KR100401929B1 - Swimming cap, fabric and method for making the same - Google Patents
Swimming cap, fabric and method for making the same Download PDFInfo
- Publication number
- KR100401929B1 KR100401929B1 KR10-2001-0064834A KR20010064834A KR100401929B1 KR 100401929 B1 KR100401929 B1 KR 100401929B1 KR 20010064834 A KR20010064834 A KR 20010064834A KR 100401929 B1 KR100401929 B1 KR 100401929B1
- Authority
- KR
- South Korea
- Prior art keywords
- resin
- swimming cap
- sieve
- cap
- fabric
- Prior art date
Abstract
이 발명은 수영모용 원단, 이를 이용하여 제조한 수영모, 그 제조방법 및 모양 도안방법이다. 수영모 제조방법은 탄력성을 가지는 통상의 수영모를 준비하는 단계;와 수영모의 내면 일정한 곳에 체(sieve)를 위치시키는 단계;와 체 위에 고무 재질의 액상고분자수지를 부어 이 수지를 상기 체의 격자에 침투시키는 단계;와 침투된 수지를 경화시키는 단계를 포함한다.The present invention is a swimming cap fabric, a swimming cap manufactured using the same, a manufacturing method and a shape design method. The method of manufacturing a swimming cap includes the steps of preparing a conventional swimming cap having elasticity; and placing a sieve at a predetermined inner surface of the swimming cap; and pouring a rubber-based liquid polymer resin on the sieve to penetrate the resin into the lattice of the sieve. And curing the infiltrated resin.
본 발명에 의하면 수영모의 내면에 형성된 요철에 의해 수중에서 물이 수영모 속으로 일부 침투해도 수영모가 잘 벗겨지지 않으며, 요철에 의한 지압효과로 착용감이 우수하고, 내면에 형성된 독특한 모양으로 시각적인 흥미를 유발시킬 수 있는 효과가 있다.According to the present invention, even if water partially penetrates into the swimming cap under water due to the irregularities formed on the inner surface of the swimming cap, the swimming cap is not easily peeled off, and due to the acupressure effect by the unevenness, the wearing comfort is excellent, and the unique shape formed on the inner surface provides visual interest There is a detrimental effect.
Description
본 발명은 수영모용 원단, 이 원단을 이용하여 제조한 수영모와 그 제조방법 및 수영모에 모양을 도안화 하는 방법에 관한 것이다.The present invention relates to a fabric for a swimming cap, a swimming cap prepared using the fabric, and a method for designing the shape of the swimming cap.
일반적으로 운동복, 헬스복, 수영복, 에어로빅복, 땀복 등의 스포츠 또는 레저용으로 사용되는 직물지는 상시복에 비해 각각의 특성에 적합한 기능성을 가져야 한다.In general, the textile paper used for sports or leisure, such as sportswear, health clothing, swimwear, aerobics, sweat, etc. should have a function suitable for each characteristic compared to the regular clothes.
수영모는 부력이 작용하는 수중에서 착용하는 것이기 때문에 머리에 착용하였을 때 수영중에도 잘 벗겨지지 않도록 제작되어야 한다.Since swimming caps are worn in buoyant waters, they should be constructed so that they do not come off while swimming.
이에 수영모는 신축성이 뛰어난 원단, 예컨대 일반적으로 알려진 폴리에스테르, 나일론 같은 합성섬유나 원사(原絲) 제작시부터 신축성을 부여하도록 분자적으로 설계되어 시중에는 라이크라(미국 듀퐁사 등록상표)라고 명명되고 있는 스판덱스 섬유직물 또는 이들이 혼용된 직물 등을 이용하고 있다.The swimming cap is molecularly designed to give elasticity from the production of highly elastic fabrics, such as commonly known polyester and nylon, or yarn, and is commercially named Lycra (registered trademark of DuPont, USA). Spandex fibrous fabrics or woven fabrics thereof are used.
