KR101074468B1 - Glass of illuminator formed partially forming film - Google Patents
Glass of illuminator formed partially forming film Download PDFInfo
- Publication number
- KR101074468B1 KR101074468B1 KR1020110007131A KR20110007131A KR101074468B1 KR 101074468 B1 KR101074468 B1 KR 101074468B1 KR 1020110007131 A KR1020110007131 A KR 1020110007131A KR 20110007131 A KR20110007131 A KR 20110007131A KR 101074468 B1 KR101074468 B1 KR 101074468B1
- Authority
- KR
- South Korea
- Prior art keywords
- glass
- glass plate
- film
- decorative
- decorative film
- Prior art date
Abstract
본 발명은 메탈재질이 부분 증착된 장식용 조명유리에 관한 것으로서, 보다 상세하게는 유리판재와, 저면이 상기 유리판재의 상부에 위치하고, 상면에는 메탈 증착막이 형성된 장식필름과, 상기 유리판재와 장식필름 사이에 개재되어 상기 유리판재와 장식필름을 접착하는 접착층을 포함하는 장식용 조명유리에 있어서, 상기 장식필름은 유리판재에 접착후 메탈 증착막을 일정부분 박리하여 박리된 투명면 영역을 통해 빛이 투과된다.
상기와 같은 본 발명에 따르면, 유리판재에 장식필름을 접착된 상태에서 인쇄층을 형성하여 유리판재 상에 정확한 위치에 특정 무늬가 형성되어 제조 단계에서 불량을 최소화할 수 있는 효과가 있다.
또한, 조명유리 표면에 야광물질이 포함되어 조명 작동시 야광물질에 의해 빛이 일정부분 산란되어 눈부심이 방지되고 또한, 상기의 효과를 위해 별도의 공정이 필요치 않아 수율이 향상되는 효과가 있다.
또한, 조명유리 표면에 야광물질이 균일하게 코팅되어 조명원 제거시 야광물질에 의해 일정시간 동안 조명유리 표면에 빛이 발광되어 심미감이 높으며 발광효율 또한 높은 효과가 있다.The present invention relates to a decorative illumination glass in which a metal material is partially deposited, and more particularly, a glass plate material, a bottom surface is positioned above the glass plate material, a decorative film having a metal deposition film formed on an upper surface thereof, and the glass plate material and a decoration film. In the decorative lighting glass comprising an adhesive layer interposed between the glass plate and the decorative film, the decorative film is adhered to the glass plate material and then the light is transmitted through the peeled transparent surface area by peeling a portion of the metal deposition film. .
According to the present invention as described above, by forming a printing layer in a state in which the decorative film is adhered to the glass plate material, a specific pattern is formed on the glass plate material at an accurate position, thereby minimizing defects in the manufacturing step.
In addition, the luminous material is included on the surface of the illumination glass, so that the light is scattered by the luminous material during the lighting operation, thereby preventing glare, and the effect of improving the yield is not required for the above effect.
In addition, since the luminous material is uniformly coated on the surface of the illumination glass, when the illumination source is removed, the light is emitted to the surface of the illumination glass for a predetermined time by the luminous substance, resulting in high aesthetics and high luminous efficiency.
Description
본 발명은 메탈재질이 부분 증착된 장식용 조명유리에 관한 것으로서, 보다 상세하게는 유리 표면에 특정 무늬를 형성하여 심미성과 장식성을 높이고 작업공정을 단순화하여 수율을 높일 수 있는 장식용 조명유리에 관한 것이다.
The present invention relates to a decorative lighting glass with a metal material partially deposited, and more particularly to a decorative lighting glass that can increase the yield by forming a specific pattern on the glass surface to enhance the aesthetics and decoration and simplify the work process.
일반적으로 유리판재는 평활성(平滑性)이 우수하고, 투시상(透視像) 및 반사상(反射像)을 얻을 수 있기 때문에 일반건축물, 점포, 주택 및 고층건축물 등의 내·외장재용로도 널리 사용되고 있다. In general, glass sheet material has excellent smoothness, and it is widely used for interior and exterior materials of general buildings, stores, houses, high-rise buildings, etc., because it can obtain perspective images and reflection images. have.
