KR100457681B1 - Melt spinning machine containing godet roller having automatic washable function to increase productivity - Google Patents
Melt spinning machine containing godet roller having automatic washable function to increase productivity Download PDFInfo
- Publication number
- KR100457681B1 KR100457681B1 KR1019970047948A KR19970047948A KR100457681B1 KR 100457681 B1 KR100457681 B1 KR 100457681B1 KR 1019970047948 A KR1019970047948 A KR 1019970047948A KR 19970047948 A KR19970047948 A KR 19970047948A KR 100457681 B1 KR100457681 B1 KR 100457681B1
- Authority
- KR
- South Korea
- Prior art keywords
- roller
- godet roller
- melt spinning
- spinning machine
- cleaning
- Prior art date
Abstract
Description
본 발명은 산업용 폴리에스터 장섬유를 제조하기 위한 용융방사기에 관한 것으로 특히 고뎃롤러 사이에 자동세정장치를 부착함으로써 공정성을 개선하면서 생산성을 높일 수 있는 용융방사기에 관한 것이다.The present invention relates to a melt spinning machine for producing an industrial polyester long fiber, and more particularly, to a melt spinning machine capable of increasing productivity while improving processability by attaching an automatic cleaning device between high rollers.
일반적으로 산업용 폴리에스터 장섬유는 방사 및 연신 공정 중에 여러 개의 고뎃 롤러를 거쳐 제조된다.In general, industrial polyester long fibers are produced via several rollers during the spinning and stretching process.
이때 고뎃롤러의 온도는 최고 250℃까지 이르는 경우가 있으며, 이에 따라 필라멘트사가 주행 중에 고뎃롤러상에서 이탈된 올리고머, 불순물 또는 유제 성분 등이 침적된 경우 높은 온도의 열에 의해 탄화되는 현상이 발생한다.At this time, the temperature of the gourd roller may reach a maximum of 250 ° C. As a result, when the filament yarn is separated from the gourd roller while the oligomer, impurities, or an oil component is deposited, the phenomenon of carbonization occurs due to high temperature.
상기한 현상의 정도가 심해지면 방사공정성을 악화시키고, 모우 등의 발생으로 인해 사의 품질이 저하되므로 일정 기간마다 고뎃롤러의 세정을 행하여야 하는바 이로인해 고뎃롤러의 운전을 정지하여야 하는 것이어서 필연적으로 생산성의 저하를 수반하게 되는 문제점이 있는 것이다.If the above-mentioned phenomenon is worsened, deterioration of the radiation processability and the quality of the yarn is deteriorated due to the occurrence of cattle, etc. Therefore, the rollers must be cleaned every certain period. There is a problem that is accompanied by a decrease in productivity.
한편 상기와 같은 문제점을 해결하기 위하여 대한민국 특허등록 제 23626호의 "방사장치 세정방법 "의 기술이 알려지고 있으며 이는 용융방사에 사용한 후 교환한 방사장치를 트리에틸렌 글리콜 바스에 넣고 가열하여 인출한 다음 황산 암모늄 수용액에 넣고 끓여줌으로써 이물질을 세정하도록 하는 것이나 이는 다음과 같은 문제점을 노출시키게 되는 것이다.On the other hand, in order to solve the above problems, the technology of the "spinning apparatus cleaning method" of the Republic of Korea Patent No. 23626 is known, which is used for melt spinning after replacing the spinning apparatus in a triethylene glycol bath and withdrawn by heating Boil in the ammonium solution to boil off the foreign material to clean, but this exposes the following problems.
⊙ 방사장치를 세정하기 위하여 소정의 화학성분의 세정액을 끓여주기위한 두 단계의 가열장치가 마련되어야 하므로 장치의 설비비가 과다하게 소요되는 것이며,⊙ In order to clean the spinning device, two-stage heating device must be provided to boil a cleaning liquid of a certain chemical component.
⊙ 세정액을 화학물질로 이용하게 되므로 세정작업시 인체에 손상을 주는 경우가 초래되어 세심한 주의를 요하게 되는 것이고, 세정후에도 방사장치에서 세정액을 제거하기 위하여 별도의 세척공정이 요구되는 것이어서 적업공정이 증가됨으로 인해 생산성이 저하되는 것이며,⊙ As the cleaning liquid is used as a chemical, it may cause damage to the human body during the cleaning operation and requires careful attention, and a separate washing process is required to remove the cleaning liquid from the spinning apparatus even after cleaning, and thus the work process is increased. Will reduce productivity.
