KR100394466B1 - Waterproofing Composition Having Permeation Mechanism, Method for Producing the Same, and Hybrid Waterproofing Construction Method Using the Same - Google Patents
Waterproofing Composition Having Permeation Mechanism, Method for Producing the Same, and Hybrid Waterproofing Construction Method Using the Same Download PDFInfo
- Publication number
- KR100394466B1 KR100394466B1 KR10-2000-0087088A KR20000087088A KR100394466B1 KR 100394466 B1 KR100394466 B1 KR 100394466B1 KR 20000087088 A KR20000087088 A KR 20000087088A KR 100394466 B1 KR100394466 B1 KR 100394466B1
- Authority
- KR
- South Korea
- Prior art keywords
- water
- weight
- waterproofing
- liquid phase
- permeable
- Prior art date
Abstract
본 발명은 콘크리트 구조물의 표면에 침투성 물 흡수 방지제를 처리하여 콘크리트 구조물의 방수, 방식 특성을 부여함과 동시에, 침투 성능을 양생 후 육안 확인이 영구히 가능하여 현장 시공에 따른 침투성능에 대한 검증과 품질관리가 효율적으로 이루어질 수 있고 도포된 물 흡수 방지제의 상부에 시멘트계 도포형 방수재와 함께 적용함으로써 물 흡수 방지제의 단점을 멤브레인(membrane) 방수에 의해 구조체의 노화방지와 방수성능을 극대화시킬 수 있는 침투성 물 흡수 방지제 조성물 및 그의 제조방법과 이를 이용한 복합 방수시공방법에 관한 것이다.The present invention treats the surface of the concrete structure with a permeable water absorption preventing agent to impart the waterproof and anticorrosive properties of the concrete structure, and at the same time, it is possible to visually check the penetration performance after curing the permeation performance. Permeable water that can be managed efficiently and applied with cement-based waterproofing material on top of the applied water absorption inhibitor to maximize the anti-aging and waterproofing performance of the structure by waterproofing the membrane. It relates to an absorption inhibitor composition, a method for producing the same, and a composite waterproof construction method using the same.
상기 조성물은 옥틸트리에톡시실란/실록산 합성물 35-50중량%, 물 35-55중량%, 에멀션화제 0.1-1.0중량%, 보호콜로이드제 0.1-1.5중량%, 및 강도보호재로서 수용성 실리케이트 5-20중량%로 이루어지는 것을 특징으로 침투성 물 흡수 방지제 조성물.The composition comprises 35-50% by weight of octyltriethoxysilane / siloxane compound, 35-55% by weight of water, 0.1-1.0% by weight of emulsifier, 0.1-1.5% by weight of protective colloid, and water-soluble silicate 5-20 as strength protector. Permeable water absorption inhibitor composition, characterized in that the weight percent.
Description
본 발명은 침투성 물 흡수 방지제 조성물 및 그의 제조방법과 이를 이용한 복합 방수시공방법에 관한 것으로, 특히 콘크리트 구조물의 표면에 침투성 물 흡수 방지제를 처리하여 콘크리트 구조물의 방수, 방식 특성을 부여함과 동시에, 침투 성능을 양생 후 육안 확인이 영구히 가능하여 현장 시공에 따른 침투성능에 대한 검증과 품질관리가 효율적으로 이루어질 수 있고 도포된 물 흡수 방지제의 상부에 시멘트계 도포형 방수재와 함께 적용함으로써 물 흡수 방지제의 단점을 멤브레인(membrane) 방수에 의해 구조체의 노화방지와 방수성능을 극대화시킬 수 있는 침투성 물 흡수 방지제 조성물 및 그의 제조방법과 이를 이용한 복합 방수시공방법에 관한 것이다.The present invention relates to a permeable water absorption preventing agent composition, a method for manufacturing the same, and a composite waterproof construction method using the same, in particular, by impregnating the surface of the concrete structure with a water permeation preventing agent to impart waterproof and anticorrosive properties of the concrete structure, After curing the performance, it is possible to check visually permanently, so that the permeation performance and quality control can be efficiently carried out according to the construction of the site, and by applying the cement-based waterproofing material on top of the applied water absorption inhibitor, The present invention relates to a permeable water absorption preventing agent composition capable of maximizing anti-aging and waterproofing performance of a structure by waterproofing a membrane, a method for preparing the same, and a composite waterproof construction method using the same.
기존의 침투성 물 흡수 방지제(이하 "침투성 방수제"라함)는 단순히 물의 유입을 감소시키는 용액이나 용제에 녹인 현탁액을 의미하며 콘크리트에 존재하는 공극( pore )을 채워서 발수효과(撥水效果)와 차수효과(遮水效果)를 부여하는 재료들이다. 침투성 방수제는 유기화합물계와 무기화합물계로 크게 나누어지며, 무기 화합물계의 대표적인 예로 실리콘을 들 수 있다.Conventional permeable water absorption inhibitors (hereinafter referred to as “permeable waterproofing agents”) simply refer to suspensions dissolved in solutions or solvents that reduce the ingress of water. Water repellency and water repelling effect by filling pores present in concrete (遮 水 效果) to give the material. The permeable waterproofing agent is largely divided into organic compound and inorganic compound, and a representative example of the inorganic compound is silicon.
