Abstract

PURPOSE: A wearing band for enhancing a concentration and a preparation method thereof are provided to have an aroma-duration prolonged by using a nano-size carrier, to be used conveniently and to be carried easily. CONSTITUTION: The preparation method of the wearing band for enhancing the concentration comprises the steps of: preparing the nano-size carrier by crushing one or a mixture of two or more selected from the group consisting of zeolite, carboxymethyl cellulose and bentonite; adding the carrier at forming fiber, pulp or porous plastic and then forming to prepare a carrier fixed adsorbing cloth; adsorbing one or more aromatic natural extract to the carrier fixed to the adsorbing cloth; and dewatering and drying the cloth.

Description

A Wearing Band for Enhancing Concentration}

발명의 분야Field of invention

본 발명은 방향성 천연 추출물이 흡착되어 있는 착용밴드 및 그 제조방법에 관한 것이다. 보다 구체적으로는, 나노사이즈의 담체를 이용하여 방향성 천연 추출물의 향이 오래 지속되도록 한 착용밴드 및 그 제조방법에 관한 것이다.The present invention relates to a wear band and a method of manufacturing the adsorbed aromatic natural extract. More specifically, the present invention relates to a wear band and a method of manufacturing the same, wherein the fragrance of the aromatic natural extract is long-lived using a nano-sized carrier.

발명의 배경Background of the Invention

근래에 이르러 아로마 오일 등의 향료의 향기를 흡입함으로서 각종 질환을치료하는 아로마테라피 요법이 크게 각광을 받고 있다.In recent years, aromatherapy treatments for treating various diseases by inhaling the fragrance of fragrances such as aroma oils have been in the spotlight.

일반적으로, 아로마테라피는 향기(Aroma)와 치료(Therapy)를 합성한 용어로서, 방향성식물(Herb)에서 추출한 100% 순수 정유(精油:에센셜 오일, Essential Oil)를 피부 또는 호흡기를 통해 체내에 흡수시켜 몸과 마음을 건강하게 하는 순수 자연 치유법을 일컫는 말이다.In general, aromatherapy is a term combining aroma and therapeutic, and it absorbs 100% pure essential oils extracted from aromatic plants through the skin or respiratory system. It is a pure natural healing method that makes the body and mind healthy.

이러한 아로마테라피는 코와 피부를 통해 뇌와 몸을 자극하여 몸과 마음의 균형을 유지시키고, 스트레스나 불규칙적인 생활 습관으로부터 발생된 질병, 정신과 및 피부과 질병을 치유하는데 뛰어난 효능이 있는 것으로 잘 알려져 있다.This aromatherapy is well known for stimulating the brain and body through the nose and skin to balance the mind and body and to cure diseases, psychiatric and dermatological diseases resulting from stress or irregular lifestyles. .

특히, 학습이나 두뇌 활동시 집중력 강화의 효과가 있는 천연 추출물의 향을 맡으면 그 두뇌 활동의 효율이 증대된다.In particular, the smell of natural extracts that enhance the concentration of learning or brain activity, the efficiency of the brain activity is increased.

아로마테라피를 통한 치료 방법에서 무엇보다 중요한 것은 방향성식물로부터의 추출물에 친숙해지는 것이다. 이를 위하여 종래에 가정이나 사무실 등에 설치되어 정유를 강제 휘발시킴으로써 실내 공기를 통하여 자연스럽게 아로마테라피가 이루어지도록 하는 발향장치가 개시된 바 있다.The most important thing in the treatment method through aromatherapy is to be familiar with extracts from aromatic plants. To this end, a fragrance device has been disclosed in which aromatherapy is naturally performed through indoor air by installing volatilized essential oil in a home or office.

