KR100518742B1 - Method for preparing the loess tile composition for construction materials - Google Patents
Method for preparing the loess tile composition for construction materials Download PDFInfo
- Publication number
- KR100518742B1 KR100518742B1 KR10-2003-0023928A KR20030023928A KR100518742B1 KR 100518742 B1 KR100518742 B1 KR 100518742B1 KR 20030023928 A KR20030023928 A KR 20030023928A KR 100518742 B1 KR100518742 B1 KR 100518742B1
- Authority
- KR
- South Korea
- Prior art keywords
- ocher
- weight
- parts
- loess
- composition
- Prior art date
Abstract
본 발명은 건축 자재용 황토타일의 제조방법에 관한 것으로, 좀 더 구체적으로는 황토 100중량부에 대하여 초경량제 5∼15중량부, 펄프 1∼3중량부, 전분 분말 3∼10중량부 및 물 50∼100중량부로 구성되는 건축 자재용 황토타일의 제조방법에 관한 것이다.The present invention relates to a method for producing ocher tiles for building materials, and more specifically, 5 to 15 parts by weight of ultralight agent, 1 to 3 parts by weight of pulp, 3 to 10 parts by weight of starch powder and water, based on 100 parts by weight of loess. It relates to a method for producing ocher tile for building materials composed of 50 to 100 parts by weight.
본 발명은 내구성 및 생산성이 우수하고 갈라짐이 없어 외관이 미려하고, 시공성 및 가공성이 용이한 고기능성 황토내장재(황토타일)를 제조할 수 있다.The present invention is excellent in durability and productivity, there is no cracking beautiful appearance, it is possible to manufacture a high-functional ocher interior material (ocher tile) easy to workability and processability.
Description
본 발명은 건축 자재용 황토타일의 제조방법에 관한 것으로, 좀 더 구체적으로는 다량의 원적외선을 발생하고 항균, 탈취, 방습 작용 등을 하여 인체에 매우 유익한 영향을 주는 황토를 주성분으로 하여 표면에 균열을 생성치 않으면서 그 강도도 매우 높아서, 건축 마감재·타일·벽돌·보드 등과 같은 각종의 건축 자재로 제작 가능한 건축 자재용 황토타일의 제조방법에 관한 것이다.The present invention relates to a manufacturing method of ocher tiles for building materials, and more specifically, to generate a large amount of far infrared rays, and to have a very beneficial effect on the human body by antibacterial, deodorant, moisture-proof action, cracks on the surface The present invention relates to a method for manufacturing ocher tiles for building materials, which can be made of various building materials such as building finishing materials, tiles, bricks, boards, etc., without having generated high strength.
한반도를 비롯한 중국의 화북지방 황하 연안 등 주로 동북아에 집중적으로 분포되어 있는 황토는 주로 석영을 함유하면서 그밖에 휘석, 각섬석 등을 함유하는 황갈색 석회질로서, 실리카(SiO2) 60∼65%, 철분 5∼6%, 알루미나(Al2O3) 10∼13%, 마그네슘(Mg)과 나트륨(Na) 각 2% 내외, 칼리 1.5%, 석회 8% 내외의 화학적 조성을 가지며, 분해력·자정력·흡수력 등이 뛰어나며 인체에 유익한 약성을 갖는 것으로 알려져 왔다.Ocher is mainly concentrated in Northeast Asia, including the Korean Peninsula and the Yellow River coast of China's northeastern region. It is yellowish brown lime that contains quartz and other fluorite and hornblende, and is 60 ~ 65% silica (SiO 2 ) and iron 5 ~. It has a chemical composition of 6%, 10-13% of alumina (Al 2 O 3 ), 2 % of magnesium (Mg) and sodium (Na), 1.5% of kali, and 8% of lime. It is known to have excellent and beneficial weakness to the human body.
이에, 예로부터 가옥의 재료로서 중요하게 쓰여졌으며, 식기나 기구로 만들어져 생활의 도구로도 활용되었다. 그 뿐 아니라 황토는 해독과 질병 치료에도 탁월한 약효를 가지고 있어 동양의학에서는 중요한 약제로 쓰여졌다.Therefore, it has been used importantly as a material for houses since ancient times, and was used as a tool of living by making dishes and utensils. In addition, ocher has excellent efficacy in treating detoxification and disease, and has been used as an important medicine in oriental medicine.
