KR100592870B1 - A concrete with steel-making slag aggregate - Google Patents

A concrete with steel-making slag aggregate Download PDF

Info

Publication number
KR100592870B1
KR100592870B1 KR1020030091922A KR20030091922A KR100592870B1 KR 100592870 B1 KR100592870 B1 KR 100592870B1 KR 1020030091922 A KR1020030091922 A KR 1020030091922A KR 20030091922 A KR20030091922 A KR 20030091922A KR 100592870 B1 KR100592870 B1 KR 100592870B1
Authority
KR
South Korea
Prior art keywords
concrete
aggregate
slag
steelmaking slag
cement
Prior art date
Application number
KR1020030091922A
Other languages
Korean (ko)
Other versions
KR20050059970A (en
Inventor
김형석
한기현
배우현
Original Assignee
재단법인 포항산업과학연구원
주식회사 창신산업개발
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 재단법인 포항산업과학연구원, 주식회사 창신산업개발 filed Critical 재단법인 포항산업과학연구원
Priority to KR1020030091922A priority Critical patent/KR100592870B1/en
Publication of KR20050059970A publication Critical patent/KR20050059970A/en
Application granted granted Critical
Publication of KR100592870B1 publication Critical patent/KR100592870B1/en

Abstract

본 발명은 제강슬래그를 골재로 이용한 콘크리트에 관한 것이다.The present invention relates to concrete using steelmaking slag as aggregate.

본 발명은 제강슬래그 조골재 및 세골재를 단독 또는 혼합으로 사용하고, 여기에 포졸란계 혼화재를 포함하는 시멘트 및 물을 혼합하여 구성되는 콘크리트에 있어서,The present invention uses a steelmaking slag coarse aggregate and fine aggregate alone or in a mixture, and in the concrete comprising a mixture of cement and water containing a pozzolanic mixture,

상기 시멘트 첨가량 100중량부에 대하여 0.6~2.0중량부의 물유리를 추가로 첨가하는 것을 특징으로 한다.0.6 to 2.0 parts by weight of water glass is further added to 100 parts by weight of the cement addition amount.

본 발명은 물유리를 첨가함으로써 제강슬래그를 콘크리트용 골재로 사용할때 야기될 수 있는 팽창의 문제점을 해결함과 아울러 포졸란계 혼화재를 포함하는 시멘트를 사용할때 야기될 수 있는 초기강도 저하의 약점을 보완함으로써 제강슬래그 골재를 콘크리트 제조에 사용함에 있어서 안정된 품질을 보증하는 효과가 있다.The present invention solves the problem of expansion that can be caused when steelmaking slag is used as concrete aggregate by adding water glass, and also compensates for the weakness of initial strength degradation that can be caused when using cement containing pozzolanic admixture. The use of steelmaking slag aggregate in the production of concrete has the effect of ensuring stable quality.

제강슬래그, 콘크리트, 물유리, 에이징, 유리석회, 포졸란계 혼화재Steel slag, concrete, water glass, aging, glass lime, pozzolanic admixture

Description

제강슬래그를 이용한 콘크리트{A concrete with steel-making slag aggregate}A concrete with steel-making slag aggregate

본 발명은 제강슬래그를 골재로 이용한 콘크리트에 관한 것으로, 보다 상세하게는 물유리를 첨가제로 사용함에 의하여 제강슬래그내 유리석회에 의한 팽창 및 포졸란계 혼화재를 포함하는 시멘트에 의한 초기강도 저하를 억제한 제강슬래그를 이용한 콘크리트에 관한 것이다.The present invention relates to concrete using steelmaking slag as aggregate, and more particularly, steelmaking which suppresses the expansion of initial strength by cement containing pozzolan-based admixture and expansion by glass lime in steelmaking slag by using water glass as an additive. It relates to concrete using slag.

일반적으로, 유리석회를 함유하고 있지 않는 고로슬래그는 일찍부터 콘크리트용 골재로 규격화 되어 있다. 하지만, 제강슬래그는 유리석회에 의한 부피팽창으로 인하여 도로용 골재, 성토재와 같은 비교적 저급한 토목용 재료로만 활용되어 왔다.In general, blast furnace slag that does not contain glass lime has been standardized as an aggregate for concrete. However, steelmaking slag has been utilized only as a relatively low-grade civil engineering material such as road aggregates and landfills due to volume expansion by glass lime.

