KR100976276B1 - General-purpose nonslip pad with safety cover for shoes - Google Patents

General-purpose nonslip pad with safety cover for shoes Download PDF

Info

Publication number
KR100976276B1
KR100976276B1 KR1020080024949A KR20080024949A KR100976276B1 KR 100976276 B1 KR100976276 B1 KR 100976276B1 KR 1020080024949 A KR1020080024949 A KR 1020080024949A KR 20080024949 A KR20080024949 A KR 20080024949A KR 100976276 B1 KR100976276 B1 KR 100976276B1
Authority
KR
South Korea
Prior art keywords
weight
shoe
slip
protective cover
main body
Prior art date
Application number
KR1020080024949A
Other languages
Korean (ko)
Other versions
KR20090099772A (en
Inventor
강경래
강태순
Original Assignee
강경래
강태순
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 강경래, 강태순 filed Critical 강경래
Priority to KR1020080024949A priority Critical patent/KR100976276B1/en
Publication of KR20090099772A publication Critical patent/KR20090099772A/en
Application granted granted Critical
Publication of KR100976276B1 publication Critical patent/KR100976276B1/en

Abstract

본 발명은 보호커버를 가진 신발 장착용 미끄럼 방지 패드에 관한 것으로, 각종 산업현장에서 착용되는 안전화는 물론이고 일반 신발의 바닥에 덧대어 착용할 수 있는 구조를 가짐과 동시에 발등을 보호하는 보호커버를 가짐으로써, 밑창이 마모되어 미끄럼 방지 기능이 상실된 안전화 등의 특수화나 일반적인 신발 착용으로 물이나 기름에 의해 미끄러지기 쉬운 위험이 있는 곳에 간단하게 착용하여 각종 안전 사고를 예방할 수 있고, 특히 용접 등의 불꽃으로부터 발등이나 신발끈을 보호할 수 있는 보호커버를 가진 신발 장착용 미끄럼 방지 패드에 관한 것이다.The present invention relates to a non-slip pad for mounting a shoe with a protective cover, as well as safety shoes worn in various industrial sites, as well as having a structure that can be worn on the bottom of the general shoe and at the same time to protect the protective cover By wearing it, it is possible to prevent various safety accidents by simply wearing it where there is a risk of slipping due to water or oil by specialization such as safety shoes that wear outsole and loss of anti-slip function or wearing general shoes. It relates to a non-slip pad for shoe mounting with a protective cover that can protect the instep or shoelaces from.

본 발명에 따르면, 미끄러짐이 방지되는 재질로 된 본체; 본체의 전방에 신발앞부분삽입공을 형성하면서 둥근 고리 형상으로 연결된 발등고리; 본체의 후방에 넓은 판체로 형성되고, 'ㄷ'형태의 절결부가 형성되어 'ㄷ'형상의 보호덮개가 형성된 덮개부;를 포함하여 구성된 보호커버를 가진 신발 장착용 미끄럼 방지 패드가 제공된다.According to the invention, the main body made of a material which is prevented from slipping; Foot ring connected in a round ring shape while forming the front of the shoe insertion hole in the front of the main body; A non-slip pad for mounting a shoe having a protective cover formed of a wide plate body at the rear of the main body and having a cut portion of a 'c' shape formed with a 'c' shaped protective cover;

신발, 안전화, 보호커버, 용접, 미끄럼방지 패드 Shoe, safety shoes, protective cover, welding, non-slip pad

Description

보호커버를 가진 신발 장착용 미끄럼 방지 패드{General-purpose nonslip pad with safety cover for shoes}Non-slip pad for shoe mounting with protective cover {General-purpose nonslip pad with safety cover for shoes}

