KR100996674B1 - Paving material composition comprising yellow soil with pro-environmental property, shock-absorbing - Google Patents

Abstract

PURPOSE: An environmentally-friendly composition for shock-absorbing yellow soil pavement is provided to minimize the production of carbon disulfide from rubber chip, thereby preventing atopy, rhinitis, asthma etc. of pedestrians or bicycle riders. CONSTITUTION: An environmentally-friendly composition for shock-absorbing yellow soil pavement comprises active yellow soil 15~20weight%, white cement 3~7 weight%, fine silica 5~10 weight%, antimicrobial agent-coated waste rubber chip powder 4~8 weight%, basalt 1~2 weight%, waste ceramics 2~3weight%, nano-capsules containing plant flavor extract 0.1~0.2 weight%, rosin-coated wood chips 1~2 weight%, a resin containing fragrant grass, agar extract and water-soluble acryl urethane 25~35 weight%, ferric oxide 5~10 weight%, an antimicrobial agent of nanosilver powder 0.1~0.3 weight%, a UV blocking agent 1~1.5 weight%, a deterioration-preventing agent 2~3 weight%, tourmaline 0.2~0.5 weight%, and water 20~25 weight%.

Description

Eco-friendly buffered ocher packaging material {Paving material composition comprising yellow soil with pro-environmental property, shock-absorbing}

The present invention relates to an environment-friendly buffered ocher packaging material composition, and more specifically, using a loess, white cement, Songseok, Goeunsa, waste rubber chip powder, waste pottery, wood chips and fragrance at the same time The present invention also relates to a green cushioning composition for protecting cushioning of a user from the sunlight by using an antimicrobial agent to achieve well-being and green growth.

In general, the buffered yellow pavement is more environmentally friendly than asphalt or concrete, and has a shock-absorbing function on pedestrian paths to protect the joints of pedestrians and to prevent accidents when bicycle riders accidentally fall on bicycle paths. Buffering ocher paving is carried out throughout the corridors and sports facilities such as river trails, playground tracks, park paths and bicycle paths.

Conventional buffer loess packaging materials have a high construction cost when using expensive urethane chips, and there is an economic burden, and the use of waste tire chips to reduce the unit cost results in a rubbery smell on the packaging surface after construction. The user is uncomfortable with the smell of the waste rubber chip is used as it is without processing, causing atopy, rhinitis, asthma, etc. have been providing.

Accordingly, efforts have been made to reduce the amount of urethane using buffer packaging materials using ocher, but the disadvantage of ocher is adversely affecting the respiratory health by the ocher powder scattered when used indoors. As a result, the loess was pasted, which caused difficulty in walking or cycling.

The invention carbon disulfide produced in that been made to solve the above problems, active yellow earth, white cement, cluster analysis, fine quartz sand, waste rubber chips powder, rubber chips by using a closed-ceramics, wood chips (CS ₂ It is intended to provide an eco-friendly buffered ocher pavement composition that minimizes the occurrence of) and prevents atopic, rhinitis, asthma, etc. to the bicycle or walkway users.

It is also intended to provide an environmentally friendly cushioning loess material composition for the comfort and the fragrant pavement of a pedestrian and a bicycle occupant walking through a forest road or a flower garden, will be.

Still another object of the present invention is to provide a well-being exercise place that creates a pleasant environment by maintaining a certain intensity without being water-pasted even when it is raining outdoors while expressing the unique property of ocher that promotes bioactivity by far-infrared radiation. In addition, it is used as a light aggregate by using Song-seok, which is left unused and discarded because there are no consumers, and promotes the ground penetration of rainwater, preventing depletion of groundwater, and recycling waste by using waste ceramics and wood chips. It is to provide a buffer loess packaging composition.

In addition, by using a binder containing natural materials to provide an environmentally friendly buffer loess packaging material that is environmentally friendly, especially in the summer to prevent the odor of the existing packaging material is aggravated due to the high temperature and to suppress the degradation and lifting of the packaging.

Eco-friendly buffered ocher packaging composition according to the present invention, activated clay 15-25% by weight, 3-7% by weight cement, fine grain sand 5-10% by weight, 4-8% by weight of antimicrobial coated waste rubber chip powder, pine 1 ~ 2% by weight of stone, 2-3% by weight of waste pottery, 0.1 ~ 0.2% by weight of nanocapsules containing plant flavor stock solution, 1-2% by weight of wood chips coated with rosin, scented herb, radish, water soluble acrylic urethane 25-35% by weight of mixed resin, 5-10% by weight of iron oxide, 0.1-0.3% by weight of antimicrobial agent composed of silver nanopowder, 1-1.5% by weight of sunscreen, 2-3% by weight of deterioration inhibitor, 0.2-0.5% by weight of tourmaline, And 20 to 25% by weight of water.

