KR100618142B1 - Painting plates manufacturing method - Google Patents

Painting plates manufacturing method Download PDF

Info

Publication number
KR100618142B1
KR100618142B1 KR1020040063284A KR20040063284A KR100618142B1 KR 100618142 B1 KR100618142 B1 KR 100618142B1 KR 1020040063284 A KR1020040063284 A KR 1020040063284A KR 20040063284 A KR20040063284 A KR 20040063284A KR 100618142 B1 KR100618142 B1 KR 100618142B1
Authority
KR
South Korea
Prior art keywords
paint
base
finishing
coating
finish
Prior art date
Application number
KR1020040063284A
Other languages
Korean (ko)
Other versions
KR20050016231A (en
Inventor
시라가키노부키
카네마츠카츠히코
Original Assignee
닛테쓰 고한 가부시키가이샤
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 닛테쓰 고한 가부시키가이샤 filed Critical 닛테쓰 고한 가부시키가이샤
Publication of KR20050016231A publication Critical patent/KR20050016231A/en
Application granted granted Critical
Publication of KR100618142B1 publication Critical patent/KR100618142B1/en

Abstract

[과제] 완만하게 색조가 변화하는 모양을 용이하게 형성할 수 있는 도장판의 제조 방법을 제공한다.[Problem] Provided is a method for producing a coated plate that can easily form a pattern in which the color tone gradually changes.

[해결 수단] 베이스 도료(1)를 금속 기판(2)의 표면에 도포하고, 그 베이스 도료(1)의 도포면에 복수 색상의 마무리 도료(3)를 스프레이 도포하는 도장판의 제조 방법에 관한 것이다. 베이스 도료(1)와 동일한 색상인 마무리 도료(3a)와 베이스 도료(1)와 이색인 마무리 도료(3b, 3c)가 부분적으로 겹쳐지도록 도포한다. 베이스 도료(1)와 동일한 색상인 마무리 도료(3a)와 베이스 도료(1)와 이색인 마무리 도료(3b, 3c)를 겹쳐지도록 도포함으로써, 베이스 도료(1)와 동일한 색상인 마무리 도료(3a)와 베이스 도료(1)와 이색인 마무리 도료(3b, 3c)를 혼재시킨 부분을 형성할 수 있다. 마무리 도료(3a, 3b, 3c)를 혼재시킨 부분에 의해 베이스 도료(1)와 이색인 마무리 도료(3b, 3c)와 베이스 도료(1)의 경계가 눈에 잘 띄지 않게 된다.RESOLUTION This invention relates to the manufacturing method of the coating plate which apply | coats the base paint 1 to the surface of the metal substrate 2, and spray-coats the finishing paint 3 of several colors to the application surface of the base paint 1. . The coating material 3a, which is the same color as the base coating 1, and the base coating 1, and the dichroic finishing paints 3b, 3c are applied so as to partially overlap each other. The finishing paint 3a having the same color as the base coating 1 is applied by applying the finishing paint 3a having the same color as that of the base paint 1 and the finishing paint 3b, 3c having a different color to overlap. And the base paint 1 and the dichroic finish paints 3b and 3c may be mixed. The portion where the finish paints 3a, 3b, and 3c are mixed causes the boundary between the base paint 1 and the dichroic finish paints 3b and 3c and the base paint 1 to be inconspicuous.

도장판, 도료, 혼재Paint, Paint, Mixed

Description

도장판의 제조 방법{Painting plates manufacturing method}Painting plate manufacturing method

도1은 본 발명의 실시 형태의 일 예를 도시한 개략도이다.1 is a schematic diagram showing an example of an embodiment of the present invention.

도2는 본 발명에 따른 도장 상태를 도시한 개략도이다.2 is a schematic view showing a painting state according to the present invention.

도3은 본 발명에 따른 건재의 일 예를 도시한 사시도이다.Figure 3 is a perspective view showing an example of the building material according to the present invention.

도4는 본 발명의 다른 실시 형태의 일 예를 도시한 개략도이다.4 is a schematic view showing an example of another embodiment of the present invention.

도5는 본 발명의 다른 실시 형태의 일 예를 도시한 것으로, 스프레이 건의 배치상태를 나타낸 개략도이다.5 shows an example of another embodiment of the present invention, and is a schematic diagram showing an arrangement of the spray gun.

도 6은 본 발명의 스프레이 건의 분사 반복 패턴의 일 예를 도시한 설명도이다.6 is an explanatory view showing an example of a spray repeating pattern of the spray gun of the present invention.

도 7은 본 발명에 따른 건재의 일 예를 도시한 사진의 복사물이다.Figure 7 is a copy of the photograph showing an example of building materials according to the present invention.

본 발명은 지붕재나 벽재 등의 건재로 이용되는 도장판의 제조 방법에 관한 것으로, 특히 다채롭고 높은 의장성을 갖는 도장판을 제조할 때에 이용되는 것이다.This invention relates to the manufacturing method of the coating plate used for building materials, such as a roofing material and a wall material, and is used especially when manufacturing the coating plate which has colorful and high designability.

종래에 속도 10m/분 이상으로 이동하는 띠형의 피도장물에 2색 이상의 도료 를 스프레이 도장함으로써, 다채(多彩) 모양의 도막을 형성하였다(예를 들면, 특허문헌 1 참조). 특허문헌 1에 기재되어 있는 도장 방법에서는 적어도 2개 이상의 도료 토출 노즐로부터 적어도 2색 이상의 서로 다른 도색의 도료를 토출시키고, 이를 통해 각 도료 토출 노즐로부터 토출된 도료가 혼재하는 복색 스프레이 패턴을 형성하고 있다.Conventionally, various coating films were formed by spray-coating two or more colors of coatings on a strip-shaped workpiece moving at a speed of 10 m / min or more (see Patent Document 1, for example). In the coating method described in Patent Document 1, at least two or more colors of paint are discharged from at least two or more paint discharge nozzles, thereby forming a multi-color spray pattern in which the paints discharged from each of the paint discharge nozzles are mixed. have.

