KR100489971B1 - Manufacturing method for a rechargeable gas-can - Google Patents
Manufacturing method for a rechargeable gas-can Download PDFInfo
- Publication number
- KR100489971B1 KR100489971B1 KR10-2003-0012663A KR20030012663A KR100489971B1 KR 100489971 B1 KR100489971 B1 KR 100489971B1 KR 20030012663 A KR20030012663 A KR 20030012663A KR 100489971 B1 KR100489971 B1 KR 100489971B1
- Authority
- KR
- South Korea
- Prior art keywords
- container body
- cap
- manufacturing
- gas
- container
- Prior art date
Abstract
본 발명은 충전용 가스 용기의 제조방법에 관한 것으로, 좀더 상세하게는 재충전 사용에 따른 압력변화에도 가스 용기의 기밀성을 최대한 확보함과 동시에 주입된 가스가 배출되는 밸브체를 상부캡으로 용접이 아닌 나사결합에 의해 간편하게 결합 및 분리가 이루어질 수 있도록, The present invention relates to a manufacturing method of a gas container for filling, and more particularly, to ensure the maximum airtightness of the gas container even when the pressure changes due to the use of refilling at the same time, the valve body for discharging the injected gas is not welded by the upper cap In order to be easily combined and separated by screwing,
고압으로 압축되어 액화상태로 주입되는 가스를 재충전시켜 사용할 수 있는 충전용 가스 용기를 제조하는 방법에 있어서, 동일 직경으로 일정한 길이를 갖도록 제작되는 관형태의 용기몸체를 제작하는 용기몸체 제작공정과; 중앙에 밸브체가 나사결합되게 내주면으로 나선부가 형성되도록 함입된 결합홈이 형성되게 상부 측이 좁고 하부 측이 점차적으로 넓게 형성되어 지고 외측단에는 절곡리이브를 갖도록 상부캡을 제작하는 상부캡 제작공정과; 상측에서 하측으로 만곡형태로 형성되어 지고 외측단에는 절곡리이브가 형성되는 하부캡을 제작하는 하부캡 제작공정과; 상기 용기몸체의 상하부에 상기 상부캡과 하부캡의 절곡리이브가 그 용기몸체의 내측면과 외측면을 감싸도록 시이밍(seaming)작업 한 후, 상기 용기몸체의 외측면과 시이밍 작업에 의해 그 용기몸체의 외측면으로 접혀진 상기 상,하부캡의 절곡리이브 끝단을 용접하여 결합하는 상,하부캡 용접공정을 포함하는 것을 특징으로 하는 충전용 가스 용기의 제조방법에 관한 것이다. Claims [1] A method of manufacturing a filling gas container which can be used by recharging a gas injected in a liquefied state by compressing a high pressure, the method comprising: a container body manufacturing step of manufacturing a tubular container body manufactured to have a constant length with the same diameter; The upper cap manufacturing process of manufacturing the upper cap so that the upper side is narrow and the lower side is gradually widened and the outer end has a bent rib to form a coupling groove in which a spiral is formed in the inner peripheral surface so that the valve body is screwed in the center. and; A lower cap manufacturing process for forming a lower cap which is formed in a curved shape from an upper side to a lower side and a bending rib is formed at an outer end thereof; After seaming the upper and lower portions of the container body and the bending ribs of the upper cap and the lower cap wrap the inner and outer surfaces of the container body, and then by the outer and the outer surface of the container body It relates to a manufacturing method of a gas container for filling, comprising an upper and lower cap welding process for welding and joining the bent rib ends of the upper and lower caps folded to the outer surface of the container body.
Description
본 발명은 충전용 가스 용기의 제조방법에 관한 것으로, 좀더 상세하게는 재충전 사용에 따른 압력변화에도 가스 용기의 기밀성을 최대한 확보함과 동시에 주입된 가스가 배출되는 밸브체를 상부캡으로 용접이 아닌 나사결합에 의해 간편하게 결합 및 분리가 이루어질 수 있도록 한 충전용 가스 용기의 제조방법에 관한 것이다. The present invention relates to a manufacturing method of a gas container for filling, and more particularly, to ensure the maximum airtightness of the gas container even when the pressure changes due to the use of refilling at the same time, the valve body for discharging the injected gas is not welded by the upper cap It relates to a method for producing a gas container for filling to be easily combined and separated by screwing.
