KR101049522B1 - Manufacturing method of luminous gutter - Google Patents

Manufacturing method of luminous gutter Download PDF

Info

Publication number
KR101049522B1
KR101049522B1 KR1020090106738A KR20090106738A KR101049522B1 KR 101049522 B1 KR101049522 B1 KR 101049522B1 KR 1020090106738 A KR1020090106738 A KR 1020090106738A KR 20090106738 A KR20090106738 A KR 20090106738A KR 101049522 B1 KR101049522 B1 KR 101049522B1
Authority
KR
South Korea
Prior art keywords
mother
luminous
pearl
layer
drying
Prior art date
Application number
KR1020090106738A
Other languages
Korean (ko)
Other versions
KR20110049956A (en
Inventor
정병훈
유중기
Original Assignee
유중기
정병훈
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 유중기, 정병훈 filed Critical 유중기
Priority to KR1020090106738A priority Critical patent/KR101049522B1/en
Publication of KR20110049956A publication Critical patent/KR20110049956A/en
Application granted granted Critical
Publication of KR101049522B1 publication Critical patent/KR101049522B1/en

Abstract

본 발명은 빛이 없는 어두운 장소에서도 야광의 은은한 빛에 의하여 고급스럽고 우아하며 아름다운 나전칠기 고유의 멋을 느낄 수 있는 야광자개판의 제조방법에 관한 것으로,The present invention relates to a method of manufacturing a luminous gutter plate that can feel the luxury of elegant, elegant and beautiful Na Lacquerware by the soft light of luminous even in a dark place without light,

구체적으로는 본 발명은 선택된 백색 및 청록색을 띠는 조개껍질을 세척·이물질제거·절단 등 통상의 과정으로 가공하여 정선된 조개껍질 조각들을 이형지 위에 빈틈없이 배열하고 그 상면에 접착성 수지액을 도포한 후 압착하고 건조한 후 이형지를 제거하여 자개판을 형성하는 공정과, Specifically, the present invention is to process the selected white and turquoise shells by the usual procedures, such as washing, removing foreign matters, cutting, arranged carefully arranged shell pieces on a release paper and apply the adhesive resin liquid on the upper surface After pressing and drying to remove the release paper to form a mother-of-pearl;

상기의 자개판의 이면 및 표면을 평편하게 연마하여 박판상의 자개기판을 만드는 공정과,A process of making a thin mother-of-pearl board by grinding the back and the surface of the mother-of-pearl plate flat;

상기 수지층이 경화되고 연마된 자개기판의 이면에 락커를 도포하고 건조하여 자개무늬의 투명도를 높이는 락커도포공정과,A lacquer application process of applying and drying lacquer on the back surface of the mother board where the resin layer is hardened and polished to increase transparency of mother-of-pearl pattern;

상기 락커가 피복된 자개기판의 하면에 점착제층을 형성하고 이형지를 부착하여 피접착물에 접착할 수 있도록 하는 점작제를 도포하는 공정과,Forming a pressure-sensitive adhesive layer on the lower surface of the mother-of-pearl-coated substrate and applying release paper to attach the release paper to adhere to the adherend;

상기 박판의 자개기판 표면에 야광안료와 무색도료 및 흡착제가 혼합된 야광도료 피복하고 건조하는 야광도료피복공정과,A luminous paint coating process for coating and drying a luminous paint mixed with a luminous pigment, a colorless paint and an adsorbent on the mother-of-pearl surface of the thin plate;

상기 야광도료가 피복된 자개기판 상면에 선택된 인쇄기법에 의하여 각종 무늬 및 그림 등을 천연색으로 인쇄하는 공정과,Printing a variety of patterns and pictures in a natural color by a printing method selected on the upper surface of the mother-of-pearl substrate coated with luminous paint,

상기 인쇄된 자개기판을 건조하는 건조공정과,A drying process of drying the printed mother-of-pearl substrate;

상기 건조된 자개기판의 상면에 잉크 또는 안료가 번지는 것을 방지하는 흡착제를 도포하는 과정과,Applying an adsorbent to prevent ink or pigment from spreading on an upper surface of the dried mother-of-pearl;

상기 흡착제가 도포된 자개기판을 자연건조 시킨 후에 에폭시 수지 또는 우레탄수지를 피복하고 건조하여 경화시키는 수지피복 및 경화공정에 의하여 이루어지는 야광자개판의 제조방법에 관한 것을 특징으로 한다. After the natural drying of the mother board to which the adsorbent is applied, it is characterized in that the manufacturing method of the luminous magnetic plate made by a resin coating and curing step of coating and drying and curing the epoxy resin or urethane resin.

