KR101141501B1 - Textile fabric and method for manufacturing the same - Google Patents

Textile fabric and method for manufacturing the same Download PDF

Info

Publication number
KR101141501B1
KR101141501B1 KR1020100073463A KR20100073463A KR101141501B1 KR 101141501 B1 KR101141501 B1 KR 101141501B1 KR 1020100073463 A KR1020100073463 A KR 1020100073463A KR 20100073463 A KR20100073463 A KR 20100073463A KR 101141501 B1 KR101141501 B1 KR 101141501B1
Authority
KR
South Korea
Prior art keywords
padding
layer
film layer
lining
delete delete
Prior art date
Application number
KR1020100073463A
Other languages
Korean (ko)
Other versions
KR20120021395A (en
Inventor
김정열
서기오
김태훈
문영주
장근훈
Original Assignee
(주)글로벌첼린지
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by (주)글로벌첼린지 filed Critical (주)글로벌첼린지
Priority to KR1020100073463A priority Critical patent/KR101141501B1/en
Publication of KR20120021395A publication Critical patent/KR20120021395A/en
Application granted granted Critical
Publication of KR101141501B1 publication Critical patent/KR101141501B1/en

Abstract

본 발명은 섬유 원단에 관한 것으로서, 안감과; 겉감과; 상기 안감과 겉감의 사이에 충전되되, 패딩층 및 상기 패딩층의 상면에 접착되는 필름층으로 이루어진 패딩을 포함하여 이루어지고, 상기 패딩의 필름층의 상면은 프린팅 처리되어 있고, 상기 겉감은 외부에서 필름층이 보일 수 있도록 투명한 소재로 되어 있는 것을 특징으로 한다. 본 발명에 따르면, 필름층을 구비하여 삼출 현상이 없기 때문에 패딩 소재로서 울 등의 천연 보온 소재 또는 온도 조절형 소재를 자유롭게 적용하여 촉감이 부드러우면서도 보온성을 향상시킨 고급 이불이나 의류를 제조할 수 있다. The present invention relates to a textile fabric, comprising: a lining; Outer; And a padding formed between the lining and the outer surface, the padding comprising a padding layer and a film layer adhered to an upper surface of the padding layer, wherein the upper surface of the film layer of the padding is printed, And is made of a transparent material so that the film layer can be seen. According to the present invention, since a film layer is provided and there is no exudation phenomenon, it is possible to freely apply a natural warming material such as a wool or a temperature-controlled material as a padding material to produce a high quality blanket or a garment have.

Description

섬유 원단 및 그 제조 방법{TEXTILE FABRIC AND METHOD FOR MANUFACTURING THE SAME}BACKGROUND OF THE INVENTION 1. Field of the Invention [0001] The present invention relates to a textile fabric,

본 발명은 섬유 원단에 관한 것으로서, 특히 의류나 이불 제조시 보온성을 강화하기 위해 안감, 겉감 및 안감과 겉감 사이에 충전되는 패딩을 포함하여 이루어진 섬유 원단 및 그 제조 방법에 관한 것이다. The present invention relates to a textile fabric, and more particularly, to a textile fabric comprising padding filled between a lining, a surface, and a lining between the lining and the outer surface, in order to enhance warmth when manufacturing clothes or duvets, and a method of manufacturing the same.

일반적으로, 겨울 의류의 보온 효과를 높이기 위해 안감과 겉감 사이에 충전되는 패딩 소재로서 초창기에는 일반 솜이나 오리털 등을 사용하였다. 그렇지만, 일반 솜의 경우에는 솜이 밖으로 튀어나오는 문제점이 있었고, 오리털의 경우에는 가격이 상대적으로 고가이며 털이 밖으로 빠져나오는 문제점이 있었다. Generally, in order to increase the warming effect of winter clothes, padding material to be filled between lining and outerwear is used. In the early days, ordinary cotton or duck hair was used. However, in the case of ordinary cotton, there was a problem that the cotton popped out. In the case of downy hair, the price was relatively high and the hair came out from the outside.

