KR100718198B1 - Film for inkjet printer and manufacturing method of the film - Google Patents
Film for inkjet printer and manufacturing method of the film Download PDFInfo
- Publication number
- KR100718198B1 KR100718198B1 KR1020060054423A KR20060054423A KR100718198B1 KR 100718198 B1 KR100718198 B1 KR 100718198B1 KR 1020060054423 A KR1020060054423 A KR 1020060054423A KR 20060054423 A KR20060054423 A KR 20060054423A KR 100718198 B1 KR100718198 B1 KR 100718198B1
- Authority
- KR
- South Korea
- Prior art keywords
- receiving layer
- weight
- parts
- ink receiving
- ink
- Prior art date
Abstract
본 발명은 잉크젯 프린터용 필름 및 그 제조방법에 관한 것으로, 특히 플라스틱 기재층과, 상기 플라스틱 기재층 상면에 코팅되어 잉크를 수용하는 잉크 수용층을 포함하여 구성된 잉크젯 프린터용 필름에 있어서, 상기 잉크 수용층은, 검화도가 상이한 적어도 두 가지 이상의 친수성 바인더를 10~60중량부로 혼합하고, 상기 친수성 바인더에 대해 경화제 0.1~5중량부, 첨가제 1~5중량부, 증류수 10~30중량부를 혼합시킨 조성물로 형성되어, 상기 플라스틱 기재층 상면에 상기 잉크 수용층이 두께 5~25㎛ 범위로 코팅시켜 건조시킨 것을 특징으로 하는 잉크젯 프린터용 필름 및 그 제조방법을 기술적 요지로 한다. 이에 따라 검화도가 상이한 적어도 두 가지 이상의 친수성 바인더와 경화제, 첨가제, 증류수가 적절한 비율로 혼합된 조성물로 이루어진 잉크 수용층을 플라스틱 기재층에 코팅시킴으로서, 잉크 건조에 있어서 발생하는 균열현상이 제거되고 필름의 컬링 현상을 현저히 감소시켜, 발색이 우수하며 투명도가 높고, 우수한 광택 및 선명도를 갖는 기록매체를 얻을 수 있으며, 기록매체에 대한 인쇄 및 보관을 편리하게 할 수 있는 이점이 있다.The present invention relates to a film for an inkjet printer and a method of manufacturing the same, and more particularly, to an inkjet printer film comprising a plastic substrate layer and an ink receiving layer coated on an upper surface of the plastic substrate layer to receive ink. 10 to 60 parts by weight of at least two hydrophilic binders having different degrees of saponification, and are formed of a composition in which 0.1 to 5 parts by weight of a curing agent, 1 to 5 parts by weight of additives, and 10 to 30 parts by weight of distilled water are mixed with respect to the hydrophilic binder. The ink receiving layer is coated on a surface of the plastic base layer in a thickness of 5 to 25 μm and dried, and an inkjet printer film and a method of manufacturing the same are technically essential. Accordingly, by coating the plastic base layer with an ink receiving layer composed of a composition in which at least two hydrophilic binders having different degrees of saponification, a curing agent, an additive, and distilled water are mixed in an appropriate ratio, cracks generated during ink drying are eliminated and By significantly reducing the curling phenomenon, it is possible to obtain a recording medium having excellent color development, high transparency, excellent gloss and clarity, and there is an advantage in that it is convenient to print and store the recording medium.
잉크젯 잉크 수용층 프린터 검화도 폴리비닐알콜 Inkjet Ink Receiving Layer Printer Kendo Polyvinyl Alcohol
Description
본 발명은 잉크젯 프린터용 필름 및 그 제조방법에 관한 것으로, 검화도가 상이한 적어도 두 가지 이상의 친수성 바인더와 경화제, 첨가제, 증류수가 적절한 비율로 혼합된 조성물로 이루어진 잉크 수용층을 플라스틱 기재층에 코팅시켜, 우수한 광택 및 선명도를 갖는 잉크 영상을 기록할 수 있는 잉크젯 프린터용 필름 및 그 제조방법에 관한 것이다.The present invention relates to a film for an inkjet printer and a method of manufacturing the same, wherein an ink receiving layer comprising a composition in which at least two hydrophilic binders having different degrees of saponification, a curing agent, an additive, and distilled water is mixed in an appropriate ratio is coated on a plastic base layer, The present invention relates to a film for an inkjet printer capable of recording an ink image having excellent gloss and clarity, and a method of manufacturing the same.