대표적인 동양 의서들인 본초강목(本草綱木), 동의보감(東醫寶鑑) 및 향약집성방 등에는 황토가 본디 색을 지닌 흙으로 약성이 가장 뛰어나 널리 중요하게 쓰이는 것으로서 맛은 달고 독이 없으며 부인병(婦人病)과 소아병(小兒病)에 탁월한 효능이 있다고 기록되어 있다. 또한, 본초강목의 중수부편에는 황토에 물을 부어 우러나온 물을 지장(地漿) 또는 토장(土漿)이라 하며, 이는 각종 독을 해독하고 마음을 안정시키는 효능이 있다고 기록되어 있다.The main oriental texts, such as the vinegar, the Dongchobogam, and the medicinal herb room, are the most widely used soils with ocher color. It has been documented that it has excellent efficacy in children and children's diseases (小兒 病). In addition, the heavy water part of the herbaceous wood is called Jijang or Sojang, which is poured from the ocher to pour water, and it is recorded that it is effective in detoxifying various poisons and stabilizing the mind.
최근에 들어서는 황토에 대한 과학적 규명에 많은 연구가 이루어져 황토가 많은 양의 원적외선을 방출하고 유해 전자파를 차단할 수 있으며, 황토 한 숟갈에는 수억마리의 미생물과 다양한 효소들이 촘촘히 들어 있어 이들이 순환작용을 하여 여러 면에서 인체에 매우 유익한 영향을 준다는 것이 과학적으로도 입증되었다.In recent years, many studies have been conducted on scientific research on ocher, and the ocher can emit a large amount of far infrared rays and block harmful electromagnetic waves.In one spoon of ocher, hundreds of millions of microorganisms and various enzymes are circulated, It has also been scientifically proven to have a very beneficial effect on the human body.
이에, 황토가 침구용 매트·황토 침대 등의 생활가구나 음식 조리용 용기 또는 건축용 내, 외장재나 온돌 등과 같은 생활용품의 소재로서 각광받고 있으며, 그 활용범위도 급속히 늘어나는 추세에 있다.Thus, yellow clay has been spotlighted as a material for living furniture such as bedding mats and ocher beds, food containers for construction, or household goods such as interior materials, exterior materials, and ondol, and the range of their application is also rapidly increasing.
한편, 순수한 황토는 열전도성과 축열성이 떨어지는 데다 물에 혼합된 상태에서는 점도(粘度)가 너무 커서 특정한 형상으로 성형하기 어렵고, 양생 후에는(수분이 증발되고 나면) 표면에 균열이 생기기 때문에 그 자체만으로는 제품화되기 어렵다는 문제점이 있다.Pure loess, on the other hand, is poor in thermal conductivity and heat storage, and in the state of mixing with water, its viscosity is so large that it is difficult to be molded into a specific shape, and after curing (after moisture evaporates), the surface itself is cracked. There is a problem that it is difficult to commercialize alone.
이에, 종래에는 황토에 시멘트·석회·모래 또는 기타의 돌가루 등과 같은 다른 재료들과 혼합하여 반죽한 다음 그것을 특정한 틀에 넣은 다음 양생한 황토 제품(예: 황토 매트, 각종 음식용기, 건축 내장재(황토타일) 등)들이 사용되어 왔다.Thus, conventionally, the clay is mixed with other materials such as cement, lime, sand or other stone powder, kneaded and then put into a specific mold and then cured ocher products (e.g., ocher mats, various food containers, building interior materials) Loess tiles) and the like have been used.
예를 들어, 한국 특허출원 제97-62065호에서는 생황토를 저입도로 스크린 (screen)한 후 함수율을 28%로 보정하고 24시간 동안 숙성시킨 후, 숙성된 황토 95중량%에 대하여 5중량%의 리그닌술폰산염을 첨가시켜 진공토련기로 혼련하고 가압성형하여 100∼150℃에서 서서히 가열, 건조시킨 황토벽돌을 개시하고 있다.For example, Korean Patent Application No. 97-62065 screens raw ocher at low granularity, corrects the water content to 28% and ages for 24 hours, and then 5 wt% based on 95% by weight of aged ocher. The ocher bricks are added by kneading with a lignin sulfonate, kneaded with a vacuum drill, press-molded, and gradually heated and dried at 100 to 150 ° C.