또한 수영모는 방수성이 클수록 좋은 평가를 받는바 수영모 또는 그 원단에 역시 분자내에 스프링 네트워크 구조(우레탄 결합)를 가지고 있어 고 탄력성인 우레탄수지를 코팅하기도 한다. 예컨대 대한민국 실용신안 등록번호 20-0158140호가 그것이다.In addition, swimming caps are highly rated as they are more waterproof. Swimming caps or their fabrics also have a spring network structure (urethane bond) in the molecule, which also coats highly elastic urethane resins. For example, Korean Utility Model Registration No. 20-0158140.
위 특허에는 스판과 나일론이 소정비율로 혼방된 원단을 형성하고, 상기 원단의 일표면에 폴리우레탄의 코팅층을 형성하여 이루어진 수영모용 원단을 개시하고 있으며, 방수성 및 신축성이 향상되고, 부드러우면서도 질긴 성질을 갖는 수영모용 직물지가 제공된다고 하고 있다.The patent discloses a fabric for swimming caps formed by forming a fabric in which a span and nylon are mixed at a predetermined ratio, and forming a coating layer of polyurethane on one surface of the fabric, which improves waterproofness and elasticity, and is soft and durable. It is said to provide textile paper for swimming caps with properties.
이러한 수영모의 착용성 및 방수성은 수영모의 절개부 둘레에 고탄력성의 밴드대(帶)를 형성하는 것에 의해 보조되어지기도 한다.The wearability and waterproofness of the swim cap may be assisted by forming a high elastic band band around the incision of the swim cap.
또한 수영모의 방수성은 수영모를 어떠한 방식으로 제조하느냐에 따라서도 그 성질의 정도에서 차이가 나는바, 재봉된 완제품상태의 수영모를 방수처리하는 방법이 대한민국 특허등록 특2000-0059623호에 개시되어 있다.In addition, the waterproofness of the swimming cap is different in the degree of its properties depending on how the swimming cap is manufactured, and a method of waterproofing the finished swimming cap in a sewing state is disclosed in Korean Patent Registration No. 2000-0059623.
위 특허는 재봉기로 재봉된 수영모를 방수 처리하는 방법으로서 접착제와 경화제를 함유하는 액상 실리콘을 준비한 다음 재봉된 수영모를 치구에 고정시킨 상태에서 도포기구를 이용하여 액상 실리콘을 수영모상에 적절한 두께로 도포하고 경화하여 완성하는 것을 특징으로 하는 수영모 제조방법이 개시되어 있다.The above patent is a method of waterproofing a swimming cap sewn with a sewing machine. After preparing liquid silicone containing an adhesive and a curing agent, the liquid silicone is applied to the swimming cap with an appropriate thickness by using an applicator while the sewing swimming cap is fixed to the jig. A method of producing a swimming cap is disclosed, which is cured and completed.
이 모두는 수영모가 갖추어야할 신축성 내지 탄력성을 위한 기술로서 한편으론 수영중에 잘 벗겨지지 않아야 할 뿐만이 아니라 장시간 착용하여도 무리가 없는, 착용성도 아울러 갖춘 수영모의 요구가 레저문화의 발달과 함께 요구되어 지고 있다.All of these are the elasticity and elasticity of swimming caps. On the other hand, the swimming cap not only needs to be peeled off during swimming, but also wearable for long periods of time. have.
한편, 수영모는 그 제품의 출처나 판매처 등을 소비자 들로 하여금 식별시키기 위해 상호 또는 상표나 일정한 로고, 도안 등이 인쇄 등의 방법으로 제공되어지고 있는데 최근에는 고급제품 일수록 상표 등의 인쇄나 인자(印字)의 형태 또한 중요한 품질평가수단 내지 당해 상표의 이미지 평가수단이 되어가고 있다.On the other hand, swimming caps are provided with a trade name or a trademark, a certain logo, a pattern, etc. in order to identify the source or the seller of the product by consumers. The form of the seal is also becoming an important quality evaluation means or an image evaluation means of the trademark.
