KR100540068B1 - Method of manufacturing a mold for lens production with primitive bridge - Google Patents

Method of manufacturing a mold for lens production with primitive bridge Download PDF

Info

Publication number
KR100540068B1
KR100540068B1 KR1020030081910A KR20030081910A KR100540068B1 KR 100540068 B1 KR100540068 B1 KR 100540068B1 KR 1020030081910 A KR1020030081910 A KR 1020030081910A KR 20030081910 A KR20030081910 A KR 20030081910A KR 100540068 B1 KR100540068 B1 KR 100540068B1
Authority
KR
South Korea
Prior art keywords
segment
blank
processing
mold
fused
Prior art date
Application number
KR1020030081910A
Other languages
Korean (ko)
Other versions
KR20050048084A (en
Inventor
정승희
Original Assignee
정승희
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 정승희 filed Critical 정승희
Priority to KR1020030081910A priority Critical patent/KR100540068B1/en
Publication of KR20050048084A publication Critical patent/KR20050048084A/en
Application granted granted Critical
Publication of KR100540068B1 publication Critical patent/KR100540068B1/en

Abstract

본 발명은 원시교정부가 하측에 형성된 안경렌즈를 생산하기 위한 몰드를 제조하는 방법에 관한 것으로, 무도수 렌즈의 하부에 원시교정부가 반달형태로 형성되는 렌즈를 제조할 수 있도록 하는 몰드를 제조하는 것이다.The present invention relates to a method for manufacturing a mold for producing a spectacle lens formed on the lower side of the primitive correction portion, and to manufacture a mold that enables the primitive correction portion to produce a lens formed in a half moon shape on the lower portion of the non-curable lens. .

이러한 본 발명은 도수가 형성되지 않은 렌즈의 하부에 반달형의 원시교정부를 형성시키기 위한 것으로, 도수가 형성되지 않은 가공전 블랭크를 가공하는 몰드1차가공공정과, 상기 블랭크의 하측에 융착되는 세그먼트를 가공하는 세그먼트 가공공정과, 상기 세그먼트를 블랭크의 하측에 융착시키는 세그먼트 융착공정과, 세그먼트가 융착된 블랭크를 최공가공하는 몰드최종공정을 수행하므로서 유리몰드를 제조하는 것으로, 시력이 정상인 사람이 착용하고 다니면서 원시교정부를 통하여 원시를 보정할 수 있는 것이다.The present invention is to form a half-moon type primitive correction unit in the lower portion of the lens is not formed, the mold primary processing step of processing the blank before the processing is not formed, and the segment fused to the lower side of the blank The glass mold is manufactured by performing a segment processing process for processing, a segment fusion process for fusion of the segment on the lower side of the blank, and a final process for molding the blank in which the segment is fused. Throughout the primitive government, primitive correction is possible.

Description

원시교정부가 형성된 렌즈 생산용 몰드의 제조방법{omitted}Method for manufacturing mold for lens production with primitive bridge

도 1은 본 발명 몰드에 의해 제조된 안경렌즈의 평면도1 is a plan view of the spectacle lens produced by the mold of the present invention

도 2는 본 발명 유리몰드의 단면도2 is a cross-sectional view of the glass mold of the present invention

도 3은 본 발명 몰드에 의해 제조된 안경렌즈의 단면도Figure 3 is a cross-sectional view of the spectacle lens produced by the mold of the present invention

도 4는 본 발명의 모재인 블랭크의 단면도4 is a cross-sectional view of a blank as a base material of the present invention.

도 5는 몰드1차가공공정의 모따기 과정을 거친 블랭크의 단면도Figure 5 is a cross-sectional view of the blank after the chamfering process of the mold primary processing process

도 6은 본 발명의 세그먼트 사시도6 is a perspective view of a segment of the present invention

도 7은 본 발명의 세그먼트를 고정치구에 고정시킨 상태의 단면도7 is a cross-sectional view of a state in which a segment of the present invention is fixed to a fixture.

도 8은 본 발명의 세그먼트에 절단면을 형성시킨 상태의 단면도8 is a cross-sectional view of the cutting surface formed on the segment of the present invention.

도 9는 본 발명의 세그먼트 접착 상태도Figure 9 is a state of segment adhesion of the present invention

도 10은 본 발명의 세그먼트 R값 가공상태도Figure 10 is a segment R value processing state diagram of the present invention

도 11은 본 발명의 블랭크에 세그먼트를 결합시킨 상태 단면도11 is a cross-sectional view of a state in which a segment is bonded to the blank of the present invention.