특히, 수용성 무기질계의 경우 현장 시공 후 침투 깊이에 대한 검증 및 확인 할 수 있는 방법이 명확하게 설정되어 있지 않으며, 직접적인 성능 확인보다는 SEM(전자주사현미경)을 통한 활성성분들의 생성을 확인하는 것으로 한정되어 있으며, 이 성분들에 의한 방수성능은 투수, 흡수, 강도 등의 간접적인 방법으로 성능 평가를 하는 것이 오늘날의 현실이다.In particular, in the case of water-soluble inorganic system, the method for verifying and verifying the depth of penetration after on-site construction is not clearly set, and it is limited to confirming the generation of active ingredients through SEM (electron scanning microscope) rather than confirming the direct performance. In today's reality, the waterproof performance of these components is evaluated by indirect methods such as permeability, absorption, and strength.
또한 유기화합물계의 경우는 무기화합물계에 비해 검증할 수 있는 방법을 가지고 있으나 성능보다는 시공적인 측면에서 보면 VOC ( Volatile Organic Concentration ) 규제, 환경적인 영향 등을 고려할 때 많은 제약을 갖고 있다.In addition, organic compounds have more verifiable methods than inorganic compounds, but in terms of construction rather than performance, they have many limitations when considering VOC (Volatile Organic Concentration) regulations and environmental impacts.
종래의 실란 및 실록산계 방수제는 통상 콘크리트 내부로의 염화 이온물의 침입을 감소시키기 위해 사용되는 단일성분으로 구성되어 있으며 일반적으로 3~6mm 정도 침투하는 재료로 알려져 있다. 콘크리트 내부로의 투수( water permeance )를 감소시키는 역할과 분자의 한쪽 끝이 골재에 부착되고, 다른 쪽은 발수(repell)하도록 하는 기구로 발수성을 부여하고 있다.Conventional silane and siloxane-based waterproofing agents are generally composed of a single component used to reduce the penetration of chloride ions into concrete and are generally known as materials penetrating about 3 to 6 mm. It provides water repellency by reducing water permeance into concrete and by attaching one end of the molecule to the aggregate and the other to repell.
실란과 실록산계는 분자구조상 통기성(=수증기 투과성능)이 있는 재료로서수증기(water vapor)가 콘크리트를 통과하게 하는 특성을 기본적으로 가지고 있는 재료이다. 이러한 특성을 갖는 반면에 시간이 경과(양생)되면서 경화되고 부스러지기 쉬운 경향을 가지되 되어 외부의 충격으로부터 발수성 피막이 손상되어 방수제로서의 기능을 상실하게 되고, 구조체의 거동에 따른 크랙 발생시 방수층의 연속성을 유지하지 못함으로써 방수막 내부로 물이 고이게 되고 사계절이 뚜렷한 국내 환경조건에 의해 동결융해( freeze-thaw damage )에 의한 방수기능 저하 및 하자를 발생시키는 것이 현실이다.Silanes and siloxanes are breathable (= water vapor permeation) materials in terms of molecular structure and are basically materials that allow water vapor to pass through concrete. On the other hand, it has a tendency to be hardened and brittle as time passes (curing), which damages the water-repellent coating from external shocks, and thus loses its function as a waterproofing agent. It is a reality that water is accumulated in the waterproof membrane due to failure to maintain and deteriorates the waterproof function and defects caused by freeze-thaw damage due to the distinctive four seasons of domestic environmental conditions.
기존 재료의 시공성을 보면 멤브레인( membrane )을 형성하는 특성에 의해 접착력 확보를 위하여 도포면은 먼지, 레이턴스, 오물 등이 깨끗하게 청소되어야 하며, 새로 타설(탈형)된 콘크리트 면은 상당 기간 동안 건조 양생이 되도록 기다려야 한다. 따라서, 콘크리트 표면을 샌드 브라스트( sand blasting )를 이용한 표면 처리를 해야 하는 경우가 많으며, 먼지를 없애고 세척했을 경우에는 완전히 건조되도록 기다려야 한다.According to the workability of existing materials, the coated surface should be cleaned of dust, latencies, dirt, etc. to secure adhesion due to the characteristics of forming a membrane, and the newly cast concrete surface is dried and cured for a long time. Wait as much as possible. Therefore, the surface of the concrete often needs to be sand blasted (sand blasting), and when the dust is removed and washed to wait to dry completely.
유용성 재료의 경우 작업시 주변 온도 및 콘크리트 표면 온도에 따라 작업을 중단해야하는 경우가 빈번하며, 강우시에는 다시 완전히 건조될 때까지 기다렸다가 시공을 해야하는 제약을 안고 있다. 분무 작업 시 바람이 많이 불면 분무증기가 날려 사람과 주변의 농작물에 피해를 줄 수 있으므로 적정한 풍속(風速)하에 작업을 해야하며, 필요하지 않는 콘크리트 부위에 접촉되거나 분사되었을 경우에는 피해를 줄 수 있다.In the case of oil-soluble materials, it is often necessary to stop the work according to the ambient temperature and the concrete surface temperature during the work, and in case of rainfall, it is necessary to wait until it is completely dried again before constructing it. If the wind blows a lot during spraying, the spray steam may blow and damage people and surrounding crops. Therefore, work should be done under the proper wind speed. .
인체 유해성 부분에서는 솔벤트 용제를 사용함으로써 분무 증기가 나고 인화성이 있으며, 인체, 동물, 주위환경에 안전성을 부여하지 못하고 있다. 특히. 손이나 피부 접촉 시 중화 할 수 없는 독성으로 인해 손상이 되므로 반드시 보호 마스크와 보호복 등의 장비로 완전하게 감싸고 분무증기(FUME)로부터 보호하는 대책이 필요하다. 저압 스프레이(15 PSI, 100kPa)를 사용하여 약 2.5~3.7㎢/ℓ로 분사하지만 정전기 및 기타 접촉성 인자에 의해 폭발성을 가짐으로써 다른 장비들에 대한 안전 조치가 필수적이다.In the human hazards, the use of solvent solvents, spray vapor and flammable, and does not give safety to humans, animals, and the environment. Especially. Since it is damaged due to toxicity that cannot be neutralized by hand or skin contact, it is necessary to completely cover it with equipment such as a protective mask and protective suit and to protect it from FUME. Using a low pressure spray (15 PSI, 100 kPa) at about 2.5 to 3.7 kW / l, it is explosive by static electricity and other contact factors, so safety measures for other equipment are essential.
