KR100967656B1 - Polyurethane foam panel frame and Manufacturing method thereof - Google Patents

Polyurethane foam panel frame and Manufacturing method thereof Download PDF

Info

Publication number
KR100967656B1
KR100967656B1 KR1020080032880A KR20080032880A KR100967656B1 KR 100967656 B1 KR100967656 B1 KR 100967656B1 KR 1020080032880 A KR1020080032880 A KR 1020080032880A KR 20080032880 A KR20080032880 A KR 20080032880A KR 100967656 B1 KR100967656 B1 KR 100967656B1
Authority
KR
South Korea
Prior art keywords
parts
polyurethane panel
synthetic resin
finishing material
resin film
Prior art date
Application number
KR1020080032880A
Other languages
Korean (ko)
Other versions
KR20090107384A (en
Inventor
정용채
Original Assignee
(주) 디유티코리아
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by (주) 디유티코리아 filed Critical (주) 디유티코리아
Priority to KR1020080032880A priority Critical patent/KR100967656B1/en
Publication of KR20090107384A publication Critical patent/KR20090107384A/en
Application granted granted Critical
Publication of KR100967656B1 publication Critical patent/KR100967656B1/en

Abstract

본 발명은 서로 맞닿아 조립되는 면에 다수 개의 요부(凹部) 조립부와 철부(凸部) 조립부를 형성시킨 폴리우레탄패널 마감재 및 그 제조방법에 관한 것으로, 폴리우레탄패널 마감재의 시공시 다수개의 요부 조립부와 철부 조립부에 의해 다수 개의 조립부들이 높은 기밀성을 유지할 수 있도록 조밀하게 조립되어 단열 및 방음 효과가 우수하고, 폴리우레탄패널 마감재의 제조시 종전에 사용하던 외피재인 종이와는 달리 유연성을 갖는 합성수지제 필름을 외피재로 사용함으로써, 폴리우레탄패널 마감재의 형태에 따라 합성수지제 필름을 접지 않아도 다양한 형상의 폴리우레탄패널 마감재를 간편하게 제조할 수 있는 장점이 있다. BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a polyurethane panel finishing material in which a plurality of recessed parts and a convex assembly are formed on a surface to be brought into contact with each other, and a method of manufacturing the same. By assembling part and iron assembly part, many assembly parts are densely assembled to maintain high airtightness, so it has excellent heat insulation and soundproofing effect, and unlike flexible paper, which is used in the past when manufacturing polyurethane panel finish, By using the synthetic resin film having an outer shell material, there is an advantage that can be easily produced a polyurethane panel finishing material of various shapes without folding the synthetic resin film according to the shape of the polyurethane panel finishing material.

폴리우레탄패널, 마감재, 요부(凹部) 조립부, 철부(凸部) 조립부, 외피재, 폴리에틸렌 Polyurethane Panel, Finishing Material, Concave Assembled Parts, Iron Assembled Parts, Sheath Material, Polyethylene

Description

폴리우레탄발포 마감재 및 그 제조방법{Polyurethane foam panel frame and Manufacturing method thereof} Polyurethane foam panel and manufacturing method thereof

본 발명은 폴리우레탄패널 마감재 및 그 제조방법에 관한 것으로, 더욱 상세하게는 서로 맞닿아 조립되는 면에 다수 개의 요부(凹部) 조립부와 철부(凸部) 조립부를 형성시킨 폴리우레탄패널 마감재를 제조함으로써, 다수 개의 조립부들이 형성된 발포패널 마감재를 간편하게 제조하여 이를 시공시 다수 개의 조립부들이 높은 기밀성을 유지할 수 있도록 조밀하게 조립되어 단열 및 방음 효과가 우수한 것을 특징으로 하는 폴리우레탄패널 마감재 및 그 제조방법에 관한 것이다.The present invention relates to a polyurethane panel finishing material and a method of manufacturing the same, and more particularly, to manufacture a polyurethane panel finishing material formed with a plurality of recessed parts and convex parts on the surface to be in contact with each other. By doing so, it is easy to manufacture a foam panel finish formed with a plurality of assembly parts and the assembly of the polyurethane panel finish material, characterized in that the assembly is densely assembled to maintain a high airtightness and excellent insulation and sound insulation effect It is about a method.

