KR100346801B1 - A antibiotic skilled have a socks - Google Patents

Abstract

The present invention provides a method of manufacturing a sock and a sock bottom having an antibacterial function to remove the odor generated from foot and shoes and smooth blood circulation by far-infrared radiation and magnetic force along with the acupressure effect. It relates to a molded protrusion structure of.

A first step of dipping the sock of the part to be processed into a solution concentrated to the extent that the active ingredient is extracted by absorbing the active ingredient from a general basic herbal medicine and then drying;

The second step of separately mixing the medicinal herbs in a powdered state by concentrating the medicinal herbs in a powder form, mixed with 5% concentrated powder, 15% by weight of the coating agent, and 80% by weight of the solvent, and then coating and drying the dried sock. ;

A third step of mixing the sintered sock with a 25% by weight of the far-infrared radiator in the fine powder form and a 25% in the weight ratio of the magnetic powder in the fine powder form, and then printing the composition in a thickness of 1 mm and then adhering by heat;

The socks were mixed with 15% by weight of fine powdered silver, 10% by weight of fine powdered copper, 10% by weight of fine powdered zinc, 30% by weight of adhesive, 35% by solvent, and then formed by ganbanite, iron oxide and synthetic resin adhesive. It is produced by the fourth process of coating and drying in a gaseous phase.

During the process, the concentrated extract is extracted from the herbal medicine and immersed in the socks and dried, so that the herbal extract penetrates and concentrates the extract in the dried fiber (3), and the powdered herbal granules and the adhesive are mixed thinly in the socks. The sock formed by coating to form a coating layer (4):

Wherein the socks are not in direct contact with the skin, the far-infrared radiation material and the magnetic material are mixed with the adhesive to form the acupressure protrusions 2 with the magnetic composition 5, and the odor removal, sterilization, and antibacterial properties are made at the direct contact with the skin. Since the antimicrobial composition 6 mixed with a metal material having a function is covered with the adhesive, the composition is characterized in that the composition is formed to form a plurality of acupressure protrusions 2 at equal intervals.

As described above, the present invention forms a protrusion-like composition on the sole of the sole in contact with the sole of the foot, thereby effectively maintaining far-infrared radiation and coercive force to promote blood circulation, and antibacterial metal ion of a material having sterilization, antibacterial and odor removal functions is bacteria. It is effective in providing socks and antimicrobial function so that the sterilization and odor removal can be made in direct contact with the gas generating the bad smell and its odor, and also the herbal pressure is evenly distributed to the pressure of the molded protrusion Since the components of the Chinese medicine are continuously discharged along with the irritation of the skin, it is effective to increase the healing power of various diseases.

Description

Socks with antibacterial function and preparation method thereof

The present invention provides a method of manufacturing a sock and a sock bottom having an antibacterial function to remove the odor generated from foot and shoes and smooth blood circulation by far-infrared radiation and magnetic force along with the acupressure effect. It is about the structure.

In general, socks are worn on the feet to absorb sweat. Shoes are worn with sneakers or shoes with socks on, so the air is not flowing smoothly. In addition to the ammonia odor of many bacteria, including athlete's foot, and inhabitants, especially during the summer season is suffering from bad smell and athlete's foot.

To solve these problems, numerous meridians located on the soles of the feet are made of adhesives, such as PVC, on mixtures containing copper powder for deodorizing socks and iron oxide mixtures to help blood circulation. By applying acupressure to the hypertension, a number of protrusions are formed to provide acupressure effect that helps smooth blood circulation and fatigue recovery.

Based on the Meridian theory of traditional oriental medicine, this therapy can cure these patients by magnetically energizing magnetic fields in the acupuncture points of the hands or toes. The skin's response point (acupuncture points) is associated with internal organs of the body, respectively.

In other words, as a technique based on the above elements, conventionally used as a socks for forming a number of protrusions on the bottom of the socks for acupressure, including Japanese Patent Application Laid-Open No. 49-94895 and Korean Patent Publication No. 89-1258 Patent Publication No. 89-5198 discloses a health sock containing sodium hypochlorite, magnetized powder, and copper powder in the protrusions to sterilize, promote blood flow, and neutralize odors.

On the basis of the above-mentioned technology, patent publication No. 89-5198 was recently developed to improve the "manufacturing method of socks for health and the patent publication No. 92-9406 published by the socks bottom mixed layer structure" and "skin irritation". Patent Publication No. 94-8968 "published as a medicinal herb and a magnet-containing substance is used in a state in which a protrusion is formed on the bottom of a sock.

