KR101054167B1 - Plating method of kitchen utensils - Google Patents
Plating method of kitchen utensils Download PDFInfo
- Publication number
- KR101054167B1 KR101054167B1 KR1020090069191A KR20090069191A KR101054167B1 KR 101054167 B1 KR101054167 B1 KR 101054167B1 KR 1020090069191 A KR1020090069191 A KR 1020090069191A KR 20090069191 A KR20090069191 A KR 20090069191A KR 101054167 B1 KR101054167 B1 KR 101054167B1
- Authority
- KR
- South Korea
- Prior art keywords
- base material
- protective layer
- kitchen
- kitchen utensils
- tce
- Prior art date
Abstract
본 발명에서는 각종 주방용품의 표면에 티타늄 또는 지르코늄을 미려하게 도금할 수 있도록 하되. 모재(母材)에 형성된 세라믹 또는 칠보의 장식문양은 전혀 손상되지 않도록 하면서 투톤(Two-tone)이상의 다양한 색상으로 아름답게 도금할 수 있도록 하여 제품의 고급화를 꾀할 수 있도록 한 새로운 주방용품의 도금방법이 개시된다.In the present invention, the surface of the various kitchen utensils to be beautifully plated with titanium or zirconium. The new kitchen utensils plating method is designed to upgrade the quality of the product by allowing the plating of ceramics or cloisonne formed on the base material to be beautifully plated in various colors of two-tone or more without being damaged at all. Is initiated.
본 발명은 주방용품 모재(母材)상에 세라믹전사 또는 칠보공예방식에 의하여 양각 또는 음각으로 형성된 장식문양부 또는 특정 부위에 용제나 잉크를 패드인쇄 또는 실크인쇄하고, 110∼130℃의 오븐에서 1∼3시간 동안 건조하는 보호층 형성단계와; 장식문양부에 보호층이 형성된 주방용품 모재를 알칼리 침전조에서 초음파세척하여 주방용품 모재에 묻어 있는 이물질을 제거하고, 이물질이 제거된 주방용품 모재를 다시 수세(水洗)하여 알칼리를 제거하며, 황산, 불산, 염산 과산화수소 및 물이 혼합된 산처리혼합물내에 수세된 주방용품 모재를 넣어 주방용품 모재에 밀착되어 있는 산화막과 이물질을 제거하고 수세한 후 건조시키는 전처리단계와; 전처리과정을 거친 주방용품 모재를 염소계 용제인 트리클로로에틸렌(T.C.E : Trichloroethylene)조에 침전시킨 상태에서 5∼7분 동안 초음파세척하여 주방용품 모재의 장식문양부에 형성된 보호층을 제거한 다음 건조시키는 1차 보호층 제거단계와; 장식문양부상의 보호층이 제거된 주방용품 모재를 염소계 용제의 일종인 메타크린(Metha Clean)용액에 넣어 주방용품 모재에 잔류하는 물기를 제거함과 동시 에 T.C.E성분을 완전하게 분해한 후 건조시키는 T.C.E성분제거 단계와; T.C.E성분이 제거된 주방용품 모재를 지그에 장착시킨 상태에서 히터조내에서 30∼40분 동안 가열하고, 가열된 상태의 주방용품 모재를 10-4∼10-5Torr의 진공도로 유지되고, 지르코늄 또는 티타늄을 증발재료로 하는 진공관내에 투입한 상태에서 열을 가하여 플라즈마현상에 의하여 증발된 양이온 상태의 증발재료가 음이온을 띠는 주방용품 모재의 표면에 증착되도록 하는 방식으로 30∼40분 동안 도금하는 진공이온증착 도금단계와; 지르코늄 또는 티타늄 도금된 주방용품 모재를 냉각조에 넣고 20∼30분 동안 냉각시키는 주방용품 모재 냉각단계와; 지르코늄 또는 티타늄으로 진공이온증착 도금된 후 냉각된 주방용품 모재를 지그에 장착한 상태에서 T.C.E와 메타크린이 채워진 침전조에 넣고 5∼10분 동안 초음파세척하여 장식문양부상의 보호층에 잔류하는 용제나 잉크를 제거하는 2차 보호층 제거단계와; 2차 보호층 제거단계를 거친 주방용 모재를 메타크린 침전조에 넣어 용제와 T.C.E를 완전하게 분리한 후 이를 다시 T.C.E침전조를 통과시키면서 건조시키는 최종 건조단계로 이루어진다. The present invention is pad printing or silk printing a solvent or ink on a decorative pattern or a specific portion formed by embossing or engraving by ceramic transfer or lacquer craft method on the kitchenware base material, and in the oven at 110 ~ 130 ℃ Forming a protective layer which is dried for 1 to 3 hours; Ultrasonic cleaning of kitchen utensils with a protective layer formed on the decorative doors in an alkali precipitation tank removes foreign substances from kitchen utensils, and washes the kitchen utensils from which foreign substances have been removed to remove alkalis, sulfuric acid, A pretreatment step of putting the washed kitchen utensil base material in an acid treatment mixture mixed with hydrofluoric acid, hydrochloric acid hydrogen peroxide, and water to remove the oxide film and the foreign matter adhering to the kitchen utensil base