본 발명은 수영모를 착용하였을 때 착용감이 우수하고 수영모를 착용한 상태에서 장기간 물속에서 수영을 할 경우에도 두부로부터 이탈되거나 벗겨지는 일이 없이 장시간의 착용이 가능한 수영모의 제작에 적합한 원단을 제공하는 것이다.The present invention is to provide a fabric suitable for the production of a swimming cap that can be worn for a long time without being detached or peeled from the head even when swimming in the water for a long time in the state wearing a swimming cap while wearing a swimming cap is excellent. .
또한 본 발명은 그러한 수영모 제조방법을 제공하는 것이다.The present invention also provides such a swimming cap manufacturing method.
더 나아가 본 발명은 수영모용 원단을 이용하여 제조한 독특한 수영모를 제공하는 것이다.Furthermore, the present invention is to provide a unique swimming cap manufactured using a fabric for swimming caps.
또한 본 발명은 수영모에 상표, 로고 등을 인자할 때 시각적인 흥미를 불러 일으킬 수 있도록 수영모에 모양을 도안화하는 방법을 제공하는 것이다.In another aspect, the present invention is to provide a method of designing the shape of the swimming cap so as to cause visual interest when printing the trademark, logo, and the like on the swimming cap.
본 발명의 다른 목적 내지 특징은 아래의 부분에서 추가적으로 설명된다.Other objects and features of the present invention are further described in the sections below.
도 1은 본 발명의 수영모가 수축된 상태에 있을 때의 도면1 is a view when the swimming cap of the present invention in the contracted state
도 2는 본 발명의 수영모가 이완된 상태에 있을 때의 도면2 is a view when the swimming cap of the present invention is in a relaxed state
도 3은 본 발명의 수영모의 내면에 엠보스가 형성된 예를 나타내는 도면3 is a view showing an example in which embossing is formed on the inner surface of the swimming cap of the present invention;
위와 같은 목적은 수영모에 고무재질의 수지물질을 마치 물방울형상으로 형성한다는 기본적인 사상의 착상으로 달성된다.The above object is achieved by the idea of a basic idea that a resin material of rubber material is formed in a water droplet shape on a swimming cap.
본 발명의 목적은 수영모용 원단에 고무재질의 액상수지를 도트인쇄(dot print)방식으로, 즉 엠보싱처리를 하는 것에 의해 달성된다.An object of the present invention is achieved by a dot print method, ie embossing, a rubber-based liquid resin on a swimming cap fabric.
본 발명자에 의해 최초로 착상되고 구체화된 본 발명의 제 1 관점은 일면에 요철이 형성된 수영모용 원단을 제공하는 것이다.The first aspect of the present invention first conceived and embodied by the present inventors is to provide a swimming cap fabric having irregularities formed on one surface thereof.
즉 본 발명의 수영모용 원단은 탄력성을 가지는 통상의 수영모용 원단으로서, 위 원단의 일면에는 고무재질의 액상고분자수지가 경화된 상태로 요철(엠보스 무늬)가 형성된 것을 특징으로 한다.That is, the swimming cap fabric of the present invention is a conventional swimming cap fabric having elasticity, characterized in that the irregularities (embossed pattern) is formed on one surface of the fabric in the state of the cured liquid polymer resin of the rubber material.
본 발명은 수영모의 제작에의 사용이 당연히 예정되는 수영모용 원단에 엠보스 무늬를 형성함으로써 이를 이용하여 수영모를 제작하여 종국적으로는 머리에 착용하였을 때 상쾌한 착용감을 주고 수중에서의 장시간 운동시 잘 벗겨지지 않도록 하기 위한 것이라는 기술적 사상에 그 특징이 있는 것이기 때문에 어느 특정한 수영모용 원단에 한정하지 않으나 통상적인 수영모가 가지고 있는 신축성(탄력성)은 있어야 한다.The present invention forms an embossed pattern on the fabric for swimming caps, which is of course intended for use in the production of swimming caps, thereby producing a swimming cap by using it and ultimately gives a refreshing feeling when worn on the head and peels off well during long time exercise in water. It is not limited to any particular swimming cap fabric, because it is characteristic of the technical idea that it is intended to prevent it, but it must have elasticity (elasticity) that a conventional swimming cap has.