본 발명은 보호커버를 가진 신발 장착용 미끄럼 방지 패드에 관한 것으로, 각종 산업현장에서 착용되는 안전화는 물론이고 일반 신발의 바닥에 덧대어 착용할 수 있는 구조를 가짐과 동시에 발등을 보호하는 보호커버를 가짐으로써, 밑창이 마모되어 미끄럼 방지 기능이 상실된 안전화 등의 특수화나 일반적인 신발 착용으로 물이나 기름에 의해 미끄러지기 쉬운 위험이 있는 곳에 간단하게 착용하여 각종 안전 사고를 예방할 수 있고, 특히 용접 등의 불꽃으로부터 발등이나 신발끈을 보호할 수 있는 보호커버를 가진 신발 장착용 미끄럼 방지 패드에 관한 것이다.The present invention relates to a non-slip pad for mounting a shoe with a protective cover, as well as safety shoes worn in various industrial sites, as well as having a structure that can be worn on the bottom of the general shoe and at the same time to protect the protective cover By wearing it, it is possible to prevent various safety accidents by simply wearing it where there is a risk of slipping due to water or oil by specialization such as safety shoes that wear outsole and loss of anti-slip function or wearing general shoes. It relates to a non-slip pad for shoe mounting with a protective cover that can protect the instep or shoelaces from.

신발의 밑창은 미끄러짐을 방지함과 동시에 바닥면과의 접촉시 충격을 완화시키는 목적으로 사용된다. 특히 산업 현장에서 사용되는 안전화 등의 특수화는 물이나 기름 등의 바닥에 미끄러지는 것을 방지하는 것이 큰 목적 중의 하나였다.The sole of the shoe is used for the purpose of preventing slipping and at the same time to alleviate the impact of contact with the floor. In particular, the specialization of safety shoes used in the industrial field was one of the main purposes to prevent slipping on the floor of water or oil.

일반적으로 미끄럼을 방지하기 위한 밑창의 경우는 바닥면과 접촉되는 면에 다수개의 돌기를 형성시키는 구조이고, 이는 금형 내에 인위적으로 표면을 거칠게 하여 성형하였으므로, 금형 제작이 길어 지고 생산 단가가 상승될 뿐 아니라 제품 성형시 밑창 표면에 형성된 요철 상태가 사용시 마모에 의해 없어져 미끄럼 방지 기능을 상실하였다.In general, the sole for preventing slip is a structure that forms a plurality of protrusions on the surface in contact with the bottom surface, which is formed by artificially roughening the surface in the mold, so that the mold production is long and the production cost is increased. Rather, the irregularities formed on the sole surface during product molding are lost by wear in use, and thus the anti-slip function is lost.

그리고 밑창의 바닥에 다수개의 돌기를 형성시키거나, 스파이크를 설치하여 바닥면을 압지하는 등의 미그럼 방지 구조가 있었다.In addition, there was a non-slip structure such as forming a plurality of protrusions on the bottom of the sole, or installing a spike to press the bottom surface.

또한 밑창의 재질을 미끄러지지 않는 천연 고무 등의 재질로 함으로써 물이나 기름이 묻은 바닥에서 미끄러지지 않도록 하고 있다.In addition, the sole of the sole is made of a non-slip natural rubber, so that it does not slip on water or oily floors.

상기와 같이 다양하게 제조되는 안전화 등의 특수화나 일반 신발의 경우 주로 밑창의 재질이나 형상에 미끄러짐을 방지하는 기능이 있다. 그러나 물이나 기름 등에 접촉되는 밑창은 시간이 경과됨에 따라 경화되어 미끄럼 방지 기능이 저하되고, 마모로 인하여 더욱더 미끄러지는 문제가 있다. 이와 같이 미끄럼 방지 기능이 저하되면 안전화 등은 교체하여 사용하여 함으로써 교체 비용이 과다하게 지출되고, 이러한 지출의 경감을 위하여 미끄럼 방지 기능이 상실된 안전화를 계속 착화함으로써 안전 사고의 위험이 상존하게 된다.Specialized shoes such as safety shoes manufactured in various ways as described above, or the general shoe has a function to prevent slipping on the material or shape of the sole. However, the sole in contact with water or oil is hardened over time, the anti-slip function is deteriorated, there is a problem of sliding more and more due to wear. As such, when the anti-slip function is lowered, the replacement cost is excessively used by replacing the safety shoes, and the risk of a safety accident remains by igniting the safety shoes that have lost the anti-slip function in order to reduce such expenses.