이에 따라, 패딩재의 개선에 대한 요구가 계속되어 왔다. 그 후, 도 1에 도시한 바와 같이. 가격이 저렴한 합섬 섬유인 폴리에스테르(polyester) 소재를 사용하되, 상?하 표면층(1),(3)과, 상?하 표면층(1),(3)의 사이에 개재되는 중간 보온층(2)으로 이루어진 3층 구조의 패딩(10)을 개발하기에 이르렀다. Accordingly, a demand for improvement of the padding material has continued. Thereafter, as shown in Fig. (3) and upper and lower surface layers (1) and (3), which are made of low-cost synthetic fiber, polyester material, ) Having a three-layer structure.

그렇지만, 안감과 겉감 사이에 종래의 패딩(10)을 충전하여 의류나 이불을 제조하게 되면, 패딩(10) 소재가 겉감 밖으로 튀어나오는, 이른바 삼출 현상 때문에 패딩(10) 소재로서 울(wool) 등의 천연 보온 소재나 온도 조절형 소재 등을 자유롭게 사용할 수 없는 문제점이 있었다. However, if the conventional padding 10 is filled between the lining and the outer cloth to produce clothes or a duvet, the padding material 10 may protrude out of the outer material. There is a problem in that it is not possible to freely use a natural warming material or a temperature-controlled material.

이에 본 발명은 상기와 같은 문제점을 해결하기 위한 것으로서, 의류나 이불 제조시 보온성을 강화하기 위해 안감, 겉감 및 안감과 겉감 사이에 충전되는 패팅을 포함하여 이루어지되 삼출 현상이 없거나 투습?방수 기능 및 온도 조절 기능을 갖는 섬유 원단 및 그 제조 방법을 제공하는데 그 목적이 있다. Accordingly, the present invention has been made to solve the above-mentioned problems, and it is an object of the present invention to solve the above-mentioned problems, and it is an object of the present invention to provide a panty- And to provide a fiber fabric having a temperature control function and a manufacturing method thereof.

상기와 같은 목적을 달성하기 위하여 본 발명의 제1 실시형태에 따른 섬유 원단은, 안감과; 겉감과; 상기 안감과 겉감의 사이에 충전되되, 패딩층 및 상기 패딩층의 상면에 접착되는 필름층으로 이루어진 패딩을 포함하여 이루어지고, 상기 패딩의 필름층의 상면은 프린팅 처리되어 있고, 상기 겉감은 외부에서 필름층이 보일 수 있도록 투명한 소재로 되어 있는 것을 특징으로 한다.
한편, 상기와 같은 목적을 달성하기 위하여 본 발명의 제2 실시형태에 따른 섬유 원단은, 안감과; 겉감과; 상기 안감과 겉감의 사이에 충전되되, 패딩층 및 상기 패딩층의 상면에 접착되는 필름층으로 이루어진 패딩을 포함하여 이루어지고, 상기 겉감은 투습?방수 기능 및 온도 조절 기능을 갖도록, 폴리에테르 및 친수성계 폴리우레탄 수지 물질 및 자일리톨과 캡사이신을 함유한 천연 냉?온감 물질로 코팅 처리되어 있는 것을 특징으로 한다. In order to achieve the above object, a textile fabric according to a first embodiment of the present invention comprises: a lining; Outer; And a padding formed between the lining and the outer surface, the padding comprising a padding layer and a film layer adhered to an upper surface of the padding layer, wherein the upper surface of the film layer of the padding is printed, And is made of a transparent material so that the film layer can be seen.
In order to achieve the above object, a textile fabric according to a second embodiment of the present invention comprises: a lining; Outer; And a padding formed between the lining and the outer surface, the padding comprising a padding layer and a film layer adhered to the upper surface of the padding layer, wherein the outer layer is made of polyether and hydrophilic Based polyurethane resin material and a natural cold and warm feeling material containing xylitol and capsaicin.

삭제delete

삭제delete

삭제delete

삭제delete

삭제delete

삭제delete

삭제delete

다른 한편, 상기와 같은 목적을 달성하기 위하여 본 발명에 따른 섬유 원단 제조 방법은, 상?하 표면층과, 상?하 표면층의 사이에 개재되는 중간 보온층으로 이루어진 3층 구조로서, 중간 보온층은 천연 보온 소재로 되어 있는 패딩층의 상면에 필름층을 접착하여 패딩을 제조하는 단계와; 안감과 겉감 사이에 상기 제조된 기능성 패딩을 충전하여 봉제하는 단계를 포함하여 이루어진 것을 특징으로 한다. In order to achieve the above-mentioned object, a method for fabricating a textile fabric according to the present invention is a three-layer structure composed of an upper and lower surface layer and a middle insulating layer sandwiched between upper and lower surface layers, The method comprising the steps of: forming a padding layer by adhering a film layer on an upper surface of a padding layer made of a natural warming material; And filling and sewing the functional padding between the lining and the outer fabric.

