KR101054651B1 - Bulletproof material - Google Patents

Bulletproof material Download PDF

Info

Publication number
KR101054651B1
KR101054651B1 KR1020090073032A KR20090073032A KR101054651B1 KR 101054651 B1 KR101054651 B1 KR 101054651B1 KR 1020090073032 A KR1020090073032 A KR 1020090073032A KR 20090073032 A KR20090073032 A KR 20090073032A KR 101054651 B1 KR101054651 B1 KR 101054651B1
Authority
KR
South Korea
Prior art keywords
bulletproof
bulletproof material
ceramic
ceramic ball
debris
Prior art date
Application number
KR1020090073032A
Other languages
Korean (ko)
Other versions
KR20110015345A (en
Inventor
김현복
Original Assignee
김현복
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 김현복 filed Critical 김현복
Priority to KR1020090073032A priority Critical patent/KR101054651B1/en
Publication of KR20110015345A publication Critical patent/KR20110015345A/en
Application granted granted Critical
Publication of KR101054651B1 publication Critical patent/KR101054651B1/en

Abstract

본 발명은 방탄 소재에 관한 것으로서,The present invention relates to a bulletproof material,

보다 구체적으로는, 세라믹볼을 소성 가공하여, 소성된 다수의 세라믹볼 주위에 세라믹 분말이 소성 가공되어 접착되게 세라믹볼을 일정한 두께의 판상으로 형성하여 방탄 소재를 제조함으로써,More specifically, by firing the ceramic ball, by forming a ceramic ball in a plate shape of a constant thickness so that the ceramic powder is plastically processed and bonded around the fired ceramic ball, to produce a bulletproof material,

방탄 소재에 총격이 가해지거나, 방탄 소재가 피폭을 받았을 때,When the bulletproof material is shot or the bulletproof material is exposed,

탄환 또는 파편이 방탄 소재를 구성하고 있는 세라믹볼과 충돌한 뒤, 세라믹볼의 둥근 외주면과 접촉되어 빗겨 나가면서 그 충격을 완화시킬 수 있게 하여, 방탄 소재의 기능을 크게 향상시킬 수 있게 함과 동시에,The bullet or debris collides with the ceramic ball constituting the bulletproof material, and then comes into contact with the round outer circumferential surface of the ceramic ball so as to mitigate the impact, thereby greatly improving the function of the bulletproof material. ,

탄환 또는 파편의 충격이 탄환 또는 파편이 충돌된 방탄 소재의 세라믹볼에 국한되게 하여 파손 범위를 최소화시킴으로써, 방탄 소재의 수명을 보다 오래 유지시킬 수 있도록 하며,The impact of bullets or debris is limited to ceramic balls made of bulletproof materials in which bullets or debris are collided, thereby minimizing the scope of breakage, thereby maintaining the life of the bulletproof material longer.

세라믹볼의 사이 사이에 공극이 형성되어, 공극 내부에 세라믹 분말이 소성 가공되어 충진됨으로써, 방탄 소재의 강도가 강화되고, 경량화되어 사용에 보다 간편함을 제공할 수 있도록 한 것이다.The voids are formed between the ceramic balls, and the ceramic powder is plastically processed and filled in the voids, so that the strength of the bulletproof material is strengthened, and the weight is reduced to provide more convenience in use.

방탄 소재 Bulletproof material

Description

방탄 소재{BULLETPROOF MATERIALS}Bulletproof material {BULLETPROOF MATERIALS}

본 발명은 방탄 소재에 관한 것으로서,The present invention relates to a bulletproof material,

총격을 받거나 폭탄이 폭발했을 때, 탄환이나 폭탄의 파편으로 부터 인명을 보호하기 위하여,To protect lives from bullets or debris when shot or exploded,

방탄 헬멧이나 방탄복 및 방탄복의 전,후에 부착되는 방탄판과 방탄 방패 등의 개인 안전 장비와,Personal safety equipment such as bulletproof helmets and body armor and bulletproof shields that are attached to the body before and after the body armor;

방탄 차량이나 전차 또는 장갑차 등에 장착되는 방탄판과,Bulletproof plates mounted on bulletproof vehicles, tanks or armored vehicles,

방탄을 요하는 건물에 설치되는 방탄벽 등의 방탄 시설물에 주로 설치되어 사용되는 방탄 소재에 관한 것이다.The present invention relates to a bulletproof material mainly installed and used in bulletproof facilities such as a bulletproof wall installed in a building requiring bulletproof.