무색야광도료, 자개기판, 광택층 Colorless luminous paint, mother board, glossy layer

Description

야광자개판의 제조방법{Manufacturing method of nightglow mother of pearl plate}Manufacturing method of nightglow mother of pearl plate

본 발명은 명함케이스, 손거울, 분첩, 휴대폰고리, 열쇠고리, 목걸이, 귀고리, 넥타이핀, 단추, USB메모리 등 각종 장식물에 부착되는 야광자개판의 제조방법 에 관한 것으로, 보다 상세하게는 일정한 두께로 가공된 조개껍질 조각이 부착되어 있는 자개기판에 야광안료가 혼합된 투명도료를 코팅한 후, 기판의 자개무늬층의 표면에 스크린 인쇄를 하므로서 어두운 장소에서도 야광의 빛이 은은하게 발산되어 고급스러우면서도 우아하며 아름다운 나전칠기의 멋을 느낄 수 있도록 한 야광자개판의 제조방법에 관한 것이다.The present invention relates to a manufacturing method of a luminous magnetic plate attached to various ornaments, such as a business card case, hand mirror, puff, mobile phone ring, key ring, necklace, ear ring, tie pin, button, USB memory, and more specifically, processing to a certain thickness After coating the transparent paint mixed with luminous pigment on the mother-of-pearl board to which the shell pieces are attached, the screen is printed on the surface of the mother-of-pearl pattern of the substrate, so that the luminous light is softly emitted even in a dark place. The present invention relates to a method of manufacturing a luminous gazette which makes you feel the coolness of Najeon lacquerware.

일반적으로 자개로 불리는 나전(螺鈿)이란 얇게 마모한 조개껍질을 여러가지 형태로 오려내어 다양한 물건 등의 표면에 박아붙여 장식하는 것을 뜻하며, 오랜 옛날부터 가구류 등에 화려하면서도 우아한 장식효과를 얻을 목적으로 이용되어 오고 있으나 제조과정이 매우 복잡하며 수공으로 작업해야 하므로 장시간 소요되며 대량생산이 불가능하여 제품단가가 고가이므로 일반적인 생활용품에 다양하게 적용시킬 수 없었다.Najeon, commonly called mother-of-pearl, means cutting thinly worn clam shells into various forms and decorating them by attaching them to the surface of various objects. However, because the manufacturing process is very complicated and requires manual work, it takes a long time and mass production is impossible, so the price of the product is high.

또한, 종래 국내공개특허공보 공개번호 제2002-11159호에서는 스크린 인쇄기법을 이용한 나전장식물 및 그 제조방법이 제안되어 왔으나, 상기에서는 알루미늄 박층위에 스크린 인쇄에 의해 도료 또는 잉크가 도포된 문양층을 형성한 후, 그 문양층 위에 무늬에 맞는 나전무늬층을 돌출되게 부착하는 나전장식물을 제조하는 것으로, 상기의 제조방법은 나전무늬층을 전통나전칠기기법과 같이 문양층의 무늬와 맞는 나전조각을 일일히 조각하여야 하므로 제조에 장시간이 소요되어 인건비가 많아져 원가의 상승요인이 된다.In addition, conventional Korean Laid-Open Patent Publication No. 2002-11159 has proposed a semi-precious plant using a screen printing method and a method of manufacturing the same, but in the above, a pattern layer coated with paint or ink is formed on a thin aluminum layer by screen printing. Then, to produce a barbed plant that adheres to the pattern of the barbed pattern on the pattern layer, the method of manufacturing the barbed bark piece to match the pattern of the pattern layer like the traditional method of lacquer painting. Since it must be sculpted, it takes a long time to manufacture, which increases labor costs, which is a factor in the cost increase.