여기에서, 상기 필름층은 열가소성 폴리우레탄 필름으로서 폴리에테르 및 친수성계 폴리우레탄 수지 성분을 함유하여 투습?방수 기능을 갖고 있고, 상기 겉감은 투습?방수 기능 및 온도 조절 기능을 갖도록, 폴리에테르와 친수성계 폴리우레탄 수지 물질 및 자일리톨과 캡사이신을 함유한 천연 냉?온감 물질로 코팅 처리되어 있을 수 있다. Here, the film layer contains a polyether and a hydrophilic polyurethane resin component as a thermoplastic polyurethane film and has a moisture-permeable and waterproof function. The outer layer is made of polyether and hydrophilic Based polyurethane resin material and natural cold and warm feeling material containing xylitol and capsaicin.

또한, 상기 필름층의 상면은 프린팅 처리되어 있고, 상기 겉감은 외부에서 필름층이 보일 수 있도록 투명한 소재로 되어 있을 수 있다. Further, the upper surface of the film layer is printed, and the outer surface may be made of a transparent material so that the film layer can be seen from the outside.

본 발명에 따르면, 패딩층 위에 필름층을 구비하여 삼출 현상이 없기 때문에 패딩 소재로서 울 등의 천연 보온 소재 또는 온도조절형 소재를 적용하여 촉감이 부드러우면서도 보온성을 향상시킨 고급 이불이나 의류를 제조할 수 있다. 이와 더불어, 패딩의 보온성 향상으로 인해 안감이나 겉감 소재로서 얇고 가벼운 소재 사용이 가능하기 때문에 보다 가벼운 이불이나 의류를 제조할 수 있다. 또한, 필름층이 투습?방수 기능을 갖기 때문에 다양한 용도의 이불이나 의류를 제조할 수 있다. 또한, 프린팅 처리된 필름층을 갖는 패딩과 투명한 겉감 적용을 통한 새로운 개념의 이불이나 의류를 제조할 수 있다. According to the present invention, since a film layer is provided on the padding layer and there is no exudation phenomenon, a natural warming material such as wool or the like or a temperature-controlled material is applied as a padding material to produce a high quality blanket or a garment can do. In addition, because of the improved thermal insulation of the padding, thinner and lighter materials can be used as lining or outer material, so lighter quilts and garments can be manufactured. Further, since the film layer has a moisture-permeable and waterproof function, it is possible to manufacture a futon or a garment for various purposes. It is also possible to produce a new concept of blanket or garment through padding with a printed film layer and transparent surface application.

도 1은 종래 패딩 개념도.
도 2는 본 발명에 따른 패딩 개념도.
도 3은 본 발명에 따른 섬유 원단 개념도.
도 4는 본 발명에 따른 섬유 원단 제조 방법을 설명하는 흐름도. 1 is a conceptual diagram of a conventional padding.
2 is a conceptual diagram of padding according to the present invention.
3 is a conceptual view of a textile fabric according to the present invention.
4 is a flow chart illustrating a method of fabricating a textile fabric according to the present invention.

이하, 본 발명의 바람직한 실시예를 첨부된 도면들을 참조하여 상세히 설명한다. 본 발명을 설명함에 있어, 관련된 공지 구성 또는 기능에 대한 구체적인 설명이 본 발명의 요지를 흐릴 수 있다고 판단되는 경우에는 그 상세한 설명은 생략한다. 또한, 이하에서 본 발명의 바람직한 실시예를 설명할 것이나, 본 발명의 기술적 사상은 이에 한정하거나 제한되지 않고 당업자에 의해 변형되어 다양하게 실시될 수 있음은 물론이다.Hereinafter, preferred embodiments of the present invention will be described in detail with reference to the accompanying drawings. In the following description of the present invention, a detailed description of known functions and configurations incorporated herein will be omitted when it may make the subject matter of the present invention rather unclear. In addition, the preferred embodiments of the present invention will be described below, but it is needless to say that the technical idea of the present invention is not limited thereto and can be variously modified by those skilled in the art.