기존 제품의 보관시 높은 온도에 의한 위험이 있을 수 있으므로 적정 온도 및 통풍이 잘되는 곳에 보관하여야하며, 인화물질과 같이 보관되어서는 안 된다.As there may be a danger of high temperature when storing the existing product, it should be stored in a proper temperature and well-ventilated place, and it should not be stored together with flammable materials.
최근 침투성 방수제가 콘크리트 구조물의 방수목적으로 많이 적용되고 있다. 지금까지 주로 사용되어온 침투성 방수제는 주성분이 시멘트, 규산질의 활성 실리카, 규사로 구성된 기조합 형태의 무기질계 분말(분체형) 재료로서, 이들 재료는 물 또는 에멀젼 등과 혼합하여 사용되어 진다.Recently, the permeable waterproofing agent has been widely applied for the waterproofing purpose of concrete structures. The permeable waterproofing agent which has been mainly used up to now is an inorganic powder (powder type) material in combination form composed mainly of cement, siliceous activated silica, and silica sand, and these materials are used in admixture with water or emulsion.
또한, 방수 메카니즘은 주성분인 활성 실리카와 콘크리트 조직내의 가용성 수산화 칼슘 및 미수화 시멘트 성분이 반응하여 불용성의 규산칼슘 수화물 및 에트링게이트( ettringite ) 등의 결정체를 생성시킴으로서 조직을 치밀하게 만들어 수밀성 및 방수성을 향상시키는 효과를 나타내고 있다.In addition, the waterproofing mechanism reacts with the active silica, which is a main component, and the soluble calcium hydroxide and unhydrated cement components in the concrete structure to produce crystals such as insoluble calcium silicate hydrate and ettringite, which makes the structure dense and thus watertight and waterproof. It has an effect of improving.
그러나 이들 재료에 있어서 활성실리카 성분의 침투성능은 제조사에서 제시하는 깊이 만큼 확인하기 어렵고, 그 시공성에 있어서 물의 사용량, 바탕 콘크리트의 건조, 습윤 조건, 도포 후 양생 등에 관한 품질관리에 많은 어려움이 따르고 있다.However, the penetration performance of active silica components in these materials is difficult to ascertain as the depth suggested by the manufacturer, and in terms of their workability, there are many difficulties in quality control regarding the amount of water used, drying of ground concrete, wet conditions, and curing after application. .
최근 환경 오염에 의한 콘크리트의 내구연한 감소와 계절적 요인으로 인하여 콘크리트의 균열, 잔갈림현상 등이 나타나고 있다. 외부에서 들어오는 물의 침투에 의한 열화 요인을 차단하여 콘크리트 표층부의 동결 파손 및 중성화 방지를 위한 처리가 필요하게 되었으며, 이에 적합한 재료 개발 부분은 약화되어 있다.Recently, due to the environmental degradation of the concrete due to environmental pollution and seasonal factors, concrete cracks, cracking phenomenon, etc. are appearing. By blocking the deterioration factor due to the ingress of water from the outside, it is necessary to treat the concrete surface layer to prevent freezing damage and neutralization, and the appropriate material development part is weakened.
일반적인 액체 침투성 방수제의 경우는 콘크리트 상판에 도포하여 방수성 및 발수성을 확보하지만 모체 크랙에 대해서는 대처하지 못하고 있으며, 유기 용제 사용 제품이 주류를 이루고 있어서 환경적 문제도 발생시키며 콘크리트 모체의 보호 기능보다는 방수성능에 치우쳐 있으며, 문제점 발생에 따른 대처 방안이 요구되는 경우 액체 침투성 방수제 위에 다른 방수층의 형성이 어려운 부분들이 있어 단일 방수의 시공법을 적용하고 있다. 모체 크랙 발생의 침투성 방수제의 경우 방수 성능이 소실되므로 크랙 추종성에 대한 재료적 문제점을 해결하여야 한다.In general, the liquid-permeable waterproofing agent is applied to the concrete plate to secure waterproofness and water repellency, but it does not cope with the mother crack, and organic solvent-based products are mainstream, causing environmental problems, and waterproofing performance rather than protection of the concrete matrix. If the problem is required, and a countermeasure is required due to the problem, there is a difficult part to form another waterproof layer on the liquid permeable waterproofing agent, so that a single waterproofing method is applied. The permeable waterproofing agent of the parental crack generation loses the waterproofing performance, so the material problem of crack followability should be solved.
반면, 도막 방수제 시공은 모체의 노화에 의하여 도막 부착 성능 저하로 진행하여 방수층 성능의 한계와 상관없이 방수층의 내구연한이 결정되기도 한다. 시공법은 프라이머 도포 후 도막방수제를 도포하며 프라이머의 기능은 모체와 방수층 사이의 접착 성능 확보의 기능적 성능에 중점을 두고 있으며, 방수 성능 역시 다양한 모체 콘크리트의 영향을 많이 받는다.On the other hand, coating film waterproofing construction proceeds to the coating film deterioration performance by the aging of the parent, and the durability of the waterproof layer may be determined irrespective of the limit of the waterproof layer performance. The construction method is to apply a coating waterproofing agent after applying the primer, the function of the primer is to focus on the functional performance of securing the adhesion performance between the mother and the waterproof layer, the waterproof performance is also affected by a variety of matrix concrete.
