KR101042495B1 - Manufacturing for the ecosystem paving reinforced composition of porous and its construction method - Google Patents
Manufacturing for the ecosystem paving reinforced composition of porous and its construction method Download PDFInfo
- Publication number
- KR101042495B1 KR101042495B1 KR1020080081968A KR20080081968A KR101042495B1 KR 101042495 B1 KR101042495 B1 KR 101042495B1 KR 1020080081968 A KR1020080081968 A KR 1020080081968A KR 20080081968 A KR20080081968 A KR 20080081968A KR 101042495 B1 KR101042495 B1 KR 101042495B1
- Authority
- KR
- South Korea
- Prior art keywords
- weight
- ecological packaging
- ecological
- soil
- bentonite
- Prior art date
Abstract
본 발명은 천연토양을 주원료로 한 생태포장강화 조성물에 관한 것으로, 보다 상세하게는, 토사, 생태포장강화제, 벤토나이트 및 고강도 다공성 무기질 점토를 포함하는 것을 특징으로 하는 생태포장강화 조성물에 관한 것이다. 이에 의해, 토사와 같은 성질로 이뤄진 친환경차수제로 현장주변의 토사를 이용하여 원지반과 동종재질로 구성되므로 고품질 및 친자연적인 시공품질이 확보되고, 외부로부터의 물리적 충격으로 인해 그 구조가 파손되거나 일부 손상되어도 간단한 시공으로 보수가 가능하며, 설계시 현장여건에 따라 포장두께의 임의 조절이 가능하여, 선형대응에 유연하고 확실한 흙 포장 품질을 형성할 수 있다. 또한, 자체치유 성능이 있어 외부 충격으로 인해 그 구조가 일시적으로 관통되거나 손상되어도 원상으로 복구되어 그 구조를 계속 유지되고, 특수가공한 고강도 소성 무기질 점토를 사용하여 탈·변색이 안되며, 자연스러운 흙 고유의 색상을 유지할 수 있다.The present invention relates to an ecological packaging reinforcement composition based on natural soils, and more particularly, to an ecological packaging reinforcement composition comprising earth and sand, ecological packaging reinforcement, bentonite and high-strength porous inorganic clay. As a result, it is an eco-friendly water repellent that is made of soil-like properties. It is composed of original ground and the same material by using earth and sand around the site. Therefore, high quality and natural construction quality is secured, and its structure is damaged or partially damaged by external physical impact. Even if damaged, it can be repaired by simple construction, and the design thickness can be arbitrarily adjusted according to the site conditions at the time of design, and it is possible to form flexible and reliable soil pavement quality for linear response. In addition, it has self-healing performance, and even if the structure is temporarily penetrated or damaged due to external impact, it is restored to its original shape and maintained. The structure is not decolored and discolored using specially processed high-strength plastic mineral clay. You can keep the color.
생태포장강화제, 벤토나이트, 무기질 점토 Ecological packaging enhancer, bentonite, mineral clay
Description
본 발명은 천연토양을 주원료로 한 생태포장강화 조성물에 관한 것으로, 보다 상세하게는, 토사, 생태포장강화제, 벤토나이트 및 다공성 고강도 무기질 점토를 포함하는 것을 특징으로 하는 생태포장강화 조성물에 관한 것이다.The present invention relates to an ecological packaging reinforcement composition based on natural soils, and more particularly, to an ecological packaging reinforcement composition comprising earth and sand, ecological packaging reinforcement, bentonite and porous high strength inorganic clay.
이제 도로는 보행자가 목적지에 도달하기 위한 수단에 그치지 않고, 도시의 환경을 개선하고 환경을 오염시키는 산업폐기물의 공해로부터 시민의 건강을 고려한 기능성이 중요하게 여겨지고 있다. Roads are no longer just a means for pedestrians to reach their destination, but the functionality of citizens is considered important from the pollution of industrial waste that improves the city's environment and pollutes the environment.