도 12는 본 발명의 보호막 도포 상태도12 is a protective film coating state of the present invention

도 13은 본 발명의 세그먼트 가공상태도Figure 13 is a segment processing state of the present invention

도 14는 본 발명의 블랭크 비사용면 가공상태도14 is a blank non-use surface processing state diagram of the present invention

[ 도면의 주요부분에 대한 부호의 설명 ][Description of Code for Major Parts of Drawing]

1 : 안경렌즈 2 : 무도수부1: eyeglass lens 2: non-transparent part

3 : 원시교정부 5 : 블랭크3: primitive government 5: blank

10 : 세그먼트 11 : 절단면10: segment 11: cutting surface

18 : 보호막 20 : 유리몰드18: protective film 20: glass mold

본 발명은 원시교정부가 하측에 형성된 안경렌즈를 생산하기 위한 몰드를 제조하는 방법에 관한 것으로, 무도수 렌즈의 하부에 원시교정부가 반달형태로 형성되는 렌즈를 제조할 수 있도록 하는 몰드를 제조하는 것이다.The present invention relates to a method for manufacturing a mold for producing a spectacle lens formed on the lower side of the primitive correction portion, and to manufacture a mold that enables the primitive correction portion to produce a lens formed in a half moon shape on the lower portion of the non-curable lens. .

나이가 들면 자연히 원시가 찾아오게 되는 것으로, 원시를 교정하기 위해서는 돋보기를 착용하여야 하나, 근시는 없으나 원시가 있는 사람은 돋보기를 가지고 다니면서 필요한 경우에만 돋보기를 착용하여 사용하므로서 돋보기를 휴대하고 보관하는 일이 번거러운 것이었다.As you grow older, you will naturally find a hyperopia, but you need to wear a magnifying glass to correct the hyperopia. This was cumbersome.

즉 시력이 정상적인 사람은 원시가 찾아온 경우 돋보기를 사용하여야 하나 돋보기를 별도로 휴대하고 다닐 경우 휴대에 불편함과 함께 자주 잊고 다님으로서 정작 필요할 때에 사용을 할 수 없는 문제가 있는 것이었다.In other words, people who have normal vision should use a magnifying glass when the primitive comes, but if they carry the magnifying glass separately, they are inconvenient to carry and often forget about it.

본 발명은 상기와 같은 점을 감안하여 무도수 안경렌즈의 하측에 반달형의 원시교정부를 형성시킴으로서 평상시는 도수가 형성되지 않은 무도수부를 통하여 사물을 보고, 근거리를 볼 때는 원시교정부를 통하여 식별할 수 있도록 하는 것으 로, 원시만 있는 사람이 돋보기를 잊고 다녀 생활에 불편을 초래하는 경우를 없애도록 하는 것이다.In view of the above, the present invention forms a half-moon primitive correction unit on the lower side of the martial arts-free spectacle lens, so that a person can usually identify the object through the non-precision martial arts unit through the primitive correction unit. It is to make sure that people who have only primitives forget the magnifying glass and cause inconvenience to life.

이러한 본 발명은 도수가 형성되지 않은 렌즈의 하부에 반달형의 원시교정부를 형성시키기 위한 것으로, 도수가 형성되지 않은 가공전 유리인 블랭크를 가공하는 몰드1차가공공정과, 상기 블랭크의 하측에 융착되는 세그먼트를 가공하는 세그먼트 가공공정과, 상기 세그먼트를 블랭크의 하측에 융착시키는 세그먼트 융착공정과, 세그먼트가 융착된 블랭크를 최공가공하는 몰드최종공정을 수행하므로서 유리몰드를 제조하는 것으로, 원시만 있는 사람이 착용하고 다니면서 원시교정부를 통하여 원시를 보정 할 수 있는 것이다.The present invention is to form a half-moon primitive bridge to the lower portion of the lens is not formed, the primary molding process for processing a blank glass before processing is not formed, and fused to the lower side of the blank A person who has only a raw material is manufacturing a glass mold by performing a segment processing process for processing a segment, a segment fusion process for fusion of the segment on the lower side of the blank, and a mold final process for processing the blank in which the segment is fused. It can be worn and carried around through primitive governments to correct primitives.