상기 제강슬래그는 용선으로 부터 강을 제조할때 발생되는 슬래그로써, 이러한 제강슬래그에는 슬래그 형성과정에서 완전히 슬래그화 되지 않은 생석회가 남아 있다. 또한, 슬래그화된 구성 광물중에서도 냉각 상변태시에 생석회가 석출되기도 한다. 이러한 생석회 성분들을 유리석회라고 하며, 상기 유리석회는 이후에 물과 반응하여 Ca(OH)2 상태가 되면서 부피 팽창을 야기함으로써, 균열이나, 파괴의 원인이 된다. 이러한 이유로 인해, 제강슬래그가 콘크리트용 골재로 사용된 예는 거의 없었다.The steelmaking slag is a slag generated when steel is manufactured from molten iron, and the steelmaking slag has quicklime that is not completely slagd during slag formation. In addition, quicklime may precipitate during cooling phase transformation among slag-constituted minerals. These quicklime components are called free lime, which subsequently reacts with water to form Ca (OH) 2 , causing volume expansion, which causes cracking and destruction. For this reason, few steelmaking slags have been used as aggregates for concrete.

그러나, 최근에는 자연골재가 점차 고갈되어 가고, 이에 따라 제강슬래그도 콘크리트용 골재로 사용하고자 하는 시도가 많아지고 있다. 이러한 종래기술로는 일본 공개특허공보 평5-279095호, 2001-130945호, 2003-2726호 및 2002-179451호가 있다.However, in recent years, natural aggregate is gradually depleted, and accordingly, many attempts are being made to use steelmaking slag as concrete aggregate. Such prior arts are Japanese Patent Laid-Open Nos. 5-279095, 2001-130945, 2003-2726, and 2002-179451.

상기 일본 공개특허공보 평5-279095호에서는 전로슬래그, 용선예비처리슬래그를 직경 5mm 이하로 풍쇄, 구상화하여 콘크리트용 골재로 사용하고 있다. 그러나, 상기 종래기술에서는 제강슬래그를 세골재로만 사용하고 있어, 조골제를 추가로 투입하여야 하는 문제점이 있다.In Japanese Patent Laid-Open No. 5-279095, converter slag and molten iron preliminary treatment slag are blown and spheroidized to a diameter of 5 mm or less and used as aggregate for concrete. However, since the steelmaking slag is used only as fine aggregate in the prior art, there is a problem that additionally adding coarse aggregate.

상기 일본 공개특허공보 2001-130945호는 제강슬래그를 콘크리트용 조골재로 사용한 예로써, 에이징(aging) 처리한 제강슬래그 조골재 및 세골재, 고로슬래그 미분말, 플라이 애쉬, 실리카 퓸을 사용하여 콘크리트를 제조하고 있다. 상기 종래기술에서 건전한 콘크리트를 만들기 위해서는 고로슬래그 미분말을 50% 이상 첨가하거나, 고로슬래그 미분말, 플라이 애쉬, 실리카 퓸 혼합량의 합이 50% 이상이 되어야 한다. 그러나, 상기와 같이 고로슬래그 미분말을 50% 이상 첨가하게 되면, 초기강도가 낮아질 가능성이 있어, 실제 현장에서의 몰드 및 거푸집 사용시 작업 효 율이 떨어져 공사기간이 길어지는 문제점이 있다.Japanese Laid-Open Patent Publication No. 2001-130945 is an example of using steelmaking slag as a coarse aggregate for concrete, and manufacturing concrete using aging-treated steelmaking slag coarse aggregate and fine aggregate, blast furnace slag fine powder, fly ash, and silica fume. . In order to make a healthy concrete in the prior art, 50% or more of blast furnace slag fine powder should be added, or the sum of blast furnace slag fine powder, fly ash and silica fume should be 50% or more. However, when 50% or more of the blast furnace slag powder is added as described above, there is a possibility that the initial strength may be lowered, resulting in a decrease in the work efficiency when the mold and the formwork are used in the actual site, and thus a long construction period.