도 2에 도시한 바와 같이, 본 발명에 따른 패딩(110)은 삼출 현상을 방지하도록, 패딩층(114) 및 상기 패딩층(114)의 상면에 소정의 접착제에 의해 접착되는 필름층(115)으로 이루어진다. 즉, 필름층(115)에 의해 패딩층(114)으로부터 패딩 소재가 외부로 빠져나오는 삼출 현상이 방지된다. 2, the padding 110 according to the present invention includes a padding layer 114 and a film layer 115 adhered to the upper surface of the padding layer 114 by a predetermined adhesive, Lt; / RTI > That is, the film layer 115 prevents the puffing material from escaping from the padding layer 114 to the outside.

상기 패딩층(114)은, 상?하 표면층(111),(113) 및 상?하 표면층(111),(113)의 사이에 개재되는 중간 보온층(112)으로 이루어진 3층 구조로서, 중간 보온층(112)은 보온성 강화를 위해 울과 같은 천연 보온 소재 또는 상변화 물질(PCM:Phase Change Material)을 함유한 온도 조절형 소재로 이루어질 수 있다. The padding layer 114 has a three-layer structure composed of upper and lower surface layers 111 and 113 and a middle insulating layer 112 interposed between the upper and lower surface layers 111 and 113, The insulating layer 112 may be made of a natural warming material such as wool or a temperature-controlled material containing a phase change material (PCM) for enhancing warming.

상기 상변화 물질은 주변의 온도가 상승하면 녹으면서 열을 흡수하고, 주변의 온도가 낮아지면 결정화하면서 열을 방출하는 축열?방열 특성을 반복적으로 나타내는 물질로서, 마이크로 캡슐로 안정화하여 소재에 적용할 수 있다. The phase-change material is a substance that repeatedly exhibits heat storage and heat-releasing characteristics that absorb heat while melting when the ambient temperature rises, and release heat while crystallizing when the ambient temperature is lowered. .

필름층(115)에 의해 삼출 현상이 방지되기 때문에 울과 같은 천연 보온 소재를 중간 보온층(112)으로 큰 어려움 없이 적용할 수가 있는 것이다. 이와 같이, 본 발명에 따른 패딩(110)은 패딩층(114)이 울 등의 천연 보온 소재 또는 온도 조절형 소재로 된 중간 보온층(112)을 갖기 때문에 촉감이 부드러우면서도 보온성이 향상된 고급 이불이나 의류를 제조하는데 사용할 수 있다.  Since the exudation is prevented by the film layer 115, a natural warming material such as wool can be applied to the intermediate warming layer 112 without any difficulty. As described above, the padding 110 according to the present invention has the padding layer 114 having the intermediate insulating layer 112 made of a natural warming material such as wool or a temperature-controlled material, so that the warmed- Or to make clothing.

상기 필름층(115)은, 얇은 두께(예를 들면 0.02~0.20mm)를 갖는 필름으로서 다양한 용도로 사용이 가능하도록 적어도 투습?방수 기능을 가질 수 있다. 예를 들어, 상기 필름층(115)은 투습?방수 기능을 갖도록 열가소성 폴리우레탄(Breathable Thermoplastic PolyUrethane) 필름으로서 폴리에테르(Polyether) 및 친수성(Hydrophilic)계 폴리우레탄(Polyurethane) 수지 성분으로 이루어질 수 있다.　The film layer 115 may have a thin thickness (for example, 0.02 to 0.20 mm) and may have at least a moisture permeable and waterproof function so as to be usable for various purposes. For example, the film layer 115 may be formed of a polyether and a hydrophilic polyurethane resin as a breathable thermoplastic polyurethane film so as to have a waterproof and waterproof function.

좀 더 구체적으로, 상기 필름층(115)의 성능을 살펴보면, Tensile Strength는 5Mpa 이상, Elongation at Break는 200~700%, Modulus at 100%는 2MPa 이상, Softening range는 120~190℃, MVP(Moisture Vapor Permeability) at film state는 1,000g/m2.day(ASTM E96-00BW) 이상이면 바람직하다. More specifically, the performance of the film layer 115 is more than 5 MPa, elongation at break is 200 to 700%, modulus at 100% is more than 2 MPa, softening range is 120 to 190 ° C., MVP Vapor Permeability at film state is preferably 1,000 g / m2.day (ASTM E96-00BW) or higher.