최근 시공되는 건축물 또는 공작물들은 건축시에 단열 또는 방음 효과를 위해 폴리우레탄패널 마감재를 이용하여 시공하며, 이러한 종래의 폴리우레탄패널 마감재는 제조시에 도 1a에 도시된 바와 같은 하형(20)을 여러 개를 연이어 연결시킨 상태에서 하형(21, 21')의 캐비티 내부에 발포제 조성물을 연속적으로 주입하고, 하형(21, 21')과 상형(22, 22')을 합형시킨 다음 컨베이어 체인(60)을 따라 이동시 키면서 가열 발포시켜 폴리우레탄패널 마감재를 성형시킨다. Recently constructed buildings or workpieces are constructed using polyurethane panel finishes for insulation or sound insulation in construction, and such conventional polyurethane panel finishes have various lower molds 20 as shown in FIG. Continuously injecting the blowing agent composition into the cavity of the lower mold 21, 21 ′ with the dogs connected successively, combining the lower mold 21, 21 ′ with the upper mold 22, 22 ′ and then conveyor chain 60. By heating and foaming while moving along to form a polyurethane panel finish.

이때 발포제 조성물을 하형 내부에 연속적으로 주입할 경우 하형(21)과 연결된 인접 하형(21')과의 사이에 공간이 형성되어 발포제 조성물이 누설됨에 따라 폴리우레탄패널 마감재의 제조장치에 이상이 발생하거나 또는 기형의 폴리우레탄패널 마감재가 성형될 우려의 문제점이 있다. At this time, when the foaming agent composition is continuously injected into the lower mold, a space is formed between the lower mold 21 and the adjacent lower mold 21 'and the foaming agent composition leaks, thereby causing an abnormality in the manufacturing apparatus of the polyurethane panel finishing material. Or there is a problem of concern that the molded polyurethane panel finish is molded.

따라서 상기와 같이 발포제 조성물이 하형(21)과 인접 하형(21') 사이에 누설되는 것을 방지하기 위하여, 도 1b에 도시된 바와 같이 기다란 띠 형태의 외피재인 종이(10)를 하형(21, 21') 캐비티의 바닥 면에 연이어 전개시키게 되며, 이때 사용하는 외피재(10)인 종이는 도 1c에 도시된 바와 같이 폴리우레탄패널 마감재에 성형시키기 위한 하형(21, 21') 바닥 면의 형상 즉, 하형(21, 21')의 바닥 면의 요부(凹部) 또는 철부(凸部)의 형상과 동일한 형상을 갖도록 사전에 미리 접었다가 다시 편 종이를 사용하여야 한다. Therefore, in order to prevent the foaming agent composition from leaking between the lower mold 21 and the adjacent lower mold 21 'as described above, as shown in FIG. ') Is developed in succession to the bottom surface of the cavity, the paper 10, the outer shell material used in this case is the shape of the bottom surface (21, 21') bottom surface for molding to the polyurethane panel finish as shown in Figure 1c In order to have the same shape as the shape of the recessed part or the convex part of the bottom face of the lower molds 21 and 21 ', it is necessary to fold it in advance and then use the folded paper.

이와 같이 접은 외피재(10)인 종이를 하형(21, 21')의 바닥 면에 펼쳐 전개시킨 다음 외피재(10)인 종이의 상부에 발포제 조성물을 주입하게 되면, 외피재(10)인 종이의 바닥 면에 의해 발포제 조성물이 하형(21)과 다른 인접 하형(21')의 연결된 이격 공간의 외부로 흘러내리지 않게 된다. 그리고 하형의 캐비티 내부에 발포제 조성물을 주입시킨 다음 그 상부에 다시 외피재인 종이(미도시)를 덮은 다음 상형(22, 22')을 하형(21, 21')과 맞추어 형합시킨 후 가열 발포시키면 외피재(10)인 상하부의 종이 내부에서 발포제 조성물이 성형되므로 발포성형물이 금형의 외부로 누출되지 않게 된다. When the paper, which is the outer cover material 10, is expanded and deployed on the bottom surfaces of the lower molds 21 and 21 ', and then the foaming agent composition is injected into the upper part of the paper, which is the skin material 10, the paper is the skin material 10. The bottom face of the foam prevents the blowing agent composition from flowing out of the spaced apart space of the lower mold 21 and the other adjacent lower mold 21 '. Then, the foaming agent composition is injected into the cavity of the lower mold, and then the upper cover 22 (22, 22 ') and the upper mold (22, 22') are matched with the lower mold (21, 21 '). Since the foaming agent composition is molded in the upper and lower parts of the paper 10, the foamed molding is not leaked to the outside of the mold.

