KR100927030B1 - Fabrication method of ceramic wall for floodlighting and lighting apparatus using ceramic wall babricated by the same - Google Patents

Fabrication method of ceramic wall for floodlighting and lighting apparatus using ceramic wall babricated by the same Download PDF

Info

Publication number
KR100927030B1
KR100927030B1 KR1020090026130A KR20090026130A KR100927030B1 KR 100927030 B1 KR100927030 B1 KR 100927030B1 KR 1020090026130 A KR1020090026130 A KR 1020090026130A KR 20090026130 A KR20090026130 A KR 20090026130A KR 100927030 B1 KR100927030 B1 KR 100927030B1
Authority
KR
South Korea
Prior art keywords
plate
light guide
transparent
manufacturing
guide plate
Prior art date
Application number
KR1020090026130A
Other languages
Korean (ko)
Inventor
강흥석
Original Assignee
강흥석
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 강흥석 filed Critical 강흥석
Priority to KR1020090026130A priority Critical patent/KR100927030B1/en
Application granted granted Critical
Publication of KR100927030B1 publication Critical patent/KR100927030B1/en

Abstract

PURPOSE: A manufacturing method of a ceramic light transmitting plate, and a lighting device using the ceramic light transmitting plate manufactured by the same are provided to maximize a lighting effect by forming various patterns through an openwork design. CONSTITUTION: A lighting device includes a floor plate(10), a power line(11), a lamp socket, four transparent rods(30), at least one transparent plate, and at least one ceramic light transmitting plate(70). The floor plate is plated in order to reflect a light. The power line penetrates at least one side of the floor plate. The lamp socket is connected to the power line through a through hole formed in the center of the floor plate. The four transparent rods are coupled in four edges of the floor plate. The transparent plate is coupled in each transparent rod. The ceramic light transmitting plate is attached to the transparent plate.

Description

도벽 투광판의 제조방법과 이를 통해 제조된 도벽 투광판을 이용한 조명장치{FABRICATION METHOD OF CERAMIC WALL FOR FLOODLIGHTING AND LIGHTING APPARATUS USING CERAMIC WALL BABRICATED BY THE SAME}Manufacturing method of light guide plate and lighting device using the light guide plate manufactured through the same {FABRICATION METHOD OF CERAMIC WALL FOR FLOODLIGHTING AND LIGHTING APPARATUS USING CERAMIC WALL BABRICATED BY THE SAME}

본 발명은 조명 커버의 일종인 도벽 투광판의 제조방법과 이를 통해 제조된 도벽 투광판을 이용한 조명장치에 관한 것이다.The present invention relates to a method of manufacturing a light guide plate, which is a kind of lighting cover, and a lighting apparatus using the light guide plate manufactured through the same.

조명 커버는 투명한 재질로 제조된 커버가 일반적으로 사용되고 있고, 최근에는 용도에 따라 반투광성 재질로 제조된 커버도 사용되고 있다. 전자는 빛의 투광성이 높아 조명의 효율을 높일 수 있는 장점은 있으나, 다양한 조명 효과를 낼 수 없는 문제점이 있고, 후자는 그 반대의 장, 단점을 갖고 있다.Lighting covers are generally used covers made of a transparent material, and recently, covers made of a translucent material are also used depending on the purpose. The former has the advantage of increasing the light transmission efficiency of the light, but there is a problem that can not produce a variety of lighting effects, the latter has the opposite advantages and disadvantages.

반투광성 재질로 제조된 커버들 중에는 본차이나와 같이 투광성 있는 도자기로 형성된 것들도 최근에는 사용되기는 하는데, 이들은 대부분 단순히 두께 조절 등으로 조명효과를 내는 것이어서 투광성을 보완시키는데는 일정한 한계가 있을 수 밖에 없었고, 도자의 장점인 다양한 문양에 의한 조명효과를 제대로 살리지 못하는 문제점이 있어 왔다.Covers made of translucent materials, such as bone china, formed of translucent ceramics have been used in recent years, but most of them are simply lightening effects by adjusting the thickness, so there is a certain limit to supplementing the light transmittance. There has been a problem that the lighting effect due to various patterns, which are the advantages of the ceramics, cannot be properly utilized.