In addition, the environment-friendly buffered ocher packaging material composition, characterized in that further adding a fluorescent material or a photoluminescent material.

In addition, the plant flavor is characterized in that the cosmos flavor, acacia flavor, rose flavor, chestnut flavor, herbal flavor.

In addition, the sunscreen is characterized in that the oxybenzone or zinc oxide.

In addition, the deterioration inhibitor is characterized in that the naphtan hydrocarbon or isoparaffinic hydrocarbon.

The present invention minimizes the use of rubber chips and improves bioactivity by far-infrared radiation, thereby minimizing the generation of carbon disulfide (CS ₂ ) while preventing atopic dermatitis, rhinitis, asthma, etc. It is advantageous in that it is an environmentally friendly buffered yellow loose packaging material composition which prevents the formation of water paste of yellow loess even in case of rain and has a certain strength.

In addition, Song-seok waste is a lightweight aggregate to secure the permeability of the package, and waste ceramics are hard aggregates complementary to softer rubber chip powder, they have the effect of securing the durability of the buffered loess pavement surface.

Also, there is an effect of providing a well-being exercise place that provides comfort such as passing through a forest or a flower field in a city center, and a fragrant environmentally friendly buffered ocher packing material composition so that there is no fatigue even for a long period of time, and various fungi and germs are suppressed to create a pleasant environment.

In addition, there is an effect of inducing interest to cyclists or pedestrians at night, doubling the exercise effect and preventing safety accidents with fluorescent materials or phosphorescent materials.

Eco-friendly buffered ocher packaging composition of the present invention, activated clay 15-25% by weight, 3-7% by weight cement, fine grain sand 5-10% by weight, 4-8% by weight of antimicrobial coated waste rubber chip powder, Songseok 1 to 2% by weight, 2 ~ 3% by weight of waste ceramics, 0.1 ~ 0.2% by weight of nanocapsules containing plant flavor stock solution, 1 ~ 2% by weight of wood chips coated with rosin, scented candles, radish fern extract and water-soluble acrylic urethane 25 to 35% by weight of resin, 5 to 10% by weight of iron oxide, 0.1 to 0.3% by weight of antimicrobial agent consisting of silver nanopowder, 1 to 1.5% by weight of sunscreen, 2 to 3% by weight of antioxidant, 0.2 to 0.5% by weight of tourmaline By weight and 20 to 25% by weight.

In addition, the environment-friendly buffered ocher packaging material composition characterized in that it further adds a fluorescent material or a photoluminescent material.

In addition, the plant flavor is characterized in that the cosmos flavor, acacia flavor, rose flavor, chestnut flavor, herbal flavor.

In addition, the sunscreen is characterized in that the mixture of oxybenzone and zinc oxide.

In addition, the deterioration inhibitor is characterized in that the naphtan hydrocarbon or isoparaffinic hydrocarbon.

Hereinafter, the composition of the present invention will be described in more detail.

The activated ocher used in the present invention is dense and clean, collected from 50-100 cm below the surface, heated to 500-700 ° C., dried and ground. The activated ocher may not only use natural loess including sand, quartz, mica, feldspar, etc. having large particle diameters, but also use charcoal, elvan, jade, etc., which are beneficial to the human body in addition to natural loess. Natural loess is composed mainly of fine sand and has a large amount of calcium carbonate. It has a viscosity that is not easily broken by this calcium carbonate, and has a property of changing to water paste by hydration with water. In addition, natural ocher contains quartz, feldspar, mica, calcite, and the like, and these substances are oxidized with iron to have a color of yellow, purple, red, gray, and pale green. Natural ocher of this nature is roasted at high temperature to make hard and insoluble active ocher. Since the active ocher is preserved as it is without losing the far-infrared effect of the natural ocher, it acts to reduce and prevent the harmfulness of the existing pavement that brings various environmental pollution and human skin diseases such as atopic dermatitis by the use of cement indiscriminately. In addition, activated ocher is hard and insoluble in water, so it is not water-pasted in rainy weather and maintains a certain strength. Activated ocher is used 15 to 25% by weight based on the total weight of the environment-friendly buffered ocher packaging composition, if less than 15% by weight does not meet the purpose of the present invention, when used in excess of 25% by weight other than active ocher This is because the required amount of ingredients can not be used. In addition, the activated ocher preferably has an average particle diameter of 1.5 mm or less.