이와 같이 종래의 방법에 의해 제조된 폴리우레탄패널 마감재는 발포제 조성물이나 또는 발포성형물이 금형의 외부로 누출되는 것을 방지하기 위하여 마감재의 형상에 따라 굴곡을 갖도록 사전에 미리 접은 형상의 종이를 사용함에 따라 제조공정이 복잡하고, 그리고 조금 복잡한 형상의 굴곡을 갖도록 접은 종이를 금형 내부에 삽입시킨 후 발포제 조성물을 가열 발포시키면, 종이 내부의 성형물이 발포되면서 종이의 접은 부분에 제대로 굴곡이 형성되지 않기 때문에 다양하고 복잡한 형상의 폴리우레탄패널 마감재를 성형시킬 수 없는 문제점이 있었다. As described above, the polyurethane panel finish produced by the conventional method uses paper of a shape that is pre-folded in advance to have a bent shape according to the shape of the finish to prevent the foam composition or the foamed article from leaking out of the mold. If the manufacturing process is complicated and the folded paper is inserted into the mold to have a slightly complicated shape of the mold, and the foaming agent composition is heated and foamed, the molding inside the paper is foamed, so that the bending part of the paper does not form properly. And there was a problem that can not form a polyurethane panel finish of a complicated shape.

따라서 현재 시중에 유통되고 있는 폴리우레탄 발포 패널 마감재의 경우에는 도 2a 내지 도 2f에 도시된 바와 같이 폴리우레탄 발포 패널 마감재(100)는 본체가 발포체 본체(30)와 이 발포체 본체를 감싼 외피재(10)인 종이로 이루어지고, 마감재(100)의 일면에 단순히 하나의 요부(凹部) 조립부(40) 또는 철부(凸部) 조립부(50)만을 형성시킨 발포패널 마감재(100)만 유통되고 있으며, 요부(凹部) 조립부 또는 철부(凸部) 조립부가 다수 개 형성된 폴리우레탄패널 마감재는 성형시킬 수 없는 문제점이 있었다.Therefore, in the case of the polyurethane foam panel finish currently on the market as shown in Figures 2a to 2f, the polyurethane foam panel finish 100 is a foam body 30 and the outer shell material surrounding the foam body ( 10) made of paper, and only the foam panel finishing material 100, which is formed by forming only one recessed part assembly 40 or an iron assembly part 50 on one surface of the finishing material 100, In addition, there is a problem in that the polyurethane panel finishing material in which a plurality of recessed parts or convex parts are formed cannot be molded.

그리고 상기와 같은 구조를 갖는 종래의 발포패널 마감재를 이용하여 시공시에는 도 3에 도시된 바와 같이 발포패널 마감재의 조립시에는 일측 발포패널 마감재(100)의 요부(凹部) 조립부와 타측 발포패널 마감재(100')의 철부(凸部) 조립부가 서로 조립되어 하나의 조립부만 형성됨에 따라 조립 부분의 기밀성이 떨어지게 되므로 고도의 단열효과나 또는 방음효과가 요구되는 건축물이나 공작물의 시공에는 적합하지 못한 문제점이 있었다. And when using the conventional foam panel finishing material having the structure as described above when assembling the foam panel finishing material as shown in Figure 3 during the assembly of the main portion () 部) of the foam panel finishing material 100 and the other foam panel As the assembling parts of the finishing material 100 'are assembled with each other and only one assembly part is formed, the airtightness of the assembly parts is inferior, so it is not suitable for the construction of a building or a workpiece requiring high insulation or sound insulation effect. There was a problem.

