KR100815474B1 - A method for implementing hologram in aluminium plate - Google Patents

A method for implementing hologram in aluminium plate Download PDF

Info

Publication number
KR100815474B1
KR100815474B1 KR1020070016987A KR20070016987A KR100815474B1 KR 100815474 B1 KR100815474 B1 KR 100815474B1 KR 1020070016987 A KR1020070016987 A KR 1020070016987A KR 20070016987 A KR20070016987 A KR 20070016987A KR 100815474 B1 KR100815474 B1 KR 100815474B1
Authority
KR
South Korea
Prior art keywords
hologram
plate
pattern
aluminum plate
aluminum
Prior art date
Application number
KR1020070016987A
Other languages
Korean (ko)
Inventor
옥광호
이영민
임현래
Original Assignee
주식회사 라임텍
이영민
임현래
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 주식회사 라임텍, 이영민, 임현래 filed Critical 주식회사 라임텍
Priority to KR1020070016987A priority Critical patent/KR100815474B1/en
Application granted granted Critical
Publication of KR100815474B1 publication Critical patent/KR100815474B1/en

Abstract

A method for forming a hologram on an aluminum plate is provided to prevent harmful matter generated during a plating process, by excluding an electroforming method in forming the hologram and to reduce the manufacturing time. A method for forming a hologram on an aluminum plate(10) comprises the steps of: removing an oxidized layer(12) by chemically treating the aluminum plate, in order to print a fine hologram pattern; forming a pattern duplicate plate(30) having the hologram pattern, by roll-printing the aluminum plate by using a pattern original plate(20); and making a hologram duplicate plate(40) by forming a desirable hologram image on the pattern duplicate plate by using screen printing or digital printing. The chemical treatment step includes a step for dipping the aluminum plate in calcium carbonate aqueous solution and then cutting the surface by using a brush polisher.

Description

알루미늄판에 홀로그램을 구현하는 방법{A Method for implementing hologram in aluminium plate}A method for implementing hologram in aluminum plate

도 1은 종래의 전주도금법을 이용한 홀로그램 구현 방법을 나타내는 도면이다.1 is a view showing a hologram implementation method using a conventional electroplating method.

도 2는 본 발명에 따른 홀로그램 구현 방법을 나타내는 도면이다.2 is a diagram illustrating a hologram implementing method according to the present invention.

도 3a 및 3b는 압연인쇄 과정을 나타내는 도면이다.3A and 3B are diagrams illustrating a rolling printing process.

도 4는 패턴복제판(30)으로부터 홀로그램복제판(40)을 형성하는 방법을 나타내는 도면이다.4 is a diagram illustrating a method of forming the hologram replica plate 40 from the pattern replica plate 30.

도 5는 다양한 실시예에 따른 홀로그램제품을 나타내는 도면이다. 5 is a diagram illustrating a hologram product according to various embodiments.

도 6은 본 발명에 따라 형성된 홀로그램 제품의 평면 및 측면형상을 나타내는 도면이다.6 is a view showing the plane and side shape of the hologram product formed in accordance with the present invention.

본 발명은 홀로그램 구현방법에 관한 것으로서, 보다 상세하게는 인체에 무해한 알루미늄 등의 비중금속에 홀로그램을 구현하는 방법에 관한 것이다.The present invention relates to a method for implementing a hologram, and more particularly, to a method for implementing a hologram on a specific gravity metal such as aluminum that is harmless to a human body.

홀로그램은 단일 파장 및 단일 주파수를 장시간 보유할수 있으며 간섭성이 좋은 레이저빔의 위상정보가 기록되어 다양한 색상, 입체적 형상 또는 동적인 이미지가 구현된 것을 말한다. 홀로그램의 독특한 영상은 생성 및 재생과정이 광학적으로 이루어지기 때문에 기존의 칼라복사기 및 정밀 스캐너에 의해 복사될 경우 그 광학적 정보의 일부만이 인쇄되는 등 복제가 쉽지 않아 각종 위조방지의 수단으로 응용되고 있으며 각종 라벨, 스티커 및 스탬핑 포일등의 형태로 제품화되고 있다.A hologram is a device that can hold a single wavelength and a single frequency for a long time and record phase information of a coherent laser beam to realize various colors, three-dimensional shapes, or dynamic images. Because the unique image of the hologram is optically generated and reproduced, only a part of the optical information is printed when it is copied by a conventional color copying machine and a precision scanner. It is commercialized in the form of labels, stickers and stamping foils.