바람직하게는 나일론 또는 스판덱스를 혼용한 것으로서 표면에는 우레탄코팅이 되어 있는 고탄력성을 가지는 원단이 좋다.Preferably, a mixture of nylon or spandex is used, and a fabric having high elasticity with urethane coating is preferable on the surface.
또한 원단에 형성되는 요철(엠보스무늬)은 그 크기나 형상에 제한이 있는 것은 아니나 물방울형상으로서 지름은 1mm ~ 2mm 의 것이 바람직하다. 요철의 크기가 1mm 보다 작을 경우에는 제조상 시간이 많이 소요되고 또 불규칙한 돗트인쇄가 될 수 있기 때문이며 요철의 크기가 2mm 보다 클 경우에는 수영모로 제작되어 착용되었을 때 반복사용으로 원단으로부터 떨어져 나가기 쉽기 때문이다.In addition, the unevenness (embossed pattern) formed in the fabric is not limited in size and shape, but as a water droplet shape, the diameter is preferably 1mm ~ 2mm. If the size of the unevenness is less than 1mm, it takes a lot of time in manufacturing and irregular dot printing. If the size of the unevenness is larger than 2mm, it is easy to fall off from the fabric by repeated use when it is made of swimming cap. .
또한 원단에 형성되는 요철(엠보스무늬)은 수영모가 머리에 착용되는 특성상 경화되었을 때도 연질의 물성을 나타내는 고무재질의 수지로 형성되는 것이 요망된다.In addition, the unevenness (embossed pattern) formed on the fabric is desired to be formed of a resin of rubber material exhibiting soft physical properties even when the swim cap is cured due to the characteristics that are worn on the head.
그러나 고무재질의 액상고분자수지이면 특별한 제한이 없다.However, there is no particular limitation as long as it is a liquid polymer resin of rubber material.
예를 들면 폴리비닐클로라이드 액상수지, 폴리비닐아세테이트 액상수지 또는 실리콘 액상수지일 수 있다. 이들 명칭이 비록 폴리비닐클로라이드 액상수지, 폴리비닐아세테이트 액상수지 또는 실리콘 액상수지라고 하더라도 이들 수지속에는 경화제, 희석제(점도조절제), 충진재, 내자외선제 및 안료 등 일반적으로 첨가될 수 있는 물질이 함유된다.For example, it may be a polyvinyl chloride liquid resin, polyvinylacetate liquid resin or silicone liquid resin. Although these names are polyvinyl chloride liquid resins, polyvinylacetate liquid resins or silicone liquid resins, these resins contain substances that can generally be added, such as hardeners, diluents (viscosity regulators), fillers, UV-resistant and pigments. .
제 2 관점에서 본 발명은 착용하였을 때 머리에 압박력을 가하기 위해 탄력성을 가지는 통상의 수영모로서, 상기 수영모의 내면에는 고무재질의 수지가 경화된 상태로 요철이 형성된 것을 특징으로 하는 수영모로서 표현될 수 있다.In a second aspect, the present invention is a conventional swimming cap having elasticity to apply a compressive force to the head when worn, the inner surface of the swimming cap can be represented as a swimming cap, characterized in that irregularities are formed in the state of the rubber resin cured. have.
역시 수지의 종류나 요철의 형상 크기는 특별히 제한되지 않는다.Again, the type of resin and the shape size of the unevenness are not particularly limited.
또한 요철이 형성되는 수영모의 부분은 내면 전체 또는 일부가 될 수가 있다. 그러나 요철은 머리의 측면부위(측두골부위)에 형성되는 것이 바람직하다.In addition, the part of the swimming cap in which the unevenness is formed may be the whole or part of the inner surface. However, the irregularities are preferably formed on the side of the head (temporal bone).
또한 요철은 수영모의 절개부의 밴드대와 평행하게 형성될 수도 있다.In addition, the unevenness may be formed in parallel with the band band of the incision of the swimming cap.
요철은 측두골부위에도 형성되고 수영모의 절개부의 밴드대(20)와 평행하게도 형성될 수 있음은 물론이다.Concavities and convexities are also formed in the temporal bone and may also be formed in parallel with the band band 20 of the incision of the swimming cap.