그러나, 이와 같은 유리판재는 건축물 등의 단순한 내·외장재로만 사용되기 때문에 미적 내지 장식적인 면은 등한시되어 장식미가 필요로 하는 조명유리에 활용하기에는 어려운 실정이다.However, such a glass sheet material is used only as a simple interior and exterior materials, such as buildings, so the aesthetic or decorative aspects are neglected, so it is difficult to utilize them in lighting glass that requires aesthetics.
종래에는 조명유리에 장식미를 표현하기 위해 유리면 자체를 샌딩하여 거친 불투명한 무늬를 형성하여 심미성을 높이기도 한다. 그러나 이러한 방법은 작업시간이 많이 소요되어 수율이 떨어지며, 유리면에 다양한 무늬을 형성하기 위해서는 수작업을 통해 작업자가 일일이 패턴을 샌딩하게 되어 생산성이 저하되는 문제점이 발생된다.Conventionally, in order to express the decorative beauty on the illumination glass, the glass surface itself is sanded to form a coarse opaque pattern to increase aesthetics. However, this method takes a lot of work time, the yield is reduced, and in order to form a variety of patterns on the glass surface, the worker sanding the pattern by hand manually causes a problem that productivity is reduced.
다른 방법으로는 유리면에 직접 알루미늄 등의 금속막을 증착하여 특정 무늬가 형성된 조명유리를 대량으로 생산할 수 있으나, 이는 고가의 장비가 사용되어 제조비용이 높은 단점을 가지게 된다.Alternatively, by depositing a metal film, such as aluminum directly on the glass surface can produce a large amount of lighting glass with a specific pattern, but this has the disadvantage that the manufacturing cost is high because expensive equipment is used.
또한, 특정 무늬가 형성된 장식필름을 미리 마련하여 조명유리에 접착하는 방법도 있으나, 이는 장식필름을 조명유리에 정확한 위치에 접착하기가 어려워 불량이 많이 발생된다.In addition, there is also a method of pre-preparing a decorative film having a specific pattern formed and bonded to the lighting glass, which is difficult to adhere the decorative film to the lighting glass at the correct position, a lot of defects are generated.
그리고 조명유리를 통해 방출되는 빛 눈부심을 방지하기 위해서는 유리 또는 장식필름 표면에 유백색 안료 등으로 코팅하는 별도의 작업공정이 소요되어 수율이 떨어지는 문제점이 발생된다.In addition, in order to prevent light glare emitted through the illumination glass, a separate work process for coating with a milky pigment or the like on the surface of the glass or decorative film takes a problem, which results in a drop in yield.
따라서, 이러한 장식용 조명유리의 불합리한 점을 극복하고 유리 표면에 다양한 무늬를 쉽게 형성하여 심미감을 높이고, 작업공정을 줄여 제조비용이 저렴한 조명유리에 대한 요구가 높아지고 있는 실정이다.
Therefore, the situation is increasing the demand for low-cost manufacturing glass to overcome the unreasonable points of such decorative lighting glass and to easily form a variety of patterns on the glass surface to increase the aesthetics, reducing the work process.
본 발명은 상기와 같은 문제점을 해결하기 위하여 안출된 것으로서, 본 발명의 목적은 작업공정을 단순화하여 수율을 높이고, 유리 표면에 특정 무늬를 형성하여 심미감이 높은 메탈 부분 증착막이 형성된 조명유리을 제공함에 있다.The present invention has been made to solve the above problems, the object of the present invention is to simplify the work process to increase the yield, to form a specific pattern on the glass surface to provide a light glass with a high aesthetic metallic partial deposition film formed; have.
본 발명의 다른 목적은 조명유리 표면에 야광물질이 포함되어 조명 작동시 야광물질에 의해 빛이 일정부분 산란되어 눈부심이 방지되고 또한, 야광물질이 빛을 일정부분 흡수하여 조명원을 제거하여도 야광물질을 통해 조명유리 표면에서 빛을 발광하는 심미성이 높은 메탈 부분 증착막이 형성된 조명유리를 제공함에 있다.