material, followed by washing with water and drying; After pretreatment, the kitchenware base material is ultrasonically washed for 5 to 7 minutes in a state of being precipitated in a chlorine-based trichloroethylene (TCE) bath to remove the protective layer formed on the decorative pattern of the kitchenware base material and then dried. Removing the protective layer; TCE which removes moisture remaining in kitchen utensils by putting the kitchen utensil base material with the protective layer on the decorative pattern removed in the Metha Clean solution which is a kind of chlorine-based solvent. Ingredient removal step; The kitchenware base material from which the TCE component is removed is mounted on a jig and heated for 30 to 40 minutes in a heater bath, and the heated kitchenware base material is maintained at a vacuum of 10 -4 to 10 -5 Torr, and zirconium or Vacuum plated for 30 to 40 minutes in such a way that the evaporation material in the cation state evaporated by the plasma phenomenon is deposited on the surface of the base material of an anionic kitchen utensil by applying heat while the titanium is introduced into a vacuum tube made of evaporation material. Ion deposition plating step; A kitchenware base material cooling step of placing a zirconium or titanium plated kitchenware base material in a cooling bath for 20 to 30 minutes; After vacuum ion evaporation plating of zirconium or titanium, the cooled kitchen utensils were placed in a jig, and then placed in a settling tank filled with TCE and methaclean and ultrasonically cleaned for 5 to 10 minutes. A second protective layer removing step of removing ink; Put the kitchen base material after the second protective layer is removed in the methacrylate precipitation tank to completely separate the solvent and TCE, and then it is composed of the final drying step to dry while passing through the TCE precipitation tank again.
주방용품, 도금, 장식문양, 보호층, 진공이온증착 도금 Kitchen utensils, plating, decorative patterns, protective layer, vacuum ion deposition plating
Description
본 발명은 주방용품의 도금방법에 관한 것으로, 더욱 상세하게는 숟가락이나 젓가락 같이 스테인레스스틸재로 만들어지며 손잡이 등 부분적으로 세라믹전사방식또는 칠보공예방식에 의하여 다양한 형태의 장식 문양(紋樣)이 양각(陽刻) 또는 음각(陰刻)되어 있는 각종 주방용품의 표면에 티타늄 또는 지르코늄을 미려하게 도금할 수 있도록 하되. 모재(母材)에 형성된 세라믹 또는 칠보의 장식문양은 전혀 손상되지 않도록 하면서 투톤(Two-tone)이상의 다양한 색상으로 아름답게 도금할 수 있도록 하여 제품의 고급화를 꾀할 수 있도록 한 주방용품의 도금방법에 관한 것이다. The present invention relates to a plating method of kitchen utensils, and more particularly, made of stainless steel materials such as spoons and chopsticks, and embossed with various forms of decorative patterns (紋樣) by a ceramic transfer method or a cloisonne craft method, such as a handle. Titanium or zirconium should be plated on the surface of various kitchen utensils that are either positive or engraved. The ceramic or cloisonne pattern formed on the base metal can be plated beautifully in various colors of two-tone or more, without damaging it. will be.
일반적으로, 숟가락이나 젓가락 같은 주방용품은 음식물을 조리하거나 조리된 음식물을 뜨거나 집는데 사용되는 도구로서, 우리 식생활에서 필수적인 제품이다. In general, kitchen utensils such as spoons and chopsticks are tools used to cook food or to cook or cook cooked foods, which are essential products in our diet.