그러나, 상기 도장 방법에서는 피도장물의 표면색과 스프레이 도장한 도료 색의 색조 차이가 비교적 크면, 피도장물의 표면과 스프레이 도장한 도료와의 경계가 눈에 띄게 나타나므로, 완만하게 색조가 변화하는 모양, 예를 들면 요변조(窯變調)의 양기와(모니엘와(monier® roof tiles))와 같은 모양을 도장으로 형성하는 것이 어려웠다.However, in the coating method, if the color tone difference between the surface color of the coating material and the sprayed paint color is relatively large, the boundary between the surface of the coating material and the spray-coated paint appears conspicuously, so that the shape of the color tone gradually changes, For example, it was difficult to form shapes such as pottery tiles (monier ® roof tiles) with paint.

[특허문헌 1] 일본 특허 공개 2003-135998호 공보(특허 청구 범위 등)[Patent Document 1] Japanese Unexamined Patent Publication No. 2003-135998 (claims, etc.)

본 발명은 상기 점에 비추어 이루어진 것으로, 완만하게 색조가 변화하는 모양을 용이하게 형성할 수 있는 도장판의 제조 방법을 제공하는 것을 목적으로 하는 것이다.This invention is made | formed in view of the said point, Comprising: It aims at providing the manufacturing method of the coating plate which can easily form the shape which changes a hue lightly.

본 발명은 베이스 도료(1)를 금속 기판(2)의 표면에 도포하고, 그 금속 기판(2)의 베이스 도료(1)의 도포면에 복수 색상의 마무리 도료(3)를 스프레이 도포하는 도장판의 제조 방법에 사용된다. 그리고, 본 발명의 특징은 베이스 도료(1)와 동일한 색상인 마무리 도료(3a)와 베이스 도료(1)와 이색인 마무리 도료(3b, 3c)가 부분적으로 겹쳐지도록 이들 마무리 도료(3a, 3b 3c)를 상기 금속 기판(2)의 베이스 도료(1)의 도포면에 도포하는 것에 있다. The present invention applies a base paint (1) to the surface of the metal substrate 2, the coating plate for spray coating the finishing paint (3) of a plurality of colors on the coating surface of the base paint (1) of the metal substrate (2) Used in the manufacturing method. Further, the characteristics of the present invention are that the finishing paints 3a, 3b and 3c, which are the same color as the base paint 1, and the base paints 1 and the finishing paints 3b and 3c, which are different colors, partially overlap. ) Is applied to the coated surface of the base paint 1 of the metal substrate (2).                         

본 발명에 따르면, 베이스 도료(1)와 동일한 색상인 마무리 도료(3a)와 베이스 도료(1)와 이색인 마무리 도료(3b, 3c)가 겹쳐지도록 도포함으로써, 베이스 도료(1)와 동일한 색상인 마무리 도료(3a)와 베이스 도료(1)와 이색인 마무리 도료(3b, 3c)를 혼재시킨 부분을 형성할 수 있다. 이 마무리 도료(3a, 3b, 3c)를 혼재시킨 부분에 의해 베이스 도료(1)와 이색인 마무리 도료(3b, 3c)와 베이스 도료(1)의 경계가 눈에 잘 띄지 않게 되므로, 색조가 완만하게 변화하는 모양을 용이하게 형성할 수 있다.According to the present invention, the finish paint 3a, which is the same color as the base paint 1, and the base paint 1 and the finish paints 3b, 3c, which are different colors, are applied so that they are overlapped with each other. The part which mixed the finish paint 3a, the base paint 1, and the dichroic finish paints 3b and 3c can be formed. Since the part which mixed these finishing paints 3a, 3b, and 3c was mixed, the boundary between the base paint 1, the dichroic finishing paints 3b, 3c, and the base paint 1 becomes less visible, so that the hue is smooth. It is possible to easily form the shape changing.

또한, 본 발명에서는 베이스 도료(1)를 희석하여 베이스 도료(1)와 동일한 색상인 마무리 도료(3a)를 조제하는 것이 바람직하다. 이 경우, 베이스 도료(1)를 이용하여 그와 동일한 색상의 마무리 도료(3a)를 조제할 수 있으므로, 마무리 도료(3a) 조제의 수고를 저감시킬 수 있는 동시에 베이스 도료(1)와 마무리 도료(3a)의 색상 차이의 발생을 적게 할 수 있다.In the present invention, it is preferable to dilute the base paint 1 to prepare a finish paint 3a having the same color as the base paint 1. In this case, since the finishing paint 3a of the same color can be prepared using the base paint 1, the trouble of preparation of the finishing paint 3a can be reduced, and the base paint 1 and the finishing paint ( The occurrence of the color difference in 3a) can be reduced.

또한, 본 발명에서는 복수 색상의 마무리 도료(3)로부터 분사해야 할 마무리 도료를 경시적으로 전환하고, 그 전환된 마무리 도료를 스프레이 건(4)을 통해 상기 금속 기판(2)에 분사하는 것이 바람직하다. 이 경우, 복수 색상의 마무리 도료(3)를 도포할 때에 하나의 스프레이 건(4)을 겸용할 수 있으므로, 복수 색상의 마무리 도료(3) 각각에 대응하는 스프레이 건(4)을 이용하는 경우에 비해 스프레이 건(4)의 갯수를 적게 할 수 있다.In addition, in the present invention, it is preferable to switch over time the finish paint to be sprayed from the finish paint 3 of a plurality of colors, and spray the converted finish paint on the metal substrate 2 through the spray gun 4. Do. In this case, since one spray gun 4 can also be used when applying the finishing paint 3 of several colors, compared with the case of using the spray gun 4 corresponding to each of the finishing paints 3 of multiple colors. The number of spray guns 4 can be reduced.