Another object of the present invention is to include a luminous material on the surface of the light glass, light is scattered by the luminous material at the time of the lighting operation to prevent glare, and the luminous material absorbs a certain portion of the light to remove the luminous source The present invention provides an illumination glass having a high aesthetic metal deposition film which emits light from a surface of an illumination glass through a material.
상기와 같은 목적을 달성하기 위한 본 발명의 일측면에 따르면, 유리판재와, 저면이 상기 유리판재의 상부에 위치하고, 상면에는 메탈 증착막이 형성된 장식필름과, 상기 유리판재와 장식필름 사이에 개재되어 상기 유리판재와 장식필름을 접착하는 접착층을 포함하는 장식용 조명유리에 있어서, 상기 장식필름은 유리판재에 접착후 메탈 증착막을 일정부분 박리하여 박리된 투명면 영역을 통해 빛이 투과된다.According to one aspect of the present invention for achieving the above object, the glass plate material, the bottom surface is located on the upper portion of the glass plate material, the upper surface is interposed between the decorative film formed with a metal deposition film, the glass plate material and the decorative film In the decorative lighting glass comprising an adhesive layer for adhering the glass plate and the decorative film, the decorative film is transmitted to the light through the transparent surface area by peeling a portion of the metal deposition film after adhering to the glass plate.
여기서 상기 접착층은 주성분으로 접착성 수지 100중량부와, 첨가제로서 야광물질 10~20중량부와, 안료 5~10중량부 및 희석제 10~50중량부를 포함하여 제공된다.Here, the adhesive layer is provided to include 100 parts by weight of the adhesive resin as a main component, 10 to 20 parts by weight of the luminous material as an additive, 5 to 10 parts by weight of the pigment and 10 to 50 parts by weight of the diluent.
장식용 조명유리의 제조방법은 유리판재의 상면에 접착층을 형성하는 단계, 상면에 메탈 증착막이 형성된 장식필름의 저면을 상기 접착층에 접착하는 단계, 상기 장식필름의 메탈 증착막을 박리 잉크로 인쇄하는 단계, 상기 장식필름을 수세하여 장식필름에 박리된 투명면 영역을 형성하는 단계를 포함하여 제공된다.Method of manufacturing a decorative lighting glass comprises the steps of forming an adhesive layer on the upper surface of the glass plate material, bonding the bottom surface of the decorative film having a metal deposition film formed on the upper surface to the adhesive layer, printing the metal deposition film of the decorative film with a peeling ink, Washing the decorative film is provided to form a transparent surface area peeled off the decorative film.
여기서 상기 접착층은 주성분으로 접착성 수지 100중량부와, 첨가제로서 야광물질 10~20중량부와, 안료 5~10중량부 및 희석제 10~50중량부를 포함하여 제공된다.Here, the adhesive layer is provided to include 100 parts by weight of the adhesive resin as a main component, 10 to 20 parts by weight of the luminous material as an additive, 5 to 10 parts by weight of the pigment and 10 to 50 parts by weight of the diluent.
또한, 상기 유리판재와 장식필름이 접착된 상태에서 유리판재를 상하 반전하여 상기 야광물질과 접착성 수지의 비중차를 이용하여 상기 야광물질을 상기 장식필름의 저면에 침강시켜 건조하는 단계가 더 포함하여 제공된다.
The method may further include inverting the glass plate vertically in a state in which the glass plate and the decorative film are adhered to each other, and drying the luminous material on the bottom surface of the decorative film by using the specific gravity difference between the luminous material and the adhesive resin. Is provided.
상기와 같은 본 발명에 따르면, 유리판재에 장식필름을 접착된 상태에서 인쇄층을 형성하여 유리판재 상에 정확한 위치에 특정 무늬가 형성되어 제조 단계에서 불량을 최소화할 수 있는 효과가 있다.According to the present invention as described above, by forming a printing layer in a state in which the decorative film is adhered to the glass plate material, a specific pattern is formed on the glass plate material at an accurate position, thereby minimizing defects in the manufacturing step.
또한, 조명유리 표면에 야광물질이 포함되어 조명 작동시 야광물질에 의해 빛이 일정부분 산란되어 눈부심이 방지되고 또한, 상기의 효과를 위해 별도의 공정이 필요치 않아 수율이 향상되는 효과가 있다.In addition, the luminous material is included on the surface of the illumination glass, so that the light is scattered by the luminous material during the lighting operation, thereby preventing glare, and the effect of improving the yield is not required for the above effect.