Patent Publication No. 92-9406 discloses sterilization and blood flow by mixing and adding ceramic powder, calcium hydroxide, calcium carbonate, copper phosphate and trace amounts of nonyl nilamide, menthol, and zinc oxide in a mixture that penetrates the bottom of a sock. It contains rubber to reinforce cohesion and odor neutralization, and iron oxide to have magnetic force. It does not protrude into the inner and outer surfaces of the socks but penetrates between tissues. It is configured to be neutralized.

In the present invention, a small amount of ceramic powder to promote blood flow by far-infrared rays and iron oxide to have magnetic properties such as calcium hydroxide, calcium carbonate, copper phosphate to remove odor and sterilization, and a synthetic resin and rubber for adhesion to socks bottom Although it is used by bonding, the concentration of the composition is so thin that it is very difficult to achieve the desired effect.

That is, far infrared rays or magnetic force can penetrate obstacles, but when the material and bacteria are not in direct contact with each other in neutralization or extinction of sterilization and odor, sterilization and odor cannot be prevented. In addition to the weak effect of the material to prevent the occurrence of a thinner concentration is a problem that can not substantially prevent the generation of sterilization and odor.

In addition, in the case of Patent Publication No. 94-8968 published as a skin stimulant herb and a magnet-containing substance, it is mainly used in socks as described above than a general woven fabric or a feeder. Chinese medicine and magnet powder can be solidified with a binder.

In the present invention, by preparing a solid composition to exert the magnetic force and the medicinal effect of the composition and stimulating the skin and muscles of the human body with this composition as a solid composition for promoting the treatment and health of the disease and the magnetic powder and the herbal medicine for the treatment or health promotion of the human body and It is composed of ceramic, copper powder and molding binder and manufactured by injecting magnetic force from the outside.

This technique is also the same as above, 5-15% of ceramic powder to promote blood flow by far infrared rays, and Angelica, Cheongung, Cheonghyang, Hallucinogen, Dragon, Dynasty, Peppermint, Yu Geun-pi, Marine Leaf, White Paper, Cinnamon With the mixing ratio of 10-20% of Chinese medicine, silica, sessin, ginseng, etc., 5-15% of fine copper powder for sterilization and odor removal, 20-60% of magnetic powder, and 50-60% molding binder with adhesive It is mixed with the composition consisting of a sock to the bottom of the composition is used, but it is also very difficult to achieve the desired effect because the concentration of the composition is too thin.

In other words, in the case of ceramics, the emission rate of far-infrared rays is not very high in small amounts, and even mixed herbs are used as raw materials in the state of being molded in adhesive, so it is difficult to expect the effect to heal the disease by the minute amount coming into contact with the human body. In addition, the same can also prevent the sterilization of the antimicrobial material and the generation of odor if the microbial material and bacteria are not in direct contact with the above problems in the neutralization or extinction of the sterilization and odor.

Therefore, the concentration of the material that prevents the sterilization action and the occurrence of odor in the composition can not substantially prevent the sterilization and odor generation, there is a problem that the treatment of diseases caused by Chinese medicine is also insufficient.

In view of the above problems, the present invention more effectively maintains far-infrared radiation and coercive force to promote blood circulation, and antimicrobial metals having sterilization, antibacterial and odor removal functions are ionized to make contact with gas generating bacteria and odors. It is an object of the present invention to provide a sock having an antibacterial function and a method for producing the same, which effectively sterilize and remove odor.

Another object of the present invention is to distribute the concentrated herbal medicine evenly and to continuously discharge the components of the Chinese medicine with the irritation of the skin, as the medicinal effect of the herbal medicine, to increase the healing power of various diseases.

1 is a cross-sectional view showing a state of acupressure protrusions and the fiber portion according to the present invention.

* Description of the symbols for the main parts of the drawings *

1: socks 2: acupressure protrusions 3: fiber

4: coating layer 5: magnetic composition 6: antimicrobial composition

In a sock and a method of manufacturing the composition comprising a mixture of ceramic, copper, zinc, iron oxide and herbal medicines with an adhesive material to form a plurality of magnetic projections to provide acupressure on the bottom of the sock,

A first step of dipping the sock of the part to be processed into a solution concentrated to the extent that the active ingredient is extracted by absorbing the active ingredient from a general basic herbal medicine and then drying;

The second step of separately sintering the medicinal herbs in a powdered state by mixing the concentrated herbal powder 5%, 15% by weight and 15% solvent weight by weight of the powdered powder and then sintered by coating the dried socks. ;

A third step of mixing the sintered sock with a 25% by weight of the far-infrared radiator in the fine powder form and a 25% in the weight ratio of the magnetic powder in the fine powder form, and then printing the composition in a thickness of 1 mm and then adhering by heat;

The socks were mixed with 15% by weight of fine powdered silver, 10% by weight of fine powdered copper, 10% by weight of fine powdered zinc, 30% by weight of adhesive, 35% by solvent, and then formed by ganbanite, iron oxide and synthetic resin adhesive. It is produced by the fourth process of coating and drying in a gaseous phase.