또한, 한국 특허출원 제2001-088925호 원적외선을 방출하는 황토와 옥돌을 분쇄한 후 수지액과 반죽한 후 경화시킨 황토/옥돌층과, 상기 황토/옥돌층의 하부에 부착되며 도형이 입력된 인쇄층과, 상기 인쇄층의 하부에 위치하여 황토/옥돌층의 강도를 유지시켜 주는 투명한 수지층으로 이루어진 황토타일을 개시하고 있다.In addition, Korean Patent Application No. 2001-088925 crushed ocher and jade which emits far infrared rays and kneaded with a resin solution and then hardened the ocher / jade stone layer, the printing attached to the lower part of the ocher / jade stone, the figure is input A loess tile comprising a layer and a transparent resin layer positioned under the printed layer to maintain the strength of the loess / ocdol layer is disclosed.
또한, 한국 특허출원 제2001-08812호에서는 종이를 물에 불려 분쇄하여 종이 덩어리가 없이 액체 상태가 되어 종이의 섬유질이 황토와 풀 등과 함께 고루 섞이게 하여 반죽을 만드는 방법과 상기 황토 반죽을 이용하여 황토판넬, 황토벽돌, 황토타일 등 황토 제품을 만들어 100℃미만에서 서서히 건조시키는 방법을 개시하고 있다.In addition, Korean Patent Application No. 2001-08812 discloses a method in which a paper is soaked in water and pulverized to become a liquid state without paper lumps so that the fibers of the paper are mixed evenly with ocher and grass, and a dough is made. Disclosed is a method of making ocher products such as panels, ocher bricks and ocher tiles and slowly drying them below 100 ° C.
또한, 한국 특허출원 제2001-03469호에서는 황토 또는 황토에 사질 40중량%까지 혼합하고, 입도 100목이하로 분쇄하고, 적정 수분함량을 조절하고, 탈기시킨 다음, 타일모양으로 성형한 후, 음지에서 건조키고, 초벌온도 800±20℃ 범위에서 열처리하고, 냉각시킨 후, 재벌온도 1,180±30℃ 범위 내에서 열처리하여 제조된 황토타일을 개시하고 있으며, 한국 특허출원 제2001-029823호에서는 황토 30∼50%; 목재 세편(細片) 30∼50% 및 물 10∼30%가 혼합되어 이루어진 황토 조성물 및 이를 이용한 황토 매트를 개시하고 있다.In addition, in Korean Patent Application No. 2001-03469, up to 40 wt% of loess or loess is mixed with sand, pulverized to less than 100 particle size, the appropriate moisture content is controlled, degassed, and then molded into tile shape. The present invention discloses ocher tiles which are manufactured by drying, heat treatment at an initial temperature of 800 ± 20 ° C., cooling, and heat treatment within a chaebol temperature of 1,180 ± 30 ° C., and Korean Patent Application No. 2001-029823, -50%; Disclosed are an ocher composition comprising 30-50% of wood chips and 10-30% of water, and an ocher mat using the same.
그러나, 종래 황토 제품들의 경우에는 황토의 함유 비율이 지나치게 낮은 데다가 고분자 화합물·시멘트 또는 석회 등과 같은 다른 조성물들이 황토의 기능을 희석시키기 때문에 황토가 가진 고유한 효능을 효과적으로 살리지 못하였으며, 황토에 혼합되는 다른 조성물들의 높은 원가와 복잡한 제조공정으로 인하여 제조원가가 매우 높다는 문제점이 있었다.However, in the case of conventional loess products, the content of loess is too low and other compositions such as high molecular compounds, cement or lime dilute the function of loess, so that the inherent effects of loess are not effectively utilized. Due to the high cost and complicated manufacturing process of the other compositions there was a problem that the manufacturing cost is very high.
이에 본 발명에서는 황토에 친환경적이며 자연상태에서 부패하지 않는 전분 분말을 첨가하고, 여기에 초경량제·펄프 등을 물과 함께 혼합 성형하여 내구성 있고 시공이 편리하며 외관상 미려한 황토내장재(황토타일)를 제조할 수 있었고, 본 발명은 이에 기초하여 완성되었다.In the present invention, the starch powder, which is eco-friendly and does not decay in natural state, is added to the ocher, and the ultralight agent, pulp, etc. is mixed and molded together with water to prepare durable, easy-to-use ocher interior material (ocher tile) in appearance. The present invention was completed based on this.