또한, 조명유리 표면에 야광물질이 균일하게 코팅되어 조명원 제거시 야광물질에 의해 일정시간 동안 조명유리 표면에 빛이 발광되어 심미감이 높으며 발광효율 또한 높은 효과가 있다.
In addition, since the luminous material is uniformly coated on the surface of the illumination glass, when the illumination source is removed, the light is emitted to the surface of the illumination glass for a predetermined time by the luminous substance, resulting in high aesthetics and high luminous efficiency.
도 1은 본 발명에 따른 메탈 부분 증착막이 형성된 조명유리의 분해 사시도이다.
도 2은 본 발명에 따른 메탈 부분 증착막이 형성된 조명유리의 단면구조를 나타낸 도면이다.
도 3a~3f는 본 발명에 따른 메탈 부분 증착막이 형성된 조명유리의 제조단계별 단면구조를 나타낸 도면이다.1 is an exploded perspective view of an illumination glass with a metal partial deposition film according to the present invention.
2 is a view showing a cross-sectional structure of the illumination glass with a metal partial deposition film according to the present invention.
3a to 3f is a view showing a cross-sectional structure for each manufacturing step of the illumination glass with a metal partial deposition film according to the present invention.
이하에서는 첨부된 도면을 참조하여 본 발명의 바람직한 일 실시예를 상세하게 설명하기로 한다.Hereinafter, a preferred embodiment of the present invention will be described in detail with reference to the accompanying drawings.
도 1은 본 발명에 따른 메탈 부분 증착막이 형성된 조명유리의 분해 사시도이고, 도 2은 본 발명에 따른 메탈 부분 증착막이 형성된 조명유리의 단면구조를 나타낸 도면이다.1 is an exploded perspective view of an illumination glass with a metal partial deposition film according to the present invention, Figure 2 is a view showing a cross-sectional structure of the illumination glass with a metal partial deposition film according to the present invention.
도면을 참조하면, 본 발명에 따른 메탈 부분 증착막이 형성된 조명유리는 유리판재(10)와, 장식필름(30)과, 유리판재(10)와 장식필름(30) 사이에 개재되어 양측을 접합하는 접착층(20)을 포함한다.Referring to the drawings, the illumination glass with the metal partial deposition film according to the present invention is interposed between the
유리판재(10)는 일반적으로 창유리 또는 병유리 등의 제조에 쓰이는 Soda-lime 유리가 가장 많이 사용되나, 여기서 본 발명에 따른 유리판재(10)는 조명용으로 열충격이나 온도의 급격한 변화에 높은 저항력을 가지는 Borosilicate 유리인 것이 바람직하다.In general, the
장식필름(30)은 저면이 접착층(20)과 접착되는 합성수지 필름(31)과 합성수지 필름(31) 상면에 부착되는 메탈 증착막(32)을 포함한다. The
합성수지 필름(31)은 PET(Polyethylene Terephthalate) 필름, PVC(Polyvinylchloride) 필름, PE(Polyethylene) 필름 등으로 이루어질 수 있으며 바람직하게는 강화 PET 필름으로 이루어진다. 강화 PET 필름은 열가소성 수지 중 내열성이 가장 우수하고, 온도, 습도의 영향을 적게 받으며 응력에 따른 크랙의 염려가 없어 조명용으로 사용하기에 가장 유리하다.The
메탈 증착막(32)은 알루미늄 재질로 이루어짐이 바람직하며, 본 발명에서는 장식필름(30)을 유리판재(10)에 접착한 후, 박리과정을 통해 메탈 증착막(32)의 일정 영역을 박리시켜 장식필름(30) 표면에 투명면 영역(32a)을 형성한다. 이러한 투명면 영역(32a)을 통하여 조명빛이 투과되며, 메탈 증착막(32)이 남겨진 영역은 빛이 투과되지 않게 된다.The