또한, 투광성 도자 커버의 제조방법은 종래 도자기 제조방법을 그대로 사용 함에 따라 도자 커버의 표면이 단순히 매끈하게 처리되어 자연석의 표면과 같은 처리 효과는 내지 못하고 있다. In addition, according to the method of manufacturing a light-transmissive porcelain cover, the surface of the porcelain cover is simply smoothed by using the conventional ceramic manufacturing method as it is, and thus the treatment effect such as the surface of natural stone is not produced.

투광성 도자 커버를 이용한 조명장치도 상기 종래 투광성 도자 커버가 갖는 문제점을 그대로 드러내게 되어 조명효율에 한계가 있고, 다양한 조명효과를 내지 못하는 문제점이 있다.Illumination apparatus using a light-transmissive ceramic cover also reveals the problems of the conventional light-transmissive ceramic cover as it is, there is a limit in the lighting efficiency, there is a problem that does not produce various lighting effects.

따라서, 본 발명은 상기와 같은 종래 투광성 도자 커버, 특히 도자로 벽면 형상을 한 조명 커버(이하, 이를 "도벽 투광판"이라 함)가 갖는 문제점을 해결하기 위한 것으로서, 자연석 표면과 같은 느낌을 주고, 투각 기법으로 다양한 문양을 형성함으로써, 투광성 보완은 물론 다양한 문양에 의한 조명효과를 극대화시킬 수 있는 도벽 투광판의 제조방법과 이를 통해 제조된 도벽 투광판을 이용한 조명장치를 제공하는데 그 목적이 있다. Accordingly, the present invention is to solve the problem of the conventional translucent ceramic cover, in particular, the illumination cover (hereinafter, referred to as "conductive wall plate") that has a wall shape as a ceramic, giving a feeling like a natural stone surface The purpose of this invention is to provide a method of manufacturing a light guide plate through which various patterns are formed by using a hollow projection technique to supplement the light transmittance and maximize the lighting effect by various patterns, and a lighting device using the light guide plate manufactured through the same. .

상기 목적을 달성하기 위하여, 본 발명에 의한 도벽 투광판의 제조방법은 원형 제작단계, 거푸집 제작단계, 슬립 주입단계, 탈형 단계 및 소성단계를 포함하여 구성된 투광성 도자 커버 제조방법에 있어서, 상기 원형 제작단계는, 석고 또는 레진으로 원판을 제조하는 단계와; 상기 원판을 절단하고 표면에 문양을 새기는 단계와; 상기 표면에 돌가루를 뿌리는 단계로 구성되고, 상기 탈형 단계와 상기 소성단계 사이에는 투각단계를 더 포함하되, 상기 투각단계는 상기 탈형 단계로 성형된 도벽의 수분함량이 전체 중량의 30~40%일때 실시하고, 투각이후 상기 소성단계 전에 붓으로 가감질하는 단계를 더 포함하는 것을 특징으로 한다.In order to achieve the above object, the manufacturing method of the light-transmissive plate according to the present invention in the method of manufacturing a translucent ceramic cover comprising a circular manufacturing step, formwork manufacturing step, slip injection step, demolding step and firing step, the circular manufacturing The step includes the steps of producing a disc from gypsum or resin; Cutting the disc and engraving a surface; It is composed of the step of spraying stone on the surface, and further comprising a hollow step between the demolding step and the firing step, the hollow step is the water content of the coating wall formed by the demolding step 30 ~ 40 of the total weight When carried out at%, after the openwork before the firing step characterized in that it further comprises the step of sensitizing with a brush.