During the process, the concentrated extract is extracted from the herbal medicine and immersed in the socks and dried, so that the herbal extract penetrates and concentrates the extract in the dried fiber (3), and the powdered herbal granules and the adhesive are mixed thinly in the socks. The socks with the coating layer 4 formed by coating:

Wherein the socks are not in direct contact with the skin, the far-infrared radiation material and the magnetic material are mixed with the adhesive to form the acupressure protrusions 2 with the magnetic composition 5, and the odor removal, sterilization, and antibacterial properties are made at the direct contact with the skin. Since the antimicrobial composition 6 mixed with a metal material having a function is covered with the adhesive, the composition is characterized in that the composition is formed to form a plurality of acupressure protrusions 2 at equal intervals.

When described in detail with reference to the accompanying drawings, preferred embodiments of the present invention configured as described above are as follows.

First, by manufacturing process, the first step is a general basic herbal medicines such as Angelica, cheonggung, peppermint, white paper, cinnamon, sessin, ginseng, etc. are added or subtracted or added to ethanol according to the prescription or put in water. Chinese medicine is inherently concentrated in fiber 3 because it boils and extracts the active ingredient, and soaks the part of the processed part in a concentrated solution so that it is absorbed well and then dries.

Since the part to be processed is immersed in the concentrated solution of the Chinese medicine so as to penetrate the fiber (3) of the socks, the drying of the composition of the Chinese medicine is uniformly infiltrated between the fibers (3) of the socks, wherein the concentrated solution When soaked by heating to 40 degrees Celsius to 100 degrees Celsius at a temperature such that the socks are not deformed, the solution can be infiltrated into the fibers 3 of the woven socks with high concentration.

In the second step, the herbal medicines are separately extracted as described above, concentrated to a particle state, and the concentrated powder of the herbal medicines pulverized to 500 or more meshes is diluted in a weight ratio of 5%, 15% by weight of the coating agent, and 80% by weight of the solvent, and then dried. The socks are coated and sintered to form a coating layer 4.

The coating layer 4 is treated with a thin mixture of adhesive and concentrated powder on the herbal treatment part of the sock to maintain the long-term efficacy even after storage and laundry wearing in the state containing the herbal medicine, so that the concentration of the herbal medicine after the solvent evaporates 5% by weight of the powder and 15% by weight of the coating agent, when the solvent is volatilized, the herbal medicine is 25% by weight and the coating agent is 75% by weight, the coating process is carried out in a very thin state. In addition, there are various other types, so detailed description thereof will be omitted.

A passage is formed through the powder of concentrated herbal medicine in the coating layer 4 without impairing the flexibility and breathable absorbency of the fiber, so that absorption and drainage are achieved. Through the hole where the powder is located, it is continuously released until the end of the socks life.

In the third step, the sintered sintered granite powder is fired at 1,200 ° C. with far-infrared radiator, and then pulverized into fine particles. The particle size is preferably 500 mesh or more. Weight ratio 25% Synthetic resin The adhesive composition is mixed with a weight ratio of about 50%, and the magnetic composition 5 is printed by a thickness of about 0.3-3 mm and a width of about 3-10 mm by a method of printing or silk printing, and then bonded by heat.

As is well known, there are many kinds of far-infrared emitters including natural jade, zeolite, etc. Among them, elvan emits far-infrared wavelength which is most beneficial to human body in fine powder particles than gemstone, and absorbs this into human body, which leads to excellent heat (Increase the body temperature 1.2 ~ 1.5 ℃) and tissue activation energy to expand the microvascular vessels and gain very beneficial effects such as blood circulation promotion and metabolism adjustment.

Here, the adhesive is a general publicly known technology, and there are technologies for bonding it with various adhesives. Therefore, the detailed description is omitted and the elvan has high far-infrared emissivity, high permeability, and is semi-permanent. It protects from harmful electromagnetic waves and deodorizes. Far-infrared rays transmit direct and instantaneous radiant energy without intermediate media.

