KR100866241B1 - Quick-drying pure cotton fabric with two faces having different properties and a method of producing same - Google Patents
Quick-drying pure cotton fabric with two faces having different properties and a method of producing same Download PDFInfo
- Publication number
- KR100866241B1 KR100866241B1 KR1020067018723A KR20067018723A KR100866241B1 KR 100866241 B1 KR100866241 B1 KR 100866241B1 KR 1020067018723 A KR1020067018723 A KR 1020067018723A KR 20067018723 A KR20067018723 A KR 20067018723A KR 100866241 B1 KR100866241 B1 KR 100866241B1
- Authority
- KR
- South Korea
- Prior art keywords
- cotton
- fabric
- yarn
- hydrophobic
- hydrophilic
- Prior art date
Abstract
본 발명은 안과 바깥 면 또는 내부층과 외부층 각각이 소수성 및 친수성인 유형의 순면직물 및 그 제조방법에 관한 것이다. 본 직물은 내부층으로 본질적으로 소수성 면과 외부층으로 본질적으로 친수성 면을 가져서 일방향으로 수분을 수송시킬 수 있다. 본 방법은 외부층과 내부층의 순면사에 각각 친수성 마감 및 소수성 마감을 하여 친수성 실 및 소수성으로 피니슁된 실을 얻은 다음; 편직함으로써 내부층과 외부층이 소수성과 친수성으로 상이한 직물 또는 조직을 얻는 것으로 기본적으로 이루어지는데, 이는 발한 기능을 가지며 착용자에게 안락하게 느껴진다.The present invention relates to a cotton fabric of the type in which the inner and outer surfaces, or the inner and outer layers, respectively, are hydrophobic and hydrophilic, and a method of making the same. The fabric has an essentially hydrophobic side as the inner layer and an essentially hydrophilic side as the outer layer to transport moisture in one direction. The method comprises hydrophilic and hydrophobic finishes on the cotton yarns of the outer and inner layers, respectively, to obtain hydrophilic and hydrophobic finished yarns; By knitting, the inner and outer layers basically consist of obtaining different fabrics or tissues in hydrophobicity and hydrophilicity, which have a sweating function and feel comfortable to the wearer.
소수성, 친수성, 상이한 속성, 순면사, 일방향, 신속 건조, 안락감Hydrophobicity, Hydrophilicity, Different Properties, Cotton Yarn, One-Way, Quick Dry, Comfort
Description
본 발명은 한 유형의 순면직물과 이의 제조방법에 관한 것이다. 특히, 두 개의 면이 상이한 속성을 갖는 유형의 신속 건조 순면직물과 이의 제조방법에 관련된다. 본 발명에서 정의되는 "두 개의 면"이라 함은 단일 니트 직물의 앞,뒷면 또는 이중 니트 직물의 내외부층을 일컬을 수 있다.The present invention relates to a type of cotton fabric and a method of manufacturing the same. In particular, it relates to a quick-drying cotton fabric of the type with two sides having different properties and to a process for its preparation. The term "two sides" as defined in the present invention may refer to the front and back sides of a single knit fabric or the inner and outer layers of a double knit fabric.
삶의 질이 계속하여 개선되고 섬유 산업이 발달함에 따라 소비자들은 편안함, 기능성, 외관 및 착용감을 비롯한 모든 면에서 의복이 계속하여 개선되길 기대한다. 따라서, 편안하고 일종의 기능성을 갖춘 직물의 생산은 앞으로의 섬유 산업의 경향이다.
소비자들은 천연 섬유 직물, 특히 순면직물을 이의 편안함 및 환경적 이로움 때문에 강하게 선호한다. 순면직물은 일반적으로 나은 흡수성을 갖지만, 수분을 흡수한 후에는 피부에 달라붙어 착용자가 불편함을 느끼게 한다. 따라서, 수분을 흡수할 수 있고 땀을 배수하여 없애 신속하게 건조할 수 있는 수분 처리 직물을 만든다면 매우 실용적일 것이며, 이는 건조되어 착용하기 편안하며 기분 좋게 만지게 될 것이다.
두 가지 주요 유형의 수분 처리 직물이 시중에 나와 있다.
첫 번째 유형의 직물은 오리털 함유 폴리에스테르 섬유와 같이 차동 섬유로 만들어진 니트로서, DUPONT의 COOLMAX와 대만의 COOLPLUS가 잘 알려진 예들이다. 이들 섬유는 독특한 네 개의 채널 디자인을 갖는 기능성 합성 섬유이다. 이들 채널들은 직물의 외부층으로 땀과 수분을 재빨리 이송한다. 따라서, 양호한 수분 처리 속성을 갖는다. 그러나 이런 유형의 기능성 섬유를 사용하여 만들어진 니트 직물은 일정한 단점을 갖는다. 이론적으로, 섬유는 모세관 작용에 의하여 물 또는 땀을 수송하는 네 개의 채널을 갖도록 고안되어 있다. 일단 이들 채널이 막히게 되면, 수분 처리 성능은 나빠진다. 실제로, 이들 섬유들은 100 내지 130 ℃에서 분산 염색을 사용하여 염색된다. 섬유내 일부 올리고머들은 고온하에서 해리되어 섬유내로 결합함으로써 채널을 막고 수분 처리 성능을 떨어뜨린다. 게다가, 이들 기능성 섬유들은 합성섬유들이다. 따라서, 이런 유형의 100% 기능성 섬유로부터의 직물 니트는 면직물의 부드러운 감촉을 결여할 것이다. 면섬유와 이런 유형의 기능성 섬유로부터 가공된 조합실을 사용한다면 심한 다모현상과 나쁜 색상 정착과 같은 결점으로부터 고생할 것이다. 여러 번의 가정 세탁 후, 이러한 실로 만들어진 니트 직물은 일반적으로 많은 표면 털을 가지고 명백한 색상 쇠퇴를 보일 것이다. 특히, 평-니트 칼라는 세탁 후 심각하게 변형될 것이다. 또한, 세탁 후 더 낮은 수분 처리 성능을 갖게 될 것이다.
두 번째 유형의 직물은 합성 섬유와 면의 조합 방적 또는 편직을 통해 증진된 수분 처리능력 및 건조 편안함을 획득한다. 실제 결과는 이런 종류의 직물이 수분 흡수 능력에서는 더 강하고 신속 건조 성능에서는 덜 강함을 보여준다. 게다가, 이런 종류의 직물은 합성 섬유를 사용할 것을 필요로 하므로 편안하거나 환경 친화적이지 않다.
따라서, 신속하게 건조되는 순면의 수분 처리 직물, 건조되어 착용하기에 편안하고 기분 좋게 손으로 만져지고 보기에 즐거우며 반복된 세탁 하에서 상태가 잘 유지되는 직물을 만드는 것이 단연코 필요하다.As the quality of life continues to improve and the textile industry develops, consumers expect clothing to continue to improve in every respect, including comfort, functionality, appearance and fit. Therefore, the production of comfortable and functional fabrics is a trend in the future textile industry.
Consumers strongly prefer natural fiber fabrics, especially cotton fabrics, because of their comfort and environmental benefits. Cotton fabrics generally have better absorbency, but after absorbing moisture, they stick to the skin and make the wearer feel uncomfortable. Therefore, it would be very practical to make a moisture treated fabric that can absorb moisture and drain away sweat to dry quickly, which will be dry, comfortable to wear and pleasant to touch.
Two major types of moisture treatment fabrics are available on the market.
