KR100610159B1 - Functional pulp composition - Google Patents
Functional pulp composition Download PDFInfo
- Publication number
- KR100610159B1 KR100610159B1 KR1020040110986A KR20040110986A KR100610159B1 KR 100610159 B1 KR100610159 B1 KR 100610159B1 KR 1020040110986 A KR1020040110986 A KR 1020040110986A KR 20040110986 A KR20040110986 A KR 20040110986A KR 100610159 B1 KR100610159 B1 KR 100610159B1
- Authority
- KR
- South Korea
- Prior art keywords
- bamboo
- functional
- powder
- pulp
- bamboo vinegar
- Prior art date
Abstract
본 발명은 기능성 펄프 조성물을 개시한다. 구체적으로 본 발명은 펄프와, 첨가제로서 대나무숯 분말, 죽초액, 죽초액을 실리카에 함유시켜 만든 실리카 분말, 제올라이트 분말 중 하나 이상을 포함하는 기능성 펄프 조성물을 개시한다. 본 발명의 기능성 펄프 조성물은 항균성, 탈취성 및/또는 신선도 유지성을 지니고 있어 기능성 포장용 지류 상자 등의 제조에 유용하게 사용될 수 있다. The present invention discloses a functional pulp composition. Specifically, the present invention discloses a functional pulp composition comprising one or more of pulp, silica powder made by containing bamboo charcoal powder, bamboo vinegar liquid, bamboo vinegar liquid as an additive, and zeolite powder. The functional pulp composition of the present invention has antimicrobial, deodorant and / or freshness retention, and thus can be usefully used for the production of functional packaging paper boxes and the like.
기능성, 대나무숯, 죽초액, 실리카, 제올라이트, 펄프, 항균성, 탈취성, 신선도 유지성, 기능성 포장용 지류 상자Functional, Bamboo Charcoal, Bamboo Vinegar, Silica, Zeolite, Pulp, Antibacterial, Deodorant, Freshness Retention, Functional Packaging Feeder Box
Description
본 발명은 항균성, 탈취성, 신선도 유지성 등의 기능성을 지니는 기능성 펄프 조성물에 관한 것이다.The present invention relates to a functional pulp composition having functionality such as antibacterial, deodorant, freshness retention and the like.
펄프 조성물로 제조되는 지류(紙類) 또는 그 지류를 이용하여 제조되는 포장용 지류 상자에 기능성을 부여하려는 시도는 계속하여 있어 왔는데, 최근의 기술로서는 인체 건강 등에 유익하게 숯가루를 함침시켜 제조한 지류에 관한 대한민국 공개특허 제10-1999-0045954호와, 청과물의 선도 유지 기능을 향상시키고자 파라핀 왁스, 전분, 미경화 멜라민 수지 혼합물을 스테아린산 수용액에 첨가하여 유화시킨 액을 제올라이트 분말에 첨가하여 라이너에 코팅시킨 대한민국 공개특허 제10-1998-087686호 등을 들 수 있다.Attempts have been made to impart functionality to feeders made from pulp compositions or packaging feeder boxes made using the feeders, but recent techniques have shown that feeders produced by impregnating charcoal to benefit human health and the like. Paraffin wax, starch, uncured melamine resin mixture is added to aqueous solution of stearic acid to emulsify the zeolite powder to improve freshness retention of fruits and vegetables. Coated Republic of Korea Patent Publication No. 10-1998-087686 and the like.
본 발명도 지류 또는 지류 상자에 항균성, 탈취성 등의 기능성을 부여하고자 하는 관점에서 완성된 것이다.The present invention is also completed from the viewpoint of providing functionality such as antibacterial, deodorant to the feeder or feeder box.
따라서 본 발명의 목적은 항균성, 탈취성, 과채류 등의 신선도 유지성 등을 지니는 기능성 지류 등의 제조에 유용하게 사용될 수 있는 기능성 펄프 조성물을 제공하는 데 있다. Accordingly, it is an object of the present invention to provide a functional pulp composition that can be usefully used for the production of functional papers having antimicrobial, deodorant, freshness and the like retention of fruits and vegetables.
본 발명의 기타의 목적이나 기타의 측면은 이하에서 제시될 것이다.
Other objects or other aspects of the present invention will be presented below.
일 측면에 있어서, 본 발명은 기능성 펄프 조성물에 관한 것이다.In one aspect, the present invention relates to a functional pulp composition.
본 발명자는 하기 실시예 및 실험예에서 확인되는 바와 같이 펄프에 첨가제로서 대나무숯 분말, 죽초액, 죽초액을 실리카에 함유시켜 만든 실리카 분말 및/또는 제올라이트 분말을 넣어 기능성 펄프 조성물을 제조한 후 이를 이용하여 기능성 포장용 지류 및 지류 상자를 제조하고, 그 지류 및 상자를 이용하여 항균성, 탈취성, 식품의 신선도 유지 등의 효과를 살펴 본 결과, 그 효과가 매우 뛰어남을 확인할 수 있었다.The present inventors prepared a functional pulp composition by putting a silica powder and / or zeolite powder made by containing bamboo charcoal powder, bamboo vinegar, bamboo vinegar solution as an additive to the silica as confirmed in the following Examples and Experimental Examples Functional packaging paper and paper box was manufactured, and the effects of antimicrobial, deodorant, maintaining the freshness of food using the paper and the paper box, the effect was found to be very excellent.
본 발명은 이러한 실험 결과에 기초하여 제공되어지는 것이다.The present invention is provided based on these experimental results.
그러므로 본 발명의 기능성 펄프 조성물은 펄프와 첨가제로서 대나무숯, 죽초액, 죽초액을 실리카에 함유시켜 만든 실리카 분말, 제올라이트 분말 중 하나 이상을 포함하는 것을 특징으로 한다.Therefore, the functional pulp composition of the present invention is characterized in that it comprises at least one of silica powder, zeolite powder made by containing bamboo charcoal, bamboo vinegar liquid, bamboo vinegar liquid as a pulp and an additive.
