KR100780730B1 - Surface processing method of the ceiling processed in ultra-violet ink - Google Patents

Surface processing method of the ceiling processed in ultra-violet ink Download PDF

Info

Publication number
KR100780730B1
KR100780730B1 KR1020070030550A KR20070030550A KR100780730B1 KR 100780730 B1 KR100780730 B1 KR 100780730B1 KR 1020070030550 A KR1020070030550 A KR 1020070030550A KR 20070030550 A KR20070030550 A KR 20070030550A KR 100780730 B1 KR100780730 B1 KR 100780730B1
Authority
KR
South Korea
Prior art keywords
ink
smc
panel
thermosetting resin
ceiling
Prior art date
Application number
KR1020070030550A
Other languages
Korean (ko)
Inventor
권영철
Original Assignee
권영철
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 권영철 filed Critical 권영철
Priority to KR1020070030550A priority Critical patent/KR100780730B1/en
Application granted granted Critical
Publication of KR100780730B1 publication Critical patent/KR100780730B1/en

Abstract

A method for treating the surface of a ceiling material coated with UV(Ultraviolet) ink is provided to prevent the ink from being peeled off or spread by using the UV ink adsorbed only by UV rays and to express colors or logos freely. In an SMC(Sheet Molding Compound) panel used as finishing materials for the ceiling, a method for treating the surface of a ceiling material coated with UV ink comprises a preparing step for removing impurities of the surface of the SMC panel(S1); an ink film forming step for applying the UV ink on the upside of the SMC panel(S3); a heating step for preheating the SMC panel(S4); and a first irradiating step for irradiating UV rays on the surface of the SMC panel(S5).

Description

유브이 잉크가 도포된 천정재의 표면처리 방법{Surface processing method of the ceiling processed in ultra-violet ink}Surface processing method of the ceiling processed in ultra-violet ink}

도 1은 본 발명의 실시예에 따른 유브이(UV)잉크가 도포된 천정재의 절개 사시도1 is a cutaway perspective view of a ceiling material coated with UV ink according to an embodiment of the present invention

도 2는 도 1에 도시된 유브이(UV)잉크가 도포된 천정재의 단면도FIG. 2 is a cross-sectional view of the ceiling material coated with UV ink shown in FIG.

도 3은 본 발명의 실시예에 따른 유브이(UV)잉크가 도포된 천정재의 표면처리 방법을 설명하기 위한 순서도Figure 3 is a flow chart for explaining the surface treatment method of a ceiling (UV) ink is applied according to an embodiment of the present invention

< 도면의 주요 부분에 대한 부호의 설명><Description of the reference numerals for the main parts of the drawings>

S1. 준비단계 S2. 1차 막 형성단계S1. Preparation step S2. Primary film formation step

S3. 잉크 막 형성단계 S4. 가열단계
S5. 1차 조사단계 S6. 2차 막 형성단계
S7. 2차 조사단계 S3. Ink film forming step S4. Heating stage
S5. First investigation step S6. Secondary film formation step
S7. 2nd investigation stage

본 발명은 유브이(UV)잉크가 도포된 천정재 및 그 표면처리 방법으로, 더욱 상세하게는 천정재로 쓰이는 열경화성수지(SMC) 판 표면에 친환경적이며 건물의 실내 분위기에 맞는 디자인과 컬러를 지원하고, 잉크가 소재에 흡수가 아닌 흡착을 통해 불필요한 후 가공 없이 표현하고자 하는 디자인과 컬러의 변형 및 벗겨짐을 막기 위해서이다.The present invention is a ceiling material coated with UV (UV) ink and its surface treatment method, more specifically, it is environmentally friendly to the surface of the thermosetting resin (SMC) plate used as the ceiling material and supports the design and color to match the indoor atmosphere of the building In order to prevent the deformation and peeling of the design and color which the ink is intended to express without unnecessary post processing through absorption rather than absorption in the material.

