KR100623073B1 - Pad for advertisement having gloss and non-gloss surface - Google Patents

Pad for advertisement having gloss and non-gloss surface Download PDF

Info

Publication number
KR100623073B1
KR100623073B1 KR1020050086175A KR20050086175A KR100623073B1 KR 100623073 B1 KR100623073 B1 KR 100623073B1 KR 1020050086175 A KR1020050086175 A KR 1020050086175A KR 20050086175 A KR20050086175 A KR 20050086175A KR 100623073 B1 KR100623073 B1 KR 100623073B1
Authority
KR
South Korea
Prior art keywords
film
advertising
pattern
molding member
matte
Prior art date
Application number
KR1020050086175A
Other languages
Korean (ko)
Inventor
김일중
Original Assignee
김일중
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 김일중 filed Critical 김일중
Priority to KR1020050086175A priority Critical patent/KR100623073B1/en
Application granted granted Critical
Publication of KR100623073B1 publication Critical patent/KR100623073B1/en

Abstract

본 발명은 물품 판매점의 계산대나 가정 또는 사무실 등의 책상 등에 올려 놓고 사용하는 광고용 패드에 관한 것으로서, 특히 다양한 질감의 표현이 가능한 스테인레스 밀러판이나 직물, 샌드페이퍼 등의 저면에 광고도안과 대응상의 무늬부 또는 민무늬부를 함께 형성한 상태에서, 이를 이용하여 투명필름지의 표면에 무광택 및 광택의 표면이 형성되게 하여, 인쇄필름의 도안과 대응상의 광택표면과 광고도안 이외의 무광택표면이 함께 연출되게 함으로서,The present invention relates to an advertising pad for use in a counter of a merchandise store, a desk of a home or office, and the like, and in particular, an advertisement pattern and a corresponding pattern on a bottom of a stainless miller plate, fabric, sand paper, etc., which can express various textures. Or in the state where the flat pattern is formed together, by using it to form a matte and glossy surface on the surface of the transparent film, thereby producing a matte surface other than the print surface and the corresponding glossy surface and advertising design,

투명의 선명한 투시가 가능한 광택표면에 의해 그 광고효과를 가일층 향상시키면서도, 광고도안 이외의 부분에는 엠보싱 처리된 무광택 표면 및 하드코팅층에 의해 긁힘이나 눌림, 스크레치, 칼자국 등으로부터 보다 내구성이 뛰어나게 하여 사용수명을 연장시키면서도 보다 고급스러운 질감 및 심미감을 함께 제공하므로 매우 뛰어난 효과를 갖는 무광택표면과 광택표면을 함께 갖는 광고용 패드 및 그 제조방법에 대한 것이다.The glossy surface that enables clear and transparent perspective further enhances the advertising effect, while the parts other than the advertisement design are more durable from scratches, crushes, scratches, and cuts by the embossed matte surface and hard coating layer. The present invention relates to an advertising pad having a matte surface and a gloss surface having a very excellent effect, while providing a more luxurious texture and aesthetic feeling while extending the product.

광고, 패드, 성형부재, 광택, 무광택, 하드코팅, 인쇄필름 Advertising, pads, molded parts, glossy, matte, hard coating, printing film

Description

무광택표면과 광택표면을 함께 갖는 광고용 패드 및 그 제조방법 {Pad for advertisement having gloss and non-gloss surface}Advertising pad having matt surface and glossy surface and manufacturing method thereof {Pad for advertisement having gloss and non-gloss surface}

도 1은 종래의 광고용 패드 사시도1 is a perspective view of a conventional advertising pad

도 2는 본 발명에 따른 광고용 패드의 사시도Figure 2 is a perspective view of the advertising pad according to the present invention

도 3a 내지 도 3g는 본 발명에 따른 광고용 패드의 제조공정도로서,3a to 3g is a manufacturing process diagram of the advertising pad according to the present invention,

도 3a는 이형필름지의 상측에 전사용 잉크층과 하드코팅층을 형성한 상태도3A is a state diagram in which a transfer ink layer and a hard coating layer are formed on an upper side of a release film paper;

도 3b는 하부몰드의 내부에 미리 적층되어진 인쇄필름 등을 도시한 상태도Figure 3b is a state diagram showing a printing film and the like laminated in advance in the lower mold

도 3c는 상기 하부몰드의 최선단에 위치한 투명필름지의 상측에 상기 이형필름지를 올려놓은 상태도3c is a state in which the release film is placed on the upper side of the transparent film located at the top of the lower mold

도 3d는 도 3c의 단계에서 별도의 성형부재를 이용하여 그 하부몰드의 내측을 가압 성형하기 위한 과정도Figure 3d is a process diagram for pressure molding the inside of the lower mold using a separate molding member in the step of Figure 3c

도 3e는 가압 성형물을 별도의 베이스판에 접착하기 위한 과정도Figure 3e is a process diagram for bonding the press-molded product to a separate base plate

도 3f는 베이스판에 경화 접착된 상태에서 최선단의 이형필름지를 제거하는 과정도Figure 3f is a process of removing the best release film paper in the state of curing bonding to the base plate

도 3g는 완성된 광고용 패드의 측단면 확대도Figure 3g is an enlarged side cross-sectional view of the completed advertising pad

도 4는 스테인레스 밀러판을 이용한 성형부재의 측단면 및 저면 상태도Figure 4 is a side cross-sectional view and a bottom state of the molding member using a stainless miller plate

도 5는 부직포 등을 이용한 성형부재의 측단면 및 저면 상태도Figure 5 is a side cross-sectional view and bottom state of the molding member using a nonwoven fabric, etc.