이와 같은 주방용품은 각종 음식물과 빈번하게 접촉되는 방식으로 사용되는 것이기 때문에 녹이 발생되거나 쉽게 부식되지 않는 등 위생성과 내식성(耐蝕性)이 확실히 보장되어야 하고, 한번 구입하면 장기간 사용되는 것이 보통이기 때문에 내 구성(耐久性)과 내마모성(耐磨耗性)이 확보되어야 함에 따라 최근에 판매되는 주방용품, 특히 숟가락과 젓가락류는 주로 스테인레스스틸재로 제조되고 있다.Since such kitchen utensils are used in a manner of frequent contact with various foods, hygiene and corrosion resistance must be assured, such as rust or corrosion, and once purchased, they are usually used for a long time. As the composition and abrasion resistance have to be secured, kitchen utensils, especially spoons and chopsticks, which are recently sold, are mainly made of stainless steel.
또한, 상기와 같이 스테인레스스틸재로 만들어지는 주방용품의 본체부와 손잡이부에는 음식을 먹고 장수하라는 의미의 '壽'자, 복을 많이 받으라는 의미의 '福'자 같은 기복문자(祈福文字) 또는 그 기능상 천편일률적인 형상을 갖는 주방용품을 보다 아름답고 고급스러워 보이도록 하고 시장에서의 경쟁력을 높이기 위하여 별도로 디자인된 장식문양을 세라믹전사방식 또는 칠보공예방식으로 양각(陽刻) 또는 음각(陰刻)형태로 형성하고 있다.In addition, the main body and the handle portion of the kitchen utensils made of stainless steel as described above, such as '자' means to eat food and long life, 'Fuku' character means to receive a lot of blessings (祈福 文字) Or, in order to make kitchen utensils with a uniform shape in terms of function more beautiful and luxurious, and to increase the competitiveness in the market, the decorative patterns designed separately are embossed or engraved in the form of ceramic transfer or cloisonne craft. Forming.
한편, 최근에는 위와 같이 스테인레스스틸재로 만들어지는 주방용품의 표면에 더욱 고급스러운 느낌의 금빛색상이 발현되도록 도금하는 기술이 제안되고 있다. On the other hand, in recent years, a technique has been proposed to plate the gold color of the more luxurious feeling on the surface of the kitchen appliances made of stainless steel as described above.
이와 같은 주방용품에 대한 도금방법으로는 습식도금방법과 건식도금방법을 들 수 있는바, 습식도금방법은 금속염의 용액을 전해액으로 하여 양극에는 피복제의 금속을, 음극에는 도금될 제품을 연결하여 직류를 통하면 전기분해에 의한 양이온이 음극인 제품에 부착되는 방식으로서 도금 전에 제품의 표면을 산용액으로 세척하고, 도금 후에는 온수로 세척하여야 하는 등의 후처리가 필요하다.The plating method for such kitchen utensils may be a wet plating method or a dry plating method. In the wet plating method, a metal salt solution is used as an electrolyte and a coating metal is connected to the anode, and a product to be plated is connected to the cathode. If direct current is applied, the cation by electrolysis is attached to the product, which is a negative electrode. After the plating, the surface of the product needs to be washed with an acid solution, and after plating, it is necessary to wash with warm water.
또, 상기 건식도금방법은 Sn, Zn, Pb, Al 같은 피복제의 용융금속에 제품을 넣어서 피복하는 방법으로서 이 방법은 제품의 미관보다는 제품이 부식되지 않도록 하기 위하여 주로 사용되고 있다. In addition, the dry plating method is a method of coating the product by coating the molten metal of the coating material such as Sn, Zn, Pb, Al, this method is mainly used to prevent the product from corroding rather than the appearance of the product.
종래의 주방용품의 도금방법에서는 제품의 외관이 투톤(Two-tone)이상의 다 양한 색상으로 발현되도록 하기 위하여 다른 색상의 도금원료를 반복하여 도금하는 습식도금법이 주로 사용되는데, 이 경우 다양한 색상의 연출이 불가능할 뿐만 아니라 그 공정이 매우 복잡하여 효율성과 생산성이 떨어진다는 문제가 있다.In the conventional plating method of kitchen utensils, a wet plating method of repeatedly plating plating materials of different colors is mainly used in order to make the appearance of the product appear in various colors of two-tone or more. In this case, various colors are produced. Not only is this impossible, but the process is so complicated that the efficiency and productivity is low.
또, 상기한 습식도금방법의 경우 도금과정에서 사용되는 화학약품으로 인하여 환경이 크게 오염될 수 있다는 심각한 문제가 제기되고 있으며, 이를 개선하기 위해서는 많은 비용을 들여 별도의 정화시설을 설치하여야 하기 때문에 생산비가 크게 상승된다는 문제가 있는 것이다. In addition, in the wet plating method, a serious problem has been raised that the environment may be greatly polluted by the chemicals used during the plating process. There is a problem that is greatly increased.