상기의 문제점을 해결하기 위하여 본 발명의 출원인들이 선출원한 국내공개특허공보 제2004-48649호에서는 스크린 인쇄기법을 이용한 자개장식물 및 그 제조방법이 제안되었으며,In order to solve the above problems, Korean Patent Application Publication No. 2004-48649, filed by the applicants of the present invention, proposes a mother-of-pearl plant using a screen printing method and a manufacturing method thereof.

상기에서는 자개무늬층의 표면에 문양층을 제외한 부분을 스크린 인쇄에 의해 도료 또는 잉크를 도포하고, 자개무늬층의 이면에 이형지를 부착하여 지지층을 형성한 후 자개무늬층 및 문양층의 상면 및 측면을 에폭시수지로 피복하므로서 전통나전칠기와 같은 효과를 가지는 나전칠기를 대량생산 할 수 있도록 한 것이다.In the above, paint or ink is applied to the surface of the mother-of-pearl pattern layer by screen printing, and a backing paper is formed on the back of the mother-of-pearl pattern layer to form a support layer. It is possible to mass-produce Na-ju lacquer which has the same effect as traditional or electric lacquer by coating it with epoxy resin.

그러나, 상기의 종래 발명은 전통나전칠기의 효과를 가지면서 대량생산이 가능하기는 하나 야간에는 전통나전칠기의 아름다운 문양과 색체를 느끼며 감상할 수 없다는 단점이 있었다. However, the conventional invention described above has the disadvantage of not being able to appreciate the beautiful patterns and colors of the traditional Najeon lacquer, although the mass production is possible while having the effect of traditional Najeon lacquer.

본 발명은 종래 자개장식물의 단점을 해소하기 위한 것으로, 통상의 자개기판에 인쇄기법을 이용하여 제조되는 자개에 있어서,The present invention is to solve the disadvantages of the conventional mother-of-pearl plants, in the mother-of-pearl manufactured by using a printing method on a conventional mother-of-pearl substrate,

자개기판의 상면에 야광안료와 무색도료 및 흡착제를 혼합한 야광도료를 피복한 후 다양한 인쇄기법 중에서 선택된 인쇄기법에 의하여 각종 무늬 및 그림 등을 천연색으로 인쇄하므로서 빛이 없는 어두운 장소에서도 야광의 은은한 빛에 의하여 고급스럽고 우아하며 아름다운 나전칠기 고유의 멋을 느낄 수 있는 야광자개판의 제조방법을 제공하려는데 있다.After coating the luminous paint mixed with luminous pigment, colorless paint and adsorbent on the upper surface of mother-of-pearl board, it prints various patterns and pictures in natural color by the printing method selected from various printing methods. The purpose of the present invention is to provide a manufacturing method of luminous enamel board which can feel the unique style of Najeon lacquer lacquer.

상기 목적을 달성하기 위한 본 발명은 선택된 백색 및 청록색을 띠는 조개껍질을 세척·이물질제거·절단 등 통상의 과정으로 가공하여 정선된 조개껍질 조각들을 이형지 위에 빈틈없이 배열하고 그 상면에 접착성수지액을 도포한 후 압착하고 건조한 후 이형지를 제거하여 자개판을 형성하는 공정과,The present invention for achieving the above object is selected by processing the usual white and turquoise clam shells in the usual process, such as washing, removing foreign matters, cutting, and arranged carefully selected shell shell pieces on the release paper and the adhesive resin on the upper surface After applying the liquid and then pressing and drying to remove the release paper to form a mother-of-pearl;

상기의 자개판의 이면 및 표면을 평편하게 연마하여 박판상의 자개기판을 만드는 공정과, A process of making a thin mother-of-pearl board by grinding the back and the surface of the mother-of-pearl plate flat;

상기 수지층이 경화되고 연마된 자개기판의 이면에 락커를 도포하고 건조하여 자개무늬의 투명도를 높이는 락커도포공정과,A lacquer application process of applying and drying lacquer on the back surface of the mother board where the resin layer is hardened and polished to increase transparency of mother-of-pearl pattern;