그리고, 도벽 투광판을 이용한 조명장치는 빛을 반사할 수있도록 도금된 바닥판과; 상기 바닥판의 적어도 일측 측면에 관통되어 인입된 전원선과; 상기 전원선이 상기 바닥판의 가운데 형성된 관통공을 통하여 연결된 램프 소켓과; 상기 바닥판의 네모서리 각각에 체결된 4개의 투명봉과; 상기 각 투명봉 상에 체결된 적어도 하나의 투명평판과; 상기 투명평판 상에 부착된 것으로 상기 제조방법을 통해 제조된 도벽 투광판을 하나 이상 포함하는 것을 특징으로 한다.In addition, the lighting apparatus using the light guide plate is a bottom plate plated to reflect light; A power supply line penetrated through at least one side surface of the bottom plate; A lamp socket connected to the power line through a through hole formed in the center of the bottom plate; Four transparent rods fastened to each of the four corners of the bottom plate; At least one transparent flat plate fastened on each transparent bar; It is attached to the transparent flat plate characterized in that it comprises one or more light guide plate manufactured through the manufacturing method.

본 발명에 의하여 표면은 자연석 처럼 오돌도돌 튀어나오고, 자체 투광성 있는 도벽에 투각으로 관통된 빛 방출 구를 일정한 문양으로 더 형성함으로써, 도벽이 갖고 있던 투광성의 한계를 극복하면서, 마치 전통적 문살 사이 창호지로 불빛이 나오는 분위기도 창출할 수 있어, 미적 효과 뿐만 아니라 실용적 가치를 높일 수 있는 효과가 있다.According to the present invention, the surface protrudes like a natural stone, and by forming a pattern of light emitting holes penetrating through the permeable wall on its own translucent wall, overcoming the limitations of the transmissiveness of the wall, it is like a window between traditional doors. This atmosphere can also be created, thereby increasing the practical value as well as the aesthetic effect.

이하, 첨부된 도면을 참조하며 본 발명의 바람직한 실시예에 대하여 상세히 설명한다.Hereinafter, with reference to the accompanying drawings will be described in detail a preferred embodiment of the present invention.

우선, 본 발명에 의한 도벽 투광판의 제조방법에 대하여 설명한다.First, the manufacturing method of the light-conducting plate by this invention is demonstrated.

이는 기본적으로, 종래 투광성 도자 커버 제조방법과 같이, 원형 제작단계-> 거푸집 제작단계->슬립 주입단계->탈형 단계->소성단계를 거치게 된다.Basically, as in the conventional light-transmissive ceramic cover manufacturing method, the circular manufacturing step-> formwork manufacturing step-> slip injection step-> demolding step-> firing step.

따라서, 본 실시예에 대한 설명은 일반적인 도자 제조 공정은 간단히 설명하거나 그 설명을 생략하고, 일반적인 공정과 차이나는 점 위주로 설명한다.Therefore, the description of the present embodiment will be described in the general ceramic manufacturing process briefly or omitted the description, and focuses on the difference from the general process.

본 실시예에서의 원형 제작 단계는, 도 4와 같이, 석고 또는 레진으로 원판을 제조하는 단계(S10)와; 상기 원판을 절단하고 표면에 문양을 새기는 단계(S20)와; 상기 표면에 돌가루를 뿌리는 단계(S30)로 구성된다.Circular production step in the present embodiment, as shown in Figure 4, the step (S10) for manufacturing the original plate gypsum or resin; Cutting the disc and carving a pattern on the surface (S20); It is composed of the step (S30) of spraying stone powder on the surface.

여기서, 레진(resin)이란 유기화합 및 그 유도체로 이루어진 비결정성 고체 또는 반도체를 말하는 것으로, 원판에 문양을 새길 때 원형 조각이 많거나 정교한 조각이 필요한 경우 특히 CNC(Computer Numerical Control Machine) 가공기로 문양을 새길 경우 석고 보다 레진을 원판으로 사용함이 바람직하다.Herein, resin refers to an amorphous solid or semiconductor composed of an organic compound and derivatives thereof, and especially when a large number of circular pieces are needed or sophisticated pieces are required when engraving a pattern on a disc, a pattern is particularly used by a Computer Numerical Control Machine (CNC) processor. In the case of carving, it is preferable to use resin as a base plate rather than gypsum.