따라서 상기의 과제를 해결하기 위한 본 발명은 서로 맞닿아 조립되는 면에 다수 개의 요부(凹部) 조립부와 철부(凸部) 조립부를 형성시킨 폴리우레탄패널 마감재를 제조함으로써, 발포패널 마감재의 시공시 다수개의 요부 조립부와 철부 조립부에 의해 다수 개의 조립부들이 높은 기밀성을 유지할 수 있도록 조밀하게 조립하여 단열 및 방음 효과가 우수한 것을 특징으로 하는 폴리우레탄패널 마감재를 제공함에 그 목적이 있다. Accordingly, the present invention for solving the above problems by manufacturing a polyurethane panel finishing material formed with a plurality of recessed parts and convex assembly on the surface to be in contact with each other, when the construction of the foam panel finish It is an object of the present invention to provide a polyurethane panel finishing material characterized by excellent heat insulation and soundproofing effect by densely assembling a plurality of assembling parts to maintain a high airtightness by a plurality of recessed parts and iron assembly parts.

그리고 본 발명은 폴리우레탄패널 마감재의 제조시 통상의 제조장치를 이용하여 유연성이 있는 합성수지제 필름을 외피재로 사용함으로써, 종전에 사용하던 외피재인 종이와는 달리 폴리우레탄 패널 마감재의 형태에 따라 합성수지제 필름을 접지 않아도 다양한 형상의 발포패널 마감재를 간편하게 제조할 수 있는 것을 특징으로 하는 폴리우레탄패널 마감재의 제조방법을 제공함에 다른 목적이 있다. In addition, the present invention uses a synthetic resin film having a flexible using a conventional manufacturing apparatus in the manufacture of the polyurethane panel finishing material as the outer skin material, unlike the conventional outer skin paper, the synthetic resin according to the shape of the polyurethane panel finishing material Another object of the present invention is to provide a method for manufacturing a polyurethane panel finish material, which can easily manufacture foam panel finishes of various shapes without folding the film.

본 발명은 발포체 본체와 그 외부를 둘러싼 외피재로 이루어진 폴리우레탄패널 마감재에 있어서, The present invention is a polyurethane panel finish made of a foam body and the outer shell material surrounding the outside,

삭제delete

삭제delete

삭제delete

상기 폴리우레탄패널 마감재(100)는 일 측면에 다수 개의 요부(凹部) 조립부(40) 또는 철부(凸部) 조립부(50)가 형성되며, 그리고 타 측면에 상기 일 측면과 대응되는 부분에 철부(凸部) 조립부(50) 또는 요부(凹部) 조립부(40)가 형성된 구조이고, The polyurethane panel finishing material 100 has a plurality of concave parts assembly 40 or convex assembly 50 is formed on one side, and on the other side corresponding to the one side It is a structure in which the convex assembly part 50 or the recessed part assembly part 40 was formed,

상기 외피재(10)는 합성수지제 필름인 것을 특징으로 하는 폴리우레탄패널 마감재를 본 발명의 과제 해결 수단으로 한다. The outer shell material 10 is a polyurethane panel finish, characterized in that the film made of a synthetic resin as a means for solving the problem of the present invention.

단, 상기 외피재(10)의 소재는 합성수지제 필름으로 폴리에틸렌, 폴리프로필렌, 폴리염화비닐로 이루어진 군에서 1종을 선택하여 사용하는 것이 바람직하다. However, the material of the outer cover material 10 is a synthetic resin film, it is preferable to use one selected from the group consisting of polyethylene, polypropylene, polyvinyl chloride.

상기의 과제 해결 수단에 의한 본 발명은 서로 맞닿아 조립되는 면에 다수 개의 요부(凹部) 조립부와 철부(凸部) 조립부를 형성시킨 폴리우레탄패널 마감재로서, 발포패널 마감재의 시공시 다수개의 요부 조립부와 철부 조립부에 의해 다수 개의 조립부들이 높은 기밀성을 유지할 수 있도록 조밀하게 조립하여 단열 및 방음 효과가 우수하며, 발포패널 마감재의 제조시 통상의 제조장치에 유연성을 갖는 합성수지제 필름을 외피재로 사용하여 제조함으로써, 합성수지제 필름을 접지 않아도 다양한 형상의 발포패널 마감재를 간편하게 제조할 수 있는 장점이 있다. The present invention by the above-mentioned problem solving means is a polyurethane panel finishing material formed with a plurality of recessed parts and convex assembly on the surface to be in contact with each other, a plurality of recesses in the construction of the foam panel finish By assembling part and iron part assembling part, the assembly part is densely assembled to maintain high airtightness, so it is excellent in heat insulation and soundproofing effect, and it is made of synthetic resin film which has flexibility in general manufacturing equipment when manufacturing foam panel finish. By using the material, there is an advantage that the foam panel finishes of various shapes can be easily produced without folding the synthetic resin film.