일반적으로 천정재에 쓰이는 소재는 금속재질과, 석고 등이 있는데, 상기 금속재질은 표면이 매끄러워 표현하고자 하는 디자인과 컬러를 구현하고자 하면 많은 공정과 도장의 유지를 위한 후 가공이 가미 되어 그에 따른 비용이 많이 들고 금속 특성상 흠집에 의한 도장의 벗겨짐이 심하며, 상기 석고로 구성된 소재는 착색제 등을 사용하여 원재료에 컬러가 혼합된 제품을 만드나, 원하는 디자인이나 도안 등을 표현하고자 컬러잉크를 표면에 입히고자 하면 흡수되어 번지는 경향이 있다.Generally, materials used for ceiling materials include metal materials and gypsum, and the metal materials have a post-processing process for maintaining a number of processes and paints to implement a design and color to express smooth surfaces. Due to the high cost and severe peeling of the coating due to the nature of the metal, the material composed of gypsum is made of color mixed with the raw materials using a colorant, etc., but the color ink is coated on the surface to express a desired design or design. It tends to be absorbed and smeared.

따라서 표현하고자 하는 컬러나, 디자인, 로고 등을 필요에 따라 상기 소재의 표면에 표현하려면 크게 기존의 인쇄 방식인 수성이나 솔벤트 잉크를 사용한 프린터 출력 방식 등을 사용하고 있다.Therefore, in order to express the color, design, logo, etc. to be expressed on the surface of the material as necessary, a printer printing method using aqueous printing or solvent ink, which is a conventional printing method, is used.

상기 수성잉크를 사용한 프린트방식은 용제가 물이기 때문에 자외선, 바람, 습기등 자연현상에 많은 영향을 받으며, 천정재에 쓰이는 소재 표면에 직접 출력하는 것은 불가능하여 별도의 실사소재에 출력한 후 이를 부착하는 과정을 거쳐야만 하며, 상기 솔벤트잉크는 흡수성이 강하고 경화시간이 비교적 짧으며 소재에 관계없이 그 표면에 직접 출력이 가능하나, 용제가 솔벤트이기에 휘발성이 강하며 역한 냄새가 나며 또한, 열에 약하기에 사용상의 제약이 많이 있으며 솔벤트의 특성 중 폴리염화비닐수지(PVC)계열의 소재를 녹이는 성질이 있어 사용상에 문제가 있어 왔다.The printing method using the water-based ink is affected by natural phenomena such as ultraviolet rays, wind, and moisture because the solvent is water, and it is impossible to output directly to the surface of the material used for the ceiling material. The solvent ink has strong absorbency, hardening time is relatively short, and can be directly output on the surface regardless of material. However, since solvent is solvent, it is volatile and has a bad smell. There are a lot of constraints and there is a problem in use because it has the property of melting the polyvinyl chloride resin (PVC) -based material among the characteristics of the solvent.

본 발명은 상기한 바와 같은 제반 문제점을 해결하기 위하여 제안된 것으로, 그 목적은 천정재로 쓰이는 열경화성수지(SMC) 판넬 표면에, 상온에서 자외선만으로 순간 흡수가 아닌 흡착이 가능하며, 휘발성 없이 흡착이 가능해, 친환경 잉크라 불리는 유브이(UV)잉크를 도포하여 흠집과 자연현상에 의한 잉크의 박리현상이나 잉크의 번짐 등 방지하고, 표현하고자 하는 컬러나 디자인 로고 등을 자유롭게 표현할 수 있으며, 열경화성수지(SMC) 판넬의 표면에 도포된 유브이(UV)잉크는 열경화성수지(SMC) 판넬의 표면에 흡음을 위한 미세한 엠보싱 처리로 인해, 다른 천정재 소재와 다르게 유브이(UV)잉크와 흡착성이 좋으며, 열경화성수지(SMC) 판넬의 표면을 파내지 않는 이상 잉크의 박리현상이 없다 하겠으며, 그 사용처 또한, 사무실천장, 수영장천장, 체육관천장, 호텔천장 등 장소에 관계없이 사용가능케 하는 유브이(UV)잉크가 도포된 천정재의 표면처리 방법을 제공함에 있다.The present invention has been proposed in order to solve the above problems, the object is that the surface of the thermosetting resin (SMC) panel used as a ceiling material, it is possible to adsorb rather than instantaneous absorption by ultraviolet light only at room temperature, adsorption without volatile It is possible to apply UV ink called eco-friendly ink to prevent peeling of ink and smearing of ink due to scratches and natural phenomena, and to freely express colors and design logos to be expressed. UV coated ink on the surface of the panel has good adsorption with UV ink unlike other ceiling materials due to the fine embossing process for sound absorption on the surface of the thermosetting resin (SMC) panel. SMC) There is no peeling phenomenon of ink unless the surface of the panel is dug out. It is also used in office ceiling, swimming pool ceiling, gym cloth. The present invention provides a surface treatment method of a ceiling material coated with UV ink that can be used regardless of a place such as a ceiling or a hotel ceiling.