The first type of fabric is a knit made of differential fibers, such as duck-containing polyester fibers, the well known examples of DUPONT's COOLMAX and Taiwan's COOLPLUS. These fibers are functional synthetic fibers with a unique four channel design. These channels quickly transfer sweat and moisture to the outer layer of the fabric. Thus, it has good water treatment properties. However, knitted fabrics made using this type of functional fiber have certain disadvantages. In theory, the fiber is designed to have four channels for transporting water or sweat by capillary action. Once these channels are blocked, the moisture treatment performance is poor. In practice, these fibers are dyed using disperse dyes at 100-130 ° C. Some oligomers in the fiber dissociate under high temperature to bind into the fiber, clogging channels and degrading water treatment performance. In addition, these functional fibers are synthetic fibers. Thus, knit fabrics from this type of 100% functional fibers will lack the soft feel of cotton fabrics. The use of combination yarns made from cotton fibers and functional fibers of this type will suffer from drawbacks such as severe hair growth and poor color fixation. After several household washings, knitted fabrics made of these threads will generally have a lot of surface hair and show a pronounced color decline. In particular, the flat-knit collar will be severely deformed after washing. It will also have lower moisture handling performance after washing.
The second type of fabric achieves enhanced moisture handling capacity and dry comfort through the combination spinning or knitting of synthetic fibers and cotton. Actual results show that this type of fabric is stronger in water absorption capacity and less strong in fast drying performance. In addition, this type of fabric requires the use of synthetic fibers and therefore is not comfortable or environmentally friendly.
Thus, there is a need to produce a cotton fabric that dries quickly, a fabric that is dry, comfortable to wear, pleasant to the touch, pleasant to look at, and well maintained under repeated washing.
본 발명은 두 개의 면이 상이한 속성을 갖는 유형의 신속 건조 순면직물을 제공한다. 하나의 직물에서 상이한 속성을 지닌 두 개의 면의 결합은 직물에 합성 섬유의 수분 처리 및 신속 건조의 이점을 제공하는 한편 착용하기 편안하며 기분 좋게 만져지며 모양 보유력, 양호한 내구성 및 신속 건조의 순면직물의 특성을 유지케 한다.The present invention provides a quick-drying pure cotton fabric of the type where the two sides have different properties. The combination of two sides with different properties in one fabric provides the fabric with the benefits of water treatment and quick drying of synthetic fibers, while being comfortable to wear and pleasant to touch, and having a shape retention, good durability and quick drying cotton fabric Maintains characteristics
위에서 기술된 목표들을 성취하기 위해서, 본 발명에서 제공되는 직물은 상이한 속성을 갖는 두 개의 면을 지닌 유형의 순면이다. 직물의 한 면은 소수성 면으로 대부분 또는 전부가 소수성 순면사인 실로부터 형성된다. 다른 면은 친수성 면으로 대부분 또는 전부가 친수성 순면사인 실로부터 형성된다. 게다가, 상기 직물은 일방향으로 물을 수송할 수 있다.In order to achieve the goals described above, the fabric provided in the present invention is a type of pure cotton with two sides with different properties. One side of the fabric is hydrophobic and is formed from a yarn that is mostly or entirely hydrophobic cotton yarn. The other side is hydrophilic and is formed from yarn, most or all of which is a hydrophilic cotton yarn. In addition, the fabric can transport water in one direction.
본 발명에서 제공되는 두 개의 상이한 속성의 면을 지닌 신속 건조 순면직물을 현재의 산물들과 비교할 때, 가장 중요한 특징은 직물의 두 개의 면(또는 내외부층)이 상이한 기능을 갖는다는 것이다. 즉, 한 면은 소수성이고 다른 면은 친수성이다. 적절한 편직을 거치게 되면 일방향으로 물을 수송할 수 있는 유형의 순면직물이 된다. 따라서, 본 발명에서 기술된 두 개의 면은 단일-니트 직물의 앞뒷면일 수 있다. 또한, 이중-니트 구조를 지닌 직물의 내외부층일 수도 있다.When comparing a quick-drying pure cotton fabric with two different attributes of cotton provided in the present invention with current products, the most important feature is that the two sides (or inner and outer layers) of the fabric have different functions. One side is hydrophobic and the other side is hydrophilic. With proper knitting, it becomes a type of cotton fabric capable of transporting water in one direction. Thus, the two sides described herein may be the front and back sides of a single-knit fabric. It may also be the inner and outer layers of a fabric having a double-knit structure.
본 발명의 바람직한 양태에 따르면, 상기 순면직물의 소수성 면과 친수성 면은 별개의 소수성 및 친수성 처리를 거친 순면사로부터 편직된다. 소수성 면을 형성하는데 사용되는 실은 소수성으로 처리된 실 60% 내지 100%와 친수성으로 처리된 실 0% 내지 40%를 바람직하게 함유해야 한다. 친수성 면을 형성하는데 사용되는 실은 바람직하게는 친수성으로 처리된 실 100% 이어야 한다.According to a preferred embodiment of the present invention, the hydrophobic and hydrophilic sides of the pure cotton are knitted from cotton yarns that have undergone separate hydrophobic and hydrophilic treatments. The yarn used to form the hydrophobic face should preferably contain 60% to 100% of the hydrophobically treated yarn and 0% to 40% of the hydrophilically treated yarn. The yarn used to form the hydrophilic side should preferably be 100% yarn treated with hydrophilicity.
본 발명에서 제공되는 상기 기술된 직물에서, 소수성 면을 형성하는 실은 의 소수성으로 처리된 실 60% 내지 99%와 친수성으로 처리된 실 1% 내지 40%를 함유한다. 또는 소수성 면을 형성하는 실은 소수성으로 처리된 실 100% 일 수도 있다.In the fabric described above provided in the present invention, the yarn forming the hydrophobic cotton contains 60% to 99% of the hydrophobic treated yarn and 1% to 40% of the hydrophilic treated yarn. Alternatively, the yarn forming the hydrophobic face may be 100% of the yarn treated with hydrophobicity.