In the present invention, the white cement is characterized in that the color of the portland cement is less gray than the conventional cement as white color, compared to the conventional cement. In addition, back cement was used to rule out the possibility that the color of the activated ocher is usually discolored by Portland cement. The back cement absorbs excess moisture in the packaging material, shortens the drying time and promotes internal curing through pozzolanic reactions, and also improves adhesion between activated ocher, rubber chip powder and silica sand. 3 to 7% by weight of the white cement is used. When the amount is less than 3% by weight, the effect of internal hardening is remarkably reduced. When the amount of the white cement is more than 7% by weight, rapid curing occurs and local cracks are generated in the composition.

In the present invention, the fine grain sand is not only to enhance the visibility and beautiful appearance by reflecting light, but also to perform the role of hard aggregates to contribute to improving the durability of the composition. Goun Gyu Sa is used 5 to 10% by weight, because less than 5% by weight is less visible light reflecting, if it exceeds 10% by weight, rather than reflecting the glare caused by the reflection of light interferes the occupant's safety.

In the present invention, in the waste rubber chip powder coated with the antimicrobial agent, rubber is usually disposed of to be discarded for replacement due to the characteristics of a product that is solidified and cured after a certain period of time, thereby recycling waste tires or waste rubber belts uniformly to a predetermined size. It is ground and powdered and coated using a resin binder, kerosene and a curing catalyst. If it is used without coating, it is unpleasant to users with a unique smell of rubber on the surface after installation. The method of coating the antimicrobial agent is organic alkoxysilane which is a reactive organic compound such as silver or copper salt, carbon black, etc. The mixed composition is mixed with a synthetic resin binder or the like to prepare a coating on the surface of waste rubber chip powder. The waste rubber chip powder uses 4 to 8% by weight based on the total weight of the buffer loess packaging composition, which is less than 4% by weight, which does not meet the object of the present invention, and when it is used in excess of 8% by weight, the waste rubber chip is used. The required amount of essential components other than the powder can not be used, and the waste rubber chip powder preferably maintains an average particle size within 1.5 mm.

Songseok stone used in the present invention is preferably selected and used in a single granularity within the range of 1.5mm for the permeability performance and the beautiful appearance of the surface. The quality meets the standard of KS F 2534 Structural Lightweight Aggregate, and the dry weight of pine stone is 1.4 or more and the unit weight is 600 kg / ㎥ or more. If less than 1% by weight is used, penetration of the fine grains is not smooth, and if it is used in excess of 2% by weight, the permeability is good and the required amount of essential components other than gypsum stone can not be used.

In the present invention, there are many ceramic companies in Korea, and a large amount of waste ceramics are generated from these companies every year, whereas the recycling degree of such waste ceramics has to be disposed of entirely as industrial waste. There was a problem that a large processing cost is required. In order to recycle this, the present invention uses crushed porcelain waste which is discarded as defective in manufacturing various porcelains in a single granule within a range of 1.5 mm. Waste ceramics are hard aggregates than activated ocher or rubber chip powder to ensure the durability of the buffered ocher pavement. If the amount of waste ceramics used is less than 2% by weight, it is insufficient to secure the abrasion resistance and durability of the buffered packaging surface, and when it is used in excess of 3% by weight, the shock buffering capacity of the buffered ocher packaging is lowered. This is because they do not use their required usage. Hard aggregates may include iron slag, a waste resource.