상기 락커가 피복된 자개기판의 하면에 점착제층을 형성하고 이형지를 부착하여 피접착물에 접착할 수 있도록 하는 점작제를 도포하는 공정과,Forming a pressure-sensitive adhesive layer on the lower surface of the mother-of-pearl-coated substrate and applying release paper to attach the release paper to adhere to the adherend;

상기 박판의 자개기판 표면에 야광안료와 무색도료 및 흡착제가 혼합된 야광도료 피복하고 건조하는 야광도료피복공정과,A luminous paint coating process for coating and drying a luminous paint mixed with a luminous pigment, a colorless paint and an adsorbent on the mother-of-pearl surface of the thin plate;

상기 야광도료가 피복된 자개기판 상면에 선택된 인쇄기법에 의하여 각종 무늬 및 그림 등을 천연색으로 인쇄하는 공정과,Printing a variety of patterns and pictures in a natural color by a printing method selected on the upper surface of the mother-of-pearl substrate coated with luminous paint,

상기 인쇄된 자개기판을 건조하는 건조공정과,A drying process of drying the printed mother-of-pearl substrate;

상기 건조된 자개기판의 상면에 잉크 또는 안료가 번지는 것을 방지하는 흡착제를 도포하는 과정과,Applying an adsorbent to prevent ink or pigment from spreading on an upper surface of the dried mother-of-pearl;

상기 흡착제가 도포된 자개기판을 자연건조 시킨 후에 경화성수지를 피복하고 건조하여 경화시키는 수지피복 및 경화공정에 의하여 이루어지는 야광자개판의 제조방법에 관한 것을 특징으로 한다. After a natural drying of the mother board to which the adsorbent is applied, it is characterized in that the manufacturing method of the luminous mother board made by a resin coating and curing step of coating the curable resin, drying and curing.

본 발명의 제조방법으로된 야광자개판을 각종 장식물에 부착하여 사용하면 밝은 곳에서는 무늬 및 그림 등이 인쇄되지 않은 부분의 자개무늬가 외부로 노출되어 천연색 인쇄무늬와 조화를 이루고 또한, 야광도료에 혼합된 야광안료는 태양광과 형광체 등의 빛을 흡수하여 축적하였다가 어두운 곳에서 서서히 빛을 방출하거나 발광하는 성질을 가진 것이므로 어두운 곳에서도 인쇄되지 않은 부분에서 발출되는 야광에 의하여 천연색 인쇄무늬와 자개무늬가 조화를 이루어 은은하게 표출되므로서 우리 고유의 아름다운 나전을 주야로 감상할 수 있는 효과가 있다.When the luminous mother board according to the manufacturing method of the present invention is attached to various ornaments and used, the mother-of-pearl pattern of the unprinted part of the pattern and the picture is exposed to the outside in harmony with the natural-colored printed pattern, and in the luminous paint The mixed luminous pigment absorbs and accumulates light such as sunlight and phosphors and then emits light slowly or emits light in the dark. As the pattern is harmoniously expressed, it has the effect of appreciating our unique beautiful day and night.

이하, 본 발명에 대하여 첨부도면을 참조하여 상세히 설명한다.Hereinafter, the present invention will be described in detail with reference to the accompanying drawings.

도 1은 본 발명에 따른 공정순서를 나타낸 블록도이며, 도 2는 본 발명에 의한 야광자개장식판의 단면 예시도이다. 1 is a block diagram showing a process sequence according to the present invention, Figure 2 is an exemplary cross-sectional view of the luminous panel plate according to the present invention.