* 도면의 주요부분에 대한 부호의 설명 *Explanation of symbols on the main parts of the drawings

1 : 베이스판 2 : 기재접착층1: base plate 2: base material adhesive layer

3 : 인쇄필름 4 : 필름접착층3: printing film 4: film adhesive layer

5 : 투명필름지 6 : 전사용 투명잉크층5: transparent film 6: transparent ink layer for transfer

7 : 하드코팅층 8 : 광택부7: hard coat layer 8: glossy part

9 : 무광처리부 10 : 이형박리지9: matte processing unit 10: release release

11 : 하부몰드 12 : 성형부재11: lower mold 12: molding member

13 : 무늬부 14 : 민무늬부13: pattern portion 14: pattern portion

15 : 가압패널15: pressure panel

본 발명은 물품 판매점의 계산대나 가정 또는 사무실 등의 책상 등에 올려 놓고 사용하는 광고용 패드에 관한 것으로서, 무광택 에칭 표면이 갖는 특성에 의해 보다 부드러운 심미감과 사용감을 얻게 하면서도 이에 의해 긁힘이나 눌림, 칼 자국 등이 잘 드러나지 않으며, 각종 광고용 문자나 그림, 도안 등이 인쇄된 부분에는 광택표면을 갖게 함으로서, 광고용 패드가 갖는 본래의 목적에 부합하면서도 효과적인 사용성을 제공하는 무광택표면과 광택표면을 함께 갖는 광고용 패드 및 그 제조방법에 대한 것이다.The present invention relates to an advertising pad for use in a counter of a merchandise store, a desk of a home or office, etc., and has a smooth aesthetic and usability by the characteristics of a matte etched surface. This pad is not easily revealed, and the advertising pad having a glossy surface and a glossy surface that provides effective usability while meeting the original purpose of the advertising pad by providing a glossy surface on a portion where various advertising characters, pictures, drawings, etc. are printed, and It is about the manufacturing method.

일반적으로 편의점이나 슈퍼마켓 등의 물품 판매점의 계산대에는 구매자가 구입하고자 하는 물품을 올려놓고 계산을 위한 패드가 올려져 있다. 이러한 패드는 통상적으로 담배나 각종 물품을 공고 및 홍보하기 위한 도안이나 그림, 사진, 문자, 도형 등이 인쇄되어 있는 형태를 갖고 있다.In general, at the checkout counter of a merchandise store such as a convenience store or a supermarket, the buyer puts the goods to be purchased and puts a pad for calculation. Such pads usually have a form in which a pattern, a picture, a picture, a letter, a figure, or the like for advertising and publicizing a cigarette or various articles is printed.

이와 같은 패드는 통상적으로 고무 또는 PVC재로 된 합성수지판의 상면에 각종 광고용 문구나 그림, 도안 등을 인쇄하여 부가적인 광고효과를 창출하면서도 그 패드 자체의 탄력성에 의해 계산대나 테이블 등의 상부면이 손상되는 것을 방지하고자 사용되는 것이다.Such pads are usually printed on the upper surface of rubber or PVC material by printing various advertising phrases, pictures, drawings, etc. to create additional advertising effects, while the upper surface of the counter or table is damaged by the elasticity of the pad itself. It is used to prevent it.

이러한 패드는 상기와 같은 물품 판매점 이외에도 사무실 등의 책상 위나, 가정용 책상 등에 깔아 놓고 사용하는데, 사무실이나 가정에서는 칼을 사용이 빈번할 수 있어 칼을 이용하여 종이나 각종 시트를 절단하고자 하는 경우 상기와 같은 패드를 이용하면 테이블이나 책상의 표면에 손상을 가하지 아니하므로 널리 사용되고 있다.These pads are used on the desks of offices, home desks, etc. in addition to the merchandise stores as described above. Knives may be frequently used in offices or homes. The same pad is widely used because it does not damage the surface of the table or desk.

특히, 상기한 바와 같은 패드는 대부분 그 표면의 광고 인쇄면을 통해 소비자나 구매자에게 지속적인 광고 효과를 얻고자 하는 것이므로, 무료로 제공되거나 매우 저렴한 비용으로 제공되므로 상기와 같은 편리성과 효율성을 갖는 광고용 패드는 전반적인 분야에서 매우 널리 사용되고 있는 것이다.In particular, since the pad as described above is intended to obtain a continuous advertising effect to consumers or buyers through the advertising printing surface of the surface, it is provided for free or at a very low cost, so the pad for advertisement having the above convenience and efficiency Is very widely used throughout the field.

이와 같은 광고용 패드는 도 1의 도시와 같이, 그 최하층에서 최상부층에 이르기까지 접착 및 융착된 다층의 구조를 갖고 있는 것으로서,As shown in FIG. 1, the advertising pad has a multilayered structure bonded and fused from the lowest layer to the uppermost layer.