홀로그램은 다양한 종류가 있으며, 일반적으로 사용되는 홀로그램은 엠보스드 홀로그램이다. 엠보스드 홀로그램은 수백 내지 수천 나노미터의 깊이와 길이를 갖는 사인파형태의 미세한 요철로 이루어진 홀로그램패턴층 및 상기 홀로그램패턴상에 미세요철로부터 반사되는 반사광의 관측이 용이하도록 금속증착층을 포함한다. 금속증착층은 Al, Ag, ZnS, ZnO, SiO2 등으로 형성된다.There are various types of holograms, and the commonly used holograms are embossed holograms. The embossed hologram includes a hologram pattern layer made of fine concavo-convex in the form of a sine wave having a depth and length of several hundreds to thousands of nanometers, and a metal deposition layer to facilitate the observation of reflected light reflected from fine iron on the hologram pattern. The metal deposition layer is formed of Al, Ag, ZnS, ZnO, SiO 2, or the like.

또한, 응용예에 따라 엠보스드 홀로그램은 금속에 구현될 필요가 있다. 일반적으로 홀로그램패턴층이 금속에 표현될 경우 전주 도금법을 이용하고 있다.In addition, embossed holograms may need to be implemented in the metal, depending on the application. In general, when the hologram pattern layer is expressed on metal, electroplating is used.

도 1은 종래의 전주도금법을 이용한 홀로그램 구현 방법을 나타내는 도면이다.1 is a view showing a hologram implementation method using a conventional electroplating method.

먼저, 모판(1)이 준비된다. 모판(1)에는 박리피막의 형태로 홀로그램패턴(2)이 형성되어 있다. 모판(1)은 보통 유리판이 사용된다. First, the mother board 1 is prepared. The mother board 1 is formed with a hologram pattern 2 in the form of a peeling film. The base plate 1 is usually a glass plate.

단계 10에서, 상기 모판(1)상에 제1금속전착층(3)을 형성시키고, 단계 20에서 제1금속전착층(3)을 모판(1)으로부터 분리시킨다. 제1금속전착층(3)은 모판(1)과 반대방향의 요철형상을 가진다.In step 10, a first metal electrodeposition layer 3 is formed on the mother plate 1, and in step 20, the first metal electrodeposition layer 3 is separated from the mother plate 1. The first metal electrodeposition layer 3 has a concave-convex shape in a direction opposite to the base plate 1.

단계 30에서, 제1금속전착층(3)의 하부의 요철면에 분리피막층(4)을 형성한 다.In step 30, the separation coating layer 4 is formed on the uneven surface of the lower portion of the first metal electrodeposition layer 3.

단계 40에서, 상기 분리피막층(4)하부에 제2금속전착층(5)을 형성한다.In step 40, a second metal electrodeposition layer 5 is formed under the separation coating layer 4.

단계 50에서, 제2금속전착층(5)를 분리한다. 제2금속전착층(5)은 모판(1)과 동일한 방향의 요철형상을 가진다. 즉, 제2금속전착층(5)은 모판(1)의 금속복제판이다. In step 50, the second metal electrodeposition layer 5 is separated. The second metal electrodeposition layer 5 has an uneven shape in the same direction as the base plate 1. That is, the second metal electrodeposition layer 5 is a metal replica of the mother plate 1.

그러나, 종래의 방법에 의하면, 상기 제2금속전착층으로 사용되는 금속은 도전성이 있어야 하고, 실제로 주로 니켈이 사용되고 있는데, 이 니켈금속은 중금속중독의 문제를 가지고 있을 뿐 아니라 제조시 취급자 및 홀로그램제품의 사용자에게 금속 알레르기를 유발한다는 문제점이 있다.However, according to the conventional method, the metal used as the second metal electrodeposition layer should be conductive, and in fact, nickel is mainly used. This nickel metal not only has the problem of heavy metal poisoning, but also the handling and hologram products during manufacture. There is a problem that causes a metal allergy to the user.

또한, 상기 전주도금법은 도금과정자체에서 발생하는 유해물질등으로 인해 환경오염문제를 발생시킨다는 문제점도 있다.In addition, the electroplating method has a problem that causes environmental pollution due to harmful substances generated in the plating process itself.

또한, 상기 전주도금법은 제조시간이 많이 걸린다는 단점도 있다. In addition, the electroplating method has a disadvantage that takes a lot of manufacturing time.

따라서, 본 발명은 상기와 같은 문제점을 해결하기 위해 안출된 것으로서, 본 발명의 목적은 친환경적이고, 사용자의 알레르기를 유발하지 않는 금속성 홀로그램 구현방법을 제공하는 것이다.Accordingly, the present invention has been made to solve the above problems, an object of the present invention is to provide a method for implementing a metallic hologram that is environmentally friendly, does not cause allergy of the user.