Since the frequency of the far-infrared wavelength is almost the same as the frequency of human molecules, when it penetrates the human body, resonance occurs in the molecule, causing the vibration to become active, and most of those vibrations turn into heat, and some energy acts as "activation energy." .

In addition, it has a cardiac calendar, deeply affecting the subcutaneous effect to activate the body's action to increase the temperature of the subcutaneous layer, the expansion of microvascular vessels, the promotion of blood circulation, the excretion of waste products in the body, the promotion of metabolism, the increase of body tissues It is well known to have medical effects such as abnormal excitatory suppression of perceptual nerve and autonomic nervous system function.

On the effect of magnetic force on the human body, this therapy based on the theory of Meridian in traditional Oriental medicine has a lot of acupuncture points on the sole of the foot. By activating the human body by circulation, it is possible to maintain a healthy state without side effects. It activates enzymes, and when a magnetic field of 1300OG is applied, the activity of trypsin, a digestive enzyme, is stimulated, and when the magnetic field of 400OG is applied, information of brain nerve cells is transmitted. It is known that an enzyme called acetylclean eserase, which is closely related to, is activated.

Therefore, if one counts too much, the metabolic order is disturbed, which is harmful to the human body and harmless and useful. Too strong a self-disruption of the metabolic order in the human body, but a proper self-metabolizing rather than a smooth metabolism will work to heal the disease.

In addition, there are two types of magnetism, yin and yang. In general, phonograms have a calming effect and induce the body's functions comfortably to normalize metabolism, while quantum groups act to induce stress. Prolonged exposure is known to interfere with metabolism, acidify surrounding tissues and activate dormant bacteria, causing various diseases.

In the magnetization input to form magnetic anisotropy, if the magnetization process is applied with a strong DC electrode to the magnetizer, the magnetic poles are oriented in a predetermined direction depending on the position of the electrode. It is desirable to enter the magnetic force to be located on the plane.

Magnetization of the magnetic material from the magnetizer. When the magnetic material is used, the iron oxide content and volume are slightly different. However, when the magnetic force of about 5.000 gauss is input at 25% of iron oxide content, 5 mm in diameter, and 1.5 mm in height, The magnetic force present was about 300 gauss magnetic force.

In the case of iron oxide as described above, it is acceptable to use it generally because of its weak magnetic force, but when it is stronger for therapeutic use, cerium ce, samarium Sm and cobalt co compounds (rare earth elements), which are strong magnetic force, are well known. Ce Co 6 Sm Co 6 Sm 2 Co 12), the yttrium cobalt compound YCo 6, or neodymium, and the like can be used, and can be used to maintain a strong magnetic force for treatment because it can take several tens of magnetic forces.

In the fourth step, 15% by weight of silver powder of fine powder, antibacterial and sterilizing metal, 10% by weight of fine powder copper and 10% by weight of zinc powder for fine odor removal are mixed with 30% solvent by weight of 35% solvent, It is applied to the protrusions 2 formed by the iron oxide and the synthetic resin adhesive and dried to form an antimicrobial composition 6 layer.

The sweat, which occurs mainly on the feet, contains relatively high amounts of organic matter such as lipids and proteins, and the fresh secreted sweat has no odor.However, the organic matter is transferred to the normal bacterial layer of the skin while moving to the skin surface. Decomposes and turns into an unpleasant smell.

In other words, the odor generated from the foot is mainly caused by this smell, and sweat secretion products are poorly ventilated by lower fatty acids such as capric acid, caproic acid, isovaleric acid and butyric acid, and mercaptan, amine, and ammonia. If not, it is degraded by the normal bacterial layer of the skin, producing a significant odor.

Therefore, in case of silver, germ is not generated by strong sterilization effect, and copper and zinc act as odor and chemical reaction to remove odor along with antibacterial function. The diffusion of ions (Ag +, Zn2 +, Cu2 +) reaches the cell membrane and is adsorbed by proteins such as the cell membrane and destroys the cell structure.

At this time, the odor and bacteria generated by the antimicrobial metal ions adsorbed to proteins such as cell membranes and enzymes binds to the -SH group of the amino acid Cystein, inhibits energy metabolism of the cell and is converted into harmless sulfides.