최하측에는 1~3mm의 두께를 갖는 고무 또는 PVC 합성수지재로 된 베이스판(100)이 형성되고, 그 상측에는 접착층(101)이 형성되어 상기 접착층(101)에 의해 상부면에 다양한 인쇄면을 갖는 인쇄필름(102)이 부착되는 것이다.Base plate 100 made of rubber or PVC synthetic resin material having a thickness of 1 to 3 mm is formed on the lower side, and an adhesive layer 101 is formed on the upper side thereof to have various printing surfaces on the upper surface by the adhesive layer 101. The print film 102 is attached.

또한, 상기한 인쇄필름(102)의 상부면에는 미세한 엠보싱에 의해 무광처리된 필름지(103)가 위치하게 되는 것으로, 이들을 서로 상하 적층한 후 프레싱 작업에 의해 가압하여 열융착방식을 통해 부착하여 구성하게 된다.In addition, the upper surface of the printing film 102 is to place the matte film 103 by the fine embossing, they are laminated up and down each other and then pressed by a pressing operation to be configured by heat bonding method Done.

여기서, 상기한 필름지를 광택의 투명필름지를 사용하게 되면 그 하측의 인쇄필름이 그대로 투시되는 광택의 광고용 패드를 형성할 수 있는 반면, 무광처리된 투명의 필름지를 사용하면 긁힘이나 눌림, 칼자국 등으로부터 보다 내구성이 향상되는 무광의 표면을 갖는 광고용 패드를 생산할 수 있게 되는 것이며,Here, using the transparent film of the glossy film can form a glossy advertising pad that the print film of the lower side is exposed as it is, while using a matte transparent film paper from scratches, crushing, cuts, etc. It is possible to produce advertising pads having a matte surface that is more durable,

상기한 무광표면의 광고용 패드를 형성함에 있어 무광택 필름지 대신 광택 필름지를 사용하되 그 필름지의 표면에 별도로 무광코팅층을 형성할 수도 있는 것이다.In forming the matte surface of the advertising pad is to use a glossy film paper instead of matte film paper, it is also possible to form a matte coating layer on the surface of the film paper separately.

그러나, 상기한 바와 같은 광고용 패드는 주지한 바와 같이 무광택 표면 또 는 광택 표면으로 된 단일의 특성만을 갖는 패드만을 생산할 수 있어 각각의 문제점을 내포하고 있는 것으로서,However, as described above, the advertising pads can produce only pads having only a single characteristic of a matte surface or a glossy surface, and thus have respective problems.

광택 표면의 광고용 패드는 내부 인쇄필름의 광고도안이나 문구 등이 선명하게 투시되어 광고 효과가 뛰어난 장점을 갖고 있으나, 표면이 긁힘이나 눌림, 칼자국 등에 의해 쉽게 손상되므로 그 내구성이 현저히 떨어지면서도 내구성이 떨어짐에 따라 그 사용수명이 극히 짧은 문제점을 갖고 있으며,Glossy surface advertising pads have the advantage of advertising effect because they clearly see the print or stationery of the internal printing film, but the surface is easily damaged by scratches, crushes, cuts, etc. Depending on the service life of the extremely short problem,

무광택 표면을 갖는 광고용 패드는 부드러운 심미감이나 고급스러운 질감을 표현하면서도 표면의 긁힘이나 눌림, 칼자국 등이 쉽게 드러나지 않아 그 사용수명이 연장되는 효과가 있으나, 엠보싱 처리된 무광택 표면에 의해 내부의 광고문구나 도안, 그림이나 사진 등이 선명하게 투시되지 못하므로 상대적으로 그 광고효과가 떨어지는 문제점이 있는 것이다.Advertising pads with a matte surface express a smooth aesthetic or luxurious texture, but the scratches, crushes, and cuts on the surface are not easily exposed, which extends the service life of the pads. Since the picture, picture or picture is not clearly visible, there is a problem that the advertising effect is relatively low.

본 발명은 전기한 바와 같은 문제점을 제거코자 안출된 것으로서, 다양한 질감의 표현이 가능한 스테인레스 밀러판이나 직물, 샌드페이퍼 등의 저면에 광고도안과 대응상의 무늬부 또는 민무늬부를 함께 형성한 상태에서, 이를 이용하여 투명필름지의 표면에 무광택 및 광택의 표면이 형성되게 하여, 인쇄필름의 도안과 대응상의 광택표면과 광고도안 이외의 무광택표면이 함께 연출되게 함으로서,The present invention has been devised to eliminate the problems described above, in the form of a pattern or a non-pattern on the advertising design and the corresponding surface on the bottom of a stainless miller plate, fabric, sand paper, etc. that can express a variety of texture, By forming a matte and glossy surface on the surface of the transparent film paper, the glossy surface of the print film and the corresponding pattern and the matte surface other than the advertising design is produced together,

투명의 선명한 투시가 가능한 광택표면에 의해 그 광고효과를 가일층 향상시키면서도, 광고도안 이외의 부분에는 엠보싱 처리된 무광택 표면과 하드코팅층에 의해 긁힘이나 눌림, 스크레치, 칼자국 등으로부터 보다 내구성이 뛰어나게 하여 사용수명을 연장시키면서도 보다 고급스러운 질감 및 심미감을 함께 제공하므로 매우 뛰어난 효과를 갖는 무광택표면과 광택표면을 함께 갖는 광고용 패드 및 그 제조방법을 제공함에 본 발명의 목적이 있는 것이다.The glossy surface that allows clear and transparent viewing further enhances the advertising effect, while the parts other than the advertisement design are more durable from scratches, crushes, scratches and cuts by the embossed matte surface and hard coating layer. It is an object of the present invention to provide an advertising pad having a matte surface and a glossy surface having a very excellent effect and a method for producing the same, while providing a more luxurious texture and aesthetics.