일반적으로 부탄가스 용기, 살충제용 용기, 방향제용 용기, 스프레이식 페인트 용기, 분사식 의약품 용기 등과 같은 각종 용기에는 내부로 약제나 가스 등이 고압으로 압축되어 액화상태로 용기 속에 충진된 후 밸브를 통해 외부로 유출되면서 기화되도록 사용된다. In general, various containers such as butane gas containers, insecticide containers, fragrance containers, spray paint containers, and spray medicine containers are compressed into a container in a liquid state by being compressed with high pressure to the inside, and then, It is used to vaporize as it exits.
상기와 같이 종래 사용되는 각종의 가스 용기는 그 대부분이 일회용으로 제작됨에 따라 재충전이 불가능하여 전량이 버려지고 있어 많은 자원이 낭비되었을 뿐만 아니라 새로운 가스 용기의 제작에 따른 비용부담과 수거작업 및 처리비용이 과다하게 소요되었으며, 버려지는 가스 용기로 인한 심각한 환경오염이 발생함은 물론 안전성이 상당히 떨어지는 문제점이 발생하였다. As described above, various types of gas containers used in the related art are impossible to be recharged as most of them are made in a single use, and thus, all of them are thrown away. This excessively excessive, serious environmental pollution caused by the gas container is thrown away, as well as a problem of significantly reduced safety.
그에 따라 근래에는 재충전하여 사용할 수 있는 여러 형태의 가스 용기가 제작되어 사용되는 바, 본원에서는 부탄가스 용기를 일예로 첨부된 도면 도 6를 참고하여 설명하면, Accordingly, in recent years, various types of gas containers that can be recharged and used are manufactured and used. Here, the butane gas container will be described with reference to FIG. 6 as an example.
도시된 바와 같이 종래 대부분이 원통형의 용기몸체(100)를 제작한 후, 그 몸체의 상,하부 끝단을 공지의 방식에 의해 강제 확관시킨 각각 확관 결합부(110)(120)를 형성하고, 상기 상부 측의 확관 결합부(110)에는 그 용기몸체로 주입되는 가스를 배출할 수 있도록 일반적인 밸브체(210)가 용접되는 마운틴컵(220)이 상부캡(200)으로 다시 용접되어 고정된 후 상기 상부캡의 외측단에 상기 결합부의 내측면과 접하는 절곡부(202)를 형성하여 그 절곡부 끝단과 상기 상부 결합부의 끝단을 공지의 맞대기 용접하여 결합한다. As shown in the prior art, most of the cylindrical container body 100 is manufactured, and then the expansion and coupling portions 110 and 120 are formed by forcibly expanding the upper and lower ends of the body by a known method. The mountain cup 220 to which the general valve body 210 is welded is again welded and fixed to the upper cap 200 in the expansion pipe coupling portion 110 of the upper side to discharge the gas injected into the container body. A bent portion 202 is formed on the outer end of the upper cap in contact with the inner surface of the coupling portion, and the bent end and the end of the upper coupling portion are joined by a known butt weld.
또한, 상기 용기몸체(100)의 하부 측의 확관 결합부(120)에도 그와 대응되게 외측단에 절곡부(302)를 구비한 하부캡(300)을 삽입하여 그 끝단과 상기 하부 측의 확관 결합부의 끝단 역시 공지의 맞대기 용접하여 결합하므로서, 일련의 가스 용기의 제조가 완료된다. In addition, a lower cap 300 having a bent portion 302 is inserted into the expansion pipe coupling portion 120 of the lower side of the container body 100 so as to correspond to the expansion pipe of the end and the lower side thereof. The ends of the joints are also known butt-welded to join, thus completing the manufacture of a series of gas containers.
상기에서, 마운틴컵에는 공지의 연소장치에 장착된 장착부와 결합되는 일반적인 가이드림부가 형성되어 진다. In the above, the mountain cup is formed with a general guide rim coupled to the mounting portion mounted on a known combustion device.
이와같이 제조되는 종래 가스 용기에 있어서는 상,하부 캡을 결합하기 위한 상기 용기몸체의 상,하부에 형성된 확관 결합부가 확관작업으로 인한 그 부위에 피로강도나 인장강도가 약할 뿐만 아니라 상기 상,하부캡의 끝단과 용기몸체의 끝단이 단순히 맞대기 용접되어 있으므로서, 상기 용기몸체에 고압으로 압축된 액화상태의 가스를 주입시 상기 가스 용기의 확관 결합부와 용접된 부분이 변형되거나 파열되는 문제점이 발생하였다. In the conventional gas container manufactured as described above, the expansion pipe coupling portion formed at the upper and lower portions of the container body for coupling the upper and lower caps is not only weak in fatigue strength or tensile strength due to the expansion operation, but also in the upper and lower caps. Since the end and the end of the container body are simply butt-welded, a problem arises that the welded portion and the welded portion of the gas container are deformed or ruptured when the liquefied gas is injected at high pressure into the container body.