전술한 과제를 해결하기 위해 본 발명은, 알루미늄판에 홀로그램을 구현하는 방법에 있어서, 미세한 홀로그램 패턴이 인쇄가능하도록, 알루미늄판에 화학처리를 수행함으로써 산화층을 제거하는 단계; 상기 알루미늄판에 패턴원판을 이용하여 압 연인쇄를 수행함으로써 홀로그램 패턴이 형성된 패턴복제판을 형성하는 단계; 및 스크린인쇄 혹은 촬영인쇄중 어느하나의 인쇄법을 이용하여 상기 패턴복제판에 대해 원하는 형상만 홀로그램 이미지를 구현함으로써 홀로그램복제판을 생성하는 단계를 포함한다. In order to solve the above problems, the present invention provides a method for implementing a hologram on an aluminum plate, the method comprising: removing an oxide layer by performing a chemical treatment on the aluminum plate so that a fine hologram pattern is printable; Forming a pattern replica plate on which the hologram pattern is formed by performing pressure-overprinting on the aluminum plate using a pattern disc; And generating a holographic replica by implementing a hologram image of only a desired shape on the pattern replica using a printing method of either screen printing or photographic printing.

여기서, 상기 화학처리단계는, 상기 알루미늄판을 탄산칼슘수용액에 침전시킨 후 브러쉬 연마기를 이용하여 표면을 깍아내는 단계를 포함한다.Here, the chemical treatment step, and the step of precipitating the aluminum plate in a calcium carbonate solution and shaving the surface using a brush polishing machine.

여기서, 상기 화학처리단계는, 상기 알루미늄판을 수산화나트륨용액에 침전시킨 후 물로 세척하는 단계를 포함하는 단계를 포함한다. Here, the chemical treatment step, comprising the step of precipitating the aluminum plate in sodium hydroxide solution and washing with water.

여기서, 상기 알루미늄판의 연신율은 18 이하이고, 1000,2000,3000,5000,6000 계열의 알루미늄합금 중 어느하나 인 것을 특징으로 한다. Here, the elongation of the aluminum plate is 18 or less, characterized in that any one of the 1000, 2000, 3000, 5000, 6000 series aluminum alloy.

일 실시예에서, 상기 압연인쇄의 압연시간은 0.05초 내지 0.1초 인 것을 특징으로 한다.In one embodiment, the rolling time of the rolling printing is characterized in that 0.05 seconds to 0.1 seconds.

일 실시예에서, 상기 압연인쇄의 압연압력은 20 내지 40 Kgf/㎠ 인 것을 특징으로 한다. In one embodiment, the rolling pressure of the rolling printing is characterized in that 20 to 40 Kgf / ㎠.

이하에서는 첨부된 도면을 참조하여 본 발명의 바람직한 일 실시예를 상세하게 설명하기로 한다. Hereinafter, with reference to the accompanying drawings will be described in detail a preferred embodiment of the present invention.

도 2는 본 발명에 따른 홀로그램 구현 방법을 나타내는 도면이다.2 is a diagram illustrating a hologram implementing method according to the present invention.

본 발명의 첫 번째 특징에서, 홀로그램은 전주도금을 이용하는 대신 압연법을 이용한다. 따라서 제조과정중에서 유해물질이 발생하지 않으며 제조상의 환경오 염 및 제조시 취급자의 건강상의 문제도 발생하지 않는다.In the first aspect of the invention, the hologram uses a rolling method instead of using electroplating. Therefore, no harmful substances are generated during the manufacturing process, and environmental pollution in manufacturing and health problems of the handling during manufacturing are not generated.

본 발명의 두 번째 특징에서, 본 발명에서 제품에 사용되는 금속복제판은 알루미늄판과 같이 인체무해한 금속이 사용된다. 따라서 제조시 취급자 및 홀로그램 제품 사용자는 중금속으로 인한 알레르기로부터 보호된다. In the second aspect of the present invention, the metal replica plate used in the product in the present invention is a metal harmless to human body, such as aluminum plate. Thus, during manufacture, handlers and users of holographic products are protected from allergies due to heavy metals.

본 발명의 세 번째 특징에서, 알루미늄판에 압연을 수행하기 이전에 화학처리 공정이 추가된다. 화학처리 공정을 통해 홀로그램과 같은 보다 미세한 압연이 가능하다.In a third aspect of the invention, a chemical treatment process is added before carrying out rolling on the aluminum plate. Chemical treatment processes allow finer rolling, such as holograms.

먼저, 복제판인 인체무해성 금속판, 예를 들면 알루미늄판(10)이 준비된다. 일반적으로, 알루미늄판(10)은 공기중에 노출되어 있으므로, 알루미늄판(10)에는 산화층(12)이 형성되어 있다. First, a human body harmless metal plate, such as an aluminum plate 10, which is a replica, is prepared. Generally, since the aluminum plate 10 is exposed to air, the oxide layer 12 is formed in the aluminum plate 10.