상기 일본 공개특허공보 2003-2726호에서는 제강슬래그를 골재로 사용하였지만 성형방법이 일반적인 콘크리트 제조방법이 아닌 가압성형법 등의 특수한 방법을 사용한 것이다. 따라서, 상기 종래기술로는 대형 구조물을 만들 수 없는 문제점이 있다.In Japanese Laid-Open Patent Publication No. 2003-2726, steelmaking slag is used as an aggregate, but the molding method uses a special method such as a pressing method rather than a general concrete manufacturing method. Therefore, there is a problem in that the prior art can not make a large structure.

상기 일본 공개특허공보 2002-179451호에서는 제강슬래그를 골재로 사용하고 고로 수쇄슬래그 입자를 20~70% 혼합하여 기존 콘크리트 제조방법으로 콘크리트를 제조하였다. 상기 종래기술에서는 제강슬래그의 유리석회에 의한 팽창은 고로슬래그의 가용성 규산에 의해서 억제된다고 하였다. 그러나, 고로 수쇄슬래그 입자에서 용출되는 가용성 규산의 양과 속도는 유리석회가 물과 반응하여 Ca(OH)2가 되는 반응에 비하여 대단히 느리다. 따라서, 양생기간이 장기간 소요되는 문제점이 있다.In Japanese Laid-Open Patent Publication No. 2002-179451, steelmaking slag is used as an aggregate and 20 to 70% of blast furnace crushing slag particles are mixed to prepare concrete using a conventional concrete manufacturing method. In the prior art, expansion of the steel slag by free lime is suppressed by soluble silicic acid of the blast furnace slag. However, the amount and rate of soluble silicic acid eluted from the blast furnace slag particles is much slower than the reaction of free lime reacting with water to form Ca (OH) 2 . Therefore, there is a problem that the curing period takes a long time.

본 발명은 상기한 종래기술의 문제점을 해결하기 위한 것으로, 물유리를 첨가제로 사용함에 의하여 제강슬래그의 팽창을 신속히 억제하고 포졸란계 혼화재를 포함하는 시멘트에 의한 초기강도 저하를 억제한 제강슬래그를 이용한 콘크리트를 제공하는데, 그 목적이 있다.The present invention is to solve the above problems of the prior art, by using water glass as an additive to quickly suppress the expansion of the steelmaking slag and concrete using the steelmaking slag suppressed the initial strength decrease by cement containing pozzolan-based admixture To provide, the purpose is.

상기한 목적을 달성하기 위한 본 발명은, 제강슬래그 조골재 및 세골재를 단독 또는 혼합으로 사용하고, 여기에 포졸란계 혼화재를 포함하는 시멘트 및 물을 혼합하여 구성되는 콘크리트에 있어서,In the present invention for achieving the above object, in the concrete composed of steel and slag coarse aggregate and fine aggregate used alone or mixed, mixed with cement and water containing a pozzolan-based admixture,

상기 시멘트 첨가량 100중량부에 대하여 0.6~2.0중량부의 물유리를 추가로 첨가하는 것을 특징으로 한다.0.6 to 2.0 parts by weight of water glass is further added to 100 parts by weight of the cement addition amount.

이하, 본 발명을 상세하게 설명한다.EMBODIMENT OF THE INVENTION Hereinafter, this invention is demonstrated in detail.

본 발명은 제강슬래그 조골재 및 세골재를 단독 또는 혼합으로 하여 골재로 사용하고, 여기에 포졸란계 혼화재를 포함하는 시멘트 및 물을 혼합하여 구성되는 콘크리트에 있어서, 물유리를 추가로 첨가하는 것을 특징으로 한다.The present invention is characterized in that the steel slag coarse aggregate and fine aggregate are used alone or as a mixture and used as aggregate, and water glass is further added to the concrete formed by mixing cement and water including a pozzolan-based admixture.