잉크젯 기록 방법은 비접촉식 프린팅(non-impact printing) 방식의 하나로서, 접촉식 프린팅(impact printing)에 비하여 소음이 적고 레이저 빔 프린터에 비하여 칼라 구현이 비교적 용이하다는 장점을 지니고 있다.The inkjet recording method is one of non-impact printing methods, and has advantages of less noise and relatively easier color implementation compared to laser beam printers compared to contact printing.
잉크젯 프린팅 방식은 출력 속도가 빠르고 프린터 가격이 낮으며, 최근에 와서는 고해상도의 화상도를 제공할 수 있다는 장점 때문에 일반 소비자들이 많이 이용하고 있다. 또한 디지털 기기인 카메라나 캠코더 등의 기기가 널리 보금됨에 따라 잉크젯 기록 장치인 프린터나 플로터 등을 이용하여 일반 가정에서 원하는 이미지를 손쉽게 출력하여 사용하게 되었다.The inkjet printing method has been widely used by consumers because of its high output speed, low printer cost, and recently, high-resolution imaging. In addition, as digital devices such as cameras and camcorders have been widely distributed, a printer or a plotter, which is an inkjet recording device, has been used to easily output and use desired images in a general home.
지금까지 잉크젯 프린터용 필름은 잉크흡수성이 개선된 상질지 시트 및 표면에 다공성 안료로 코팅된 코팅지 시트가 주종으로 사용되어 왔다. 잉크젯 프린터의 빠른 보급과 잉크젯 영상의 다양한 컬러화 및 품질 향상에 따라 잉크젯 프린터용 필름은 높은 표면 광택, 높은 영상 질 및 높은 영상 색농도를 가질 것이 요구되고 있다.Until now, the film for inkjet printers has been mainly used as a high-quality paper sheet with improved ink absorption and a coated paper sheet coated with a porous pigment on the surface. With the rapid spread of inkjet printers and various colorization and quality improvement of inkjet images, the films for inkjet printers are required to have high surface gloss, high image quality and high image color density.
그러나 종래의 잉크젯 프린터용 필름은 대부분 불투명하고, 높은 표면광택을 갖는 기재층 또는 투명한 기재층을 사용할 때도 기재층 상에 형성되는 잉크 수용층이 불투명하여 만족스러운 광택 및 투명도를 갖는 잉크 영상을 제대로 얻을 수 없었다.However, conventional films for inkjet printers are mostly opaque, and even when using a substrate layer having a high surface gloss or a transparent substrate layer, the ink receiving layer formed on the substrate layer is opaque so that an ink image having satisfactory gloss and transparency can be obtained properly. There was no.
따라서, 향상된 투명도 또는 광택을 갖는 잉크젯 프린터용 필름을 제공하기 위해, 예를 들면 전분, 수용성 셀룰로스 유도체, 폴리비닐 알코올 및 폴리비닐피롤리돈으로부터 선택된 친수성 중합체 수지로 된 잉크 수용층을 플라스틱 필름 또는 종이 위에 형성하고자 시도해왔다.Thus, in order to provide a film for an inkjet printer with improved transparency or gloss, for example, an ink receiving layer of a hydrophilic polymer resin selected from starch, water soluble cellulose derivatives, polyvinyl alcohol and polyvinylpyrrolidone is placed on a plastic film or paper. I have tried to form.
셀룰로스 유도체로는 일본 특개소 제56-080489호 공보, 특개소 제63-160,875호 공보 및 특개평 제3-69,338호 공보에 개시된 바와 같은 히드록시프로필메틸셀룰로스, 메틸셀룰로스, 카르복시메틸셀룰로스, 히드록시프로필셀룰로스 및 히드록시에틸셀룰로스를 들 수 있다. 그리고, 셀룰로스 유도체 또는 폴리비닐알코올 등의 수용성 고분자를 지지체 위에 코팅하는 방법(미국특허 제3,889,270호), 수용성 고분자 외에 백색안료를 함께 코팅하는 방법(미국특허 제4,269,891호, 제4,425,405호), 수용성 고분자를 복층구조로 코팅하는 방법(미국특허 제4,425,652호, 제 4,301,195호, 제4,379,804호) 등이 개시되어 있다.Cellulose derivatives include hydroxypropylmethylcellulose, methylcellulose, carboxymethylcellulose, hydroxy as disclosed in Japanese Patent Laid-Open No. 56-080489, Japanese Patent Laid-Open Nos. 63-160,875, and Japanese Patent Laid-Open No. 3-69,338. Propyl cellulose and hydroxyethyl cellulose. In addition, a method of coating a water-soluble polymer such as cellulose derivative or polyvinyl alcohol on a support (US Patent No. 3,889,270), a method of coating a white pigment together with a water-soluble polymer (US Patent Nos. 4,269,891, 4,425,405), water-soluble polymer And a method of coating a multilayer structure (US Pat. Nos. 4,425,652, 4,301,195, 4,379,804) and the like are disclosed.