본 발명에서, 상기 '알루미늄판'은 모재가 스텐레스 혹은 구리등이고 그 표면만이 알루미늄막이 형성된 판을 포함한다. 홀로그램은 옹스트롬 단위의 막에도 형성가능하기 때문이다.In the present invention, the 'aluminum plate' includes a plate on which a base material is stainless steel or copper, and only its surface is formed of an aluminum film. This is because the hologram can also be formed in the film of the angstrom unit.

단계 100에서, 알루미늄판(10)에 화학처리 공정을 수행함으로써 산화층(12)을 제거한다. 화학처리 공정은 다음과 같이 2가지 방법으로 수행가능하다.In step 100, the oxide layer 12 is removed by performing a chemical treatment process on the aluminum plate 10. The chemical treatment process can be carried out in two ways as follows.

첫 번째 방법은 연마법이다. 먼저, 알루미늄판(10)을 탄산칼슘(CaCO3)수용액에 수초동안 침전시킨다. 그 후, 알루미늄판(10)을 상기 수용액으로부터 꺼낸 후 브러쉬 연마기를 이용하여 표면을 깍아냄으로써 표면상의 산화층을 제거한다.The first method is polishing. First, the aluminum plate 10 is precipitated for several seconds in an aqueous solution of calcium carbonate (CaCO 3). Then, after removing the aluminum plate 10 from the aqueous solution, the surface of the oxide layer is removed by scraping off the surface using a brush polishing machine.

두 번째 방법은 세척법이다. 먼저, 알루미늄판(10)을 수산화나트륨(NaOH)용액(일명 가성소다)에 수초 동안 침전시킨다. 그 후, 알루미늄판(10)을 상기 수용액 으로부터 꺼낸 후 물로 세척함으로써 산화층을 제거한다.The second method is washing. First, the aluminum plate 10 is precipitated in a sodium hydroxide (NaOH) solution (aka caustic soda) for several seconds. Thereafter, the aluminum plate 10 is removed from the aqueous solution and then washed with water to remove the oxide layer.

본 발명에서 홀로그램패턴은 전주도금방식이 아닌 압연방식을 이용하여 형성된다. 일반적으로, 압연방식으로는 홀로그램패턴의 미세한 요철을 형성하기 힘들다. 그러나, 본 출원인은 화학처리 공정을 통해 알루미늄판의 화학적 물성을 개선함으로써 보다 용이하게 홀로그램패턴의 형성이 가능하도록 하였다. In the present invention, the hologram pattern is formed using a rolling method rather than the electroplating method. In general, it is difficult to form fine unevenness of the hologram pattern by the rolling method. However, the applicant has made it possible to more easily form the hologram pattern by improving the chemical properties of the aluminum plate through the chemical treatment process.

단계 200 및 300에서, 알루미늄판(10)에 대해 패턴원판(20)을 이용하여 압연인쇄를 수행함으로써 홀로그램 패턴이 형성된 패턴복제판(30)을 형성한다. 이는 도 3a 및 3b에서 보다 자세히 설명한다. In steps 200 and 300, the pattern replica plate 30 on which the hologram pattern is formed is formed by performing rolling printing on the aluminum plate 10 using the pattern disc 20. This is explained in more detail in FIGS. 3A and 3B.

단계 400에서, 스크린인쇄 혹은 촬영인쇄를 이용하여 패턴복제판(30)에 대해 원하는 형상만 홀로그램 이미지를 구현함으로써 홀로그램복제판(40)을 생성한다. 이는 도 4에서 보다 상세히 설명한다. In operation 400, the holographic replica 40 is generated by realizing only the desired shape of the pattern replica plate 30 using screen printing or photographing printing. This is described in more detail in FIG. 4.

도 3a 및 3b는 압연인쇄 과정을 나타내는 도면이다.3A and 3B are diagrams illustrating a rolling printing process.

본 발명에서, 홀로그램 패턴은 전주 도금방식이 아닌 압연방식을 이용하여 형성된다. 압연은 롤러등의 압착기를 이용하여 요철형태의 패턴을 금속에 형성하는 방식이다. 본 발명에서 홀로그램이 형성되는 판의 재료를 알루미늄으로 선택함으로써 사용자의 알레르기 발생을 방지하였으며, 알루미늄에 대해 홀로그램을 형성하기 위해 전주도금방식대신에 압연방식을 채택함으로써 도금법의 유해물질발생의 문제점을 해결하였다. 또한 압연방식을 채택함으로 인해 발생가능한 문제점인 미세한 요철의 형성 어려움의 문제점을 화학처리단계를 추가함으로써 해결하였다.In the present invention, the hologram pattern is formed using a rolling method rather than the electroplating method. Rolling is a method of forming a concave-convex pattern on a metal by using a pressing machine such as a roller. In the present invention, by selecting the material of the plate on which the hologram is formed as aluminum to prevent the occurrence of allergy to the user, to solve the problem of the generation of harmful substances in the plating method by adopting the rolling method instead of the electroplating method to form a hologram for aluminum It was. In addition, the problem of difficulty in the formation of fine irregularities, which is a problem that can be caused by the rolling method, was solved by adding a chemical treatment step.