상기 기술된 면사로부터의 니트인 직물의 소수성 면은 또한 일정 함량의 친수성 포인트(예, 도 1에서 친수성으로 처리된 실)를 함유하는데, 이는 소수성 면의 물을 친수성 면으로 수송할 수 있다. 이는 수송된 물과 땀을 재빨리 퍼지게 하여 증발시킬 수 있다. 이는 소수성 면과 함께 물 이송에 대한 유인력을 제공하는 내-외부 격차를 형성한다. 이러한 특질에 의하여, 물과 땀은 직물의 소수성 면으로부터 친수성 면으로 신속하게 침투한 다음 재빨리 퍼지고 증발할 수 있다. 이러한 방식으로, 일방향으로의 물 수송과 신속 건조 효과가 빠르게 성취된다. 그 결과, 직물의 소수성 면은 건조하고 안락하게 남아 있고; 수분 처리 및 신속-건조 기능을 갖는다. 이러한 직물로부터 제조된 의류는 건조 및 안락한 착용, 땀 흡수 및 신속 건조를 특징으로 한다. 따라서, 특정 실시예에서, 상기 소수성 면은 소수성 실로 전적으로 형성될 수 있고, 적절한 편직 기술 결과, 소량의 "친수성 포인트"을 가질 것이다. 또한 상이한 직물 구조에 따라 적절히 소량의 친수성 실을 소수성 실에 추가하여 물이 소수성 표면으로부터 흡수될 수 있는 것을 보장할 수 있다. 상기에서 기술되었듯이, 소수성 면을 형성하는 실은 최소한 대부분의 소수성으로 처리된 실을 함유한다. 즉, 추가되는 친수성 실의 함량은 50% 또는 그 아래로 유지되어야 한다. 바람직하게, 소수성 면을 형성하는 실은 소수성으로 처리된 실 60% 내지 99%와 친수성으로 처리된 실 1% 내지 40%를 함유한다. 상기 친수성 면은 대부분 또는 전부 친수성으로 처리된 실이다. 이상적으로는 친수성으로 처리된 실 100% 이다. 즉, 소수성 면에서 물은 직물의 친수성 면으로 빠르게 흡수되어 확산된다. 더욱이, 직물의 특질, 즉, 두 개의 면의 속성에서의 차이는 영향받지 않은 채 남아 있다. 본 발명의 직물은 두 개의 상이한 속성의 면을 형성할 수 있고 일방향으로 물 수송을 성취할 수 있는 임의 공지된 편직 방법에 의해 편직될 수 있다. 즉, 상기 직물은 상기 기술된 순면사로부터의 니트인 다양한 구조 및 패턴의 이중-니트 직물이거나 또는 상기 기술된 순면사로부터의 니트의 단일-니트 플레이티드(plated) 직물일 수 있다. 예컨대, 상기 직물은 리브(rib) 직물, 이중-니트 양면 직물, 이중-니트 리브 자카드(jacquard) 직물, 및 모든 단일 니트 플레이티드 직물일 수 있다. 단일 니트 플레이티드 직물은 단일-니트 플레이티드 저지(jersey) 직물, 단일-니트 플레이티드 피크(pique) 직물, 단일 니트 플레이티드 라코스테(Lacoste) 직물 또는 단일 니트 플레이티드 자카드 직물일 수 있으나, 이들에 국한되지는 않는다.The hydrophobic cotton of the fabric that is knit from the cotton yarn described above also contains a certain amount of hydrophilic points (eg, the hydrophilic yarn in FIG. 1), which can transport the hydrophobic cotton's water to the hydrophilic cotton. This can quickly spread the evaporated water and sweat. This, together with the hydrophobic side, forms an internal-external gap that provides attraction to water transfer. By this feature, water and sweat can quickly penetrate from the hydrophobic side of the fabric to the hydrophilic side and then quickly spread and evaporate. In this way, the water transport in one direction and the quick drying effect are quickly achieved. As a result, the hydrophobic side of the fabric remains dry and comfortable; Has moisture treatment and quick-drying function. Garments made from such fabrics are characterized by dry and comfortable wear, sweat absorption and quick drying. Thus, in certain embodiments, the hydrophobic face may be formed entirely of hydrophobic yarns and will have a small amount of "hydrophilic point" as a result of proper knitting techniques. It is also possible to add appropriately small amounts of hydrophilic yarns to the hydrophobic yarns according to different fabric structures to ensure that water can be absorbed from the hydrophobic surface. As described above, the yarns forming the hydrophobic face contain at least the most hydrophobicly treated yarns. That is, the amount of hydrophilic yarn added should be maintained at or below 50%. Preferably, the yarn forming the hydrophobic face contains from 60% to 99% of the hydrophobically treated yarn and from 1% to 40% of the hydrophilically treated yarn. The hydrophilic cotton is yarn treated most or all of the hydrophilicity. Ideally 100% of the treated hydrophilic yarn. That is, in the hydrophobic aspect, water is quickly absorbed and diffused into the hydrophilic side of the fabric. Moreover, the difference in the properties of the fabric, ie the properties of the two sides, remains unaffected. The fabric of the present invention can be knitted by any known knitting method that can form two different properties of cotton and can achieve water transport in one direction. That is, the fabric may be a double-knit fabric of various structures and patterns that are knit from the cotton yarn described above or a single-knit plated fabric of knit from the cotton yarn described above. For example, the fabric may be a rib fabric, a double-knit double sided fabric, a double-knit rib jacquard fabric, and all single knit plated fabrics. The single knit plated fabric may be a single-knit plated jersey fabric, a single-knit plated peak fabric, a single knit plated Lacoste fabric or a single knit plated jacquard fabric, but It is not limited.
따라서, 본 발명은 100% 순면물질로 제조되며 편안함을 수분 처리 및 신속 건조 기능과 통합시킨 신속 건조 면직물을 제공한다. 더욱이, 입었을 때 아주 기분 좋게 만져지며 최상의 안락감을 갖는다.Thus, the present invention provides a quick dry cotton fabric made from 100% cotton material and incorporating comfort with moisture treatment and quick drying functions. Moreover, it feels very comfortable to wear and has the best comfort.
더 나아가, 본 발명은 두 개의 상이한 속성의 면을 지닌 상기 신속 건조 순면직물의 제조방법도 제공한다. 독특한 처리 공정에 의해 면사는 편직된 순면직물의 두 개의 면 각각이 상이한 기능을 갖게 하여 일방향으로의 물 수송, 편안한 착용감 및 증진된 수분 처리 및 신속 건조와 같은 특별한 효과를 성취하는 상이한 처리를 거친다.Furthermore, the present invention also provides a method of making the quick-drying pure cotton fabric with two different properties of cotton. By a unique treatment process, the cotton yarn undergoes different treatments, each of which has two different sides of the knitted cotton fabric having different functions to achieve special effects such as water transport in one direction, comfortable fit and enhanced moisture treatment and quick drying.
본 발명에서 제공되는 두 개의 상이한 속성의 면을 지닌 순면직물의 제조방법은 다음과 같은 단계들을 포함한다: 순면사에 별개의 친수성 및 소수성 처리를 한다. 그 결과 친수성으로 처리된 실과 소수성으로 처리된 실을 얻는다. 그러고 나서, 두 가지 유형의 실을 적절히 편직하여 일방향으로 물을 수송할 수 있고 두 개의 면이 상이한 속성을 갖는 직물을 얻는다.The method for producing a cotton fabric having two different properties of cotton provided in the present invention comprises the following steps: The cotton yarn is subjected to separate hydrophilic and hydrophobic treatments. The result is a yarn treated with hydrophilicity and a yarn treated with hydrophobicity. The two types of yarn are then properly knitted to obtain a fabric that can transport water in one direction and that the two sides have different properties.
구체적으로, 본 발명에 의하여 제공되는 방법에 따른 실에 사용되는 상기 친수성 처리 공정은 하기와 같은 절차로 기본적으로 이루어진다: 실 염색하기, 배쓰에서 유연하게 하기 및 건조하기.Specifically, the hydrophilic treatment process used for the yarns according to the method provided by the present invention consists essentially of the following procedures: dyeing yarns, flexing in baths and drying.
1) 상기 기술된 절차에서, 실 염색하기 공정은 알려진 정련하기, 염색하기, 비누칠하기, 및 고정하기의 절차로 구성된다.1) In the procedure described above, the yarn dyeing process consists of known refining, dyeing, soaping, and fixing procedures.
2) 배쓰에서 유연하게 하는 상기 절차는 친수성 유연제(친수성 유연유로도 부름)로 면사를 처리하는 것으로 구성된다. 본 발명에 따르면, 면사는 지방족 아민, 지방족 아민 유도체, 유기 실리콘 및 이들의 화합물로 구성된 군으로부터 바람직하게 선택되는 친수성 유연제로 처리한다. 더욱 바람직하게, 폴리에테르-변성 에폭시에탄 또는 에폭시프로판 중합체의 유기 실리콘 유연제를 사용한다. 유연제는 1 리터의 처리 배쓰당 1 내지 10 그램의 농도로 사용한다. 상기 유연제 함유 처리 배쓰 대 처리될 면사의 액체 비율은 1:5 및 1:10 사이이다. 처리는 10 내지 50 분 소요되며, 처리 온도는 30 내지 100 ℃이다.2) The procedure for softening in the bath consists of treating the cotton yarn with a hydrophilic softener (also called hydrophilic softener). According to the invention, the cotton yarn is treated with a hydrophilic softener preferably selected from the group consisting of aliphatic amines, aliphatic amine derivatives, organosilicones and compounds thereof. More preferably, an organic silicone softener of polyether-modified epoxy ethane or epoxy propane polymer is used. Softeners are used at a concentration of 1 to 10 grams per liter of treatment bath. The liquid ratio of the softener-containing treatment bath to the cotton yarn to be treated is between 1: 5 and 1:10. The treatment takes 10 to 50 minutes and the treatment temperature is 30 to 100 ° C.