이하, 본 발명의 바람직한 실시예를 설명한다.Hereinafter, preferred embodiments of the present invention will be described.

도 2는 본 발명에 따른 광고용 패드의 사시도이고, 도 3a 내지 도 3g는 본 발명에 따른 광고용 패드의 제조공정도이다.Figure 2 is a perspective view of the advertising pad according to the present invention, Figure 3a to Figure 3g is a manufacturing process of the advertising pad according to the present invention.

먼저, 무광택표면과 광택표면을 함께 갖는 광고용 패드는,First, an advertising pad having a matte surface and a glossy surface together,

최하단에 1~3mm의 두께를 갖는 연질 탄력상의 베이스판(1)이 위치하고, 그 베이스판(1)의 상측에는 기재접착층(2)이 형성되며, 상기 접착층(2)의 상측에는 하측으로부터 순차적으로 인쇄필름(3)과, 필름접착층(4), 투명필름지(5), 전사용 투명잉크층(6), 하드코팅층(7)을 형성하되,A soft elastic base plate 1 having a thickness of 1 to 3 mm is positioned at the lowermost end thereof, and a base material bonding layer 2 is formed on the upper side of the base plate 1, and the upper side of the adhesive layer 2 is sequentially formed from the lower side. A printing film 3, a film adhesive layer 4, a transparent film paper 5, a transfer transparent ink layer 6, and a hard coating layer 7 are formed,

상기 투명필름지(5)의 전체 표면은, 상기 인쇄필름(3)의 도안과 대응위치에 형성된 광택부(8)를 제외한 무광처리부(9)가 형성되도록 구성하여 이루어진 것이다.The entire surface of the transparent film paper 5 is configured such that the matte processing unit 9 is formed except for the gloss unit 8 formed at a position corresponding to the pattern of the printing film 3.

상기한 바와 같은 광고용 패드를 제조하기 위한 방법 및 공정으로는,As a method and a process for manufacturing the advertising pad as described above,

이형박리지(10)의 표면에 하드코팅층(7)과 전사용 투명잉크층(6)을 순차적으 로 형성하고,The hard coating layer 7 and the transfer transparent ink layer 6 are sequentially formed on the surface of the release paper 10,

별도의 인쇄필름(3)의 상측에는 필름접착층(4)을 이용하여 투명필름지(5)를 부착하여 이를 별도의 하부몰드(11) 내에 삽입시키고,The transparent film paper 5 is attached to the upper side of the separate printing film 3 by using the film adhesive layer 4 and inserted into the separate lower mold 11,

상기 투명필름지(5)의 상측에는 상기 전사용 투명잉크층(6)이 맞닿도록 상기 이형박리지(10)를 적층시켜,On the upper side of the transparent film 5, the release paper 10 is laminated so that the transfer transparent ink layer 6 abuts,

이를 별도의 성형부재(12)를 이용하여 가압 열융착시키되,This is pressurized heat fusion using a separate molding member 12,

상기 성형부재(12)의 저면에는, 인쇄필름(3)의 도안 이외부분과 대응되는 무늬부(13)와 상기 인쇄필름(3)의 도안과 일치하는 민무늬부(14)를 각각 형성하여, 상기 성형부재(12)의 가압에 의해 그 무늬부(13) 만이 상기 투명필름지(5)에 전사되게 하고,On the bottom of the molding member 12, a pattern portion 13 corresponding to a portion other than the pattern of the printing film 3 and a plain pattern portion 14 corresponding to the pattern of the printing film 3 are formed, respectively, By pressing the molding member 12, only the pattern portion 13 is transferred to the transparent film sheet 5,

열압착된 인쇄필름(3)은 상부면에 기재접착층(2)이 형성된 베이스판(1)의 상측에 부착 형성하며,The thermocompression printing film 3 is attached to the upper side of the base plate 1, the base adhesive layer 2 is formed on the upper surface,

상기 기재접착층(2)이 경화되면, 최상측에 위치한 이형박리지(10)를 제거하여 하드코팅층(7)이 최상측 표면이 되도록 제조하여 이루어진 것이다.When the base material adhesive layer 2 is cured, the hard release layer 7 is made to be the top surface by removing the release release 10 located at the top.

