KR100853277B1 - Coated article having crater pattern and its coating method - Google Patents

Coated article having crater pattern and its coating method Download PDF

Info

Publication number
KR100853277B1
KR100853277B1 KR1020080014932A KR20080014932A KR100853277B1 KR 100853277 B1 KR100853277 B1 KR 100853277B1 KR 1020080014932 A KR1020080014932 A KR 1020080014932A KR 20080014932 A KR20080014932 A KR 20080014932A KR 100853277 B1 KR100853277 B1 KR 100853277B1
Authority
KR
South Korea
Prior art keywords
crater
paint
coating
liquid
forming
Prior art date
Application number
KR1020080014932A
Other languages
Korean (ko)
Inventor
유영권
Original Assignee
유영권
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 유영권 filed Critical 유영권
Priority to KR1020080014932A priority Critical patent/KR100853277B1/en
Application granted granted Critical
Publication of KR100853277B1 publication Critical patent/KR100853277B1/en

Abstract

A coated article having crater patterns and a coating method for the same are provided to form the same patterns as those of craters of a planet or stars of the sky by irregularly forming grooves on the surface of paints applied on an object. A coated article having crater patterns is composed of: an object(100) to be coated; a second paint layer(120) applied to the surface of the object and provided with irregular grooves(121) formed on the outer surface; and a transparent paint layer(130) formed on the outer surface of the second paint layer. A first paint layer(110) is formed between the surface of the object and the second paint layer. A coating method for forming crater patterns comprises the steps of: applying first paint fluid on the object and drying the applied first paint fluid; applying second paint fluid on the dried first paint fluid; forming the grooves on the surface of the second paint fluid by spraying crater forming fluid before the second paint fluid is dried; drying the second paint fluid; and applying and drying transparent paint fluid on the dried second paint fluid.

Description

크레이터 패턴을 형성한 도장품 및 도장방법{Coated article having crater pattern and its coating method}Coated article having crater pattern and its coating method}

본 발명은 도료가 사물에 도장된 도장품 및 도장방법에 관한 것으로서, 특히 도장 외측면에 크레이터의 패턴을 형성할 수 있게 구성한 것이다.The present invention relates to a coating product and a coating method in which paint is applied to an object, and is particularly configured to be able to form a crater pattern on an outer surface of a coating.

일반적으로 사물이 부식하는 것을 막거나 또는 외관이 수려하도록 하기 위해 사물의 외측면에 도료를 칠하는 도장작업을 수행한다.In general, painting is performed on the outer surface of the object to prevent the object from corroding or to make the appearance beautiful.

종래의 도장작업은 단지 도료를 사물의 외측면에 균일하게 바르고, 건조시키는 방식으로 진행되었으나, 최근에는 도장자체에도 다양한 문양을 넣거나 또는 패턴을 구현함으로써, 종래의 일률적인 도장방식을 점차 벗어나고 있다.Conventional painting work was carried out in a manner that only the paint is uniformly applied to the outer surface of the object, and dried, but recently, by putting various patterns or patterns to the paint itself, it is gradually deviating from the conventional uniform coating method.

본 발명은 앞에서 설명한 바와 같은 종래의 일률적인 도장방식을 벗어나, 소비자의 다양한 기호를 충족시킬 수 있는 새로운 도장방식을 연구하던 중 발명된 것으로서, 도장 외측면에 크레이터와 같은 홈이 불균일하게 형성됨으로써, 행성의 표면 또는 밤하늘의 별과 같은 패턴을 연출할 수 있게 구성한 크레이터 패턴을 형성 한 도장품 및 도장방법을 제공하는 데 그 목적이 있다.The present invention was invented while researching a new coating method that can satisfy various preferences of consumers, beyond the conventional uniform coating method as described above, and the grooves such as craters are formed unevenly on the outer surface of the coating, An object of the present invention is to provide a coating product and a method of painting in which a crater pattern is formed to produce a pattern such as a surface of a planet or a star in a night sky.