아울러, 본 발명에서는 베이스 도료 및 그와 동일한 색상인 마무리 도료의 색상을 라이트 오렌지로 하는 동시에 베이스 도료와 이색인 마무리 도료의 색상을 다크 오렌지와 베이지로 하는 것이 바람직하다. 이 경우, 요변조의 양기와(모니엘와)와 같은 색상 및 모양을 도장으로 용이하게 형성할 수 있다.In addition, in this invention, it is preferable to make the color of the base paint and the finishing paint which is the same color as light orange, and to set the color of the base paint and the bicolor finishing paint to dark orange and beige. In this case, the same color and shape as the fragrance of the thixotropic agent (Moniewa) can be easily formed by painting.

도1에 본 발명의 일 예를 도시한다. 이 예에서는 장척(長尺)의 금속 기판(2)을 길이 방향으로 진행(반송)시키면서 베이스 도료(1)와 마무리 도료(3)의 도포(도장)를 수행한다.1 shows an example of the present invention. In this example, coating (painting) of the base paint 1 and the finish paint 3 is performed while the long metal substrate 2 is advanced (transferred) in the longitudinal direction.

금속 기판(2)은 종래부터 건재를 형성하는 데에 이용되고 있는 것으로, 예를 들면 스테인리스 강판, 아연 도금 강판, 알루미늄-아연 도금 강판(갈바륨 강판) 등을 들 수 있는데, 이에 한정되는 것은 아니다. 또한, 이 금속 기판(2)의 표면에는 프라이머(Primer) 도장으로 하도(下塗) 도장을 실시할 수 있다.The metal substrate 2 is conventionally used for forming a building material, for example, a stainless steel sheet, a galvanized steel sheet, an aluminum-zinc plated steel sheet (galvalume steel sheet), etc. are not limited to this. The surface of the metal substrate 2 can also be coated with primer coating by primer coating.

베이스 도료(1)는 종래부터 건재 등에 사용되고 있는 것으로, 금속 기판(2)에 내식, 내후, 내마모 등의 성능을 부여하기 위해 도장되는 것이다. 이와 같은 베이스 도장(1)으로는 폴리에스테르 수지 도료, 우레탄 수지 도료, 불화비닐리덴 수지 도료, 아크릴 수지 도료, 폴리올레핀 수지 도료 등을 각각 단독으로 혹은 2종류 이상을 혼합하여 사용할 수 있다. 또한, 베이스 도료(1)에는 안료가 배합되어 있는데, 이로 인해 베이스 도료(1)는 소망하는 색으로 착색되어 있다. 이 안료로는 각종 착색 안료, 방청 안료, 체질 안료(실리카, 알루미나, 탄산칼슘, 황산바륨, 카올린 크레이 탤크 등)를 예시할 수 있는데, 이들에 한정되는 것은 아니다. 안료는 착색성이나 도료중의 수지와의 밀착성 향상, 베이스의 은폐성 등을 고려하여 배합할 수 있다. 아울러 베이스 도료(1)로는, 예를 들면 일본 특허 공개 2002-146280호 공보에 개시되어 있는 바와 같은 축성(縮性) 도료(축성이 있는 도료로 광택 소거의 효과가 있는 도료)를 이용할 수 있다.The base paint 1 is conventionally used for building materials and the like, and is coated in order to provide the metal substrate 2 with performances such as corrosion resistance, weather resistance, and wear resistance. As such base coating 1, polyester resin paint, urethane resin paint, vinylidene fluoride resin paint, acrylic resin paint, polyolefin resin paint, etc. can be used individually or in mixture of 2 or more types, respectively. Moreover, although the pigment is mix | blended with the base paint 1, the base paint 1 is colored by the desired color by this. Examples of the pigment include various color pigments, rust preventive pigments, and extender pigments (silica, alumina, calcium carbonate, barium sulfate, kaolin cratalc, etc.), but are not limited thereto. A pigment can be mix | blended in consideration of coloring property, adhesiveness improvement with resin in coating material, concealability of a base, etc. As the base paint 1, for example, a build-up paint (a paint having an effect of removing glossiness with a build-up paint) can be used as disclosed in JP-A-2002-146280.

또한, 베이스 도료(1)에는 광택 소거제나 흠 방지제 혹은 접착(앵커 효과)을 향상시킬 목적으로 골재를 배합할 수 있다. 골재로는 유리 섬유, 유리 비드, 수지 비드, 마이카 등을 예시할 수 있는데, 이들에 한정되는 것은 아니다. 아울러, 베이스 도료(1)에는 합성 미분 실리카, 유기벤트나이트, 카르복시메틸셀룰로오스, 폴리비닐알콜 등의 증점제, 멜라민계나 벤조구아나민계나 이소시아네이트계 등의 가교제, 폴리아크릴산 등의 분산제 등을 배합하여도 된다. 또한, 본 발명에 있어서 베이스 도료(1)의 점도는, 예를 들면 포드컵 No.4법에 의한 측정으로 30~120초로 하는 것이 바람직하지만, 이에 한정되는 것은 아니다.In addition, aggregate can be mix | blended with the base paint 1 for the purpose of improving a gloss scavenger, an anti-wound agent, or adhesiveness (anchor effect). Examples of the aggregate include glass fibers, glass beads, resin beads, mica, and the like, but are not limited thereto. In addition, the base paint 1 may be blended with a thickener such as synthetic finely divided silica, organic bentite, carboxymethyl cellulose, polyvinyl alcohol, crosslinking agents such as melamine-based, benzoguanamine-based or isocyanate-based, dispersing agents such as polyacrylic acid, and the like. . In addition, although the viscosity of the base coating material 1 is 30-120 second by the measurement by the pod cup No. 4 method in this invention, for example, it is not limited to this.