이때, 상기한 성형부재(12)를 스테인레스 밀러판을 이용하되, 그 스테인레스 밀러판의 저면에는 요철상의 무늬부(13)와 광택표면상의 민무늬부(14)가 인쇄필름(3)의 도안과 대응상으로 형성되게 하면 되는 것이며,At this time, the molding member 12 using a stainless miller plate, and the bottom surface of the stainless miller plate corresponds to the pattern of the uneven pattern portion 13 and the flat pattern portion 14 on the glossy surface to correspond to the pattern of the printing film 3 To form into an image,

상기한 성형부재(12)를 부직포 또는 샌드페이퍼, 직물, 목재, 엠보싱 시트지 등을 사용하고자 할 경우에는 상기 성형부재(12)의 상측에 별도의 가압패널(15)를 부착하여, 이들 성형부재(12)에는 상기 인쇄필름(4)의 도안과 대응상의 크기를 갖 도록 절개 관통상의 민무늬부(14)를 형성하면 되는 것이다.In the case of using the nonwoven fabric or sandpaper, woven fabric, wood, embossed sheet, or the like, the pressing member 15 is attached to the upper side of the molding member 12, and these molding members 12 ) Is to form a cut through the flat pattern 14 to have a size corresponding to the pattern of the printing film (4).

이상과 같은 본 발명 무광택표면과 광택표면을 함께 갖는 광고용 패드 및 그 제조방법을 그 제조공정에 따라 보다 상세히 설명하면 다음과 같다.The advertising pad and the manufacturing method of the present invention having a matte surface and a glossy surface as described above in more detail according to the manufacturing process as follows.

도시와 같이 본 발명 광고용 패드를 생산하기 위해서는 먼저, 도 3a의 도시와 같이 비닐재로 된 이형박리지(10)의 표면에 하드코팅층(7)과 전사용 투명잉크층(6)을 각각 도포 형성한다.In order to produce the advertising pad of the present invention as shown in Figure 3a, as shown in Figure 3a, first, the hard coating layer 7 and the transfer transparent ink layer 6 are formed on the surface of the release paper 10 made of vinyl material, respectively. do.

이때, 상기한 하드코팅층(7)은 경화성 투명 코팅액으로 이루어진 것으로서 비닐지나 장판 등의 표면에 주로 도포하는 물질로서 그 표면의 내구성을 향상시킴은 물론 내오염성이나 내산성 등이 우수하여 사용수명을 연장시키는 효과를 제공하게 된다.At this time, the hard coating layer 7 is made of a curable transparent coating liquid and mainly applied to the surface of vinyl paper or sheet, etc. to improve the durability of the surface, as well as to improve the durability and acid resistance, etc. Will provide an effect.

또한, 상기한 전사용 투명잉크층(6)은 상기 하드코팅층(7)이 이형박리지(10)로부터 잘 분리되어 후술하는 타측의 투명필름지(5) 측으로 매끄럽게 전사되어 견고한 고착 형성이 이루어지도록 하는 역할을 하게 된다.In addition, the transfer transparent ink layer 6 is such that the hard coating layer 7 is well separated from the release film 10 to be smoothly transferred to the other side of the transparent film paper 5 to be described later to form a firm fixation. It will play a role.

이와 같이 전사용 투명잉크층(6)와 하드코팅층(7)이 형성된 이형박리지(10)를 별도의 하부몰드(11) 내로 삽입하게 되는데, 도 3b의 도시와 같이 상기한 하부몰드(11) 내측에는 미리 광고용 인쇄필름(3)과 그 상측의 필름접착층(4) 및 최선단의 투명필름지(5)가 위치하고 있는 상태로서, 상기한 전사용 투명잉크층(6)이 하측으로 향하도록 그 이형박리지(10)를 하부몰드(11)의 내측으로 안치시키면 되는 것이다.In this way, the release release paper 10 having the transfer transparent ink layer 6 and the hard coating layer 7 formed therein is inserted into a separate lower mold 11, the lower mold 11 as illustrated in FIG. 3B. The printing film 3 for advertisement, the film adhesive layer 4 of the upper side, and the transparent film paper 5 of the upper end are previously located inside, and the said release transparent ink layer 6 is oriented so that the said transfer transparent ink layer 6 may face downward. The release paper 10 may be placed inside the lower mold 11.

이와 같은 상태에서 도 3c의 도시와 같이 별도의 성형부재(12)를 이용하여 상기 하부몰드(11) 내의 필름지 등을 가압하게 되면 이들이 서로 열융착되며 각각의 필름지가 융착되는 것인데,In this state, as shown in Figure 3c by pressing the film in the lower mold 11 using a separate forming member 12, they are thermally fused to each other and each film is fused.

상기한 성형부재(12)의 하부 저면에는 요철상의 무늬부(13)와 민무늬부(14)가 형성되어 있으므로, 상기 무늬부(13)가 위치하는 투명필름지(5)의 해당부분에는 상기 무늬부(13)에 의한 엠보싱 형태의 무광처리부(9)가 형성되는 것이며, 상기 민무늬부(14)가 가압 위치하는 투명필름지(5)의 해당부분에는 매끄러운 투명의 광택부(8)가 형성되는 것이다.Since the lower surface of the molding member 12 is formed with the uneven pattern portion 13 and the non-pattern portion 14, the pattern portion in the corresponding portion of the transparent film paper 5 where the pattern portion 13 is located The matte treatment part 9 of the embossing form by 13 is formed, and the smooth transparent gloss part 8 is formed in the corresponding part of the transparent film paper 5 in which the flat pattern part 14 is pressed.