청구범위를 포함하는 본 명세서에서 "펄프"란 침엽수펄프(NP), 활엽수펄프(LP) 등의 목재펄프와, 짚펄프(straw pulp), 버개스펄프(bagasse pulp), 갈대펄프, 대나무펄프 등의 비목재펄프를 포함하는 개념이며, 쇄목펄프(GP), 리파이너펄프 (RGP), 열처리기계펄프(TMP) 등의 기계펄프(MP)와, 아황산펄프(SP), 크라프트펄프(KP), 소다펄프(soda plup) 등의 화학펄프(CP)를 포함하는 개념이다. 또한, 표백(B), 반표백(S), 미표백(U) 펄프를 포함하고, 천연 펄프 및 재생 펄프를 포함하는 개념이다As used herein, the term "pulp" refers to wood pulp such as coniferous pulp (NP), hardwood pulp (LP), straw pulp, bagasse pulp, reed pulp, bamboo pulp, and the like. It is a concept that includes non-wood pulp, mechanical pulp such as groundwood pulp (GP), refiner pulp (RGP), heat treatment machine pulp (TMP), sulfite pulp (SP), kraft pulp (KP), and soda. It is a concept including chemical pulp (CP) such as soda plup. In addition, it is a concept including bleaching (B), semi-bleaching (S), and unbleaching (U) pulp, and including natural pulp and recycled pulp.
한편, 청구범위를 포함하는 본 명세서에서 상기 "기능성"이란 항균성, 탈취성 및/또는 신선도 유지성을 포함하는 의미로서 정의되어 진다. On the other hand, in the present specification, including the claims, the "functional" is defined as meaning including antimicrobial, deodorant and / or freshness retention.
"기능성"이 이와 같이 정의되어지는 한, 어떠한 펄프 조성물이 펄프와 첨가제로서 대나무숯 분말, 죽초액, 죽초액을 실리카에 함유시켜 만든 실리카 분말, 제올라이트 분말 중 하나 이상을 포함하고, 또 그것이 상기 항균성, 탈취성 및/또는 신선도 유지성을 갖는/요하는 펄프 제품(포장용 지류 등)의 제조에 사용될 수 있다면, 그러한 펄프 조성물은 모두 본 발명의 기능성 펄프 조성물에 포함되는 것으로 이해되어져야 한다. As long as " functionality " is defined as such, any pulp composition comprises one or more of bamboo charcoal powder, bamboo vinegar liquor, bamboo vinegar powder, zeolite powder as a pulp and an additive as silica, and the antimicrobial, deodorizing It is to be understood that all such pulp compositions are included in the functional pulp compositions of the present invention, if they can be used in the manufacture of pulp products (such as packing papers) that have / requireability and / or freshness retention.
한편, 청구범위를 포함하는 본 명세서에서, "첨가제로 포함한다"는 것의 의미는 펄프보다 실질적으로 적은 양으로 포함한다는 의미이면서 또한 전술하는 바의 기능성을 나타낼 수 있을 만큼의 양으로 포함한다는 의미로서 정의될 수 있다. 여기서 "펄프보다 실질적으로 적은 양"이란 펄프 제품이 제조되기 위해 필요한 펄프와 첨가제의 통상적인 비율을 넘어서지 않는 양으로 정의될 수 있다.On the other hand, in the present specification, including the claims, the term "including as an additive" means to include substantially less than the pulp, and also to include in an amount sufficient to represent the functionality described above. Can be defined. “Substantially less than pulp” can be defined herein as an amount that does not exceed the conventional ratio of pulp and additives needed for the pulp product to be made.
당업자라면 본 출원의 출원시를 기준으로 당업계에 공지된 기술과 본 발명의 하기 실시예 및 실험예에 기초하는 한 그의 통상의 능력 범위 내에서 전술하는 바의 기능성을 나타낼 수 있는(그 기능성의 정도에 있어서는 차이는 있더라도) 펄프 제품의 제조에 적합한 펄프와 첨가제의 비율을 결정할 수 있을 것이다. One of ordinary skill in the art can demonstrate the functionality described above within the scope of its usual capability, based on the techniques known in the art based on the filing of the present application and the following Examples and Experimental Examples of the present invention (the functionality of It will be possible to determine the ratio of pulp and additive suitable for the manufacture of the pulp product, although differences in degree may occur.
예컨대, 본 발명의 기능성 펄프 조성물이 기능성 종이 또는 기능성 판지 등의 기능성 지류를 제조하는데 사용될 경우에 상기 첨가제인 대나무숯 분말, 죽초액, 죽초액을 실리카에 함유시켜 만든 실리카 분말 및/또는 제올라이트 분말은 펄프 100 중량부에 대해 1 내지 70 중량부로 첨가되는 것이 바람직하다.For example, when the functional pulp composition of the present invention is used to produce functional papers such as functional paper or functional cardboard, silica powder and / or zeolite powder made by containing the above-mentioned additives such as bamboo charcoal powder, bamboo vinegar liquor, bamboo vinegar liquor, etc. It is preferably added in 1 to 70 parts by weight with respect to parts by weight.
펄프 100 중량부에 대해서 1 중량부 미만인 경우에는 상기 첨가제가 펄프 내에 전체적으로 균일하게 분포되기가 어려워 본 발명에서 목적하는 효과를 달성하기가 어려울 수 있고, 반면 70 중량부를 초과하는 경우에는 너무 함량이 많아서 펄프의 섬유소가 상호 결합력이 약해지므로 정상적으로 지류를 제조할 수 없거나 지류로서 요구되는 기계적 강도 등이 저하될 수 있기 때문이다.If it is less than 1 part by weight with respect to 100 parts by weight of pulp, it may be difficult to achieve the desired effect in the present invention because it is difficult to distribute the additive uniformly throughout the pulp, whereas if it exceeds 70 parts by weight is too high This is because the fibrin of the pulp is weakened in the mutual bonding force, so that the feeder cannot be manufactured normally or the mechanical strength required as the feeder can be lowered.