따라서 본 발명은 미끄럼 방지 기능이 저하된 안전화도 계속 사용할 수 있도록 하고, 물에 의한 미끄러짐을 보다 효과적으로 방지하는 것과, 기름에 의해 미끄러지는 것을 보다 효과적으로 방지하는 것을 구별함으로써, 안전사고의 방지를 더욱더 방지할 수 있도록 함에 목적이 있다.Therefore, the present invention can continue to use the safety shoes with reduced anti-slip function, and further prevents the prevention of safety accidents by distinguishing between more effectively preventing slippage by water and more effectively preventing slipping by oil. The purpose is to make it possible.

그리고 불꽃이 튀는 산업현장인 용접 장소에서는 용접 불꽃이 안전화의 끈에 튀어 불이 붙거나, 계속되는 손상에 의해 끈이 끊어지는 등의 문제점이 있었다. 이는 끈을 보호하는 구조가 없었기 때문이다.And in the welding site of the industrial site where sparks splash, there was a problem that the welding sparks bounce off the laces of the safety shoes and catch fire, or the strings are broken by continuous damage. This is because there is no structure to protect the strings.

따라서 본 발명은 미끄러짐을 방지하는 구조를 가지는 것은 물론이고, 용접하는 산업현장 등에서도 다양하게 활용될 수 있는 구조의 미끄럼 방지 패드를 제공함에 목적이 있다.Accordingly, an object of the present invention is to provide a non-slip pad having a structure that prevents slippage, as well as a structure that can be variously used in welding industrial sites.

상기 목적을 달성하기 위하여 미끄럼 방지기능이 저하된 신발이나 어떠한 신발의 밑창에 간단하게 착용할 수 있는 구조를 가진 패드를 제공하게 된다. 즉 신발 밑창에 덧대어 착용할 수 있고, 탈거가 용이한 구조를 가진 것으로, 물과 기름에 각각 적합한 재질로 된 것으로 용이하게 선택하여 사용할 수 있는 패드를 제공한다. 또한 신발에 장착했을 때 발등 부분을 덮을 수 있는 보호커버를 가짐으로써, 용접 불티 등으로부터 신발의 발등이나 신발 끈 등을 보호할 수 있다.In order to achieve the above object is to provide a pad having a structure that can be easily worn on the shoe of the non-slip function or any shoe sole. That is, the pad can be worn on the sole of the shoe and has a structure that is easy to remove, and is made of a material suitable for water and oil. In addition, by having a protective cover that can cover the instep portion when attached to the shoe, it is possible to protect the instep of the shoe, shoe laces, etc. from welding sparks.

상기와 같이 밑창에 덧대어 착용할 수 있는 구조를 제공하고, 물과 기름에 각각 적합한 재질을 용이하게 적용할 수 있도록 한 구조를 제공함으로써, 일반적인 신발로서 미끄러짐을 효과적으로 방지할 수 있고, 밑창의 경화와 마모로 인한 미끄러짐 방지 기능이 저하된 안전화 등의 특수화를 계속 사용할 수 있음으로써, 안전사고를 방지하는 효과는 물론이고 잦은 신발 교체를 방지할 수 있게 된다.By providing a structure that can be worn over the sole as described above, and by providing a structure that can be easily applied to each material suitable for water and oil, it can effectively prevent slip as a general shoe, hardening the sole By continuing to use specializations such as safety shoes with reduced slip protection due to wear and tear, it is possible to prevent frequent accidents as well as to prevent safety accidents.

뿐만 아니라 용접 등의 작업 환경에서도 신발등이나 신발 끈 등을 보다 효과적으로 보호할 수 있게 된다.In addition, it is possible to more effectively protect shoes and shoelaces in the working environment, such as welding.

본 발명은 미끄러짐이 방지되는 재질로 된 본체(1); 본체(1)의 전방에 신발앞부분삽입공(2)을 형성하면서 둥근 고리 형상으로 연결된 발등고리(3); 본체(1)의 후방에 넓은 판체로 형성되고, 'ㄷ'형태의 절결부(4)가 형성되어 'ㄷ'형상의 보호덮개(5)가 형성된 덮개부(6);를 포함하여 구성된다.The present invention is a body (1) made of a material to prevent slip; Foot ring (3) connected in a round ring shape while forming the front portion of the shoe insertion hole (2) in front of the main body (1); The cover part 6 is formed of a wide plate body at the rear of the main body 1, and a cutout portion 4 having a 'c' shape is formed to form a 'c' shaped protective cover 5.