마무리 도료(3)로 베이스 도료(1)와 동일한 것을 사용할 수 있다. 즉, 마무리 도료(3)로 상기와 마찬가지로 폴리에스테르수지 도료 등의 각종 수지 도료에 안료나 골재 및 기타 성분을 배합한 것을 이용할 수 있다. 또한, 마무리 도료(3)로 서로 색이 다른 복수 색상의 마무리 도료(3a, 3b, 3c)를 이용한다. 여기서는 색상이 다른 3종류의 마무리 도료(3a, 3b, 3c)를 이용하는 경우에 대하여 설명하지만, 이에 한정되지 않으며, 마무리 도료(3)는 서로 다른 2종류이어도 되고, 4종류 이상이어도 된다. 그리고, 색이 다른 복수 색상의 마무리 도료(3a, 3b, 3c)중 1종류의 마무리 도료(3a)는 베이스 도료(1)와 동일 색상으로, 나머지 다른 마무리 도료(3b, 3c)는 베이스 도료(1)와 이색으로 각각 제조되어 있다. 이 경우, 베이스 도료(1)와 동일 색상의 마무리 도료(3a)는 베이스 도료(1)와 같은 안료를 사용하여 착색하고, 베이스 도료(1)와 이색의 마무리 도료(3b, 3c)는 베이스 도료(1)와 다른 안료를 사용하여 착색할 수 있다. 또한, 베이스 도료(1)와 동일 색상의 마무리 도료(3a)는 베이스 도료(1)를 적절한 무색의 용매로 희석하여 조제하는 것이 바람직하다. 이와 같이, 베이스 도료(1)를 이용하여 베이스 도료(1)와 동일 색상의 마무리 도료(3a)를 조제할 수 있으므로, 베이스 도료(1)와 마무리 도료(3a)를 따로 조제하는 경우에 비해 수고를 저감시킬 수 있는 동시에 베이스 도료(1)와 마무리 도료(3a)의 색상 차이가 잘 발생하지 않게 된다. 또한, 후술하는 바와 같이 베이스 도료(1)는 롤 코터로, 마무리 도료(3a)는 스프레이 건으로 각각 도장하므로, 베이스 도료(1)를 그대로 전용하여 마무리 도료(3a)로 하는 것보다 희석하여 점도를 저하시키는 쪽이 바람직하다. 본 발명에 있어서 마무리 도료(3)의 점도는, 예를 들면 포드컵 No.4법(JIS K 5400)에 의한 측정으로 15~45초로 하는 것이 바람직하지만, 이에 한정되는 것은 아니다.As the finish paint 3, the same paint as the base paint 1 can be used. That is, as the finish paint 3, a mixture of pigments, aggregates and other components with various resin paints such as polyester resin paints and the like can be used. In addition, as the finishing paint 3, the finishing paints 3a, 3b, and 3c of plural colors different from each other are used. Although the case where three types of finishing paints 3a, 3b, and 3c of which colors are different is demonstrated here, it is not limited to this, Two types of finishing paints 3 may differ, and four or more types may be sufficient as it. One of the finish paints 3a of the plurality of finish paints 3a, 3b, and 3c having different colors is the same color as the base paint 1, and the other finish paints 3b and 3c are the base paints ( 1) and dichroic, respectively. In this case, the finish paint 3a of the same color as the base paint 1 is colored using the same pigment as the base paint 1, and the base paint 1 and the dichroic finish paints 3b and 3c are the base paint. A pigment different from (1) can be used for coloring. Moreover, it is preferable to dilute and prepare the base paint 1 by the appropriate colorless solvent for the finishing paint 3a of the same color as the base paint 1. In this way, since the base paint 1 can be used to prepare the finish paint 3a of the same color as the base paint 1, the base paint 1 and the finish paint 3a are compared with the case of separately preparing the paint. At the same time, the color difference between the base paint 1 and the finish paint 3a hardly occurs. As will be described later, the base paint 1 is coated with a roll coater, and the finish paint 3a is coated with a spray gun, respectively, so that the base paint 1 is used as it is and is diluted with the finish paint 3a. It is preferable to reduce. In the present invention, the viscosity of the finish coating material 3 is preferably set to 15 to 45 seconds, for example, by measurement by the Pod Cup No. 4 method (JIS K 5400), but is not limited thereto.

도1에 도시된 본 발명에서 이용하는 도장 장치는, 도장 부스(10)에 하나의 스프레이 건(4)을 설치하여 형성되어 있다. 스프레이 건(4)으로는, 예를 들면 에어 펌프(14)로부터 공급되는 공기를 이용하여 마무리 도료(3)를 분사할 수 있는 것을 이용할 수 있다. 이 스프레이 건(4)에는 복수(3개)의 배관(11a, 11b, 11c)의 일단이 접속되어 있는 동시에 배관(11a, 11b, 11c)의 타단은 마무리 도료(3a, 3b, 3c)를 각각 저장하고 있는 도료 탱크(12a, 12b, 12c)에 접속되어 있다. 또한, 상기 각 배관(11a, 11b, 11c)의 도중에는 전자 밸브 등의 밸브(13a, 13b, 13c)가 설치되어 있다. 이들 밸브(13a, 13b, 13c)는 컴퓨터 등으로 구성되는 제어 장치(16)에 의해 개폐 제어되는 것이다. 또한, 밸브(13a, 13b, 13c)보다 상류측(도료 탱크(12a, 12b, 12c)측)의 각 배관(11a, 11b, 11c)의 도중에는 펌프(15a, 15b, 15c)가 설치되어 있다. 아울러, 도장 장치에는 롤 코터(17) 및 건조로(18)가 구비되어 있다.The coating device used in the present invention shown in FIG. 1 is formed by providing one spray gun 4 in the painting booth 10. As the spray gun 4, the thing which can inject the finishing paint 3 using the air supplied from the air pump 14, for example can be used. One end of plural (three) pipes 11a, 11b, 11c is connected to the spray gun 4, and the other ends of the pipes 11a, 11b, 11c are finished paints 3a, 3b, 3c, respectively. It is connected to the paint tank 12a, 12b, 12c stored. Moreover, valve | bulb 13a, 13b, 13c, such as a solenoid valve, is provided in the middle of each said piping 11a, 11b, 11c. These valves 13a, 13b, 13c are controlled to be opened and closed by the control device 16 constituted by a computer or the like. Further, pumps 15a, 15b, and 15c are provided in the middle of the pipes 11a, 11b, and 11c on the upstream side (paint tanks 12a, 12b, and 12c) than the valves 13a, 13b, and 13c. In addition, the coating apparatus is equipped with the roll coater 17 and the drying furnace 18. As shown in FIG.