그러므로 어떠한 펄프 조성물이 펄프와 첨가제로서 대나무숯, 죽초액, 죽초액을 실리카에 함유시켜 만든 실리카 분말, 제올라이트 분말 중 하나 이상을 포함하고, 그것이 전술한 바의 기능성을 가지는 한, 펄프와 거기에 포함되는 첨가제의 비율은 임의의 것이라도 무방한 것으로 받아들여져야 한다.Therefore, as long as any pulp composition comprises at least one of a bamboo charcoal, bamboo vinegar, bamboo vinegar, zeolite powder as a pulp and an additive in silica, zeolite powder, and as long as it has the functionality described above, the pulp and additives contained therein The ratio of is to be taken as arbitrary.
한편, 본 발명의 기능성 펄프 조성물에 포함되는 대나무숯 분말은 그것을 얻기 위해 사용된 대나무 종류에 상관없이 또 그 제조 방법에 상관없이 대나무에 직·간접적으로 고온의 열을 가하여 얻어지는 탄화된 모든 고체 분말로서 정의된다. On the other hand, the bamboo charcoal powder included in the functional pulp composition of the present invention is any carbonized solid powder obtained by directly or indirectly applying high temperature heat to bamboo regardless of the type of bamboo used to obtain it and the method of producing the same. Is defined.
그러므로 본 발명의 기능성 펄프 조성물에 포함되는 대나무숯 분말은 그것이 왕대속(Phyllostachys)에 속하는 대나무에서 얻어졌든지, 해장죽속(Arundinaria)에 속하는 대나무에서 얻어졌든지, 조릿대속(Sasa)에 속하는 대나무에서 얻어졌든지 또는 이대속(Pseudosasa)에 속하는 대나무에서 얻어졌든지를 불문하며, 또 그것을 제조하기 위하여 특별히 개발된 탄화로를 사용하였던지, 열 전달 매개체로 특별히 고안된 용기를 사용하였던지 또는 냉각 시간을 달리하였던지를 불문하고 분류학상 대나무로 분류되는 식물(즉 벼목 화본과)로부터 얻어진 탄화된 모든 고체 분말을 포함하는 것으로 이해되어야 한다. Therefore, the bamboo charcoal powder included in the functional pulp composition of the present invention is obtained from bamboo belonging to Phyllostachys or bamboo belonging to Arundinaria or bamboo belonging to Sasa Whether obtained from bamboos belonging to Pseudosasa or by using specially developed carbonization furnaces, using specially designed vessels as heat transfer media or cooling times It should be understood to include all carbonized solid powders obtained from plants classified as taxonomically bamboo (ie, rice paddy family), whether or not otherwise.
한편, 죽초액은 일반적으로 대나무의 탄화 과정에서 발생하는 연기를 냉각시킨 다음 정치 숙성시키거나 여과 정제하거나 증류시켜 제조되는 적갈색의 투명한 액체를 말한다. On the other hand, bamboo vinegar is generally a reddish brown transparent liquid prepared by cooling the smoke generated during the carbonization process of bamboo and then politically aged, filtered or distilled.
대나무를 탄화시켜 거기서 발생하는 연기를 냉각시켜 방치하여 두면 3개의 층으로 분리되게 되는데, 상층은 데르핀유 등의 경질유층이고, 중층이 죽초액층이며 하층이 타르층이다. 이러한 중층의 죽초액을 엄밀하게는 조죽초액이라 하는데, 현재 시중에 유통되고 있는 죽초액은 이러한 조죽초액을 정치 숙성시키거나 여과 정제하거나 증류시킨 것들이다. Carbonization of the bamboo and cooling the smoke generated there is left to separate into three layers, the upper layer is a light oil layer, such as derpin oil, the middle layer is bamboo shoot liquid layer, the lower layer is a tar layer. This middle layer of bamboo vinegar is strictly called crude bamboo vinegar, and the bamboo vinegar solution currently on the market is those that are politically aged, filtered, purified or distilled.
죽초액은 강산성(pH 2.8 ~ 3.1)으로 그 주성분은 아세트산과 포름산 등의 유기산이며, 기타 페놀 등이 포함되어 있다. Bamboo vinegar is strongly acidic (pH 2.8 ~ 3.1) and its main component is organic acid such as acetic acid and formic acid, and contains other phenols.
본 발명의 기능성 펄프 조성물에 포함되는 "죽초액"이란 전술한 바의 죽초액, 즉 조죽초액에서 정치 숙성되거나 여과 정제되거나 증류된 것이 바람직하지만, 조죽초액이라도 무방하며 또한 조죽초액으로부터 상기 방법 이외의 다른 방법으로 정제된 죽초액이라도 무방하다. The term "bamboo vinegar" included in the functional pulp composition of the present invention is preferably vinegar liquor as described above, that is, it has been politically aged, filtered, or distilled from the crude vinegar liquor. Bamboo vinegar may be purified.
죽초액이 조죽초액으로부터 정제된 것이 이상, 죽초액이 전술한 바의 기능성 을 나타낸다면, 그 기능성의 정도에 있어서는 차이가 있을지라도 당업자라면 그의 통상의 능력 범위안에서 본 발명의 하기 실시예 및 실험예에 기초하는 한 조죽초액 또한 전술한 바의 기능성을 지닐 것이라 예상할 수 있으며, 그의 통상의 능력을 활용하는 한 전술한 바의 기능성을 용이하게 확인할 수 있을 것이다.If the bamboo vinegar is purified from the crude bamboo vinegar, if the bamboo vinegar shows the functionality as described above, even if there is a difference in the degree of functionality, those skilled in the art based on the following Examples and Experimental Examples of the present invention within the usual range As long as the crude bamboo vinegar can also be expected to have the functionality as described above, it will be easy to confirm the functionality of the above-described as long as it utilizes its ordinary ability.