따라서, 상기한 바와 같은 무늬부(13) 및 민무늬부(14)를 통해 인쇄필름(3)에 미리 인쇄된 광고용 도안이나 그림, 사진, 문자 등이 무광처리부(9)로 인해 그 시인성이 떨어지는 것을 방지할 수 있게 되는 것이다.Therefore, the print pattern, the picture, the picture, the text, etc., which are printed in advance on the printing film 3 through the pattern part 13 and the flat pattern part 14 as described above, are poor in visibility due to the matte processing part 9. It can be prevented.

즉, 광고용 도안부분은 성형부재(12)의 민무늬부(14)에 의한 광택부(8)로 형성되게 하고, 상기한 광고용 도안 이외의 전체부분은 성형부재(12)의 요철상 무늬부(13)에 의해 엠보싱의 무광처리부(9)가 형성되게 하여 이에 의한 보다 고급스럽고 부드러운 심미감을 갖게 하는 것이다.That is, the advertising design portion is formed by the gloss portion 8 by the flat pattern portion 14 of the molding member 12, the entire portion other than the advertising design described above is the uneven pattern portion 13 of the molding member 12 By forming the matte processing portion 9 of the embossing to thereby give a more elegant and soft aesthetics.

여기서, 상기한 성형부재(12)는 변형이 되지 않고 가공성이 용이한 스테인레스 밀러판을 사용하는 것이 가장 이상적인 것으로서, 그 스테인레스 밀러판의 저면에 무늬부(13) 및 민무늬부(14)를 광고용 도안과 대응상으로 각각 형성하여 이에 의한 무늬의 전사를 통해 그 패드의 표면이 가공되게 하는 것이다.Here, the molding member 12 is the most ideal to use a stainless miller plate that is not deformable and easy to work, the pattern portion 13 and the flat pattern portion 14 on the bottom surface of the stainless miller plate for advertising design And the corresponding surface is formed so that the surface of the pad is processed by transferring the pattern.

또한, 상기한 성형부재(12)는 보다 다양한 질감 및 무늬의 표현을 가능케 하 기 위해, 부직포나 샌드페이퍼, 엠보싱 시트지, 직물, 목재 등을 이용할 수도 있는 것인데, 상기한 바와 같은 성형부재(12)는 연질이면서도 변형이 용이하므로 그 배면 즉, 상측면에 별도의 가압패널(15)을 부착하여 상기 적층 필름을 가압하면 되는 것이다.In addition, the molding member 12 may use a nonwoven fabric, sandpaper, embossed sheet paper, fabric, wood, etc. in order to enable the expression of a variety of textures and patterns, the molding member 12 as described above Since it is soft and easy to deform, a separate pressing panel 15 is attached to the rear surface, that is, the upper side, to press the laminated film.

이때, 상기와 같은 직물 및 시트지 등의 성형부재(12)에 무늬부(13) 및 민무늬부(14)를 형성하기 위해서는 전체면 중 광고용 도안에 해당하는 부분만을 절개 타공하여 이에 의한 민무늬부(14)가 형성되게 하면 되는 것이다.At this time, in order to form the pattern portion 13 and the plain pattern portion 14 in the molding member 12, such as the fabric and sheet paper as described above, only the portion corresponding to the advertising pattern of the entire surface cut and perforated by the patternless portion 14 ) Is formed.

이와 같이 상기한 성형부재(12)에 의해 하부몰드(11) 내에서 가압 열융착되어진 인쇄필름(3) 및 투명필름지(5)는 도 3e의 도시와 같이 상부면에 기재접착층(2)이 도포 형성된 베이스판(1)의 상측에 상기 인쇄필름(3)이 접착되도록 부착하면 완성되는 것이다.As described above, the substrate adhesive layer 2 is coated on the upper surface of the printing film 3 and the transparent film 5 which are pressurized and heat-sealed in the lower mold 11 by the molding member 12. The printing film 3 is attached to the upper side of the formed base plate 1 to be completed.

이때의 기재접착층(2)은 상기 베이스판(1)과 가압 상태의 인쇄필름(3)을 서로 부착시키기 위한 것으로서, 상기한 베이스판(1)은 연질 탄력재이므로 하부몰드(11) 내에서는 압착되지 못하므로 별도의 접착공정을 통해 부착시키는 것이며, 그 재질은 고무 또는 PVC 등의 합성수지재를 사용하여 1~3mm 정도의 두께를 갖게 하는 것이 바람직하다.At this time, the base material adhesive layer 2 is for attaching the base plate 1 and the printing film 3 in a pressurized state to each other. Since the base plate 1 is a soft elastic material, it is crimped in the lower mold 11. Since it is not possible to attach through a separate bonding process, the material is preferably to have a thickness of about 1 ~ 3mm using a synthetic resin material such as rubber or PVC.