상기와 같은 도장 장치를 이용하여 장척의 띠형 금속 기판(2)에 연속적으로 도장을 실시하는 경우에 다음과 같이 수행한다. 먼저, 금속 기판(2)을 연직 상향으로 반송(진행)시키면서 롤 코터(17)를 통해 베이스 도료(1)를 금속 기판(2)의 표면(한쪽 면)에 도포한다. 그 후, 금속 기판(2)의 베이스 도료(1)의 도장면을 상향으로 하여 대략 수평으로 반송되도록 금속 기판(2)의 반송 방향을 반송 롤(20)을 통해 전환시킨다. 그 후, 금속 기판(2)을 대략 수평으로 반송시키면서 도장 부스(10)를 통과시키되, 금속 기판(2)의 베이스 도료(1)의 도장면에 마무리 도료(3)를 거듭 스프레이 건(4)으로 분사하여 스프레이 도포한다. 마무리 도료(3)의 스프레이에 의한 도포 패턴은 평면에서 보는 경우에 원형 혹은 타원형 등으로 할 수 있다. 그 이후, 금속 기판(2)을 건조로(18)에 도입하여 금속 기판(2)에 도장된 베이스 도료(1) 및 마무리 도료(3)를 건조시킨다. 이와 같이 하여 금속 기판(2)에 베이스 도료(1) 및 마무리 도료(3)를 도장할 수 있다. 또한, 금속 기판(2)에 형성되는 베이스 도료(1)나 마무리 도료(3)의 도막은 10~30㎛로 하는 것이 바람직하지만, 이에 한정되는 것은 아니다. 또한, 마무리 도료(3)의 스프레이 조건은 무화압(霧化壓) 0.1~0.3MPa, 패턴압 0.1~0.3MPa, 토출량 100~500밀리리터/분 등으로 할 수 있지만, 이에 한정되는 것은 아니다. 아울러, 라인 스피드(금속 기판(2)의 반송 속도)는 30~120m/분, 건조로(18)에서의 건조 온도는 180~250℃, 건조 시간 20~100초 등으로 할 수 있지만, 이에 한정되는 것은 아니다.In the case where coating is continuously performed on the elongated strip-shaped metal substrate 2 using the coating device as described above, it is performed as follows. First, the base paint 1 is applied to the surface (one side) of the metal substrate 2 via the roll coater 17 while conveying (advancing) the metal substrate 2 vertically upward. Then, the conveyance direction of the metal substrate 2 is switched through the conveyance roll 20 so that the coating surface of the base coating material 1 of the metal substrate 2 may be upward and conveyed substantially horizontally. Thereafter, the coating booth 10 is passed while the metal substrate 2 is substantially horizontally conveyed, and the finishing paint 3 is repeatedly applied to the coating surface of the base paint 1 of the metal substrate 2. Spray by spraying. The application pattern by the spray of the finishing paint 3 can be circular, elliptical, etc. when it sees from a plane. Thereafter, the metal substrate 2 is introduced into the drying furnace 18 to dry the base paint 1 and the finish paint 3 coated on the metal substrate 2. In this way, the base coating 1 and the finishing coating 3 can be coated on the metal substrate 2. Moreover, although it is preferable to set the coating film of the base paint 1 and the finishing paint 3 formed in the metal substrate 2 to 10-30 micrometers, it is not limited to this. In addition, although the spray conditions of the finish coating material 3 can be made into 0.1-0.3 Mpa of atomization pressures, 0.1-0.3 Mpa of pattern pressures, 100-500 milliliters / minute of discharge amount, etc., it is not limited to this. In addition, although the line speed (the conveyance speed of the metal substrate 2) can be 30-120 m / min, the drying temperature in the drying furnace 18 can be 180-250 degreeC, 20-100 seconds of drying time, etc., it is limited to this. It doesn't happen.

본 발명은 상기와 같이 마무리 도료(3)를 스프레이 도포함에 있어서, 제어 장치(116)에 설정된 타임 스케줄에 따라 스프레이 건(4)으로부터 분사되는 마무리 도료(3a, 3b, 3c)의 종류를 경시적으로 순차 전환시키면서 수행한다. 예를 들면, 스프레이 건(4)으로 마무리 도료(3a)를 분사하는 경우에는 제어 장치(16)를 통해 밸브(13a)를 개방 동작, 다른 밸브(13b, 13c)를 폐쇄 동작하도록 제어하고, 펌프(15a)의 작용으로 도료 탱크(12a)로부터 배관(11a)을 통해 마무리 도료(3a)가 스프레이 건(4)으로 공급된다. 따라서, 에어 펌프(14)의 작용에 의해 스프레이 건(4)에서 마무리 도료(3a)가 분사된다. 또한, 스프레이 건(4)으로 마무리 도료(3b)를 분사하는 경우에도 상기와 동일하게 하여 수행할 수 있다. 즉, 제어 장치(16)를 통해 밸브(13b)를 개방 동작, 다른 밸브(13a, 13c)을 폐쇄 동작하고, 펌프(15b)로 도료 탱크(12b)로부터 배관(11b)을 통해 마무리 도료(3b)를 스프레이 건(4)에 공급하며, 에어 펌프(14)를 통해 스프레이 건(4)으로부터 마무리 도료(3b)를 분사한다. 또한, 스프레이 건(4)으로 마무리 도료(3c)를 분사하는 경우에도 상기와 동일하게 하여 수행할 수 있는데, 제어 장치(16)를 통해 밸브(13c)를 개방 동작, 다른 밸브(13a, 13b)를 폐쇄 동작하고, 펌프(15c)로 도료 탱크(12c)로부터 배관(11c)을 통해 마무리 도료(3c)를 스프레이 건(4)에 공급한 후, 에어 펌프(14)를 통해 스프레이 건(4)으로부터 마무리 도료(3c)를 분사한다.In the present invention, the spray coating of the finish paint (3) as described above, the type of the finish paint (3a, 3b, 3c) sprayed from the spray gun 4 in accordance with the time schedule set in the control device 116 over time Sequential transition to For example, in the case of spraying the finish paint 3a with the spray gun 4, the control device 16 controls the valve 13a to open, and the other valves 13b and 13c to close. Under the action of 15a, the finish paint 3a is supplied from the paint tank 12a to the spray gun 4 through the pipe 11a. Therefore, the finishing paint 3a is sprayed from the spray gun 4 by the action of the air pump 14. In addition, when spraying the finishing paint 3b with the spray gun 4, it can carry out similarly to the above. That is, the valve 13b is opened through the control device 16 and the other valves 13a and 13c are closed, and the finishing paint 3b is passed through the pipe 11b from the paint tank 12b with the pump 15b. ) Is supplied to the spray gun 4, and the finish paint 3b is sprayed from the spray gun 4 through the air pump 14. In addition, when spraying the finishing paint 3c with the spray gun 4, it can carry out similarly to the above, The valve 13c is opened by the control apparatus 16, and other valves 13a and 13b are performed. To the spray gun 4 through the pipe 11c from the paint tank 12c with the pump 15c to the spray gun 4 and then to the spray gun 4 through the air pump 14. The finishing paint 3c is sprayed from.