이러한 강제 발향장치의 일 예로서, 국내 공개특허공보 제 2000-30403호(2000. 6. 5)에는 다공성의 향 발산체에 그 향 발산체를 가열하는 전열선을 마련하고, 그 전열선이 배열된 향 발산체의 중앙에 인체에 유익한 아로마 액체향이나 기타 액체향을 함침시킨 후 전열선에 전기를 통전시켜 전열선에서 발생하는 열기에 의해 함침된 향이 발산되게 한 향 발산장치가 개시되어 있다.As an example of such a forced fragrance apparatus, Korean Laid-Open Patent Publication No. 2000-30403 (June 5, 2000) provides a heating wire for heating the fragrance emitter in a porous fragrance emitter, and the fragrance in which the heating wire is arranged. Disclosed is a fragrance emanation device which impregnates aroma liquid fragrance or other liquid fragrance beneficial to the human body in the center of the divergence body and then energizes the heating wire to emit the scent impregnated by the heat generated from the heating wire.

또한, 국내 공개특허공보 제 2001-28991호(2001. 4. 6)에는 전기적인 열을이용하여 향료를 휘발시킴으로써 실내 공기를 쾌적한 상태로 유지토록 한 전기 발향기가 개시되어 있다.In addition, Korean Laid-Open Patent Publication No. 2001-28991 (April 6, 2001) discloses an electric fragrance which maintains indoor air in a comfortable state by volatilizing perfume using electric heat.

그러나, 상술한 바와 같은 종래의 강제 발향장치들은 공통적으로 전기적인 열을 이용하여 향료를 휘발시키도록 되어 있기 때문에 필수적으로 전기적인 배선이 필요하며, 그 결과 휴대 및 이동이 불편한 문제점이 있으며, 향료를 가열 및 휘발시킴으로써 향이 변질될 우려가 있었다.However, since the conventional forced fragrance devices as described above are commonly designed to volatilize the fragrance by using electrical heat, electrical wiring is essentially required, and as a result, there is a problem in that it is inconvenient to carry and move. There was a fear that the fragrance may be altered by heating and volatilization.

한편, 종래에 전술한 바와 같은 장제 발향장치외에 용기에 액상의 방향제를 충진하여 액상의 방향제가 기화되면서 용기의 통공을 통해 외부로 발산되도록 한 자연 발향용기가 개발되어 널리 이용되고 있다.On the other hand, in addition to the conventional fragrance fragrance device as described above, by filling the liquid fragrance into the container, the natural fragrance container has been developed and widely used so that the liquid fragrance is vaporized to the outside through the through hole of the container.

그러나, 기존의 천연 추출물의 향을 제공하기 위한 제품은 아로마 향이나 기능성 소재를 훈증이나 용기에 의하여 사용하여 효과의 지속성이 없으며 향의 휘산성을 조절할 수가 없었다. 또한, 그 사용이나 이동성이 제한되어 있어 불편하다는 단점이 지적되어 왔다.However, the existing products for providing the aroma of natural extracts using aroma or functional materials by fumigation or container, there is no sustainability of effect and could not control the volatility of the fragrance. In addition, it has been pointed out that its use or mobility is limited and inconvenient.

이에 본 발명자는 위해 나노사이즈의 담체를 사용하여 지속시간을 길게 하고 그 사용이 간편한 착용밴드를 개발하고 본 발명을 완성하기에 이르렀다.Therefore, the inventors of the present invention have developed a wear band which is easy to use and has a long time duration by using a nano-sized carrier to complete the present invention.

본 발명의 목적은 나노사이즈 담체에 방향성 천연 추출물을 흡착하여 향의 지속시간이 길고, 사용이 간편하고 이동성을 갖춘 착용밴드 및 그 제조방법을 제공하는데 있다.An object of the present invention is to provide a wear band and a method of manufacturing the same by adsorbing the aromatic natural extract on the nano-sized carrier has a long duration of fragrance, easy to use and mobile.