그러나, 상기 종래 기술들은 잉크 흡수성이 떨어지는 단점을 지니고 있으며, 이를 개선하기 위하여 여러 가지 방안이 제안되지만 분사량이 많은 잉크젯 프린팅의 경우에 있어서는 잉크 흡수성의 개선 정도에 한계를 보이고 있다.However, the prior arts have disadvantages of inferior ink absorbency, and various methods have been proposed to improve them, but in the case of inkjet printing with a large amount of injection, the degree of improvement in ink absorbency has been limited.
또한 종래의 기술들은 높은 착색 특성을 갖는 수성 염료잉크로 이루어지는 착색 물질이 통상 사용되어 왔으며, 최근에는 우수한 내광성을 갖는 수성 안료잉크도 개발되어 현재 실용화되고 있다. 하지만, 수성 안료잉크를 사용하여 프린팅 할 경우에는, 잉크 수용층이 이 수성 안료잉크로 인하여 팽윤되어 건조되면서 잉크 수용층상에 프린팅되어 있는 잉크 영상이 균열되는 문제점이 발생한다.In addition, the conventional techniques have been commonly used a coloring material consisting of an aqueous dye ink having a high coloring properties, and recently, an aqueous pigment ink having excellent light resistance has also been developed and put into practical use. However, when printing using an aqueous pigment ink, a problem arises in that the ink image printed on the ink receiving layer is cracked while the ink receiving layer is swollen and dried due to the aqueous pigment ink.
이러한 균열은 착색 안료를 착색 물질로서 포함하는 잉크 영상이 잉크 수용층 상에 정착될 때 균열하는 현상이며, 이는 육안으로 관찰될 뿐만 아니라, 잉크 영상의 색농도를 불균일하게 할 수 있다. 이러한 영상균열 현상은 색이 상이한 2종 이상의 잉크를 다량으로 포함하는 색 혼합 영상에서 현저하게 발견된다.Such cracking is a phenomenon in which an ink image containing a colored pigment as a coloring material is cracked when it is fixed on the ink receiving layer, which is not only observed with the naked eye, but also makes the color density of the ink image uneven. Such image cracking phenomenon is remarkably found in color mixed images containing a large amount of two or more inks different in color.
그 결과, 잉크 영상에 형성되는 균열로 인해 잉크 영상은 색농도 및 광택이 낮게 되어 불선명하게 된다. 또한 상기와 같은 잉크젯 프린터용 필름은 잉크 수용층 상에서의 잉크 건조율이 낮아서 잉크 수용층의 프린팅면이 장시간 동안 습하고 점착성이 있는 상태를 유지하기 때문에 취급이 어렵다.As a result, the ink image has low color density and gloss due to cracks formed in the ink image, resulting in unclearness. In addition, such an inkjet printer film is difficult to handle because the ink drying rate on the ink receiving layer is low, so that the printing surface of the ink receiving layer maintains a wet and tacky state for a long time.
또한 수성 안료잉크 영상의 균열 문제를 해결하기 위해, 일본 특개평 제10-67,168호 공보에는 실리카졸 입자 또는 알루미나 졸 입자 및 결합제를 포함하는 잉크젯 필름이 제공되어 있다. 그러나, 건조과정 중에 얻어지는 잉크 수용층이 균열 되고 투명도가 감소되는 경향이 있는 것으로 밝혀졌다.Further, in order to solve the problem of cracking of an aqueous pigment ink image, Japanese Patent Laid-Open No. 10-67,168 is provided with an inkjet film containing silica sol particles or alumina sol particles and a binder. However, it has been found that the ink receiving layer obtained during the drying process tends to crack and the transparency decreases.