또한, 상기 용기몸체로 규정된 이상의 고압이 발생하거나 외부화재 등의 재해로 인한 온도상승에 의해 가스 용기의 형태가 쉽게 변형 및 파열은 물론 경우에 따라서는 폭발까지 발생하는 문제점을 가지고 있었다. In addition, the gas container has a problem in that the shape of the gas container is easily deformed and ruptured, as well as an explosion, in some cases, due to an increase in temperature due to the occurrence of a high pressure or an external fire.
이에, 본 발명은 상기와 같은 종래의 제반 문제점을 해소하고자 안출한 것으로, 그 목적은 재충전 사용에 따른 압력변화에도 가스 용기의 기밀성을 최대한 확보함과 동시에 주입된 가스가 배출되는 밸브체를 상부캡으로 용접이 아닌 나사결합에 의해 간편하게 결합 및 분리가 이루어질 수 있도록 하는 데 있다. Accordingly, the present invention has been made to solve the conventional problems as described above, the object is to ensure the maximum airtightness of the gas container at the same time the pressure change according to the recharge use and at the same time the top of the valve body to discharge the injected gas In order to be able to be easily combined and separated by screwing rather than welding.
상기와 같은 목적을 이루기 위한 본 발명은 고압으로 압축되어 액화상태로 주입되는 가스를 재충전시켜 사용할 수 있는 충전용 가스 용기를 제조하는 방법에 있어서, 동일 직경으로 일정한 길이를 갖도록 제작되는 관형태의 용기몸체를 제작하는 용기몸체 제작공정과; 중앙에 밸브체를 나사결합할 수 있도록 내주면에 나선부가 형성되도록 함입된 결합홈이 형성되게 상부 측이 좁고 하부 측이 점차적으로 넓게 형성되어 지고, 외측단에는 절곡리이브를 갖도록 상부캡을 제작하는 상부캡 제작공정과; 상측에서 하측으로 만곡형태로 형성되어 지고, 외측단에는 절곡리이브가 형성되는 하부캡을 제작하는 하부캡 제작공정과; 상기 용기몸체의 상하부에 상기 상부캡과 하부캡의 절곡리이브가 그 용기몸체의 내측면과 외측면을 감싸도록 시이밍(seaming)작업 한 후, 상기 용기몸체의 외측면과 시이밍작업에 의해 그 용기몸체의 외측면으로 접혀진 상기 상,하부캡의 절곡리이브 끝단을 용접하여 결합하는 상,하부캡 용접공정을 포함하는 것을 특징으로 한다. The present invention for achieving the above object is a method of manufacturing a filling gas container that can be used to refill the gas injected in a liquefied state by compression at high pressure, the tubular container manufactured to have a constant length with the same diameter Container body manufacturing process for manufacturing a body; The upper side is narrow and the lower side is gradually widened to form a coupling groove formed so that a spiral portion is formed on the inner circumferential surface so as to screw the valve body in the center, and the upper cap is manufactured to have a bending rib at the outer end. Upper cap manufacturing process; A lower cap manufacturing process for forming a lower cap formed in a curved shape from an upper side to a lower side, and having a bending rib formed at an outer end thereof; After seaming to cover the inner and outer surfaces of the container body with the bending ribs of the upper cap and the lower cap on the upper and lower parts of the container body, by the outer surface and the seaming operation of the container body. It characterized in that it comprises an upper and lower cap welding process for welding by joining the end of the bending ribs of the upper and lower caps folded to the outer surface of the container body.
이하, 본 발명의 바람직한 실시예를 첨부된 도면을 참고하여 좀더 상세하게 설명하면 다음과 같다. Hereinafter, preferred embodiments of the present invention will be described in detail with reference to the accompanying drawings.
도 1은 본 발명의 공정을 나타낸 블럭도이다. 1 is a block diagram illustrating the process of the present invention.