도 1은 나노사이즈 담체에 방향성 천연 추출물을 흡착한 것을 도시한 것이다. 도 1a는 나노사이즈의 담체를 균등하게 고착하여 만든 흡착포를 나타낸 것이고, 도 1b는 흡착포 내의 나노사이즈 담체의 모양을 확대하여 나타낸 것이며, 도 1c는 나노사이즈의 담체에 방향성 천연 추출물이 흡착된 모양을 나타낸 것이다.Figure 1 illustrates the adsorption of aromatic natural extract on the nano-size carrier. Figure 1a shows the adsorption cloth made by uniformly fixing the nano-sized carrier, Figure 1b is an enlarged view of the shape of the nano-sized carrier in the adsorption cloth, Figure 1c is a shape in which the aromatic natural extract is adsorbed on the nano-sized carrier It is shown.

상기 목적을 달성하기 위하여 본 발명은 (a) 제올라이트, CMC 및 벤토나이트로 구성된 군에서 선택된 하나 또는 둘이상의 혼합물을 분쇄하여 나노사이즈의 담체를 만드는 단계; (b) 섬유, 펄프 또는 다공성 플라스틱의 제조 성형시 상기 담체를 첨가한 다음 제조 성형하여 담체가 고착된 흡착포를 만드는 단계; (c) 상기 흡착포에 고착된 담체에 바질, 버가못, 로즈마리, 페퍼민트, 클라리세이지 및 라벤더 추출물로 구성된 군에서 선택된 하나 이상의 방향성 천연 추출물을 흡착하는 단계; 및 (d) 상기 방향성 천연 추출물이 흡착된 흡착포를 탈수·건조시키는 단계를 포함하는 착용밴드의 제조방법을 제공한다.In order to achieve the above object, the present invention comprises the steps of (a) pulverizing one or two or more mixtures selected from the group consisting of zeolite, CMC and bentonite to make a nano-sized carrier; (b) adding the carrier and then forming and molding the fiber, pulp or porous plastic to form an adsorbent cloth to which the carrier is fixed; (c) adsorbing at least one aromatic natural extract selected from the group consisting of basil, bergamot, rosemary, peppermint, clary sage and lavender extract to a carrier fixed to the adsorption cloth; And (d) dehydrating and drying the adsorption cloth to which the aromatic natural extract is adsorbed.

본 발명은 또한, (a) 제올라이트, CMC 및 벤토나이트로 구성된 군에서 선택된 하나 또는 둘이상의 혼합물을 분쇄하여 나노사이즈의 담체를 만드는 단계; (b) 섬유, 펄프 및 다공성 플라스틱으로 구성된 군에서 선택된 하나 또는 둘 이상을 혼합하여 성형된 수지제품에 상기 담체를 도포하는 단계; (c) 상기 담체가 도포된 수지를 가열하여 담체가 팽윤·고착된 흡착포를 제조하는 단계; (d) 상기 흡착포에 고착된 담체에 바질, 버가못, 로즈마리, 페퍼민트, 클라리세이지 및 라벤더 추출물로 구성된 군에서 선택된 하나 이상의 방향성 천연 추출물을 흡착하는 단계; 및 (e) 상기 방향성 천연 추출물이 흡착된 흡착포를 탈수·건조시키는 단계를 포함하는 착용밴드를 제조방법을 제공한다.The invention also comprises the steps of (a) milling one or more mixtures selected from the group consisting of zeolite, CMC and bentonite to make a nano-sized carrier; (b) applying the carrier to a molded resin product by mixing one or two or more selected from the group consisting of fibers, pulp and porous plastics; (c) heating the resin to which the carrier is applied to produce an adsorbent cloth in which the carrier is swelled and fixed; (d) adsorbing at least one aromatic natural extract selected from the group consisting of basil, bergamot, rosemary, peppermint, clary sage and lavender extract to a carrier fixed to the adsorption cloth; And (e) dehydrating and drying the adsorption cloth to which the aromatic natural extract is adsorbed.