상기와 같은 목적을 달성하기 위한 본 발명에 따른 유브이(UV)잉크가 도포된 천정재의 표면처리 방법은 천정의 마감재로 사용되는 열경화성수지(SMC) 판넬에 있어서, (a) 상기 열경화성수지(SMC) 판넬 표면의 불순물을 제거하는 준비단계와, (b) 상기 (a)단계를 거친 열경화성수지(SMC) 판넬의 상면에 유브이(UV)잉크를 도포하는 잉크 막 형성단계와, (c) 상기 (b)형성단계를 거친 열경화성수지(SMC) 판넬을 예비 가열하는 가열단계 및 (d) 상기 (c)단계를 거친 열경화성수지(SMC) 판넬의 표면을 자외선으로 조사하는 1차 조사단계를 포함하는 것을 특징으로 한다.Surface treatment method of the UV material (UV) ink coated ceiling material according to the present invention for achieving the above object is in the thermosetting resin (SMC) panel used as a finishing material of the ceiling, (a) the thermosetting resin (SMC) (B) an ink film forming step of applying UV ink on the upper surface of the thermosetting resin (SMC) panel which has undergone the steps (a), and (c) the (b) And (d) a first irradiation step of irradiating the surface of the thermosetting resin (SMC) panel that has undergone the forming step with ultraviolet rays. It is done.

삭제delete

삭제delete

천정의 마감재로 사용되는 열경화성수지(SMC) 판넬에 있어서, (a) 상기 열경화성수지(SMC) 판넬 표면의 불순물을 제거하는 준비단계와, (b) 상기 (a)단계를 거친 열경화성수지(SMC) 판넬의 상면에 유브이(UV)잉크를 도포하는 잉크 막 형성단계와, (c) 상기 (b)형성단계를 거친 열경화성수지(SMC) 판넬을 예비 가열하는 가열단계 및 (d) 상기 (c)단계를 거친 열경화성수지(SMC) 판넬의 표면을 자외선으로 조사하는 1차 조사단계를 포함하는 것을 특징으로 한다.A thermosetting resin (SMC) panel used as a ceiling finishing material, comprising: (a) a step of removing impurities from the surface of the thermosetting resin (SMC) panel; and (b) a thermosetting resin (SMC) having undergone the step (a). An ink film forming step of applying UV ink on the upper surface of the panel, (c) a heating step of preheating the thermosetting resin (SMC) panel which has passed the (b) forming step, and (d) step (c) It characterized in that it comprises a first irradiation step of irradiating the surface of the thermosetting resin (SMC) panel with ultraviolet rays.

또한, 상기 (a)단계를 거친 열경화성수지(SMC) 판넬의 상면에 잉크의 접착을 용이하게 클린너(CLEAR)액을 도포하는 1차 막 형성단계를 더 포함하는 것을 특징으로 한다.The method may further include a primary film forming step of applying a CLEAR liquid to easily adhere the ink to the upper surface of the thermosetting resin (SMC) panel which has passed the step (a).

또한, 상기 (d)단계를 거친 열경화성수지(SMC) 판넬의 표면에 투명한 액체 용제인 유브이(UV)코팅액을 도포하는 2차 막 형성단계를 더 포함하는 것을 특징으로 한다.The method may further include a secondary film forming step of applying a UV coating solution, which is a transparent liquid solvent, to the surface of the thermosetting resin (SMC) panel which has passed the step (d).

또한, 상기 2차 막 형성단계를 거친 후 자외선으로 조사하는 2차 조사단계를 더 포함하는 것을 특징으로 한다.The method may further include a secondary irradiation step of irradiating with ultraviolet rays after the secondary film forming step.