일반적으로 방탄 헬멧이나 방탄복 및 방탄복의 전,후에 부착되는 방탄판과 방탄 방패 등의 개인 안전 장비와,In general, personal safety equipment such as bulletproof helmets and body armor and bulletproof shields that are attached to the body before and after the body armor,

방탄 차량이나 전차 또는 장갑차 등에 장착되는 방탄판과,Bulletproof plates mounted on bulletproof vehicles, tanks or armored vehicles,

방탄을 요하는 건물에 설치되는 방탄벽 등의 방탄 시설물에는 총격을 받거나 폭탄이 폭발했을 때, 탄환이나 폭탄의 파편으로 부터 인명을 보호하기 위하여, 방탄 소재가 주로 설치되어 사용되고 있다.Bulletproof materials are installed and used in bulletproof facilities such as bulletproof walls installed in bulletproof buildings to protect people from bullets or debris when they are shot or explode.

그리고 이들 방탄 소재는 방탄 소재에 총격이 가해지거나, 방탄 소재가 피폭을 받았을 때,And these bulletproof materials are shot when the bulletproof material is shot, or when the bulletproof material is exposed,

탄환이나 폭탄의 파편에 의하여 방탄 소재가 깨어지거나, 균열이 발생하여 방탄 소재로서의 기능을 상실하게 된다.Bulletproof material breaks or cracks due to fragments of bullets or bombs, and thus loses its function as a bulletproof material.

따라서 이와 같은 방탄 소재의 기능을 최대한 오래 유지하고, 성능을 향상시키기 위하여,Therefore, in order to maintain the function of such a bulletproof material as long as possible, to improve performance,

방탄 소재를 하나의 단일체로 구성하는 것을 피하고, 여러 개의 조각으로 나누어 연결시켜 사용함으로써,Avoid using bulletproof materials as a single unit, and use them by dividing them into several pieces,

방탄 소재가 충격을 받았을 때, 충격이 방탄 소재 전체로 파급되는 것을 피하고, 충격을 받은 부분만으로 한정되게 하여, 파손 범위를 최소화할 수 있게 하고 있다.When the bulletproof material is impacted, the impact is prevented from spreading to the entire bulletproof material, and limited to only the impacted part, thereby minimizing the damage range.

그 한 예로서, 대략 3 - 5 cm 크기의 세라믹판을 다수 연결하여 붙이거나, 또는 구형의 세라믹볼을 여러 겹으로 접착시킨 방탄판을 방탄복이나 방탄 방패 등의 소재로 사용한 경우가 있으나,As an example, there are cases where a large number of ceramic plates of about 3-5 cm are connected and attached, or a bulletproof plate in which a plurality of spherical ceramic balls are bonded together is used as a body armor or a bulletproof shield.

이 경우, 방탄판이 일체로 된 것에 비해서는 수명을 어느 정도 길게 할 수 있으나,In this case, the service life can be extended to some extent as compared with the one in which the bulletproof plate is integrated.

방탄 소재로서의 근본적인 문제를 해결하기에는 여전히 미흡한 실정에 있었다.It was still insufficient to solve the fundamental problem as a bulletproof material.

본 발명은 이와 같은 종래의 방탄 소재가 갖고 있는 제반 문제점을 제거하기 위하여 연구된 것으로서,The present invention has been studied in order to remove all the problems of such a conventional bulletproof material,

본 발명의 목적은 방탄 소재에 총격이 가해지거나, 방탄 소재가 피폭을 받아 충격을 받았을 때,An object of the present invention is when the bulletproof material is shot, or when the bulletproof material is exposed and shocked,

방탄 소재가 파손되는 범위를 최소화시킬 뿐만 아니라, 방탄 소재의 수명을 오래 유지시킴과 동시에, 방탄 소재의 기능을 향상시켜, 우수한 품질의 방탄 소재를 보다 저렴한 가격으로 제공할 수 있도록 하는 데 있다.In addition to minimizing the extent to which the bulletproof material is damaged, the life of the bulletproof material is maintained for a long time, and the function of the bulletproof material is improved to provide a superior quality bulletproof material at a lower price.

본 발명의 또 다른 목적은 방탄 소재를 경량화하여, 사용에 간편함을 제공할 수 있게 하는 데 있다.Still another object of the present invention is to make the anti-ballistic material lighter, thereby providing convenience in use.