따라서, 본 발명의 목적은 인체 건강상의 문제점 해결은 물론 전래하는 황토 내장재의 습식 시공기간을 단축할 수 있도록 규격화된 완제품 사용을 유도, 황토 본연의 특성인 우수한 내열, 내화성, 보온성, 단열성, 탈취능력, 항균능력, 습도조절능력 및 원적외선 방출능력 등을 일상 생활공간에 쉽게 도입하여 주거환경의 혁신적인 개선을 도모할 수 있는 건축 자재용 황토타일의 제조방법을 제공하는데 있다.Therefore, the object of the present invention is to solve the problems of human health as well as to use the standardized finished product to shorten the wet construction period of the conventional ocher interior material, excellent heat resistance, fire resistance, insulation, insulation, deodorizing ability of the ocher natural characteristics It provides an antimicrobial ability, humidity control ability and far-infrared ray emission ability in daily living spaces to provide a manufacturing method of ocher tiles for building materials which can promote innovative improvement of residential environment.
본 발명의 다른 목적은 상기 건축 자재용 황토타일의 제조방법을 제공하는데 있다. Another object of the present invention is to provide a method of manufacturing the ocher tile for the building material.
상기 목적을 달성하기 위한 본 발명의 건축 자재용 황토타일 조성물은 황토 100중량부에 대하여 초경량제 5∼15중량부, 펄프 1∼3중량부, 전분 분말 3∼10중량부 및 물 50∼100중량부로 구성된다.The ocher tile composition for building materials of the present invention for achieving the above object is 5 to 15 parts by weight of ultralight agent, 1 to 3 parts by weight of pulp, 3 to 10 parts by weight of starch powder and 50 to 100 parts by weight of water, based on 100 parts by weight of ocher. It consists of wealth.
본 발명의 다른 목적을 달성하기 위한 건축 자재용 황토타일의 제조방법은 상기 황토 조성물을 혼합시키는 단계; 상기 조성물을 규격화된 틀에 넣고 원하는 두께로 평탄하게 고른 후, 미장한 성형물을 제공하는 단계; 상기 성형물의 함수율 이상으로 가습하면서 상기 성형물의 온도를 75∼95℃로 승온시키는 단계; 및 상기 성형물이 승온된 후, 습기를 제거하고 70∼120℃에서 18∼24시간 건조시키는 단계;를 포함한다. The method for producing ocher tiles for building materials for achieving another object of the present invention comprises the steps of mixing the ocher composition; Placing the composition in a standardized mold and flattening to a desired thickness, providing a plastered molding; Raising the temperature of the molded product to 75 to 95 ° C. while humidifying above the molded product moisture content; And after the molding is heated, removing moisture and drying at 70 to 120 ° C. for 18 to 24 hours.
이하 본 발명을 좀 더 구체적으로 살펴보면 다음과 같다.Looking at the present invention in more detail as follows.
전술한 바와 같이, 본 발명은 현대 건축물에 시공되고 있는 건축 내장용 벽체 및 온돌 바닥 시공에 있어 필연적으로 발생하는 습기 및 화학적 독성물질 분출에 따른 인체건강상의 문제점을 해결하기 위하여 옛 선조들로부터 4천년이상 전래 사용되어 오던 황토를 친환경적이며 자연상태에서 부패하지 않는 전분 분말을 주성분으로 사용하고 초경량제, 펄프 등을 물과 함께 혼합 성형하여 내구성 있고 시공이 편리하며 외관상 미려한 황토내장재(황토타일)를 제조 시공하였다.As described above, the present invention is 4,000 years from old ancestors in order to solve the problems of human health caused by the release of moisture and chemical toxic substances inevitably in the construction of the wall and on-floor floor for building interiors that are being constructed in modern buildings It is manufactured by using ocher, which has been used in the past, as an eco-friendly and non-corrosive starch powder as its main ingredient, and mixing and molding ultralight agent and pulp together with water to manufacture durable, convenient and beautiful appearance ocher tile. It was constructed.
본 발명에 따른 황토내장재는 기존의 인체건강상의 문제점 해결은 물론 전래하는 습식 시공기간을 단축할 수 있도록 규격화된 완제품 사용을 유도, 황토 본연의 특성인 우수한 내열, 내화성, 보온성, 단열성, 탈취능력, 항균능력, 습도조절능력 및 원적외선 방출능력 등을 일상 생활공간에 쉽게 도입하여 주거환경의 혁신적인 개선을 도모할 수 있다.The ocher interior material according to the present invention induces the use of standardized finished products to solve the conventional human health problems as well as shorten the wet construction period, excellent heat resistance, fire resistance, insulation, heat insulation, deodorizing ability, The antibacterial ability, humidity control ability and far infrared ray emission ability can be easily introduced into daily living spaces, and the innovative improvement of residential environment can be achieved.