상기의 효과를 달성하기 위한 본 발명의 구성을 첨부된 도면을 중심으로 상세히 설명하면, 아래의 내용과 같다.Referring to the configuration of the present invention for achieving the above effects in detail with reference to the accompanying drawings, as follows.

참고로, 도 4는 본 발명에 따른 실시예인 폴리우레탄패널 마감재를 나타낸 단면도에 관한 것이다.For reference, Figure 4 relates to a cross-sectional view showing a polyurethane panel finishing material according to an embodiment of the present invention.

본 발명은 도 4에 도시된 바와 같이, 발포체 본체와 그 외부를 둘러싼 외피재로 이루어진 폴리우레탄패널 마감재에 있어서, The present invention, as shown in Figure 4, in the polyurethane panel finish made of a foam body and the outer shell material surrounding the outside,

상기 폴리우레탄패널 마감재(100)는 일 측면에 다수 개의 요부(凹部) 조립부(40) 또는 철부(凸部) 조립부(50)가 형성되며, 그리고 타 측면이 평면으로 이루어진 구조이고, The polyurethane panel finishing material 100 has a plurality of recessed parts 40 or convex assembly 50 is formed on one side, and the other side is a flat structure,

상기 외피재(10)는 합성수지제 필름인 것을 특징으로 하는 폴리우레탄패널 마감재에 관한 것이다. The outer cover material 10 relates to a polyurethane panel finish, characterized in that the film made of a synthetic resin.

참고로, 도 5는 본 발명에 따른 다른 실시예인 폴리우레탄패널 마감재를 나타낸 단면도에 관한 것이다.For reference, Figure 5 relates to a cross-sectional view showing a polyurethane panel finishing material according to another embodiment of the present invention.

그리고 본 발명은 다른 실시예로서, 본 발명은 도 5에 도시된 바와 같이, 발포체 본체와 그 외부를 둘러싼 외피재로 이루어진 폴리우레탄패널 마감재에 있어서, And another embodiment of the present invention, the present invention, as shown in Figure 5, in the polyurethane panel finish made of a foam body and the outer shell material surrounding the outside,

상기 폴리우레탄패널 마감재(100)는 일 측면에 다수 개의 요부(凹部) 조립부(40) 또는 철부(凸部) 조립부(50)가 형성되며, 그리고 타 측면에 상기 일 측면과 대응되는 부분에 철부(凸部) 조립부(50) 또는 요부(凹部) 조립부(40)가 형성된 구조이고, The polyurethane panel finishing material 100 has a plurality of concave parts assembly 40 or convex assembly 50 is formed on one side, and on the other side corresponding to the one side It is a structure in which the convex assembly part 50 or the recessed part assembly part 40 was formed,

상기 외피재(10)는 합성수지제 필름인 것을 특징으로 하는 폴리우레탄패널 마감재에 관한 것이다. The outer cover material 10 relates to a polyurethane panel finish, characterized in that the film made of a synthetic resin.

본 발명에서 상기 외피재(10)의 소재는 합성수지제 필름으로 폴리에틸렌, 폴리프로필렌, 폴리염화비닐로 이루어진 군에서 1종을 선택하여 사용하는 것이 바람직하며, 상기에서 열거한 종류에만 반드시 한정되는 것이 아니고, 상기와 동등 이상의 물성을 갖는 합성수지제 필름인 경우에는 모두 적용되어 질 수 있다.In the present invention, the material of the outer cover material 10 is a synthetic resin film, it is preferable to use one selected from the group consisting of polyethylene, polypropylene, polyvinyl chloride, it is not necessarily limited to only the above-mentioned type. In the case of a synthetic resin film having physical properties equal to or higher than those described above, all may be applied.

참고로, 도 6은 본 발명에 따른 또 다른 실시예인 다양한 종류의 폴리우레탄패널 마감재를 나타낸 단면도에 관한 것이다.For reference, Figure 6 relates to a cross-sectional view showing a polyurethane panel finish of various kinds which is another embodiment according to the present invention.