본 발명의 야광자개판의 제조방법은 각종 조개류 중에서 백색 및 청록색을 띠고 있는 조개껍질을 선택하여 세척하고 이물질을 제거한 후 절단하고 조개껍질을 정선하는 제1공정과,The manufacturing method of the noctilucent plate of the present invention is the first step of selecting and washing the shells having a white and turquoise color among various shellfish, cutting off after removing foreign substances, and selecting the shells,

상기에서 정선된 조개껍질 조각을 이형지위에 빈틈없이 배열하고 그 상면 접착성 수지액을 도포하는 제2공정과,A second step of arranging the shell pieces selected in the above on a release paper and applying the top adhesive resin liquid;

상기 수지액이 도포된 조개껍질을 유압프레스로 3∼5시간 압착한 후 접착성 수지액을 경화시키고 이형지를 제거하여 자개판을 형성하는 제3공정과,A third step of pressing the resin liquid coated clam shell with a hydraulic press for 3 to 5 hours, curing the adhesive resin liquid and removing the release paper to form a mother-of-pearl;

상기에서 형성된 자개판의 표면 및 이면을 0.08 내지 0.12mm로 얇게 연마하여 자개기판(110)을 형성하는 제4공정과,A fourth step of forming the mother board 110 by grinding the surface and the back surface of the mother board formed above to 0.08 to 0.12 mm;

상기 자개기판(110)의 이면에 락커를 피복하여 자개기판의 투명도를 높이도록 이면광택층(160)을 형성하는 제5공정과,A fifth process of forming a back gloss layer 160 to cover the back surface of the mother substrate 110 to increase transparency of the mother substrate;

상기 이면광택층(160)의 하면에 점착제를 도포하여 점착제층(170)을 형성하고 이형지(180)를 부착하는 제6공정과,A sixth step of forming an adhesive layer 170 by applying an adhesive to a lower surface of the back gloss layer 160 and attaching a release paper 180;

상기 자개기판(110)의 표면에 야광안료와 무색의 도료 및 흡착제가 혼합된 무색야광도료를 피복하고 건조하여 무색야광도료층(120)을 형성하는 제7공정과,A seventh step of forming a colorless luminous paint layer 120 by coating and drying a colorless luminous paint mixed with a luminous pigment, a colorless paint and an adsorbent on the surface of the mother substrate 110;

상기 무색야광도료층(120) 상면에 무늬 및 그림을 천연색으로 인쇄하고 건조하여 인쇄층(130)을 형성하는 제8공정과,An eighth process of forming a printed layer 130 by printing and drying a pattern and a picture in a natural color on an upper surface of the colorless luminous paint layer 120;

상기 인쇄층(130) 상면에 흡착제(140)를 피복하고 자연건조하는 제9공정과,A ninth process of coating the adsorbent 140 on the upper surface of the printed layer 130 and air drying the same;

상기 흡착제 상면에 경화 후에 광택을 가지는 경화성 수지를 피복하고 경화시켜 경화수지층(150)을 형성하는 제10공정으로 이루어진다.After curing the upper surface of the adsorbent, the curable resin having a gloss is coated and cured to form a cured resin layer 150.

상기 무색야광도료는 자개기판(110)의 표면 전체에 피복되는 것으로 야광안료 10∼40중량%, 바인더수지 89∼55중량%, 흡착제 1∼5중량%를 혼합한 것으로 자개기판(110)에 피복한 후 4시간 이상 자연건조한다.The colorless luminous paint is coated on the mother substrate 110 by coating 10 to 40% by weight of luminous pigment, 89 to 55% by weight of binder resin, and 1 to 5% by weight of adsorbent. After 4 hours or more to dry naturally.

상기에서 야광안료는 주로 무기계 안료가 사용되며 무색 바인더 수지내에 균일하게 분포되어야 좋은 효과가 나타나게 되는 것으로, 야광안료의 혼합율이 10중량% 이하이면 어두운 곳에서 발광하는 시간이 짧고 광이 희미하여 인쇄무늬 및 자개무늬가 발현되지 못하며, 40중량% 이상이면 발광시간이 길고 광이 밝아져 인쇄무늬 및 자개무늬가 잘 발현된다는 장점이 있으나 무색 바인더 수지의 양이 적어짐에 따라 야광도료가 피복된 무색야광도료층(120)이 균질할 수 없을 뿐만 아니라 견고하지 못하여 쉽게 손상될 우려가 있다.In the above, the luminous pigment is mainly used inorganic pigments, and evenly distributed in the colorless binder resin is a good effect appears, when the mixing ratio of the luminous pigment is less than 10% by weight, the light emitting time in the dark place is short and the light is faded And the mother-of-pearl pattern is not expressed, and if the weight is more than 40% by weight, the light emission time is long and the light is bright, so that the printed pattern and the mother-of-pearl pattern are well expressed. Layer 120 may not only be homogeneous but also not robust and easily damaged.