또한 조죽초액에서 정제되는 방식에 따라 죽초액이 전술한 바의 기능성의 정도에 있어서 차이를 나타낼지라도, 당업자는 본 발명이 개시하는 바에 기초하는 한 그 죽초액이 조죽초액에서 어떠한 방식으로 정제되든지 간에 모든 죽초액이 전술한 바의 기능성을 나타낼 개연성을 가지고 있다고 예측할 것이며, 또한 당업자라면 본 발명의 하기 실시예 및 실험예에 기초하는 한 그의 통상의 능력 범위안에서 전술한 바의 기능성을 갖는 죽초액을 확인·선별할 수 있을 것이다.Also, although bamboo liquor may differ in the degree of functionality as described above depending on the manner in which it is purified in crude bamboo liquor, those skilled in the art will appreciate that all bamboo liquor liquor may be purified in crude bamboo liquor as long as it is based on the present disclosure. It will be predicted that there is a probability to show the functionality as described above, and those skilled in the art will be able to identify and select the bamboo vinegar solution having the functionality as described above within its usual capability range, based on the following Examples and Experimental Examples of the present invention. Could be.
그러므로 청구범위를 포함하는 본 명세서에서, 본 발명의 기능성 펄프 조성물에 포함되는 "죽초액"이란 조죽초액으로부터 정치 숙성되거나 여과 정제되거나 증류된 것들뿐만 아니라 그 전단계의 조죽초액을 포함하는 의미로서 이해되어야 하며, 나아가 어떠한 죽초액이 조죽초액에서 정제되어 상기 기능성을 갖는다면 그러한 죽초액도 포함하는 의미로서 이해되어져야 한다. Therefore, in the present specification, including the claims, the term "jujube liquor" included in the functional pulp composition of the present invention should be understood as including not only those that have been politically aged, filtered, purified, or distilled from the crude jujube liquor, but also the prior stage jujube liquor. Furthermore, if any bamboo liquor is purified from crude bamboo liquor and has the above functionality, it should be understood as a meaning including such bamboo liquor.
한편, 본 발명의 기능성 펄프 조성물에 포함되는 죽초액을 실리카에 함유시켜 만든 분말은 죽초액을 함유한 실리카(Silica)를 분말화하여 얻어지는 것을 의미하는데, 여기서 실리카로서는 천연 실리카(규조토)와 합성 실리카(이산화규소(silicon dioxide)) 모두 사용될 수 있다. 그럼에도 바람직하게는 하기 실시예 및 실험예에서 보여지는 바와 같이 천연 실리카이다.On the other hand, the powder made by containing the bamboo vinegar solution contained in the functional pulp composition of the present invention in silica means that the powder obtained by pulverizing the silica (Silica) containing bamboo vinegar solution, wherein the silica is natural silica (diatomaceous earth) and synthetic silica (dioxide) Both silicon dioxide can be used. Nevertheless, preferred is natural silica as shown in the following Examples and Experimental Examples.
또한 본 발명의 기능성 펄프 조성물에 포함되는 제올라이트 분말의 경우도 천연 제올라이트 분말와 합성 제올라이트(알루미나실리게이트) 분말 모두 사용될 수 있다. 마찬가지로 바람직하게는 천연 제올라이트 분말이다.In addition, in the case of the zeolite powder included in the functional pulp composition of the present invention, both natural zeolite powder and synthetic zeolite (alumina silicate) powder may be used. Likewise preferred is natural zeolite powder.
한편, 전술한 바의 기능성의 관점에 봤을 때, 본 발명의 기능성 펄프 조성물에는 대나무숯 분말, 죽초액, 죽초액을 실리카에 함유시켜 만든 실리카 분말, 제올라이트 분말 중 두개가 포함되는 것이 바람직하며, 세개가 포함되는 것이 더 바람직하고, 네개 모두 포함되는 경우가 더더욱 바람직하다.On the other hand, in view of the functionality of the above, the functional pulp composition of the present invention preferably comprises two of the bamboo charcoal powder, bamboo powder, bamboo powder made by containing bamboo vinegar liquid, bamboo vinegar liquid, zeolite powder, including three More preferably, all four are even more preferred.
가장 바람직하게는 대나무숯 분말, 죽초액을 천연 실리카에 함유시켜 만든 실리카 분말 및 천연 제올라이트 분말을 포함하는 경우이다.Most preferably, it contains bamboo charcoal powder, silica powder made by containing bamboo shoot liquid in natural silica, and natural zeolite powder.
상기에서 본 발명의 기능성 펄프 조성물에 대나무숯 분말, 죽초액, 죽초액을 실리카에 함유시켜 만든 실리카 분말 및/또는 제올라이트 분말이 포함될 때, 그것들 중 하나가 포함되든지, 두개가 포함되든지, 세개가 포함되든지 또는 네개 모두가 포함되든지를 불문하고, 그것들이 펄프와의 배합량은 하기 실시예 및 실험예가 보여주듯이 펄프 100 중량부를 기준으로 하였을 때 1 내지 70 중량부인 것이 바람직하고, 8.6 내지 56.2 중량부인 것인 더 바람직하다. When the functional pulp composition of the present invention includes the bamboo charcoal powder, bamboo vinegar solution, silica powder made by containing the bamboo vinegar solution and / or zeolite powder, one of them, two or three, or Regardless of whether all four are included, they are preferably 1 to 70 parts by weight, more preferably 8.6 to 56.2 parts by weight, based on 100 parts by weight of pulp, as shown in the following Examples and Experimental Examples. Do.
또한 상기에서 본 발명의 기능성 펄프 조성물에 대나무숯 분말, 죽초액을 천연 실리카에 함유시켜 만든 실리카 분말 및 천연 제올라이트 분말이 포함될 때 그것들의 펄프와의 배합량은 전술한 바가 그대로 유효하지만, 그것들 사이의 비율은 그것들 자체의 전체 중량(100 중량%)을 기준으로 하였을 때 대나무숯 분말은 20 내지 70 중량% 범위이고, 죽초액을 천연 실리카에 함유시켜 만든 분말은 6 내지 50 중량% 범위이고, 천연 제올라이트 분말은 40 내지 80 중량% 범위인 것이 바람직하다. 그 이유는 하기 실시예(특히 실시예 6) 및 실험예에서 확인할 수 있다.In addition, when the functional pulp composition of the present invention includes bamboo charcoal powder, silica powder made by containing bamboo vinegar solution and natural zeolite powder, and natural zeolite powder, the mixing amount with the pulp is effective as it is, but the ratio between them Based on their total weight (100% by weight), the bamboo charcoal powder ranges from 20 to 70% by weight, the powder made from bamboo containing bamboo vinegar ranges from 6 to 50% by weight, and the natural zeolite powder is 40% by weight. It is preferably in the range from 80% by weight. The reason can be confirmed in the following example (especially Example 6) and an experiment example.