도로를 포장하는 일반적인 도로 포장재는 주로 아스팔트나 콘크리트로 된 것으로서, 이들은 투수성이 없고 환경 친화적인 것이 아니며 햇빛을 받으면 복사열이 발생하여 대기온도를 상승시킴은 물론, 폭우시 유수(流水)를 집중시켜, 하천범람 등의 요인이 된다. 특히 하절기 등에는 그 정도가 더욱 심하다. 또한, 상기 아스팔트나 콘크리트로는 한번 설치하여 사용하다가 노후화로 인하여 다시 포설작업을 하고자 할 때에는 상기 노후화된 아스팔트나 콘크리트를 걷어내고 그 자리에 새로 운 아스팔트나 콘크리트를 포설해야 하는데, 이때 걷어낸 아스팔트나 콘크리트는 산업폐기물로 분류되어 그들을 처리하기가 매우 어려운 문제점이 있었다.The general road pavement for paving roads is mainly made of asphalt or concrete, which are not permeable and environmentally friendly, and radiant heat is generated when the sunlight causes the air temperature to rise. And river flooding. Especially in summer, the degree is even worse. In addition, when the asphalt or concrete is installed once and used for laying work again due to aging, the aged asphalt or concrete should be removed and new asphalt or concrete should be laid in place. Concrete was classified as industrial waste, which made it very difficult to treat them.
따라서 상기의 문제점을 해소하고자 흙, 시멘트 및 생석회를 배합하여 된 도로포장재가 제공되어 있으나 이는 시멘트계열의 혼합으로 친환경성이 떨어지고, 질감이 좋지 않으며 초기 압축강도를 유지하기가 어렵고, 투수가 되지 않는 문제점이 있음은 물론, 균열이 발생하는 문제점이 있었다.Therefore, to solve the above problems, there is provided a road paving material which is a mixture of soil, cement and quicklime, but it is not environmentally friendly due to the mixing of cement series, poor texture, difficult to maintain the initial compressive strength, and not permeable Of course, there was a problem that a crack occurs.
한편, 점질토, 사질토 및 고함수점질토 등의 토양에 시멘트와 생석회를 혼합한 마사토에 리그닌 술폰산 중합체, 요소수지계 합성고분자 에멀젼 및 아스팔트 유제를 첨가한 토양안정제를 첨가하여 내수성 및 고결강도를 부여할 수 있는 도로포장재(대한민국 특허 제12002호)와, 생석회를 대신하여 나프탈렌, 산화칼슘, 규산알루미늄, 수분으로 이루어진 로말디(LOMAR D)라는 물질이 첨가되어 압축강도를 증대시키고, 경화속도를 단축시킬 수 있는 도로포장재(대한민국특허 제50937호)가 제공되어 있다.On the other hand, it is possible to impart water resistance and grain strength by adding a soil stabilizer added with lignin sulfonic acid polymer, urea resin-based synthetic polymer emulsion and asphalt emulsion to masato mixed with cement and quicklime in soil such as clay soil, sandy soil and high water clay. In addition to road paving material (Korean Patent No. 12002) and a material called lomaldi (LOMAR D) consisting of naphthalene, calcium oxide, aluminum silicate, and water in place of quicklime, it can increase the compressive strength and shorten the curing speed. Road paving material (Korean Patent No. 50937) is provided.
그러나, 상기와 같이 토양에 아스팔트 유제, 생석회 또는 로말디를 첨가하여 토양안정처리를 하는 경우 어느 정도의 압축강도 향상이나 동결 방지 효과는 있을 수 있으나 자연 친화적인 표면질감과 마사토의 단점인 파쇠되어, 입자가 쌓이는 현상, 습식시공으로 인해 발생되는 균열을 방지하는 데에는 한계가 있었다.However, if the soil stabilization treatment by adding asphalt emulsion, quicklime or lomaldi to the soil as described above may have some degree of compressive strength improvement or freeze protection effect, but is a disadvantage of nature-friendly surface texture and Masato, There was a limit in preventing cracks caused by particle accumulation and wet construction.