이하, 본 발명의 바람직한 실시예에 따른 유브이(UV)잉크가 도포된 천정재의 표면처리 방법를 첨부된 도면에 의거하여 상세히 설명한다.Hereinafter, a method for surface treatment of a ceiling ink coated with UV ink according to a preferred embodiment of the present invention will be described in detail with reference to the accompanying drawings.

도 1 내지 도 3은 본 발명의 실시예에 따른 유브이(UV)잉크가 도포된 천정재의 표면처리 방법을 도시한 것으로, 도 1은 본 발명의 실시예에 따른 유브이(UV)잉크가 도포된 열경화성수지(SMC) 판넬의 절개 사시도와, 도 2는 도 1에 도시된 유브이(UV)잉크가 도포된 열경화성수지(SMC) 판넬의 단면도와, 도 3은 본 발명의 실시예에 따른 유브이(UV)잉크가 도포된 열경화성수지(SMC) 판의 표면처리 방법을 설명하기 위한 순서도를 각각 나타낸 것이다1 to 3 illustrate a surface treatment method of a ceiling material coated with UV ink according to an embodiment of the present invention, and FIG. 1 is a thermosetting resin coated with UV ink according to an embodiment of the present invention. 2 is a cutaway perspective view of a resin (SMC) panel, FIG. 2 is a cross-sectional view of a UV curable (SMC) panel coated with UV ink shown in FIG. 1, and FIG. 3 is a UV (UV) panel according to an embodiment of the present invention. Flow chart for explaining surface treatment method of ink-coated thermosetting resin (SMC) plate is shown.

상기 도면에 도시된 바와 같이, 본 발명의 실시예에 따른 유브이(UV)잉크가 도포된 천정재의 표면처리 방법은 준비단계(S1)와, 1차 막 형성단계(S2)와, 잉크 막 형성단계(S3)와, 가열단계(S4)와, 1차 조사단계(S5)와, 2차 막 형성단계(S6)와, 2차 조사단계(S7)를 포함하고 있다.As shown in the figure, the surface treatment method of the ceiling material coated with UV (UV) ink according to an embodiment of the present invention is a preparation step (S1), the primary film forming step (S2), the ink film forming step (S3), a heating step (S4), a primary irradiation step (S5), a secondary film forming step (S6), and a secondary irradiation step (S7).

삭제delete

삭제delete

삭제delete

삭제delete

상기와 같은 구성을 가진 본 발명의 실시예에 따른 유브이(UV)잉크가 도포된 천정재의 표면처리 방법는 다음과 같이 설명한다.Surface treatment method of the ceiling material coated with UV (UV) ink according to an embodiment of the present invention having the configuration as described above will be described as follows.

먼저, 천정의 마감재로 사용되는 열경화성수지(SMC) 판넬(10) 표면에 묻어 있는 불순물을 에어(AIR)나 붓 등으로 제거하여 상기 열경화성수지(SMC) 판넬(10)를 준비한다. (준비단계, S1)First, the thermosetting resin (SMC) panel 10 is prepared by removing impurities from the surface of the thermosetting resin (SMC) panel 10 used as a ceiling finishing material with air or a brush. (Preparation stage, S1)

이어서, 액상의 클린너(CLEAR)을 상기 열경화성수지(SMC) 판넬(10) 상면에 도포하여 유브이(UV)잉크의 접착을 용이하게 하기 위한 클린너(CLEAR)층(20)을 형성시킨다. (1차 막 형성단계, S2)Subsequently, a liquid cleaner (CLEAR) is applied to the upper surface of the thermosetting resin (SMC) panel 10 to form a CLEAR layer 20 for facilitating adhesion of the UV ink. (First film formation step, S2)

이어서, 클린너(CLEAR)층(20) 상면에 유브이(UV)잉크를 도포하여 디자인이나 도안, 로고 등을 형성시키는 유브이(UV)잉크층(30)을 형성시킨다. (잉크 막 형성단계, S3)Subsequently, a UV ink layer 30 is formed on the upper surface of the CLEAR layer 20 to form a design, a design, a logo, or the like. (Ink Film Formation Step, S3)

이어서, 상기 유브이(UV)잉크층(30) 내부의 경화를 위해 예비 가열을 한다. (가열단계, S4)Subsequently, preheating is performed to cure the UV ink layer 30. (Heating step, S4)

상기 가열단계(S4)는 유브이(UV)잉크층(30)의 두께로 인한 자외선의 투과가 용이하게 이루어지지 않고 외부에 비해 경화 속도가 느린 내부를 경화시켜 접착성 을 용이하게 하기 위해서이다.The heating step (S4) is to facilitate the adhesion by curing the inside of the curing rate slower than the outside due to the easy transmission of ultraviolet light due to the thickness of the UV (UV) ink layer 30.