친수성 기를 함유하기 때문에, 본 발명의 상기 기술된 유연제는 물 분자와 수소 결합을 형성할 수 있다. 따라서, 물에 대하여 탁월한 습윤 속성을 갖는다. 게다가, 침투성을 증진시키기 위하여, 에틸 방향족 지방족 에테르 계면활성제(PBN 등) 또는 지방족 알콜 폴리옥시에틸렌 에테르 비-이온성 계면활성제(66-HK 등)와 같은 폴리옥시에틸렌 에테르 화합물을 침투제로서 처리 배쓰에 가할 수 있다. 일반적으로 상기 침투제는 1 리터의 처리 배쓰에 대하여 1 내지 5 그램 사용한다.Because it contains hydrophilic groups, the softeners described above of the present invention can form hydrogen bonds with water molecules. Thus, it has excellent wetting properties for water. Furthermore, in order to enhance the permeability, polyoxyethylene ether compounds such as ethyl aromatic aliphatic ether surfactants (PBN, etc.) or aliphatic alcohol polyoxyethylene ether non-ionic surfactants (66-HK, etc.) may be used as treatment agents. Can be added. Generally the penetrant is used in the amount of 1 to 5 grams for 1 liter of treatment bath.
처리 공정 동안에, 면사는 다른 유형의 유연제로 오염되면 안 되며, 수반되는 장치는 주의 깊게 세정해야 한다.During the treatment process, the cotton yarn should not be contaminated with other types of softeners and the accompanying equipment should be carefully cleaned.
3) 처리된 면사를 대략 80 내지 150 ℃에서 건조한다.3) The treated cotton yarn is dried at approximately 80 to 150 ° C.
본 발명의 방법에 따른 면사에 사용되는 상기 소수성 처리 공정은 실을 염색하기, 소수성 제제로 처리하기 및 건조하기를 포함한다.The hydrophobic treatment process used for the cotton yarn according to the method of the present invention includes dyeing the yarn, treating with a hydrophobic agent and drying.
상기 기술된 절차에서, 실 염색하기는 알려진 정련하기, 염색하기, 비누칠하기, 및 고정하기의 공정으로 구성된다.In the procedure described above, yarn dyeing consists of the processes of known refining, dyeing, soaping, and fixing.
바람직하게, 소수성 처리는 40 내지 100 ℃ 사이에서 5 내지 60 분간 리터당 1 내지 100 g의 소수성 제제를 가지고 수행한다.Preferably, the hydrophobic treatment is carried out with 1 to 100 g of hydrophobic preparation per liter for 5 to 60 minutes between 40 and 100 ° C.
본 발명에서 사용되는 소수성 제제는 다음에서 선택될 수 있다: 지방족 산 아미드, 폴리시안아미드, 유기 실리콘 또는 탄화불소 소수성 제제. 구체적으로, 본 발명에 적용되는 상기 소수성 제제는 히드록시메틸 지방족 산 아미드, 에테르화 폴리히드록시메틸 멜라민, 하이드로실리콘 오일 에멀젼 및 유기 불소 에멀젼으로 구성된 군으로부터 선택될 수 있다. 상기 히드록시메틸 지방족 산 아미드 소수성 제제는 바람직하게 장쇄 히드록시메틸 지방족 산 아미드이다. 탄소 쇄의 바람직한 길이는 14 내지 28개의 탄소 원자이다. 상기 하이드로실리콘 오일 에멀젼은 양이온의 실리콘을 지닌 하이드로실리콘 오일 에멀젼일 수 있으며 또는 활성기-보유(active group-carrying) 폴리디메틸실록산 하이드로실리콘 오일 에멀젼 또는 메틸 하이드로실리콘 오일 에멀젼일 수 있다. 상기 유기 불소 에멀젼은 불소-함유 알킬 아크릴레이트 공중합체 에멀젼, 불소수지, 및 탄화불소 및 탄화수소의 배위 혼합물로 구성된 군으로부터 선택된다.Hydrophobic agents used in the present invention may be selected from: aliphatic acid amides, polycyanamides, organosilicon or fluorocarbon hydrophobic agents. Specifically, the hydrophobic agent applied in the present invention may be selected from the group consisting of hydroxymethyl aliphatic acid amide, etherified polyhydroxymethyl melamine, hydrosilicone oil emulsion and organic fluorine emulsion. The hydroxymethyl aliphatic acid amide hydrophobic agent is preferably a long chain hydroxymethyl aliphatic acid amide. The preferred length of the carbon chain is 14 to 28 carbon atoms. The hydrosilicone oil emulsion may be a hydrosilicone oil emulsion with a cationic silicone or may be an active group-carrying polydimethylsiloxane hydrosilicone oil emulsion or a methyl hydrosilicone oil emulsion. The organic fluorine emulsion is selected from the group consisting of fluorine-containing alkyl acrylate copolymer emulsions, fluororesins, and coordination mixtures of fluorocarbons and hydrocarbons.
소수성 제제로 처리된 면사는 바로 탈수한 후에, 100 내지 180 ℃에서 건조 한다.Cotton yarns treated with a hydrophobic formulation are immediately dehydrated and dried at 100 to 180 ° C.
면사에 별개의 친수성 및 소수성 처리를 거치도록 상기 기술된 방법을 이용한 후, 친수성으로 처리된 실과 소수성으로 처리된 실을 얻을 수 있다.After using the method described above to undergo separate hydrophilic and hydrophobic treatment on the cotton yarn, it is possible to obtain a hydrophilic treated yarn and a hydrophobic treated yarn.