최근 도막 방수제의 복합 방수공법이 시공되고 있으나 도막과 도막 또는 시트와 도막의 시공이 있으며 상기에서 언급한 도막방수 역시 콘크리트 모체 보호를 통한 구조체의 내구연한 연장과 같은 모체에 대한 기능성 제품이 아니라 방수성능의 우선 확보를 통한 물, 공기, 자외선 등 콘크리트 노화의 유해환경으로부터 차단되는 부가 기능으로 모체의 노화를 방지하므로 구조물에서 가장 중요한 모체의 기능 향상 및 노화 방지 기능은 충분히 발휘되지 못하고 있다.Recently, the composite waterproofing method of the coating waterproofing agent is being constructed, but there is the construction of the coating film and the coating film or sheet and the coating film, and the above-mentioned coating waterproofing is also not a functional product for the mother such as the durable extension of the structure through the protection of the concrete matrix, but the waterproof performance. As a supplementary function that blocks the harmful environment of concrete aging such as water, air, and ultraviolet rays by securing the priorities of the mother to prevent aging of the mother, the most important mother's function improvement and anti-aging function in the structure is not sufficiently exhibited.
그밖에 액체방수공법이 시공되고 있으나 구조물 크랙 추종성이 없어 방수 성능의 장기적 안정성이 떨어져 사용의 제한을 받고 있는 실정이다.In addition, the liquid waterproofing method is being constructed, but there is no structure crack tracking, so the long-term stability of the waterproof performance is limited and the use is restricted.
이상과 같은 재료의 적용성과 성능상의 문제점, 시공상의 문제요인들을 수용성화를 통하여 보다 환경 친화적인 경향과 VOC 규제에 적극 대응하고, 안전한 방수재료의 제조와 기존 액체형 침투성 방수재료, 도막방수재료 등의 단일 재료적 한계점을 침투성 표면 보호 처리제와 시멘트계 도막 방수제를 적용한 복합공법으로 상호 보완하고자 제조기술과 적용 공법의 개발이 요구되고 있다.By applying the above-mentioned materials, performance problems, and construction problems to water-soluble materials, we actively respond to environmentally friendly trends and VOC regulations, and manufacture safe waterproof materials, existing liquid-type permeable waterproof materials, and film waterproofing materials. The development of manufacturing technology and application method is required to complement the single material limitation with the composite method applying permeable surface protection treatment agent and cement-based coating waterproofing agent.
국내 특허공개 제99-0078673호에서는 실리콘 에멀젼 수용성 발수, 방수제의 조성물 및 제조 방법에 대해 개시하고 있으며, 제조방법의 경우 1차로 필요한 조성물을 콤파운드 형태로 제조한 다음, 유화제를 첨가하여 제조물을 얻는 방식을 적용하고 있다.Korean Patent Laid-Open No. 99-0078673 discloses a composition and a method for preparing a silicone emulsion water-soluble water repellent, a waterproofing agent, and in the case of the manufacturing method, a method for obtaining a product by first preparing a required composition in a compound form and then adding an emulsifier Is applying.
이러한 방법은 제조설비의 거대화와 온도 제어에 따른 제조공정상의 불안정성을 가지고 있으며, 이후 완제품 생산을 위한 추가 설비가 요구된다. 또한 시공에 따른 강도 저하는 없는 것으로 나타났으나, 성능 평가부분에서 단일재료에 대한 검증만을 적용하고 있고 방수제의 침투깊이를 확인할 수 있는 기능을 갖고 있지 않다.This method has manufacturing process instability due to the enlargement of manufacturing equipment and temperature control, and then additional equipment for producing finished products is required. In addition, there was no decrease in strength according to the construction, but only the verification of the single material is applied in the performance evaluation part, and it does not have a function to confirm the penetration depth of the waterproofing agent.
국내 특허공개 제92-18161호에는 침투성 실리콘계 발수제 조성물이 개시되어 있다. 본 선행기술은 발수제의 기능을 더욱 향상시키기 위한 재료로 흄실리카를추가함으로서 화학적인 열화물질로부터 보호하고자하는 특성과 유용성 재료를 바탕으로 한 조성물로서, 표면 보호효과는 부여 가능 하지만 구조물의 크랙에 대한 저항성 및 이로 인한 보호효과를 보장할 수 없는 단점과 제조물의 도포 이후 필요에 따른 수용성 멤브레인 방수재 적용시 발수성능에 의해 도포 적용이 불가능한 문제점을 내제하고 있다. 특히, 환경친화성 문제에 있어 유용성 재료를 적용함으로써 시공자의 위험에 대한 노출에 대안을 제시하지 못하고 있다.Korean Patent Publication No. 92-18161 discloses a permeable silicone-based water repellent composition. The present prior art is a composition based on the properties and useful materials to be protected from chemical deterioration by adding fume silica as a material for further improving the function of the water repellent, and can provide a surface protection effect, The disadvantages of not being able to guarantee the resistance and the protection effect thereof and the application of the water-soluble membrane waterproofing material as necessary after application of the product are impossible due to the water repellency. In particular, the application of oil-soluble materials in environmental friendliness does not provide an alternative to exposure to the builders' risks.