이어서, 유브이(UV)잉크층(30) 표면 전체에 자외선을 조사하여 유브이(UV)잉크층(30)을 경화시킨다. (1차 조사단계, S5)Subsequently, the entire surface of the UV ink layer 30 is irradiated with ultraviolet rays to cure the UV ink layer 30. (First investigation stage, S5)

상기 1차 조사단계(S5)에 조사하는 자외선은 자외선 램프로 조사 하는게 바람직하며 자외선 조사시 온도는 15 ~ 25℃가 적당하다.Ultraviolet rays irradiated in the first irradiation step (S5) is preferably irradiated with an ultraviolet lamp, the temperature is 15 to 25 ℃ is appropriate when irradiating ultraviolet rays.

이어서, 상기 유브이(UV)잉크층(30) 표면에 열을 가하여 유브이(UV)잉크층(30)을 경화시킨다. (2차 막 형성단계, S6)Subsequently, heat is applied to the surface of the UV ink layer 30 to cure the UV ink layer 30. (Secondary film formation step, S6)

상기 2차 막 형성단계(S6)는 액상의 투명한 용제로 광택을 띄며, 상기 유브이(UV)잉크층(30)의 박리와 컬러의 변색을 막는다.The secondary film forming step (S6) is glossy with a liquid transparent solvent, and prevents peeling and discoloration of the UV ink layer 30.

이어서, 상기 유브이(UV)코팅층(40) 표면 전체에 자외선으로 조사하여 유브이(UV)코팅층(40)을 경화시킨다.(2차 조사단계, S7)Subsequently, the entire surface of the UV coating layer 40 is irradiated with ultraviolet rays to cure the UV coating layer 40. (Secondary irradiation step, S7)

상기 2차 조사단계(S7)에 조사하는 자외선은 자외선 램프로 조사 하는게 바람직하며 자외선 조사시 실온이 적당하다. Ultraviolet rays irradiated in the secondary irradiation step (S7) is preferably irradiated with an ultraviolet lamp, the room temperature is appropriate when irradiating ultraviolet rays.

이상에서와 같이 본 발명에 따른 유브이(UV)잉크가 도포된 천정재의 표면처리 방법에 의하면, 천정재로 쓰이는 열경화성수지(SMC) 판넬 표면에, 상온에서 자외선만으로 순간 흡수가 아닌 흡착이 가능하며, 휘발성 없이 흡착이 가능해 친환경 잉크라 불리는 유브이(UV)잉크를 도포하여 흠집과 자연현상에 의한 잉크의 박리현상이나 잉크의 번짐 등 방지하고, 표현하고자 하는 컬러나 디자인 로고 등을 자유롭게 표현할 수 있으며, 열경화성수지(SMC) 판넬의 표면에 도포 된 유브이(UV)잉크는 열경화성수지(SMC) 판넬의 표면에 흡음을 위한 미세한 엠보싱 처리로 인해, 다른 천정재 소재와 다르게 흡착성이 좋으며, 열경화성수지(SMC) 판넬의 표면을 파내지 않는 이상 잉크의 박리현상이 없다 하겠으며, 그 사용처 또한, 사무실천장, 수영장천장, 체육관천장, 호텔천장 등 장소에 관계없이 사용가능케 할 수 있는 효과가 있다.As described above, according to the surface treatment method of the ceiling material coated with UV ink according to the present invention, it is possible to adsorb on the surface of the thermosetting resin (SMC) panel used as the ceiling material, rather than instantaneous absorption by ultraviolet light only at room temperature. It can be adsorbed without volatility, and can be coated with UV ink called eco-friendly ink to prevent peeling and ink bleeding due to scratches and natural phenomena, and to freely express colors and design logos. UV ink coated on the surface of SMC panel has good adsorption unlike other ceiling materials due to fine embossing for sound absorption on the surface of SMC panel. There is no peeling phenomenon of ink unless it is dug out of the surface. Its use also includes office ceiling, swimming pool ceiling, gymnasium ceiling, and hotel ceiling. There is an effect that allows you to use regardless of such places.