본 발명에 있어서, 상기 수지의 사용양은 상기 담체 100 중량부에 대하여 2 내지 50 중량부인 것이 바람직하고, 상기 방향성 천연 추출물은 담체 100중량부에 대하여 5~50 중량부의 범위에서 하나 또는 둘 이상을 혼합하여 사용하는 것이 바람직하다.In the present invention, the use amount of the resin is preferably 2 to 50 parts by weight based on 100 parts by weight of the carrier, the aromatic natural extract is mixed one or two or more in the range of 5 to 50 parts by weight based on 100 parts by weight of the carrier. It is preferable to use.

본 발명은 또한, 상기 방법에 의해 제조된 착용밴드를 제공한다.The present invention also provides a wearing band manufactured by the above method.

이하, 실시예를 통하여 본 발명을 더욱 상세히 설명하고자 한다. 이들 실시예는 오로지 본 발명을 예시하기 위한 것으로서, 본 발명의 범위가 이들 실시예에 의해 제한되는 것으로 해석되지는 않는다 할 것이다.Hereinafter, the present invention will be described in more detail with reference to Examples. These examples are only for illustrating the present invention, and the scope of the present invention is not to be construed as being limited by these examples.

실시예 1 : 나노사이즈 담체의 제조Example 1 Preparation of Nanosize Carriers

제올라이트, 카르복시메틸셀룰로오스(carboxymethyl cellulose: CMC) 및 벤토나이트와 실리카류로 구성된 군에서 선택된 하나 또는 둘 이상의 혼합물을 통상의 졸-겔 제조법(sol-gel)과 분쇄법에 의하여 나노사이즈의 담체를 제조하였다.One or two or more mixtures selected from the group consisting of zeolite, carboxymethyl cellulose (CMC) and bentonite and silica were prepared by conventional sol-gel preparation and grinding to prepare nano-sized carriers. .

졸-겔(sol-gel)법에 의한 나노사이즈 담체의 제조과정을 구체적으로 기술하면, 졸은 1㎛ 이하의 콜로이드 입자의 분산을 의미하며 화학반응에 의해 금속 알콕사이드(metal alkoxide) 용액으로부터 혹은 함수/무수 금속 옥사이드(hydrous/anhydrous metal oxide)의 콜로이드 입자를 이용하여 제조가 가능하며, 공정을 진행하면서 졸의 점성이 점점 증가하여 겔을 형성하게 되므로 졸-겔 프로세스라 부른다. 여기서, 겔이란 산화물 세라믹에서 볼 수 있는 결합과 유사한 M-O-M(Metal-oxide-Metal) 결합을 형성하는 삼차원 고분자 네트워크(three-dimentional polymeric network)를 의미한다.Specifically describing the preparation of the nano-sized carrier by the sol-gel method, sol refers to the dispersion of colloidal particles of 1 μm or less and is obtained from a metal alkoxide solution by chemical reaction or It is possible to manufacture using colloidal particles of hydrous / anhydrous metal oxide, and it is called a sol-gel process because the viscosity of the sol gradually increases to form a gel during the process. Here, the gel refers to a three-dimentional polymeric network that forms a metal-oxide-metal (M-O-M) bond similar to that found in oxide ceramics.