상기와 같은 목적을 달성하기 위한 본 발명의 크레이터 패턴을 형성한 도장품은 도장하고자 하는 사물체와, 상기 사물체의 표면에 도포되며 외측 표면에 불균일한 홈들이 형성된 2차 도료층 및, 상기 2차 도료층의 외측 표면에 형성된 투명 도료층을 포함하는 것을 기술적 특징으로 한다.The coated article formed with the crater pattern of the present invention for achieving the above object is a secondary paint layer and a secondary paint layer formed on the surface of the object and the non-uniform grooves are formed on the outer surface, and the secondary It is a technical feature to include a transparent paint layer formed on the outer surface of a paint layer.

또한, 본 발명의 바람직한 실시예에 따르면, 상기 사물체의 표면과 2차 도료층의 사이에 1차 도료층이 형성된다.In addition, according to a preferred embodiment of the present invention, a primary paint layer is formed between the surface of the object and the secondary paint layer.

또한, 본 발명에 따른 크레이터 패턴을 형성한 도장방법은 사물체에 1차 도료액을 도포하고 건조하는 단계와, 건조된 1차 도료액에 2차 도료액을 도포하는 단계와, 상기 2차 도료액이 건조되기 이전에 크레이터 형성액을 뿌려 2차 도료액의 표면에 홈을 형성하는 단계와, 2차 도료액을 건조하는 단계와, 상기 건조된 2차 도료액에 투명 도료액을 도포하고 건조하는 단계를 포함하는 것을 기술적 특징으로 한다.In addition, the coating method of forming a crater pattern according to the present invention comprises the steps of applying and drying the primary coating liquid to the object, the step of applying a secondary coating liquid to the dried primary coating liquid, and the secondary coating Before the liquid is dried, spraying the crater forming liquid to form grooves on the surface of the secondary coating liquid, drying the secondary coating liquid, and applying the transparent coating liquid to the dried secondary coating liquid and drying it. Technical features, including the step of doing.

또한, 본 발명의 바람직한 실시예에 따르면, 상기 1차 도료액은 폴리우레탄과 시너의 혼합용액이다.In addition, according to a preferred embodiment of the present invention, the primary coating liquid is a mixed solution of polyurethane and thinner.

또한, 본 발명의 바람직한 실시예에 따르면, 상기 1차 도료액이 건조하여 형성된 1차 도료층의 표면을 평탄화하는 단계를 더 포함한다.In addition, according to a preferred embodiment of the present invention, further comprising the step of planarizing the surface of the primary coating layer formed by drying the primary coating liquid.

또한, 본 발명의 바람직한 실시예에 따르면, 상기 2차 도료액은 투명 폴리우레탄, 불투명 유색도료, 금분, 은분이 혼합된다.In addition, according to a preferred embodiment of the present invention, the secondary coating liquid is a mixture of transparent polyurethane, opaque colored paint, gold powder, silver powder.

또한, 본 발명의 바람직한 실시예에 따르면, 상기 크레이터 형성액은 폴리우레탄과 시너의 혼합용액이다.In addition, according to a preferred embodiment of the present invention, the crater forming solution is a mixed solution of polyurethane and thinner.

또한, 본 발명의 바람직한 실시예에 따르면, 상기 2차 도료액의 표면에 홈을 형성하는 단계에서는, 크레이터 형성액을 손에 묻힌 후 튕겨 뿌림으로써, 불균일한 홈들을 형성한다.In addition, according to a preferred embodiment of the present invention, in the step of forming a groove on the surface of the secondary paint liquid, by spraying the crater forming liquid to the hand and then sprinkled to form non-uniform grooves.

앞서 설명한 바와 같이, 본 발명의 크레이터 패턴을 형성한 도장품 및 도장방법은 사물체에 도장된 도료의 표면에 홈을 불균일하게 형성함으로써, 행성의 크레이터 또는 밤하늘의 별과 같은 패턴을 형성하여 외관이 수려하다는 장점이 있다.As described above, the coated article and the coating method forming the crater pattern of the present invention by unevenly forming grooves on the surface of the paint coated on the object, thereby forming a pattern like a planet crater or a star in the night sky, It has the advantage of being beautiful.