본 발명은 상기 문제점을 해결하기 위해 안출된 것으로서, 검화도가 상이한 적어도 두 가지 이상의 친수성 바인더와 경화제, 첨가제, 증류수가 적절한 비율로 혼합된 조성물로 이루어진 잉크 수용층을 플라스틱 기재층에 코팅시켜, 우수한 광택 및 선명도를 갖는 잉크 영상을 기록할 수 있고, 잉크 건조에 있어서 발생하는 균열현상이 제거되는 잉크젯 프린터용 필름 및 그 제조방법의 제공을 목적으로 한다.The present invention has been made to solve the above problems, by coating an ink receiving layer composed of a composition in which at least two hydrophilic binders having different degrees of saponification, a curing agent, an additive, and a distilled water are mixed in an appropriate ratio, and having excellent gloss. And it is an object of the present invention to provide an inkjet printer film and a method of manufacturing the same, which can record an ink image having a sharpness, in which a crack phenomenon generated in ink drying is eliminated.
상술한 바와 같은 목적 달성을 위한 본 발명은, 플라스틱 기재층과, 상기 플라스틱 기재층 상면에 코팅되어 잉크를 수용하는 잉크 수용층을 포함하여 구성된 잉크젯 프린터용 필름에 있어서, 상기 잉크 수용층은, 검화도가 상이한 적어도 두 가지 이상의 친수성 바인더를 10~60중량부로 혼합하고, 상기 친수성 바인더에 대해 경화제 0.1~5중량부, 첨가제 1~5중량부, 증류수 10~30중량부를 혼합시킨 조성물로 형성되어, 상기 플라스틱 기재층 상면에 상기 잉크 수용층이 두께 5~25㎛ 범위로 코팅시켜 건조시킨 것을 특징으로 하는 잉크젯 프린터용 필름 및 그 제조방법을 기술적 요지로 한다.In the present invention for achieving the above object, an ink-jet printer film comprising a plastic substrate layer and an ink receiving layer coated on an upper surface of the plastic substrate layer to receive ink, wherein the ink receiving layer has a degree of saponification. At least two or more different hydrophilic binders are mixed in an amount of 10 to 60 parts by weight, and are formed of a composition in which 0.1 to 5 parts by weight of a curing agent, 1 to 5 parts by weight of an additive, and 10 to 30 parts by weight of distilled water are mixed with respect to the hydrophilic binder. An inkjet printer film and a method of manufacturing the same, wherein the ink receiving layer is coated on the upper surface of the substrate layer in a thickness of 5 to 25 μm and dried.
또한, 상기 잉크 수용층의 조성물은, 검화도 88%, 중합도 1700인 폴리비닐알콜 5~40중량부와, 검화도 98%, 중합도 1700인 폴리비닐알콜 5~40중량부를 포함하는 친수성 바인더가 혼합되는 것이 바람직하다.In addition, the composition of the ink receiving layer is mixed with 5 to 40 parts by weight of polyvinyl alcohol having a degree of polymerization of 88% and a degree of polymerization of 1700, and 5 to 40 parts by weight of polyvinyl alcohol having a degree of polymerization of 98% and a degree of polymerization of 1700. It is preferable.
또한, 상기 잉크 수용층의 조성물은, 고형분이 12~13%인 폴리아미드아민/에피클로로히드린계를 포함하는 경화제가 혼합되는 것이 바람직하다.Moreover, it is preferable that the hardening | curing agent containing the polyamide amine / epichlorohydrin system whose solid content is 12 to 13% is mixed with the composition of the said ink receiving layer.
또한, 상기 잉크 수용층의 조성물은, 알루미나 함유량이 20~26%, pH 3.5~4.5인 알루미늄클로르하이드롤 수용액을 포함하는 첨가제가 혼합되는 것이 바람직하다.Moreover, it is preferable that the composition of the said ink receiving layer mix | blends the additive containing the aluminum chlorhydrol aqueous solution whose alumina content is 20 to 26% and pH 3.5-4.5.