상기 원판을 절단하고 표면에 문양을 새기는 단계(S20)는 CNC 가공기로 자동으로 할 수 있음은 물론 디자인된 모눈종이를 상기 원판 표면에 대고 수작업으로 할 수도 있다. 홈 파기 등에는 깊이가 1~2mm 정도가 되도록 함이 바람직하다.Cutting the disc and engraving the pattern on the surface (S20) can be done automatically by a CNC machine, as well as by hand to the designed grid paper on the surface of the disc. For digging grooves, it is desirable to have a depth of about 1 to 2 mm.

다음, 문양이 새겨진 원판 표면에는, 도 5와 같이, 돌가루와 접착수지가 들어 있는 스톤스프레이 등을 이용하여 미세 돌가루를 뿌린다(S30). 이는 성형후 자연석 처럼 표면이 보이게 하기 위함이다.Next, the surface of the pattern is engraved, as shown in Figure 5, using a stone spray, etc. containing stone powder and adhesive resin (S30). This is to make the surface look like natural stone after molding.

이렇게 완성된 원형 표면에 석고 분리제(카리비누)를 부드러운 붓으로 2~3번 정도 반복하며 칠해준 다음, 거푸집 제작단계(S40)에 들어간다.Thus finished plaster surface (caribbean soap) to the finished circular surface repeated two or three times with a soft brush, and then enters the die production step (S40).

석고로 만든 거푸집이 건조되었으면, 슬립(slip) 주입단계(S50)로 들어간다.Once the mold made of gypsum is dried, it enters a slip injection step (S50).

여기서, 슬립을 이루는 소지의 비율은, 투광성을 고려하여, 장석 23 중량%, 규석 10 중량%, 카오린 35 중량%, 도석 27 중량% 및 세리사이트 5 중량%로 하고, 특히, 투광성을 좀 더 높이기 위해서는 선택적으로 상기 성분들의 총 중량비율 3~4%에 해당하는 량으로 본웨시를 더 포함하는 것이 바람직하다.Here, the ratio of the base to the slip is made of 23% by weight of feldspar, 10% by weight of quartzite, 35% by weight of kaolin, 27% by weight of pottery stone and 5% by weight of sericite in consideration of light transmittance. In order to optionally further comprise a bone wesh in an amount corresponding to 3 to 4% of the total weight ratio of the components.

그러나, 투광성을 위한 슬립 소지의 비율은 상기 성분 및 그 함량에 한정되지 아니하고 약간의 변형을 가하거나 다른 조성물로 대체될 수 있다.However, the ratio of slip possession for light transmission is not limited to the above components and their contents, but may be slightly modified or replaced with other compositions.

슬립 주입한지 약 2시간 정도 후에 탈형 단계로 들어가고, 탈형 후 성형된 도벽의 수분 함량이 전체 중량의 30~40%가 될때 투각단계로 들어감이 바람직하다(S60).After about 2 hours of slip injection, it enters the demolding step, and when the moisture content of the molded wall after demolding is 30 to 40% of the total weight, it is preferable to enter the hollow step (S60).

상기 성형된 도벽의 수분 함량이 너무 낮으면 투각하기 어려워질 뿐만 아니라 작업시 크렉이 많이 생길 수 있고, 그렇다고 너무 높으면 투각된 형상이 변형되기 쉬운 문제점이 있다.If the moisture content of the molded conductive wall is too low, not only it is difficult to be hollow, but a lot of cracks may be generated during the work, but if too high, the hollowed out shape may be easily deformed.

투각한 이후 소성단계로 들어가기 전에 붓으로 가감질하여 투각시 생긴 크렉등을 없애는 것이 바람직하다.It is preferable to remove the cracks and the like generated by hollowing out with a brush before entering the firing step after the hollowing out.