이를 위하여 본 발명은,To this end, the present invention,

세라믹볼을 소성 가공하여, 소성된 다수의 세라믹볼 주위에 세라믹 분말이 소성 가공되어 접착되게 세라믹볼을 일정한 두께의 판상으로 형성하여 방탄 소재를 제조함으로써,By firing the ceramic ball, by forming a ceramic ball in a plate shape of a certain thickness so that the ceramic powder is plastically processed and bonded around a plurality of fired ceramic balls, to produce a bulletproof material,

방탄 소재에 총격이 가해지거나, 방탄 소재가 피폭을 받았을 때,When the bulletproof material is shot or the bulletproof material is exposed,

탄환 또는 파편이 방탄 소재를 구성하고 있는 세라믹볼과 충돌한 뒤, 세라믹볼의 둥근 외주면과 접촉되어 빗겨 나가면서 그 충격을 완화시킬 수 있게 하여, 방탄 소재의 기능을 크게 향상시킬 수 있게 함과 동시에,The bullet or debris collides with the ceramic ball constituting the bulletproof material, and then comes into contact with the round outer circumferential surface of the ceramic ball so as to mitigate the impact, thereby greatly improving the function of the bulletproof material. ,

탄환 또는 파편의 충격이 탄환 또는 파편이 충돌된 방탄 소재의 세라믹볼에 국한되게 하여 파손 범위를 최소화시킴으로써, 방탄 소재의 수명을 보다 오래 유지시킬 수 있도록 하며,The impact of bullets or debris is limited to ceramic balls made of bulletproof materials in which bullets or debris are collided, thereby minimizing the scope of breakage, thereby maintaining the life of the bulletproof material longer.

세라믹볼의 사이 사이에 공극이 형성되어, 공극 내부에 세라믹 분말이 소성 가공되어 충진됨으로써, 방탄 소재의 강도가 강화되고, 경량화되어 사용에 보다 간편함을 제공할 수 있도록 한 것을 특징으로 한다.The voids are formed between the ceramic balls, and the ceramic powder is plastically processed and filled in the voids, so that the strength of the bulletproof material is strengthened, and the weight is reduced, thereby providing convenience in use.

본 발명의 방탄 소재는 방탄 소재에 총격이 가해지거나, 방탄 소재가 피폭을 받았을 때,When the bulletproof material of the present invention is shot on the bulletproof material or when the bulletproof material is exposed,

탄환 또는 파편이 방탄 소재를 구성하고 있는 세라믹볼과 충돌한 뒤, 탄환 또는 파편이 세라믹볼의 둥근 외주면과 접촉되어 빗겨 나가면서 그 충격을 완화시킴으로써, 방탄 소재의 기능을 크게 향상시킬 수 있게 함과 동시에,After the bullet or debris collides with the ceramic ball constituting the bulletproof material, the bullet or debris comes into contact with the round outer circumferential surface of the ceramic ball and mitigates its impact, thereby greatly improving the function of the bulletproof material. At the same time,

탄환 또는 파편의 충격이 탄환 또는 파편이 충돌된 방탄 소재의 세라믹볼에 국한되게 하여, 파손 범위를 최소화시킴으로써, 방탄 소재의 수명을 보다 오랜 기간 유지시킬 수 있도록 하며,The impact of bullets or debris is limited to ceramic balls made of bulletproof materials in which bullets or debris collides, minimizing the extent of breakage, thereby maintaining the life of the bulletproof material for a longer period of time,

세라믹볼의 사이 사이에 공극이 형성되어, 공극 내부에 세라믹 분말이 소성 가공되어 충진됨으로써, 방탄 소재의 강도가 강화되고, 경량화되어 사용에 보다 간편함을 제공할 수 있는 효과가 있다.The voids are formed between the ceramic balls, and the ceramic powder is plastically processed and filled in the voids, whereby the strength of the bulletproof material is strengthened, and the weight is reduced, thereby providing convenience in use.

이하 본 발명의 바람직한 실시예를 첨부 도면을 참조하여 구체적으로 설명하면 다음과 같다.Hereinafter, exemplary embodiments of the present invention will be described in detail with reference to the accompanying drawings.