본 발명은 이와 같은 종래의 문제점을 해결하기 위한 것으로, 그 목적은 각종 주방용품의 표면에 티타늄 또는 지르코늄을 미려하게 도금할 수 있도록 하되, 주방용품 모재(母材)에 형성된 세라믹 또는 칠보의 장식문양은 전혀 손상되지 않도록 하면서 투톤(Two-tone)이상의 다양한 색조로 아름답게 도금할 수 있도록 하여 제품의 고급화를 꾀함과 동시에 소비자의 요구에 맞추어 제품의 다양화를 꾀할 수 있도록 한 새로운 주방용품의 도금방법을 제공하는 것이다. The present invention is to solve such a conventional problem, its purpose is to be able to plate titanium or zirconium beautifully on the surface of various kitchen utensils, the decorative pattern of ceramic or cloisonne formed on the kitchen utensil base (母 材) The new kitchen utensil plating method is designed to make the product beautifully plated in various shades of two-tone or more without being damaged at all, and to diversify the product to meet the needs of consumers. To provide.
상기의 목적을 달성하기 위하여, 본 발명에 따른 주방용품의 도금방법은 스테인레스스틸재 주방용품 모재(母材)상에 세라믹전사 또는 칠보공예방식에 의하여 양각 또는 음각으로 형성된 장식문양부에 용제나 잉크를 패드인쇄 또는 실크인쇄하고, 110∼130℃의 오븐에서 1∼3시간 동안 건조하는 보호층 형성단계와; 장식문양부에 보호층이 형성된 주방용품 모재를 알칼리 침전조에서 초음파세척하여 주방용품 모재에 묻어 있는 이물질을 제거하고, 이물질이 제거된 주방용품 모재를 다시 수세(水洗)하여 알칼리를 제거하며, 황산, 불산, 염산 과산화수소 및 물이 혼합된 산처리혼합물내에 수세된 주방용품 모재를 넣어 주방용품 모재에 밀착되어 있는 산화막과 이물질을 제거하고 수세한 후 건조시키는 전처리단계와; 전처리과정을 거친 주방용품 모재를 염소계 용제인 트리클로로에틸렌(T.C.E : Trichloroethylene)조에 침전시킨 상태에서 5∼7분 동안 초음파세척하여 주방용품 모재의 장식문양부에 형 성된 보호층을 제거한 다음 건조시키는 1차 보호층 제거단계와; 장식문양부상의 보호층이 제거된 주방용품 모재를 염소계 용제의 일종인 메타크린(Metha Clean)용액에 넣어 주방용품 모재에 잔류하는 물기를 제거함과 동시에 T.C.E성분을 완전하게 분해한 후 건조시키는 T.C.E성분제거 단계와; T.C.E성분이 제거된 주방용품 모재를 지그에 장착시킨 상태에서 히터조내에서 30∼40분 동안 가열하고, 가열된 상태의 주방용품 모재를 10-4∼10-5Torr의 진공도로 유지되고, 지르코늄 또는 티타늄을 증발재료로 하는 진공관내에 투입한 상태에서 열을 가하여 플라즈마현상에 의하여 증발된 양이온 상태의 증발재료가 음이온을 띠는 주방용품 모재의 표면에 증착되도록 하는 방식으로 30∼40분 동안 도금하는 진공이온증착 도금단계와; 지르코늄 또는 티타늄 도금된 주방용품 모재를 냉각조에 넣고 20∼30분 동안 냉각시키는 주방용품 모재 냉각단계와; 지르코늄 또는 티타늄으로 진공이온증착 도금된 후 냉각된 주방용품 모재를 지그에 장착한 상태에서 T.C.E와 메타크린이 채워진 침전조에 넣고 5∼10분 동안 초음파세척하여 장식문양부상의 보호층에 잔류하는 용제나 잉크를 제거하는 2차 보호층 제거단계와; 2차 보호층 제거단계를 거친 주방용 모재를 메타크린 침전조에 넣어 용제와 T.C.E를 완전하게 분리한 후 이를 다시 T.C.E침전조를 통과시키면서 건조시키는 최종 건조단계를 포함한다.In order to achieve the above object, the plating method of the kitchen utensils according to the present invention is a solvent or ink on the decorative door formed in the embossed or intaglio on the stainless steel kitchen utensil base material by ceramic transfer or cloisonne craft method Pad printing or silk printing, and a protective layer forming step of drying for 1 to 3 hours in an oven at 110 ~ 130 ℃; Ultrasonic cleaning of kitchen utensils with a protective layer formed on the decorative doors in an alkali precipitation tank removes foreign substances from kitchen utensils, and washes the kitchen utensils from which foreign substances have been removed to remove alkalis, sulfuric acid, A pretreatment step of putting the washed kitchen utensil base material in an acid treatment mixture mixed with hydrofluoric acid, hydrochloric acid hydrogen peroxide, and water to remove the oxide film and the foreign matter adhering to the kitchen utensil base material, followed by washing with water and drying; After pretreatment, the kitchenware base material is ultrasonically washed for 5 to 7 minutes while precipitated in a chlorine-based trichlorethylene bath to remove the protective layer formed on the decorative pattern of the kitchenware base material, and then dried. Removing the primary