⊙ 방사장치를 세정하기 위하여 본체에서 분리시켜야 하는 것이므로 장치의 가동이 세정공정을 거치는 약 2∼8시간이상 정지되어야 하는 것이어서 생산성의 저하를 수반하게 되는 문제점이 있는 것이다.⊙ Since the spinning device needs to be separated from the main body in order to clean, the operation of the device should be stopped for about 2 to 8 hours through the cleaning process, which leads to a decrease in productivity.
본 발명은 상기한 기존의 세정방법에서 기인되는 제반 문제점을 해결하기 위한 것으로 고온의 고뎃 롤러의 표면 중 필라멘트사가 닿지 않는 부분에 고뎃롤러 표면의 침적물을 제거할 수 있는 세정날을 접촉시켜 침적물이 고온에 의해 탄화되기 전에 제거토록 하여 공정성을 개선하는 데 그 목적이 있는 것이다.The present invention is to solve the problems caused by the conventional cleaning method described above by contacting the cleaning blade that can remove the deposits on the surface of the high-pressure roller on the part of the surface of the high-temperature roller, the filament yarn does not touch the deposit is high temperature Its purpose is to improve fairness by removing it before it is carbonized.
도 1은 본 발명을 구현하기 위한 일 실시예를 보이는 개략 구성도.1 is a schematic block diagram showing an embodiment for implementing the present invention.
도 2는 본 발명의 세정장치의 외관을 보이는 사시도.Figure 2 is a perspective view showing the appearance of the cleaning device of the present invention.
* 도면의 주요부분에 대한 부호의 설명 *Explanation of symbols on the main parts of the drawings
1,2 : 고뎃롤러 3 : 고뎃롤러박스1,2: high speed roller 3: high speed roller box
4 : 고정용 볼트 5 : 프레임4: fixing bolt 5: frame
6,6' : 석면재질의 세정날 7 : 세정장치6,6 ': Asbestos cleaning blade 7: Cleaning device
고뎃롤러(1)(2)를 세정하기 위한 장치의 형태는 첨부한 도 1에서와 같이 고뎃롤러박스(3)내에 소정의 간격으로 이격,설치되는 한 조의 고뎃롤러(1)(2)사이에 위치되는 상태로 고정용 볼트(4)를 이용하여 고뎃롤러 박스(3)의 후면에 프레임(5)을 부착시킴과 아울러 프레임(5)의 양단부에는 고뎃롤러(1)(2)의 표면과 미소(微小)압력으로 접하는 석면재질의 세정날(6)(6')을 일체로 결합하여 본 발명의 세정장치(7)를 구성한다.The shape of the apparatus for cleaning the roller rollers (1) and (2) is as shown in FIG. 1 between the pair of roller rollers (1) and (2) which are spaced apart and installed at predetermined intervals in the roller roller box (3). Attach the
이와 같이하여 개량된 용융방사기에 의해 산업용 폴리에스터 필라멘트사를 제조하는 경우 기존의 용융방사기로 제조하는 경우에 비해 공정성이 우수하여 세정 주기를 획기적으로 단축시킬 수 있으며, 이에 따라 생산성이 증가하고 물성 또한 우수한 제품을 생산할 수 있었다.In this way, when the industrial polyester filament yarn is manufactured by the improved melt spinning machine, the process cycle is excellent compared to the case of manufacturing the conventional melt spinning machine, and thus the washing cycle can be shortened drastically, thus increasing productivity and physical properties. Could produce a good product.
한편 상기한 세정날(6)(6')을 구성하는데 사용되는 재질은 석면을 사용하며 이는 고온의 고뎃롤러(1)(2)와 접촉하여도 손상되지 않는 내열 및 내마모성을 유지할 수 있도록 하기 위함이다.On the other hand, the material used to construct the cleaning blades (6) and (6 ') is asbestos, which is to maintain heat and abrasion resistance that is not damaged even in contact with the hot roller (1) (2). to be.
이하 본 발명을 실시예 및 비교예를 통하여 구체적으로 설명하겠는 바, 본 발명이 실시예에 의해 한정되는 것은 아니다.Hereinafter, the present invention will be described in detail through Examples and Comparative Examples, but the present invention is not limited to the Examples.