상기 제강슬래그에는 슬래그화 되지 않은 유리석회가 남아있고, 또한 슬래그화된 구성 광물중에서도 냉각변태시 유리석회가 석출된다. 이러한 유리석회는 이후에 물과 반응하여 Ca(OH)2 상태가 되면서 2배 이상의 부피팽창을 일으키게 되며, 이후 박리, 균열, 파괴의 원인이 된다. 따라서, 제강슬래그는 도로용 골재, 성토재와 같은 비교적 저급의 토목용 재료로만 활용되어 왔다.In the steelmaking slag, unslagized glass lime remains, and also in the slag-constituted minerals, glass lime precipitates upon cooling transformation. These glass limes are subsequently reacted with water to form Ca (OH) 2 , causing more than two times of volume expansion, and then causing peeling, cracking, and breaking. Therefore, steelmaking slag has been utilized only for relatively low-grade civil engineering materials such as road aggregates and fillets.

본 발명에서는 상기와 같은 유리석회에 의한 부피팽창을 억제하기 위하여, 물유리를 첨가하여 가용성 규산을 신속하게 공급함으로써, 칼슘실리케이트를 생성시켜 팽창을 억제하게 된다.In the present invention, in order to suppress the volume expansion caused by the glass lime as described above, by adding water glass and rapidly supplying soluble silicic acid, calcium silicate is produced to suppress expansion.

상기 물유리는 물에 투입되면 즉각적으로 가용성 규산과 소다성분으로 해리되어 가용성 규산을 공급함으로써, 유리석회에서 생성된 Ca(OH)2와 곧바로 반응하여 칼슘실리케이트를 생성하여 이후의 팽창을 억제하게 된다. 또한, 상기 소다성분은 고로슬래그 미분말의 수화를 활성화시켜 초기강도를 증진시킬 수 있는 효과가 있다.The water glass immediately dissociates into soluble silicic acid and soda component when supplied to water to supply soluble silicic acid, thereby directly reacting with Ca (OH) 2 generated from glass lime to form calcium silicate to inhibit subsequent expansion. In addition, the soda component has the effect of increasing the initial strength by activating the hydration of the blast furnace slag fine powder.

상기 물유리의 첨가량이 시멘트 첨가량 100중량부에 대하여 0.6중량부 미만이면 초기강도를 확보할 수 없고, 2.0중량부를 초과하면 내해수성을 저하시키는 문제점이 있으므로, 상기 물유리 첨가량은 시멘트 첨가량 100중량부에 대하여 0.6~2.0중량부로 제한하는 것이 바람직하다.If the added amount of the water glass is less than 0.6 parts by weight based on 100 parts by weight of cement, the initial strength cannot be secured. If the amount of water glass is more than 2.0 parts by weight, there is a problem of lowering the seawater resistance. It is preferable to limit it to 0.6-2.0 weight part.

본 발명에 있어서 에이징 처리한 제강슬래그를 사용한다면 제강슬래그의 부피팽창을 보다 저감할 수 있어 보다 바람직하다.In the present invention, when the aging steelmaking slag is used, the volume expansion of the steelmaking slag can be further reduced, which is more preferable.

또한, 본 발명에 있어서 시멘트에 포함되는 포졸란계 혼화재로는 고로 슬래그 미분말, 플라이 애쉬, 실리카 퓸 등이 있다.Further, in the present invention, the pozzolan-based admixture included in cement includes blast furnace slag fine powder, fly ash, silica fume and the like.

본 발명에서와 같이 제강슬래그를 골재로 사용할 경우에는 미량의 철분이 장기간에 걸쳐 용출되어 나옴으로써, 식물의 생육에 좋은 효과를 나타낸다. 특히, 인공어초 및 해중림초와 같은 해양생태계 복원용 구조물용으로 사용시 상당히 좋은 효과를 얻을 수 있다.When steelmaking slag is used as an aggregate as in the present invention, a small amount of iron is eluted for a long time, thereby showing a good effect on plant growth. In particular, when used for the structure for marine ecosystem restoration such as artificial reefs and marine deforestation can be obtained a very good effect.