그리고, 본 발명에서는 마무리 도료(3)인 색이 다른 복수 색상의 마무리 도료(3a~3c)를 스프레이 도포할 때, 베이스 도료(1)와 동일한 색상인 마무리 도료 (3a)와 이에 인접하는 이색의 마무리 도료(3b, 3c)를 부분적으로 겹치도록 도포한다. 여기서, 베이스 도료(1)와 동일한 색상인 마무리 도료(3a)와 이색의 마무리 도료(3b, 3c)가 겹쳐지는 비율은 적절하게 설정 가능하지만, 베이스 도료(1)와 동일한 색상인 마무리 도료(3a)와 이와 인접하는 이색의 마무리 도료(3b, 3c)는 면적 환산(마무리 도료(3a~3c)가 서로 겹쳐지는 면적의 비율)으로 5~50% 겹쳐지도록 하는 것이 바람직하다. 이와 같은 겹쳐지는 부분이 형성되도록 마무리 도료(3a~3c)의 1회당 분사량 등의 스프레이 조건이나 라인 스프드 등이 조정된다. 그리고, 도2에 도시한 바와 같이, 상기 마무리 도료(3a~3c)의 겹쳐지는 부분(30)에서 베이스 도료(1)와 동일한 색상인 마무리 도료(3a)와 베이스 도료(1)와 이색인 마무리 도료(3b, 3c)를 얼룩과 같이 혼재시킨 부분을 형성할 수 있다. 이 혼재에 의해 베이스 도료(1)와 이색의 마무리 도료(3b, 3c)의 경계가 눈에 잘 띄지 않게 되므로, 색조가 완만하게 변화하는 모양을 마무리 도료(3a~3c)로 용이하게 형성할 수 있다.And in this invention, when spray-coating the finishing paints 3a-3c of several colors from which the color of the finishing paint 3 differs, the finishing paint 3a which is the same color as the base paint 1, and the dichroism adjacent to this The finishing paints 3b and 3c are applied so as to partially overlap. Here, the ratio at which the finish paint 3a, which is the same color as the base paint 1, and the finish paints 3b, 3c of the dichroic color, can be set appropriately, but the finish paint 3a, which is the same color as the base paint 1, can be set appropriately. ) And the dichroic finishing paints 3b and 3c adjacent thereto are preferably overlapped by 5 to 50% in terms of area conversion (ratio of areas where the finishing paints 3a to 3c overlap each other). Spray conditions such as the injection amount per finish of the finish paints 3a to 3c, line soup, and the like are adjusted so that such overlapping portions are formed. As shown in Fig. 2, in the overlapping portions 30 of the finish paints 3a to 3c, the finish paint 3a and the base paint 1, which are the same color as the base paint 1, are different from each other. The part which mixed paint 3b, 3c like a stain can be formed. This mixture makes the boundary between the base paint 1 and the dichroic finish paints 3b and 3c inconspicuous, making it possible to easily form a pattern in which the hue changes smoothly with the finish paints 3a to 3c. have.

상기와 같이 하여 제조된 도장판을 롤 성형 등의 굽힘 가공을 실시하거나 소정의 크기로 절단하거나 하여 금속 지붕재나 금속 벽재 등의 건재로 형성하는 것이다. 도3에 도시된 건재는 대략 파도형으로 형성한 가로 연결 지붕재(21)로, 그 상단에는 표면측으로 절곡 형성된 결합용 볼록부(22)가, 하단에는 이면측으로 절곡 형성된 결합용 오목부(23)가 각각 형성되어 있다. 그리고, 이 가로 연결 지붕재(21)는 금속 지붕재임에도 불구하고, 요변조의 양기와(모니엘와)와 같은 외관을 제공한다.The coating plate produced as described above is subjected to bending processing such as roll forming or cutting into a predetermined size to form a building material such as a metal roofing material or a metal walling material. The building material shown in FIG. 3 is a horizontally-connected roofing material 21 formed in a substantially wave shape, and a coupling convex portion 22 bent to the front side at the upper end thereof, and a coupling recess 23 bent to the back side at the lower end thereof. Are formed respectively. And although this horizontal connecting roofing material 21 is a metal roofing material, it provides the external appearance like the fragrance | waist timber (Moniewa).