이와 같은 후접착공정이 마무리되면 제품이 완성되는 것이며, 이후 도 3f의 도시와 같이 최상측의 이형박리지(10)를 제거하면 실제 사용할 수 있는 제품이 되는 것이며, 그 이형박리지(10)의 하부에는 하드코팅층(7)이 견고하게 형성되어 있 으므로 그 내구성 및 내화학성 등이 뛰어나게 되는 것이다.When the post-adhesion process is completed, the product is completed, and then, as shown in FIG. 3F, the upper release mold release 10 is removed to become a product that can be used in practice. Since the hard coating layer 7 is formed firmly on the lower end is excellent in durability and chemical resistance.

특히, 상기한 전사용 투명잉크층(6)은 전기한 열융착과정에서 상기 하드코팅층(6)과 섞이면서 별도의 구분층이 형성되지 아니하고 하드코팅층(7)으로 흡수 소멸되는 특징을 갖게 된다.In particular, the transfer transparent ink layer 6 is characterized in that it is absorbed and extinguished into the hard coating layer 7 without forming a separate partition layer while being mixed with the hard coating layer 6 in the aforementioned heat fusion process.

따라서, 도 3g의 도시와 같이 완성된 광고용 패드의 단면은 그 하측으로부터 베이스판(1), 박막의 기재접착층(2), 광고용 도안이 표면에 형성된 인쇄필름(3), 박막의 필름접착층(4), 광고 도안에 따라 광택부(8)와 무광처리부(9)가 형성된 투명필름지(5), 하드코팅층(7)이 순차적으로 적층되어 형성되는 것이다.Therefore, the cross section of the completed advertising pads as shown in Fig. 3G is formed from the base plate 1, the base material adhesive layer 2 of the thin film, the print film 3 having the advertising design on the surface, and the film adhesive layer 4 of the thin film. ), The transparent film 5 and the hard coating layer 7 having the gloss 8 and the matte treatment 9 formed thereon are sequentially stacked.

그러므로, 상기한 광택부(8)에 의해 인쇄필름(3)의 광고도안 등이 선명하게 투시되므로 패드 본래의 목적을 충실하게 달성할 수 있는 것이며, 그 이외의 부분에는 무광처리부(9)에 의해 고급스러운 심미감 및 부드럽고 다양한 질감의 표현이 연출되는 것이다.Therefore, since the advertisement pattern of the printing film 3 is clearly displayed by the gloss portion 8 described above, the original purpose of the pad can be faithfully achieved, and the matte processing portion 9 is provided in other portions. High quality aesthetics and soft and varied textures are expressed.

또한, 도 4 내지 도 5의 도시와 같이 상기한 성형부재(12)를 형성함에 있어, 도 4의 도시와 같은 스테인레스 밀러판을 사용하는 경우 광고용 도안의 형상에 따라 그 하부면에 다양한 형태의 무늬부(14)와 민무늬부(14)를 함께 형성하여 이에 의해 필름지를 가압하면 그 무늬부(14)의 무늬 모양이 그대로 전사되는 것이며,In addition, in forming the forming member 12 as shown in Figures 4 to 5, in the case of using a stainless miller plate as shown in Figure 4 according to the shape of the advertising design pattern of various forms on the lower surface When the portion 14 and the flat pattern portion 14 are formed together and the film is pressed by this, the pattern of the pattern portion 14 is transferred as it is,

도 5의 도시와 같이 부직포 또는 샌드페이퍼, 직물, 엠보싱 시트지, 나무 등을 이용할 경우에는 이들 성형부재(12)가 연질이면서 변형이 용이하므로 이때에는 별도의 가압패널(15)의 저면에 상기한 성형부재(12)를 부착한 후, 광고용 도안과 대응형상으로 이들을 절개하여 천공함으로서, 미절개부는 무늬부(13)가 되는 것이 며, 절개 천공부는 민무늬부(14)로 각각 형성되어 이들을 이용한 보다 다양한 질감의 표현 및 표면처리가 가능한 것이다.In the case of using a non-woven fabric or sandpaper, fabric, embossed sheet, wood, etc. as shown in Figure 5, since these molding members 12 are soft and easy to deform, the molding members described above on the bottom of the separate pressure panel 15 After attaching (12), perforating them by cutting them in the shape of an advertisement pattern and corresponding shape, the uncut portion becomes a pattern portion 13, and the cut portion is formed of a plain pattern portion 14, respectively, and more diverse textures using them Expression and surface treatment is possible.

또한, 상기한 바와 같은 실시예에서는 인쇄필름(3)에 형성된 광고용 도안을 민무늬부(14)에 의한 광택부(8)로 표현되게 하였으나, 반대로 상기한 광고용 도안부분만을 무광처리부(9)로 형성하여 그 나머지 부분을 광택부(8)로 처리하여 구매자나 소비자의 관심도를 증폭시킬 수도 있는 것이며, 이들을 적절한 형태로 혼용하여 사용할 수도 있는 것이다.In addition, in the above-described embodiment, the commercial pattern formed on the printing film 3 is represented by the glossy part 8 by the flat pattern part 14, but, on the contrary, only the commercial pattern part is formed of the matte processing part 9. The remaining portion may be treated with the gloss unit 8 to amplify the interest of the buyer or the consumer, and may be used by mixing them in an appropriate form.