이에 따라 검화도가 상이한 적어도 두 가지 이상의 친수성 바인더와 경화제, 첨가제, 증류수가 적절한 비율로 혼합된 조성물로 이루어진 잉크 수용층을 플라스틱 기재층에 코팅시킴으로서, 잉크 건조에 있어서 발생하는 균열현상이 제거되고 필름의 컬링 현상을 현저히 감소시켜, 발색이 우수하며 투명도가 높고, 우수한 광택 및 선명도를 갖는 기록매체를 얻을 수 있으며, 기록매체에 대한 인쇄 및 보관을 편리하게 할 수 있는 이점이 있다.Accordingly, by coating the plastic base layer with an ink receiving layer composed of a composition in which at least two hydrophilic binders having different degrees of saponification, a curing agent, an additive, and distilled water are mixed in an appropriate ratio, cracks generated during ink drying are eliminated and By significantly reducing the curling phenomenon, it is possible to obtain a recording medium having excellent color development, high transparency, excellent gloss and clarity, and there is an advantage in that it is convenient to print and store the recording medium.
본 발명에 따른 잉크젯 프린터용 필름은 플라스틱 기재층 상면에 잉크가 정착되어 흡수될 수 있도록 잉크 수용층이 형성되어 있다. 상기 잉크 수용층은 잉크를 정착시키고, 흡수시키는 잉크 정착층과 잉크 흡수층이 혼합되어 상기 플라스틱 기재층 상면에 단일막으로 형성되며, 검화도가 상이한 적어도 두 가지 이상의 친수성 바인더와 경화제, 첨가제로 형성되며, 상기 물질에 증류수를 혼합하여 농도가 조절된 조성물로 이루어진다.In the inkjet printer film according to the present invention, an ink receiving layer is formed so that the ink is fixed and absorbed on the upper surface of the plastic substrate layer. The ink receiving layer is formed of a single film on the upper surface of the plastic substrate layer by mixing an ink fixing layer and an ink absorbing layer for fixing and absorbing ink, and formed of at least two hydrophilic binders, curing agents, and additives having different degrees of saponification, Distilled water is mixed with the material to form a composition having a controlled concentration.
상기 잉크 수용층의 조성물의 비율은 상기 친수성 바인더는 10~60중량부로, 상기 친수성 바인더에 대해 경화제 0.1~5중량부, 첨가제 1~5중량부, 증류수 10~30중량부로 형성된다.The proportion of the composition of the ink receiving layer is 10 to 60 parts by weight of the hydrophilic binder, 0.1 to 5 parts by weight of the curing agent, 1 to 5 parts by weight of additives, 10 to 30 parts by weight of distilled water relative to the hydrophilic binder.
먼저, 상기 친수성 바인더는 소수성인 플라스틱 기재층 위에 친수성의 물질로 구성된 잉크 수용층이 형성되도록 하여, 상기 플라스틱 기재층이 잉크를 용이하게 흡수할 수 있도록 한다.First, the hydrophilic binder allows an ink receiving layer made of a hydrophilic material to be formed on a hydrophobic plastic base layer, so that the plastic base layer can easily absorb ink.
그리고 상기 친수성 바인더는 검화도가 상이한 적어도 두 개 이상의 물질이 혼합되어 형성되며, 친수성 바인더로는 일반적으로 폴리비닐알콜, 폴리비닐피롤리돈 및 그 유도체와 같은 비닐계 친수성 고분자, 폴리에틸렌 옥사이드, 폴리프로필렌 옥사이드를 포함하는 옥사이드계 고분자, 셀룰로스계 고분자, 폴리아크릴아미드, 폴리아크릴산 등의 아크릴계 친수성 고분자, 이온 변성시킨 수용성 고분자 등이 사용된다.In addition, the hydrophilic binder is formed by mixing at least two substances having different degrees of saponification, and as a hydrophilic binder, generally, vinyl-based hydrophilic polymers such as polyvinyl alcohol, polyvinylpyrrolidone and derivatives thereof, polyethylene oxide, and polypropylene Oxide-based polymers, cellulose-based polymers, acrylic hydrophilic polymers such as polyacrylamide, polyacrylic acid, ion-modified water-soluble polymers, and the like are used.
상기 잉크 수용층에 사용되는 친수성 바인더 성분은 점도, 용해도 등을 고려하여 적절한 비율로 어느 하나를 선택하거나 또는 이들을 혼합하여 사용한다.The hydrophilic binder component used in the ink receiving layer is selected in an appropriate ratio in consideration of viscosity, solubility, or the like, or a mixture thereof is used.