상기에서 흡착제는 인쇄잉크(도료)를 흡착하고, 표면을 경화시키는 조제로 락커계 및 우레탄계가 각각 단독으로 사용하거나 혼합하여 사용된다.In the above, the adsorbent is used to adsorb the printing ink (paint) and to harden the surface, each of which is used alone or mixed with a lacquer-based and a urethane-based.

상기에서 무기계야광안료는 눈에 가장 밝게 느끼는 색(530㎚ 전후의 파장)을 가지며, 잔광시간이 2000분 이내이며 인체에 무해한 제품이 선택되어야 하며, 주로 칼슘, 스트르튬, 바륨 중 적어도 하나 이상이 함유된 금속산화물이 포함된 안료 또는 "ZnS:Cu" 안료 등을 사용한다.In the above inorganic luminous pigments have a color (the wavelength around 530nm) that is brightest to the eyes, afterglow time is less than 2000 minutes, harmless to the product should be selected, at least one of calcium, strontium, barium Pigments containing contained metal oxides or " ZnS: Cu " pigments.

상기에서 경화성 수지는 투명한 것으로 에폭시수지, 우레탄수지, 아크릴수지 UV경화수지 중에서 적어도 하나 이상을 포함하여 사용한다.The curable resin is used to include at least one of epoxy resin, urethane resin, acrylic resin UV curable resin as a transparent.

상기 무늬 및 그림은 무색야광도료층(120)의 상면에 스크린 인쇄기법 또는 디지털 인쇄기법 중에서 선택하여 인쇄하는 것이다.The pattern and picture are printed on the upper surface of the colorless luminous paint layer 120 by screen printing or digital printing.

상기 인쇄된 무늬 및 그림의 상면에 락커계 및 우레탄계 흡착제를 도포하는 것은 무색야광도료층(120)에 함유된 흡착제와 함께 인쇄된 잉크(도료) 상면 및 하면 각각에서 잉크를 흡착하고 경화시켜 잉크가 번지지 않게 하므로서 무늬 및 그림이 훼손되는 것을 방지하기 위한 것이며, 흡착제를 인쇄된 부위에 한정시켜 도포하면 재료를 절약할 수 있다.The coating of the lacquer and urethane absorbents on the upper surface of the printed pattern and the painting may absorb and cure the ink on the upper and lower surfaces of the ink (paint) printed together with the adsorbent contained in the colorless luminous paint layer 120. It is to prevent the pattern and the painting from being damaged by preventing smearing, and the material can be saved by applying the adsorbent to the printed area.

상기 흡착제가 도포되고 건조된 자개기판(110)의 상면 및 측면에 피복되는 경화수지는 에폭시수지 또는 우레탄수지 등에 락커계 또는 우레탄계 경화제를 혼합하여 투명도와 견고한 강도를 갖도록 한다.The cured resin coated on the upper and side surfaces of the mother board 110 coated with the adsorbent and dried to mix a lacquer-based or urethane-based curing agent to the epoxy resin or urethane resin to have transparency and solid strength.

상기에서 야광자개판(100)의 최상층에 형성되는 경화수지를 피복할 때는 인쇄된 잉크 또는 도료가 누렇게 변하는 것을 방지하기 위하여 15∼25℃의 실온에서 2∼3시간 1차 건조한 후, 오븐 등의 열처리 장치에서 40∼60℃의 온도로 2∼8시간 건조하여야 한다.When coating the cured resin formed on the uppermost layer of the luminous gasket 100, in order to prevent the printed ink or paint from yellowing, after primary drying for 2 to 3 hours at room temperature of 15 to 25 ℃, such as an oven It should be dried for 2-8 hours at the temperature of 40-60 degreeC in a heat processing apparatus.