한편, 본 발명의 기능성 펄프 조성물에 포함되는 펄프로서는, 그것이 첨가제로서 포함되는 대나무숯 분말, 죽초액, 죽초액을 실리카에 함유시켜 만든 분말 및/또는 제올라이트 분말이 전술한 바의 기능성을 나타내는 것을 방해하지 않는다면, 의도하는 용도에 따라 당업계에 공지된 임의의 펄프를 사용할 수 있다.On the other hand, as the pulp included in the functional pulp composition of the present invention, a powder made by containing bamboo charcoal powder, bamboo vinegar liquid, bamboo vinegar liquid, and / or zeolite powder contained as an additive does not prevent it from exhibiting the functionality as described above. Depending on the intended use, any pulp known in the art may be used.
본 발명의 기능성 펄프 조성물은 또는 그것으로 제조되는 기능성 포장용 지류 또는 기능성 포장용 지류 상자의 용도 등에 따라 통상의 각종 펄프용 첨가제를 포함할 수 있다.The functional pulp composition of the present invention may include various conventional pulp additives according to the use of the functional packaging paper or the functional packaging paper feed box manufactured therefrom.
이때 첨가되는 상기 각종 첨가제는 기능성 포장용 지류 또는 기능성 포장용 지류 상자의 용도에 따라 요구되는 성질(예컨대, 기계적 강도나 표면 거칠기 등)을 해치지 않으면서 그것의 첨가제로서의 효과를 나타낼 수 있다면, 그것의 펄프에의 배합량을 특정한 범위로 한정되지 않는다. The various additives added at this time may be effective as its additives without impairing the properties required (eg, mechanical strength or surface roughness) depending on the purpose of the functional packaging paper or the functional packaging paper box. The compounding quantity of is not limited to a specific range.
다른 측면에 있어서, 본 발명은 본 발명의 기능성 펄프 조성물을 이용하여 제조되는 기능성 포장용 지류에 관한 것이다.In another aspect, the present invention relates to a functional packaging feeder prepared using the functional pulp composition of the present invention.
또 다른 측면에 있어서 본 발명은 본 발명의 펄프 조성물을 이용하여 제조되는 지류를 이용하여 얻어지는 기능성 포장용 지류 상자에 관한 것이다.In yet another aspect, the present invention relates to a functional packaging paper box obtained by using a feeder produced using the pulp composition of the present invention.
여기서, "기능성"의 의미는 모든 바람직한 양태들을 포함하여 이미 전술한 바 그대로 유효하다.Here, the meaning of “functionality” is valid as already described above, including all preferred embodiments.
한편, 상기 기능성 포장용 지류는 농산물, 화훼, 식품, 과채류, 엽경 채류, 과수류 등의 포장, 저장 또는 보관에 사용될 수 있지만, 이에 한정되지 않고 상기 기능성이 요구되는 모든 물품에 적용될 수 있다. 특히, 과일, 채소 등의 청과류 및 쌀 등의 농산물에 유용하게 적용될 수 있다.Meanwhile, the functional packaging paper may be used for packaging, storing, or storing agricultural products, flowers, foods, fruit vegetables, leafy vegetables, fruit trees, and the like, but is not limited thereto and may be applied to all articles requiring the functionality. In particular, it can be usefully applied to agricultural products, such as fruits and vegetables and fruits and vegetables.
한편, 상기 "지류"는 일반 종이 및 판지를 포함하는 것으로서, 구체적으로 백상지, 중절지, 박엽지, 신문용지, 도공용지, 도공지, 그라프트지, 편광지 등의 일반 종이와 지기용 판지, 골판지 원지 등을 포함하는 의미이다. On the other hand, the "paper" includes a general paper and cardboard, specifically, paper, paper, cardboard, cardboard, cardboard, coated paper, coated paper, paper for cardboard, cardboard, corrugated paper And the like.
한편, 본 발명의 일 측면에 따른 기능성 포장용 지류는 본 발명에 따른 기능성 펄프 조성물로 제조된 모든 기능성 포장용 지류를 포함하는 것이다. 여기서 그 제조 방법은 특별히 문제되지 않는다.On the other hand, the functional packaging paper according to one aspect of the present invention includes all the functional packaging paper made of the functional pulp composition according to the present invention. Here, the manufacturing method is not particularly problematic.
한편, 본 발명의 기능성 포장용 지류 상자의 일 양태는 항균성, 탈취성, 신선도 유지성의 효과를 위해 과채류, 농산물, 식품, 화훼 등을 포장하기 위한 지류 상자 경우 등을 포함한다. On the other hand, one aspect of the functional packaging paper box of the present invention includes a case of a paper box for packaging fruits, agricultural products, food, flowers and the like for the effect of antibacterial, deodorant, freshness retention.
한편, 상기 본 발명의 기능성 포장용 지류 또는 기능성 포장용 지류 상자는 신선도의 유지가 필요한 농산물, 화훼, 식품의 포장, 저장 또는 보관에 사용될 수 있지만, 항균성이나 탈취성 등이 요구되는 기타의 물품의 포장, 저장 또는 보관에도 사용될 수 있다.Meanwhile, the functional packaging paper feeder or functional packaging paper feeder box of the present invention may be used for packaging, storing, or storing agricultural products, flowers, and foods requiring maintenance of freshness, but for packaging other items requiring antibacterial or deodorizing properties, It can also be used for storage or storage.
그럼에도 바람직하게는 농산물, 화훼, 식품의 포장, 저장 또는 보관에 사용되는 경우이다.Nevertheless, it is preferably used for the packaging, storage or storage of agricultural products, flowers and food.