따라서 근래에는 토양안정처리용 조성물(특허출원 제1997-35649호)로서 은 마사토 100 중량부에 포틀랜트 시멘트 2∼5 중량부, 고무화 아스팔트 방수액 10∼15 중량부, 플라이 애쉬 1∼4 중량부 및 칼슘 설포 알루미네이트 1∼3 중량부로 이 루어진 것이 있고, 황토, 적도, 마사토, 고령토, 백토, 흑토 및 규사로 이루어진 군으로부터 어느 하나의 토양을 선택하여 수지용액 또는 에멀젼을 혼합한 것들이 있다.Therefore, in recent years, as a composition for soil stabilization treatment (Patent Application No. 1997-35649), 100 parts by weight of silver Masato 2 to 5 parts by weight of Portland cement, 10 to 15 parts by weight of rubberized asphalt waterproofing liquid, 1 to 4 parts by weight of fly ash And calcium sulfo aluminate 1 to 3 parts by weight, and any one soil is selected from the group consisting of ocher, equatorial, masato, kaolin, white clay, black clay, and silica sand, and those in which a resin solution or an emulsion is mixed.
그러나 투수가 전혀 되지 않거나 극히 미량의 투수만 가능하다는 문제점이 있고, 자연 친화적이지 못하며 한번 포설하여 사용하다가 노후화로 인하여 걷어내게 되면 그 걷어내어진 것을 재활용하지 못하고 산업폐기물로 처리하는 수밖에 없는 근본적인 문제점이 지적되고 있었다.However, there is a problem that there is no pitcher at all or only a very small amount of pitcher, and it is not natural-friendly, and once it is laid out and used for aging, it can not be recycled and disposed of as industrial waste. It was being pointed out.
이에 의하여, 상기의 문제점 및 환경오염문제로 근래에 산업 폐기물을 활용한 고강도 투수성 포장에 대한 관심이 높아져서 연구가 활발하게 진행하게 되었다.As a result, in recent years due to the above problems and environmental pollution problems, the interest in high-intensity permeable packaging using industrial wastes has been increased, and research has been actively conducted.
본 발명의 목적은 천연토양을 주원료로 한 생태포장강화 조성물을 제공하기 위한 것으로, 보다 상세하게는 토사, 생태포장강화제, 벤토나이트 및 다공성 고강도 무기질 점토를 포함하는 것을 특징으로 하는 생태포장강화 조성물을 제공하는 데 있다.An object of the present invention is to provide an ecological packaging reinforcement composition based on natural soils, and more specifically, to provide an ecological packaging reinforcement composition comprising soil, ecological reinforcement, bentonite and porous high-strength mineral clay. There is.
본 발명은 토사에 일정량의 생태포장강화제, 벤토나이트와 그리고 다공성 고강도 무기질 점토를 첨가하여 방수층의 통기성을 강화한 생태포장강화 조성물을 제공한다.The present invention provides an ecological packaging reinforcement composition to enhance the air permeability of the waterproof layer by adding a predetermined amount of ecological packaging enhancer, bentonite and porous high-strength inorganic clay to the soil.
본 발명에 따른 생태포장강화 조성물은 토사 60 ~ 85 중량%. 생태포장강화제 5 ~ 20 중량%, 벤토나이트 5 ~ 10 중량% 및 다공성 고강도 무기질 점토 5 ~ 10 중량%의 비율로 이루어질 수 있다.Ecological packaging reinforced composition according to the present invention 60 to 85% by weight of soil. Ecological packaging reinforcing agent may be made of a ratio of 5 to 20% by weight, bentonite 5 to 10% by weight and porous high strength inorganic clay 5 to 10% by weight.