도 1 은 본 발명의 종단면도,1 is a longitudinal cross-sectional view of the present invention;

도 2 는 본 발명의 구성 상태를 나타낸 부분 확대 종단면도,
도 3 은 본 발명의 방탄 소재에 탄환이 충돌했을 때의 작용 상태를 나타낸 부분 확대도로서,2 is a partially enlarged longitudinal sectional view showing a configuration state of the present invention;
3 is a partially enlarged view showing an operating state when a bullet impacts the bulletproof material of the present invention.

본 발명의 방탄 소재는,Bulletproof material of the present invention,

세라믹볼(1)을 직경 1 - 20 mm 로 소성 가공하여,The ceramic ball 1 is fired to a diameter of 1 to 20 mm,

소성된 세라믹볼(1)을 소성틀 내에 밀착되게 다져 넣은 뒤,After sintering the sintered ceramic ball (1) in close contact with the firing mold,

소성틀 내의 세라믹볼(1) 사이 사이에 형성된 공극(2)에 세라믹 분말(3)을 주입시킨 후,After injecting the ceramic powder (3) into the gap (2) formed between the ceramic balls (1) in the firing frame,

소성틀을 소성로 내에 넣고 소성시키면, 판상의 방탄판(5)이 성형된다.When the baking mold is put into a baking furnace and baked, the plate-shaped bulletproof board 5 is shape | molded.

이렇게 소성된 본 발명의 방탄 소재는,The bulletproof material of the present invention fired in this way,

방탄판(5)이 다수의 세라믹볼(1)에 의하여 밀착된 상태에서 세라믹볼(1) 사이 사이에 형성된 공극(2)에 세라믹 분말(3)이 소성 가공되어 충진되어 있기 때문에,Since the ceramic powder 3 is plastic-processed and filled in the space | gap 2 formed between ceramic balls 1 in the state in which the bulletproof board 5 was closely contacted with the several ceramic balls 1,

방탄판(5)에 총격이 가해지거나, 방탄판(5)이 피폭을 받았을 때,When shooting is applied to the bulletproof plate 5 or when the bulletproof plate 5 is exposed,

탄환 또는 파편이 방탄판(5)을 구성하고 있는 세라믹볼(1)과 충돌한 뒤, 세라믹볼(1)의 둥근 외주면과 접촉되어 빗겨 나가면서 그 충격이 크게 완화됨으로써,The impact is greatly alleviated while the bullet or the debris collides with the ceramic ball 1 constituting the bulletproof plate 5 and then comes into contact with the round outer circumferential surface of the ceramic ball 1 to be combed.

방탄 소재의 기능을 크게 향상시킬 수 있게 된다.The function of the bulletproof material can be greatly improved.

또한 탄환 또는 파편의 충격이 탄환 또는 파편이 충돌된 방탄판(5)의 세라믹볼(1) 또는 바로 옆에 인접해 있는 세라믹볼(1)에 국한되게 되어 파손 범위가 최소화됨으로써,In addition, the impact of the bullet or debris is limited to the ceramic ball 1 of the bulletproof plate 5 in which the bullet or the debris collides or the ceramic ball 1 adjacent to the adjacent one, thereby minimizing the damage range,

방탄 소재의 수명을 보다 오래 유지시킬 수 있게 되는 장점이 있다.The advantage is that the life of bulletproof material can be maintained longer.

또한 세라믹볼(1)의 사이 사이에 공극(2)이 형성되어 공극 내부에 세라믹 분말(3)이 소성 가공되어 충진됨으로써, 방탄판(5)의 강도가 크게 강화되고, 경량화되어 사용에 보다 간편함을 제공할 수 있는 잇점이 있다.In addition, the voids 2 are formed between the ceramic balls 1, and the ceramic powder 3 is plastically processed and filled in the voids, so that the strength of the bulletproof plate 5 is greatly strengthened, and the weight is reduced, making it easier to use. There are advantages that can be provided.

삭제delete

삭제delete

삭제delete

도 4 는 본 발명의 다른 실시예의 구성 상태를 나타낸 부분 종단면도로서,4 is a partial longitudinal cross-sectional view showing a configuration state of another embodiment of the present invention;

상기 세라믹볼(1)의 내부에 방탄 합성섬유볼(9)이 내장되어 소성된 구조로서,As a structure in which the bulletproof synthetic fiber ball 9 is built-in and fired in the ceramic ball 1,

세라믹볼(1) 전체가 세라믹으로 형성된 경우에 비하여, 방탄판(5)이 경량화되는 효과가 있다.Compared to the case where the whole ceramic ball 1 is made of ceramic, there is an effect that the bulletproof plate 5 is reduced in weight.