또 다른 측면에 있어서, 본 발명은 전술한 바의 기능성 펄프 조성물의 제조 방법에 관한 것이다. 본 발명의 기능성 펄프 조성물의 제조 방법은 전술한 바와 같이 펄프에 첨가제로서 대나무숯 분말, 죽초액, 죽초액을 실리카에 함유시켜 만든 실리카 분말, 제올라이트 분말 중 하나 이상을 첨가하는 단계를 포함하는 것을 특징으로 한다.In another aspect, the present invention relates to a method of preparing the functional pulp composition as described above. The method for producing the functional pulp composition of the present invention is characterized in that it comprises the step of adding one or more of the bamboo charcoal powder, bamboo vinegar, bamboo powder made by containing the bamboo vinegar solution, silica powder, zeolite powder as an additive to the pulp as described above. .
여기서 "펄프", "기능성" 등의 의미는 모든 바람직한 양태들을 포함하여 이미 전술한 바가 그대로 유효하다.The meaning of "pulp", "functional" and the like herein is valid as described above, including all preferred embodiments.
또 다른 측면에 있어서, 본 발명은 두 겹 이상의 지류를 접착제로 접착시켜 얻어지는 포장용 지류 또는 포장용 상자에 있어서, 상기 접착제는 대나무숯 분말, 죽초액, 죽초액을 실리카에 함유시켜 만든 실리카 분말, 제올라이트 분말 중에서 선택된 하나 이상의 것을 첨가제로서 포함하는 것을 특징으로 하는 기능성 포장용 지류 또는 기능성 포장용 상자에 관한 것이다.In another aspect, the present invention is a packaging paper or packaging box obtained by adhering two or more layers of paper with an adhesive, wherein the adhesive is selected from bamboo charcoal powder, bamboo powder made by containing bamboo vinegar liquid, bamboo vinegar liquid, zeolite powder A functional packaging paper or functional packaging box comprising at least one as an additive.
여기서 "기능성" 등의 의미는 이미 전술한 바가 그대로 유효하다.Here, the meaning of "functionality" or the like is already valid as described above.
두 겹 이상의 지류를 접착제로 접착시켜 포장용 지류를 제조하거나 포장용 상자를 제조할 때 그러한 지류가 본 발명의 펄프 조성물에 의하여 제조되지 아니한 지류라고 하더라도, 상기 접착제에 첨가제로서 대나무숯 분말, 죽초액, 죽초액을 실리카에 함유시켜 만든 실리카 분말, 제올라이트 분말 중에서 선택된 하나 이상을 포함시켜 상기 포장용 지류를 제조하거나 포장용 지류 상자를 제조하더라도 전술한 바의 기능성이 발휘될 수 있다.When bonding two or more layers of paper to make a packing paper or making a packaging box, even if the paper is not made by the pulp composition of the present invention, bamboo charcoal powder, bamboo liquor liquid, bamboo liquor liquid as additives to the adhesive may be used. The above-described functionality may be exhibited even when the packaging paper is prepared or the packaging paper box is manufactured by including one or more selected from silica powder and zeolite powder made by inclusion in silica.
이하 본 발명을 실시예를 참조하여 설명한다. 그러나 이러한 실시예가 본 발명의 범위를 제한하는 것은 아니다.Hereinafter, the present invention will be described with reference to Examples. However, these examples do not limit the scope of the present invention.
<실시예> <Example> 기능성 포장용 지류 및 기능성 포장용 지류 상자의 제조Preparation of functional packaging paper and functional packaging paper box
<실시예 1> 기능성 포장용 지류 및 기능성 포장용 지류 상자의 제조예 1 <Example 1> Manufacturing example 1 of the functional packaging paper and the functional packaging paper box
대나무숯 분말 10 중량%를 90 중량%의 펄프 분말과 혼합하여 기능성 펄프 조성물을 형성하고 상기 혼합물을 초지기에 투입하여 초지를 제조한 후 탈수 건조하여 기능성 지류를 제조하였다. 또한 제조된 기능성 지류를 이용하여 과채류 또는 식품 등의 보관에 사용되는 통상적인 형태의 기능성 포장용 지류 상자를 제조하였다. 10% by weight of bamboo charcoal powder was mixed with 90% by weight of pulp powder to form a functional pulp composition, and the mixture was put into a paper machine to prepare a paper, followed by dehydration drying to prepare a functional feeder. In addition, a functional packaging paper box of a conventional type used for the storage of fruits, vegetables or foods was prepared using the prepared functional paper.
<실시예 2> 기능성 포장용 지류 및 기능성 포장용 지류 상자의 제조예 2 Example 2 Manufacturing Example 2 of Functional Packaging Paper and Functional Packaging Paper Box
죽초액 8 중량%를 90 중량%의 펄프 분말과 혼합하여 기능성 펄프 조성물을 형성하고 상기 혼합물을 초지기에 투입하여 초지를 제조한 후 탈수 건조하여 기능성 지류를 제조하였다. 또한 제조된 기능성 지류를 이용하여 과채류 또는 식품 등의 보관에 사용되는 통상적인 형태의 기능성 포장용 지류 상자를 제조하였다. 8% by weight of bamboo vinegar was mixed with 90% by weight of pulp powder to form a functional pulp composition, and the mixture was put into a paper machine to prepare a paper, followed by dehydration drying to prepare a functional paper. In addition, a functional packaging paper box of a conventional type used for the storage of fruits, vegetables or foods was prepared using the prepared functional paper.
<실시예 3> 기능성 포장용 지류 및 기능성 포장용 지류 상자의 제조예 3 Example 3 Manufacturing Example 3 of Functional Packaging Paper and Functional Packaging Paper Box
죽초액을 천연 실리카에 함유시켜 만든 분말 8 중량%를 90 중량%의 펄프 분말과 혼합하여 기능성 펄프 조성물을 형성하고 상기 혼합물을 초지기에 투입하여 초지를 제조한 후 탈수 건조하여 기능성 지류를 제조하였다. 또한 제조된 기능성 지류를 이용하여 과채류 또는 식품 등의 보관에 사용되는 통상적인 형태의 기능성 포장용 지류 상자를 제조하였다. 8 wt% of the powder prepared by containing the bamboo vinegar solution in natural silica was mixed with 90 wt% of pulp powder to form a functional pulp composition, and the mixture was put into a paper machine to prepare a paper, followed by dehydration drying to prepare a functional paper. In addition, a functional packaging paper box of a conventional type used for the storage of fruits, vegetables or foods was prepared using the prepared functional paper.