protective layer; TCE ingredient that removes water left in kitchen utensils by putting the kitchen utensil base material with the protective layer on the decorative pattern removed in the Metha Clean solution, a kind of chlorine-based solvent, and completely decomposes and dries the TCE element. A removing step; The kitchenware base material from which the TCE component is removed is mounted on a jig and heated for 30 to 40 minutes in a heater bath, and the heated kitchenware base material is maintained at a vacuum of 10 -4 to 10 -5 Torr, and zirconium or Vacuum plated for 30 to 40 minutes in such a way that the evaporation material in the cation state evaporated by the plasma phenomenon is deposited on the surface of the base material of an anionic kitchen utensil by applying heat while the titanium is introduced into a vacuum tube made of evaporation material. Ion deposition plating step; A kitchenware base material cooling step of placing a zirconium or titanium plated kitchenware base material in a cooling bath for 20 to 30 minutes; After vacuum ion evaporation plating of zirconium or titanium, the cooled kitchen utensils were placed in a jig, and then placed in a settling tank filled with TCE and methaclean and ultrasonically cleaned for 5 to 10 minutes. A second protective layer removing step of removing ink; It includes a final drying step of putting the kitchen base material, which has undergone the second protective layer removal step, into the methaclean precipitation tank to completely separate the solvent and the TCE, and then drying it again through the TCE precipitation tank.
본 발명에서 상기 최종 건조단계를 거쳐 도금완료된 주방용품 모재의 특정 부분 표면에 설계에 따라 정해진 형상의 문양을 레이져가공하되, 레이져가공된 부분이 주방용품 모재의 재료인 스테인레스스틸이 드러나도록 하여 도금된 부분과 레 이져가공된 부분의 색상이 서로 다르게 발현(發顯)되도록 하는 레이져가공단계를 포함하는 특징을 갖는다. In the present invention, the laser processing a pattern of a predetermined shape according to the design on the surface of the specific part of the kitchen utensil base material plated through the final drying step, the laser processed portion is plated to reveal the stainless steel material of the kitchen utensil base material It is characterized by including a laser processing step for causing the color of the portion and the laser processed portion to be expressed differently.
본 발명을 적용하면, 숟가락이나 젓가락 같이 스테인레스스틸재로 만들어지 며 손잡이 등에 세라믹전사방식 또는 칠보공예방식에 의하여 다양한 형태의 장식 문양(紋樣)이 양각(陽刻) 또는 음각(陰刻)되어 있는 각종 주방용품을 지르코늄이나 티타늄으로 도금하는 과정에서 주방용품 모재상에 형성된 장식문양부를 보호할 수 있도록 전처리한 상태에서 지르코늄이나 티나늄을 증발재료로 하여 진공이온증방식으로 도금함으로써 주방용품 모재상의 세라믹 또는 칠보의 장식문양은 전혀 손상되지 않도록 하면서 다양하고 아름답게 도금할 수 있다는 효과가 있다. According to the present invention, various kitchens are made of stainless steel materials such as spoons and chopsticks, and various patterns of decorative patterns are embossed or engraved by ceramic transfer method or cloisonne craft method. In order to protect the decorative pattern formed on the base material of kitchen utensils in the process of plating the product with zirconium or titanium, the ceramic or cloisonne on the base of kitchen utensils is plated by vacuum ion deposition method using zirconium or titanium as evaporation material. The decorative pattern of the effect is that it can be plated variously and beautifully without being damaged at all.