또한, 제강슬래그는 기존의 천연 쇄석보다 단단하여 좋은 내마모성을 나타내며, 이로 인해 동일 배합의 경우에 자연쇄석을 사용한 콘크리트보다 높은 압축강도를 나타낸다. 따라서, 팽창과 관련된 문제점을 상기와 같은 방법을 통해 해결한다면, 콘크리트로 제조되는 파일(pile), 전신주, 암거 및 수로관 등의 2차 제품의 재료로도 매우 적합하다.In addition, steelmaking slag is harder than the existing natural crushed stone shows good wear resistance, and thus exhibits higher compressive strength than concrete using natural crushed stone in the same formulation. Therefore, if the problem associated with expansion is solved through the above method, it is also very suitable as a material of secondary products such as piles, telegraph poles, culverts and water pipes made of concrete.

이하, 실시예를 통하여 본 발명은 보다 상세하게 설명한다.Hereinafter, the present invention will be described in more detail with reference to Examples.

[실시예1]Example 1

제강슬래그 세골재:제강슬래그 조골재=1:1, 물:시멘트=1:1로 하여 콘크리트를 배합하였다. 이때, 시멘트는 4,000±10㎠/g 입도의 고로슬래그 미분말이 45% 혼합된 슬래그시멘트를 사용하였고, 제강슬래그 골재는 0.15~5mm를 세골재로 사용하였고, 5~25mm를 조골재로 사용하였으며, 물유리 첨가량은 하기 표 1과 같다.Steelmaking slag fine aggregate: Steelmaking slag coarse aggregate = 1: 1, water: cement = 1: 1 Concrete was mix | blended. At this time, cement was used slag cement mixture of blast furnace slag powder of 4,000 ± 10㎠ / g particle size 45%, steel slag aggregate was used 0.15 ~ 5mm fine aggregate, 5 ~ 25mm coarse aggregate, water glass addition amount Is shown in Table 1 below.

상기와 같이 제조된 시편은 성형후 24시간 경과 후 탈형을 실시하고, 탈형 후 23℃의 항온 수조에서 24시간 양생하여 초기 압축강도를 측정하였고, 같은 배합의 시편을 28일간 양생하여 ASTM C 1202-97에 명시된 방법에 의해 염소이온 침투저항성을 측정하였으며, 그 결과는 하기 표 1과 같다.The specimen prepared as described above was demolded after 24 hours after molding, and cured in a constant temperature water bath at 23 ° C. for 24 hours to measure initial compressive strength. The specimens of the same formulation were cured for 28 days to ASTM C 1202- Chlorine ion penetration resistance was measured by the method specified in 97, and the results are shown in Table 1 below.

구분division 물유리 첨가량 (시멘트 첨가량 100 중량부에 대한 중량부)Water glass addition amount (parts by weight based on 100 parts by weight of cement) 초기 압축강도 (kg/㎠)Initial compressive strength (kg / ㎠) 28일 양생후 염소이온 침투 저항성 (coulombs)Resistance to chloride ion penetration after 28 days of curing (coulombs) 비교재1Comparative Material 1 00 5858 11381138 비교재2Comparative Material 2 0.20.2 6666 12111211 비교재3Comparative Material 3 0.40.4 7272 12451245 발명재1Invention 1 0.60.6 8080 12321232 발명재2Invention 2 0.80.8 9292 13751375 발명재3Invention 3 1.01.0 9797 13401340 발명재4Invention 4 1.21.2 112112 14921492 발명재5Invention 5 1.41.4 116116 17711771 발명재6Invention 6 1.61.6 124124 20122012 발명재7Invention 7 1.81.8 127127 22152215 발명재8Invention Material 8 2.02.0 129129 22782278 비교재4Comparative Material 4 2.22.2 131131 24002400

상기 표 1에서 알 수 있는 바와 같이, 본 발명의 범위를 만족하는 발명재1~8은 비교재에 비하여 우수한 초기강도를 가질 뿐만 아니라 염소이온 침투에 대한 저항성도 2300coulomb 이하로 내해수성도 매우 우수함을 알 수 있다.As can be seen in Table 1, Inventive Materials 1 to 8 satisfying the scope of the present invention not only has excellent initial strength compared to the comparative material, but also has excellent resistance to chlorine ion penetration of 2300 coulomb and excellent seawater resistance. Able to know.