이러한 본 발명의 건축 자재용 황토타일 조성물은 황토 100중량부에 대하여 초경량제 5∼15중량부, 펄프 1∼3중량부, 전분 분말 3∼10중량부 및 물 50∼100중량부로 구성된다.The ocher tile composition for building materials of the present invention is composed of 5 to 15 parts by weight of ultralight agent, 1 to 3 parts by weight of pulp, 3 to 10 parts by weight of starch powder and 50 to 100 parts by weight of water, based on 100 parts by weight of ocher.
상기 초경량제는 화강암, 맥반석 또는 일라이트과 같이 황토와 유사한 성분 구성을 갖는 암석을 고압하에서 가열하여 순간적으로 압력을 제거하여 팽창시킨 것을 미세하게 분쇄시킨 것으로, (주)서경 CMT의 제품명 MICRO SHELL과 같은 시판되는 제품을 사용할 수 있다.The ultra-light agent is finely crushed by heating the rock having a component composition similar to ocher, such as granite, elvan or illite, under high pressure by instantaneous removal of pressure, such as product name MICRO SHELL of Seokyung CMT Co., Ltd. Commercially available products can be used.
본 발명에 따르면, 상기 초경량제는 최종 조성물의 점도 및 성형제품의 적정 강도를 유지하면서 최종 제품의 경량화를 가능하게 한다. 따라서, 상기 초경량제의 사용량은 황토 100중량부에 대하여 5∼15중량부가 바람직하다. 특히, 최종 제품의 비중이 1일 때 제품의 경량화 측면에서 바람직하므로 상기 초경량제의 사용량을 성형제품의 비중을 고려하여 상기 사용량 범위내에서 조절할 수 있다.According to the present invention, the ultralight agent enables the weight reduction of the final product while maintaining the viscosity of the final composition and the appropriate strength of the molded product. Therefore, the amount of the ultralight agent is preferably 5 to 15 parts by weight based on 100 parts by weight of ocher. In particular, when the specific gravity of the final product is 1, it is preferable in terms of weight reduction of the product, so that the amount of the ultralight agent can be adjusted within the above usage range in consideration of the specific gravity of the molded product.
상기 펄프는 제품 표면의 크랙(crack)을 방지하기 위해 첨가되며, 그 사용량은 황토 100중량부에 대하여 1∼3중량부가 바람직하다. 이때 1중량부미만이면 첨가 효과가 거의 없으며, 3중량부를 초과하면 제품의 표면 강도가 저하되며, 아울러, 조성물의 점도가 증가하여 성형성이 저하되는 경향이 있다.The pulp is added to prevent cracking of the product surface, the amount of the pulp is preferably 1 to 3 parts by weight based on 100 parts by weight of ocher. At this time, if it is less than 1 part by weight, there is almost no effect of addition, and if it exceeds 3 parts by weight, the surface strength of the product is lowered, and the viscosity of the composition increases, and the moldability tends to be lowered.
상기 전분 분말은 제품의 강도를 높이기 위해 사용되며, 그 사용량은 황토 100중량부에 대하여 3∼10중량부가 바람직하다. 이때 3중량부미만이면 제품 강도가 떨어지고, 10중량부를 초과하면 조성물의 점도가 증가하여 성형성이 떨어지는 경향이 있다.The starch powder is used to increase the strength of the product, the amount is preferably 3 to 10 parts by weight based on 100 parts by weight of ocher. At this time, if the content is less than 3 parts by weight, the product strength is lowered. If the content is more than 10 parts by weight, the viscosity of the composition is increased and the moldability tends to be poor.
상기 물은 최종 제품의 성형성을 위해 황토 100중량부에 대하여 물 50∼100중량부로 첨가된다. 물은 전분의 사용량에 따라 비례하여 변화되어야 성형성 및 강도 측면에서 바람직하다. 따라서, 물을 50중량부미만으로 사용하면 점도가 증가하여 성형성이 저하되고, 100중량부를 초과하면 강도가 떨어지는 경향이 있다.The water is added to 50 to 100 parts by weight of water based on 100 parts by weight of ocher for formability of the final product. Water is preferably changed in proportion to the amount of starch used in view of formability and strength. Therefore, when water is used in less than 50 parts by weight, the viscosity increases and moldability is lowered, and when it exceeds 100 parts by weight, the strength tends to be lowered.