또, 도금이 완료된 주방용품 모재의 특정부위에 대하여 내부의 스테인레스스틸재의 색상이 드러나도록 레이져가공하면 도금된 부분과 레이져가공된 부분의 색상이 서로 다르게 발현(發顯)되기 때문에 주방용품이 투톤(Two tone)색상을 갖게 되면서 아름답고 고급스러운 느낌의 제품이 되어 경쟁력이 제고된다는 효과가 있다.In addition, when the laser processing is performed to reveal the color of the stainless steel material inside for the specific part of the base material of the kitchen utensil that has been plated, the color of the plated part and the laser processed part is different from each other. Two tone) has the effect of enhancing the competitiveness by becoming a beautiful and luxurious product with color.
또, 주방용품 모재에서 장식문양부가 아닌 다른 부위에 대하여 다양한 모양으로 용제나 잉크를 인쇄한 상태에서 전처리한 후 진공이온증착도금하는 과정을 반복하면, 투 톤 이상의 색조를 띠는 주방용품의 도금이 가능하기 때문에 소비자의 요구에 맞추어 제품의 다양화를 꾀할 수 있다는 효과가 있다. In addition, if you repeat the process of pre-treatment of vacuum ion deposition after printing solvents or inks in various shapes for other parts of kitchen utensils other than decorative patterns, plating of kitchen utensils having a color tone of two or more tones is performed. It is possible to diversify the product to meet the needs of consumers.
이하, 첨부된 도면에 의하여 본 발명의 바람직한 실시예를 보다 상세하게 설명한다.Hereinafter, preferred embodiments of the present invention will be described in detail with reference to the accompanying drawings.
도 1은 본 발명에 따른 주방용품의 도금방법을 나타내는 공정도이다.1 is a process chart showing a plating method of kitchen appliances according to the present invention.
이를 참조하면, 본 발명은 주방용품 모재(母材)에 형성된 세라믹 또는 칠보의 장식문양은 전혀 손상되지 않도록 하면서 다양하고 아름답게 도금할 수 있도록 하여 제품의 고급화를 꾀할 수 있도록 하는 것이다. Referring to this, the present invention is to allow the decorative pattern of the ceramic or cloisonne formed on the kitchenware base material (母 材) to be variously and beautifully plated without damaging at all, so as to improve the quality of the product.
이를 위하여, 본 발명에 따른 주방용품의 도금방법은 주방용품 모재에 형성된 장식문양부에 대한 보호층 형성단계(ST1)와, 전처리단계(ST2)와, 1차 보호층제거단계(ST3)와, T.C.E성분 제거단계(ST4)와, 진공이온증착 도금단계(ST5)와, 주방용품 모재 냉각단계(ST6)와, 2차 보호층제거단계(ST7) 및 최종 건조단계(ST8)로 이루어지며, 필요에 따라 상기 최종 건조단계(ST8) 이후에 주방용품 모재의 특정 부위에 문양을 가공하는 레이져가공단계(ST9)가 더 포함될 수 있도록 구성된다. To this end, the plating method of the kitchen utensils according to the present invention is a protective layer forming step (ST1), pre-treatment step (ST2), the first protective layer removing step (ST3) for the decorative door formed on the base material kitchen utensils, TCE component removal step (ST4), vacuum ion deposition plating step (ST5), kitchenware base material cooling step (ST6), secondary protective layer removal step (ST7) and the final drying step (ST8), According to the final drying step (ST8) after the laser processing step (ST9) for processing the pattern on a specific portion of the base material kitchenware is configured to be further included.
본원발명의 보호층 형성단계(ST1)에서는 숟가락이나 젓가락 같이 스테인레스스틸재로 만들어지는 주방용품 모재(母材)상의 장식문양부 또는 특정 부위에 대하여 용제나 잉크를 패드인쇄방식이나 실크인쇄방식으로 인쇄하고, 이를 110∼130℃의 오븐에서 1∼3시간 동안 유지시키는 방식으로 건조하여 해당 부위에 보호층이 형성되도록 한다. In the protective layer forming step (ST1) of the present invention, a solvent or ink is printed by pad printing or silk printing on a decorative pattern or a specific portion of a kitchen material base material made of stainless steel such as a spoon or chopsticks. Then, it is dried in a manner of maintaining for 1 to 3 hours in an oven at 110 ~ 130 ℃ to form a protective layer on the site.
상기의 용제나 잉크의 보호층은 주방용품 모재상에 세락믹전사 방식 또는 칠보공예방식에 의하여 양각 또는 음각형태로 형성된 장식문양부에 도포되어 도금과정에서 장식문양부를 보호할 수 있도록 한다.The protective layer of the solvent or ink is applied to the decorative pattern formed in the embossed or engraved form on the kitchenware base material by ceramic transfer method or lacquer craft method to protect the decorative pattern during the plating process.