본 발명은 도수가 형성되지 않은 무도수부(2)와 원시교정부(3)를 하나의 렌즈(1)에 형성시키되 상기 원시교정부(3)는 렌즈(1)의 하측에 반달형을 갖도록 형성한 것으로, 가공전 유리인 블랭크(5)를 렌즈 형태로 가공하되 도수가 형성되지 않는 상태로 가공하는 몰드1차가공공정과, 상기 블랭크(5)의 하측에 융착되고 원시교정용 도수를 갖는 세그먼트(10)를 가공하는 세그먼트 가공공정과, 상기 세그먼트(10)를 블랭크(5)의 하측에 융착시키는 세그먼트 융착공정과, 세그먼트(10)가 융착된 블랭크(5)를 유리몰드(20)로 최종 가공하는 몰드최종공정을 수행하므로서 이루어진다.According to the present invention, the non-power-free part 2 and the primitive bridge portion 3, in which no frequency is formed, are formed in one lens 1, but the primitive bridge portion 3 is formed to have a half moon shape under the lens 1. And a mold primary processing step of processing the blank 5, which is glass before processing, in the form of a lens but not in the state of forming a lens, and a segment having a fusion rate at the lower side of the blank 5 and having a raw correction power ( 10) a segment processing process for processing the segment, a segment fusion process for fusion bonding the segment 10 on the lower side of the blank 5, and a blank process 5 in which the segment 10 is fused with the glass mold 20. By performing the final mold process.

본 발명의 몰드1차가공공정은 모재를 선택하여 도수가 형성되지 않는 상태로 연마 가공하는 공정에 관한 것으로, 모재인 가공전 유리인 블랭크(5)를 선택하여 선택된 R값에 맞게 절삭가공하되 도수가 형성되지 않게 가공하는 초벌가공과정과, 초벌가공이 완료된 블랭크(5)의 외측면을 모따기하는 모따기과정과, 모따기가 완료된 블랭크(5)를 펠렛가공기로 이차 가공하는 펠렛과정과, 펠렛가공된 블랭크(5)의 사용면과 비사용면을 우레탄 패드로 연마하여 광택을 내주는 연마과정을 수행하므로서 이루어진다.The mold primary processing process of the present invention relates to a process of polishing by selecting the base material and the state is not formed, the blank (5) of the glass before the base material is selected to be cut to match the selected R value And a pelletizing process for secondary processing the blanks 5, which have been chamfered, with a pellet processing machine, and a pellet processing process. The use surface and the non-use surface of the blank 5 are polished with a urethane pad, thereby performing a polishing process to give a gloss.

본 발명의 세그먼트 가공공정은 원형의 세그먼트(10)를 양분하고 양분된 절단면(11)이 상부를 향하게 고정치구(15)에 경사지게 채우고 접착제로 접착시키는 세그먼트 고정과정과, 고정된 세그먼트(10)의 절단면(11)을 경사지게 절삭하고 연마지를 사용하여 절단면(11)을 연마하여 가공하는 절단면 가공과정과, 세그먼트(10)를 분리하여 양 절단면(10)이 서로 마주보는 형태로 배치하고 접착제(16)로 절단면을 접착시키는 세그먼트 접착과정과, 상기 세그먼트(10)의 하부는 블랭크(5)의 R값에 맞추어 가공하고 상부는 원시교정부(3)의 R값에 맞추어 가공하는 세그먼트 커브가공 과정과, 상기 세그먼트(10)의 커브를 연마하고 세그먼트(10)를 분리하여 세그먼트(10)를 완성하는 세그먼트 완성과정으로 이루어진다.The segment processing process of the present invention bisects a segment fixing process of dividing the circular segment 10 and filling the fixing jig 15 inclinedly with the bisected cutting surface 11 facing upwards, and bonding with adhesive, The cutting surface processing process of cutting the cutting surface 11 inclined and polishing the cutting surface 11 using abrasive paper, and separating the segment 10 so that both cutting surfaces 10 face each other and the adhesive 16 Segment bonding process for bonding the cutting surface to the furnace, and the lower part of the segment 10 is processed according to the R value of the blank (5) and the upper part is the segment curve processing process to be processed according to the R value of the primitive bridge (3), Polishing the curve of the segment 10 and the segment 10 is separated to complete the segment 10 consists of a segment completion process.