도시된 바와 같이 고압으로 압축되어 액화상태로 주입되는 가스를 재충전시켜 사용할 수 있는 통상의 충전용 가스 용기를 제조하는 방법에 있어, In the method for manufacturing a conventional filling gas container that can be used to refill the gas injected in a liquefied state as shown in the high pressure,
본 발명은 동일 직경으로 일정한 길이를 갖도록 절단기 등과 같은 일반적인 방식으로 절단되어 제작되는 관형태의 용기몸체를 제작하는 용기몸체 제작공정(S1)과; The present invention is a container body manufacturing process (S1) for producing a tubular container body is cut and manufactured in a general manner such as a cutter to have a constant length with the same diameter;
상기 용기몸체 제작공정을 통하여 제작된 용기몸체의 상단으로 위치할 수 있도록 중앙에 밸브체의 외주면으로 형성된 나선부가 나사결합되게 내주면으로 통상의 나선가공기를 통하여 가공되는 나선부가 형성되도록 함입된 결합홈이 형성되게 상부 측이 좁고 하부 측이 점차적으로 넓게 형성되어 지고 외측단에는 절곡리이브가 형성되도록 통상의 프레스 작업에 의해 상부캡을 제작하는 상부캡 제작공정(S2)과; Coupling grooves are formed so that the spiral portion formed through the usual spiral processing machine to the inner circumferential surface to be screwed into the spiral portion formed in the outer peripheral surface of the valve body in the center to be located to the upper end of the container body produced through the container body manufacturing process An upper cap manufacturing process (S2) of forming an upper cap by a normal press work so that an upper side is formed to be narrow and a lower side is gradually formed to be wider and a bending rib is formed at an outer end thereof;
상기 용기몸체 제작공정을 통하여 제작된 용기몸체의 하단으로 위치할 수 있도록 통상의 프레스 작업에 의해 상측에서 하측으로 만곡형태로 형성되어 지고 외측단에는 절곡리이브가 형성되는 하부캡을 제작하는 하부캡 제작공정(S3)과; The lower cap is formed in a curved shape from the upper side to the lower side by a normal press work so that it can be located to the lower end of the container body produced through the container body manufacturing process and the outer cap is formed a lower cap formed bending bend Manufacturing process (S3);
상기 용기몸체의 상하부에 상기 상부캡과 하부캡의 절곡리이브가 그 용기몸체의 내측면과 외측면을 감싸도록 공지의 시이밍(seaming)작업 한 후, 상기 용기몸체의 외측면과 시이밍 작업에 의해 그 용기몸체의 외측면으로 접혀진 상기 상,하부캡의 절곡리이브 끝단을 용접하여 결합하는 상,하부캡 용접공정(S4)을 포함하는 것을 나타낸 것이다. After the known seaming operation so that the bending ribs of the upper cap and the lower cap surround the inner and outer surfaces of the container body at the upper and lower portions of the container body, the seaming operation with the outer surface of the container body is performed. By the upper and lower caps folded to the outer surface of the container body by the upper and lower cap welding process (S4) for joining by welding to combine the ends of the cap is shown.
상기에서, 상부캡의 제작공정 후 그 결합홈의 외측 상부캡의 상면으로 필요에 따라 공지의 연소장치에 장착된 장착부와 결합되는 일반적인 가이드림부를 용접하여 형성할 수도 있다. In the above, after the manufacturing process of the upper cap to the upper surface of the outer upper cap of the coupling groove may be formed by welding a general guide rim coupled to the mounting portion mounted to a known combustion device as needed.
도 2는 본 발명의 용기몸체 제작공정을 나타낸 요부도이다. Figure 2 is a main part showing a container body manufacturing process of the present invention.
도시된 바와 같이 동일 직경(W)으로 제작하고자 하는 가스 용기의 길이에 따라 일정한 길이(L)를 갖도록 통상의 절단기 등과 같은 일반적인 방식으로 절단하여 제작하는 관형태의 용기몸체(10)를 제작하는 것을 나타낸 것이다. As shown in the drawing to produce a tubular container body 10 that is cut and manufactured in a general manner such as a conventional cutter so as to have a constant length (L) according to the length of the gas container to be produced with the same diameter (W) It is shown.
도 3은 본 발명의 상부캡 제작공정을 나타낸 요부도이다. Figure 3 is a main part showing the upper cap manufacturing process of the present invention.