그리고, 상기 패딩층(114)과 필름층(115)을 접착하는 접착제는 투습성을 갖는 대략 0.02~0.20mm 두께인 폴리우레탄 접착제로서, 폴리올(Polyol) 성분, 반응성이 높은 이소시아네이트(Isocyanate) 및 연결 반응을 일으킬 수 있는 디올(diol)류의 쇄연장제(Chain extender)를 배합하여 만든 고형분 25~50중량%과 유기용제(Organic Solvent) 50~75중량%을 배합하여 만들 수 있다.The adhesive for bonding the padding layer 114 and the film layer 115 is a polyurethane adhesive having a moisture permeability of about 0.02 to 0.20 mm and is composed of a polyol component, a highly reactive isocyanate, And 25-50 wt% of a solid component and 50-75 wt% of an organic solvent, which are prepared by blending a diol chain extender capable of reacting with an organic solvent.

이 때, 상기 고형분은, 폴리올 75.5~86.8중량%, 이소시아네이트 1.8~2.6중량% 및 쇄연장제 11.4~21.9중량%의 비율로 배합하여 만들 수 있는데, 필요에 따라서는 일정량의 촉매(catalyst)를 첨가할 수도 있다. At this time, the solid content may be prepared by blending the solid content in the ratio of 75.5 to 86.8% by weight of polyol, 1.8 to 2.6% by weight of isocyanate and 11.4 to 21.9% by weight of chain extender. If necessary, You may.

그런데, 상기 접착제는 접착성 폴리머(12a) 및 친수성 폴리머(12b) 성분으로 이루어질 수 있도록 상기 폴리올이 500~4,000의 분자량을 갖는 접착성의 부탄디올(Butane diol)계 폴리에스터(Polyester) 폴리올 30~70중량% 및 500~3,000의 분자량을 갖는 친수성의 폴리에틸렌글리콜(polyethylene glycol) 폴리올 30~70중량%으로 배합하여 만들 수 있다.However, the adhesive may be composed of an adhesive butane diol polyester polyol having a molecular weight of 500 to 4,000 in an amount of 30 to 70 wt%, such that the polyol may be composed of the adhesive polymer 12a and the hydrophilic polymer 12b component And 30 to 70% by weight of a hydrophilic polyethylene glycol polyol having a molecular weight of 500 to 3,000.

상기 이소시아네이트는, 폴리올과 쉽게 반응하는 톨루엔 디이소시아네이트(TDI:Toluene Diisocynate), 디페닐메탄 디이소시아네이트(MDI:DiphenylMethane Diisocynate) 및 헥사메틸렌 디이소시아네이트(HMDI:Hexamethylene Diisocynate) 중 어느 하나 또는 두 가지 이상의 물질을 배합하여 사용할 수 있다.The isocyanate may be any one or more of toluene diisocyanate (TDI), diphenyl methane diisocynate (MDI) and hexamethylene diisocynate (HMDI), which react easily with the polyol And can be used in combination.

상기 쇄연장제는, 1,4 부탄디올 및 1,6 헥산디올 성분을 적정하게 배합하여 사용할 수 있다. 또한, 상기 유기용제는, 디메틸포름아미드(DMF:Dimethylformamide), 메틸에틸케톤(MEK:Methylethylketone) 및 에틸아세테이트(EA:EthylAcetate) 등의 물질 또는 이들의 배합물질을 사용할 수 있다. 예를 들면, 액안정성을 위하여 메틸에틸케톤 70~80 중량% 및 디메틸포름아미드 20~30중량%으로 배합하여 사용할 수 있다. The chain extender can be used by mixing 1,4-butanediol and 1,6-hexanediol in an appropriate amount. The organic solvent may be a material such as dimethylformamide (DMF), methylethylketone (MEK) and ethyl acetate (EA), or a mixture thereof. For example, 70 to 80% by weight of methyl ethyl ketone and 20 to 30% by weight of dimethylformamide can be used for the liquid stability.