본 발명에 따르면, 상기 성분들을 잘 혼합시킨 다음, 규격화된 틀에 넣고 원하는 두께로 성형한다. 그 다음, 성형된 성형물의 함수율 이상으로 고온의 습기(증기)를 가하면서 상기 성형물의 온도를 75∼95℃로 승온시킨다. 이렇게 증기를 공급하면서 성형물의 온도를 상승시킴으로써 제품의 크랙 또는 균열을 방지하고 특히 뒤틀림 현상을 방지할 수 있다.According to the invention, the components are mixed well, then placed into a standardized mold and molded to the desired thickness. Then, the temperature of the molded product is raised to 75 to 95 ° C while hot moisture (vapor) is added above the water content of the molded product. By raising the temperature of the molding while supplying steam in this way, it is possible to prevent cracking or cracking of the product, and particularly to prevent warpage.
한편, 상기 성형물 자체의 온도가 75∼95℃로 승온된 후에는 습기를 순간적으로 제거한다. 이와 같이, 고온의 증기를 순간적으로 제거함으로써 성형물 자체적으로 가지고 있는 다량의 수분을 급속으로 강제 증발시킬 수 있다. 따라서, 성형물 내부의 기공성을 증대시킴으로써 압착 또는 합성수지 배합 황토제품과 달리, 전래하는 황토 본연의 특성을 배가시킨 성형물을 제조할 수 있다.On the other hand, after the temperature of the molded product itself is elevated to 75 to 95 ° C, moisture is removed instantaneously. In this way, by removing the hot steam instantaneously, a large amount of moisture possessed by the molding itself can be rapidly forcibly evaporated. Therefore, by increasing the porosity inside the molding, it is possible to produce a molded article that doubles the characteristics of the original loess, unlike the compressed or synthetic resin blended loess products.
그 다음, 70∼120℃에서 18∼24시간 동안 상기 성형물을 건조시켜 본 발명의 건축 자재용 황토타일을 제조한다. 이때 건조 온도가 120℃를 초과하면 제품에 뒤틀림 현상이 나타나고, 70℃미만이면 건조시간이 길어지며 제품의 강도가 떨어지는 경향이 있다.Then, the molded product is dried at 70 to 120 ° C. for 18 to 24 hours to prepare the ocher tile for building materials of the present invention. At this time, if the drying temperature exceeds 120 ℃ warpage phenomenon appears in the product, if less than 70 ℃ drying time is prolonged and the strength of the product tends to be lowered.
이와 같이 제조된 본 발명의 황토 내장재는 고기능성이며 무한한 황토자원을 활용하여 우수한 황토내장재(황토타일)의 대중화를 유도할 수 있고, 규격화된 제품을 사용함으로써 기존 습식 시공상의 문제점인 시공기간 단축 및 편의성을 유도할 수 있는 효과가 있다.The ocher interior material of the present invention prepared as described above can induce the popularization of excellent ocher interior materials (ocher tiles) by utilizing high functional and infinite ocher resources, and shorten the construction period, which is a problem of conventional wet construction by using standardized products. There is an effect that can lead to convenience.
이하 실시예를 통하여 본 발명을 좀 더 구체적으로 살펴보지만, 하기 예에 본 발명의 범주가 한정되는 것은 아니다.Hereinafter, the present invention will be described in more detail with reference to the following examples, but the scope of the present invention is not limited to the following examples.
실시예 1Example 1
먼저, 정선된 황토를 채취 이물질 등을 제거한 후, 황토 100중량부에 대하여 초경량제((주)서경 CMT MICRO SHELL) 10중량부, 펄프 1.5중량부, 감자전분 분말 6중량부 및 물 70중량부를 잘 혼합하였다.First, the selected ocher is removed to remove foreign substances, etc., then, based on 100 parts by weight of ocher, 10 parts by weight of ultra-lightweight (Samkyung CMT MICRO SHELL), pulp 1.5 parts by weight, potato starch powder 6 parts by weight and water 70 parts by weight Mix well.