그리고, 상기 본체(1)는 물에 미끄러지지 않는 재질이고, 본체(1)에는 기름에 미끄러지지 않는 재질로 된 내유밀착패드(7)가 다수 개 부착된다. 또한, 본체(1)에는 내유밀착패드(7)가 부착될 수 있는 부착홈(8)이 형성될 수도 있다.The main body 1 is made of a material which does not slip in water, and the main body 1 has a plurality of oil-tight pads 7 made of a material which does not slip in oil. In addition, the main body 1 may be provided with an attachment groove 8 to which the oil-resistant pad 7 may be attached.

이와 같이 본 발명은 하나의 패드에 물과 기름에 각각 미끄러지지 않는 재질이 동시에 형성될 수 있고, 물에 미끄러지지 않는 재질의 패드만을 사용할 수도 있다. 이는 본체(1)에 내유밀착패드(7)를 선택에 따라 부착하여 사용할 수 있는 구조이기 때문이다. 뿐만아니라 신발에 장착하였을 때 보호덮개(5)가 발등을 덮어 신발이나 신발끈(9)을 보호할 수 있게 된다.As described above, the present invention may simultaneously form a material that does not slip into water and oil on one pad, and may use only pads that do not slip into water. This is because the oil-resistant adhesive pad 7 can be attached to the main body 1 according to the selection. In addition, the protective cover (5) when the shoe is attached to the foot can protect the shoe or shoelaces (9).

물에 미끄러지지 않는 특징을 가진 본체(1)는 천연고무(NR, Natural Rubber) 25~35중량％, 카본 마스터 배치(M/B : Master Batch) 15~25중량％, 부타디엔 고무(BR, Polybutadiene Rubber) 5~15중량％, 아연화 10~20중량％, 스테아린산(ST/acid) 0.2~0.3중량％, 산화철 10~20중량％, 산화티타늄 10~20중량％, 점착부여제 0.5~1.0중량％, 씨젯(CZ) 0.5~1.0중량％, 디(D) 0.2~0.3중량％, 티에스(TS) 0.05~0.15중량％, 유황 0.5~1.5중량％로 이루어진다.
상기의 CZ, D, TS 등은 동양제철화학에서 생산되는 제품명이고, D는 화학명 1,3-DIPHENYL GUANIDINE로서, 천연고무, 합성고무에 광범위하게 사용되고, 임계온도 140℃ 전후의 대표적인 염기성 촉진제이다. CZ은 화학명 N-CYCLOHEXYL BENZOTHIAZYL 2-SULFENAMIDE로서, 지효성 촉진제의 대표적인 것으로 FURNACE BLACK의 다량배합에도 안전한 가류가 가능하며 인장강도가 요구되는 제품에 사용하고 특히 SBR에 적당하다. TS는 화학명 TETRAMETHYL THIURAM로서, NR, IR, BR, SBR, NBR, IIR 및 LATEX용 초촉진제로 성능은 TT, TET와 비슷하나 SCORCH성이 적고, 가류제 용도로는 사용하지 않는다. 임계온도는 105℃전후로 THIAZOLE계 촉진제의 활성제로 작용한다.The main body 1, which does not slip into water, has 25 to 35% by weight of natural rubber (NR), 15 to 25% by weight of carbon master batch (M / B), and butadiene rubber (BR, polybutadiene rubber). ) 5-15 wt%, galvanization 10-20 wt%, stearic acid (ST / acid) 0.2-0.3 wt%, iron oxide 10-20 wt%, titanium oxide 10-20 wt%, tackifier 0.5-1.0 wt%, It consists of 0.5-1.0 weight% of Seajet (CZ), 0.2-0.3 weight% of di (D), 0.05-0.15 weight% of TS (TS), and 0.5-1.5 weight% of sulfur.
CZ, D, TS and the like are product names produced by Dongyang Steel Chemical, and D is the chemical name 1,3-DIPHENYL GUANIDINE, which is widely used in natural rubber and synthetic rubber, and is a representative basic accelerator around 140 ° C of critical temperature. CZ is the chemical name N-CYCLOHEXYL BENZOTHIAZYL 2-SULFENAMIDE, which is a representative of the slow-release accelerator. It is safe for vulcanization even in large amounts of FURNACE BLACK, and is suitable for products requiring tensile strength, especially suitable for SBR. TS is the chemical name TETRAMETHYL THIURAM. It is a super accelerator for NR, IR, BR, SBR, NBR, IIR, and LATEX. Its performance is similar to that of TT and TET, but its SCORCH property is low, and it is not used for vulcanizing agents. The critical temperature acts as an activator of THIAZOLE type accelerator around 105 ° C.