상기 필름층(115)이 투습?방수 기능을 가짐으로써 다양한 용도의 이불이나 의류를 제조할 수 있다. 즉, 외부에서 내부로 침투하는 물을 차단시킬 뿐만 아니라 내부에서 발생하는 습기를 외부로 배출시킬 수 있기 때문에 쾌적성을 한층 강화시킨 기능성 이불이나 의류를 제조할 수 있다. 예를 들면, 등산복이나 스키복 등을 들 수 있다. The film layer 115 has a moisture-permeable and waterproof function, so that it is possible to manufacture a futon or a garment for various purposes. That is, not only the water penetrating from the outside to the inside can be cut off but also the moisture generated from the inside can be discharged to the outside, so that a functional quilt or clothing can be manufactured which further enhances the comfort. For example, a mountain climbing suit or a ski suit may be mentioned.

그리고, 상기 필름층(115)의 표면은 색상 연출을 위해 프린팅 처리될 수 있다. The surface of the film layer 115 may be printed for color rendering.

결과적으로, 본 발명에 따른 패딩(110)은 상?하 표면층(111),(113) 및 상?하 표면층(111),(113)의 사이에 개재되는 중간 보온층(112)을 갖는 3층 구조의 패딩층(114)과, 프린팅 처리되어 1.5층 구조의 필름층(115)을 포함한 총 4.5층 구조를 갖는다.
As a result, the padding 110 according to the present invention has a three-layered structure having a middle insulating layer 112 sandwiched between upper and lower surface layers 111, 113 and upper and lower surface layers 111, Padding layer 114 of a structure and a film layer 115 of a 1.5-layer structure printed thereon.

도 3에 도시한 바와 같이, 본 발명에 따른 섬유 원단(100)은, 안감(120), 겉감(130) 및 상기 안감(120)과 겉감(130) 사이에 충전되는 상술한 패딩(110)으로 이루어진다. 이와 같이, 패딩(110)에 천연 보온 소재 또는 온도조절형 소재를 사용하여 패딩(110)의 보온성이 강화되기 때문에 안감이나 겉감으로서 보다 얇고 가벼운 소재 사용이 가능하여 보다 얇고 가벼운 이불이나 의류를 제조할 수 있다. 3, the fabric 100 according to the present invention includes a lining 120, a fabric 130, and a padding 110 as described above, which is filled between the lining 120 and the fabric 130 . Since the thermal insulation of the padding 110 is strengthened by using the natural heat-insulating material or the temperature-controlled material in the padding 110, thinner and lighter materials can be used for the lining or the surface, .

그리고, 상기 패딩(110)의 필름층(115)의 상면이 프린팅 처리되어 있는 경우에는, 상기 겉감(130)은 외부에서 필름층(115)이 보일 수 있도록 투명한 소재로 되어 있는 것이 좋다. 이와 같이, 프린팅 처리된 필름층(115)을 갖는 패딩(110)과 투명한 겉감(130)을 적용하게 되면, 새로운 개념의 이불이나 의류를 제조할 수 있다. When the upper surface of the film layer 115 of the padding 110 is printed, the outer surface 130 may be made of a transparent material so that the film layer 115 can be seen from the outside. Thus, by applying the padding 110 and the transparent outer cloth 130 having the printed film layer 115, it is possible to produce a new concept of futon or garment.

그리고, 상기 겉감(130)은 투습?방수 기능 및 온도 조절 기능을 가짐으로써 쾌적성을 부여할 수 있도록, 폴리에테르 및 친수성계 폴리우레탄 수지 물질 및 Hygroscopic material인 자일리톨(Xylitol)과 Pyrogen material인 캡사이신(Capsaicin)을 함유한 천연 냉?온감 물질로 코팅 처리되어 있는 것이 좋다.
The outer surface 130 is made of a polyether and a hydrophilic polyurethane resin material and a hygroscopic material such as xylitol and a pyrogen material such as capsaicin Capsaicin) is recommended to be coated with natural cold and warm feeling material.

도 4에 도시한 바와 같이, 본 발명에 따른 섬유 원단 제조 방법은, 먼저 패딩층의 상면에 필름층을 접착하여 패딩을 제조한다(S110). 이 때, 상기 패딩층은 상?하 표면층과, 상?하 표면층의 사이에 개재되는 중간 보온층으로 이루어진 3층 구조로서, 중간 보온층은 필름층에 의해 삼출 현상이 방지되기 때문에 보온성 강화를 위해 울과 같은 천연 보온 소재 또는 상변화 물질을 함유한 온도 조절형 소재를 특별한 어려움 없이 적용할 수 있다. As shown in FIG. 4, in the method of fabricating a textile fabric according to the present invention, a film layer is first adhered to the upper surface of a padding layer to produce padding (S110). At this time, the padding layer has a three-layer structure composed of an upper and lower surface layer and a middle insulating layer interposed between the upper and lower surface layers. The middle insulating layer prevents the exudation by the film layer, It is possible to apply a thermally controlled material containing a natural warming material such as wool or a phase change material without difficulty.