본 발명에서 폴리우레탄패널 마감재의 면에 형성시키는 조립부는 요부(凹部) 조립부의 형태가 2~5개인 것이 바람직하며, 요부(凹部) 조립부의 개수는 상기 범위의 개수에만 반드시 한정되는 것이 아니고, 폴리우레탄패널 마감재의 크기에 따라 그 개수를 적절히 조정할 수 있다. In the present invention, the assembly portion formed on the surface of the polyurethane panel finishing material is preferably in the form of recessed parts 2 to 5, the number of recessed parts assembly is not necessarily limited to the number of the above range, poly The number can be adjusted according to the size of the urethane panel finish.

그리고 본 발명에 따른 폴리우레탄패널 마감재들을 조립시에는 도 7에 도시된 바와 같이 일 측면에 요부(凹部) 조립부 또는 철부(凸部) 조립부가 다수 개 형성된 마감재(100)를 타 측면에 다수 개의 철부(凸部) 조립부 또는 요부(凹部) 조립부가 형성된 마감재(100')에 각각 삽입시키면, 양 패널 마감재의 조립부 결합상태가 조밀하게 되므로 단열 및 방음효과가 우수한 것이 특징이다.And when assembling the polyurethane panel finishing material according to the present invention, as shown in Figure 7 a plurality of finishing material 100 formed on the other side (요 部) assembly or convex (assembly) assembly portion on the other side When inserted into the finishing material (100 ') formed in the convex assembly portion or recessed portion assembly portion, respectively, the assembled state of both panel finish material is densely coupled, it is characterized by excellent heat insulation and sound insulation effect.

참고로, 도 7은 본 발명에 따른 폴리우레탄패널 마감재들의 결합된 상태를 나타낸 단면도를 나타낸 것이다. For reference, Figure 7 shows a cross-sectional view showing a combined state of the polyurethane panel finishes according to the present invention.

이하 본 발명에 따른 폴리우레탄패널 마감재의 제조공정을 첨부한 도면인 도 7을 중심으로 상세히 설명하면 아래의 내용과 같다.Hereinafter, with reference to Figure 7 attached to the manufacturing process of the polyurethane panel finishing material according to the present invention will be described in detail as follows.

도 7은 본 발명에 따른 폴리우레탄패널 마감재의 제조방법을 나타낸 공정블럭도에 관한 것이다.Figure 7 relates to a process block diagram showing a method for producing a polyurethane panel finish according to the present invention.

본 발명은 도 7에 도시된 바와 같이, 발포체 본체와 그 외부를 둘러싼 외피재로 이루어진 폴리우레탄패널 마감재의 제조방법에 있어서, In the present invention, as shown in Figure 7, in the manufacturing method of the polyurethane panel finish made of a foam body and the outer shell material surrounding the outside,

다수 개의 요부(凹部) 조립부 또는 철부(凸部) 조립부가 형성된 금형 캐비티의 바닥 면에 하부 합성수지제 필름을 전개시키는 단계(100);Developing (100) a lower synthetic resin film on a bottom surface of a mold cavity in which a plurality of recessed or assembled parts are formed;

상기에서 전개시킨 합성수지제 필름의 상부에 발포제 조성물을 주입시키는 단계(200);Injecting a blowing agent composition on top of the synthetic resin film developed above (200);

주입된 발포제 조성물의 상부에 상부 합성수지제 필름을 덮는 단계(300);Covering the upper synthetic resin film on top of the injected blowing agent composition (300);

하형과 상형을 형합시키는 단계(400);Combining the lower mold with the upper mold (400);

하형과 상형을 형합시킨 금형에 가열하여 발포제 조성물을 발포시켜 성형물을 제조하는 단계(500);Preparing a molding by heating a mold in which the lower mold and the upper mold are molded to foam the foaming agent composition;

를 거쳐 제조되는 것을 특징으로 하는 폴리우레탄패널 마감재의 제조방법에 관한 것이다.It relates to a method for producing a polyurethane panel finish, characterized in that is produced through.

본 발명에서 합성수지제 필름의 소재에 대해서는 상기에서 상세히설명한 바 있으므로 여기서는 생략하기로 한다.Since the material of the synthetic resin film in the present invention has been described in detail above, it will be omitted here.