상기 투각단계에서는 원판 문양 새김단계(S20)에서 이미 결정된 문양, 이것이 거푸집을 통해 성형된 도벽에 찍힌 문양을 그대로 따라 투각하게 된다(도 6).In the hollow step, the pattern already determined in the disc pattern engraving step (S20), which is hollowed out according to the pattern imprinted on the conductive wall formed through the mold (FIG. 6).

상기 투각단계로 드러난 문양는, 도 6과 같이, 규칙적으로 관통되어 형성된 전통적 꽃살 문양인 것이 바람직하다.The pattern revealed by the hollow step is, as shown in Figure 6, it is preferable that the traditional flower pattern formed through regularly.

투각단계가 완료되면, 소성단계(S70)로 들어가 900℃에서 약 1시간 1차 소성(초벌구이)을 하고, 백미트유 등으로 시유한 후 1250℃에서 약 16시간 2차 소성(재벌구이)을 함으로써 도벽 투광판을 완성하게 된다.When the hollowing step is completed, go to the firing step (S70) to perform the primary firing (primary roasting) for about 1 hour at 900 ℃, after lubricating with white meat oil etc. By doing so, the light guide plate is completed.

상기와 같은 단계를 거쳐 완성된 도벽 투광판은 표면은 자연석 처럼 오돌도돌 튀어나오고, 규칙적으로 투각 관통된 문양으로 전통적 꽃살 무늬 등을 그대로 구현 가능하며, 도자 커버의 투광성을 보완할 수 있어, 미적 효과 뿐만 아니라 실용적 가치를 높일 수 있는 장점이 있다.Finished through the steps as described above, the surface of the floodlight plate is protruding like a natural stone, and can be embodied as a traditional perforated pattern as a regular perforated pattern, and can complement the transparency of the ceramic cover, as well as aesthetic effect But there is an advantage that can increase the practical value.

다음은, 상기 실시예에 의하여 제조된 도벽 투광판을 이용한 조명장치의 실시예에 대하여 설명한다.Next, an embodiment of a lighting apparatus using the light guide plate manufactured by the above embodiment will be described.

이는, 도 1과 같이, 빛을 반사할 수 있도록 도금된 바닥판(10)과; 상기 바닥판의 적어도 일측 측면에 관통(14)되어 인입된 전원선(11)과; 상기 전원선이 상기 바닥판의 가운데 형성된 관통공(16)을 통하여 연결된 램프 소켓(20)과; 상기 바닥판의 네모서리 각각에 체결된 4개의 투명봉(30)과; 상기 각 투명봉 상에 체결된 적어도 하나의 투명평판(50)(60)과; 상기 투명평판 상에 부착된 것으로 상기 제조방법을 통해 제조된 도벽 투광판(70)을 하나 이상 포함한다.This, as shown in Figure 1, the plate 10 is plated to reflect light; A power line 11 penetrated through at least one side of the bottom plate and drawn therein; A lamp socket 20 to which the power line is connected through a through hole 16 formed in the center of the bottom plate; Four transparent rods 30 fastened to each of the four corners of the bottom plate; At least one transparent flat plate 50 and 60 fastened to each transparent rod; At least one conductive wall floodlight plate 70 manufactured by the manufacturing method attached to the transparent flat plate is included.

여기서, 상기 투명평판은 2개(50)(60)로 구성되고 상측 투명평판(60)에는 창호지 문양의 화선지가 내측에 삽입된 것을 사용하는 것이 바람직하다. 이렇게 함으로써, 투각으로 관통된 문양을 통하여 램프의 빛이 바로 빠져 나오는 것을 차단하고, 마치 전통적 문살 사이 창호지로 불빛이 나오는 분위기를 창출할 수 있는 효과가 있다.Here, the transparent flat plate is composed of two (50, 60) and the upper transparent flat plate 60, it is preferable to use that the drawing paper of the window paper pattern is inserted inside. By doing so, it is possible to cut out the light of the lamp through the hollow penetrating pattern and to create an atmosphere in which the light is emitted to the window between the traditional doors.