그리고, 상기 필름층은 기능성 이불이나 의류를 제조하는데 사용할 수 있도록 적어도 투습?방수 기능을 가질 수 있다. 즉, 상기 필름층은 열가소성 폴리우레탄 필름으로서 폴리에테르 및 친수성계 폴리우레탄 수지 성분을 함유할 수 있다. And, the film layer may have at least a moisture-proofing and waterproofing function so that it can be used for producing functional duvets or clothes. That is, the film layer may contain a polyether and a hydrophilic polyurethane resin component as a thermoplastic polyurethane film.

그리고, 상기 겉감은 쾌적성을 부여하기 위해 투습?방수 기능 및 온도 조절 기능을 갖도록, 폴리에테르와 친수성계 폴리우레탄 수지 물질 및 자일리톨과 캡사이신을 함유한 천연 냉?온감 물질로 코팅 처리되어 있는 것이 좋다. The outer surface is preferably coated with a natural cold and warm feeling material containing polyether, a hydrophilic polyurethane resin material and xylitol and capsaicin so as to have a breathable / waterproof function and a temperature control function in order to provide comfort .

계속해서, 안감과 겉감 사이에 상기 제조된 패딩을 충전하여 봉제한다(S120). 즉, 필름층이 접착된 패딩을 적용하여 이불이나 의류를 제조하는 것이다. 이 때, 상기 필름층의 상면이 프린팅 처리되어 있을 경우에는, 상기 겉감은 외부에서 필름층이 보일 수 있도록 투명한 소재로 되어 있는 것이 좋다. Subsequently, the fabricated padding is filled between the lining and the outer cloth and sewed (S120). That is, the padding to which the film layer is adhered is applied to manufacture a futon or a garment. At this time, when the upper surface of the film layer is printed, the outer surface may be made of a transparent material so that the film layer can be seen from the outside.

한편, 본 발명에 따른 섬유 원단 및 그 제조 방법을 한정된 실시예에 따라 설명하였지만, 본 발명의 범위는 특정 실시예에 한정되는 것은 아니며, 본 발명과 관련하여 통상의 지식을 가진자에게 자명한 범위내에서 여러 가지의 대안, 수정 및 변경하여 실시할 수 있다. While the present invention has been shown and described with reference to certain exemplary embodiments thereof, it is to be understood that the scope of the invention is not limited to the disclosed exemplary embodiments, but, on the contrary, Various modifications, alterations, and alterations can be made within the scope of the present invention.

따라서, 본 발명에 개시된 실시예 및 첨부된 도면들은 본 발명의 기술 사상을 한정하기 위한 것이 아니라 설명하기 위한 것이고, 이러한 실시예 및 첨부된 도면에 의하여 본 발명의 기술 사상의 범위가 한정되는 것은 아니다. 본 발명의 보호 범위는 아래의 청구범위에 의하여 해석되어야 하며, 그와 동등한 범위 내에 있는 모든 기술 사상은 본 발명의 권리범위에 포함되는 것으로 해석되어야 할 것이다.Therefore, the embodiments disclosed in the present invention and the accompanying drawings are intended to illustrate and not to limit the technical spirit of the present invention, and the scope of the technical idea of the present invention is not limited by these embodiments and the accompanying drawings . The scope of protection of the present invention should be construed according to the following claims, and all technical ideas within the scope of equivalents should be construed as falling within the scope of the present invention.