상기 혼합물을 300㎜×300㎜의 소형틀에 넣어 12㎜의 두께로 파이프로 평탄하게 고른 후 미장하여 성형물을 제조한 다음, 고온의 증기를 공급하여 상기 성형물의 자체 온도를 약 90℃ 정도로 상승시켰고, 약 3시간 정도가 소요되었다. 그 다음, 증기를 완전히 제거하고 약 80℃에서 약 20시간 건조시켜 본 발명의 황토 타일을 제조하였다.The mixture was placed in a small frame of 300 mm × 300 mm, flattened to a pipe thickness of 12 mm, and then plastered to prepare a molding. Then, a high temperature steam was supplied to raise the molding temperature to about 90 ° C. It took about 3 hours. The steam was then completely removed and dried at about 80 ° C. for about 20 hours to prepare the ocher tiles of the present invention.
비교예 1Comparative Example 1
상기 실시예 1에서 감자전분 분말을 첨가하지 않은 것을 제외하고는 동일하게 실시하였다.Except for the addition of potato starch powder in Example 1 was carried out in the same manner.
비교예 2Comparative Example 2
상기 실시예 1에서 고온의 증기를 공급하지 않고 건조시킨 것을 제외하고는 동일하게 실시하였다.The same process as in Example 1 except that the drying without supplying a high temperature steam.
비교예 3Comparative Example 3
상기 실시예 1에서 약 125℃에서 약 15시간 건조시킨 것을 제외하고는 동일하게 실시하였다.Except for drying for about 15 hours at about 125 ℃ in Example 1 was carried out in the same manner.
상기 실시예 1, 비교예 1, 비교예 2 및 비교예 3에 따른 황토타일의 비중, 제품강도, 변형정도 및 크랙발생을 측정하였고, 그 결과를 하기 표 1에 기재하였다.The specific gravity, product strength, deformation degree and crack occurrence of the ocher tiles according to Example 1, Comparative Example 1, Comparative Example 2 and Comparative Example 3 were measured, and the results are shown in Table 1 below.
1) 제품강도: 압축강도 측정기로 측정함.1) Product strength: Measured by compressive strength tester.
2) 변형: 제품을 수평면에 놓고 들린 높이가 1.5㎜이상인 경우.2) Deformation: When the product is placed on the horizontal surface, the lifted height is over 1.5mm.
3) 크랙발생: 육안으로 측정함.3) Crack occurrence: Visually measured.
전술한 바와 같이, 본 발명은 황토에 수용성이며 친환경적 물질인 전분 분말, 초경량제, 펄프 등을 적정량의 물과 함께 혼합 사용함으로써, 전분류의 농도를 쉽게 조절할 수 있어 제품의 강도조절이 용이하고(밟아도 깨지지 않음), 혼합시 사용되는 다량의 수분을 급속강제 증발시켜 잔여하는 황토내장재(황토타일) 내부의 기공성을 증대시킴으로써 압착 또는 합성수지 배합 황토제품과 달리, 전래하는 황토 본연의 특성을 배가시킨 황토내장재(황토타일)를 제조할 수 있다.As described above, the present invention is easy to adjust the concentration of the starch by using a suitable amount of water mixed with starch powder, ultralight agent, pulp, etc., which are water-soluble and environmentally friendly materials in yellow soil, and easy to control the strength of the product ( It does not break even when stepped on), and it rapidly evaporates a large amount of water used during mixing to increase the porosity inside the remaining ocher lining (ocher tile), thereby doubling the characteristics of the original ocher unlike the compressed or synthetic resin-containing ocher products. Ocher interior materials (ocher tile) can be produced.
또한, 황토와 성분이 유사한 암석을 급속 가열 팽창 미분화시켜서 제조된 초경량제를 사용하여 제품의 경량화 및 가공성을 증대시키고, 친환경물질만을 사용함으로써 폐기시 2차공해를 전혀 유발하지 않으며, 고기능성이며 무한한 황토자원을 활용하여 우수한 황토내장재(황토타일)의 대중화를 유도할 수 있다.In addition, by using ultra-lightening agent manufactured by rapid thermal expansion and micronization of rocks similar in composition to ocher, it is possible to increase the weight and processability of the product, and by using only environmentally friendly materials, it does not cause any secondary pollution when discarded, and is highly functional and infinite. The use of loess resources can lead to the popularization of excellent loess interior materials.
아울러, 규격화된 제품을 사용함으로써 기존 습식 시공상의 문제점인 시공기간 단축 및 편의성을 유도할 수 있는 효과가 있다.In addition, by using a standardized product there is an effect that can lead to a reduction in the construction period and convenience, which is a problem in the existing wet construction.
Claims (3)