그러나, 물유리 첨가량이 본 발명의 범위보다 적은 비교재1~3은 초기강도가 부족한 문제점이 있었으며, 물유리 첨가량이 본 발명의 범위보다 많은 비교재4는 내해수 저항성이 떨어지는 문제점이 있었다. 이때 물유리 첨가량이 2.0중량부를 초과하는 경우에는 고로슬래그 미분말의 활성이 과도하게 촉진되어 콘크리트 조직의 치밀도가 저하되었기 때문인 것으로 판단되었다.However, Comparative Materials 1 to 3 in which the amount of added water glass is less than the range of the present invention had a problem of insufficient initial strength, and Comparative Material 4 in which the amount of added water glass was more than the range of the present invention had a problem of inferior seawater resistance. In this case, when the amount of added water glass exceeded 2.0 parts by weight, it was determined that the activity of the blast furnace slag fine powder was excessively accelerated and the density of the concrete structure was lowered.

하기 표 2는 종래의 고로슬래그 미분말의 자극제로 많이 사용되던 소석회 분말의 첨가량에 따른 특성변화를 나타낸 것이다.Table 2 shows the characteristics change according to the amount of addition of the slaked lime powder which was used as a stimulant of the conventional blast furnace slag fine powder.

구분division Ca(OH)2 첨가량 (시멘트 첨가량 100중량부에 대한 중량부)Ca (OH) 2 addition amount (weight part with respect to 100 weight part of cement addition amounts) 초기 압축강도 (kg/㎠)Initial compressive strength (kg / ㎠) 28일 양생 후 염소이온 침투 저항성 (coulomb)Resistance to chloride ion penetration after 28 days of curing (coulomb) 종래재1Conventional Materials 1 2.02.0 7575 18351835 종래재2Conventional material 2 2.52.5 7373 20172017 종래재3Conventional Materials 3 3.03.0 9898 23122312 종래재4Conventional Materials 4 3.53.5 119119 25432543 종래재5Conventional Materials 5 4.04.0 122122 26692669 종래재6Conventional Materials 6 4.54.5 125125 27382738 종래재7Conventional Materials 7 5.05.0 134134 30113011

상기 표 2에서 알 수 있는 바와 같이, 종래의 소석회를 첨가하는 경우에는 초기 압축강도는 증가시킬 수 있으나, 내해수성(염소이온침투 저항성)을 함께 만족시키지는 못하고 있다.As can be seen in Table 2, when the conventional slaked lime is added, the initial compressive strength can be increased, but it does not satisfy the seawater resistance (chlorine ion permeation resistance) together.

[실시예2]Example 2

실시예 1과 같은 배합방법으로 하기 표 3에 나타낸 바와 같이, 천연쇄석 골재와 제강슬래그 골재에 대해서 각 재령에 따른 압축강도 변화를 관찰하였다. 천연쇄석 콘크리트의 경우 세골재는 표준사를 사용하였고, 제강슬래그 콘크리트의 경우는 제강슬래그 세골재를 사용하였다. 물유리를 첨가한 경우, 물유리 첨가량은 시멘트 100중량부에 대하여 1.5중량부를 사용하였다.As shown in Table 3 by the same mixing method as in Example 1, the changes in compressive strength for each age was observed for natural crushed aggregate and steelmaking slag aggregate. In the case of natural crushed concrete, fine aggregate was used as standard yarn, and in the case of steel slag concrete, steel aggregate slag fine aggregate was used. When water glass was added, the water glass addition amount used 1.5 weight part with respect to 100 weight part of cement.

구분division 3일 강도 (kgf/㎠)3 days strength (kgf / ㎠) 7일 강도 (kgf/㎠)7 days strength (kgf / ㎠) 28일 강도 (kgf/㎠)28 days strength (kgf / ㎠) 3개월 강도 (kgf/㎠)3 months intensity (kgf / ㎠) 6개월 강도 (kgf/㎠)6 months strength (kgf / ㎠) 천연쇄석 콘크리트Natural crushed concrete 125125 249249 389389 463463 472472 물유리 첨가 천연쇄석 콘크리트Water Glass Added Natural Stone 149149 279279 392392 455455 468468 제강슬래그 콘크리트Steel slag concrete 106106 254254 407407 475475 489489 물유리 첨가 제강슬래그 콘크리트Steel slag concrete with water glass 162162 301301 415415 478478 496496