접착층(20)은 접착성 수지(21)를 주성분으로 하고 첨가제로서 야광물질 등 다양한 물질이 첨가될 수 있다.The
접착성 수지(21)는 접착성을 가지면서 경화되고, 조명원으로부터 광에 영향을 미치지 않는 투광성 수지로 에폭시 수지 또는 실리콘 수지로 이루어짐이 바람직하다.The
첨가제로는 야광물질(22), 안료(23), 희석제, 금속분말 등이 첨가될 수 있다.As the additive, a
야광물질(22)은 조명원으로부터 발생되는 빛을 흡수하고, 조명원을 제거하였을 때 야광물질(22)에서 빛을 방출하는 것으로, 본 발명에 따른 야광물질(22)은 입도가 큰 알갱이로 첨가되는 것이 바람직하다. 이는 조명원으로부터 빛이 조사되어 야광물질(22)에 빛이 일부 흡수되고 일부는 야광물질(22)에 반사되어 빛이 산란되도록 한다.The
또한, 야광물질(22)의 입도가 크면 발광세기가 강하고 잔광 시간이 길게 유지되는 장점이 있으나, 너무 많은 중량비의 야광물질(22)을 접착층(20)에 첨가하게 되면 조명유리를 통해 빛이 유출되는 양이 적어지는 단점이 발생된다.In addition, when the particle size of the
그래서 야광물질(22)의 함량은 100중량부의 접착성 수지(21)에 10~20중량부의 야광물질(22)이 첨가됨이 바람직하다.Therefore, the content of the
안료(23)는 사용자의 임의에 따라 다양한 색상의 안료(23)가 첨가될 수 있으며, 5~10중량부의 안료(23)를 첨가하는 것이 바람직하다.
희석제는 야광물질(22)과 접착성 수지(21) 및 안료(23)를 액상화시켜 용이하게 용해되도록 하기 위한 물질로서, 용해도가 크며, 회수성이 우수한 석유경질유분, 알코올, 톨루엔, 에테르, 아세톤 및 할로겐화탄화수소 등이 사용될 수 있다. 희석제의 함량은 수지의 종류에 따라 각각 다르게 설정할 수 있으나 일반적으로 10~50중량부의 희석제를 첨가하는 것이 바람직하다.The diluent is a material for liquefying the
또한, 접착층(20)은 간단하게 양면이 접착성을 가지는 양면테이프일 수도 있다.
In addition, the
아래에서는 본 발명에 따른 메탈 부분 증착막이 형성된 조명유리의 제조방법에 대해 자세히 설명하도록 한다.
Hereinafter will be described in detail for the manufacturing method of the illumination glass with a metal partial deposition film according to the present invention.
도 3a~3f는 본 발명에 따른 메탈 부분 증착막이 형성된 조명유리의 제조단계별 단면구조를 나타낸 도면이다.3a to 3f is a view showing a cross-sectional structure for each manufacturing step of the illumination glass with a metal partial deposition film according to the present invention.
도면을 참조하면, 도 3a에 도시된 바와 같이 먼저 유리판재(10)의 일면에 접착층(20)을 형성한다. 이때에 접착층(20)은 주성분인 접착성 수지(21)에 야광물질(22), 안료(23), 희석제 또는 금속분말 등이 첨가될 수 있으며, 유리판재(10) 상에 첨가제가 혼합된 접착층(20)을 도포하게 된다.Referring to the drawings, as shown in FIG. 3A, an
그리고 상면에 메탈 증착막(32)을 가지는 장식필름(30)을 준비하여 도 3b에 도시된 바와 같이 장식필름(30)의 저면을 접착층(20)에 접착한다. Then, the
그런 다음 도 3c를 참조하면, 상부에 장식필름(30)이 접착된 상태의 유리판재(10)를 상하 반전하여 건조하게 된다. 여기서 접착층(20)에 첨가되는 야광물질(22)은 입도가 큰 알갱이 형태로 접착성 수지(21)보다 비중이 높아 장식필름(30)의 저면에 균일하게 침강된다. 그리고 희석제가 증발되면서 야광물질(22)이 균일하게 코팅된다.Then, referring to Figure 3c, the
상기와 같이 코팅된 야광물질(22)은 조명원에서 빛이 조사되면 야광물질(22)이 빛을 일정시간 동안 흡수하고, 조명원을 차단하면 야광물질(22)이 빛을 외부로 발광한다. 이때, 야광물질(22)이 장식필름(30)의 저면 근처 즉, 조명유리의 외측에 균일하게 밀집되어 발광시 발광효율을 높이게 된다.When the
또한, 입도가 큰 야광물질(22)은 조명을 통해 조사되는 빛이 일부 반사되어 빛이 산란되는 효과도 가지게 된다. 이는 종래에 빛을 산란시켜 눈부심을 방지하기 위해 유리 또는 장식필름(30)에 유백색 안료(23)를 코팅하는 것과 동일한 효과를 가지게 되어 공정단계를 줄여 수율이 향상된다.In addition, the