〈실시예〉<Example>
고유점성도가 0.08이고, 광택이 브라이트인 폴리에스터 수지를 건조 후 스크류 압출식 방사기에서 통상의 원형노즐을 통해 방사온도 290℃로 방사하였다.A polyester resin having an intrinsic viscosity of 0.08 and a bright gloss was dried and spun at a spinning temperature of 290 ° C. through a conventional circular nozzle in a screw extruder.
유제 부여 장치를 거친후 온도가 각각 60, 120, 150, 230℃인 고뎃롤로에는 석면 재질의 세정날이 달린 첨부한 도 1과 같은 세정 장치를 설치하였다.After passing through the emulsion applying apparatus, the gouring rollers having temperatures of 60, 120, 150, and 230 ° C., respectively, were installed with the cleaning apparatus as shown in FIG.
이렇게 하여 얻어진 산업용 폴리에스터 필라멘트사의 섬도는 1003 데니어였고, 인장강도는 8.9g/d 파단신도는 13.1%였다.The fineness of the industrial polyester filament yarn thus obtained was 1003 denier, and the tensile strength was 8.9 g / d elongation at break of 13.1%.
이의 공정성을 파악하기 위하여 96시간 동안 생산하여 본 결과 정상제품의 생산 비율을 나타내는 LPIA율이 98%에 이르렀으며 생산하는 동안 고뎃 롤러 부분의 세정 작업을 별도로 할 필요가 없었다.In order to understand its fairness, it was produced for 96 hours. As a result, the LPIA ratio representing the production rate of normal products reached 98%, and there was no need to clean the roller parts during production.
일반적으로 방사공정에 있어서 상업적인 생산이 가능하기 위해서는 LPIA율이 95% 이상이어야 한다.In general, the LPIA rate should be 95% or higher to enable commercial production in spinning processes.
〈비교예 1〉<Comparative Example 1>
온도가 230℃인 고뎃롤러에 세정 장치에 부착된 세정날의 재질이 면인 것을 제외하고는 실시예와 동일하게 실시하였다.It carried out similarly to the Example except the material of the washing | cleaning blade attached to the washing | cleaning apparatus to the high temperature roller whose temperature is 230 degreeC is cotton.
그 결과 면 재질의 세정날이 고온에 의해 손상을 받아 공정에 문제가 발생하여 생산을 중단하여야만 했다.As a result, the cleaning blade made of cotton was damaged by high temperatures, which caused problems in the process and had to be stopped.
〈비교예 2〉<Comparative Example 2>
온도가 230℃인 고뎃롤러에 세정 장치를 설치하지 않은 것을 제외하고는 실시예와 동일하게 실시하였다.It carried out similarly to the Example except the washing apparatus was not installed in the high temperature roller whose temperature is 230 degreeC.
그 결과 LPIA율은 96%였으며, 생산중 고뎃롤러를 물로 세정하는 작업을 2회 실시하여야만 했다.As a result, the LPIA rate was 96%, and the production of high speed rollers had to be performed twice with water.
이상과 같은 본 발명은 고뎃 롤러의 표면 중 필라멘트사가 닿지 않는 부분에 고뎃롤러 표면의 침적물을 제거할 수 있는 석면 재질의 세정날을 접촉시켜 침적물이 고온에 의해 탄화되기 전에 제거토록 하므로써 방사공정성을 향상시키과 아울러 모우 등의 발생을 차단할 수 있는 것이므로 사의 품질개선을 추구할 수 있는 것이며, 고뎃롤러의 운전중에 계속적인 세정이 행해지는 것이므로 별도로 고뎃롤러의 운전을 정지할 필요성이 배제되는 것이므로 기존방법에 비해 생산성의 향상을 기할 수 있으며, 세정장치의 구성이 매우 간단하여 취급이 안전함과 아울러 용이하게 되고 설비상의 경제적 부담이 거의 없는 효과가 있는 것이다.The present invention as described above by contacting the cleaning blade of the asbestos material that can remove the deposits on the surface of the high roller in contact with the part of the surface of the high roller, the filament yarn is not touched to remove the deposit before carbonization by high temperature to improve spinning processability In addition, it is possible to prevent the occurrence of moor, etc., so that the quality improvement of the company can be pursued. Since the continuous cleaning is performed during the operation of the high roller, the need to stop the operation of the high roller is eliminated. Productivity can be improved, and the configuration of the cleaning device is very simple, so that the handling is safe and easy, and there is almost no economic burden on the equipment.
Claims (2)