한편, 국내 특허공개 제98-024917호에서는 콘크리트와 같은 다공성 무기 건축자재의 표면에 적용되는 경우 전체 적용면에 적용을 육안 검사할 수 있는 알킬알콕시실란의 수성-기초 에멀션을 함유한 침투성 물 흡수 방지제로서, 상기 에멀션이 알킬알콕시실란, 오일-용해성 염료, 에멀션화제 및 물을 함유한 것이 개시되어 있다.On the other hand, in Korean Patent Publication No. 98-024917, when applied to the surface of a porous inorganic building material such as concrete, permeable water absorption inhibitor containing an aqueous-based emulsion of alkylalkoxysilane that can be visually inspected for application to the entire application surface. As such, the emulsions contain alkylalkoxysilanes, oil-soluble dyes, emulsifiers and water.
본 선행기술에서는 알킬알콕시실란의 수성 분산물은 장시간동안 물 흡수 방지 효과를 유지하는 것으로 발견되어, 콘크리트 등에 대한 보호재로서 유용하나 저분자량 알킬알콕시실란은 기질 내부로 침투하므로, 적용 직후 적용이 완료되었는지를 여부를 검사하기 어렵다는 점을 인식하고, 알킬알콕시실란의 수성-기초 에멀션을 함유하는 침투성 물 흡수 방지제가 콘크리트와 같은 다공성 무기 건축자재에 적용되는 경우, 건축자재의 표면이 착색되고, 표면 소수성층이 형성된 다음, 염료는 색이 바래거나 소수성 층을 유지하면서 염색한 색을 잃게 하였다. 따라서 적용의 완료를 확인하기 쉬우므로, 상기 침투성 물 흡수 방지제는 콘크리트와 같은 다공성 무기 건축 자재물의 물 흡수를 방지하는데 유용하다.In the prior art, aqueous dispersions of alkylalkoxysilanes have been found to maintain the effect of preventing water absorption for a long time, which is useful as a protective material for concrete and the like, but low molecular weight alkylalkoxysilanes penetrate into the substrate. Recognizing that it is difficult to examine whether or not a permeable water absorption inhibitor containing an aqueous-based emulsion of alkylalkoxysilane is applied to a porous inorganic building material such as concrete, the surface of the building material is colored and the surface hydrophobic layer After this was formed, the dye faded or lost the dyed color while maintaining the hydrophobic layer. Thus, since it is easy to confirm the completion of the application, the permeable water absorption inhibitor is useful for preventing the water absorption of porous inorganic building materials such as concrete.
그런데 본 선행기술은 시공성에 있어서 작업의 시작과 종료 시점을 육안 확인 가능한 성능을 부여한 것으로 재료 성능상의 침투 깊이 검증 부분에 대해서는 언급되어 있지 않다. 또한, 침투 깊이에 대한 검증은 여전히 현장에서 시료를 채취해야 하는 근본적인 문제점에 대한 제시는 없는 상태이다. 본 선행기술은 흡수방지제의 조성물 중 염료에 의한 작업성의 원활성 이외에 다른 성능상의 기능향상은 제시하고 있지 않다.However, the present prior art provides performance that can be visually confirmed at the start and end of work in constructability, and does not mention the penetration depth verification part of the material performance. In addition, verification of penetration depth still lacks the fundamental problem of sampling at the site. The prior art does not suggest any performance improvement other than the smoothness of workability by dyes in the composition of the absorption inhibitor.
유기실리콘의 유화기술은 다양한 방법으로 제조되고 있으나 재료 특성을 발수제, 흡수방지제, 방수제로서 활용되어 지고 있으며, 성능의 단일성을 가지고 있다. 선행기술에서는 수용화된 조성물의 표면 도포시 구조체의 강도 저하에 대한 확인정도의 내용이며, 발수 및 방수성능, 침투 깊이 등의 요구성능이 유용성인 경우보다 수용화된 경우 크게 향상된 부분이 없는 상태이다.The organosilicon emulsification technology is manufactured by various methods, but the material properties are utilized as a water repellent, an absorption inhibitor, and a waterproofing agent, and have a unity of performance. In the prior art, the content of the confirmation of the reduction of the strength of the structure during the application of the surface of the accommodated composition, there is no significant improvement when the water repellent, waterproof performance, penetration depth, etc. if the required performance is acceptable than when it is useful .
또한, 현장 적용시 유성 재료의 경우 시간 차이에 의한 작업의 경계면을 확인하기 어려운 부분을 염료를 통해서 개선하는 방법을 택하고 있어 다양한 요구조건을 충족시키는 기술은 부재한 상황에서 본 발명이 개발되게 되었다.In addition, in the case of oil-based materials in the field application, the method of improving the part which is difficult to check the boundary of the work due to the time difference is selected through the dye, and thus the present invention is developed in the absence of a technology that satisfies various requirements. .
본 발명은 유용성 재료를 수용화하는 제조기술과 강도 향상제를 적용함으로써 발수, 방수, 흡수방지 효과와 무기 실리케이트(silicate) 적용으로 강도 향상효과를 부여하고 있다.The present invention imparts a water repellent, waterproof, anti-absorption effect and an inorganic silicate to enhance the strength by applying a manufacturing technique and a strength enhancer to accommodate the oil-soluble material.
시공면에서는 고점도(크림) 형태를 적용함으로써 벽면과 천정면의 작업시 재료의 흘러내림이나 튀는 현상을 방지하여 작업의 신속성과 경계면 부분의 명확성으로 균일한 시공을 할 수 있도록 하였다.In the construction surface, high viscosity (cream) shape was applied to prevent the material from falling or splashing when working on the wall and ceiling surfaces, so that the construction could be performed uniformly with the speed and clarity of the interface.