본 발명에서 발포제 조성물을 발포시켜 성형물을 제조하는 단계는 통상적인 방법에 의해 발포제 조성물을 발포시키며, 본 발명에서 발포제 조성물은 폴리우레 탄 발포제 조성물로서, 발포온도는 사용하는 발포제의 종류에 따라 30~100℃의 온도에서 발포시키며, 외피재로 사용되는 소재인 폴리에틸렌, 폴리프로필렌, 폴리염화비닐 등은 융점이 최소 발포온도 이상인 110℃ 이상에서 용융되므로 외피재인 합성수지 필름에 아무런 손상을 입히지 않고 발포패널 마감재를 성형시킬 수 있다.In the present invention, the step of preparing a molded article by foaming the foaming agent composition foams the foaming agent composition by a conventional method. In the present invention, the foaming agent composition is a polyurethane foaming agent composition, and the foaming temperature is 30 to 30 depending on the type of foaming agent to be used. Foaming at a temperature of 100 ℃, polyethylene, polypropylene, polyvinyl chloride, etc., which are used as the outer shell material, are melted at 110 ° C or higher with a melting point above the minimum foaming temperature. Thus, the foam panel finish material is not damaged in any way. Can be molded.

그리고 상기 (500)단계에서 상형은 그 내부 면이 다수 개의 철부(凸部) 조립부 또는 요부(凹部) 조립부가 형성되거나(도 2a 내지 도 2d의 형태) 또는 평면 구조(도 2e의 형태)인 것이 특징이다. In the step (500), the upper die may have a plurality of convex assembly parts or recess assembly parts (in the form of FIGS. 2A to 2D) or a planar structure (in the form of FIG. 2E). Is characteristic.

그리고 본 발명은 종래에 사용하던 외피재인 종이와는 달리 합성수지제 필름을 사용함에 따라 발포패널 마감재의 형상에 따라 종이를 접어야 했던 과정을 생략할 수 있어 제조공정이 간단하고, 또한 합성수지제 필름의 유연성에 의해 다수 개의 조립부가 형성된 복잡한 구조의 폴리우레탄패널 마감재도 쉽게 제조할 수 있는 것이 특징이다. And according to the present invention, unlike the paper used in the prior art, the process of having to fold the paper according to the shape of the foam panel finishing material can be omitted by using a synthetic resin film, the manufacturing process is simple, and the flexibility of the synthetic resin film It is characterized by the fact that the polyurethane panel finishing material of a complicated structure in which a plurality of assembly portions are formed.

상술한 바와 같이, 본 발명의 구성을 첨부한 도면을 중심으로 상세히 설명하였지만 첨부된 도면에만 반드시 한정되지 않고, 해당 기술분야의 당업자라면 하기의 특허청구범위에 기재된 본 발명의 사상 및 영역으로부터 벗어나지 않는 범위 내에서 본 발명을 다양하게 수정 및 변경시킬 수 있음을 이해할 수 있을 것이다.As described above, the configuration of the present invention has been described in detail with reference to the accompanying drawings, but is not necessarily limited to the accompanying drawings, and those skilled in the art do not depart from the spirit and scope of the present invention as set forth in the claims below. It will be understood that various modifications and variations can be made within the scope of the invention.

도 1 a 내지 1c는 종래의 폴리우레탄패널 마감재에 발포제 조성물을 주입시키는 과정을 나타낸 사시도.Figure 1a to 1c is a perspective view showing a process of injecting a foaming agent composition in a conventional polyurethane panel finish.

도 2a 내지 2f는 상기의 방법에 의해 제조된 종래의 폴리우레탄패널 마감재를 나타낸 단면도,Figure 2a to 2f is a cross-sectional view showing a conventional polyurethane panel finish produced by the above method,

도 3은 종래의 폴리우레탄패널 마감재들이 조립된 상태를 나타낸 단면도,3 is a cross-sectional view showing a state in which the conventional polyurethane panel finishes are assembled;

도 4는 본 발명에 따른 실시예인 폴리우레탄패널 마감재를 나타낸 단면도,Figure 4 is a cross-sectional view showing a polyurethane panel finishing material according to an embodiment of the present invention,

도 5는 본 발명에 따른 다른 실시예인 폴리우레탄패널 마감재를 나타낸 단면도,5 is a cross-sectional view showing a polyurethane panel finishing material according to another embodiment of the present invention;