여기에서 잉크 흡수력이 우수한 수용성 고분자로서, 폴리비닐알콜, 폴리비닐피롤리돈 및 그 유도체와 같은 비닐계 친수성 고분자를 사용하는 것이 바람직하며, 특히 폴리비닐알콜을 검화도가 상이한, 바람직하게는 검화도가 88%, 중합도 1700인 것과, 검화도가 98%, 중합도가 1700인 것을 혼합하여 사용하는 것이 바람직하다. 이에 의해 잉크 흡수력, 선명성(번짐성), 잉크균열성, 투명성이 우수한 것을 확인할 수 있다.Here, as a water-soluble polymer having excellent ink absorption, it is preferable to use a vinyl-based hydrophilic polymer such as polyvinyl alcohol, polyvinylpyrrolidone and derivatives thereof, in particular polyvinyl alcohol having a different degree of saponification, preferably saponification degree. Is 88%, polymerization degree 1700, saponification degree 98%, polymerization degree 1700 is preferably used in mixture. Thereby, it can be confirmed that it is excellent in ink absorption power, clarity (bleeding property), ink cracking property, and transparency.
그리고 상기 경화제는 상기 친수성 바인더에 대해 0.1~5중량부의 비율로 형성되며, 잉크 수용층을 상기 플라스틱 기재층 상면에 경화시키기 위한 것이다. 여기에서, 상기 플라스틱 기재층 상면에의 잉크 수용층의 신속하고 견고한 경화를 위 해 상기 경화제는 고형분이 12~13%인 폴리아미드아민/에피클로로히드린계의 물질로 형성되는 것이 바람직하다. And the curing agent is formed in a ratio of 0.1 to 5 parts by weight relative to the hydrophilic binder, it is for curing the ink receiving layer on the upper surface of the plastic base layer. Herein, the curing agent is preferably formed of a polyamide amine / epichlorohydrin-based material having a solid content of 12 to 13% for rapid and solid curing of the ink receiving layer on the upper surface of the plastic base layer.
그리고 상기 첨가제는 가교제, 형광염료, pH조절제, 산화방지제, 소포제, 레벨링제, 윤활제, 컬링방지제, 계면활성제 중에서 어느 하나 또는 이들을 혼합하여 사용할 수 있으며, 바람직하게는 상기 친수성 바인더에 대해 1~5중량부로 형성되며, 특히 알루미나 함유량이 20~26%, pH 3.5~4.5인 알루미늄클로르하이드롤 수용액이 포함되도록 사용하는 것이 바람직하다. And the additive may be used any one or a mixture of crosslinking agents, fluorescent dyes, pH adjusting agents, antioxidants, antifoaming agents, leveling agents, lubricants, anti-curling agents, surfactants, preferably 1 to 5% by weight based on the hydrophilic binder It is preferably used so as to contain an aqueous solution of aluminum chlorhydrol having an alumina content of 20 to 26% and a pH of 3.5 to 4.5.
상기 친수성 바인더, 경화제 및 첨가제는 상기 친수성 바인더에 대해 10~30중량부의 증류수에 혼합하여 코팅액을 형성시켜, 상기 플라스틱 기재층 상면에 도포하여 코팅막을 형성시킬 수 있도록 한다.The hydrophilic binder, the curing agent and the additive is mixed with 10 to 30 parts by weight of distilled water with respect to the hydrophilic binder to form a coating liquid, it is applied to the upper surface of the plastic base layer to form a coating film.
상기의 조성물로 형성된 잉크 수용층을 상기 플라스틱 기재층 상면에 코팅한다. 여기에서 잉크 수용층의 코팅량이 클수록 잉크 흡수도가 증가하는 경향이 있지만, 일정한 코팅량에 도달하게 되면 더 이상 잉크 흡수도는 향상되지 않는다. 따라서, 잉크 수용층의 코팅량은 100~200g/m3 정도가 적당하며, 일반적인 두께는 약 5~30㎛가 바람직하며, 더 바람직한 두께는 10~15㎛가 된다.An ink receiving layer formed of the composition is coated on the upper surface of the plastic base layer. Here, although the absorbency of the ink tends to increase as the coating amount of the ink receiving layer increases, the ink absorbance does not improve any more when a constant coating amount is reached. Therefore, the coating amount of the ink receiving layer is suitably about 100 to 200 g / m 3 , the general thickness is preferably about 5 to 30 μm, and more preferably 10 to 15 μm.