또한, 본 발명의 크레이터 패턴을 형성한 도장품 및 도장방법은 크레이터 형성액을 뿌려 도료의 표면에 홈을 형성함으로써, 제조방법이 수월하고 신속하여 생산성이 우수하다는 장점이 있다.Further, the coated article and the coating method in which the crater pattern of the present invention is formed have an advantage that the production method is easy and quick and the productivity is excellent by spraying the crater forming liquid to form grooves on the surface of the paint.

아래에서는 본 발명에 따른 크레이터 패턴을 형성한 도장품 및 도장방법의 양호한 실시예를 첨부한 도면을 참조로 하여 상세히 설명한다.Hereinafter, with reference to the accompanying drawings, a preferred embodiment of a coating product and a coating method having a crater pattern according to the present invention will be described in detail.

도면에서, 도 1은 본 발명에 따른 크레이터 패턴을 형성한 도장품을 나타낸 단면도이고, 도 2는 본 발명에 따른 크레이터 패턴을 형성한 도장방법을 나타낸 블록도이며, 도 3은 본 발명에 따른 크레이터 패턴을 형성한 도장품의 일 예를 나타낸 사진들이다.In the drawings, Figure 1 is a cross-sectional view showing a coating product formed with a crater pattern according to the present invention, Figure 2 is a block diagram showing a coating method for forming a crater pattern according to the present invention, Figure 3 is a crater according to the present invention Photographs showing an example of a painted article forming a pattern.

도 1에 도시된 바와 같이, 크레이터 패턴을 형성한 도장품은 도장하고자 하 는 사물체(100)의 외표면에 1차 도료층(110)이 형성되고, 1차 도료층(110)의 외측면에 2차 도료층(120)이 형성되며, 2차 도료층(120)의 외측면에 투명 도료층(130)이 형성된다. 여기에서 2차 도료층(120)은 그 표면에 불균일한 홈(121)이 행성의 크레이터와 같은 패턴으로 전체에 형성된다.As shown in FIG. 1, in the painted article having the crater pattern, the primary paint layer 110 is formed on the outer surface of the object 100 to be coated, and on the outer surface of the primary paint layer 110. The secondary paint layer 120 is formed, and the transparent paint layer 130 is formed on the outer surface of the secondary paint layer 120. Here, the secondary paint layer 120 is formed on the entire surface of the non-uniform grooves 121 in the same pattern as the craters of the planet.

아래에서는 이와 같이 구성된 도장품의 도장방법에 대해 설명한다.Hereinafter, the coating method of the coating product comprised in this way is demonstrated.

도 2에 도시된 바와 같이, 크레이터 패턴을 형성한 도장방법의 첫 번째 단계는, 폴리우레탄과 시너(thinner)를 혼합하여 도장하고자 하는 사물에 칠을 한다. 이때 폴리우레탄과 시너를 혼합한 1차 도료액을 스프레이 장치로 균일하게 도포한다(S10).As shown in FIG. 2, the first step of the coating method in which the crater pattern is formed is a mixture of polyurethane and thinner to paint an object to be painted. At this time, the primary coating liquid mixed with the polyurethane and thinner is uniformly applied with a spray device (S10).

그리고 1차 도료액을 약 4시간정도 건조시켜 1차 도료층을 형성한다(S12).Then, the primary coating liquid is dried for about 4 hours to form a primary coating layer (S12).

1차 도료액을 사물에 도포하여 1차 도료층(110)을 형성한 이유는 사물의 외표면을 균일하게 하고, 차후에 도포되는 2차 도료액이 균일하게 도포될 수 있도록 하기 위해서이다.The reason why the primary paint layer 110 is formed by applying the primary paint liquid to the object is to make the outer surface of the object uniform and to apply the secondary paint liquid applied later.

1차 도료액이 건조되어 1차 도료층(110)을 형성한 후에 평탄작업을 수행한다(S14). After the primary coating liquid is dried to form the primary coating layer 110, the flat coating is performed (S14).

평탄작업이 완료된 후에는 2차 도료액을 도포한다.After the flattening is completed, apply the secondary paint solution.