상기 도벽 투광판(70)은, 도 1과 같이, 하나의 투명평판(60) 상에 4개가 부착되고, 이웃한 도벽 투광판 사이에는 투광 도자로 제조된 측면 부재(80)가 하나 이상 부착되고, 상기 램프 소켓(20)은 상기 각 도벽 투광판 밑에 램프(22)가 하나씩 끼워질 수 있는 구조로 하는 것이 바람직하다.As shown in FIG. 1, four conductive wall floodlight plates 70 are attached to one transparent flat plate 60, and at least one side member 80 made of a transparent light guide is attached between adjacent conductive wall floodlight plates. Preferably, the lamp socket 20 has a structure in which one lamp 22 is fitted under each of the light guide plates.

도 1은 본 실시예인 도벽 투광판을 이용한 조명장치의 분해사시도이므로, 각 대응되는 부품들을 체결되면, 도 2와 같은 구조를 갖게 되고, 도 2의 AA선을 절단 하면 도 3과 같은 구조를 갖게 된다.1 is an exploded perspective view of a lighting apparatus using a light guide plate according to the present embodiment, when the corresponding parts are fastened, the structure is the same as that of FIG. 2, and the AA structure of FIG. do.

도 1에서 미설명된 도면부호 1은 하측 체결 나사, 2는 와셔, 3은 상측 체결나사, 13은 내측 도선, 15 및 17은 도선 연결구, 12 및 18은 관통공(특히, 18은 조명장치 벽걸이용 관통공), 41, 43 및 45는 하부 투명평판(50)을 지지하는 지지부재이고, 42, 52 및 62는 상측나사 체결용 관통공이다.In Fig. 1, reference numeral 1 denotes a lower fastening screw, 2 a washer, 3 is an upper fastening screw, 13 is an inner lead, 15 and 17 are lead connectors, and 12 and 18 are through holes (in particular, 18 is a wall of a lighting device). For through holes), 41, 43, and 45 are support members for supporting the lower transparent flat plate 50, and 42, 52, and 62 are through holes for fastening upper screws.

그리고, 도 2에서 미설명된 도면 부호 72는 투각으로 관통된 빛 방출 구, 74는 표면에 오돌도돌 굴곡진 형상을 나타낸다.In addition, reference numeral 72, which is not described in FIG. 2, represents a light-emitting sphere penetrating through the hollow, and 74 represents an odoldodol curved shape on the surface.

상기 실시예에서 4개의 투명봉(30), 지지부재(41)(43)(45) 및 투명평판(50)(60)은 아크릴 소재로 만들어 질 수 있고, 바닥판(10)에는 크롬도금으로 빛의 반사도를 높이는 것이 바람직하다.In the embodiment, the four transparent rods 30, the support members 41, 43, 45 and the transparent flat plate 50, 60 may be made of acrylic material, and the bottom plate 10 is made of chromium plating. It is desirable to increase the reflectivity of light.

상기 실시예에 의한 도벽 투광판을 이용한 조명장치는 자체 투광성 있는 도벽에 투각으로 관통된 빛 방출 구를 일정한 문양으로 더 형성함으로써, 도벽이 갖고 있던 투광성의 한계를 극복하면서, 마치 전통적 문살 사이 창호지로 불빛이 나오는 분위기도 창출할 수 있는 장점이 있다.The lighting apparatus using the light guide plate according to the above embodiment forms a light emitting hole penetrating through the permeable light on the self-transmissive light wall in a constant pattern, thereby overcoming the limitations of light transmittance of the light wall, as a window between traditional doors. It also has the advantage of creating an atmosphere of light.

도 7은 상기 실시예에 의한 조명장치를 2개 결합하여 구현한 일 실시 모습을 보여주는 사진으로, 투각 관통된 빛 방출 구 사이로 빛이 나오면서 백색의 도자 색이 아닌 갈색의 은은한 색으로 마치 전통적 문살 사이로 불빛이 나오는 효과가 있음을 보여준다.FIG. 7 is a photograph showing an embodiment of a combination of two lighting apparatuses according to the above embodiment. The light is emitted through a through-hole light emitting port, and is not a white ceramic color. Shows that there is a light effect.