성능면에서는 기존의 침투성 방수제의 침투 성능을 현장에서 직접 품질관리 할 수 있도록 하였으며, 표면 처리 후 3-4 시간 이후 상부 방수제를 도포 및 설치를 통하여 단일재료로서 부족한 크랙 저항성, 추종성 부족으로 인한 방수제로서 요구성능을 시트/도막재와 복합 적용함으로써 상호 보완하도록 하였다.In terms of performance, the permeation performance of the existing permeable waterproofing agent can be directly controlled in the field, and after 3-4 hours after surface treatment, the upper waterproofing agent is applied and installed as a waterproofing material due to insufficient crack resistance and lack of followability as a single material. The required performance was complemented by applying the composite with the sheet / film material.
따라서 본 발명은 이러한 종래기술의 문제점을 감안하여 안출된 것으로, 그 목적은 콘크리트 구조물의 표면에 침투성 물 흡수 방지제를 처리하여 콘크리트 구조물의 방수, 방식 특성을 부여함과 동시에, 침투 성능을 양생 후 육안 확인이 영구히 가능하여 현장 시공에 따른 침투성능에 대한 검증과 품질관리가 효율적으로 이루어질 수 있는 침투성 물 흡수 방지제 조성물 및 그의 제조방법을 제공하는 데 있다.Therefore, the present invention has been made in view of the problems of the prior art, the object of which is to treat the permeable water absorption inhibitor on the surface of the concrete structure to impart waterproof and corrosion-resistant characteristics of the concrete structure, and at the same time, after curing the penetration performance naked eyes The present invention provides a permeable water absorption preventing agent composition and a method of manufacturing the same, which can be verified permanently and can efficiently perform the verification and quality control of the permeation performance according to the construction of the site.
본 발명의 다른 목적은 콘크리트 구조물에 도포된 물 흡수 방지제의 상부에 시멘트계 도포형 방수재를 함께 적용함으로써 물 흡수 방지제의 단점을 멤브레인(membrane) 방수에 의해 극복하여 구조체의 노화방지와 방수성능을 극대화시킬 수 있는 침투성 물 흡수 방지제 조성물을 이용한 복합 방수시공방법을 제공하는 데 있다.Another object of the present invention is to overcome the disadvantages of the water absorption inhibitor by the membrane waterproofing by applying a cement-based coating waterproofing material on top of the water absorption inhibitor applied to the concrete structure to maximize the anti-aging and waterproof performance of the structure It is to provide a composite waterproof construction method using a permeable water absorption inhibitor composition.
도 1은 본 발명의 침투성 물 흡수 방지제 조성물을 사용하여 복합 방수시공한 경우 방수층의 단면구조를 보여주는 단면사진이다.1 is a cross-sectional photograph showing a cross-sectional structure of the waterproof layer when the composite waterproof construction using the permeable water absorption inhibitor composition of the present invention.
A. 침투성 물 흡수 방지제 조성물A. Permeable Water Absorption Composition
본 발명에 따른 침투성 물 흡수 방지제 조성물의 주성분은 옥틸-트리-에톡시 실란/실록산(Octyltriethoxysilane/siloxane)과 무기질계 소디움실리케이트(Sodium Silicate)로서 기존 재료의 특성과 구조체의 강도 증진 효과를 부여함으로써 보다 완벽한 방수성능과 작업 안정성을 부여한다.The main components of the permeable water absorption preventing agent composition according to the present invention are octyl-tri-ethoxysilane / siloxane and inorganic sodium silicate, which impart the effect of enhancing the properties of the existing materials and the strength of the structure. It gives perfect waterproof performance and work stability.
상기 침투성 물 흡수 방지제는 1차 표면 처리제로서 콘크리트 구체에 도포되어 공극 내부에서 경화하며, 발수 성질을 부여함으로써 외부에서 침투하는 물을 차단하는 재료이다. 시공 후 콘크리트와 모르타르의 내부에 연속적인 폴리머 필름을 형성하여 발수성을 가지고 있기 때문에 충전효과와 물의 흡수 방지효과의 상승효과에 의해 방수성을 발휘하게 된다.The permeable water absorption preventing agent is a material that is applied to concrete spheres as a primary surface treatment agent to cure inside the pores and to impart water repellent properties to block water penetrating from the outside. Since it has water repellency by forming a continuous polymer film inside concrete and mortar after construction, it exhibits waterproofness by synergistic effect of filling effect and water absorption prevention effect.
물 흡수 방지효과는 재료 특성상 수증기 투과성을 가지고 있으며, 구조체 표면의 공극에 얇은 막을 공극벽에 형성하여, 형성된 발수성 막에 의해 공극이 물에 젖지 않게 되고, 모세관 현상이 발생하지 않게 되어 물의 유입을 막을 수 있게 된다.The water absorption prevention effect has water permeability due to the material property, and a thin film is formed on the pore wall in the pores of the structure surface, so that the pores do not get wet by the formed water repellent membrane and the capillary phenomenon does not occur, thereby preventing the inflow of water. It becomes possible.
수증기 투과성능은 건물 내에 습기가 함유되어 있을 때 그 수중기가 건물에 손상없이 외부로 배출 가능한 특성으로서 1차 표면 처리제의 필수적인 특성중의 한가지이다.Water vapor permeability is one of the essential properties of the primary surface treatment agent, which can be discharged to the outside without damaging the building when moisture is contained in the building.