주방용품 모재의 표면에 투 톤(Two-tone)이상의 색조로 도금하고자 하는 경우 장식문양부가 형성되어 있지 않은 주방용품 모재의 표면에 별도로 디자인된 형태에 따라 용제나 잉크를 패드인쇄 또는 실크인쇄방식으로 도포할 수 있다.If you want to plate more than two-tone color on the surface of kitchen utensils base, you can use pad printing or silk printing method according to the shape designed separately on the surface of kitchen utensils without decorative pattern. It can be applied.
본 발명의 전처리단계(ST2)에서는 장식문양부 또는 특정 부위에 용제나 잉크의 보호층이 형성된 주방용품 모재를 알칼리침전조에 침전시킨 상태에서 초음파세척하여 주방용품 모재의 표면에 달라붙어 있는 이물질이 제거되도록 하고, 이물질이 제거된 주방용품 모재를 다시 수세(水洗)하여 알칼리성분을 제거한다.In the pretreatment step (ST2) of the present invention, foreign matters that adhere to the surface of the kitchenware base material are removed by ultrasonic cleaning in a state where the decorative pattern or the kitchenware base material having a protective layer of a solvent or ink formed on a specific portion is precipitated in an alkali precipitation tank. In addition, the kitchenware base material from which the foreign substances have been removed is washed again with water to remove the alkali component.
또, 알칼리성분이 제거된 주방용품 모재를 산처리혼합물내에 넣어 주방용품 모재에 밀착되어 있는 산화막과 이물질이 제거되도록 한 다음 이를 다시 수세하고 건조시킨다. 상기 전처리단계(ST2)에서 적용되는 산처리혼합물은 황산, 불산, 염산, 과산화수소 및 물을 각각 정해진 비율로 혼합한 것이 사용된다.In addition, the kitchenware base material from which the alkali component is removed is put in an acid treatment mixture to remove the oxide film and the foreign matter adhered to the kitchenware base material, and then washed again with water and dried. The acid treatment mixture applied in the pretreatment step (ST2) is a mixture of sulfuric acid, hydrofluoric acid, hydrochloric acid, hydrogen peroxide and water in a predetermined ratio.
본 발명의 1차 보호층제거단계(ST3)에서는 주방용품 모재의 장식문양부 또는 특정부위에 형성된 보호층을 제거하게 된다. In the first protective layer removing step (ST3) of the present invention to remove the protective layer formed on the decorative pattern or a specific portion of the kitchen material base material.
이를 위하여 상기의 전처리단계를 거친 주방용품 모재를 염소계 용제인 트리클로로에틸렌(T.C.E : Trichloroethylene)조에 침전시키고, 5∼7분 동안 초음파세척하고 건조하면 상기 주방용품 모재의 장식문양부 또는 특정부위에 형성된 보호층이 제거된다. To this end, the kitchen utensil base material subjected to the above pretreatment step is precipitated in a trichlorethylene (TCE: Trichloroethylene) bath which is a chlorine-based solvent, and ultrasonic cleaning and drying for 5 to 7 minutes is formed on the decorative pattern or specific part of the kitchen utensil base material. The protective layer is removed.
한편, 본 발명의 T.C.E성분 제거단계(ST4)에서 장식문양부상의 보호층이 제거된 주방용품 모재를 염소계 용제의 일종인 메타크린(Metha Clean)용액에 침전시키면 주방용품 모재에 잔류하는 물기가 제거됨과 동시에 T.C.E성분이 완전하게 분 해되어 제거되며, 이 상태에서 건조시킨다. On the other hand, in the TCE component removal step (ST4) of the present invention, when the kitchen utensil base material from which the protective layer on the decorative pattern is removed is precipitated in the Metha Clean solution, which is a kind of chlorine-based solvent, water remaining in the kitchen utensil base material is removed. At the same time, the TCE component is completely dissolved and removed, and dried in this state.
이와 같이 T.C.E성분이 제거된 주방용품 모재에 대하여 상기 진공이온증착 도금단계(ST5)를 통하여 도금과정을 수행한다.Thus, the plating process is performed through the vacuum ion deposition plating step (ST5) for the kitchen utensil base material from which the T.C.E component is removed.