본 발명에서, 압연은 롤러를 이용하여 수행된다. 먼저, 도 3a 의 첫 번째 방 법에서, 홀로그램패턴이 새겨진 홀로그램원판(20)을 롤러 M1 의 둘레에 고정시킨다. 패턴원판(20)은 철, 니켈 등의 강도가 높은 금속으로 제조되고, 홀로그램의 패턴(미세한요철)이 인각되어 있다. 상기 패턴원판의 금속은 연성을 가지므로 어느정도 굴곡을 버틸 수 있다. 도면에는 롤러의 굴곡도가 높은 것을 표시되었지만 롤러의 직경을 크게 할 경우 굴곡도가 낮은, 즉 완만한 굴곡면이 형성되어 원판(20)을 롤러 M1 에 고정시키는데에는 아무 문제가 없다. 고정방법은 접착체, 점착제를 이용할 수 있다. 롤러 M2 는 알루미늄판(10)을 하부에서 지지하는 역할을 하며 압력 D 만큼 가해진다. 롤러 M2는 보통 고무로 형성됨으로써 압력이 만약 과도하게 발생한다면 이를 흡수한다.In the present invention, rolling is performed using a roller. First, in the first method of FIG. 3A, the hologram disc 20 having the hologram pattern engraved is fixed to the circumference of the roller M1. The pattern disc 20 is made of a metal having high strength, such as iron and nickel, and the pattern of the hologram (fine unevenness) is inscribed. Since the metal of the pattern disc is ductile, it may be able to withstand some bending. Although the figure shows that the roller has a high degree of curvature, when the diameter of the roller is increased, there is no problem in fixing the disc 20 to the roller M1 because a low degree of curvature, that is, a smooth curve surface is formed. The fixing method can use an adhesive agent and an adhesive. The roller M2 serves to support the aluminum plate 10 from the bottom and is applied by the pressure D. The roller M2 is usually formed of rubber and absorbs pressure if excessively generated.

도 3b의 두 번째 방법에서, 롤러 M2 대신에 하부 지지판(50)이 사용된다. 하부 지지판(50)은 판의 형태로 제조되어 알루미늄판(10)의 하부를 전체 평면에서 지지한다. In the second method of FIG. 3B, the lower support plate 50 is used instead of the roller M2. The lower support plate 50 is manufactured in the form of a plate to support the lower portion of the aluminum plate 10 in the entire plane.

본 출원인은 상기 전처리후의 압연조건에 대해 수회 반복적인 실험을 수행하였으며, 다음은 그 결과이다.The applicant has carried out several repeated experiments on the rolling conditions after the pretreatment, and the following are the results.

바람직한 실시예에서, 압연시간은 0.05초 내지 0.1초이다. In a preferred embodiment, the rolling time is from 0.05 seconds to 0.1 seconds.

바람직한 실시예에서, 압연압력은 20 내지 40 Kgf/㎠ 이며, 보다 바람직하게는 30Kgf/㎠ 이다. In a preferred embodiment, the rolling pressure is 20 to 40 Kgf / cm 2, more preferably 30 Kgf / cm 2.

바람직한 실시예에서, 알루미늄판의 조건은 다음과 같다.In a preferred embodiment, the conditions of the aluminum plate are as follows.

[표 1]TABLE 1

범위range 두께thickness 0.05 ~ 2 mm0.05 to 2 mm 강도burglar 1000,2000,3000,5000,6000 계열 모두 가능1000,2000,3000,5000,6000 series all available 연신률Elongation 18 이하18 or less

본 출원인의 수회에 거친 실험결과 상기와 같은 조건에서 홀로그램패턴이 정상적으로 인쇄되었음이 밝혀졌다.Experimental results of the applicant several times, it was found that the hologram pattern was normally printed under the above conditions.

본 발명은 전주도금법 대신에 압연방식을 채택함으로써, 도금법을 채택함으로써 발생하는 문제점, 즉 유해물질발생, 취급자의 건강위협등의 문제점이 발생되지 않는다.In the present invention, by adopting the rolling method instead of the electroplating method, problems caused by adopting the plating method, that is, the generation of harmful substances, threats to the health of the operator, etc. do not occur.