도 1은 본 발명에 의한 도벽 투광판을 이용한 조명장치의 분해사시도이다.1 is an exploded perspective view of a lighting apparatus using a light guide plate according to the present invention.

도 2는 본 발명에 의한 도벽 투광판을 이용한 조명장치의 사시도와 요부 확대도이다.Figure 2 is a perspective view and an enlarged view of the main portion of the lighting apparatus using a light guide plate according to the present invention.

도 3은 도 1의 AA선 단면도이다.3 is a cross-sectional view taken along the line AA of FIG.

도 4는 본 발명에 의한 도벽 투광판의 제조방법을 보여주는 공정 순서도이다.4 is a process flowchart showing the manufacturing method of the light guide plate according to the present invention.

도 5는 본 발명에 의한 도벽 투광판의 제조방법에서 스톤스프레이 뿌림단계를 보여주는 일 실시 상태도이다.Figure 5 is an embodiment showing a stone spray sprinkling step in the manufacturing method of the light guide plate according to the present invention.

도 6은 본 발명에 의한 도벽 투광판의 제조방법에서 투각 단계를 보여주는 일 실시 상태도이다.6 is an exemplary embodiment showing a projection step in the manufacturing method of the light guide plate according to the present invention.

도 7은 본 발명에 의한 도벽 투광판을 이용한 조명장치의 일 실시 상태도이다.7 is a view showing an embodiment of a lighting apparatus using a light guide plate according to the present invention.

<도면의 주요부분에 대한 부호의 설명><Description of the symbols for the main parts of the drawings>

10: 바닥판 20 : 램프 소켓10: bottom plate 20: lamp socket

30: 투명봉 41, 43, 45: 지지부재30: transparent rod 41, 43, 45: support member

50, 60: 투명평판 70: 도벽 투광판50, 60: transparent flat plate 70: conductive wall floodlight plate

72: 투각 관통된 빛 방출 구 74: 표면 요철72: hollow penetration light emission sphere 74: surface irregularities

Claims (8)