그리고 기름에 미끄러지지 않는 특징을 가진 내유밀착패드(7)는 니트릴 부타디엔 고무(NBR, Nitrile Butadiene Rubber) 25~35중량％, 카본 마스터 배치(M/B : Master Batch) 15~25중량％, 부타디엔 고무(BR, Polybutadiene Rubber) 5~15중량％, 아연화 10~20중량％, 스테아린산(ST/acid) 0.2~0.3중량％, 산화철 10~20중량％, 산화티타늄 10~20중량％, 점착부여제 0.5~1.0중량％, CZ 0.5~1.0중량％, D 0.2~0.3중량％, TS 0.05~0.15중량％, 유황 0.5~1.5중량％로 이루어진다.In addition, the oil-resistant adhesive pad 7 having a non-slip property in oil is 25 to 35% by weight of nitrile butadiene rubber (NBR), 15 to 25% by weight of carbon master batch (M / B), butadiene rubber (BR, Polybutadiene Rubber) 5-15% by weight, 10-20% by weight zinc, 0.2-0.3% by weight stearic acid, 10-20% by weight iron oxide, 10-20% by weight titanium oxide, tackifier 0.5 It consists of -1.0 weight%, CZ 0.5-1.0 weight%, D 0.2-0.3 weight%, TS 0.05-0.15 weight%, and sulfur 0.5-1.5 weight%.

상기에 사용되는 재질의 특성은 아래와 같다. 우선 물에 미끄러지지 않는 특성을 가지는 천연고무는 모든 고무중 촉감이 좋고, 기계적 성질이 우수하여, 자동차 타이어, 산업 트럭 타이어, 신발, 호스, 벨트, 공기 스프링, 일반용 및 공업용품 등에 사용된다.Properties of the material used in the above is as follows. First of all, natural rubber, which has a property of not slipping in water, has good feel and excellent mechanical properties among all rubbers, and is used in automobile tires, industrial truck tires, shoes, hoses, belts, air springs, general and industrial products, and the like.

기름에 미끄러지지 않는 특성을 가진 니트릴 부타디엔 고무는 내유, 내마모, 내노화성이 뛰어나, 오일 씰, 가스켓, 내유 호스, 콘베어 벨트, 인쇄 롤, 방직용 top roll 등의 내유 제품에 사용된다.Nitrile butadiene rubber, which is non-slip, has excellent oil resistance, abrasion resistance, and aging resistance, and is used in oil resistance products such as oil seals, gaskets, oil hoses, conveyor belts, printing rolls, and textile top rolls.

이하의 성분은 물에 미끄러지지 않는 특성을 가지는 것과, 기름에 미끄러지지 않는 특성을 가지는 것 모두에 포함되는 성분이다.The following components are components included in both the characteristics which do not slip into water and those which do not slip in oil.

카본 마스터 배치(Carbon M/B)는 카본이 포함된 것으로 강도를 향상시킨다. 부타디엔 고무(BR, Polybutadiene Rubber)는 NR보다 탄성이 좋고 내마모성이 우수하여 자동차 및 항공기용 타이어, 신발, 방진고무, 고무롤, 벨트, 호스 등의 공업용품에 사용된다.Carbon M / B contains carbon and improves strength. Butadiene rubber (BR) has better elasticity and better wear resistance than NR, and is used in industrial products such as tires for automobiles and airplanes, shoes, dustproof rubber, rubber rolls, belts, and hoses.