The plant flavor used in the present invention is extracted from the flower of the plant having a particular effect and has the ability to grow the plant itself, heal the disease and heal the wound. General chemical flavors are more disgusting when mixed with existing odors, while natural plant flavors remove various odors and affect the mental world, helping to relax and immerse yourself in deep meditation. The natural plant flavoring stock solution with the same function as the raw material was developed by the micro-encapsulated buffer ocher packaging composition with aroma. Phyto-flavored microcapsules are used in various forms according to the needs of users by encapsulating and solidifying liquid fragrance by forming a membrane on the outer wall using microcapsule technology. When the microcapsules are broken, the fragrance can be sustained for a long time by adding about 0.1 to 0.2% by weight of the plant flavor microcapsule to the environmentally friendly cushioning packaging composition. The microcapsules can be prepared with cerasin, gum arabic, fragrance components and curing agents. The detailed method is already well known to those skilled in the art, so a detailed description thereof will be omitted. Nanocapsules containing phyto-flavored undiluted solution use 0.1 ~ 0.2% by weight. If less than 0.1% by weight, the inherent efficacy of the perfume can not be sustained for a long time. . Plant flavors used in the present invention may be cosmos flavor, acacia flavor, rose flavor, chestnut flavor, herbal flavor and the like, in addition to the general flavor preferred by the general public can be used regardless of the type.

Wood chips formed with a rosin film used in the present invention may be produced by shredding the waste wood by a wood shredder, or may be used by using sawdust coming out as a by-product from the ash. In general, if wood chips are used as they are, they absorb moisture and decay over time, so they dry sufficiently to form a film with rosin to block decomposition by water and to prevent contact with oxygen in the air to function as a barrier. Not to facilitate bonding with the binder. Since the coating method of the wood chip is well known to those skilled in the art, a detailed description thereof will be omitted. Wood chips are used in 1 to 2% by weight, which is less than 1% by weight does not meet the purpose of the present invention, when used in excess of 2% by weight can not use the required amount of essential components other than wood chips Because. In addition, it is preferable that the wood chips also maintain an average particle diameter of 1.5 mm or less for the purpose of matching the uniformity of the active ocher and the material.

The scented herb, ummu fern extract and water-soluble acrylic urethane mixed resin used in the present invention are combined with activated ocher, fine grain sand, rubber chip powder, wood chips and pine stone, porcelain chips, and to prevent scattering or loss of the materials. In general, the buffer ocher packaging material using a urethane binder, but the odor of the urethane is severe due to high temperature in the summer, the environmentally friendly and natural ingredients include herb and radish extract. It is a kind of seaweed, mixed with vinegar and silver scented herb and ummu fern 20: 1 by weight, and heated to high temperature to make an adhesive, and also mixed with acrylic urethane which has fluidity when heated as a polymer. . The mixing ratio is most preferably about 4: 1 mixed with the mixed extract and the acrylic urethane based on the weight of the mixed extract of scented herbs and radish. If more acrylic urethane is mixed, the smell will continue to occur, and if you mix more herbs and herbaceous extract, the price will be expensive and economical. The resin is used in the range of 25 to 35% by weight, which is less than 25% by weight of the aggregate, the binding strength of the aggregate is weak, the durability of the eco-friendly buffered ocher packaging composition is less durable, and when used in excess of 35% by weight, it takes a long time to cure other than the binder This is because the required amount of essential ingredients is not used.

The pigment used in the present invention is preferably selected from iron oxide among the clay mineral pigments, but inorganic pigments such as barium sulfate may be used. It is preferable to use red color, but other colors such as yellow may be used to secure more visibility and harmony with the surroundings. Iron oxide is used 5 to 10% by weight because less than 5% by weight is not clear color, when used more than 10% by weight does not use the required amount of essential components other than iron oxide.

The antimicrobial agent used in the present invention may use a variety of antimicrobial agents, but an antimicrobial agent composed of silver nano powder is most preferred. Silver powder, which has been sintered to 0.001 micrometer or less like silver, is not only an inorganic antimicrobial agent that can penetrate into the pores of the composition to obtain antibacterial and bactericidal effects, but also prevents mold from forming in the eco-friendly buffered ocher packaging material It has been proven to have antibacterial effect for a long time without falling. Therefore, there is an effect of preventing health to the athlete when the packed buffer ocher packaging composition is used in the playground. Antimicrobial agent made of silver nano powder is used 0.1 ~ 0.3% by weight, because less than 0.1% by weight of the antibacterial effect is lowered when used in excess of 0.3% by weight for economic reasons increase the unit price.

The ultraviolet screening agent used in the present invention shields the ultraviolet rays that are irradiated on the environmentally cured yellow clay packaging composition and prevents the composition from being decomposed, deteriorated or oxidized by ultraviolet rays to improve durability. As the sunscreen, it is preferable to use an organic sunscreen such as oxybenzone or an inorganic sunscreen such as zinc oxide, but any one can be used as long as it is commonly used. 1 ~ 1.5% by weight of the sunscreen is used, less than 1% by weight is not enough UV protection effect, when used in excess of 1.5% by weight of the sunscreen effect is slight increase, but only the unit price increases because it is not economical .