본 발명에 따른 생태포장강화 조성물은 a)토사 b)생태포장강화제; c)벤토나이트; 및 d)다공성 고강도 무기질 점토를 혼합시킬 수 있다.Ecological packaging reinforcement composition according to the present invention is a) earth soil b) ecological packaging enhancer; c) bentonite; And d) porous high strength inorganic clays.
바람직하게는. 본 발명에서 "토사"는 화강암이 풍화되어 생긴 화강토를 의미하며, "생태포장강화제"는 산화칼슘, 실리카, 석회, 알무미나, 산화철, 산화마그네슘 등을 주성분으로 포함할 수 있고, 바람직하게는, 산화칼슘(CaO) 50 ~ 70 중량%, 실리카(SiO2) 15 ~ 30 중량%, 알루미나(Al2O3) 10 ~ 15 중량%, 산화마그네슘(MgO) 3 ~ 5 중량% 및 산화철(FeO3) 2 ~ 5 중량%를 포함할 수 있다. Preferably. In the present invention, "soil" refers to granite produced by weathering granite, and "eco-packaging fortification" may include calcium oxide, silica, lime, alumina, iron oxide, magnesium oxide, and the like as a main component. , 50 to 70% by weight of calcium oxide (CaO), 15 to 30% by weight of silica (SiO 2 ), 10 to 15% by weight of alumina (Al 2 O 3 ), 3 to 5% by weight of magnesium oxide (MgO) and iron oxide (FeO) 3 ) may contain 2 to 5% by weight.
바람직하게는, "무기질 점토"는 흙의 분류법 중 'ASHTO 분류법'의 CL(소성이 중간치 이하인 무기질 점토)에 해당되며, 고온(800 ~ 1100℃)에서 가열하여 미분말형(8 mesh 이하)로 빻은 것이나 이에 제한하지 아니한다. AASHTO 분류법(AASHTO Soil Classificaion System)은 미국도로교통공무원협회(ASSHTO, American Society of State Highway and Transportaton Officials)에서 개발한 흙의 분류 체계로서 당업계에 널리 공지되어 있으며, 체 분석으로 구한 입도분포와 소성지수, 액성한계 및 군지수를 이용하여 분류하고, 도로 또는 노상토를 구분하는데 이용될 수 있다.Preferably, the "inorganic clay" corresponds to the CL of the 'ASHTO classification' in the classification of soil, which is ground to a fine powder (8 mesh or less) by heating at high temperature (800-1100 ° C). But not limited thereto. The AASHTO Soil Classificaion System is a soil classification system developed by the American Society of State Highway and Transportaton Officials (ASSHTO) and is well known in the art. They can be classified using indexes, liquid limits, and military indices and used to distinguish roads or subgrade soils.
바람직하게는, 생태포장강화 조성물의 형태는 분말형(8 mesh이하)이며 방수제(차수제) 및 수질오염 정화제로 사용할 수 있다. Preferably, the form of the ecological packaging reinforcement composition is a powder form (8 mesh or less) and can be used as a water repellent (water repellent) and water pollution purifying agent.
바람직하게는, 생태포장강화 조성물의 분자구조는 판 구조로서 물을 접하면 물 분자를 가두는 형태로 유지되어 차수목적을 충족하고, 다공성 입체그물눈 구조로 토사내의 통기성 및 오염 물질을 분자구조층에 걸러내어 수질을 정화할 수 있다.Preferably, the molecular structure of the ecological packaging reinforcement composition is in the form of a plate structure is maintained in the form of water molecules trapped when contacted with water to meet the purpose of the order, the porous three-dimensional mesh structure of the air permeability and contaminants in the soil structure structure layer You can filter the water quality.
바람직하게는, 생태포장강화 조성물은 물과 접촉된 환경에서 시간이 흘러 물분자가 빠져나가 건조한 환경으로 바뀌어도 분자구조가 파괴되지 않고 유지되며 상기 분자구조가 다시 물을 만나면 물분자를 가두게 되므로 그 구조가 지속적으로 유지될 수 있다.Preferably, the ecological packaging reinforcement composition maintains the molecular structure intact even if the water molecules pass through the environment in contact with water and change to a dry environment, and confines the water molecules when the molecular structure encounters water again. The structure can be maintained continuously.