본 발명의 세그먼트 융착공정은 도수가 형성되지 않은 블랭크(5)의 하측에 세그먼트(10)의 절단면(11)이 위치할 라인을 선정하는 라인선정과정과, 세그먼트(10)를 그어진 라인에 맞추어 결합시키되 절단면(11)의 하부가 블랭크(5)에 밀착되도록 잡아주는 세그먼트 결합과정과, 블랭크(5)를 전기로에 넣고 가열하여 세그먼트(10)를 블랭크(5)에 융착시키는 세그먼트 융착과정과, 블랭크(5)에 세 그먼트(10)가 융착되면 전기로에서 꺼내어 블랭크(5)와 절단면(11)에 보호막(18)을 도포하는 보호막 도포과정을 수행하므로서 이루어진다.In the segment fusion process of the present invention, a line selection process of selecting a line on which the cut surface 11 of the segment 10 is to be positioned below the blank 5 in which no frequency is formed, and combining the segment 10 in accordance with the drawn line Segment joining process to hold the lower portion of the cutting surface 11 to be in close contact with the blank (5), Segment fusion process for welding the segment 10 to the blank (5) by placing the blank (5) in the electric furnace and the blank, When the segment 10 is fused to (5), it is made by carrying out a protective film applying process of taking out of the electric furnace and applying the protective film 18 to the blank 5 and the cut surface 11.

본 발명의 몰드최종공정은 커브가공기로 세그먼트(10)를 절삭하고 펠렛가공기로 세그먼트(10)를 가공하는 사용면 가공과정과, 블랭크(5)와 절단면(11)에 부착된 보호막(18)을 제거하는 보호막 제거과정과, 블랭크(5)의 비사용면을 가공하여 광택을 내는 비사용면 가공과정을 수행하므로서 유리몰드(20)를 제조하게 되는 것이다.The mold final process of the present invention is a surface treatment process for cutting the segment 10 with a curve machine and processing the segment 10 with a pellet machine, and a protective film 18 attached to the blank 5 and the cut surface 11. The glass mold 20 is manufactured by performing a removal process of removing the protective film and processing an unused surface of the blank 5 to polish the unused surface.

이러한 본 발명을 첨부도면에 의거 상세히 설명하면 다음과 같다.Referring to the present invention in detail based on the accompanying drawings as follows.

본 발명은 도 1 또는 도 3에 도시된 바와 같은 안경렌즈(1)를 제작하기 위하여 도 2에 도시된 유리몰드(20)를 제작하는 것으로, 먼저 초벌가공공정을 수행하여 도수가 형성되지 않은 블랭크(5)를 제작하는 과정을 살펴본다.The present invention is to produce the glass mold 20 shown in Figure 2 in order to manufacture the spectacle lens 1 as shown in Figure 1 or Figure 3, first to perform the first machining process blank is not formed blank Examine the process of making (5).

모재인 몰드를 선정하되 제작을 원하는 렌즈의 곡률 반경에 맞는 블랭크(5)를 선정하여 커브 가공기로 초벌가공과정을 수행하여 블랭크(5)를 절삭 가공하도록 하며, 상기 블랭크(5)는 절삭 후 도 4 와 같이 일반적인 근시 교정용 안경렌즈와 유사한 형태가 되나 블랭크(5)에 도수가 형성되지 않은 선그라스와 같은 일반렌즈의 형태가 된다.The mold is selected as the base material, but the blank 5 suitable for the radius of curvature of the lens desired to be manufactured is selected, and the blank 5 is cut by performing the initial machining process with a curve machine, and the blank 5 is cut after cutting. As shown in FIG. 4, the lens is similar to a general myopia correcting spectacle lens, but has a form of a general lens such as sunglass in which no power is formed on the blank 5.

초벌가공이 끝난 블랭크(5)는 외측 각진 부분을 깍아 내는 면취기를 이용하여 도 5 와 같이 모따기과정을 수행하도록 하고, 모따기과정이 끝나면 펠렛 가공기를 이용한 펠렛과정을 거치도록 하여 이차 가공을 하도록 하되 상기 펠렛가공기는 접시형의 가공 치구에 펠렛 다이아몬드를 접합한 후 이를 회전시켜가며 블랭크(5) 를 가공하게 된다.Blanks (5) after the first processing is to perform a chamfering process as shown in Figure 5 using a chamfer to cut out the outer angled part, and after the chamfering process is subjected to a secondary process by going through a pellet process using a pellet processing machine Pellet processing machine is to bond the pellet diamond to the dish-like jig and then rotate it to process the blank (5).

펠렛과정이 완료되면 블랭크(5)의 외표면을 우레탄 패드에 연마재를 묻혀 광택을 내면서 연마하게 되는 연마과정을 거치도록 하고, 연마과정이 완료된 블랭크(5)는 검사공정을 거쳐 합격된 것만 사용하도록 한다.When the pellet process is completed, the outer surface of the blank 5 is polished by polishing it with a polishing pad on the urethane pad, and the polishing process is completed. do.