여기서 접착층(20)에 첨가되는 안료(23)의 색상에 따라 조명색이 표현된다. 또한, 금속분말을 첨가하여 조명을 비출때 금속분말에 의해 빛이 반사되어 심미성을 높일수도 있다.Here, the illumination color is expressed according to the color of the
그리고 도 3d에 도시된 바와 같이 장식필름(30)의 상면에 소정 형상의 무늬를 가지는 인쇄층(40)을 형성한다. 이때, 유리판재(10)에 장식필름(30)이 부착된 상태에서 정확한 위치에 인쇄층(40)을 형성하여 불량을 최소화할 수 있게 된다.And as shown in Figure 3d to form a printed
그리고 도 3e와 같이 박리 잉크를 사용하여 박리공정을 거쳐 인쇄층(40) 하부의 메탈 증착막(32)은 박리되지 않고 그 외 부분은 메탈 증착막(32)이 박리되어 장식필름(30)에 투명면 영역(32a)이 형성된다. 여기서 박리공정은 그라비아 인쇄 또는 스크린 인쇄를 통해 메탈 증착막(32)을 박리하는 것이 바람직하다.3E, the
그런 다음 수세과정을 거쳐 인쇄층(40)이 제거되어 도 3f와 같이 완성된다.
Then, the
상기와 같이 완성된 장식용 조명유리는 외부 조명원과 야광물질이 외부 조명원을 흡수하여 발생하는 광원을 번갈아 가며 사용하여 사용자로 하여금 심미감을 더 높이게 할 수 있다.The completed decorative lighting glass as described above can be used to alternate the light source generated by the external light source and the luminous material absorbs the external light source to increase the user's aesthetics.
아래에서는 상기와 같이 작동되는 메탈 부분 증착막이 형성된 조명유리에 대해 자세히 설명하도록 한다.
Hereinafter will be described in detail with respect to the illumination glass with a metal partial deposition film formed as described above.
먼저 외부 조명원을 작동하여 빛을 발생시키고, 발생되는 빛을 조명유리에 첨가된 야광물질이 빛을 흡수한다.First, the external light source is operated to generate light, and the luminous material added to the illumination glass absorbs the generated light.
이때에, 외부 조명원으로부터 야광물질에 빛의 흡수가 포화상태가 되는 시간과, 빛의 흡수가 포화상태가 된 야광물질이 외부 조명원이 제거된 상태에서 빛 방출이 완료되는 시간을 미리 조명제어부에 설정한다.At this time, the lighting control unit in advance the time that the absorption of light from the external light source to the luminous material is saturated, and the time when the light emission is completed in the state that the external light source is removed from the luminous material that the light absorption is saturated. Set to.
그리하여 야광물질에 빛의 흡수가 포화상태가 되면 조명제어부가 외부 조명원의 작동을 중단시키고, 야광물질을 통해 빛이 방출된다. 그리고 야광물질의 빛 방출이 완료되면 다시 조명제어부가 외부 조명원을 작동시킨다. 이렇게 외부 조명원과 야광물질의 빛이 번갈아가며 방출되어 은은한 효과가 연출되도록 한다.
Thus, when the absorption of light in the luminous material is saturated, the lighting control unit stops the operation of the external light source, and the light is emitted through the luminous material. When the light emission of the luminous material is completed, the lighting control unit operates the external light source again. In this way, the light of the external light source and the luminous material are alternately emitted to produce a subtle effect.