또한, 전기도금에 의해 모재에 형성되는데 걸리는 시간(보통 12시간)으로 인해 도금방식은 제조시간이 매우 길지만, 본 발명에서는 모재의 한번의 롤러통과로 홀로그램제조판이 완성되기 때문에, 제조시간이 매우 감소한다.In addition, due to the time taken to form the base metal by electroplating (usually 12 hours), the plating method takes a very long time. However, in the present invention, since the holographic plate is completed in one roller passage of the base material, the manufacturing time is greatly reduced. do.

또한, 홀로그램의 재료 자체를 인체에 무해한 알루미늄으로 선택함으로서 실제품을 사용하는 소비자의 알레르기 발생을 방지할 수 있다.In addition, by selecting the material of the hologram as aluminum that is harmless to the human body, it is possible to prevent the occurrence of allergies of consumers using the actual product.

도 4는 패턴복제판(30)으로부터 홀로그램복제판(40)을 형성하는 방법을 나타내는 도면이다. 4 is a diagram illustrating a method of forming the hologram replica plate 40 from the pattern replica plate 30.

패턴복제판(30)은 홀로그램패턴이 전면에 형성된 알루미늄판(10)을 의미한다. 홀로그램복제판(40)은 원하는 부위에만 홀로그램패턴이 형성된 제품을 의미한다.The pattern replica plate 30 means an aluminum plate 10 having a hologram pattern formed on its entire surface. The hologram replica plate 40 means a product in which a hologram pattern is formed only on a desired portion.

상기 방법은 스크린인쇄법 및 촬영인쇄법 2가지를 이용하여 수행된다.The method is performed using two screen printing methods and photographic printing method.

첫 번째 방법인 스크린 인쇄법에서, 단계 411에서 상기 패턴복제판(30)상부 에 마스크를 이용하여 원하는 부위에만 이미지가 형성된 인쇄층(31)을 형성한 후, 단계 412에서, 상기 패턴복제판(30)을 부식시킴으로써 이미지부분만을 남겨두고 다른 부분의 홀로그램패턴을 제거함으로써 홀로그램복제판(40)을 생성한다.In the first method, the screen printing method, in step 411, a print layer 31 having an image formed only on a desired portion is formed on the pattern replica plate 30 using a mask, and then in step 412, the pattern replica plate 30 is formed. By removing the hologram pattern of the other part while leaving only the image part by corroding, the hologram replica plate 40 is produced.

두 번째 방법인 촬영 인쇄법에서, 단계 421에서, 패턴복제판(30)의 상부에 감광제층(32)을 형성한 후, 단계 422 및 423에서, 상기 감광제층(32)의 표면에 원하는 부위(34)에 레이저빔을 조사(노광)함으로써 이미지(35)를 도안하고, 단계 424에서, 노광되지 않은 감광제층 및 그 하부의 홀로그램패턴을 부식을 통해 제거함으로써 원하는 부위(42)에만 홀로그램이 형성된 홀로그램복제판(40)을 형성한다. In the second method, the photographing printing method, in step 421, the photoresist layer 32 is formed on the pattern replica plate 30, and in steps 422 and 423, a desired portion 34 on the surface of the photoresist layer 32 is formed. The holographic replica plate in which the hologram is formed only on the desired portion 42 by removing the image 35 by irradiating (exposure) to the laser beam and removing the unexposed photoresist layer and the hologram pattern thereunder through corrosion in step 424. 40 is formed.

도 5는 다양한 실시예에 따른 홀로그램제품을 나타내는 도면이다.5 is a diagram illustrating a hologram product according to various embodiments.

홀로그램복제판(40)은 알루미늄판(10)의 원하는 부위에 홀로그램패턴이 형성된 것이다. 변형된 실시예에서, 홀로그램제품이 되기 위하여 상기 홀로그램복제판(40)의 상부 혹은 하부에 이하의 층 중 어느 하나 또는 이들의 조합이 형성되는 것도 가능하다.The hologram replica plate 40 has a hologram pattern formed on a desired portion of the aluminum plate 10. In a modified embodiment, it is also possible to form any one or a combination of the following layers on the top or bottom of the holographic replica plate 40 to be a hologram product.

금속박막층(51)은 Al, Ag, ZnS, SiO2 등의 무기화합물이 증착된 층으로서, 홀로그램패턴(42)의 미세요철로부터 반사되는 반사광의 관측을 보다 용이하게 한다. 일반적으로 100~1000 ㎛이다.The metal thin film layer 51 is a layer on which inorganic compounds, such as Al, Ag, ZnS, and SiO2, are deposited, and makes it easier to observe the reflected light reflected from the roughness of the hologram pattern 42. Generally 100-1000 micrometers.