도시된 바와 같이 상기한 용기몸체가 제작된 후에는 그 용기몸체의 상단으로 위치할 수 있도록 중앙에 밸브체(210)의 외주면으로 형성된 나선부가 나사결합되게 내주면으로 통상의 나선가공기를 통하여 가공되는 나선부(22)가 형성되도록 함입된 결합홈(24)이 형성되게 상부 측이 좁고 하부 측이 점차적으로 넓게 형성되어 지고 외측단에는 절곡리이브(26)를 갖도록 통상의 프레스 작업에 의해 상부캡(20)을 제작한다. As shown in the figure, after the container body is manufactured, a spiral thread is formed on the inner circumferential surface of the valve body 210 so as to be screwed into the upper end of the container body. The upper cap is formed by the usual press operation so that the upper side is narrow and the lower side is gradually widened and the outer end has the bent rib 26 so that the engaging groove 24 embedded in the portion 22 is formed. 20).
도 4는 본 발명의 하부캡 제작공정을 나타낸 요부도이다. Figure 4 is a main part showing a lower cap manufacturing process of the present invention.
도시된 바와 같이 상기한 용기몸체의 하단으로 위치할 수 있도록 통상의 프레스 작업에 의해 상측에서 하측으로 만곡형태로 형성되어 지고 외측단에는 절곡리이브(32)가 형성되는 하부캡(30)을 제작한다. As shown, the lower cap 30 is formed in a curved shape from the upper side to the lower side by a normal press work so as to be located at the lower end of the container body, and the bent rib 32 is formed at the outer end. do.
상기에서, 상부캡와 하부캡의 절곡리이브 직경은 상기 용기몸체의 내측면과 외측면을 감싸도록 공지의 시이밍작업을 행할 수 있을 정도로 상기 용기몸체의 직경 보다 큰 직경을 갖도록 한다. In the above, the bending rib diameter of the upper cap and the lower cap is to have a diameter larger than the diameter of the container body to be able to perform a known seaming operation to surround the inner surface and the outer surface of the container body.
도 5는 본 발명의 상,하부캡 용접공정을 나타낸 요부도이다. 5 is a main view showing the upper and lower cap welding process of the present invention.
도시된 바와 같이 상기한 용기몸체(10)와 상,하부캡(20)(30)의 제작이 완료되면 상기 용기몸체의 상하부에 상기 상부캡과 하부캡의 절곡리이브(26)(32)가 그 용기몸체의 내측면과 외측면을 감싸도록 공지의 시이밍(seaming)작업 한 후, 상기 용기몸체의 외측면과 시이밍 작업에 의해 그 용기몸체의 외측면으로 접혀진 상기 상,하부캡(20)(30)의 절곡리이브(26)(32) 끝단을 용접하여 결합한다. As shown, when the manufacturing of the container body 10 and the upper and lower caps 20 and 30 is completed, the bending caps 26 and 32 of the upper cap and the lower cap are formed on upper and lower portions of the container body. After the known seaming work to surround the inner and outer surfaces of the container body, the upper and lower caps 20 which are folded to the outer surface of the container body by the outer surface and the seaming operation of the container body 20 The ends of the bending ribs 26 and 32 of the 30 are welded to each other.
그런 다음 상기 상부캡(20)의 결합홈(24)으로 형성된 나선부에 밸브체를 나사결합하므로서, 일련의 가스 용기를 제작이 완료되는 것이다. Then, by screwing the valve body to the spiral portion formed by the coupling groove 24 of the upper cap 20, a series of gas containers are completed.
따라서, 종래 용기몸체의 상단과 하단으로 상부캡과 하부캡을 결합하기 위해 행하였던 별도의 확관작업을 삭제할 수 있을 뿐만 아니라 용기몸체의 상단과 하단으로 상부캡과 하부캡의 외측단에 형성된 절곡리이브를 그 용기몸체의 내측면과 외측면으로 시이밍작업에 의해 압착과 같은 형태로 밀착되어 접혀진 후 용기의 외측면으로 위치한 상,하부캡의 절곡리이브 끝단과 용접을 통하여 결합하므로서, 상당히 높은 기밀성을 가지게 되는 것이다. Therefore, not only can the separate expansion work performed to combine the upper cap and the lower cap to the upper and lower ends of the container body, but also the bending formed in the outer end of the upper cap and the lower cap to the upper and lower ends of the container body. The eve is pressed and folded into the inner and outer sides of the container body in the same form by crimping by seaming, and then joined by welding with the bent rib ends of the upper and lower caps located on the outer side of the container. It will have confidentiality.