가류제로서 아연화와, 스테아린산(ST/acid)이 사용되고, 아연화는 가황 촉진제의 역할도 하는 것으로 고무 제품들을 보다 유용한 것으로 만드는 역할을 한다.As a vulcanizing agent, zinc and stearic acid (ST / acid) are used, and zincation also acts as a vulcanization accelerator, making rubber products more useful.

마찰력 향상을 위하여 산화철과 산화티타늄이 사용되고, 미끄럼 방지를 위한 점착력의 부여를 위하여 점착부여제가 사용된다. 점착부여제는 고무덩어리만 녹인다고 해서 끈적거리는 점착제가 되는 것은 아니다. 끈적거림을 나타내기 위한 특수한 물질을 첨가하는데 바로 이것이 점착부여제(Tackifier)다. 고무는 보통 분자량이 수십만~수백만 정도가 되는 고분자 물질이지만 점착부여제는 몇백~3,4천 정도 되는 것들이 대부분이다. 주로 합성된 것들이 많지만 소나무의 송진과 같은 것도 사용되는 경우가 있다. 점착제의 점착성을 높이기 위하여 배합하는 재료로 천연 수지계(로진, 폴리테르판 수지 등)와 합성 수지계(석유 수지, 쿠마론, 인덴 수지 등)가 있고, 본 발명은 어떠한 것을 사용하더라도 상관없다.Iron oxide and titanium oxide are used to improve friction, and a tackifier is used to impart adhesion to slip. A tackifier does not become a sticky adhesive just by melting a lump of rubber. It adds a special substance to show stickiness, which is a tackifier. Rubber is usually a polymer with a molecular weight ranging from hundreds of thousands to millions, but most of the tackifiers are from several hundred to three thousand. Many are synthesized, but pine pine rosin may be used. In order to raise the adhesiveness of an adhesive, the material mix | blended includes a natural resin type | system | group (a rosin, a polyterpane resin, etc.) and a synthetic resin system (petroleum resin, coumarone, an indene resin, etc.), and this invention may use what kind of thing.

그리고 가류 촉진제로서 D, M, DM, CZ, NA22, EUR, TT, TS, TRA, PZ, EZ, BZ, TL 중에서 어떠한 것이라도 가능하나, 본 발명에서는 CZ, D, TS가 사용되었으며, 가류촉진제는 고무와 가류제와의 가류 반응을 촉진시키며 가류시간의 단축, 가류온도 저하, 물리적/화학적 성질을 저하시키는 약품이다.And any one of D, M, DM, CZ, NA22, EUR, TT, TS, TRA, PZ, EZ, BZ, TL as a vulcanization accelerator, CZ, D, TS was used in the present invention, vulcanization accelerator Is a chemical that accelerates the vulcanization reaction between rubber and vulcanizing agent, shortens vulcanization time, decreases vulcanization temperature and decreases physical and chemical properties.

그리고 가황제로서 S가 사용되는데, 이는 화학적인 가교 반응이 고무분자간에 이루어져 탄성의 상태 변화를 갖도록 첨가된다.And S is used as a vulcanizing agent, which is added so that chemical crosslinking reaction is made between rubber molecules to have a change of state of elasticity.

상기와 같은 성분들로 물에 미끄러지지 않는 패드 또는 기름에 미끄러지지 않는 패드가 제조되고, 이러한 패드의 구조적인 특성은 도 1 내지 도 3에 도시되어 있고, 이의 사용 상태도가 도 4과 도 5에 도시되어 있다.A pad that does not slip into water or a pad that does not slip into oil is manufactured with the above components, and the structural characteristics of the pad are shown in FIGS. 1 to 3, and the state of use thereof is shown in FIGS. 4 and 5. have.

도 4와 도 5에 도시된 바와 같이, 신발의 밑 부분에 본 발명의 패드를 넣어 체결한다. 발등고리(3)와 덮개부(6)를 위로 젖히고, 신발의 앞부분을 보호덮개(5)를 들어 올리면서 삽입하면 절결부(4)가 신발이 삽입되는 구멍으로 형성된다. 그리고 계속하여 신발의 앞부분을 발등고리(3)에 의해 형성된 신발앞부분삽입공(2)에 삽입하게 되면, 도 4와 도 5와 같이 신발에 장착된다.As shown in Figure 4 and 5, the pad of the present invention is fastened to the bottom of the shoe. When the foot loop (3) and the cover part 6 is folded up, and the front part of the shoe is inserted while lifting the protective cover (5), the cutout part (4) is formed as a hole into which the shoe is inserted. Then, when the front part of the shoe is inserted into the shoe front part insertion hole 2 formed by the foot loop 3, the shoe is mounted on the shoe as shown in FIGS. 4 and 5.