착색프라이머층(52)은 색상을 가지는 열경화성 랙커가 코팅되어 형성되며 색상효과를 표현한다. The colored primer layer 52 is formed by coating a thermosetting racker having a color and expresses a color effect.

기재필름층(53)은 외부로부터 홀로그램복제판(40)을 보호하기 위한 층이며, 플라스틱제 필름으로 선택가능하다.The base film layer 53 is a layer for protecting the hologram replica plate 40 from the outside and can be selected as a plastic film.

점착체층(54)는 홀로그램복제판(40)을 외부의 물체의 표면에 부착시키기 위한 것으로 주로 홀로그램이 스티커등에 사용될 때 형성된다.The adhesive layer 54 is for attaching the hologram replica plate 40 to the surface of an external object and is mainly formed when a hologram is used for a sticker or the like.

도 6은 본 발명에 따라 형성된 홀로그램 제품의 평면 및 측면형상을 나타내는 도면이다. 6 is a view showing the plane and side shape of the hologram product formed in accordance with the present invention.

왼쪽도면에서, 플레이트 P는 도 5의 여러 가지 층들이 적층된 것이다. 홀로그램이미지 H 는 홀로그램 패턴중에서 원하는 부위로 선택되어 도안된 부분이다. In the left view, the plate P is a lamination of the various layers of FIG. 5. The hologram image H is a portion selected and designed as a desired part of the hologram pattern.

오른쪽도면에서, 플레이트 P1 은 원하는 이미지 부분이 양각으로 표현된 부위 H1을 포함하며, 플레이트 P2 은 원하는 이미지 부분이 양각으로 표현된 부위 H2을 포함한다. 패턴원판(20)을 음각 혹은 양각으로 제조함으로써 그 반대의 형상을 가지는 홀로그램복제판(40)의 홀로그램이미지를 양각 혹은 음각으로 선택할 수 있다. 음각이든 양각이든 홀로그램의 이미지 효과가 발생된다는 점에서는 동일하다.In the right figure, the plate P1 comprises a portion H1 in which the desired image portion is embossed and the plate P2 comprises a portion H2 in which the desired image portion is embossed. By manufacturing the pattern original plate 20 in an intaglio or embossed, the hologram image of the holographic replica plate 40 having the opposite shape can be embossed or engraved. The same is true for holographic image effects, whether engraved or embossed.

한편, 본 발명에 따른 홀로그램 구현 방법은 컴퓨터 프로그램으로 작성 가능하다. 상기 프로그램을 구성하는 코드들 및 코드 세그먼트들은 당해 분야의 컴퓨터 프로그래머에 의하여 용이하게 추론될 수 있다. 또한, 상기 프로그램은 컴퓨터가 읽을 수 있는 정보저장매체(computer readable media)에 저장되고, 컴퓨터에 의하여 읽혀지고 실행됨으로써 홀로그램 구현 방법을 구현한다. 상기 정보저장매체는 자기 기록매체, 광 기록매체, 및 캐리어 웨이브 매체를 포함한다.On the other hand, the hologram implementation method according to the invention can be written in a computer program. Codes and code segments constituting the program can be easily inferred by a computer programmer in the art. In addition, the program is stored in a computer readable media, and read and executed by a computer to implement the hologram implementation method. The information storage medium includes a magnetic recording medium, an optical recording medium, and a carrier wave medium.

이제까지 본 발명에 대하여 그 바람직한 실시예들을 중심으로 살펴보았다. 본 발명이 속하는 기술 분야에서 통상의 지식을 가진 자는 본 발명이 본 발명의 본질적인 특성에서 벗어나지 않는 범위에서 변형된 형태로 구현될 수 있음을 이해할 수 있을 것이다. 그러므로 개시된 실시예들은 한정적인 관점이 아니라 설명적인 관점에서 고려되어야 한다. 본 발명의 범위는 전술한 설명이 아니라 특허청구범위에 나타나 있으며, 그와 동등한 범위 내에 있는 모든 차이점은 본 발명에 포함된 것으로 해석되어야 할 것이다.So far I looked at the center of the preferred embodiment for the present invention. Those skilled in the art will appreciate that the present invention can be implemented in a modified form without departing from the essential features of the present invention. Therefore, the disclosed embodiments should be considered in descriptive sense only and not for purposes of limitation. The scope of the present invention is shown in the claims rather than the foregoing description, and all differences within the scope will be construed as being included in the present invention.

전술한 바와 같이 본 발명에 의하면, 홀로그램이 형성되는 제품의 모제가 알루미늄이기 때문에 사용자의 중금속 알레르기 발생을 방지할 수 있다.As described above, according to the present invention, since the mother of the product on which the hologram is formed is aluminum, it is possible to prevent heavy metal allergy from occurring.