바람직하게는, 생태포장강화 조성물은 양이온 치환능력이 있어 수자원과 토 사내의 중금속 등을 흡착하고, 각 분자에는 눈에 보이지않는 미세한 공극이 있어 오염물질을 걸러주어 탈취 및 정화 성능을 발휘할 수 있다.Preferably, the ecological packaging enhancing composition has a cation substitution ability to adsorb water and heavy metals in the soil, and each molecule has invisible fine pores to filter out contaminants to exhibit deodorization and purification performance.
바람직하게는, 기존 황토포장은 포장재료에 안료를 첨가하여 사용하기 때문에 시간이 경과함에 따라 탈색, 변색되나 본 공법에서는 특수가공한 고강도 소성 무기질 재료를 사용하므로 자연스러운 황토의 색상이 반 영구적이며, 안료가 단순 혼합처리하는 기존 공법에 비해 20배 이상의 내구성을 갖을 수 있다.Preferably, the existing ocher packaging is discolored and discolored over time because the pigment is added to the packaging material, but the natural ocher color is semi-permanent because the method uses a specially processed high-strength plastic inorganic material. It can have a durability 20 times more than the existing method of simple mixing process.
바람직하게는, 본 발명에 따른 생태포장강화 조성물의 시공시 지하수, 용출수 및 사면의 유출수 등 유수(流水)가 발생할 우려가 있으면 담당자와 협의하여 임시 배수로 등을 두어 펌핑하거나 배수시설을 철저히 한 다음에 시공하여야 한다. 또한, 생태 강화포장 공사는 장비사용이 많아 사고의 위험이 많으므로 안전관리를 철저히 하여야 하고, 제품취급시 눈에 들어가지 않도록 하며, 눈에 들어간 경우 물로 씻는다. 재료의 보관은 습기가 차지 않고 서늘하고 비에 젖지 않는 곳에 보관해야 한다.Preferably, when construction of the ecological packaging reinforcement composition according to the present invention there is a risk of running water such as groundwater, elution water and effluent of slopes, in consultation with the person in charge to put a temporary drainage pump or drainage facilities thoroughly Should be installed on In addition, ecological reinforcement paving works have a lot of equipments, so there are many risks of accidents. Therefore, safety management should be carried out thoroughly. Do not get into eyes when handling products, and if it gets into eyes, wash with water. Storage of materials should be stored in a cool, dry, non-wetting environment.
바람직하게는, 시공장소의 환경(silt, 암반, 토사, 풍화토 등)에 따라 생태 포장강화제의 소요량이 증감될 수 있으며, 현장토사의 상태에 따라 소요량이 증감될 수 있다.Preferably, the amount of ecological paving reinforcement may be increased or decreased depending on the environment of the city factory (silt, rock, earth and sand, weathered soil, etc.), and the amount may be increased or decreased depending on the state of the site soil.