<실시예 4> 기능성 포장용 지류 및 기능성 포장용 지류 상자의 제조예 4 Example 4 Manufacturing Example 4 of a Functional Packaging Paper Feeder and a Functional Packaging Paper Feeder Box
대나무숯 분말 10 중량%, 죽초액 8 중량%를 82 중량%의 펄프 분말과 혼합하여 기능성 펄프 조성물을 형성하고 상기 혼합물을 초지기에 투입하여 초지를 제조한 후 탈수 건조하여 기능성 지류를 제조하였다. 또한 제조된 기능성 지류를 이용하여 과채류 또는 식품 등의 보관에 사용되는 통상적인 형태의 기능성 포장용 지류 상자를 제조하였다. 10% by weight of bamboo charcoal powder and 8% by weight of bamboo vinegar were mixed with 82% by weight of pulp powder to form a functional pulp composition, and the mixture was put into a paper machine to prepare a paper, followed by dehydration drying to prepare a functional paper. In addition, a functional packaging paper box of a conventional type used for the storage of fruits, vegetables or foods was prepared using the prepared functional paper.
<실시예 5> 기능성 포장용 지류 및 기능성 포장용 지류 상자의 제조예 5 Example 5 Manufacturing Example 5 of Functional Packaging Paper and Functional Packaging Paper Box
대나무숯 분말 10 중량%, 죽초액을 천연 실리카에 함유시켜 만든 분말 8 중량%를 82 중량%의 펄프 분말과 혼합하여 기능성 펄프 조성물을 형성하고 상기 혼합물을 초지기에 투입하여 초지를 제조한 후 탈수 건조하여 기능성 지류를 제조하였다. 또한 제조된 기능성 지류를 이용하여 과채류 또는 식품 등의 보관에 사용되는 통상적인 형태의 기능성 포장용 지류 상자를 제조하였다. 10% by weight of bamboo charcoal powder and 8% by weight of powder made by adding bamboo vinegar to natural silica were mixed with 82% by weight of pulp powder to form a functional pulp composition, and the mixture was put into a paper machine to prepare a paper, followed by dehydration drying. Functional tributaries were prepared. In addition, a functional packaging paper box of a conventional type used for the storage of fruits, vegetables or foods was prepared using the prepared functional paper.
<실시예 6> 기능성 포장용 지류 및 기능성 포장용 지류 상자의 제조예 6 Example 6 Manufacturing Example 6 of Functional Packaging Paper and Functional Packaging Paper Box
대나무숯 분말 10 중량%, 죽초액을 천연 실리카에 함유시켜 만든 분말 8 중량%, 천연 제올라이트 분말 18 중량%를 64 중량%의 펄프 분말과 혼합하여 기능성 펄프 조성물을 형성하고 상기 혼합물을 초지기에 투입하여 초지를 제조한 후 탈수 건조하여 기능성 지류를 제조하였다. 또한 제조된 기능성 지류를 이용하여 과채류 또는 식품 등의 보관에 사용되는 통상적인 형태의 기능성 포장용 지류 상자를 제조하였다. 10% by weight of bamboo charcoal powder, 8% by weight powder made from bamboo vinegar and 18% by weight of natural zeolite powder are mixed with 64% by weight of pulp powder to form a functional pulp composition, and the mixture is put into a paper machine After preparing the dehydration and drying to prepare a functional feeder. In addition, a functional packaging paper box of a conventional type used for the storage of fruits, vegetables or foods was prepared using the prepared functional paper.
<비교예> 일반 포장용 지류 및 일반 포장용 지류 상자의 제조예 <Comparative example> Production example of general packing paper and general packing paper box
상기 실시예에서 대나무숯 분말, 죽초액, 죽초액을 다공성 실리카에 함유시켜 만든 분말, 또는 천연 제올라이트 분말을 첨가하지 않고 일반 펄프만을 가지고 상기 실시예와 동일한 방법으로 일반 포장용 지류 및 일반 포장용 지류 상자를 제조하였다.In the above embodiment, a general packaging paper and a general packaging paper box were manufactured using the same method as in the above example with only the normal pulp without adding bamboo charcoal powder, bamboo vinegar liquid, bamboo vinegar liquid in porous silica, or natural zeolite powder. .
<실험예> Experimental Example 기능성 포장용 지류 및 기능성 포장용 지류 상자의 항균성 실험, 탈취성 실험, 식품의 신선도 유지 실험Antimicrobial test, deodorant test and food freshness preservation test of functional packing paper and functional packing paper box
<실험예 1> 기능성 포장용 지류의 항균 실험 Experimental Example 1 Antimicrobial Experiment of Functional Packaging Feeder
항균성은 대장균(Escherichia coli)과 녹농균(Pseudomonas aeruginosa)을 사용하여 평가하였다. 항균성은 박테리아 감소율로서 평가하였다. <실시예 1> 내지 < 실시예 6>에서 얻어진 각 기능성 지류를 60mm×60mm 의 크기로 오려 멸균된 실험용 접시에 놓아두었다. Antimicrobial activity was evaluated using Escherichia coli and Pseudomonas aeruginosa. Antimicrobial activity was assessed as bacterial reduction rate. Each functional paper obtained in <Example 1> to <Example 6> was cut into a size of 60 mm x 60 mm and placed in a sterilized laboratory dish.
각 배양액 0.5㎖(각 배양액은 대장균 104/㎖와 녹농균 106/㎖를 포함함)를 각 실험용 접시에 접종한 다음 24 시간 동안 35℃에서 방치한 후에 생균수를 계수하여 박테리아 감소율을 산출하여 하기 <표 1>에 나타내었다. 감소율의 부호가 마이너스인 것은 박테리아의 증가를 의미한다.0.5 ml of each culture (each containing 10 4 / ml E. coli and 10 6 / ml Pseudomonas aeruginosa) was inoculated into each dish and left at 35 ° C for 24 hours, after which the number of viable cells was counted to calculate the bacterial reduction rate. It is shown in Table 1 below. A negative sign of the rate of reduction indicates an increase in bacteria.