상기 무색야광도료층(120)은 150∼200㎛의 두께를 유지하여야 하며, 상기 경화수지층(150)의 두께는 300㎛ 이상의 두께를 유지하여야 한다.The colorless luminous paint layer 120 should maintain a thickness of 150 ~ 200㎛, the thickness of the cured resin layer 150 should maintain a thickness of 300㎛ or more.

상기에서 무색야광도료층(120)이 150㎛ 미만이면 야광도료층이 견고하지 못하여 손상될 우려가 있고, 야광안료의 양이 너무적어 발광이 미약하여 어두운 곳에서 자개의 표현이 불가능하며, 200㎛를 초과하면 재료의 낭비가 되고, 피장식물 부착하였을 때 슬림하거나 핸섬한 느낌을 줄 수 없다.If the colorless luminous paint layer 120 is less than 150㎛ the luminous paint layer is not strong, there is a risk of damage, the amount of luminous pigment is so small that the light emission is weak, it is impossible to express mother-of-pearl in the dark, 200㎛ If it exceeds, it is a waste of material, and when attached to the plant, it cannot give a slim or handsome feeling.

또한 경화수지층(150)의 두께가 300㎛ 미만이면 견고하지 못하여 야광자개판내의 자개 및 무늬 등이 손상될 우려가 있으며 피장식물에 부착되었을 때 피장식물과 잘 조화될 수 있는 두께로 300㎛ 이상에서 선택할 수 있다.In addition, when the thickness of the cured resin layer 150 is less than 300㎛ may not be strong and may damage the mother-of-pearl and pattern in the luminous mother board, and when attached to the plant, the thickness can be well harmonized with the plant. You can choose from.

상기 자개기판(110)의 이면의 점착제층(170)의 점착제는 양면 점착테이프를 이용할 수도 있다.The pressure-sensitive adhesive of the pressure-sensitive adhesive layer 170 on the back surface of the mother-of-pearl substrate 110 may use a double-sided adhesive tape.

도 1은 본 발명에 따른 공정순서를 나타낸 블록도1 is a block diagram showing a process sequence according to the present invention

도 2는 본 발명에 따른 야광자개장식판의 단면 예시도Figure 2 is a cross-sectional view of the luminous children's decorative plate according to the invention

<도면의 주요부분에 부호의 설명><Description of the symbols in the main part of the drawing>

100 : 야광자개판 110 : 자개기판100: luminous mother board 110: mother board

120 : 무색야광도료층 130 : 인쇄층120: colorless luminous paint layer 130: printing layer

140 : 흡착제 150 : 경화수지층140: adsorbent 150: cured resin layer

160 : 이면광택층 170 : 점착제층160: back surface gloss layer 170: adhesive layer

180 : 이형지 180: release paper

Claims (6)