상기한 과제 해결 수단에 의한 본 발명에 따르면, 토사와 같은 성질로 이뤄진 친환경차수제로 현장주변의 토사를 이용하여 원지반과 동종재질로 구성되므로 고품질 및 친자연적인 시공품질이 확보되고, 외부로부터의 물리적 충격으로 인해 그 구조가 파손되거나 일부 손상되어도 간단한 시공으로 보수가 가능하며, 설계시 현장여건에 따라 포장두께의 임의 조절이 가능하여, 선형대응에 유연하고 확실한 흙 포장 품질을 형성할 수 있다. 또한, 자체치유 성능이 있어 외부 충격으로 인해 그 구조가 일시적으로 관통되거나 손상되어도 원상으로 복구되어 그 구조를 계속 유지되고, 특수가공한 고강도 소성 무기질 점토를 사용하여 탈색 및 변색이 되지 으며, 자연스러운 흙 고유의 색상을 유지할 수 있다.According to the present invention by the above-mentioned means for solving the problem, it is composed of the base and the same material by using the earth and sand around the site as an eco-friendly water repellent made of the same properties as the earth and sand to ensure high quality and natural construction quality, physical from the outside Even if the structure is damaged or partially damaged due to the impact, it can be repaired by simple construction, and it is possible to arbitrarily adjust the pavement thickness according to the site conditions at the time of design, thereby forming a flexible and reliable soil pavement quality for linear response. In addition, it has self-healing performance, and even if the structure is temporarily penetrated or damaged due to external impact, the structure is restored to its original state, and the structure is maintained continuously, and it is discolored and discolored using specially processed high-strength plastic mineral clay. You can keep your own color.
이하, 본 발명을 하기 실시예를 통하여 상세히 설명한다.Hereinafter, the present invention will be described in detail through the following examples.
실시예Example
실시예Example 1: 생태포장강화 조성물의 제조 1: Preparation of Ecological Packaging Reinforcement Composition
토사 60~85중량%, 생태포장강화제 5~20중량%, 벤토나이트 5~10중량%, 다공성 고강도 무기질 점토 5 ~ 10 중량%의 비율로 본 발명에 따른 생태포장강화 조성물을 제조하였다. Soil 60 to 85% by weight, 5 to 20% by weight of ecological packaging enhancer, 5 to 10% by weight of bentonite, 5 to 10% by weight of porous high-strength inorganic clay was prepared according to the present invention.
이때, 생태포장강화제는 산화칼슘(CaO) 50 ~ 70 중량%, 실리카(SiO2) 15 ~ 30 중량%, 알루미나(Al2O3) 10 ~ 15 중량%, 산화마그네슘(MgO) 3 ~ 5 중량% 및 산화철(FeO3) 2 ~ 5 중량%이다. 무기질 점토는 고온(800 ~ 1100℃)에서 가열하여 미분말형(8 mesh 이하)로 빻았다. At this time, the ecological packaging enhancer 50 to 70% by weight of calcium oxide (CaO), 15 to 30% by weight of silica (SiO 2 ), 10 to 15% by weight of alumina (Al 2 O 3 ), magnesium oxide (MgO) 3 to 5 weight % And iron oxide (FeO 3 ) 2 to 5% by weight. Inorganic clay was ground to a fine powder (8 mesh or less) by heating at a high temperature (800 ~ 1100 ℃).
실시예Example 2: 생태포장강화 조성물의 시공 2: Construction of Ecological Packaging Reinforcement Composition
도 1에 나타낸 바와 같이, 원지반 위에 실시예 1에서 제조한 생태포장강화 조성물을 70 ~ 100 mm로 시공하였다. As shown in Figure 1, the ecological packaging reinforcement composition prepared in Example 1 on the base was constructed in 70 ~ 100 mm.
실시예Example 3: 강도 시험 3: strength test
일정규모의 강도가 얼마만큼 유지되는가 알아보고, 성능을 유지시키기 위하여 실시하였다. This study was conducted to find out how much strength of a certain scale was maintained and to maintain performance.
도 2에 나타낸 바와 같이, 기존 산책로는 시공직 후의 강도를 100으로 기준했을때 1년 후의 강도는 50으로 떨어져 박리, 패임 등이 현격히 증가하였다. 이에 비하여 생태포장강화 산책로는 그 강도가 대부분 유지됨을 알 수 있었다. As shown in FIG. 2, when the existing walkway is based on the strength after the construction job of 100, the strength after one year drops to 50, and the peeling, the dents, etc. are significantly increased. On the other hand, the ecological pavement-enhanced trails were found to maintain most of their strength.