도 6은 본 발명에 따른 또 다른 실시예들인 폴리우레탄패널 마감재를 나타낸 단면도,Figure 6 is a cross-sectional view showing a polyurethane panel finishing material according to another embodiment of the present invention,

도 7은 본 발명에 따른 폴리우레탄패널 마감재들이 조립된 상태를 나타낸 단면도,7 is a cross-sectional view showing a state in which the polyurethane panel finishes according to the present invention assembled;

도 8은 본 발명에 따른 폴리우레탄패널 마감재의 제조방법을 나타낸 공정블럭도에 관한 것이다.8 is a process block diagram showing a method for manufacturing a polyurethane panel finish according to the present invention.

* 도면의 주요부분에 대한 부호의 설명 *Explanation of symbols on the main parts of the drawings

100 : 발포 패널 마감재 10 : 외피재100: foam panel finish 10: shell material

21 : 하형 22 : 상형21: lower mold 22: upper mold

30 : 발포체 본체 40 : 요부(凹部) 조립부 30: foam body 40: recessed assembly

50 : 철부(凸部) 조립부50: iron assembly

Claims (5)

삭제delete 발포체 본체와 그 외부를 둘러싼 외피재로 이루어진 폴리우레탄패널 마감재에 있어서, In the polyurethane panel finish made of a foam body and the outer shell material surrounding the outside, 상기 폴리우레탄패널 마감재는 일 측면에 다수 개의 요부(凹部) 조립부 또는 철부(凸部) 조립부가 형성되며, 그리고 타 측면에 상기 일 측면과 대응되는 부분에 철부(凸部) 조립부 또는 요부(凹部) 조립부가 형성된 구조이고, The polyurethane panel finishing material has a plurality of concave parts or convex parts formed on one side, and convex parts or concave parts on the other side corresponding to the one side ( 조립 部) is a structure in which the assembly portion is formed, 상기 외피재는 합성수지제 필름이고,The outer cover material is a synthetic resin film, 상기 외피재의 소재는 합성수지제 필름으로 폴리에틸렌, 폴리프로필렌, 폴리염화비닐로 이루어진 군에서 1종을 선택하여 사용하고, The material of the outer cover material is a synthetic resin film used by selecting one type from the group consisting of polyethylene, polypropylene, polyvinyl chloride, 상기 조립부는 요부(凹部) 조립부의 형태가 2~5개인 것을 선택하여 사용하는 것을 특징으로 하는 발포패널 마감재.The assembly portion is a foam panel finishing material, characterized in that for use in the form of the recessed parts 2-5 parts. 삭제delete 삭제delete 발포체 본체와 그 외부를 둘러싼 외피재로 이루어진 폴리우레탄패널 마감재의 제조방법에 있어서, In the manufacturing method of the polyurethane panel finishing material consisting of a foam body and the outer shell material surrounding the outside, 다수 개의 요부(凹部) 조립부 또는 철부(凸部) 조립부가 형성된 하형 캐비티의 바닥 면에 하부 합성수지제 필름을 전개시키는 단계(100);Developing (100) a lower synthetic resin film on a bottom surface of a lower mold cavity in which a plurality of recessed or assembled parts are formed; 상기에서 전개시킨 하부 합성수지제 필름의 상부에 발포제 조성물을 주입시키는 단계(200);Injecting a blowing agent composition into the upper portion of the lower synthetic resin film developed above (200); 주입된 발포제 조성물의 상부에 상부 합성수지제 필름을 덮는 단계(300);Covering the upper synthetic resin film on top of the injected blowing agent composition (300); 하형과 상형을 형합시키는 단계(400);Combining the lower mold with the upper mold (400); 하형과 상형을 형합시킨 금형에 가열하여 발포제 조성물을 발포시켜 성형물 을 제조하는 단계(500);Preparing a molding by heating a mold in which the lower mold and the upper mold are joined to foam the blowing agent composition; 를 거쳐 제조되는 것을 특징으로 하는 폴리우레탄패널 마감재의 제조방법.Method for producing a polyurethane panel finish, characterized in that is produced through.
KR1020080032880A 2008-04-08 2008-04-08 Polyurethane foam panel frame and Manufacturing method thereof KR100967656B1 (en)