더욱 구체적으로, 졸-겔 프로세스는 그 원료 물질에 따라 콜로이드 입자를 이용한 콜로이드 졸-겔과 금속 알콕사이드와 같은 유기금속 전구체(organometallic precursor)를 이용한 고분자 졸-겔로 분류할 수 있는데 후자가 더 일반적이다. 알콕사이드 분자는 사용된 개개의 알콕사이드, 용매 또는 다른 인자들의 영향을 받아 모노머(monomers), 다이머(dimers) 등으로 존재하며 금속 알콕사이드의 가수 분해 반응과 축중합 반응 때문에 중합이 일어난다. 중합되는 동안 외부에서 첨가되는 물은 개시제로서 작용하며 산이나 염기는 이들 반응에 대해서 촉매 역할을 한다. 졸의 초기 점도는 다소 낮고 대부분의 경우 물의 점도와 비슷하다. 그러나, 축중합반응이 상당한 크기로 일어나면 졸은 겔로 변화한다. 이들 반응이 일어나기 시작할 때 금속 알콕사이드 용액은 졸로 변하기 시작한다. 초기 겔화단계 중에 존재하는 상대적으로 낮은 분자량 종(species)은 올리고머(oligomer)로 불리운다.More specifically, the sol-gel process may be classified into a polymer sol-gel using colloidal sol-gel using colloidal particles and an organometallic precursor such as a metal alkoxide, depending on the raw material, the latter being more common. Alkoxide molecules exist as monomers, dimers, etc. under the influence of the individual alkoxides, solvents or other factors used, and polymerization occurs due to hydrolysis and polycondensation reactions of the metal alkoxides. Water that is added externally during the polymerization acts as an initiator and acids or bases catalyze these reactions. The initial viscosity of the sol is rather low and in most cases comparable to that of water. However, if the polycondensation occurs at a significant size, the sol turns into a gel. When these reactions begin to occur, the metal alkoxide solution begins to turn into a sol. The relatively low molecular weight species present during the initial gelling step are called oligomers.

실시예 2: 수지에 나노사이즈 담체가 고착된 흡착포의 제조Example 2 Preparation of Adsorbent Cloth with Nano-Sized Carrier Adhered to Resin

상기 실시예 1에서 제조된 담체를 섬유, 펄프 또는 다공성 플라스틱의 제조 성형시 첨가한 다음 제조 성형하여 상기 담체가 고착된 흡착포를 제조하였다. 또 다른 방법으로 섬유, 펄프 또는 다공성 플라스틱을 단독 또는 둘 이상 혼합·성형하여 만든 수지제품에 상기 담체를 도포한 다음 180℃로 3분간 가열하여 담체를 팽윤·고착시켜 흡착포를 제조하였다. 본 실시예에 있어서 사용된 수지의 양은 담체 100 중량부에 대하여 2~50 중량부이었다.The carrier prepared in Example 1 was added during the production molding of fibers, pulp or porous plastic, and then manufactured and molded to prepare an adsorbent cloth to which the carrier was fixed. In another method, the carrier was applied to a resin product made by mixing or molding fibers, pulp, or porous plastics alone or two or more, and then heated at 180 ° C. for 3 minutes to swell and fix the carrier to prepare an absorbent fabric. The amount of resin used in this example was 2 to 50 parts by weight based on 100 parts by weight of the carrier.

상기 담체를 섬유, 펄프 또는 스폰지의 수지 표면에 도포하여 여과포를 만드는데는 바인더를 사용하여 접착이 용이하게 할 수 있으나, 바인더를 사용하지 않더라도 담체 자체의 팽윤성을 이용하여 180℃의 열에 3분간 가열하여 평활 고착시키면 접착이 가능하다.The carrier may be easily adhered using a binder to apply the carrier to the resin surface of the fiber, pulp, or sponge to make a filter cloth. However, even when the binder is not used, the carrier is heated for 3 minutes in a heat of 180 ° C. by using the carrier itself. Smooth fixing allows adhesion.

상기 바인더로는 초산 비닐 용액, 우레탄 바인더 또는 섬유, 펄프 등에 사용하는 접착제 중에서 선택하여 담체 100 중량부에 대해 1~5 중량부의 범위로 사용할 수 있다.The binder may be used in an amount of 1 to 5 parts by weight based on 100 parts by weight of a carrier by selecting from an adhesive used for a vinyl acetate solution, a urethane binder or a fiber, pulp, or the like.