각종 조개류중에서 백색 및 청록색을 띠고 있는 조개껍질을 선택하여 세척하고 이물질을 제거한 후 절단하고 조개껍질을 정선하는 제1공정과,The first step of selecting and washing white and turquoise shells from various shellfishes, removing and removing foreign matters, and selecting shells; 상기에서 정선된 조개껍질 조각을 이형지위에 빈틈없이 배열하고 그 상면 접착성 수지액을 도포하는 제2공정과,A second step of arranging the shell pieces selected in the above on a release paper and applying the top adhesive resin liquid; 상기 수지액이 도포된 조개껍질을 유압프레스로 3∼5시간 압착한 후 접착성 수지액을 경화시키고 이형지를 제거하여 자개판을 형성하는 제3공정과,A third step of pressing the resin liquid coated clam shell with a hydraulic press for 3 to 5 hours, curing the adhesive resin liquid and removing the release paper to form a mother-of-pearl; 상기에서 형성된 자개판의 표면 및 이면을 0.08 내지 0.12mm로 얇게 연마하여 자개기판(110)을 형성하는 제4공정과,A fourth step of forming the mother board 110 by grinding the surface and the back surface of the mother board formed above to 0.08 to 0.12 mm; 상기 자개기판(110)의 이면에 락커를 피복하여 자개기판의 투명도를 높이도록 이면광택층(160)을 형성하는 제5공정과,A fifth process of forming a back gloss layer 160 to cover the back surface of the mother substrate 110 to increase transparency of the mother substrate; 상기 이면광택층(160)의 하면에 점착제를 도포하여 점착제층(170)을 형성하고 이형지(180)를 부착하는 제6공정과,A sixth step of forming an adhesive layer 170 by applying an adhesive to a lower surface of the back gloss layer 160 and attaching a release paper 180; 상기 자개기판(110)의 표면에 야광안료와 무색의 도료 및 흡착제가 혼합된 무색야광도료를 피복하고 건조하여 무색야광도료층(120)을 형성하는 제7공정과,A seventh step of forming a colorless luminous paint layer 120 by coating and drying a colorless luminous paint mixed with a luminous pigment, a colorless paint and an adsorbent on the surface of the mother substrate 110; 상기 무색야광도료층(120) 상면에 무늬 및 그림을 천연색으로 인쇄하고 건조하여 인쇄층(130)을 형성하는 제8공정과,An eighth process of forming a printed layer 130 by printing and drying a pattern and a picture in a natural color on an upper surface of the colorless luminous paint layer 120; 상기 인쇄층(130) 상면에 흡착제(140)를 피복하고 자연건조하는 제9공정과,A ninth process of coating the adsorbent 140 on the upper surface of the printed layer 130 and air drying the same; 상기 흡착제 상면에 경화 후에 광택을 가지는 경화성 수지를 피복하고 경화시켜 경화수지층(150)을 형성하는 제10공정으로 이루어진 것을 특징으로 하는 야광자개판의 제조방법.And a tenth step of forming a cured resin layer 150 by coating and curing a curable resin having a gloss after curing on the upper surface of the adsorbent. 청구항 1에 있어서,The method according to claim 1, 상기 무색야광도료층(120)은 야광안료 10∼40중량%, 무색 바인더 수지 89∼55중량%, 흡착제 1∼5중량%를 혼합한 무색야광도료를 자개기판(110)에 150∼200㎛ 두께로 피복한 후 4시간 이상 자연건조하는 것을 특징으로 하는 야광자개판의 제조방법.The colorless luminous paint layer 120 is 150 to 200㎛ thick colorless luminous paint mixed with 10 to 40% by weight of luminous pigment, 89 to 55% by weight of colorless binder resin, 1 to 5% by weight of adsorbent. Method of producing a noctilucent open plate characterized in that the natural drying for 4 hours or more after coating. 청구항 1 또는 청구항 2에 있어서,The method according to claim 1 or 2, 상기 야광안료는 눈에 가장 밝게 느끼는 530㎚ 전후의 파장을 가지며, 잔광시간이 2000분 이내이며 인체에 무해한 것을 특징으로 하는 야광자개판의 제조방법.The luminous pigment has a wavelength around 530 nm that is most brightly visible to the eyes, the afterglow time is less than 2000 minutes and is harmless to the human body manufacturing method of the luminous plate. 청구항 1에 있어서,The method according to claim 1, 상기 경화수지층(150)은 무늬 및 그림 인쇄면이 변하는 것을 방지하기 위하여 15∼25℃의 실온에서 2∼3시간 1차 건조하고, 열처리 장치에서 40∼60℃의 온도로 2∼8시간 건조하는 것을 특징으로 하는 야광자개판의 제조방법.The cured resin layer 150 is first dried at a temperature of 15 to 25 ° C. for 2 to 3 hours, and then dried at a temperature of 40 to 60 ° C. for 2 to 8 hours in order to prevent a pattern and a printing surface from changing. Method of manufacturing a noctilucent plate. 청구항 1에 있어서,The method according to claim 1, 상기 경화수지층(150)의 두께는 300㎛ 이상인 것을 특징으로 하는 야광자개판의 제조방법.The thickness of the cured resin layer 150 is a manufacturing method of the luminous gland plate, characterized in that 300㎛ or more. 삭제delete
KR1020090106738A 2009-11-06 2009-11-06 Manufacturing method of luminous gutter KR101049522B1 (en)