또한, 본 발명에 의하면 홀로그램이 전주도금법을 사용하지 않기 때문에 도금과정에서 발생하는 여러 가지 문제점, 즉 유해물질발생, 취급자의 건강위협 등의 여러 가지 문제점이 해소된다.In addition, according to the present invention, since the hologram does not use the electroplating method, various problems that occur during the plating process, that is, the generation of harmful substances and the threat of health of the operator, are solved.

또한, 본 발명은 도금법에 비해 제조시간이 매우 감소된다.In addition, the present invention significantly reduces the production time compared to the plating method.

또한, 본 발명에 의하면, 화학처리공정을 추가함으로써, 압연방식을 선택하더라도 보다 미세한 요철의 형성이 가능하다.Further, according to the present invention, by adding a chemical treatment step, even finer irregularities can be formed even if the rolling method is selected.

Claims (8)

알루미늄판에 홀로그램을 구현하는 방법에 있어서,In the method of implementing a hologram on an aluminum plate, 미세한 홀로그램 패턴이 인쇄가능하도록, 상기 알루미늄판에 화학처리를 수행함으로써 산화층을 제거하는 단계;Removing the oxide layer by performing a chemical treatment on the aluminum plate so that a fine hologram pattern is printable; 상기 알루미늄판(10)에 패턴원판(20)을 이용하여 압연인쇄를 수행함으로써 홀로그램 패턴이 형성된 패턴복제판(30)을 형성하는 단계; 및Forming a pattern replica plate (30) having a hologram pattern by performing rolling printing on the aluminum plate (10) using the pattern disc (20); And 스크린인쇄 혹은 촬영인쇄중 어느하나의 인쇄법을 이용하여 상기 패턴복제판(30)에 대해 원하는 형상만 홀로그램 이미지를 구현함으로써 홀로그램복제판(40)을 생성하는 단계를 포함하는 것을 특징으로 하는 홀로그램 구현 방법.The hologram replica method comprising the step of generating a holographic replica plate 40 by implementing only the desired shape for the pattern replica plate 30 using the screen printing or photographing printing method. 제 1 항에 있어서, 상기 화학처리단계는,The method of claim 1, wherein the chemical treatment step, 상기 알루미늄판을 탄산칼슘수용액에 침전시킨 후 브러쉬 연마기를 이용하여 표면을 깍아내는 단계를 포함하는 것을 특징으로 하는 홀로그램 구현 방법.And depositing the aluminum plate in an aqueous calcium carbonate solution, and then scraping the surface using a brush polishing machine. 제 1 항에 있어서, 상기 화학처리단계는,The method of claim 1, wherein the chemical treatment step, 상기 알루미늄판을 수산화나트륨용액에 침전시킨 후 물로 세척하는 단계를 포함하는 단계를 포함하는 것을 특징으로 하는 홀로그램 구현 방법.After the aluminum plate is precipitated in sodium hydroxide solution, the hologram comprising the step of including the step of washing with water. 제 1 항에 있어서, 상기 알루미늄판의 연신율은 18 이하인 것을 특징으로 하 는 홀로그램 구현 방법.The method of claim 1, wherein the elongation of the aluminum plate is 18 or less. 제 1 항에 있어서, 상기 알루미늄판은 1000,2000,3000,5000,6000 계열의 알루미늄 중 어느하나 인 것을 특징으로 하는 홀로그램 구현 방법.The method of claim 1, wherein the aluminum plate is any one of 1000, 2000, 3000, 5000, 6000 series of aluminum. 제 1 항에 있어서, 상기 압연인쇄의 압연시간은 0.05초 내지 0.1초 인 것을 특징으로 하는 홀로그램 구현 방법.The method of claim 1, wherein the rolling time is about 0.05 seconds to about 0.1 seconds. 제 1 항에 있어서, 상기 압연인쇄의 압연압력은 20 내지 40 Kgf/㎠ 인 것을 특징으로 하는 홀로그램 구현 방법.The method of claim 1, wherein the rolling pressure of the roll printing is 20 to 40 Kgf / ㎠. 제 1 항에 있어서, 상기 알루미늄판은 스텐레스, 동 중 어느하나의 금속표면에 알루미늄박막이 형성된 판을 포함하는 것을 특징으로 하는 홀로그램 구현 방법.The method of claim 1, wherein the aluminum plate comprises a plate having an aluminum thin film formed on a metal surface of any one of stainless steel and copper.
KR1020070016987A 2007-02-20 2007-02-20 A method for implementing hologram in aluminium plate KR100815474B1 (en)