그리고 상기 플라스틱 기재층은, 폴리에틸렌테레프탈레이트(PET) 필름으로 형성되는 것이 바람직하며, 이는 소수성의 성질을 띄어 상기 친수성 바인더가 포함된 잉크 수용층에 의한 잉크가 용이하게 흡수되도록 한다.In addition, the plastic base layer is preferably formed of a polyethylene terephthalate (PET) film, which exhibits hydrophobic properties so that the ink can easily be absorbed by the ink receiving layer containing the hydrophilic binder.
여기에서 상기 플라스틱 기재층은 잉크 수용층과의 부착력을 높이기 위해 프 라이머 처리를 할 수도 있으며, 투명성과 표면 균일성을 위해 물리적인 코로나 처리를 할 수도 있다. 여기에서 코로나 처리는 상기 플라스틱 기재층의 표면장력을 인위적으로 높여 잉크 수용층과의 부착력을 더욱 높일 수 있도록 한 것이다.Here, the plastic substrate layer may be a primer treatment to increase adhesion with the ink receiving layer, and may be a physical corona treatment for transparency and surface uniformity. Corona treatment is to artificially increase the surface tension of the plastic substrate layer to further increase the adhesion to the ink receiving layer.
상기와 같은 조성물을 함유하는 잉크 수용층을 도 1에 도시한 바와 같이, 플라스틱 기재층 상면에 적절한 두께로 코팅하면 잉크젯 프린터용 필름이 완성되게 된다.As shown in FIG. 1, when the ink receiving layer containing the composition as described above is coated on the upper surface of the plastic base layer, an inkjet printer film is completed.
이하에서는 본 발명의 바람직한 실시예에 대해 설명하고자 한다.Hereinafter will be described for the preferred embodiment of the present invention.
먼저, 두께 100㎛의 코로나 처리된 폴리에틸렌테레프탈레이트 필름 위에 하기 표 [1]의 중량비를 갖는 조성물을, 전체 고형분이 12%로 함유되도록 제조하였으며, 각각 바코터를 사용하여 잉크 수용층을 코팅한 다음 오븐(110℃, 3분)에서 건조시켜 잉크 수용층을 약 15㎛되도록 잉크젯 프린터용 필름을 제조하였다.First, a composition having a weight ratio of the following Table [1] on a corona treated polyethylene terephthalate film having a thickness of 100 μm was prepared to contain 12% of total solids, and each was coated with an ink receiving layer using a bar coater, followed by an oven It dried at (110 degreeC, 3 minutes), and manufactured the film for inkjet printers so that an ink receiving layer might be about 15 micrometers.
상기 실시예 1,2,3,4 및 비교1,2,3에 따른 잉크젯 프린터용 필름에 대한 잉크 흡수력, 컬러화상의 선명성(번짐성), 내광성, 잉크 균열성에 대한 평가 결과는 표 2와 같다. 화상 인쇄는 컬러 잉크젯 프린터(상표:hpdeskjet948C)를 이용하여 출력한 것이다.The results of the evaluation of the ink absorption power, the clarity (bleeding resistance), light resistance, and cracking property of the ink for the inkjet printer films according to Examples 1, 2, 3, 4 and Comparative 1, 2, 3 are shown in Table 2. . Image printing is output using the color inkjet printer (brand: hpdeskjet948C).
<평가 결과><Evaluation result>
(1)잉크 흡수력(1) ink absorption
A4사이즈의 본 발명의 실시예에 따른 잉크젯 프린터용 필름에 표준화상을 찍 은 후 바로 백상지를 겹치고 5kg의 쇠뭉치를 10초 동안 올려 놓은 뒤 백상지에 묻어 나오는 잉크의 정도를 확인하여 평가하였다.Immediately after taking a normalized image on the film for an ink jet printer according to the embodiment of the present invention A4 size, the overlapped white paper and placed on a 5kg iron for 10 seconds to evaluate the degree of the ink on the white paper.
○ : 묻어나지 않음.○: Not buried.
× : 묻어남.×: buried.
(2)컬러화상의 선명성(번짐성)(2) Sharpness (smearing) of color image
A4사이즈의 본 발명의 실시예에 따른 잉크젯 프린터용 필름에 표준화상을 찍은 후 40℃, 80% 상대 습도의 항온항습기에서 48시간 방치 후 화상의 번짐 정도를 확인하여 평가하였다.After taking a normalized image on the film for an ink jet printer according to the embodiment of the present invention of A4 size, it was evaluated by checking the degree of smear of the image after standing for 48 hours in a constant temperature and humidity chamber at 40 ° C and 80% relative humidity.