이같이 도수가 형성되지 않은 블랭크(5)가 제조되면 상기 블랭크(5)의 하측을 가려주고 블랭크(5)에 융착되는 세그먼트(10)를 제조하여야 하며, 상기 세그먼트(10)를 제조하는 과정은 다음과 같다.As such, when the blank 5 having no frequency is formed, a segment 10 that covers the lower side of the blank 5 and is fused to the blank 5 should be manufactured. The process of manufacturing the segment 10 is as follows. Same as

세그먼트(10)는 블랭크(5)의 직경과 같은 것을 사용하되 도 6 과 같이 원형으로 제작한 후 이를 양분하여 사용하도록 한다.Segment 10 is to use the same as the diameter of the blank (5) but to make a circular shape as shown in Figure 6 to use it by dividing it.

평편한 판상이고 반원형의 형상을 갖는 세그먼트(10)를 도 7 과 같이 고정치구(15)에 쌓아주되 절단면(11)이 상부로 향하게 하고, 상기 세그먼트(10)는 핏치와 송진을 혼합한 접착제로 고정치구(15)에 접착하여 고정시키는 세그먼트 고정과정을 수행한다.A flat plate-like and semi-circular shape segment 10 is stacked on the fixture jig 15 as shown in FIG. 7, with the cutting surface 11 facing upward, and the segment 10 is made of an adhesive mixed with pitch and rosin. A segment fixing process of bonding and fixing the fixing fixture 15 is performed.

고정치구(15)에 고정된 세그먼트(10)는 상부를 도 8 과 같이 절삭하여 절단면(11)을 형성시키도록 하되 상기 세그먼트(10)의 절단면(11)은 경사각도가 18-20도를 갖도록 하며, 상기 세그먼트(10)의 절단면(11)이 18-20도를 갖도록 할 경우 본 발명에 의해 제조되는 유리몰드(20)를 장기간 사용할 수 있게 된다.The segment 10 fixed to the fixture jig 15 is to cut the upper portion as shown in Figure 8 to form a cutting surface 11, but the cutting surface 11 of the segment 10 has an inclination angle of 18-20 degrees. And, if the cut surface 11 of the segment 10 to have 18-20 degrees, the glass mold 20 manufactured by the present invention can be used for a long time.

상기와 같이 절단면(11)이 형성된 세그먼트(10)는 절단면(11)을 우레탄 패드로 연마하여 광택을 내도록 하고, 세그먼트(10)의 절단면(11) 연마가 완료되면 고정치구(15)에 경유를 부어 세그먼트(10)를 분리시키도록 한다.As described above, the segment 10 on which the cutting surface 11 is formed is polished by polishing the cutting surface 11 with a urethane pad, and after the cutting of the cutting surface 11 of the segment 10 is completed, light oil is applied to the fixing fixture 15. Pour segment 10 to separate.

분리된 세그먼트(10)는 도 9 에 도시된 바와 같이 절단면(11)이 서로 마주보는 상태로 놓은 후 경사면 사이에 접착제(16)를 도포하여 세그먼트(10)끼리 서로 접착 고정시키도록 하며, 여기서 접착제(16)는 세그먼트(10)의 접착과 함께 연마가 끝난 절단면(11)을 보호해 주게 된다.As shown in FIG. 9, the separated segments 10 are placed with the cutting surfaces 11 facing each other, and then the adhesive 16 is applied between the inclined surfaces so that the segments 10 are adhesively fixed to each other. (16) protects the cutting surface 11 which has been polished together with the adhesion of the segment (10).

그리고 세그먼트(10)를 고정시킨 후에는 세그먼트(10)의 상부는 원시교정부(3)의 R값에 맞추어 가공하고, 하측은 블랭크(5)의 R값에 맞추어 도 10 과 같이 가공하도록 하되 하측의 R값은 블랭크(5)의 R값보다 두칸 정도 높게 하여 가공하므로서 세그먼트(10)와 블랭크(5)의 융착 작업시 공기가 잘 빠지고 융착이 일정하게 될 수 있도록 한다.After fixing the segment 10, the upper part of the segment 10 is machined in accordance with the R value of the primitive cross section 3, and the lower side is machined in accordance with the R value of the blank 5 as shown in FIG. R value of is to be processed by two spaces higher than the R value of the blank (5) so that the air during the fusion operation of the segment (10) and the blank (5) is good to remove the fusion is constant.