본 발명에서는 상기와 같이 스프레이 건(4)이 하나인 도장 장치를 이용하지만, 도4에 도시한 바와 같이 2개의 스프레이 건(4)을 구비한 도장 장치를 이용하여 도 된다. 이 경우, 하나의 스프레이 건(4)을 이용하는 도장 장치에 비해 스프레이 건(4)의 개수가 늘어 장치가 대규모화 될 우려가 있지만, 스프레이 도포를 효율적으로 수행할 수 있다는 이점을 갖는다. 또한, 도4에 도시한 도장 장치에서는 마무리 도료(3a, 3b)로 2종류가 이용되고 있지만, 이에 한정되는 것이 아니며, 상기와 마찬가지로 3종류 혹은 그 이상의 복수 색상의 마무리 도료(3)를 이용하여도 된다. 또한, 도4의 도장 장치에서는 스프레이 건(4)을 금속 기판(2)의 반송 방향과 거의 평행한 방향으로 나열하였지만, 이에 한정되지 않으며, 도5에 도시한 바와 같이 스프레이 건(4)을 금속 기판(2)의 반송 방향(화살표로 도시)과 거의 직교하는 방향으로 나열하여도 된다.In the present invention, a coating apparatus having one spray gun 4 is used as described above, but as shown in FIG. 4, a coating apparatus having two spray guns 4 may be used. In this case, the number of spray guns 4 is increased compared to the coating apparatus using one spray gun 4, which may increase the size of the apparatus, but has the advantage that spray application can be efficiently performed. In addition, in the coating apparatus shown in FIG. 4, although two types are used as finishing paints 3a and 3b, it is not limited to this, It is the same as the above, using the three or more color finishing paints 3, You may also In addition, although the spray gun 4 is arranged in the direction substantially parallel to the conveyance direction of the metal substrate 2 in the coating apparatus of FIG. 4, it is not limited to this, As shown in FIG. You may arrange | position in the direction substantially orthogonal to the conveyance direction (shown by the arrow) of the board | substrate 2. As shown in FIG.

[실시예]EXAMPLE

이하, 본 발명을 실시예에 의해 구체적으로 설명한다.Hereinafter, an Example demonstrates this invention concretely.

도1에 도시한 도장 장치를 이용하여 도장판을 제조하였다. 금속 기판(2)으로는 폭 914mm, 두께 0.35mm의 장척의 강판을 이용하였다.The coating plate was manufactured using the coating apparatus shown in FIG. As the metal substrate 2, a long steel plate having a width of 914 mm and a thickness of 0.35 mm was used.

베이스 도료(1)로는 폴리에스테르계 수지 도료(일본유지 BASF 코팅스(주)제의 "S03-G4651")에 안료를 배합하여 라이트 오렌지 색상으로 착색한 것을 이용하였다. 또한, 베이스 도료(1)의 점도(20℃)는 포드컵 No.4를 이용한 점도 측정에서 60초이었다.As the base paint (1), a pigment was blended with a polyester resin paint (" S03-G4651 " manufactured by Japan Oil & Chemicals BASF Coatings Co., Ltd.) and used to be colored in light orange color. In addition, the viscosity (20 degreeC) of the base coating material 1 was 60 second in the viscosity measurement using Pod Cup No.4.

베이스 도료(1)와 동일 색상인 마무리 도료(3a)로는 베이스 도료(1)를 시클로헥사논 및 솔벤트나프사를 주성분으로 하는 용매로 희석한 것을 이용하였다. 이 마무리 도료(3a)의 점도(20℃)는 포드컵 No.4를 이용한 점도 측정에서 30초이었다.As the finishing paint 3a having the same color as the base paint 1, the base paint 1 was diluted with a solvent containing cyclohexanone and solvent naphtha as main components. The viscosity (20 degreeC) of this finishing coating material 3a was 30 second in the viscosity measurement using Pod Cup No.4.

베이스 도료(1)와 이색의 마무리 도료(3b)로는 상기와 동일한 폴리에스테르계 수지 도료에 안료를 배합하여 다크 오렌지의 색상으로 착색한 것을 이용하였다. 또한, 상기와 동일한 용매를 배합하여 마무리 도료(3b)의 점도(20℃)를 포드컵 No.4를 이용한 점도 측정에서 30초로 하였다.As the base paint (1) and the dichroic finish paint (3b), a pigment was blended in the same polyester resin paint as described above and colored in a dark orange color. In addition, the same solvent was mix | blended and the viscosity (20 degreeC) of the finishing coating material 3b was made into 30 second by the viscosity measurement using Pod Cup No.4.

베이스 도료(1)와 이색의 마무리 도료(3c)로는 상기와 동일한 폴리에스테르계 수지 도료에 안료를 배합하여 베이지 색상으로 착색한 것을 이용하였다. 또한, 상기와 동일한 용매를 배합하여 마무리 도료(3c)의 점도(20℃)를 포드컵 No.3을 이용한 점도 측정에서 30초로 하였다.As the base paint (1) and the dichroic finish paint (3c), a pigment was mixed with the same polyester resin paint as described above and colored in beige. In addition, the same solvent was mix | blended and the viscosity (20 degreeC) of the finishing coating material 3c was made into 30 second by the viscosity measurement using Pod Cup No.3.