즉, 상기 용기몸체의 상,하단으로 각각의 상,하부캡의 외측단으로 형성된 절곡리이브를 내측면과 외측면으로 시이밍작업에 의해 1차적으로 밀착되게 접혀진 다음 그 용기몸체의 외측면으로 접혀진 상,하부캡의 외측단인 절곡리이브를 재차 용접하여 결합함에 따라 용기몸체와 상,하부캡이 완전히 밀봉되어져 긴밀한 기밀성을 가지게 되는 것이다. That is, the upper and lower ends of the container body is folded into the inner side and the outer cap of the lower cap of the upper and lower sides of the inner side and the outer side by primary seam folded by the seaming operation and then to the outer side of the container body By welding the folded ribs, which are the outer ends of the folded upper and lower caps again, the container body and the upper and lower caps are completely sealed to have tight airtightness.
그에 따라 재충전 사용에 따른 고압으로 압축된 액화상태의 가스를 주입시에도 그 결합부분에서 변형 및 파열되는 것을 최소화할 수 있을 뿐만 아니라 외부에서 발생하는 압력이나 온도상승에 따른 용기몸체의 내부 압력변화에서도 가스 용기의 변형이나 파열 및 폭발하는 것을 최소화할 수 있는 조건을 구바하게 되는 것이다. As a result, even when injecting liquefied gas compressed at high pressure according to recharging, it is possible to minimize deformation and rupture at the joint part, and also to change the internal pressure of the container body due to external pressure or temperature rise. It is designed to minimize the deformation, rupture and explosion of the gas container.
상술한 바와 같이 본 발명은 재충전하여 사용할 수 있도록 제조되는 가스 용기를 용기몸체의 상,하단을 확관작업 없이 그 용기몸체의 상,하단으로 상,하부캡의 외측단으로 형성된 절곡리이브에 의해 내측면과 외측면으로 밀착되게 접혀진 후 그 용기몸체의 외측면과 그에 접혀진 끝단을 용접작업을 통하여 결합하므로서, 상당히 높을 기밀성을 유지하게 되어 재충전에 따른 고압으로 압축된 액화상태의 가스를 주입시와 가스 용기 내의 압력변화에도 가스 용기의 변형이나 파열을 방지할 수 있을 뿐만 아니라 상부캡으로 내주면에 나선부가 형성된 결합홈에 의해 밸브체의 파손이나 손상시에도 간편하게 결합 및 분리할 수 있어 편리하게 교체할 수 있는 효과를 가지는 것이다. As described above, the present invention provides a gas container manufactured to be recharged and used by bending the ribs formed at the outer end of the upper and lower caps to the upper and lower ends of the container body without expanding the upper and lower ends of the container body. After being folded in close contact with the side and the outer surface, the outer surface of the container body and the folded end thereof are joined by welding, thereby maintaining a very high airtightness and injecting the gas in a liquefied state compressed at high pressure according to recharging. Not only can the gas container be deformed or ruptured even when the pressure in the container changes, but the coupling grooves with spirals formed on the inner circumferential surface of the upper cap can be easily combined and separated even when the valve body is damaged or damaged. It is to have an effect.
도 1은 본 발명의 공정을 나타낸 블럭도.1 is a block diagram illustrating the process of the present invention.
도 2는 본 발명의 용기몸체 제작공정을 나타낸 요부도.Figure 2 is a main part showing a container body manufacturing process of the present invention.
도 3은 본 발명의 상부캡 제작공정을 나타낸 요부도.Figure 3 is a main part showing the upper cap manufacturing process of the present invention.
도 4는 본 발명의 하부캡 제작공정을 나타낸 요부도.Figure 4 is a main part showing a lower cap manufacturing process of the present invention.
도 5는 본 발명의 상,하부캡 용접공정을 나타낸 요부도.Figure 5 is a main part showing the upper, lower cap welding process of the present invention.
도 6은 종래 충전용 가스 용기를 나타낸 요부 단면도.6 is a sectional view showing the main parts of a conventional gas container for filling;
도면의 주요 부분에 대한 부호의 설명Explanation of symbols for the main parts of the drawings
10 : 용기몸체10: container body
20 : 상부캡20: upper cap
22 : 나선부 24 : 결합홈 22: spiral 24: coupling groove
26,32 : 절곡리이브 26,32: Bending Live
30 : 하부캡30: lower cap
210 : 밸브체210: valve body
Claims (1)