2차 도료액은 투명 폴리우레탄, 불투명 유색도료, 금분, 은분을 혼합한 것으로서, 중량비로 35±5%의 투명 폴리우레탄, 35±5%의 불투명 유색도료, 25±5%의 금분, 5±5%의 은분을 혼합한 혼합물과 여기에 시너 및 경화제를 첨가 희석하여 2차 도료액을 만든다.The secondary paint solution is a mixture of transparent polyurethane, opaque colored paint, gold powder and silver powder. 35 ± 5% transparent polyurethane by weight, 35 ± 5% opaque colored paint, 25 ± 5% gold powder, 5 ±. A secondary coating solution is prepared by diluting a mixture of 5% silver powder and thinner and hardener added thereto.

이와 같이 투명 폴리우레탄, 불투명 유색도료, 금분, 은분 및 시너 그리고 경화제가 혼합된 2차 도료액을 보관하는데, 보관하기 이전에 금분과 은분이 불투명 유색도료에 의해 엉기지 않도록 거름망에 거른 후에 보관한다. 거름망으로 2차 도료액을 거름으로써, 엉겨서 부피가 커진 금분과 은분은 거름망을 통과하지 못하고, 엉기지 않은 상태의 금분과 은분만이 거름망을 통과하게 되면서, 금분과 은분의 엉김이 최소화된다. 그리고 부피가 커 거름망에 걸러진 금분과 은분은 다시 으깨어 거름망을 통과시킨다.As such, the secondary paint solution containing transparent polyurethane, opaque colored paint, gold powder, silver powder and thinner, and curing agent is stored, and before storage, the gold powder and silver powder are filtered through a sieve to prevent them from being entangled by the opaque colored paint. . By filtering the secondary coating liquid with a sieve, the bulky gold powder and silver powder cannot pass through the sieve, and only the untangled gold and silver flour pass through the sieve, minimizing the tangle of the gold powder and the silver powder. Gold and silver powder filtered through a large sieve is crushed again and passed through the sieve.

이와 같이 거름망을 통과한 2차 도료액을 적정한 온도와 직사광선이 들지 않는 장소에 보관하고 있다가 차후에 2차 도료액을 사용하고자 할 경우에 시너를 약간 첨가하여 희석시킨 후에 도장작업을 수행한다. 여기에서 2차 도료액의 도장작업 이전에 시너를 약간 첨가하는 이유는 차후에 구체적으로 설명될 크레이터 형성액을 뿌렸을 때에 크레이터의 패턴 형성이 보다 원활하게 이루어질 수 있도록 하기 위해서이다.In this way, the secondary paint liquid that has passed through the strainer is stored in a place where the proper temperature and direct sunlight does not come in. Then, when the secondary paint liquid is to be used later, paint is added after a thinner is diluted. Here, the reason why the thinner is slightly added before the painting operation of the secondary coating liquid is to make the crater pattern formation more smoothly when spraying the crater formation liquid which will be explained in detail later.

이와 같이 구성된 2차 도료액을 1차 도료액이 건조된 사물에 도포한다(S20).The secondary coating solution configured as described above is applied to the object on which the primary coating solution is dried (S20).

그리고 2차 도료액이 건조하기 이전에, 크레이터 형성액을 2차 도료액에 뿌려 2차 도료액에 크레이터와 같은 홈(121)이 형성되게 한다(S22).And before the secondary paint liquid is dried, the crater forming liquid is sprayed on the secondary paint liquid so that the grooves 121 like craters are formed in the secondary paint liquid (S22).

여기에서 크레이터 형성액은 폴리우레탄과 시너를 혼합한 혼합액으로서, 2차 도료액이 건조되기 이전에 크레이터 형성액을 뿌리게 되면 크레이터 형성액에 포함된 시너가 2차 도료액을 희석하여 크레이터 형성액이 뿌려진 자리에 홈(121)이 형성된다.Here, the crater forming liquid is a mixed liquid of polyurethane and thinner, and when the crater forming liquid is sprayed before the secondary coating liquid is dried, the thinner contained in the crater forming liquid dilutes the secondary coating liquid to make the crater forming liquid. The groove 121 is formed in this scattered place.