실시예 3: 흡착포에 방향성 천연 추출물의 흡착Example 3: Adsorption of Aromatic Natural Extract on Adsorption Cloth

상기 실시예 2에서 제조된 흡착포에 바질, 버가못, 로즈마리, 페퍼민트, 클라리세이지, 라벤더 추출물을 담체 100 중량부에 대해 약 20 중량부 범위로 하나 또는 둘 이상을 혼합하여 흡착하였다.Basil, bergamot, rosemary, peppermint, clary sage, and lavender extract were adsorbed onto the adsorbent fabric prepared in Example 2 in a range of about 20 parts by weight based on 100 parts by weight of the carrier.

상기 흡착은 저압탱크에 상기 바질, 버가못, 로즈마리, 페퍼민트, 클라리세이지, 라벤더 추출물을 투여하여 충분히 혼합한 후 비이온이나 음이온상태로 pH를 조정한 후, 3% 미만의 계면활성제를 소량 투여한 다음, 30~50 ℃에서 흡착포를 투여하고, 3~6 시간 후 내용물을 꺼낸 후 건조하여 완성시켰다.The adsorption is a mixture of basil, bergamot, rosemary, peppermint, clary sage, lavender extract in a low pressure tank and then sufficiently mixed and then adjusted the pH to a nonionic or anionic state, and then a small amount of less than 3% of the surfactant Adsorption cloths were administered at 30 to 50 ° C., the contents were taken out after 3 to 6 hours, and then dried to complete.

본 발명에 이용된, 바질, 버가못, 로즈마리, 페퍼민트, 클라리세이지, 라벤더 추출물 추출물은 대부분 프랑스, 동남아 등에서 재배되는 특정식물의 추출액을수입하여 사용하였으며, 국내에서 자생되는 소량의 식물 추출액은 수증기증류법(Steam Distillation)을 이용하여 간단하게 추출하여 사용할 수도 있다.Basil, bergamot, rosemary, peppermint, clary sage, lavender extract extract used in the present invention was mostly used by importing the extract of a specific plant cultivated in France, Southeast Asia, etc. Steam Distillation) can be used for simple extraction.

수증기 증류법에 의하면, 식물의 뿌리나 잎을 자르거나 으깨어서 추출이 잘되도록 선행 가공한 후, 가열 용기에서 수증기로 가열하면, 식물의 세포벽이 깨지며 추출액이 수증기와 함께 증발하는데 증발되는 추출액을 냉각·회수하여 액체 추출액을 수득할 수 있다.According to the steam distillation method, the roots or leaves of the plant are cut or crushed and preprocessed to extract well, and then heated with steam in a heating vessel, the cell wall of the plant is broken and the extract is evaporated as the extract evaporates with water vapor. Recovery to obtain a liquid extract.

최종적으로 방향성 천연 추출물이 흡착된 흡착포를 탈수·건조시켜 착용밴드를 제작하였다.Finally, a band was prepared by dehydrating and drying the adsorption cloth in which the aromatic natural extract was adsorbed.

제작된 나노사이즈 담체에 방향성 천연 추출물이 흡착된 흡착포는 도 1에 나타낸 바와 같다. 도 1a는 나노사이즈의 담체를 균등하게 고착하여 만든 흡착포를 나타낸 것이고, 도 1b는 흡착포 내의 나노사이즈 담체의 모양을 확대하여 나타낸 것이며, 도 1c는 나노사이즈의 담체에 방향성 천연 추출물이 흡착된 모양을 나타낸 것이다.The adsorption cloth in which the aromatic natural extract is adsorbed on the prepared nano-sized carrier is shown in FIG. 1. Figure 1a shows the adsorption cloth made by uniformly fixing the nano-sized carrier, Figure 1b is an enlarged view of the shape of the nano-sized carrier in the adsorption cloth, Figure 1c is a shape in which the aromatic natural extract is adsorbed on the nano-sized carrier It is shown.