상기 기술된 처리 후 본 발명의 구성에 따르면, 두 가지 유형의 면사는 직물이 되기 위해 일정한 편직 공정을 거치면서 편직될 수 있다. 직물의 한 면(친수성 면)은 대부분 또는 전부 친수성 실로 바람직하게는 100% 친수성 실이다. 다른 면(소수성 면)은 대부분 또는 전부 소수성 실로 친수성 실의 비율이 50%를 초과해서는 안되며 바람직하게는 1%와 40% 사이일 것이다. 직물의 두 개의 면은 본질적으로 상이한 속성을 갖는다. 한 면은 친수성이고 다른 면은 소수성을 보인다. 이리하여 직물은 편안하며 수분 처리 및 신속 건조 기능을 갖는다. 이러한 유형의 두 개의 상이한 속성의 면을 제조할 수 있는 임의 편직 방법이 채택될 수 있다. 구체적으로, 편직 방법은 리브 직물 편직 방법, 이중-니트 양면 편직 방법, 이중 니트 리브 자카드 편직 방법, 단일-니트 플레이티드 저지 편직 방법, 단일-니트 플레이티드 피크 편직 방법, 단일-니트 플레이티드 라코스테 편직 방법, 및 단일-니트 플레이티드 자카드 편직 방법을 포함하나, 이들에 국한되지는 않는다. 단일-니트 구조(가령 단일-니트 플레이티드 구조) 직물은 필요한 만큼 니트일 수 있다. 한 면은 대부분 또는 전부 소수성으로 처리된 순면사이고 다른 면은 대부분 또는 전부 친수성으로 처리된 순면사이다. 이중-니트 구조 직물도 니트일 수 있다. 이의 한 면은 대부분 또는 전부 소수성으로 처리된 실이고 다른 면은 대부분 또는 전부 친수성으로 처리된 실이다. 전체 직물을 친수성 및 소수성 성질 양쪽 모두를 가져 일방향으로의 물 수송을 결과시킬 것이다. 구체적인 편직 기술은 업계에서 통상적으로 사용되는 잘 알려진 기술이므로, 본원에서 더 기술하지 않을 것이다.According to the configuration of the present invention after the treatment described above, two types of cotton yarn can be knitted while undergoing a certain knitting process to become a fabric. One side (hydrophilic side) of the fabric is most or all hydrophilic yarn, preferably 100% hydrophilic yarn. The other side (hydrophobic side) is mostly or all hydrophobic yarns, with the proportion of hydrophilic yarns not exceeding 50% and preferably between 1% and 40%. The two sides of the fabric have essentially different properties. One side is hydrophilic and the other side is hydrophobic. Thus the fabric is comfortable, has moisture treatment and quick drying function. Any knitting method can be adopted that can produce two different attributes of this type of cotton. Specifically, the knitting methods are rib weave knitting method, double-knit double side knitting method, double knit rib jacquard knitting method, single-knit plated jersey knitting method, single-knit plated peak knitting method, single-knit plated lacoste knitting Methods, and single-knit plated jacquard knitting methods, but are not limited to these. Single-knit structures (such as single-knit plated structures) fabrics may be knit as needed. One side is cotton yarn treated with most or all hydrophobicity and the other side is cotton yarn treated with most or all hydrophilicity. Double-knit structured fabrics may also be knits. One side thereof is the yarn treated most or all hydrophobicly and the other side is the yarn treated most or all hydrophilically. The entire fabric will have both hydrophilic and hydrophobic properties, resulting in water transport in one direction. Specific knitting techniques are well known techniques commonly used in the art and will not be further described herein.
본 발명의 산물의 품질을 증진시키기 위하여 적절한 후-처리 절차를 추가로 적용할 수 있을 것이다. 예컨대, 수분-흡수 및 신속-건조 속성에 부가하여 직물이 양호한 모양 보유력, 치수 안정성 및 보풀 내성과 같은 특성을 갖게 하기 위하여 머서법(mercerization), 효소 세탁, 또는 수지 피니슁과 같은 절차를 선택적으로 수행할 수 있다.Appropriate post-treatment procedures may be further applied to enhance the quality of the product of the present invention. For example, in addition to the moisture-absorbing and quick-drying properties, procedures such as mercerization, enzyme washing, or resin finishes can optionally be selected to give the fabric properties such as good shape retention, dimensional stability, and fluff resistance. Can be done.
상기 수지 피니슁은 수지, 촉매 및 침투제 혼합물을 사용하여 직물 또는 의류를 처리하는 것으로 구성될 수 있다. 예컨대, 상기 혼합물에서 수지는 디메톡시에틸렌 요소(DMEU), 디메틸올디히드록시에틸렌 요소(DMDHEU), 디메틸프로필렌 요소(DMPU), 디히드록시메틸트리아존(DMT), 또는 변성 N-메틸디히드록시에틸 요소 또는 변성 디메틸올디히드록시에틸렌 요소 수지와 같은 이의 변성물과 같은 화합물일 수 있다. 대략 20 내지 150 그램의 수지가 1 리터의 혼합물을 만드는데 사용된다. 상기 촉매는 마그네슘염, 질산염, 또는 붕불화 아연일 수 있다. 대략 5 내지 30 그램의 촉매가 1 리터의 혼합물을 만드는데 사용된다. 상기 침투제는 에틸 방향족 지방족 에테르 계면활성제(예컨대 PBN) 또는 지방족 알콜 폴리옥시에틸렌 에테르 비-이온성 계면활성제(예컨대, 66-HK)와 같은 폴리에텐옥시 에테르 화합물일 수 있다. 대략 0.5 내지 4 그램의 침투제가 1 리터의 혼합물을 만드는데 사용된다. 수지 피니슁의 온도는 일반적으로 140 내지 180℃이다. 대략 1 내지 4 분이 이 온도에서 수지 피니슁을 위해 충분하다.The resin finish may consist of treating the fabric or garment using a resin, catalyst and penetrant mixture. For example, the resin in the mixture may be dimethoxyethylene urea (DMEU), dimethyloldihydroxyethylene urea (DMDHEU), dimethylpropylene urea (DMPU), dihydroxymethyltriazone (DMT), or modified N-methyldihydroxy. Compounds such as ethyl urea or modified dimethyloldihydroxyethylene urea resins thereof. Approximately 20 to 150 grams of resin are used to make 1 liter of the mixture. The catalyst may be magnesium salt, nitrate, or zinc borohydride. Approximately 5-30 grams of catalyst is used to make 1 liter of the mixture. The penetrant may be a polyetheneoxy ether compound such as ethyl aromatic aliphatic ether surfactant (such as PBN) or aliphatic alcohol polyoxyethylene ether non-ionic surfactant (such as 66-HK). Approximately 0.5-4 grams of penetrant is used to make 1 liter of the mixture. The temperature of the resin finish is generally 140 to 180 ° C. Approximately 1 to 4 minutes is sufficient for the resin finish at this temperature.
수지 피니슁, 머서법, 또는 효소 세탁과 같은 상기 기술된 공정을 사용함으로써, 세탁된 직물의 직물 표면을 깨끗이 하고 모양 보유력을 유지시켜 직물의 외관과 내구성을 증진시킬 수 있다.By using the processes described above, such as resin finishes, mercer methods, or enzyme laundering, the fabric surface of the washed fabric can be cleaned and shape retained to enhance the appearance and durability of the fabric.
수분 처리 직물을 만들기 위해서 현재 사용되는 모든 기술들은 직물 피니슁 공정에 기초하고 있다. 이 공정은 직물의 두 개의 면 사이에 상이한 속성을 획득할 수 없고 이리하여 일방향으로의 물 수송 기능을 만들 수 없다. 게다가, 현재 기술에서 신속 건조 직물은 합성 섬유 및 면/합성 섬유 혼방 산물 중에서 주로 발견된다. 순면 산물에서 여전히 어떠한 보고도 이루어진 바 없다. 본 발명의 직물은 두 개의 면 사이의 차이점에 의하여 순면직물을 통해 물 또는 땀의 일방향 수송을 실제로 획득하고 건조 안락감 및 신속-건조 효과를 만들어낸다. 특히, 본 발명은 특수 실 처리 공정을 사용하고 동일 직물에 두 개의 상이한 속성, 즉, 친수 성질과 소수 성질을 지니도록 적절한 편직 공정을 사용한다(한 면은 전적으로 친수성 및 흡수성이다. 이는 물을 흡수하기에 좋다. 다른 면은 소수성으로 물에 반발하여 직물을 건조하고 안락하게 유지시킨다). 두 개의 면의 차이점에 의해 직물은 일방향으로의 물 수송을 보장할 수 있으며 편직물질(직물)이 후속 공정(특히, 세탁, 머서법, 및 수지 피니슁 공정) 동안 또는 가정 세탁 공정 동안에 공동 효과에 놓이지 않도록 그리고 내내 일정한 내구성을 유지하도록 보증할 수 있다.All the technologies currently used to make moisture treated fabrics are based on the fabric finishing process. This process cannot obtain different properties between the two sides of the fabric and thus cannot make water transport function in one direction. In addition, in the present technology quick-drying fabrics are found primarily among synthetic and cotton / synthetic fiber blend products. No reports have yet been made on cotton products. The fabric of the present invention actually obtains one-way transport of water or sweat through the cotton fabric by the difference between the two sides and produces a drying comfort and quick-drying effect. In particular, the present invention employs a special yarn treatment process and employs a suitable knitting process to have two different properties, ie hydrophilic and hydrophobic, on the same fabric (one side is entirely hydrophilic and absorbent. It absorbs water. The other side is hydrophobic and repels water to keep the fabric dry and comfortable). The difference between the two sides allows the fabric to ensure water transport in one direction, and the knitted material (fabric) is subject to the joint effect during subsequent processes (especially washing, mercer, and resin finishing) or during the home washing process. It can be guaranteed not to lie down and to maintain constant durability throughout.