○ : 번짐현상이 관찰되지 않음.(Circle): Smearing phenomenon is not observed.
△ : 약간의 번짐이 발생하나 실제 사용에 있어 문제가 없음.(Triangle | delta): Although a little bleeding occurs, there is no problem in actual use.
× : 번짐현상이 발생하고 실제 사용에 문제가 있음.×: Smear occurs and there is a problem in actual use.
(3)잉크 균열성(3) ink cracking
A4사이즈의 본 발명의 실시예에 따른 잉크젯 프린터용 필름에 표준화상을 찍은 후 육안 관찰에 의해 평가되었다.It was evaluated by visual observation after taking a normalized image on an A4 sized film for inkjet printer according to an embodiment of the present invention.
○ : 잉크 균열현상이 없음.(Circle): There is no ink cracking phenomenon.
△ : 약간의 균열현상이 발생하나 실제 사용에 있어 문제가 없음.(Triangle | delta): Although a little cracking phenomenon arises, there is no problem in actual use.
× : 균열현상이 발생하고 실제 사용에 문제가 있음.X: Cracking phenomenon occurs and there is a problem in actual use.
(4)잉크 영상의 투명성(4) transparency of ink images
A4사이즈의 본 발명의 실시예에 따른 잉크젯 프린터용 필름에 표준화상을 찍은 후 육안 관찰에 의해 평가되었다.It was evaluated by visual observation after taking a normalized image on an A4 sized film for inkjet printer according to an embodiment of the present invention.
○ : 잉크 수용층이 투명함.(Circle): An ink receiving layer is transparent.
× : 잉크 수용층이 불투명함.X: The ink receiving layer is opaque.
상기 표 [2]에 나타낸 바와 같이 본 발명에 따른 조성물을 갖는 잉크 수용층을 갖는 잉크젯 프린터용 필름은 잉크 흡수력, 선명성, 균열성, 광택성이 우수함을 알 수 있었다. 특히 비교예1,2,3,4에서 나타낸 바와 같이 상기 친수성 바인더 하나만을 사용한 경우에는 잉크 흡수력, 선명성, 잉크 균열성, 투명성이 현저히 감소됨을 알 수 있으며, 검화도가 다른 친수성 바인더를 혼합하여 사용한 경우에는 우수한 잉크젯 프린터용 필름 특성을 지님을 알 수 있었다.As shown in the above Table [2], it was found that the film for an inkjet printer having the ink receiving layer having the composition according to the present invention was excellent in ink absorption, sharpness, cracking and glossiness. In particular, when only one hydrophilic binder is used as shown in Comparative Examples 1, 2, 3, and 4, it can be seen that ink absorption, sharpness, ink cracking, and transparency are remarkably reduced. In the case it can be seen that it has excellent film properties for inkjet printers.
상기 구성에 의한 본 발명은 검화도가 상이한 적어도 두 가지 이상의 친수성 바인더와 경화제, 첨가제, 증류수가 적절한 비율로 혼합된 조성물로 이루어진 잉크 수용층을 플라스틱 기재층에 코팅시킴으로서, 수성 안료와 염료 잉크 건조에 있어서 발생하는 균열현상이 제거되고 필름의 컬링 현상을 현저히 감소시켜, 발색이 우수하며 투명도가 높고, 우수한 광택 및 선명도를 갖으며, 색상 치우침이 해소되고 우수한 잉크 흡수력을 갖는 기록매체를 얻을 수 있으며, 기록매체에 대한 인쇄 및 보관을 편리하게 할 수 있는 효과가 있다.According to the present invention, the plastic base layer is coated with an ink receiving layer comprising a composition in which at least two hydrophilic binders having different degrees of saponification, a curing agent, an additive, and distilled water are mixed in an appropriate ratio, thereby drying the aqueous pigment and the dye ink. It is possible to obtain a recording medium having excellent color development, high transparency, excellent gloss and clarity, eliminating color shifting, and excellent ink absorption by eliminating cracking and remarkably reducing the curling phenomenon of the film. There is an effect that can facilitate the printing and storage of the media.
Claims (8)