인상재 분말에 PEO-PPO-PEO 블록 공중합체를 첨가함으로써 알지네이트 인상재가 갖추어야 할 물성에는 영향을 미치지 않으면서 인상재 분말과 물의 혼합 시에 기포 발생이 억제되어 정교한 인상채득을 가능하게 한다. 또한, 트리클로산, 자일리톨 등을 더 첨가한 조성물은 인상채득 과정에 항균효과, 청량감을 부여하는 효과가 있다. As described above, the alginate impression material composition of the present invention is suppressed by the addition of the PEO-PPO-PEO block copolymer to the alginate impression material powder without mixing the impression material powder and water without affecting the physical properties of the alginate impression material To enable sophisticated impression acquisition. In addition, the composition further added triclosan, xylitol and the like has the effect of providing antibacterial effect, refreshing feeling in the impression acquisition process.
Claims (6)