따라서 이와 같은 본 발명의 방탄 소재에 의하면,Therefore, according to such a bulletproof material of the present invention,

방탄 소재에 총격이 가해지거나, 방탄 소재가 피폭을 받았을 때,When the bulletproof material is shot or the bulletproof material is exposed,

탄환 또는 파편이 방탄 소재를 구성하고 있는 세라믹볼(1)과 충돌한 뒤, 세라믹볼(1)의 둥근 외주면과 접촉되어 빗겨 나가면서 그 충격을 완화시킬 수 있게 하여, 방탄 소재의 기능을 크게 향상시킬 수 있게 함과 동시에,The bullet or debris collides with the ceramic ball 1 constituting the bulletproof material, and then comes into contact with the round outer circumferential surface of the ceramic ball 1 to mitigate the impact, thereby greatly improving the function of the bulletproof material. At the same time,

탄환 또는 파편의 충격이 탄환 또는 파편이 충돌된 방탄 소재의 세라믹볼(1)에 국한되게 하여 파손 범위를 최소화시킴으로써, 방탄 소재의 수명을 보다 오래 유지시킬 수 있을 뿐만 아니라,By minimizing the damage range by limiting the impact of the bullet or fragments to the ceramic ball (1) of the bulletproof material in which the bullet or fragments collide, not only can maintain the life of the bulletproof material longer,

세라믹볼(1)의 사이 사이에 공극(2)이 형성되어 공극 내부에 세라믹 분말(3)이 소성 가공되어 충진됨으로써, 방탄판(5)의 강도가 강화되고, 경량화되어 사용에 간편함을 제공할 수 있는 장점이 있다.The voids 2 are formed between the ceramic balls 1, and the ceramic powders 3 are plastically processed and filled in the voids, so that the strength of the bulletproof plate 5 can be strengthened, and the weight of the bulletproof plate 5 can be easily provided. There is an advantage.

이상에서는 본 발명을 특정한 실시예에 의거하여 설명하였으나, 본 발명은 본 발명의 기술적 사상 내에서 여러 변형예가 가능하며, 상기 실시예 만으로 본 발 명의 기술적 범위가 한정되는 것은 물론 아니다.In the above, the present invention has been described based on specific embodiments, but the present invention may be modified in various ways within the technical idea of the present invention, and the technical scope of the present invention is not limited to the above embodiments.

도 1 은 본 발명의 종단면도,1 is a longitudinal cross-sectional view of the present invention;

도 2 는 본 발명의 구성 상태를 나타낸 부분 확대 종단면도,2 is a partially enlarged longitudinal sectional view showing a configuration state of the present invention;

도 3 은 본 발명의 방탄 소재에 탄환이 충돌했을 때의 작용 상태를 나타낸 부분 확대도,3 is a partially enlarged view showing an operating state when a bullet hits the bulletproof material of the present invention;

도 4 는 본 발명의 다른 실시예의 구성 상태를 나타낸 부분 종단면도.4 is a partial longitudinal cross-sectional view showing the construction of another embodiment of the present invention;

* 도면의 주요 부분에 대한 부호의 간단한 설명* Brief description of symbols for the main parts of the drawing

1 : 세라믹볼 1: ceramic ball

2 : 공극 2: void

3 : 세라믹 분말 3: ceramic powder

5 : 방탄판 5: bulletproof plate

삭제delete

9 : 방탄 합성섬유볼 9: ballistic synthetic fiber ball

Claims (3)

삭제delete 세라믹볼을 소성 가공하여, 소성된 다수의 세라믹볼이 밀착된 상태에서 일정한 두께의 판상으로 형성되고,By firing the ceramic ball, a plurality of fired ceramic balls are formed in a plate shape of a constant thickness in close contact, 상기 세라믹볼 주위에 세라믹 분말이 소성 가공되어 충진된 것을 특징으로 하는 방탄 소재.Ballistic material, characterized in that the ceramic powder is filled by plastic processing around the ceramic ball. 제 2 항에 있어서,The method of claim 2, 상기 세라믹볼의 내부에 방탄 합성섬유볼이 내장된 것을 특징으로 하는 방탄 소재.Bulletproof material, characterized in that the bulletproof synthetic fiber ball is built in the ceramic ball.
KR1020090073032A 2009-08-07 2009-08-07 Bulletproof material KR101054651B1 (en)