이상을 정리하면, 본 발명은 현재의 기술에 대하여 다음과 같은 이점을 갖는다.In summary, the present invention has the following advantages over the current technology.
1. 순면사에 별개의 친수성 및 소수성 처리를 수행하도록 상이한 처리 방법을 사용하여 상이한 속성을 두 가지 종류의 실을 얻는다. 두 가지 종류의 실은 일정한 편직 공정에 따른 니트이다. 결과 만들어진 직물의 한 면은 대부분 또는 전부 소수성 순면사로부터 형성되며 수분과 공기에 대해 양호한 투과성을 갖는다. 다른 면은 대부분 또는 전부 친수성 순면사로부터 형성되며 탁월한 물 흡수 및 퍼짐 능력을 갖는다. 친수성 면과 소수성 면 사이의 이러한 차이는 물 수송을 위한 유인력을 제공한다. 물 및 땀은 아주 신속하게 소수성 면으로부터 친수성 면으로 수송될 수 있다. 이리하여 소수성 면은 건조하게 안락하게 남아 있게 되어 수분 처리 및 신소 건조 기능이 이리하여 성취된다.1. Two kinds of yarns with different properties are obtained using different treatment methods to perform separate hydrophilic and hydrophobic treatments on the cotton yarn. Two types of yarn are knits following a certain knitting process. One side of the resulting fabric is formed from mostly or entirely hydrophobic cotton yarns and has good permeability to moisture and air. The other side is formed from most or all hydrophilic cotton yarns and has excellent water absorption and spreading ability. This difference between the hydrophilic and hydrophobic sides provides the attraction for water transport. Water and sweat can be transported from hydrophobic cotton to hydrophilic cotton very quickly. Thus the hydrophobic side remains dry and comfortable so that the moisture treatment and dye drying functions are thus achieved.
2. 직물은 100% 순면 물질을 사용하여 피니슁되었을 때 손으로 만지기에 아주 좋으며 입었을 때 최상의 안락감을 제공한다.2. The fabric is made of 100% cotton material, which is very good to touch by hand when finished and provides the best comfort when worn.
3. 선택된 친수성 유연제 및 소수성 제제는 양호한 내구성을 갖는다. 이는 일방향으로의 수송 기능의 내구성을 보장한다. 본 발명의 직물은 AATCC 143 세탁 방법에 따라 10번 이상의 가정 세탁 후 최상의 일방향 물 수송과 신속 건조 기능을 보유한다.3. The selected hydrophilic softeners and hydrophobic formulations have good durability. This ensures the durability of the transport function in one direction. The fabric of the present invention has the best one-way water transport and quick drying after 10 or more home washes according to the AATCC 143 washing method.
4. 본 발명의 직물은 탁월한 내구성을 갖는다. AATCC 143 방법에 따라 세탁했을 때, 이는 10 번 이상의 가정 세탁에 놓일 수 있고(현재 산물에 대한 전형적인 세탁성 지표는 5번의 세탁에 견딜 것을 요구한다) 여전히 좋은 착용감을 유지한다. 더욱이, 색깔 쇠퇴가 세탁 후 최소한이다. 현재 기술과 비교시, 본 발명의 10번의 세탁 후 직물 채색(쇠퇴)에서의 변화는 3.5 또는 그 이상 수준에서 유지될 수 있다(AATCC 143 방법에 따라 시험시).4. The fabric of the present invention has excellent durability. When washed according to the AATCC 143 method, it can be placed in more than 10 home washes (a typical washability indicator for current products requires to withstand 5 washes) and still maintains a good fit. Moreover, the color decline is minimal after washing. Compared with the current technology, the change in fabric coloration (decay) after 10 washes of the present invention can be maintained at a level of 3.5 or higher (tested according to the AATCC 143 method).
하기에는 본 발명의 구성과 결과에 대한 상세한 논의가 특정 구체예에 비추어 제공되는데, 이는 본 발명의 이용 범위를 어떠한 방식으로든 제한하는 것이 아니다.The following provides a detailed discussion of the construction and results of the present invention in light of certain embodiments, which do not in any way limit the scope of use of the present invention.
실시예 1: 60s/2 이중-니트 양면 직물 Example 1: 60s / 2 double-knit double sided fabric
본 실시예의 60s/2 이중-니트 양면 직물의 제조 방법:Process for producing 60s / 2 double-knit double sided fabric of this example:
1. 순면사 처리:1. Cotton yarn treatment:
a. 친수성 처리 공정 및 면사 염색:a. Hydrophilic Treatment Process and Cotton Yarn Dyeing:
정련하기 → 염색하기 → 비누칠하기, 고정하기 → 배쓰에서 유연하게 하기 (친수성 유연제) → 건조하기Refining → dyeing → soaping, fixing → softening in bath (hydrophilic softener) → drying
1) 정련하기, 염색하기, 비누칠하기 및 고정하기는 보통의 작업 공정에 따라 수행된다. 1) Refining, dyeing, soaping and fixing are carried out according to the usual working process.
2) 폴리에테르-변성 에폭시에탄 유기 실리콘 유연제 "Magnasoft HWS"(GE사로부터)가 친수성 유연제로 사용된다. 4 그램이 리터당 사용된다. 처리는 30 ℃에서 30분간 지속한다. 액체 비율은 약 1:10이다. 2) The polyether-modified epoxy ethane organosilicone softener "Magnasoft HWS" (from GE) is used as the hydrophilic softener. 4 grams are used per liter. The treatment lasts for 30 minutes at 30 ° C. The liquid ratio is about 1:10.
3) 처리된 면사를 120 ℃에서 건조한다.3) The treated cotton yarn is dried at 120 ° C.
b. 소수성 처리 공정 및 면사 염색:b. Hydrophobic Treatment Process and Cotton Yarn Dyeing:
정련하기 → 염색하기 → 비누칠하기, 고정하기 → 소수성 제제로 처리하기 → 건조하기Refining → Dyeing → soaping, fixing → treatment with hydrophobic agents → drying
1) 정련하기, 염색하기, 비누칠하기 및 고정하기는 보통의 공정에 따라 행해진다.1) Refining, dyeing, soaping and fixing are done according to the usual process.
2) 소수성 처리는 히드록시메틸 스테아르아미드-유형(stearamide-type) 소수성 제제 Polysofter CAM-100(대만의 SeKi Chemical Co.에서 제조)를 가지고 대략 처리 배쓰 1 리터 당 Polysofter CAM-100 80 그램으로 90 ℃에서 8 분간 행한다. 2) Hydrophobic treatment was carried out at 90 ° C. with 80 grams of Polysofter CAM-100 per liter of treatment bath with hydroxymethyl stearamide-type hydrophobic formulation Polysofter CAM-100 (manufactured by SeKi Chemical Co., Taiwan). 8 minutes at.