원형 제작단계, 거푸집 제작단계, 슬립 주입단계, 탈형 단계 및 소성단계를 포함하여 구성된 투광성 도자 커버 제조방법에 있어서,In the method of manufacturing a translucent ceramic cover comprising a circular manufacturing step, formwork manufacturing step, slip injection step, demolding step and firing step, 상기 원형 제작단계는,The prototype manufacturing step, 석고 또는 레진으로 원판을 제조하는 단계와;Preparing a disc from gypsum or resin; 상기 원판을 절단하고 표면에 문양을 새기는 단계와;Cutting the disc and engraving a surface; 상기 표면에 돌가루를 뿌리는 단계로 구성되고,Consists of spraying stone on the surface, 상기 탈형 단계와 상기 소성단계 사이에는 투각단계를 더 포함하되,Between the demolding step and the firing step further comprises an openwork step, 상기 투각단계는 상기 탈형 단계로 성형된 도벽의 수분함량이 전체 중량의 30~40%일때 실시하고, 투각이후 상기 소성단계 전에 붓으로 가감질하는 단계를 더 포함하는 것을 특징으로 하는 도벽 투광판의 제조방법.The projection step is carried out when the moisture content of the conductive wall formed by the demolding step is 30 to 40% of the total weight, and after the hollow projection step of the coating wall before and after the firing step further comprising the step of adjusting Manufacturing method. 제 1 항에 있어서,The method of claim 1, 상기 원판을 절단하고 표면에 문양을 새기는 단계는 CNC 가공기로 자동으로 또는 디자인된 모눈종이를 상기 원판 표면에 대고 수작업으로 하고,The step of cutting the disc and engraving the surface is done manually by pressing the disc surface automatically or designed with a CNC machine, 상기 표면에 돌가루를 뿌리는 단계는 스톤스프레이를 이용하며,The step of spraying stone on the surface using a stone spray, 상기 투각단계는 상기 표면에 새겨진 문양에 따라 도벽 투광판을 관통시키며 투각하는 것을 특징으로 하는 도벽 투광판의 제조방법.The projection step is a manufacturing method of the light guide plate, characterized in that through the penetration through the light guide plate according to the pattern engraved on the surface. 제 2 항에 있어서,The method of claim 2, 상기 슬립 주입단계의 슬립을 이루는 소지의 비율은 장석 23 중량%, 규석 10 중량%, 카오린 35 중량%, 도석 27 중량% 및 세리사이트 5 중량%로 하고, 선택적으로 상기 성분들의 총 중량비율 3~4%에 해당하는 량으로 본웨시를 더 포함하는 것을 특징으로 하는 도벽 투광판의 제조방법.The proportion of the base forming the slip of the slip injection step is 23% by weight of feldspar, 10% by weight of quartz, 35% by weight of kaolin, 27% by weight of pottery stone and 5% by weight of sericite, and optionally 3 to 3% by weight of the total weight of the components. A method for manufacturing a light guide plate, characterized in that it further comprises Bonwei in an amount corresponding to 4%. 삭제delete 제 3 항에 있어서,The method of claim 3, wherein 상기 투각단계로 드러난 문양는 규칙적으로 관통되어 형성된 전통적 꽃살 문양인 것을 특징으로 하는 도벽 투광판의 제조방법. The pattern revealed by the hollow step is a method of manufacturing a floodlight plate, characterized in that the traditional flower pattern formed through the regular. 빛을 반사할 수있도록 도금된 바닥판과;A bottom plate plated to reflect light; 상기 바닥판의 적어도 일측 측면에 관통되어 인입된 전원선과;A power supply line penetrated through at least one side surface of the bottom plate; 상기 전원선이 상기 바닥판의 가운데 형성된 관통공을 통하여 연결된 램프 소켓과;A lamp socket connected to the power line through a through hole formed in the center of the bottom plate; 상기 바닥판의 네모서리 각각에 체결된 4개의 투명봉과;Four transparent rods fastened to each of the four corners of the bottom plate; 상기 각 투명봉 상에 체결된 적어도 하나의 투명평판과;At least one transparent flat plate fastened on each transparent bar; 상기 투명평판 상에 부착된 상기 제 5 항에 의하여 제조된 도벽 투광판을 하나 이상 포함하는 것을 특징으로 하는 도벽 투광판을 이용한 조명장치.Illumination apparatus using a light guide plate, characterized in that it comprises at least one of the light guide plate made of claim 5 attached to the transparent plate. 제 6 항에 있어서,The method of claim 6, 상기 투명평판은 2개로 구성되고 상측 투명평판에는 창호지 문양의 화선지가 내측에 삽입된 것을 특징으로 하는 도벽 투광판을 이용한 조명장치.The transparent plate is composed of two and the upper transparent plate is a lighting device using a light guide plate, characterized in that the drawing paper of the window paper pattern is inserted inside. 제 7 항에 있어서,The method of claim 7, wherein 상기 도벽 투광판은 하나의 투명평판 상에 4개가 부착되고, 이웃한 도벽 투광판 사이에는 투광 도자로 제조된 측면 부재가 하나 이상 부착되고,Four conductive wall floodlight plates are attached on one transparent flat plate, and at least one side member made of a transparent light guide is attached between neighboring conductive wall light emitting plates. 상기 램프 소켓은 상기 각 도벽 투광판 밑에 램프가 하나씩 끼워질 수 있는 구조로 된 것을 특징으로 하는 도벽 투광판을 이용한 조명장치. The lamp socket is a lighting device using a light guide plate, characterized in that the lamp is fitted under the light guide plate one by one structure.
KR1020090026130A 2009-03-26 2009-03-26 Fabrication method of ceramic wall for floodlighting and lighting apparatus using ceramic wall babricated by the same KR100927030B1 (en)