That is, the antimicrobial composition 6 volatilizes 35% of the solvent in a state in which 15% of silver, which is an antibacterial metal, and 10% of copper, 10% of zinc, and 35% of solvent, 35% of solvent, are mixed for the purpose of antibacterial and odor removal. Afterwards, silver is increased to about 23% by weight, 15% by weight of copper, and 15% by weight of zinc to 46% by weight of the adhesive, thereby increasing the density of the antimicrobial metal and exhibiting strong antimicrobial activity.

In the fifth step, as usual, the dried socks are passed through the magnetizer to magnetize the iron oxide, as described in the third step.

Therefore, the use range of each composition is combined according to the following ratio depending on the constitution and conditions as follows.

As an example, in the second step (weight ratio)

Chinese Herb Concentrated Fine Powder 5-40%

Adhesive 10-80%

Solvent 30-85%

As an example, in the third step (weight ratio)

Far Infrared Emitter Powder 20-40%

Ferrite 20-40%

Adhesive 40-60%

As an example, in the fourth step (weight ratio)

Silver powder 10-40%

Copper powder 5-25%

Zinc powder 5-25%

Adhesive 30-80%

Solvent 20-50%

The composition as described above forms acupressure protrusions (2) with a composition including an adhesive on the socks to activate the body angle tube connected to the foot and meridians by the magnetic force and far-infrared radiation and acupressure on the acupressure protrusions (2) to promote blood circulation, etc. The effect of and to prevent the occurrence of bacteria and odors using antibacterial metal is already well known.

In the present invention, as a characteristic element, the coating layer (4) made by mixing the concentrated herbal powder into the fiber (3) containing the concentrated herbal medicine to continuously release the components of the herbal medicine from the socks (1) to increase the therapeutic effect The magnetic composition (5) forming a high permeability and far-infrared rays and magnetic force is formed in the interior of the acupressure protrusions (2), the plurality of which are formed at equal intervals and the antimicrobial composition (6) containing the antibacterial metal is the acupressure protrusions (2). By increasing the density to be located on the outside of each of the materials contained in the composition is to work efficiently.

As described above, the present invention forms a protrusion-like composition on the sole of the sole in contact with the sole of the foot, thereby effectively maintaining far-infrared radiation and coercive force to promote blood circulation, and antibacterial metal ion of a material having sterilization, antibacterial and odor removal functions is bacteria. Direct contact with gas and odor-producing gas has an effect of providing socks and antimicrobial functions that effectively sterilize and remove odors and the method of manufacturing the same. Since the components of the Chinese medicine are continuously discharged along with the irritation of the skin, the medicine has the effect of increasing the healing power of various diseases.

Claims (2)

In the socks and the method of manufacturing the composition consisting of a mixture of ceramic, copper, zinc and iron oxide and herbal medicines with an adhesive to form a plurality of magnetic projections to provide acupressure on the bottom of the socks, A first step of dipping the sock of the part to be processed into a solution concentrated to the extent that the active ingredient is extracted by absorbing the active ingredient from a general basic herbal medicine and then drying; As described above, the second step of sintering by separately mixing the medicinal herb to a particle state of 5% concentrated powder, 15% by weight of the coating agent and 80% by weight of the solvent, and then coating the dried sock in a sintered state. ; A third step of mixing the sintered sock with a 25% by weight of the far-infrared radiator in the fine powder form and a 25% in the weight ratio of the magnetic powder in the fine powder form, and then printing the composition in a thickness of 1 mm and then adhering by heat; The socks were mixed with 15% by weight of fine powdered silver, 10% by weight of fine powdered copper, 10% by weight of fine powdered zinc, 30% by weight of adhesive, and 35% by solvent, and then acupressure formed by elvan, iron oxide and synthetic resin adhesive. A sock having a antimicrobial function and a method for producing the same, which are produced by a fourth step of applying and drying on a protrusion. The method of claim 1, During the process, the concentrated extract is extracted from the herbal medicine and immersed in the socks and dried, so that the herbal extract penetrates and concentrates the extract in the dried fiber (3), and the powdered herbal granules and the adhesive are mixed thinly in the socks. The sock formed by coating to form a coating layer (4): Wherein the socks are not in direct contact with the skin, the far-infrared radiation material and the magnetic material are mixed with the adhesive to form the acupressure protrusions 2 with the magnetic composition 5, and the odor removal, sterilization, and antibacterial properties are made at the direct contact with the skin. Socks with a antimicrobial function and a method for manufacturing the same, characterized in that the composition is formed so as to form a plurality of acupressure protrusions (2) at equal intervals so as to cover the antimicrobial composition (6) mixed with a metal material having a function.