본 발명에 따라 제조되는 착용밴드는 상기 흡착포를 부착한 수지에 벨크로 테이프(velcro tape)를 부착하여 손목이나 발목에 착용하기에 적합하도록 할 수 있다.The wearing band manufactured according to the present invention can be made to be suitable for wearing on the wrist or ankle by attaching a velcro tape to the resin to which the adsorption cloth is attached.

본 발명의 실시예에 따라 제작한 착용밴드는 방향성 천연 추출물이 나노사이즈 담체에 흡착되어 있어 향의 지속시간이 길고, 공기와의 접촉면적이 커서 학습이나 두뇌 활동시 착용하면 집중력과 기억력의 향상의 효과를 극대화 할 수 있다.The wear band produced according to the embodiment of the present invention has a long duration of fragrance because the aromatic natural extract is adsorbed on the nano-sized carrier, and has a large contact area with air, so that it can improve concentration and memory when worn during learning or brain activity. The effect can be maximized.

본 발명의 착용밴드는 방향성 천연 추출물의 향이 나노사이즈 담체에 흡착된 것을 사용하여 향의 지속시간이 길고, 공기와의 접촉면적이 커서 학습이나 두뇌 활동시 착용하면 집중력과 기억력의 향상의 효과를 극대화 할 수 있으므로 학습이나 두뇌 활동시 착용하여 집중력과 기억력 향상을 도모할 수 있다. 또한, 착용밴드로 구성되므로 이동성이 좋고 사용이 간편한 장점을 가진다.The wear band of the present invention uses the scent of the aromatic natural extract adsorbed on the nano-sized carrier, and the scent duration is long, and the contact area with air is large, and when worn during learning or brain activity, the effect of improving concentration and memory is maximized. Because it can be worn during learning or brain activity, it can improve concentration and memory. In addition, since the wear band has a good portability and easy to use.

본 발명의 단순한 변형 내지 변경은 이 분야의 통상의 지식을 가진 자에 의하여 용이하게 이용될 수 있으며, 이러한 변형이나 변경은 모두 본 발명의 영역에 포함되는 것으로 볼 수 있다.Simple modifications and variations of the present invention can be readily used by those skilled in the art, and all such variations or modifications can be considered to be included within the scope of the present invention.

Claims

Method of manufacturing a wearing band comprising the following steps:

(a) milling one or more mixtures selected from the group consisting of zeolite, CMC and bentonite to make a nano-sized carrier;

(b) adding the carrier and then forming and molding the fiber, pulp or porous plastic to form an adsorbent cloth to which the carrier is fixed;

(c) adsorbing at least one aromatic natural extract selected from the group consisting of basil, bergamot, rosemary, peppermint, clary sage and lavender extract to a carrier fixed to the adsorption cloth; And

(d) dehydrating and drying the adsorption cloth to which the aromatic natural extract is adsorbed.

The method of claim 1, wherein the use amount of the resin is 2 to 50 parts by weight based on 100 parts by weight of the carrier.

The method of claim 1, wherein the aromatic natural extract is added in an amount of 5 to 50 parts by weight based on 100 parts by weight of the carrier.

Method of manufacturing a wearing band comprising the following steps:

(b) applying the carrier to a molded resin product by mixing one or two or more selected from the group consisting of fibers, pulp and porous plastics;

(c) heating the resin to which the carrier is applied to produce an adsorbent cloth in which the carrier is swelled and fixed;

(d) adsorbing at least one aromatic natural extract selected from the group consisting of basil, bergamot, rosemary, peppermint, clary sage and lavender extract to a carrier fixed to the adsorption cloth; And

(e) dehydrating and drying the adsorption cloth to which the aromatic natural extract is adsorbed.

The method according to claim 4, wherein the amount of the resin used is 2 to 50 parts by weight based on 100 parts by weight of the carrier.

The method of claim 4, wherein the aromatic natural extract is added in an amount of 5 to 50 parts by weight based on 100 parts by weight of the carrier.

A wearing band manufactured by the method of any one of claims 1 to 6.