본 발명은 첨부된 도면에 도시된 실시예를 참고로 설명되었으나, 이는 예시적인 것이며, 당해 분야에서 통상의 지식을 가진 자라면 이로부터 다양한 변형 및 균등한 실시예가 가능하다는 점을 이해할 수 있을 것이다. 따라서 본 발명의 진정한 보호범위는 첨부된 청구범위에 의해서만 정해져야 할 것이다.Although the present invention has been described with reference to the embodiments shown in the accompanying drawings, it is intended to be illustrative, and those skilled in the art will understand that various modifications and equivalent embodiments are possible from this. Therefore, the true scope of protection of the present invention should be defined only by the appended claims.

Claims (7)

삭제delete 삭제delete 삭제delete 천정의 마감재로 사용되는 열경화성수지(SMC) 판넬에 있어서,In the thermosetting resin (SMC) panel used as a ceiling finishing material, (a) 상기 열경화성수지(SMC) 판넬 표면의 불순물을 제거하는 준비단계;(a) preparing to remove impurities from the surface of the thermosetting resin (SMC) panel; (b) 상기 (a)단계를 거친 열경화성수지(SMC) 판넬의 상면에 유브이(UV)잉크를 도포하는 잉크 막 형성단계;(b) an ink film forming step of coating a UV ink on an upper surface of the thermosetting resin (SMC) panel which has passed the step (a); (c) 상기 (b)형성단계를 거친 열경화성수지(SMC) 판넬을 예비 가열하는 가열단계; 및(c) a heating step of preheating the thermosetting resin (SMC) panel which has been subjected to the forming step (b); And (d) 상기 (c)단계를 거친 열경화성수지(SMC) 판넬의 표면을 자외선으로 조사하는 1차 조사단계;를 포함하는 것을 특징으로 하는 유브이(UV)잉크가 도포된 천정재의 표면처리 방법 (d) a first irradiation step of irradiating the surface of the thermosetting resin (SMC) panel with ultraviolet rays through step (c); surface treatment method of the ceiling material coated with UV ink (UV) ink comprising a 상기 제 4 항에 있어서, 상기 (a)단계를 거친 열경화성수지(SMC) 판넬의 상면에 잉크의 접착을 용이하게 클린너(CLEAR)액을 도포하는 1차 막 형성단계;를 더 포함하는 것을 특징으로 하는 유브이(UV)잉크가 도포된 천정재의 표면처리 방법.The method of claim 4, further comprising: forming a primary film for applying a CLEAR liquid to easily adhere the ink to the upper surface of the thermosetting resin (SMC) panel which has passed the step (a). A surface treatment method of a ceiling material coated with UV ink. 상기 제 4 항에 있어서, 상기 (d)단계를 거친 열경화성수지(SMC) 판넬의 표면에 투명한 액체 용제인 유브이(UV)코팅액을 도포하는 2차 막 형성단계;를 더 포함하는 것을 특징으로 하는 유브이(UV)잉크가 도포된 천정재의 표면처리 방법.The method of claim 4, wherein the secondary film forming step of applying a UV coating (UV) coating liquid transparent liquid solvent to the surface of the thermosetting resin (SMC) panel through the step (d); (UV) A surface treatment method of a ceiling material coated with ink. 상기 제 6 항에 있어서,The method of claim 6, 상기 2차 막 형성단계를 거친 후 자외선으로 조사하는 2차 조사단계;를 더 포함하는 것을 특징으로 하는 유브이(UV)잉크가 도포된 천정재의 표면처리 방법. And a second irradiation step of irradiating with ultraviolet rays after the second film forming step. The surface treatment method of the ceiling material to which the UV ink is applied is further included.
KR1020070030550A 2007-03-28 2007-03-28 Surface processing method of the ceiling processed in ultra-violet ink KR100780730B1 (en)