3) 소수성 제제로 처리된 면사를 바로 탈수하고 150 ℃에서 건조한다. 3) The cotton yarn treated with the hydrophobic agent is immediately dehydrated and dried at 150 ° C.
2. 편직 공정2. Knitting Process
상기 기술된 바대로 처리된 면사를 이중층 구조 순면직물로 편직하기 위해 이중-니트 양면 편직 방법을 사용하는데, 여기에서 한 층은 소수성으로 처리된 실로부터의 소수성 층(대략 20%의 친수성 실이 추가될 수도 있다) 니트이고 다른 층은 친수성으로 처리된 실로부터의 친수성 층 니트이다.A double-knit double-sided knitting method is used to knit the treated yarn into a double layer construction cotton fabric as described above, in which one layer is added a hydrophobic layer (approximately 20% of the hydrophilic yarn from the hydrophobic treated yarn) And the other layer is a hydrophilic layer knit from a yarn treated with hydrophilicity.
3. 수지 피니슁3. Resin Finish
수지 피니슁은 수지, 촉매 및 침투제 혼합물로 수행된다.Resin finishes are performed with a mixture of resin, catalyst and penetrant.
사용되는 수지는 디메틸올디히드록시에틸렌 요소 (DMDHEU) Fixapret CP(BASF Corp.에 의해 제조)이고 120 그램을 리터당 사용한다. 촉매는 MgCl2 (24 g/L)이고, 침투제는 PBN (4 g/L)이다.The resin used is dimethyloldihydroxyethylene urea (DMDHEU) Fixapret CP (manufactured by BASF Corp.) and uses 120 grams per liter. The catalyst is MgCl 2 (24 g / L) and the penetrant is PBN (4 g / L).
수지 피니슁은 140 ℃에서 수행된다.Resin finish is performed at 140 ° C.
상기 기술된 단계들을 수행한 결과 본 실시예의 60s/2 이중층 양면 구조 직물을 얻었다. 이의 성능을 M&S P136B 방법에 따라 시험하였고, 그 결과는 표 1에 기록되어 있다.The steps described above resulted in the 60s / 2 double layer double-sided fabric of this example. Its performance was tested according to the M & S P136B method and the results are reported in Table 1.
상기 표의 데이터는 본 발명의 두 개의 상이한 속성의 면을 지닌 신속 건조 순면직물의 물증발율이 통상적인 순면직물보다 훨씬 높음을 보여준다. 즉, 몸체가 땀이 날 때, 증발이 이루어지는 직물의 외부면으로 땀이 신속하게 흡수되어 수송될 수 있다.The data in the table show that the water evaporation rate of the quick-drying pure cotton fabrics with two different properties of the present invention is much higher than that of conventional pure cotton fabrics. That is, when the body sweats, the sweat can be quickly absorbed and transported to the outer surface of the fabric where evaporation takes place.
실시예 2: 60s/2 이중-니트 리브 자카드 직물Example 2: 60s / 2 double-knit rib jacquard fabric
본 발명의 60s/2 이중-니트 리브 자카드 직물의 제조방법은 다음과 같다:The process for producing the 60s / 2 double-knit rib jacquard fabric of the present invention is as follows:
1. 면사 처리:1. Cotton yarn treatment:
a. 친수성 처리 공정 및 머서화된 순면사 염색:a. Hydrophilic Treatment Process and Mercerized Cotton Yarn Dyeing:
정련하기 → 염색하기 → 비누칠하기, 고정하기 → 배쓰에서 유연하게 하기 (친수성 유연제) → 건조하기Refining → dyeing → soaping, fixing → softening in bath (hydrophilic softener) → drying
1) 정련하기, 염색하기, 비누칠하기 및 고정하기는 보통 작업 공정에 따라 수행된다. 1) Refining, dyeing, soaping and fixing are usually carried out according to the working process.
2) 8 그램의 고등급 지방족 아민 유도체 및 유기 실리콘 화합물 유연제 Ultraphil HMS(CIBA Corp.에 의해 제조)가 리터당 사용된다. 처리는 40 ℃에서 10 분간 지속한다. 2) 8 grams of high grade aliphatic amine derivatives and organosilicon compound softener Ultraphil HMS (manufactured by CIBA Corp.) are used per liter. The treatment lasts 10 minutes at 40 ° C.
3) 처리된 면사는 100 ℃에서 건조한다.3) The treated cotton yarn is dried at 100 ° C.
b. 소수성 처리 공정 및 머서화된 면사 염색:b. Hydrophobic Treatment Process and Mercerized Cotton Yarn Dyeing:
정련하기 → 염색하기 → 비누칠하기, 고정하기 → 소수성 제제로 처리하기 → 건조하기Refining → Dyeing → soaping, fixing → treatment with hydrophobic agents → drying
1) 정련하기, 염색하기, 비누칠하기 및 고정하기는 보통의 공정에 따라 행해진다.1) Refining, dyeing, soaping and fixing are done according to the usual process.
2) 소수성 처리는 소수성 제제로 탄화불소 화합물 Olephobol CO(CIBA Corp.)를 가지고 70 ℃에서 20분간 행한다. 대략 20 그램의 소수성 제제를 처리 배쓰 1 리터당 사용한다. 2) The hydrophobic treatment is carried out for 20 minutes at 70 ° C. with the fluorocarbon compound Olephobol CO (CIBA Corp.) as a hydrophobic agent. Approximately 20 grams of hydrophobic agent is used per liter of treatment bath.
3) 소수성 제제로 처리된 면사를 바로 탈수하고 120 ℃에서 건조한다. 3) The cotton yarn treated with the hydrophobic agent is immediately dehydrated and dried at 120 ° C.
2. 편직 공정2. Knitting Process
상기 기술된 바대로 처리된 머서화된 면사를 양면 구조 순면직물로 편직하기 위해 이중-니트 리브 자카드 편직 방법을 사용하는데, 여기에서 한 면은 소수성으로 처리된 실로부터의 소수성 면 니트이고 다른 면은 친수성으로 처리된 실로부터의 친수성 면 니트이다.A double-knit rib jacquard knitting method is used to knit a mercerized cotton yarn treated as described above into a double-sided structure cotton fabric, where one side is hydrophobic cotton knit from a hydrophobic treated yarn and the other side is Hydrophilic cotton knit from yarn treated with hydrophilicity.
3. 수지 피니슁3. Resin Finish
수지 피니슁은 수지, 촉매 및 침투제 혼합물로 수행된다.Resin finishes are performed with a mixture of resin, catalyst and penetrant.
사용된 수지는 변성 2D 수지 FR-CL이고 80 그램이 리터당 사용된다. 촉매는 MgCl2 (16 g/L)이고, 침투제는 66-HK (2 g/L)이다.The resin used is a modified 2D resin FR-CL and 80 grams are used per liter. The catalyst is MgCl 2 (16 g / L) and the penetrant is 66-HK (2 g / L).
수지 피니슁은 180 ℃에서 수행된다.Resin finish is performed at 180 ° C.
상기 기술된 단계들을 수행한 결과 본 실시예의 60s/2 리브 자카드 직물이 얻어졌다. 이의 성능은 M&S P136B 방법에 따라 시험되었고, 그 결과는 표 2에 기록되어 있다.The steps described above resulted in the 60s / 2 rib jacquard fabric of this example. Its performance was tested according to the M & S P136B method and the results are reported in Table 2.