즉 블랭크(5)의 R값보다 2도 정도 높게 가공하여 세그먼트(10)가 블랭크(6)에 놓여질 때 절단면(11)의 하측이 맞닿을 때 나머지 부위는 약간 떨어지게 하여 융착시 절단면(11)의 하부에서부터 순차적으로 융착이 이루어지도록 하여 융착이 일정하게 이루어질 수 있도록 한다.In other words, when the segment 10 is placed on the blank 6 and the lower side of the cutting surface 11 abuts, the remaining portion is slightly dropped so that the remaining portion of the cutting surface 11 is fused when the segment 10 is placed on the blank 6. Fusion is made sequentially from the bottom to ensure that the fusion is made constant.

그리고 세그먼트(10)의 양쪽 커브 형성부위를 우레탄 패드로 연마하여 광택을 내 준 후 경유로 세그먼트(10)를 분리하고 검사과정을 거쳐 불량품을 가려내도록 한다.After polishing both sides of the curved portion of the segment 10 with a urethane pad to polish it, the segment 10 is separated by a diesel gas, and the defective part is selected through the inspection process.

위와 같이 세그먼트(10)의 제작이 완료되면 세그먼트(10)를 블랭크(5)의 하측에 대고 융착시켜 주어야 하며, 이하 세그먼트(10)의 융착공정에 대하여 살펴본다.When the fabrication of the segment 10 is completed as described above, the segment 10 should be fused to the lower side of the blank 5, and the fusion process of the segment 10 will be described below.

먼저 블랭크(5)의 하측에 치구를 이용하여 세그먼트(10)의 절단면(11)이 위 치할 지점에 라인을 긋고, 상기 라인에 세그먼트(10)를 올려 놓는다.First, a line is drawn at a point where the cut surface 11 of the segment 10 is to be positioned by using a jig below the blank 5, and the segment 10 is placed on the line.

이때 세그먼트(10)를 올려 놓을 때 도 11 과 같이 세그먼트(10)가 블랭크(5)에 밀착되도록 하고, 세그먼트(10)가 밀착된 블랭크(5)는 블랭크(5)의 비사용면 R값과 정확히 일치되는 R값을 가진 세락믹 몰드에 올려놓고, 전기로에 넣은 후 온도를 서서히 가열하여 세그먼트(10)가 블랭크(5)에 융착되어 일체화되도록 한다.At this time, when the segment 10 is placed, the segment 10 is in close contact with the blank 5 as shown in FIG. 11, and the blank 5 in which the segment 10 is in close contact with the non-use surface R value of the blank 5 is used. It is placed on a ceramic mold having an exact matched R value, placed in an electric furnace, and gradually heated to allow the segment 10 to be fused and integrated into the blank 5.

여기서 전기로에 넣어지는 블랭크(5)는 유리컵으로 씌워져 넣어지도록 하고, 전기로는 730-770도가 되도록 1시간 30분에 걸쳐 가열하므로서 세그먼트(10)가 블랭크(5)에 융착되도록 하며, 세그먼트(10)의 융착이 끝나면 전기로를 서서히 냉각시킨 후 블랭크(5)를 꺼내도록 하고, 이때 급냉시키거나 냉각전에 전기로를 개방하면 블랭크(5)가 파손되게 된다.Here, the blank 5 to be put in the electric furnace is covered with a glass cup, and the electric furnace is heated to 730-770 degrees for 1 hour and 30 minutes while allowing the segment 10 to be fused to the blank 5, and the segment 10 ) After fusion is completed, the electric furnace is gradually cooled and then the blank 5 is taken out. At this time, if the electric furnace is quenched or opened before cooling, the blank 5 is broken.

세그먼트(10)의 융착이 완료되고 완전히 냉각된 후에는 도 12 와 같이 블랭크(5)의 사용면과 세그먼트(10)의 절단면(11)에 접착제를 이용한 보호막(18)을 형성시키게 되며, 상기 보호막(18)은 세그먼트(10)의 가공공정을 수행할 때 손상을 방지하는 것이다.After fusion of the segment 10 is completed and completely cooled, a protective film 18 using an adhesive is formed on the use surface of the blank 5 and the cut surface 11 of the segment 10 as shown in FIG. 12. Reference numeral 18 is to prevent damage when performing the machining process of the segment 10.

이와 같이 세그먼트(10)를 블랭크(5)에 융착시킨 후에는 몰드최종공정을 수행하여 유리몰드(20)를 완성하게 된다.As such, after the segment 10 is fused to the blank 5, the final molding process is performed to complete the glass mold 20.