먼저, 천연쇄석콘크리트와 제강슬래그 콘크리트를 비교하면, 초기강도에 있어서 천연쇄석콘크리트가 다소 높은 압축강도를 보이고 있다. 이것은 제강슬래그 골재에서 용출되는 유리석회의 팽창에 의해 강도가 다소 저하되기 때문인 것으로 판단되었다.First, when comparing natural crushed concrete and steelmaking slag concrete, natural crushed concrete shows a rather high compressive strength in initial strength. This was judged to be due to a slight decrease in strength due to the expansion of the glass lime eluted from the steelmaking slag aggregate.

천연골재 콘크리트에 물유리를 첨가하였을 경우의 초기강도 개선은 물유리의 소다성분에 의해 고로슬래그 미분말의 수화가 촉진되어 일어난 것으로 판단되었다.The initial strength improvement when water glass was added to natural aggregate concrete was considered to be caused by the hydration of blast furnace slag powder by the soda component of water glass.

제강슬래그 콘크리트에 물유리를 첨가한 시편이 초기강도 개선 효과가 가장 크며, 장기강도 측면에서도 가장 우수하게 나타났다. 이것은 제강슬래그의 팽창 약점을 보완하면서도, 동시에 고로슬래그 미분말의 수화 활성을 촉진하여 초기강도 발현을 촉진함으로써 제강슬래그 골재가 가지는 고강도 특성이 그대로 반영되었기 때문으로 판단되었다.The specimens with water glass added to steelmaking slag concrete had the greatest initial strength improvement effect and the best long-term strength. This is because the high strength characteristics of steelmaking slag aggregates are reflected as they compensate for the weakness of expansion of steelmaking slag, while at the same time promoting the hydration activity of the blast furnace slag fine powder.

상술한 바와 같이, 본 발명에 따르면 물유리를 첨가함으로써 제강슬래그를 콘크리트용 골재로 사용할때 야기될 수 있는 팽창의 문제점을 해결함과 아울러 포졸란계 혼화재를 포함하는 시멘트를 사용할때 야기될 수 있는 초기강도 저하의 약점을 보완함으로써 제강슬래그 골재를 콘크리트 제조에 사용함에 있어서 안정된 품질을 보증하는 효과가 있다. As described above, according to the present invention, the addition of water glass solves the problem of expansion that may occur when steelmaking slag is used as concrete aggregate, and the initial strength that may be caused when using cement including pozzolan-based admixtures. Complementing the weakness of the degradation has the effect of ensuring a stable quality in the use of steelmaking slag aggregate in the production of concrete.

또한, 본 발명에 따르면 콘크리트의 내해수성도 확보되어 해양용 구조물로도 이용이 가능한 추가적인 효과가 있다.In addition, according to the present invention there is an additional effect that can also be used as a marine structure to ensure the sea water resistance of concrete.

Claims (2)

제강슬래그 조골재 및 세골재를 단독 또는 혼합으로 사용하고, 여기에, 포즐란계 시멘트 및 물을 혼합하여 구성되는 콘크리트에 있어서,In the concrete composed of steel slag coarse aggregate and fine aggregate used alone or in a mixture, and mixed with a foslan-based cement and water, 상기 시멘트 첨가량 100중량부에 대하여 0.6~2.0 중량부의 물유리를 첨가하여 조성됨을 특징으로 하는 제강슬래그를 이용한 콘크리트.Concrete using steel slag, characterized in that the composition is added by adding 0.6 ~ 2.0 parts by weight of water glass based on 100 parts by weight of the cement. 제 1항에 있어서, 상기 제강슬래그는 에이징 공정을 거친 것임을 특징으로 하는 제강슬래그를 이용한 콘크리트.The method of claim 1, wherein the steelmaking slag is a concrete using steelmaking slag, characterized in that through the aging process.
KR1020030091922A 2003-12-16 2003-12-16 A concrete with steel-making slag aggregate KR100592870B1 (en)