<비교 실험예> 일반 포장용 지류의 항균 실험 <Comparative Experimental Example> Antibacterial experiment of general packing paper
또한, 비교 실험예로서 상기 비교예에서 제조한 일반 포장용 지류을 사용하였다.In addition, the general packing paper manufactured by the said comparative example was used as a comparative experiment example.
한편, 비교 실험예는 결과의 정확한 비교를 위해서 상기 실험예와 가능한 한 동일한 조건 하에서 이루어지도록 하였다.On the other hand, the comparative experimental example was made under the same conditions as possible as the experimental example for the accurate comparison of the results.
<실험예 2> 기능성 포장용 지류의 탈취 실험 Experimental Example 2 Deodorization Experiment of Functional Packaging Paper
플라스크 8개를 준비하고 6개의 플라스크에는 각각 상기 <실시예 1> 내지 < 실시예 6>에서 얻어진 포장용 지류를 오려 넣고, 1개의 플라스크에는 상기 <비교예>에서 제조한 포장용 지류를 넣었으며, 나머지 1개의 플라스크에는 아무것도 넣지 않았다. 한편, 지류는 플라스크의 내부 표면적을 약 70% 감싸도록 하였다. 위 7개의 플라스크 각각에 암모니아 용액 4㎛를 넣고 기화시켰다. 일정한 시간(30분)이 경과 후에 가스검지관법에 의하여 7개의 플라스크 안의 기체 농도를 계산하여 탈취율(%)을 구하였다. Eight flasks were prepared, and each of the six flasks was cut out of the packing paper obtained in <Example 1> to <Example 6>, and one flask was packed with the packing paper prepared in <Comparative Example>. Nothing was put in one flask. The feeder, on the other hand, was to cover about 70% of the inner surface area of the flask. Into each of the seven flasks 4㎛ ammonia solution was evaporated. After a certain period of time (30 minutes), the gas concentration in the seven flasks was calculated by the gas detection tube method to determine the deodorization rate (%).
탈취율은 다음의 식에 따라 계산하였다.Deodorization rate was calculated according to the following equation.
탈취율(%) = ((Cb - Cs)/Cb) x 100%Deodorization rate (%) = ((Cb-Cs) / Cb) x 100%
* Cs: 실시예 1 내지 6의 포장용 지류 또는 비교예의 포장용 지류로 내부를 감싼 플라스크에서의 최종 기체 농도(ppm)* Cs: final gas concentration (ppm) in the flask wrapped inside with the packaging feeder of Examples 1-6 or the packaging feeder of Comparative Example
* Cb: 아무것도 넣지 않은 플라스크에서의 최종 기체 농도(ppm)* Cb: final gas concentration (ppm) in an empty flask
트리메틸아민의 탈취율의 측정도 상기와 동일한 방법을 사용하였다.The same method as the above was used for the measurement of the deodorization rate of trimethylamine.
하기 <표 2>은 암모니아와 트리메틸아민의 탈취율을 나타낸 것이다.Table 2 shows the deodorization rate of ammonia and trimethylamine.
<실험예 3> 기능성 포장용 지류 상자의 신선도 유지 효과 실험 1 Experimental Example 3 Freshness Retention Effect Experiment 1 of Functional Packaging Feeder Box
두부 8모를 준비하여 7모는 각각 상기 <실시예 1> 내지 <실시예 6>의 기능성 포장용 지류 상자 및 <비교예>에서 제조된 일반 포장용 지류 상자로 포장하고 나머지 1모는 아무런 포장도 하지 않고 상온(약 25℃)에 방치하였다. Prepare 8 heads of tofu, and 7 hairs are packed in the functional packaging paper box of <Example 1> to <Example 6> and the general packaging paper box manufactured in <Comparative Example>, and the other 1 hair is not packaged at room temperature ( About 25 ° C.).
변질 여부를 관능 평가하여 변질(냄새로 판단함)하기까지의 일수를 하기 <표 3>에 나타내었다.The number of days until deterioration (determined by smell) by sensory evaluation of deterioration is shown in Table 3 below.
<실험예 4> 기능성 포장용 지류 상자의 신선도 유지 효과 실험 2 Experimental Example 4 Freshness Retention Effect Experiment 2 of Functional Packaging Feeder Box
상추 800 g을 준비하여 상기 <실시예 1> 내지 <실시예 6>에서 제조한 기능성 포장용 지류 상자로 각각 100 g씩 포장하고, 100 g은 상기 <비교예>에서 제조한 일반 포장용 지류 상자로 포장하였으며, 나머지 100 g은 아무런 포장도 하지 않고 상온(약 25℃)에 방치하였다. 800 g lettuce was prepared and packaged 100 g each into the functional packaging paper box manufactured in <Example 1> to <Example 6>, and 100 g was packed with a general packaging paper box manufactured in <Comparative Example>. The remaining 100 g was left at room temperature (about 25 ℃) without any packaging.
신선도 유지 여부는 육안으로 관능 평가를 하여 시들거나 부패하는 등 노화 및 녹화 퇴색 등의 외양이 나타날 때까지의 일수를 하기 <표 4>에 나타내었다.The freshness is shown in <Table 4> until the appearance of aging and fading, such as fading or decay, by visual evaluation of visual evaluation.
전술한 바와 같이, 본 발명에 따르면 기능성 펄프 조성물이 제공된다. As mentioned above, according to the present invention a functional pulp composition is provided.
또한 본 발명에 따르면 기능성 펄프를 이용하여 제조된 기능성 포장용 지류 및 기능성 포장용 지류 상자이 제공된다.According to the present invention there is also provided a functional packaging paper and a functional packaging paper box manufactured using the functional pulp.
본 발명의 기능성 포장용 지류 및 지류 상자는 항균성, 탈취성, 신선도 유지성을 지니고 있으며, 따라서 과채류, 농작물, 화훼, 식품 등의 포장에 유용하게 사용될 수 있다.The functional packaging paper and the paper box of the present invention has antibacterial, deodorant, freshness retention, and thus can be usefully used for packaging fruits, crops, flowers, foods and the like.
Claims (15)