본 발명의 몰드최종공정은 커브가공기로 도 13 과 같이 세그먼트(10)를 절삭하고 펠렛가공기로 가공하게 되며, 세그먼트(10)를 절삭가공할 때 절단면(11)이 파손될 우려가 있으므로 최소압력으로 가공하도록 하고, 세그먼트(10)의 가공이 완료되면 세그먼트(10)의 가공면을 우레탄 패드로 연마하여 광택을 내도록 한다.In the final process of the mold of the present invention, the segment 10 is cut and processed with a pellet machine as shown in FIG. 13, and the cutting surface 11 may be damaged when cutting the segment 10. When the processing of the segment 10 is completed, the processed surface of the segment 10 is polished with a urethane pad to give a gloss.

세그먼트(10)의 광택작업이 완료되면 보호막(18)을 제거하고, 도 14와 같이 블랭크(5)의 비사용면을 커브가공기와 펠렛가공기로 가공한 후 광택과정을 거치도록 하여 최종 유리몰드(20)를 제작하도록 하며, 이렇게 제작된 유리몰드(20)는 검사장치를 이용하여 완성된 제품으로 검사과정을 거쳐 출하되게 된다.After the polishing of the segment 10 is completed, the protective film 18 is removed, and the unused surface of the blank 5 is processed with a curve cutter and a pelletizer as shown in FIG. 20) to be produced, the glass mold 20 is produced as a finished product using the inspection device is to be shipped through the inspection process.

이렇게 제조된 유리몰드(20)를 사용하여 제조된 이중초점 렌즈(1)는 도 3 에 도시된 바와 같이 상측은 도수가 형성되지 않은 무도수부(2)를 구성하게 되고, 하측은 함몰된 형태의 원시교정부(3)를 구성하게 되어, 시력은 정상적이나 원시를 갖고 있는 사람이 착용하고 다니면서 편리하게 사용할 수 있는 것이다.As shown in FIG. 3, the bifocal lens 1 manufactured by using the glass mold 20 manufactured as described above constitutes the non-hydrophobic part 2 having no power, and the lower side of the bifocal lens 1. The primitive school government (3) is to be formed, the vision can be worn and worn by people with normal or primitive and can be used conveniently.

본 발명은 도수가 형성되지 않은 무도수부와 반달형의 원시교정부가 하나의 렌즈에 형성되는 이중 초점 렌즈를 생산하기 위한 유리몰드를 간단한 과정에 의거 제조할 수 있도록 하는 것으로, 시력은 정상이나 원시를 가진 사람의 활동에 제약을 받지 않고 편리하게 사용할 수 있는 것이다.The present invention enables the production of a glass mold for producing a bifocal lens formed in one lens by a non-guided portion and a half-moon primitive bridge, in which a vision is normal or hyperopia. It can be used conveniently without being restricted by human activities.

Claims (3)