불균일한 크레이터 패턴을 구현하기 위해서는, 크레이터 형성액을 미스트 형태로 분사하는 스프레이 장비를 이용하는 것보다 손에 묻혀 튕겨서 뿌린다. In order to achieve a non-uniform crater pattern, rather than using a spray device that sprays the crater forming liquid in the form of mist, it is buried in the hand and splashed.

보다 바람직하게, 손에 크레이터 형성액을 흠뻑 묻힌 후에 바로 2차 도료액에 뿌리는 것보다는, 크레이터 형성액이 흠뻑 묻힌 손을 한 번 떨어내어 손에 묻은 크레이터 형성액 일부를 떨어낸 후에 손가락을 튕겨 손가락에 묻어 있는 크레이터 형성액을 2차 도료액에 뿌린다. 그러면 손가락을 튕기는 운동에너지에 의해 손에서 떨어져 나간 크레이터 형성액은 미스트 보다 큰 입자 형태이며, 크레이터 형성액의 입자 크기가 불균일하다. More preferably, rather than sprinkling the crater-forming liquid on the hand immediately after spraying it with the second coating liquid, the hand with the crater-forming liquid is dropped once and the portion of the crater-forming liquid on the hand is dropped, then the finger is bounced off. Sprinkle crater-forming liquid on your fingers into the secondary paint solution. Then, the crater-forming liquid separated from the hand by the kinetic energy of flipping fingers is in the form of particles larger than the mist, and the grain size of the crater-forming liquid is nonuniform.

따라서 크레이터 형성액에 의해 형성된 홈(121)은 그 크기가 불균일하며, 2차 도료액에 형성된 홈(121)의 직경은 15mm 미만의 크고 작은 홈(121)들로 혼합되어 행성의 표면과 같은 형상을 갖게 된다.Therefore, the grooves 121 formed by the crater formation liquid are non-uniform in size, and the diameter of the grooves 121 formed in the secondary coating liquid is mixed into the grooves 121 large and small, which are less than 15 mm, to form the surface of the planet. Will have

이때 단위 면적당 상대적으로 직경이 큰 홈과, 상대적으로 작은 홈 그리고 미세한 홈의 개수 비율은 약 10 : 100 : 500개인 것이 바람직하다.In this case, the ratio of the number of relatively large grooves, relatively small grooves and fine grooves per unit area is preferably about 10: 100: 500.

이와 같이 2차 도료액에 크레이터와 같은 홈들이 형성된 후에 약 48시간을 건조시킨다(S24). 건조과정이 지나면 투명 도료액을 도포하여 투명 도료층(130)을 형성한다(S30).As such, after the grooves, such as craters, are formed in the secondary coating liquid, it is dried for about 48 hours (S24). After the drying process is applied to the transparent coating liquid to form a transparent coating layer 130 (S30).

이와 같이 완전 건조된 2차 도료층(120)에 투명 도료액을 도포하여 2차 도료층(120)의 외측면에 투명 도료층(130)을 형성함으로써 마감처리한다. 투명 도료는 투명 폴리우레탄인 것이 바람직하다.The transparent paint solution is applied to the completely dried secondary paint layer 120 as described above to form a transparent paint layer 130 on the outer surface of the secondary paint layer 120 to finish. It is preferable that a transparent paint is a transparent polyurethane.

도 1은 본 발명에 따른 크레이터 패턴을 형성한 도장품을 나타낸 단면도이고, 1 is a cross-sectional view showing a painted article having a crater pattern according to the present invention,

도 2는 본 발명에 따른 크레이터 패턴을 형성한 도장방법을 나타낸 블록도이며, 2 is a block diagram showing a coating method for forming a crater pattern according to the present invention,

도 3은 본 발명에 따른 크레이터 패턴을 형성한 도장품의 일 예를 나타낸 사진들이다.Figure 3 is a photograph showing an example of a painted article formed with a crater pattern according to the present invention.