이와 같이 착용되면, 본체(1)가 작업장 등의 바닥면에 접촉되는데, 상기 접촉부분은 물에 젖은 바닥면에서 미끄러지는 것을 효과적으로 방지하는 재질로 되어 있다.When worn in this way, the main body 1 is in contact with the bottom surface of the workplace and the like, the contact portion is made of a material that effectively prevents slipping on the bottom surface wet with water.

따라서 작업 환경이 유성 재질의 액상이 젖어 있는 경우는 적합하지 않을 수 있다. 이 경우는 내유밀착패드(7)를 부착하여 사용할 수 있다. 내유밀착패드(7)는 본 발명의 제조시에 일체로 형성시킬 수도 있고, 필요시 부착할 수 있는 구조로 할 수 있다.Therefore, the working environment may not be suitable when the liquid phase of the oily material is wet. In this case, the oil-resistant adhesive pad 7 can be attached and used. The oil-resistant adhesive pad 7 may be integrally formed at the time of manufacture of the present invention and may have a structure that can be attached if necessary.

도 2에 도시된 바와 같이 본체(1)에 내유밀착패드(7)를 부착하여 사용하면, 기름이 묻은 바닥에서 미끄러짐을 효과적으로 방지할 수 있게 된다. 그리고 부착홈(8)을 형성시켜 내유밀착패드(7)의 부착과 사용을 보다 용이하게 할 수도 있다.As shown in FIG. 2, when the oil-resistant adhesion pad 7 is attached to the main body 1 and used, the slippage can be effectively prevented from the oiled floor. In addition, the attachment groove 8 may be formed to facilitate attachment and use of the oil-resistant adhesion pad 7.

그리고, 도 4와 도 5에 도시된 바와 같이, 보호덮개(5)가 신발끈(9)을 덮어, 용접 현장 등의 불꽃이 튀기는 곳에서 사용시 신발끈(9)을 보호할 수 있게 된다.And, as shown in Figure 4 and 5, the protective cover 5 covers the shoelace (9), it is possible to protect the shoelace (9) in use in the place where the sparks splash, such as welding sites.

도 1은 본 발명의 전체 사시도1 is an overall perspective view of the present invention

도 2는 본 발명의 다른 실시 예의 사시도2 is a perspective view of another embodiment of the present invention

도 3은 도 3의 단면도3 is a cross-sectional view of FIG.

도 4와 도 5는 본 발명의 사용 상태도4 and 5 is a state diagram used in the present invention

※ 도면의 주요 부분에 대한 부호의 설명[Description of Drawings]

1 : 본체 2 : 신발앞부분삽입공1: Body 2: Shoe part insertion hole

3 : 발등고리 4 : 절결부3: foot loop 4: notch

5 : 보호덮개 6 :덮개부5: protective cover 6: cover

7 : 내유밀착패드 8 : 부착홈7: oil-resistant pad 8: attachment groove

9 : 신발끈9: shoelace

Claims (4)