그리고, 금속 기판(2)을 라인 스피드 65m/분으로 반송하면서 베이스 도료(1) 및 마무리 도료(3a~3c)의 도포를 수행하였다. 여기서, 스프레이 조건으로는 무화압 0.20MPa, 패턴압 0.17MPa, 토출량 290밀리리터/분(각 색)으로 하였다. 또한, 스프레이 도장에 있어서의 스프레이 패턴은 마무리 도료(3a)를 0.15초간 분사 → 0.10초간 무분사 → 마무리 도료(3b)를 0.20초간 분사 → 0.10초간 무분사 → 마무리 도료(3c)를 0.20초간 분사 → 0.08초간 무분사 → 마무리 도료(3a)를 0.15초간 분사 → …의 순서로 반복하였다. 각 마무리 도료(3a~3c)의 분사(ON)와 무분사(OFF)의 반복 패턴을 도6에 도시하였다. 이와 같이 하여 베이스 도료(1)와 동일 색상의 마무리 도료(3a)와 이색의 마무리 도료(3b, 3c)가 부분적으로(면적 환산으로 20%) 겹쳐지도록 하였다. 또한, 스프레이 건으로는 아사히 사낙제 컬러 콤비건 "T2925"를 이용하였다. 다음에는 스프레이 도장 후의 금속 기판(2)을 건조로(18)로 도입하여 온도 230℃에서 50초간 건조시켜 베이스 도료(1)의 도막 두께가 18㎛, 마무리 도료(3a~3c)의 도막 두께가 5~10㎛인 도장판을 얻었다. 그 이후, 도장판을 롤 성형 등을 통해 굽힘 가공하는 동시에 소정의 길이로 절단하여 가로 연결 지붕재(21)를 형성하였다. 이 가로 연결 지붕재(21)는 색조가 완만하게 변화하는 모양을 갖는다(도7 참조).And the base coating 1 and the finishing coatings 3a-3c were apply | coated, conveying the metal substrate 2 at the line speed of 65 m / min. Here, as spray conditions, atomization pressure of 0.20 MPa, pattern pressure of 0.17 MPa, and discharge amount of 290 milliliters / minute (each color) were taken. In addition, the spray pattern in spray painting is spraying the finishing paint 3a for 0.15 seconds → no spraying for 0.10 seconds → spraying the finishing paint 3b for 0.20 seconds → no spraying for 0.10 seconds → spraying the finishing paint 3c for 0.20 seconds → No spraying for 0.08 sec. → Spraying the finishing paint 3a for 0.15 sec. Repeated in the order of. 6 shows a repeating pattern of injection (ON) and non-injection (OFF) of each of the finishing paints 3a to 3c. In this manner, the finish paint 3a of the same color as the base paint 1 and the finish paints 3b, 3c of different colors were partially overlapped (20% in area conversion). In addition, Asahi Sanak color combination "T2925" was used as a spray gun. Next, the metal substrate 2 after spray coating is introduced into the drying furnace 18 and dried at a temperature of 230 ° C. for 50 seconds, so that the coating thickness of the base coating 1 is 18 μm and the coating thickness of the finishing coatings 3a to 3c is obtained. The coating board of 5-10 micrometers was obtained. Thereafter, the paint plate was bent through roll forming or the like, and cut to a predetermined length to form a transverse connecting roofing material 21. This horizontally connected roofing material 21 has a shape in which the color tone changes gradually (see FIG. 7).

본 발명은 베이스 도료와 동일한 색상인 마무리 도료와 베이스 도료와 이색인 마무리 도료가 겹쳐지도록 도포함으로써, 베이스 도료와 동일한 색상인 마무리 도료와 베이스 도료와 이색인 마무리 도료를 혼재시킨 부분을 형성할 수 있다. 이 마무리 도료를 혼재시킨 부분에 의해 베이스 도료와 이색인 마무리 도료와 베이스 도료의 경계가 눈에 잘 띄지 않게 되므로, 색조가 완만하게 변화하는 모양을 용이하게 형성할 수 있다.The present invention can be formed by mixing the finish paint, which is the same color as the base paint, and the base paint, and the finish paint, which is the same color as the base paint, so that a portion of the finish paint, which is the same color as the base paint, and the base paint, and the dichroic finish paint are mixed. . The portion where the finish paint is mixed makes the boundary between the base paint, the dichroic finish paint, and the base paint hardly noticeable, so that a pattern in which the color tone gradually changes can be easily formed.

Claims (4)

베이스 도료를 금속 기판의 표면에 도포하고, 그 금속 기판의 베이스 도료의 도포면에 복수 색상의 마무리 도료를 스프레이 도포하는 도장판의 제조 방법에 있어서, In the manufacturing method of the coating plate which apply | coats a base paint to the surface of a metal substrate, and spray-coats a finish paint of multiple colors to the application surface of the base paint of this metal substrate, 베이스 도료와 동일한 색상인 마무리 도료 및 베이스 도료와 이색인 복수의 마무리 도료중 어느 하나의 마무리 도료를 금속기판의 표면에 도포한 후, 소정의 도포정지기간을 두고 그 도포정지기간 후에 그 마무리 도료와 부분적으로 겹쳐지도록 다른 마무리 도료가 금속기판의 표면에 도포되도록 복수의 마무리 도료를 경시적으로 순차 전환하며 금속기판의 표면에 도포하는 것을 특징으로 하는 도장판의 제조 방법.After applying the finish paint of the same color as the base paint and the finish paint of the base paint and a plurality of finish paints of different colors to the surface of the metal substrate, and after the coating stop period for a predetermined coating stop period, A method of manufacturing a coated plate, characterized in that the coating is applied to the surface of the metal substrate while the plurality of finishing paints are sequentially switched over time so that another finishing paint is applied to the surface of the metal substrate so as to partially overlap. 제1항에 있어서, 베이스 도료를 희석하여 베이스 도료와 동일한 색상의 마무리 도료를 제조하는 것을 특징으로 하는 도장판의 제조 방법.The method of manufacturing a coated plate according to claim 1, wherein the base paint is diluted to produce a finish paint of the same color as the base paint. 제1항 또는 제2항에 있어서, 하나의 스프레이 건으로 복수 색상의 마무리 도료를 경시적으로 순차 전환하며 도포하는 것을 특징으로 하는 도장판의 제조 방법.The method for producing a coating plate according to claim 1 or 2, wherein a single spray gun is used to sequentially apply a plurality of colors of finishing paint over time. 제1항 또는 제2항에 있어서, 베이스 도료 및 그와 동일한 색상인 마무리 도료의 색상을 라이트 오렌지로 하는 동시에 베이스 도료와 이색인 마무리 도료의 색상을 다크 오렌지와 베이지로 하는 것을 특징으로 하는 도장판의 제조 방법.The paint plate according to claim 1 or 2, wherein the color of the base paint and the finishing paint of the same color is light orange, and the colors of the base paint and the finishing paint of bicolor are dark orange and beige. Method of preparation.
KR1020040063284A 2003-08-12 2004-08-11 Painting plates manufacturing method KR100618142B1 (en)