삭제delete 가공전 유리인 블랭크(5)를 렌즈 형태로 가공하되 도수가 형성되지 않는 상태로 가공하는 몰드1차가공공정과, 상기 블랭크(5)의 하측에 융착되고 원시교정용 도수를 갖는 세그먼트(10)를 가공하는 세그먼트 가공공정과, 상기 세그먼트(10)를 블랭크(5)의 하측에 융착시키는 세그먼트 융착공정과, 세그먼트(10)가 융착된 블랭크(5)의 세그먼트(10)를 원시교정부(3)의 R 값에 맞추어 가공하고 블랭크(5)의 비사용면을 가공하는 몰드최종공정을 수행하여 유리몰드(20)를 제조하는 몰드 제조방법에 있어서,A mold primary processing step of processing the blank 5, which is glass before processing, into a lens shape, but without a power being formed, and a segment 10 that is fused at a lower side of the blank 5 and has a frequency for primitive correction. A segment processing step of processing a die, a segment fusion step of fusing the segment 10 to the lower side of the blank 5, and a segment 10 of the blank 5 on which the segment 10 is fused. In the mold manufacturing method for manufacturing the glass mold 20 by performing a mold final process for processing in accordance with the R value of the) and the unused surface of the blank (5), 세그먼트 가공공정은 원형의 세그먼트(10)를 양분하고 양분된 절단면(11)이 상부를 향하게 고정치구(15)에 채운 후 접착제로 접착시키는 세그먼트 고정과정과, 고정된 세그먼트(10)의 절단면(11)을 경사지게 절삭하고 연마기를 사용하여 절단면(11)을 연마하여 가공하는 절단면 가공과정과, 세그먼트(10)를 분리하여 양 절단면(10)이 서로 마주보는 형태로 배치하고 접착제(16)로 절단면을 접착시키는 세그먼트 접착과정과, 상기 세그먼트(10)의 하부는 블랭크(5)의 R값에 맞추어 가공하고 상부는 원시교정부(3)의 R값에 맞추어 가공하는 세그먼트 커브가공 과정과, 상기 세그먼트(10)의 커브를 연마하고 세그먼트(10)를 분리하여 세그먼트(10)를 완성하는 세그먼트 완성과정으로 이루어지는 것을 특징으로 하는 원시교정부가 형성된 렌즈 생산용 몰드의 제조방법.The segment processing process is a segment fixing process of dividing the circular segment 10 and filling the fixing jig 15 so that the divided cutting surface 11 faces upward, and then bonding it with an adhesive, and the cutting surface 11 of the fixed segment 10. ), The cutting surface processing process of cutting the slanted surface 11 by using a polishing machine and grinding the cutting surface 11, and separating the segments 10 so that the two cutting surfaces 10 face each other, and cutting the cutting surface with the adhesive 16 Segment bonding process for bonding, the lower part of the segment 10 is processed in accordance with the R value of the blank (5), the upper part is processed in accordance with the R value of the primitive correction section (3), and the segment ( 10) A method of manufacturing a mold for forming a lens with a primitive correction, characterized in that consisting of a segment completion process of polishing the curve of 10) and separating the segment (10) to complete the segment (10). 가공전 유리인 블랭크(5)를 렌즈 형태로 가공하되 도수가 형성되지 않는 상태로 가공하는 몰드1차가공공정과, 상기 블랭크(5)의 하측에 융착되고 원시교정용 도수를 갖는 세그먼트(10)를 가공하는 세그먼트 가공공정과, 상기 세그먼트(10)를 블랭크(5)의 하측에 융착시키는 세그먼트 융착공정과, 세그먼트(10)가 융착된 블랭크(5)의 세그먼트(10)를 원시교정부(3)의 R 값에 맞추어 가공하고 블랭크(5)의 비사용면을 가공하는 몰드최종공정을 수행하여 유리몰드(20)를 제조하는 몰드 제조방법에 있어서,A mold primary processing step of processing the blank 5, which is glass before processing, into a lens shape, but without a power being formed, and a segment 10 that is fused at a lower side of the blank 5 and has a frequency for primitive correction. A segment processing step of processing a die, a segment fusion step of fusing the segment 10 to the lower side of the blank 5, and a segment 10 of the blank 5 on which the segment 10 is fused. In the mold manufacturing method for manufacturing the glass mold 20 by performing a mold final process for processing in accordance with the R value of the) and the unused surface of the blank (5), 세그먼트 융착공정은 도수가 형성되지 않은 블랭크(5)의 하측에 세그먼트(10)의 절단면(11)이 위치할 라인을 선정하는 라인선정과정과, 세그먼트(10)를 그어진 라인에 맞추어 결합시키되 절단면(11)의 하부가 블랭크(5)에 밀착되도록 잡아주는 세그먼트 결합과정과, 블랭크(5)를 전기로에 넣고 1시간 30분 동안 730-770도로 서서히 가열하여 세그먼트(10)를 블랭크(5)에 융착시키는 세그먼트 융착과정과, 블랭크(5)에 세그먼트(10)가 융착되면 전기로에서 꺼내어 블랭크(5)와 절단면(11)에 보호막(18)을 도포하는 보호막 도포과정을 수행하는 것을 특징으로 하는 원시교정부가 형성된 렌즈 생산용 몰드의 제조방법.In the segment fusion process, a line selection process of selecting a line on which the cut surface 11 of the segment 10 is to be positioned below the blank 5 where the frequency is not formed, and combining the segment 10 in accordance with the drawn line, Segment joining process to hold the lower part of 11) to be in close contact with the blank (5), the blank (5) is put into the electric furnace and gradually heated to 730-770 degrees for 1 hour 30 minutes to fusion the segment (10) to the blank (5) When the segment 10 is fused to the blank 5, and the segment 10 is fused to the blank 5, the prismatic correction characterized in that the protective film is applied to take out of the electric furnace to apply a protective film 18 to the blank 5 and the cut surface 11 Method for producing a mold for producing an additional lens.
KR1020030081910A 2003-11-18 2003-11-18 Method of manufacturing a mold for lens production with primitive bridge KR100540068B1 (en)