상기 표의 데이터는 본 발명의 두 개의 상이한 속성의 면을 지닌 신속 건조 순면직물의 물증발율이 통상적인 순면직물보다 훨씬 높음을 보여준다. 즉, 몸체가 땀이 날 때, 증발이 이루어지는 직물의 외부면으로 땀이 신속하게 흡수되어 수송될 수 있다.The data in the table show that the water evaporation rate of the quick-drying pure cotton fabrics with two different properties of the present invention is much higher than that of conventional pure cotton fabrics. That is, when the body sweats, the sweat can be quickly absorbed and transported to the outer surface of the fabric where evaporation takes place.
실시예 3: 60s/2 단일-니트 플레이티드 저지/피크 직물Example 3: 60s / 2 single-knit plated jersey / peak fabric
본 실시예의 60s/2 단일-니트 플레이티드 저지/피크 직물의 제조방법은 다음과 같다:The method of making the 60s / 2 single-knit plated jersey / peak fabric of this example is as follows:
1. 면사 처리:1. Cotton yarn treatment:
a. 친수성 처리 공정 및 면사 염색:a. Hydrophilic Treatment Process and Cotton Yarn Dyeing:
정련하기 → 염색하기 → 비누칠하기, 고정하기 → 배쓰에서 유연하게 하기 (친수성 유연제) → 건조하기Refining → dyeing → soaping, fixing → softening in bath (hydrophilic softener) → drying
1) 정련하기, 염색하기, 비누칠하기 및 고정하기는 보통 작업 공정에 따라 수행된다. 1) Refining, dyeing, soaping and fixing are usually carried out according to the working process.
2) 2 그램의 유연제 JH-PPE200A15 (Jen Hsiang Chemical Industrial Co., Ltd.로부터의 유기 실리콘 유연제)가 리터당 사용된다. 처리는 50 ℃에서 40 분간 지속한다. 2) 2 grams of softener JH-PPE200A15 (organic silicone softener from Jen Hsiang Chemical Industrial Co., Ltd.) is used per liter. The treatment lasts 40 minutes at 50 ° C.
3) 처리된 면사를 140 ℃에서 건조한다.3) The treated cotton yarn is dried at 140 ° C.
b. 소수성 처리 공정 및 면사 염색:b. Hydrophobic Treatment Process and Cotton Yarn Dyeing:
정련하기 → 염색하기 → 비누칠하기, 고정하기 → 소수성 제제로 처리하기 → 건조하기Refining → Dyeing → soaping, fixing → treatment with hydrophobic agents → drying
1) 정련하기, 염색하기, 비누칠하기 및 고정하기는 보통의 공정에 따라 행해진다.1) Refining, dyeing, soaping and fixing are done according to the usual process.
2) 소수성 처리는 나노플루오로중합체로 처리 배쓰 1 리터당 대략 5 그램의 소수성 제제 농도로 50 ℃에서 40분간 행해진다. 2) The hydrophobic treatment is carried out at 50 ° C. for 40 minutes at a concentration of approximately 5 grams of hydrophobic agent per liter of the treatment bath with the nanofluoropolymer.
3) 소수성 제제로 처리된 면사를 바로 탈수하고 160 ℃에서 건조한다. 3) The cotton yarn treated with the hydrophobic agent is immediately dehydrated and dried at 160 ° C.
2. 편직 공정2. Knitting Process
단일-니트 플레이티드 저지-피크 편직 방법을 사용한다. 한 면은 소수성으로 처리된 실 70% 및 친수성으로 처리된 실 30%이고, 다른 면은 친수성으로 처리된 실 100% 이다. 두 개의 면이 상이한 속성을 갖는 단일-니트 순면직물로 편직한다.The single-knit plated jersey-peak knitting method is used. One side is 70% hydrophobized yarn and 30% hydrophilic yarn, and the other side is 100% hydrophilic yarn. The two sides are knitted into a single-knit cotton fabric with different properties.
3. 수지 피니슁3. Resin Finish
수지 피니슁은 수지, 촉매 및 침투제 혼합물로 수행된다.Resin finishes are performed with a mixture of resin, catalyst and penetrant.
사용된 수지는 디메틸올디히드록시에틸렌 요소(DMDHEU) CP로서, 약 30 그램이 리터당 사용된다. 촉매는 MgCl2 (6 g/L)이고, 침투제는 지방족 알콜 폴리옥시에틸렌 에테르 비-이온성 계면활성제 66-HK (2 g/L)이다.The resin used is dimethyloldihydroxyethylene urea (DMDHEU) CP, about 30 grams used per liter. The catalyst is MgCl 2 (6 g / L) and the penetrant is an aliphatic alcohol polyoxyethylene ether non-ionic surfactant 66-HK (2 g / L).
수지 피니슁은 약 160 ℃에서 수행된다.Resin finish is performed at about 160 ° C.
상기 기술된 단계들을 수행한 결과 본 실시예의 60s/2 및 40s/1 단일-니트 플레이티드 저지 또는 단일-니트 플레이티드 피크 직물이 얻어졌다. 이의 성능은 M&S P136B 방법에 따라 시험되었고, 그 결과는 표 3에 기록되어 있다.The steps described above resulted in the 60s / 2 and 40s / 1 single-knit plated jersey or single-knit plated peak fabrics of this example. Its performance was tested according to the M & S P136B method and the results are reported in Table 3.
상기 표의 데이터는 본 발명의 두 개의 상이한 속성의 면을 지닌 신속 건조 순면직물의 물증발율이 통상적인 순면직물보다 훨씬 높음을 보여준다. 즉, 몸체가 땀이 날 때, 증발이 이루어지는 직물의 외부면으로 땀이 신속하게 흡수되어 수송될 수 있다.The data in the table show that the water evaporation rate of the quick-drying pure cotton fabrics with two different properties of the present invention is much higher than that of conventional pure cotton fabrics. That is, when the body sweats, the sweat can be quickly absorbed and transported to the outer surface of the fabric where evaporation takes place.
본 발명의 특정 실시예에 따르면, 두 개의 면이 상이한 속성을 갖는 내구적인 신속 건조 순면직물을 제조하는 실행가능한 방법은 선택적으로 다음과 같은 단계들을 포함할 수 있다: (1) 실 머서법, (2) 실 정련하기, (3) 효소 세탁법, (4) 특정 실 염색하기, (5) 특정 편직, (6) 직물 머서법, (7) 수지 피니슁, (8) 의류 만들기 및 (9) 의류 세탁 등. 머서법, 효소 세탁법 및 수지 피니슁과 같은 공정들의 적용은 세탁 후에 직물의 외관을 유지시킬 수 있게 하여 외관과 내구성을 증진시킬 수 있다.According to a particular embodiment of the present invention, a viable method of producing a durable quick-drying cotton fabric having two attributes with different properties may optionally include the following steps: (1) the yarn mercer method, ( 2) refining yarn, (3) enzymatic washing, (4) dyeing certain threads, (5) specific knitting, (6) textile mercer, (7) resin finishes, (8) clothing making, and (9) clothing Laundry etc. Application of processes such as mercer, enzyme laundering and resin finishes can enhance the appearance and durability by making it possible to maintain the appearance of the fabric after washing.
도 1은 본 발명의 두 개의 상이한 속성의 면을 지닌 신속 건조 순면직물의 물 수송 효과를 보여주는 개략도이다.1 is a schematic diagram showing the water transport effect of a quick-drying pure cotton fabric with two different properties of the present invention.
Claims (21)