이를 위하여 T.C.E성분이 제거된 주방용품 모재를 지그에 장착시킨 상태에서 히터조내에서 30∼40분 동안 가열하고, 가열된 상태의 주방용품 모재를 10-4∼10-5Torr의 진공도로 유지되고, 지르코늄 또는 티타늄을 증발재료로 하는 진공관내에 투입한 상태에서 열을 가하면, 진공관내에서 플라즈마현상에 의하여 증발된 양이온 상태의 증발재료가 음이온을 띠는 주방용품 모재의 표면에 증착되도록 하는 방식으로 30∼40분 동안 도금하면 주방용품 모재의 표면에 지르코늄 또는 티타늄이 고르게 도금된다.To this end, the kitchen appliance base material from which the TCE component is removed is mounted on a jig and heated for 30 to 40 minutes in a heater bath, and the heated kitchen utensil base material is maintained at a vacuum of 10 -4 to 10 -5 Torr. When heat is applied in a vacuum tube made of zirconium or titanium as an evaporation material, 30 to 30 are evaporated by the plasma phenomenon in the vacuum tube so that the evaporation material in the cation state is deposited on the surface of the anion-containing kitchenware base material. After 40 minutes of plating, the surface of the base of the kitchen utensils is evenly plated with zirconium or titanium.
그런 다음, 상기의 진공이온증착 도금단계(ST5)를 통하여 표면에 지르코늄 또는 티타늄이 도금된 주방용품 모재를 냉각조에 넣고 20∼30분 동안 냉각시키면 는 상기의 주방용품 냉각단계(ST6)가 수행된다.Then, through the vacuum ion deposition plating step (ST5) to put the kitchenware base material plated with zirconium or titanium on the surface in the cooling bath and cooled for 20 to 30 minutes, the kitchenware cooling step (ST6) is performed. .
본 발명의 2차보호층제거단계(ST7)에서는 지르코늄 또는 티타늄으로 진공이온증착 도금된 후 냉각된 주방용품 모재를 지그에 장착한 상태에서 T.C.E와 메타크린이 채워진 침전조에 넣고 5∼10분 동안 초음파세척하여 장식문양부상의 보호층에 잔류하는 용제나 잉크를 제거하게 되며, 이 후 최종 건조단계(ST8)에서는 주방용 모재를 메타크린 침전조에 넣어 용제와 T.C.E를 완전하게 분리한 후 이를 다시 T.C.E침전조를 통과시키면서 건조시켜 지르코늄 또는 티타늄이 도금된 주방용품이 얻어지는 것이다.In the secondary protective layer removing step (ST7) of the present invention, vacuum ion deposition plated with zirconium or titanium and then placed in a jig with a cooled kitchen utensil base material in a jig filled with TCE and methacrylate filled sedimentation tank for 5 to 10 minutes After washing, the solvent or ink remaining in the protective layer on the decorative pattern is removed, and then, in the final drying step (ST8), the kitchen base material is placed in a methacrylic sedimentation tank to completely separate the solvent and the TCE, and then the TCE sedimentation tank is again used. It is dried while passing to obtain a kitchen utensil plated with zirconium or titanium.
본 발명에서 상기 최종 건조단계(ST8)를 거쳐 도금완료된 주방용품 모재에대하여는 그 특정 부분의 표면에 설계에 따라 정해진 형상의 문양을 레이져가공하는 단계(ST9)가 포함될 수 있다. In the present invention, the kitchenware base material plated through the final drying step (ST8) may include a step (ST9) of laser processing a pattern of a predetermined shape according to the design on the surface of the specific portion.
상기 레이져가공단계(ST9)를 거쳐 주방용품의 특정 부위가 레이져에 의하여 가공되면 가공된 부분이 주방용품 모재의 재료인 스테인레스스틸이 드러나기 때문에 지르코늄 또는 티타늄에 의하여 도금된 부분과 레이져가공된 부분의 색상이 서로 다르게 발현(發顯)되면서 투톤(Two-tone)의 색조를 갖는 아름다운 색상의 주방용품이 얻어질 수 있게 되는 것이다. When the specific part of the kitchen utensil is processed by the laser through the laser processing step (ST9), the processed part is exposed to stainless steel, which is the material of the kitchen utensil base material, and the color of the part coated with zirconium or titanium and the laser processed part. This different expression (발현) will be able to obtain a beautiful color kitchen utensils having a two-tone color tone.
도 1은 본 발명에 따른 주방용품의 도금방법을 나타내는 공정도이다.1 is a process chart showing a plating method of kitchen appliances according to the present invention.
Claims (2)