제 3 의 관점에서 본 발명은 수영모용 원단의 제조방법으로 표현된다.In a third aspect, the present invention is represented by a method for producing a swimming cap fabric.
본 발명의 제 3 의 관점에 따른 수영모용 원단의 제조방법은 탄력성을 가지는 통상의 수영모용 원단을 준비하는 단계;와 위 원단에 체(sieve)를 위치시키는 단계;와 상기 체 위에 고무 재질의 액상고분자수지를 부어 이 수지를 체의 격자에 침투시키는 단계;와 이 침투된 수지를 경화시키는 단계를 포함하는 방법으로 요약될 수 있다.Method for producing a swimming cap fabric according to a third aspect of the present invention comprises the steps of preparing a conventional swimming cap fabric having elasticity; and placing a sieve (sieve) on the fabric; and the liquid phase of the rubber material on the sieve Pouring the polymer resin to penetrate the resin into the lattice of the sieve; and curing the penetrated resin can be summarized.
위와 같은 방법을 통상 실크인쇄 혹은 돗트인쇄라고 부른다.This method is usually called silk printing or dot printing.
동일하게 위의 방법은 수영모를 제조하는데에 적용될 수 있다.Equally, the above method can be applied to manufacturing swimming caps.
즉, 본 발명은 탄력성을 가지는 통상의 수영모를 준비하는 단계;와 이 수영모의 내면 일정한 곳에 체(sieve)를 위치시키는 단계;와 상기 체 위에 고무 재질의 액상고분자수지를 부어 이 수지를 상기 체의 격자에 침투시키는 단계;와 상기 침투된 수지를 경화시키는 단계를 포함함을 특징으로 하는 수영모의 제조방법을 제공한다.That is, the present invention comprises the steps of preparing a conventional swimming cap having elasticity; and positioning a sieve (sieve) at a certain inner surface of the swimming cap; and poured a liquid polymer resin of rubber material on the sieve to the resin of the sieve It penetrates into the lattice; and provides a method of producing a swimming cap comprising the step of curing the permeated resin.
제 4 의 관점에서 본 발명은 수영모에 문자, 로고 등의 상표나 그 자체가 모양의 형성을 목적으로하는 각종의 무늬를 도안하는 방법을 제공한다.In a fourth aspect, the present invention provides a method of designing a variety of patterns for the purpose of forming a trademark such as letters, logos, or the like on a swimming cap.
본 발명은 탄력성을 가지는 통상의 수영모를 준비하는 단계;와 상기 수영모의 내면 소정의 위치, 즉 상표 등의 모양을 도안할 위치에 체를 위치시키는 단계;와 이 체 위에 소정의 문자 또는 도안이 음각으로 오려진 쉬트지(종이, 비닐 등)를 덮는 단계;와 쉬트의 오려진 부분에 고무 재질의 액상고분자수지를 부어 이 수지를 상기 체의 격자에 침투시키는 단계;와 이 침투된 수지를 경화시키는 단계를 포함함을 특징으로 하는 수영모에 모양을 형성하는 방법을 제공하는 것이다.The present invention comprises the steps of preparing a conventional swimming cap having elasticity; and placing a sieve at a predetermined position on the inner surface of the swimming cap, that is, a position to design the shape of a trademark, etc .; and a predetermined letter or pattern on the sieve is intaglio Covering the cut sheets (paper, vinyl, etc.) with; and pouring a liquid polymer resin made of rubber material into the cut portions of the sheet to penetrate the resin into the lattice of the sieve; and to cure the penetrated resin. It is to provide a method for forming a shape on the swimming cap, characterized in that it comprises a step.
이와 같은 방법으로 탄력성이 있는 수영모의 내면에 일정한 모양의 무늬를 형성하면 착용감, 방수성 향상, 지압효과 등의 기능상의 이점 뿐만이 아니라 수영모를 보는 사람으로 하여금 시각적인 호기심을 유발시킬 수 있어 수영모에 부착된 상표 등의 이미지에 양질의 호감을 갖게 할 수도 있다.Forming a pattern on the inner surface of the elastic swimming cap in this way will not only provide functional benefits such as improved fit, waterproofness, and acupressure effect, but can also cause visual curiosity for the viewer of the swimming cap. It can also give a good impression to images such as trademarks.