내구성 면에서는 실리콘 수지와 물, 재료에 포함되어 있는 알콕시(alkoxy) 기가 상호작용하여 폴리실록산(polysiloxanes)과 강하게 결합함으로써 Si-O-Si의 가교결합에 의한 밀도 증가로 견고하게 구조물에 부착하게 되고, 망상구조를 형성한 실리콘 수지계 폴리머 막은 탁월한 방수성능과 화학결합상의 내화학적 안정성, 물리적, 생물학적 영향으로부터 강하게 저항할 수 있는 특성을 부여하고 있다.In terms of durability, the silicone resin, water, and alkoxy groups included in the material interact with each other to strongly bond with polysiloxanes, thereby firmly attaching to the structure due to an increase in density due to crosslinking of Si-O-Si. The silicone resin-based polymer film having a network structure has excellent waterproofing properties, chemical stability on chemical bonding, and strong resistance to physical and biological effects.
본 발명에 따른 침투성 물 흡수 방지제 조성물은옥틸트리에톡시실란/실록산(octyl-tri-ethoxy silan/siloxane) 35-50중량%, 물 35-55중량%, 에멀션화제 0.1-1.0중량%, 보호콜로이드제 0.1-1.5중량%, 및 강도보호재로서 수용성 실리케이트(Silicate) 5-20중량%로 이루어지는 것을 특징으로 한다.Permeable water absorption preventing composition according to the present invention is octyl-tri-ethoxy silan / siloxane 35-50% by weight, water 35-55% by weight, emulsifier 0.1-1.0% by weight, protective colloid 0.1-1.5% by weight, and 5-20% by weight of water-soluble silicate (Silicate) as a strength protective material.
본 발명의 주성분으로 역할을 하는 옥틸트리에톡시 실란/실록산은 1개의 옥틸(Octyl)기와 3개의 에톡시(Ethoxy)기 각각이 실리콘 원자(Si)에 직접 결합된 트리 기능성(tri-functional) 실리콘 레진 화합물로서 하기의 반응식 1과 같이 3H2O와 반응하여 실리콘 레진 네트웍을 형성하는 실란과 하기 반응식 2와 같이 2개의 실란이 H2O와 반응하여 Si-0-Si 가교결합을 이루고 있는 실록산의 혼합물로 이루어져 있다.The octyltriethoxy silane / siloxane, which serves as a main component of the present invention, is a tri-functional silicone in which one octyl group and three ethoxy groups are each directly bonded to a silicon atom (Si). As the resin compound, silane reacts with 3H 2 O to form a silicone resin network as shown in Scheme 1 below, and two silanes react with H 2 O to form Si-0-Si crosslinked as shown in Scheme 2 below. It consists of a mixture.
상기 실란과 실록산의 혼합물은 구조체 표면 및 내부 박막 형성시 상대적으로 작은 크기의 실란은 고침투력을 부여하고, 상대적으로 큰 실록산은 표면에 인접하게 침투하여 콘크리트 구조체의 다양한 공극 크기를 동시에 적용할 수 있도록 하기 위해 부분 혼합물을 적용하고 있다.When the mixture of silane and siloxane is formed on the surface of the structure and the inner thin film, the relatively small size of the silane gives high penetration force, and the relatively large siloxane penetrates adjacent to the surface so that various pore sizes of the concrete structure can be simultaneously applied. Partial mixtures are applied for this purpose.
또한 상기 실란과 실록산의 혼합물은 주 결합제 및 구조체내에 침투하여 미세공극의 표면과 화학적 결합력에 의해 방수성 박막을 형성하여 외부 침투 성분으로부터 보호하는 역할을 한다.In addition, the mixture of the silane and the siloxane penetrates into the main binder and the structure to form a waterproof thin film by chemical bonding force with the surface of the micropore, thereby protecting it from external permeation components.
상기 실란과 실록산의 혼합물은 35 중량% 미만의 낮은 함유량을 가질 경우 유화안정성은 향상되나 내부 박막 형성의 조밀도가 낮아 외부 수압에 대한 저항성을 상실하게 되어 방수성능을 충분히 발휘하지 못하며, 표면 도포에 따른 압축강도 향상의 목적을 달성하지 못하는 문제점이 있다. 또한 50중량%를 초과하여 첨가시 이후 공정으로 적용되는 무기질 침투성 도막 방수제 적용시 막간 접착력 저하로 충분한 재료의 침투성능을 저하시키는 요인으로 작용한다. 또한, 물에 대한 유화 안정성에 있어 유화제보다 과량의 유용성 재료를 첨가함으로써 제조시 불완전한 형태의 안정물을 얻으며, 장기적인 저장안정성에도 악 영향을 주게 된다.When the mixture of the silane and the siloxane has a low content of less than 35% by weight, the emulsion stability is improved, but the density of the internal thin film formation is low, so the resistance to external water pressure is lost, and thus the waterproof performance is not sufficiently exhibited. There is a problem that does not achieve the purpose of improving the compressive strength according. In addition, when the inorganic permeable coating waterproofing agent applied in the subsequent process when added in excess of 50% by weight, it acts as a factor that lowers the permeation performance of the sufficient material due to the decrease in interlayer adhesion. In addition, the addition of excess oil-soluble material than the emulsifier in the emulsion stability to water to obtain a stable form of the incomplete manufacturing, and adversely affect the long-term storage stability.