실시예Example 4: 표면색상 탈·변색 시험 4: Surface color decolorization and discoloration test
시공 직후 색상이 일정시간 탈·변색되지 않고, 유지되는가 알아보고, 성능을 유지시키기 위하여 실시하였다. Immediately after the construction, the color was deteriorated and discolored for a certain period of time.
도 3에 나타낸 바와 같이, 기존 산책로는 시공직 후의 색상을 100으로 기준했을때 1년 후의 색상은 50, 3년 후에는 30으로 떨어져 처음과 비교하여 자연색을 잃어버린다는 것을 알 수 있었다. 이에 비하여 생태포장강화 산책로는 탈·변색이 일어나지 않기 때문에 처음의 자연색이 지속적으로 유지되었다As shown in FIG. 3, when the color of the existing walkway is based on 100 after the construction job, the color after one year drops to 50 after 30 years and loses the natural color as compared with the first time. On the other hand, the ecological pavement-enhanced trails did not decolor and discolor so that the natural colors of the first were maintained.
실시예Example 5: 통기성 시험 5: breathability test
통기성을 강조하면 강도 및 차수에 치명적인 결함이 발생되므로 모든 조건에서 가장 적합한 투수계수를 찾아보았다. 생태강화포장은 강도와 차수성을 저감시키지 않은 상태의 최적의 통기성을 확보하여 1년 후와 3년 후에도, 투수계수(1 X 10-6 cm/sec)가 지속적으로 유지됨을 알 수 있었다(도 4). Emphasis on breathability leads to fatal defects in strength and order, so we have found the best permeability coefficient under all conditions. Ecological reinforcement packaging ensured the best air permeability without reducing the strength and degree of permeability, so that the permeability coefficient (1 X 10 -6 cm / sec) was continuously maintained even after 1 year and 3 years (Fig. 4).
상기에서는 본 발명의 바람직한 실시예를 참조하여 설명하였지만, 해당기술 분야의 숙련된 당업자는 하기의 특허 청구의 범위에 기재된 본 발명의 사상 및 영역으로부터 벗어나지 않는 범위 내에서 본 발명을 다양하게 수정 및 변경시킬 수 있음을 이해할 수 있을 것이다. It will be apparent to those skilled in the art that various modifications and variations can be made in the present invention without departing from the spirit or scope of the present invention as defined by the following claims It can be understood that
본 발명은 천연토양을 주원료로 한 생태포장강화 조성물에 관한 것으로, 고궁, 공원 유원지 등의 산책로 및 광장, 자전거 및 보행자 전용도로, 문화재, 유적지 등 진입로 및 단지 내의 포장, 아파트단지 및 운동시설 포장, 호안, 저수지 및 방조제의 강화 처리 등 다양하게 응용이 가능하다.The present invention relates to an ecological pavement-enhancing composition based on natural soils, including pavements, plazas, parks, amusement parks, pavements, bicycles and pedestrian-only roads, cultural properties, historic sites, pavements, apartment complexes and sports facilities, Various applications are possible, such as reinforcement treatment of shores, reservoirs, and embankments.
도 1은 본 발명에 따른 생태포장강화제의 단면 상세도를 나타낸 것이다. Figure 1 shows a cross-sectional detail of the ecological packaging enhancer according to the present invention.
도 2는 본 발명에 따른 생태포장강화제의 강도시험을 통하여 기존의 산책로와 비교한 것이다. Figure 2 is compared with the existing walkway through the strength test of the ecological packaging enhancer according to the present invention.
도 3은 본 발명에 따른 생태포장강화제의 표면색상에 대하여 탈, 변색 시험을 통하여 기존의 산책로와 비교한 것이다. Figure 3 is compared with the conventional walkway through the decolorization, discoloration test for the surface color of the ecological packaging enhancer according to the present invention.
도 4는 본 발명에 따른 생태포장강화제의 통기성 시험을 통하여 기존의 산책로와 비교한 것이다. Figure 4 is compared with the existing walkway through the breathable test of ecological packaging enhancer according to the present invention.
Claims (6)