* 도면의 주요부분에 대한 부호의 설명 *Explanation of symbols on the main parts of the drawings

100 : 사물체 110 : 1차 도료층100: object 110: primary paint layer

120 : 2차 도료층 121 : 홈120: secondary paint layer 121: groove

130 : 투명 도료층130: transparent paint layer

Claims (8)

도장하고자 하는 사물체(100)와,The object 100 to be painted, 상기 사물체의 표면에 도포되며 외측 표면에 불균일한 홈들이 형성된 2차 도료층(120) 및, A secondary paint layer 120 applied to a surface of the object and having uneven grooves formed on an outer surface thereof; 상기 2차 도료층의 외측 표면에 형성된 투명 도료층(130)을 포함하는 것을 특징으로 하는 크레이터 패턴을 형성한 도장품.Painted article formed with a crater pattern, characterized in that it comprises a transparent paint layer 130 formed on the outer surface of the secondary paint layer. 제1항에 있어서,The method of claim 1, 상기 사물체의 표면과 2차 도료층의 사이에 1차 도료층(110)이 형성된 것을 특징으로 하는 크레이터 패턴을 형성한 도장품.The coated article having a crater pattern, characterized in that the primary paint layer (110) is formed between the surface of the object and the secondary paint layer. 사물체에 1차 도료액을 도포하고 건조하는 단계(S10, S12)와,Coating and drying the primary coating liquid on the object (S10, S12), 건조된 1차 도료액에 2차 도료액을 도포하는 단계(S20)와,Applying a secondary coating solution to the dried primary coating solution (S20); 상기 2차 도료액이 건조되기 이전에 크레이터 형성액을 뿌려 2차 도료액의 표면에 홈을 형성하는 단계(S22)와,Spraying crater forming liquid to form grooves on the surface of the secondary coating liquid before the secondary coating liquid is dried (S22); 2차 도료액을 건조하는 단계(S24)와,Drying the secondary coating solution (S24); 상기 건조된 2차 도료액에 투명 도료액을 도포하고 건조하는 단계(S30)를 포함하는 것을 특징으로 하는 크레이터 패턴을 형성한 도장방법.Coating method of forming a crater pattern comprising the step (S30) of applying a transparent coating liquid to the dried secondary coating liquid and dried. 제3항에 있어서,The method of claim 3, 상기 1차 도료액은 폴리우레탄과 시너의 혼합용액인 것을 특징으로 하는 크레이터 패턴을 형성한 도장방법.The primary coating liquid is a coating method with a crater pattern, characterized in that the mixed solution of polyurethane and thinner. 제3항 또는 제4항에 있어서,The method according to claim 3 or 4, 상기 1차 도료액이 건조하여 형성된 1차 도료층의 표면을 평탄화하는 단계(S14)를 더 포함하는 것을 특징으로 하는 크레이터 패턴을 형성한 도장방법.And coating the surface of the primary paint layer formed by drying the primary paint liquid (S14). 제3항에 있어서,The method of claim 3, 상기 2차 도료액은 투명 폴리우레탄, 불투명 유색도료, 금분, 은분이 혼합된 것을 특징으로 하는 크레이터 패턴을 형성한 도장방법.The secondary coating solution is a coating method of forming a crater pattern, characterized in that the transparent polyurethane, opaque colored paint, gold powder, silver powder is mixed. 제3항에 있어서,The method of claim 3, 상기 크레이터 형성액은 폴리우레탄과 시너의 혼합용액인 것을 특징으로 하는 크레이터 패턴을 형성한 도장방법.The crater forming solution is a coating method with a crater pattern, characterized in that the mixture solution of polyurethane and thinner. 제3항에 있어서,The method of claim 3, 상기 2차 도료액의 표면에 홈을 형성하는 단계(S22)에서는,In the step (S22) to form a groove on the surface of the secondary coating liquid, 크레이터 형성액을 손에 묻힌 후 튕겨 뿌림으로써, 불균일한 홈들을 형성하는 것을 특징으로 하는 크레이터 패턴을 형성한 도장방법.A coating method in which a crater pattern is formed by depositing a crater forming solution on a hand and then sprinkling it to form uneven grooves.
KR1020080014932A 2008-02-19 2008-02-19 Coated article having crater pattern and its coating method KR100853277B1 (en)