비록 본 발명이 상기 언급된 바람직한 실시예와 관련하여 설명되어졌지만, 발명의 요지와 범위로부터 벗어남이 없이 다양한 수정이나 변형을 하는 것이 가능하다. 따라서 첨부된 특허등록청구의 범위는 본 발명의 요지에서 속하는 이러한 수정이나 변형을 포함할 것이다.
Although the present invention has been described in connection with the above-mentioned preferred embodiments, it is possible to make various modifications or variations without departing from the spirit and scope of the invention. Accordingly, the scope of the appended claims should include all such modifications and changes as fall within the scope of the present invention.
10 : 유리판재 20 : 접착층
21 : 접착성 수지 22 : 야광물질
23 : 안료 30 : 장식필름
31 : 합성수지 필름 32 : 메탈 증착막
32a : 투명면 영역 40 : 인쇄층10
21: adhesive resin 22: luminous material
23: Pigment 30: Decorative Film
31
32a: transparent surface area 40: printed layer
Claims (5)
저면이 상기 유리판재의 상부에 위치하고, 상면에는 메탈 증착막이 형성된 장식필름과;
상기 유리판재와 장식필름 사이에 개재되어 상기 유리판재와 장식필름을 접착하는 접착층을; 포함하는 장식용 조명유리에 있어서,
상기 장식필름은 유리판재에 접착후 메탈 증착막을 일정부분 박리하여 박리된 투명면 영역을 통해 빛이 투과되며,
상기 접착층은 접착성 수지 100중량부와, 첨가제로서 야광물질 10~20중량부와, 안료 5~10중량부 및 희석제 10~50중량부를 포함하는 것을 특징으로 하는 메탈 부분 증착막이 형성된 조명유리.
Glass plate material;
A decorative film having a bottom surface positioned above the glass plate material and having a metal deposition film formed thereon;
An adhesive layer interposed between the glass plate and the decorative film to bond the glass plate and the decorative film; In the decorative lighting glass containing,
After the decorative film is adhered to the glass plate material, light is transmitted through the peeled transparent surface area by peeling a portion of the metal deposition film.
The adhesive layer is 100 parts by weight of the adhesive resin, 10 to 20 parts by weight of the luminous material as an additive, 5 to 10 parts by weight of the pigment and 10 to 50 parts by weight of the diluent comprises a metal glass deposition film formed illumination glass.
상면에 메탈 증착막이 형성된 장식필름의 저면을 상기 접착층에 접착하는 단계;
상기 장식필름의 메탈 증착막을 박리 잉크로 인쇄하는 단계;
상기 장식필름을 수세하여 장식필름에 박리된 투명면 영역을 형성하는 단계;를 포함하는 것을 특징으로 하는 메탈 부분 증착막이 형성된 조명유리의 제조방법.
Forming an adhesive layer on an upper surface of the glass plate;
Bonding a bottom surface of a decorative film having a metal deposition film formed thereon to an adhesive layer;
Printing a metal deposition film of the decorative film with a peeling ink;
And washing the decorative film to form a transparent surface region peeled off the decorative film.
상기 접착층은 접착성 수지 100중량부와, 첨가제로서 야광물질 10~20중량부와, 안료 5~10중량부 및 희석제 10~50중량부를 포함하는 것을 특징으로 하는 메탈 부분 증착막이 형성된 조명유리의 제조방법.
The method of claim 3,
The adhesive layer is 100 parts by weight of the adhesive resin, 10 to 20 parts by weight of the luminous material as an additive, 5 to 10 parts by weight of the pigment and 10 to 50 parts by weight of the diluent of the production of the metal partial deposition film formed illumination glass Way.
상기 유리판재와 장식필름이 접착된 상태에서 유리판재를 상하 반전하여 상기 야광물질과 접착성 수지의 비중차를 이용하여 상기 야광물질을 상기 장식필름의 저면에 침강시켜 건조하는 단계가 더 포함되는 것을 특징으로 하는 메탈 부분 증착막이 형성된 조명유리의 제조방법.
The method of claim 4, wherein
And inverting the glass plate vertically in the state in which the glass plate and the decorative film are adhered to each other to settle the luminous material on the bottom surface of the decorative film by using a specific gravity difference between the luminous material and the adhesive resin, and drying the glass plate. Method for producing a light glass with a metal partial deposition film characterized in that.