100 : 섬유 원단 110 : 패딩
111 : 상 표면층 112 : 중간 보온층
113 : 하 표면층 114 : 패딩층
115 : 필름층 120 : 안감
130 : 겉감100: Textile fabric 110: Padding
111: upper surface layer 112: middle insulating layer
113: lower surface layer 114: padding layer
115: film layer 120: lining
130:

Claims (12)

삭제delete 삭제delete 삭제delete 삭제delete 삭제delete 삭제delete 삭제delete 섬유 원단(100)으로서,
안감(120)과;
겉감(130)과;
상기 안감(120)과 겉감(130)의 사이에 충전되되, 패딩층(114) 및 상기 패딩층(114)의 상면에 접착되는 필름층(115)으로 이루어진 패딩(110)을 포함하여 이루어지고,
상기 패딩(110)의 필름층(115)의 상면은 프린팅 처리되어 있고,
상기 겉감(130)은 외부에서 필름층(115)이 보일 수 있도록 투명한 소재로 되어 있는 것을 특징으로 하는 섬유 원단. As the textile fabric 100,
A lining 120;
A surface 130;
And a padding 110 made of a film layer 115 filled between the lining 120 and the surface 130 and adhered to the upper surface of the padding layer 114 and the padding layer 114,
The upper surface of the film layer 115 of the padding 110 is subjected to printing processing,
Wherein the outer surface (130) is made of a transparent material so that the film layer (115) can be seen from the outside. 섬유 원단(100)으로서,
안감(120)과;
겉감(130)과;
상기 안감(120)과 겉감(130)의 사이에 충전되되, 패딩층(114) 및 상기 패딩층(114)의 상면에 접착되는 필름층(115)으로 이루어진 패딩(110)을 포함하여 이루어지고,
상기 겉감(130)은 투습?방수 기능 및 온도 조절 기능을 갖도록, 폴리에테르 및 친수성계 폴리우레탄 수지 물질 및 자일리톨과 캡사이신을 함유한 천연 냉?온감 물질로 코팅 처리되어 있는 것을 특징으로 하는 섬유 원단. As the textile fabric 100,
A lining 120;
A surface 130;
And a padding 110 made of a film layer 115 filled between the lining 120 and the surface 130 and adhered to the upper surface of the padding layer 114 and the padding layer 114,
Wherein the outer cloth (130) is coated with a natural cold and warm feeling material containing polyether, a hydrophilic polyurethane resin material and xylitol and capsaicin so as to have a moisture permeation / waterproof function and a temperature control function. 상?하 표면층과, 상?하 표면층의 사이에 개재되는 중간 보온층으로 이루어진 3층 구조로서, 중간 보온층은 천연 보온 소재 또는 상변화 물질을 함유한 온도조절형 소재로 되어 있는 패딩층의 상면에 필름층을 접착하여 패딩을 제조하는 단계와;
안감과 겉감 사이에 상기 제조된 패딩을 충전하여 봉제하는 단계를 포함하여 이루어진 것을 특징으로 하는 섬유 원단 제조 방법. A middle insulating layer interposed between the upper and lower surface layers and the upper and lower surface layers, wherein the intermediate insulating layer is formed of an upper surface of a padding layer made of a thermoregulating material containing a natural warming material or a phase change material Attaching a film layer to the padding to produce padding;
And filling and sewing the manufactured padding between the lining and the outer cloth. 청구항 10에 있어서,
상기 필름층은 열가소성 폴리우레탄 필름으로서 폴리에테르 및 친수성계 폴리우레탄 수지 성분을 함유하여 투습?방수 기능을 갖고 있고,
상기 겉감은 투습?방수 기능 및 온도 조절 기능을 갖도록, 폴리에테르와 친수성계 폴리우레탄 수지 물질 및 자일리톨과 캡사이신을 함유한 천연 냉?온감 물질로 코팅 처리되어 있는 것을 특징으로 하는 섬유 원단 제조 방법. The method of claim 10,
The film layer contains a polyether and a hydrophilic polyurethane resin component as a thermoplastic polyurethane film and has a moisture-proof and waterproof function.
Wherein the outer surface is coated with a natural cold and warm feeling material containing polyether, a hydrophilic polyurethane resin material and xylitol and capsaicin so as to have a moisture permeability, a waterproof function and a temperature control function. 청구항 10에 있어서,
상기 필름층의 상면은 프린팅 처리되어 있고,
상기 겉감은 외부에서 필름층이 보일 수 있도록 투명한 소재로 되어 있는 것을 특징으로 하는 섬유 원단 제조 방법. The method of claim 10,
The upper surface of the film layer is subjected to printing processing,
Wherein the outer surface is made of a transparent material so that the film layer can be seen from the outside.
KR1020100073463A 2010-07-29 2010-07-29 Textile fabric and method for manufacturing the same KR101141501B1 (en)