In the composition of the present invention, a mixture of magnesium silicate and colloidal silica may be further used as UV resistance and surface hardening component. They not only strengthen the buffered ocher packaging composition with its strong alkalinity, but also make the surface texture dense to increase the durability of the buffered ocher packaging composition.

The deterioration inhibitor used in the present invention uses a naphtanic hydrocarbon or an isoparaffinic hydrocarbon, and is used for reinforcing urethane and the like. In particular, the purpose of the present invention is to prevent a phenomenon in which the smell of urethane or the like becomes worse due to the high temperature in the middle of summer, and to prevent lifting due to deterioration of the packaging, thereby increasing the durability of the composition. The deterioration inhibitor is used in an amount of from 2 to 3% by weight. When the amount of the deterioration inhibitor is less than 2% by weight, the effect of preventing deterioration is insufficient. When the amount of the deterioration inhibitor is more than 3% by weight, the cost of the composition increases.

Tourmaline used in the present invention is the only mineral having permanent electrical properties among the minerals on earth. Tourmaline is widely known to release air ions, purify water, remove odors, and promote metabolism by releasing negative ions and far infrared rays through antioxidant activity and a small current of 0.06A. Tourmaline should be added within the range of 0.2 to 0.5% by weight, since addition of less than 0.2% significantly reduces the effect of anion and far-infrared release, and when it exceeds 0.5%, the unit cost of the composition increases with expensive tourmaline. .

In the composition of the present invention, a fluorescent substance or a photoluminescent substance may be further added. This is to induce interest to the driver, cyclist or pedestrian at night, to double the exercise effect and to prevent safety accidents.

While the invention has been described above with reference to the preferred embodiments, it will be apparent to those skilled in the art that many various obvious modifications are possible without departing from the scope of the invention. Therefore, the scope of the invention should be construed by the claims described to include examples of many such variations.

≪ Example 1 >

20% by weight activated ocher, 5% by weight cement, 8% by weight Goeunsa sand, 6% by weight waste rubber chip powder coated with antimicrobial agent, 1% by weight Song Seok, 2% by weight waste ceramics, 1 weight of wood chips formed with rosin 25% by weight of a binder containing a mixture of%, scented candles, agar, and water-soluble acrylic urethane was added to the stirrer, followed by stirring. %, 1% by weight of sunscreen, 2% by weight of antioxidant, 0.5% by weight of tourmaline, 20% by weight of water was further mixed for 5 minutes to prepare an environmentally friendly buffer ocher packaging material composition. At this time, the activated ocher, pine scavenger, waste ceramics, wood chips are particles within 1.5 mm, plant flavor is acacia flavor, mixed extract of scented candle and wormwood and water-soluble acrylic urethane ratio is 4: 1 ratio, the sunscreen is oxybenzone-based The deterioration inhibitor was a naphthenic hydrocarbon.

<Example 2>

20% by weight activated ocher, 5% by weight cement, 8% by weight Goeunsa sand, 5% by weight waste rubber chip powder coated with antimicrobial agent, 2% by weight Song Seok, 2% by weight waste ceramics, 1 weight of wood chips formed with rosin 25% by weight of a binder containing a mixture of%, scented candles, agar, and water-soluble acrylic urethane was added to the stirrer, followed by stirring, followed by 0.2% by weight of nanocapsules containing vegetable flavor solution, 8% by weight of iron oxide, and 0.3% of antimicrobial powder. %, 1% by weight of sunscreen, 2% by weight of antioxidant, 0.5% by weight of tourmaline, 20% by weight of water was further mixed for 5 minutes to prepare an environmentally friendly buffer ocher packaging material composition. At this time, the activated ocher, pine scavenger, waste ceramics, wood chips particles within 1.5㎜, plant flavors of acacia flavor, mixed extract of scented candles and urticaria and water-soluble acrylic urethane ratio of 4: 1 ratio, the sunscreen is oxybenzone-based The deterioration inhibitor was a naphthenic hydrocarbon.