즉, 평상시의 수영모(도 1의 1)는 수축되어 있어 내면에 형성된 엠보스무늬(10)에 의해 표현된 문자(7), 로고 등의 표장(mark)이 희미하게 보이다가(도 1 참조) 머리에 착용하고 있을 때에는(도 2) 수영모(1)가 이완되고 머리의 표면과 접촉하여 엠보스무늬가 수영모의 외면으로 도들도들하게 보이게 되므로 보이지 않았던 상표가 사용시에 나타나는 시각적인 흥미감이 유발되는 것이다.That is, the usual swim cap (1 in FIG. 1) is shrunk so that marks such as letters 7 and logos represented by the embossed pattern 10 formed on the inner surface are faintly visible (see FIG. 1). When worn on the head (FIG. 2), the swim cap 1 relaxes and contacts the surface of the head, causing the embossed pattern to appear jagged to the outside of the swim cap, causing visual interest when the invisible trademark appears upon use. Will be.
이러한 본 발명의 방법을 사용하여 수영모에 상표를 부착(표시, 사용)하는경우에는 당해 상표를 대하는 소비자의 심리에 고급스런 친밀감을 불러일으켜서 상표 및 제품의 이미지가 상승되는 효가가 있을 것이다.In the case of using (marking, using) a trademark on a swimming cap by using the method of the present invention, there will be an effect that the image of the trademark and the product is enhanced by inducing a high level of intimacy to the consumer's psychology of the trademark.
이상의 설명과 첨부된 도면에 의해 본 발명은 실시될 수 있음이 당업자에게 명백할 것이다. 따라서 이하에서 설명하는 구체예는 하나의 예시에 지나지 않는다.It will be apparent to those skilled in the art that the present invention may be practiced by the foregoing description and the accompanying drawings. Therefore, the specific example described below is only one illustration.
주식회사 풍원에서 판매하는 폴리비닐아세테이트 액상수지를 희석제로 점도조절하여 준비해 두고, 두께가 600 ~ 800㎛이고 격자간격이 20 ~ 30 메쉬(mesh, 격자수/inch)인 체(sieve)를 준비하여 이 체를 탄력성이 있는 수영모용 원단(나일론 20d 68%, 스판덱스 40d 32%의 혼사로 직조된 원단에 표면에 우레탄 코팅이 된 것)에 올려놓고 미리 준비한 폴리비닐아세테이트 액상수지를 격자에 잘 침투 되도록 골고루 부운 후 130 ~ 140 ℃의 분위기 하에 있는 콘베이어에서 2분간 체류하면서 건조(경화)시켜서 본 발명의 수영모를 제작하였다.Prepare polyvinylacetate liquid resin sold by Poongwon Co., Ltd. by adjusting viscosity with diluent, and prepare sieve with 600 ~ 800㎛ thickness and 20 ~ 30 mesh (mesh, lattice number / inch). The sieve is placed on an elastic swimming cap fabric (nylon 20d 68%, spandex 40d 32% blended with a urethane coating on the surface) and the polyvinylacetate liquid resin prepared in advance is evenly distributed to the grid. After the swelling, the swimming cap of the present invention was produced by drying (curing) while staying in a conveyor under an atmosphere of 130 to 140 ° C. for 2 minutes.
이상 설명한 본 발명에 의하면 수영모의 내면에 형성된 요철에 의해 수중에서 물이 수영모 속으로 일부 침투해도 수영모가 잘 벗겨지지 않으며,According to the present invention described above, even if the water partially penetrates into the swimming cap by the unevenness formed on the inner surface of the swimming cap, the swimming cap does not peel off well,
요철에 의한 지압효과로 착용감이 우수하고,Excellent fit by the acupressure effect by the unevenness,
내면에 형성된 독특한 모양으로 시각적인 흥미를 유발시킬 수 있는 효과가 있다.The unique shape formed on the inside has the effect of causing visual interest.
Claims (11)