이상과 같은 본 발명 무광택표면과 광택표면을 함께 갖는 광고용 패드 및 그 제조방법은, 투명의 선명한 투시가 가능한 광택표면에 의해 그 광고효과를 가일층 향상시키면서도, 광고도안 이외의 부분에는 엠보싱 처리된 무광택 표면 및 하드코팅층에 의해 긁힘이나 눌림, 스크레치, 칼자국 등으로부터 보다 내구성이 뛰어나게 하여 사용수명을 연장시키면서도 보다 고급스러운 질감 및 심미감을 함께 제공하므로 매우 뛰어난 효과를 갖는 것이다.The above-described advertising pad having a matte surface and a glossy surface together with a manufacturing method thereof has a matte surface embossed to a portion other than an advertisement design while further enhancing the advertising effect by a glossy surface that is transparent and transparent. And by the hard coating layer is more durable from scratches, crushing, scratches, cuts and the like to provide a more luxurious texture and aesthetics while extending the service life is to have a very excellent effect.

Claims (4)

이형박리지(10)의 표면에 하드코팅층(7)과 전사용 투명잉크층(6)을 순차적으로 형성하고,The hard coating layer 7 and the transfer transparent ink layer 6 are sequentially formed on the surface of the release paper 10, 별도의 인쇄필름(3)의 상측에는 필름접착층(4)을 이용하여 투명필름지(5)를 부착한 후 이를 별도의 하부몰드(11) 내에 삽입시키고,The transparent film sheet 5 is attached to the upper side of the separate printing film 3 by using the film adhesive layer 4 and then inserted into the separate lower mold 11, 상기 투명필름지(5)의 상측에는 상기 전사용 투명잉크층(6)이 서로 맞닿도록 상기 이형박리지(10)를 적층시켜,On the upper side of the transparent film 5, the release film 10 is laminated so that the transfer transparent ink layer 6 abuts each other, 이를 별도의 성형부재(12)를 이용하여 가압 열융착시키되,This is pressurized heat fusion using a separate molding member 12, 상기 성형부재(12)의 저면에는, 인쇄필름(3)의 도안 이외부분과 대응되는 무늬부(13)와 상기 인쇄필름(3)의 도안과 일치하는 민무늬부(14)를 각각 형성하여, 상기 성형부재(12)의 가압에 의해 그 무늬부(13) 만이 상기 투명필름지(5)에 전사되게 하고,On the bottom of the molding member 12, a pattern portion 13 corresponding to a portion other than the pattern of the printing film 3 and a plain pattern portion 14 corresponding to the pattern of the printing film 3 are formed, respectively, By pressing the molding member 12, only the pattern portion 13 is transferred to the transparent film sheet 5, 열압착된 인쇄필름(3)은 상부면에 기재접착층(2)이 형성된 베이스판(1)의 상측에 부착 형성하여, 상기 기재접착층(2)이 경화되면 최상측에 위치한 이형박리지(10)를 제거하여 하드코팅층(7)이 패드의 최상측 표면이 되도록 제조하여 이루어지는 무광택표면과 광택표면을 함께 갖는 광고용 패드의 제조방법에 있어서,The thermally compressed printing film 3 is attached to the upper side of the base plate 1 on which the base adhesive layer 2 is formed on the upper surface thereof, and when the base adhesive layer 2 is cured, the release film 10 positioned at the uppermost side thereof is hardened. In the method of manufacturing an advertising pad having a matte surface and a glossy surface made by removing the hard coating layer 7 to be the uppermost surface of the pad, 성형부재(12)를 스테인레스 밀러판을 이용하되, 그 스테인레스 밀러판의 저면에는 요철상의 무늬부(13)와 광택표면상의 민무늬부(14)가 인쇄필름(3)의 도안과 대응상으로 형성함을 특징으로 하는 무광택표면과 광택표면을 함께 갖는 광고용 패드의 제조방법.The molding member 12 is made of a stainless miller plate, and the bottom surface of the stainless miller plate is formed with a concave-convex pattern part 13 and a flat surface part 14 on a glossy surface in correspondence with the drawing of the printing film 3. Method for producing an advertising pad having a matte surface and a glossy surface characterized in that. 제 1항에 있어서,The method of claim 1, 성형부재(12)를 부직포 또는 샌드페이퍼, 직물, 목재, 엠보싱 시트지 중 어느 하나를 사용하되, 상기 성형부재(12)의 상측에는 별도의 가압패널(15)를 부착하고, 이들 성형부재(12)에는 상기 인쇄필름(4)의 도안과 대응상의 크기를 갖는 절개 관통상의 민무늬부(14)를 형성함을 특징으로 하는 무광택표면과 광택표면을 함께 갖는 광고용 패드의 제조방법.The molding member 12 may be made of any one of nonwoven fabric or sandpaper, fabric, wood, and embossed sheet paper, and a separate pressing panel 15 may be attached to the upper side of the molding member 12, and the molding member 12 may be attached to the molding member 12. A method of manufacturing an advertising pad having a matte surface and a glossy surface, characterized in that to form a cut-through flat pattern portion 14 having a size corresponding to the pattern of the printing film 4. 삭제delete 삭제delete
KR1020050086175A 2005-09-15 2005-09-15 Pad for advertisement having gloss and non-gloss surface KR100623073B1 (en)