<Example 3>

20% by weight activated ocher, 5% by weight cement, 8% by weight Goeunsa sand, 5% by weight waste rubber chip powder coated with antimicrobial agent, 1% by weight Song Seok, 3% by weight waste ceramics, 1 weight of wood chips formed with rosin 25% by weight of a binder containing a mixture of%, scented candles, agar, and water-soluble acrylic urethane was added to the stirrer, followed by stirring. %, 1% by weight of sunscreen, 2% by weight of antioxidant, 0.5% by weight of tourmaline, 20% by weight of water was further mixed for 5 minutes to prepare an environmentally friendly buffer ocher packaging material composition. At this time, the activated ocher, pine scavenger, waste ceramics, wood chips particles within 1.5㎜, plant flavors of acacia flavor, mixed extract of scented candles and urticaria and water-soluble acrylic urethane ratio of 4: 1 ratio, the sunscreen is oxybenzone-based The deterioration inhibitor was a naphthenic hydrocarbon.

In order to more easily understand the characteristics of the above Examples 1 to 3 are presented comparative examples that can be compared with the embodiments of the present invention.

Comparative Example 1

50% by weight of yellow clay, 30% by weight of waste tire chips and 20% by weight of EVA emulsion were added to a stirrer and stirred to prepare a general buffered loess pavement composition.

Comparative Example 2

30% by weight of ordinary soil, 40% by weight of yellow soil, 20% by weight of EVA emulsion, and 10% by weight of Portland cement were added to a stirrer to prepare a general sodium cement packaging material composition.

The following test example is an experiment comparing the characteristics of the examples according to the present invention with the characteristics of Comparative Examples 1 and 2 in order to more easily understand the characteristics of Examples 1 to 3 according to the present invention disclosed above The results are shown.

<Test Example>

Eco-friendly buffered loess packaging composition according to the embodiment and the packaging composition prepared by Comparative Example 1 and Comparative Example 2 was evaluated by curing for 7 days is shown in Table 1.

division Surface Cracking Permeability coefficient (cm / sec) Wear loss rate (%) Example 1 none 100 × 10 ^-2 1.8 Example 2 none 120 × 10 ^-2 1.7 Example 3 none 80 × 10 ^-2 1.5 Comparative Example 1 Crack 5 × 10 ^-2 18.3 Comparative Example 2 Crack 7 × 10 ^-2 27.9

As shown in Table 1, Examples 1 to 3 not only improved the occurrence of cracks and improved the permeability up to 24 times, but also significantly reduced the wear loss rate to improve the durability of the buffer loess packaging composition. Surface cracks were visually observed, and the coefficient of permeability was measured by KS F 2322 (water permeability test method) and the wear loss rate (STI-TM 0012) of the packaging material as follows.

O measuring instrument; Weed Taber Abrasion Tester

O measurement condition; After immersing the package in a constant temperature water tank for 24 hours, it was taken out and left for 30 minutes at room temperature.

O disk speed = 60 rpm

O load = 500 grams

O wear tab = H-10 (Coarse type)

* Translate ; Wear loss rate = 100 × (before measurement Wt - after measurement Wt) / before measurement Wt

Claims (5)

Activated clay 15-25% by weight, 3-7% by weight cement, 5-10% by weight Goeunsa sand, 4-8% by weight of antimicrobial coated rubber chip powder, 1-2% by Song-seok stone, 2 ~ by waste ceramic 3% by weight, 0.1 ~ 0.2% by weight of nanocapsules containing plant flavor stock solution, 1 ~ 2% by weight of wood chips coated with rosin, 25 ~ 35% by weight of resin mixed with scented herbs, radish and water-soluble acrylic urethane, iron oxide 5 ~ 10% by weight, antimicrobial agent 0.1 ~ 0.3% by weight of silver nano powder, sunscreen 1 ~ 1.5% by weight, deterioration inhibitor 2 ~ 3% by weight, tourmaline 0.2 ~ 0.5% by weight, characterized in that consisting of 20 to 25% by weight of water Eco-friendly buffered ocher pavement composition for the road. The eco-friendly buffered ocher pavement composition of claim 1, further comprising a fluorescent material or a photoluminescent material. The environmentally friendly buffer loess pavement composition of claim 1, wherein the plant flavor is cosmos flavor, acacia flavor, rose flavor, chestnut flavor, or herbal flavor. The green cushioning ocher packing material composition according to claim 1, wherein the ultraviolet screening agent is a mixture of oxybenzone or zinc oxide. According to claim 1, wherein the deterioration agent eco-friendly buffered loess pavement composition, characterized in that the naphtan-based hydrocarbon or isoparaffinic hydrocarbon.