미끄러짐이 방지되는 재질로 된 본체(1); 본체(1)의 전방에 신발앞부분삽입공(2)을 형성하면서 둥근 고리 형상으로 연결된 발등고리(3); 본체(1)의 후방에 넓은 판체로 형성되고, 'ㄷ'형태의 절결부(4)가 형성되어 'ㄷ'형상의 보호덮개(5)가 형성된 덮개부(6);를 포함하여 구성됨을 특징으로 하는 보호커버를 가진 신발 장착용 미끄럼 방지 패드.A main body 1 made of a material of which slip is prevented; Foot ring (3) connected in a round ring shape while forming the front portion of the shoe insertion hole (2) in front of the main body (1); It is formed of a wide plate body in the rear of the main body 1, the 'c' shaped cutout portion 4 is formed to form a 'c' shaped cover 5, the cover portion 6; Non-slip pad for shoe mounting with protective cover. 제 1항에 있어서, 상기 본체(1)는 물에 미끄러지지 않는 재질이고, 본체(1)에는 기름에 미끄러지지 않는 재질로 된 내유밀착패드(7)가 다수 개 부착됨을 특징으로 하는 보호커버를 가진 신발 장착용 미끄럼 방지 패드.The shoe with a protective cover according to claim 1, wherein the main body (1) is made of a material which does not slip in water, and the main body (1) has a plurality of oil-resistant pads (7) made of a material which does not slip in oil. Non-slip pad for mounting. 제 2항에 있어서, 본체(1)는 천연고무 25~35중량％, 카본 마스터 배치 15~25중량％, 부타디엔 고무 5~15중량％, 아연화 10~20중량％, 스테아린산 0.2~0.3중량％, 산화철 10~20중량％, 산화티타늄 10~20중량％, 점착부여제 0.5~1.0중량％, 가류 촉진제로서 동양제철화학의 제품명 씨젯(CZ) 0.5~1.0중량％, 가류 촉진제로서 동양제철화학의 제품명 디(D) 0.2~0.3중량％, 가류 촉진제로서 동양제철화학의 제품명 티에스(TS) 0.05~0.15중량％, 유황 0.5~1.5중량％로 구성됨을 특징으로 하는 보호커버를 가진 신발 장착용 미끄럼 방지 패드.The main body 1 according to claim 2, the main body 1 is 25 to 35% by weight of natural rubber, 15 to 25% by weight of carbon master batch, 5 to 15% by weight of butadiene rubber, 10 to 20% by weight of zinc, 0.2 to 0.3% by weight of stearic acid, 10 to 20% by weight of iron oxide, 10 to 20% by weight of titanium oxide, 0.5 to 1.0% by weight of tackifier, product name of Dongyang Steel Chemical as vulcanization accelerator 0.5 to 1.0% by weight of CZ (CZ), as a vulcanization accelerator D (D) 0.2 ~ 0.3% by weight, as a vulcanization accelerator, product name of Ts (TS) 0.05 ~ 0.15% by weight, sulfur 0.5 ~ 1.5% by weight, Non-slip pad for shoe mounting with a protective cover . 제 2항에 있어서, 내유밀착패드(7)는 니트릴 부타디엔 고무 25~35중량％, 카본 마스터 배치 15~25중량％, 부타디엔 고무 5~15중량％, 아연화 10~20중량％, 스테아린산 0.2~0.3중량％, 산화철 10~20중량％, 산화티타늄 10~20중량％, 점착부여제 0.5~1.0중량％, 가류 촉진제로서 동양제철화학의 제품명 씨젯(CZ) 0.5~1.0중량％, 가류 촉진제로서 동양제철화학의 제품명 디(D) 0.2~0.3중량％, 가류 촉진제로서 동양제철화학의 제품명 티에스(TS) 0.05~0.15중량％, 유황 0.5~1.5중량％로 구성됨을 특징으로 하는 보호커버를 가진 신발 장착용 미끄럼 방지 패드.The oil-resistant adhesive pad 7 according to claim 2, wherein the oil-resistant adhesive pad 7 is composed of 25 to 35% by weight of nitrile butadiene rubber, 15 to 25% by weight of carbon master batch, 5 to 15% by weight of butadiene rubber, 10 to 20% by weight of zincated and 0.2 to 0.3 stearic acid. 10% to 20% by weight of iron oxide, 10 to 20% by weight of titanium oxide, 0.5 to 1.0% by weight of tackifier, 0.5 to 1.0% by weight of product name Seajet (CZ) as a vulcanization accelerator, Dongyang Steel as a vulcanization accelerator For shoe mounting with a protective cover, characterized in that the chemical name D (D) 0.2 ~ 0.3% by weight, as a vulcanization accelerator, the product name of Dongyang Steel Chemical (TS) 0.05 ~ 0.15% by weight, sulfur 0.5 ~ 1.5% by weight. Anti-slip pads.
KR1020080024949A 2008-03-18 2008-03-18 General-purpose nonslip pad with safety cover for shoes KR100976276B1 (en)