상기 실란/실록산 혼합물의 경우 실란의 침투 특성과 실록산의 표면 처리 역할을 부여하기 위해 적용되었으며, 혼합비율은 1:0.02-0.5으로 설정되는 것이 바람직하며, 비율이 0.02 미만의 경우 침투성능 향상으로 표면처리의 효과가 상대적으로 떨어지며, 0.5 이상의 경우 침투성능의 저하를 수반하게 된다.In the case of the silane / siloxane mixture was applied in order to give the penetration characteristics of the silane and the surface treatment role of the siloxane, the mixing ratio is preferably set to 1: 0.02-0.5, when the ratio is less than 0.02 the surface by improving the penetration performance The effect of the treatment is relatively low, and in the case of 0.5 or more, it is accompanied by a decrease in penetration performance.
적용되는 물의 양은 35-55 중량%로 분산하려고 하는 옥틸트리에톡시 실란의 유화에 적정한 량을 첨가하고, 특히. 적용되는 물은 이온교환수지 처리를 한 다음 사용을 하거나, 첨가제(AMP-95 ANGUS社)를 사용하여 금속성 이온으로부터 비효율적인 유화형태가 되지 않도록 처리한 것을 사용하도록 한다.The amount of water applied adds an appropriate amount to the emulsification of octyltriethoxy silane to be dispersed at 35-55% by weight, in particular. Applied water should be used after treatment with ion exchange resin, or treated with additives (AMP-95 ANGUS) to prevent inefficient emulsification from metallic ions.
상기 조성물에 대한 유화제는 O/W형의 에멀션화제로서 HLB(Hyrophile-Lipophile Balance value) 4.3의 솔비탄 모노올레이트(Sorbitan monooleate)계를 적용하며, 실란 재료의 유화에 적합한 비이온성 계면활성제로 HLB 값을 선택하여 적용하도록 한다. 특히, HLB값의 범위는 3.5-6 사이를 적용하도록 한다. HLB값이 3.5 미만 경우 소수성으로 제조 후 희석하는 경우 불안정한 유화형태를 만들게 되며, 6을 초과하는 경우 O/W형으로 전체적인 점도 저하로 저장안정성이 불균일하거나 유화 상태가 파괴된다. 에멀션화의 경우 유화 작용과 억포작용을 동시에 가지는 에멀션화제를 사용하여야 한다.The emulsifier for the composition is applied to a sorbitan monooleate (HLB) type of HLB (Hyrophile-Lipophile Balance value) 4.3 as an emulsifier of O / W type, and HLB as a nonionic surfactant suitable for emulsification of silane material Select a value and apply it. In particular, the range of HLB values should be applied between 3.5-6. If the HLB value is less than 3.5, it is unstable to form an unstable emulsified form after dilution with hydrophobicity. If the HLB value is greater than 6, the O / W type causes a decrease in overall viscosity, resulting in uneven storage stability or destruction of the emulsified state. In the case of emulsification, an emulsifier having both emulsification and suppression should be used.
첨가되는 에멀션화제는 0.1 중량% 미만 적용시 유적이 표면으로 떠오르는 현상이 발생하여 안정한 유화액상을 얻을수 없으며, 저장안정성 또한 상용화하기에는 부족하며, 1.0 중량% 초과 적용시는 유화균형성을 파괴하여 장기저장시 층분리 및 유분의 응집현상이 발생하여 침전이 발생하게된다.If the emulsifier is added less than 0.1% by weight, the phenomenon of oil surface floating occurs on the surface, so that the stable emulsion phase cannot be obtained, and the storage stability is also insufficient for commercialization. During sedimentation and flocculation of oil, precipitation occurs.
본 발명에 적용되는 에멀션화 안정제는 폴리비닐알콜을 이용한 보호콜로이드 시스템을 적용하여 장기적인 저장안정성을 부여하고 있다. 첨가되는 보호콜로이드제는 0.1 중량% 미만인 경우 저장 중 층분리(물과 조성물) 및 침전물의 뭉침 현상이 발생하여 충분한 기능발휘가 어려우며, 1.5 중량% 초과 적용시는 저장중의 점도 상승 및 응집(뭉침) 현상으로 균일한 액상을 유지하기 어렵게 되며, 도포 작업시 작업성과 침투력을 저하시키게 된다.The emulsifying stabilizer applied to the present invention is imparting long-term storage stability by applying a protective colloid system using polyvinyl alcohol. When the protective colloid agent added is less than 0.1% by weight, delamination (water and composition) and agglomeration of sediment occur during storage, so that it is difficult to exhibit sufficient function. It is difficult to maintain a uniform liquid phase due to the) phenomenon, and it lowers workability and penetration during the coating operation.
강도보호재료는 유화액상 제조 후 첨가되며, 조직 치밀화 및 구조체 강도 저하를 방지를 목적으로 수용성 소디움계 실리케이트를 5-20중량% 범위로 적용하고 있다. 표면 침투 후 알칼리 조건하에서 점진적인 화학반응을 통하여 구조체 내부의 겔(gel)-상태 충진이 형성되며, 구조체의 내구적 안정화를 부여하는 성분으로, 5 중량% 미만 적용시 옥틸트리알콕시 실란에 의한 강도 및 구조체 충진 효과가 떨어져 발명에서 얻고자 하는 성능 향상 기능이 없게 되며, 첨가에 따른 침투성능 저하를 유발하게 되고, 20 중량%를 초과하여 첨가하는 경우 방수성능 및 화학적 침투로부터 보호효과를 상실하게 되며, 구조체 공극을 더욱 조밀한 충진으로 강도만을 향상시키게 된다.The strength protective material is added after the emulsion phase is prepared, and a water-soluble sodium silicate is applied in the range of 5-20% by weight for the purpose of preventing tissue densification and lowering of structural strength. After the surface penetration, the gel-state filling inside the structure is formed through a gradual chemical reaction under alkaline conditions, and it gives endurance stabilization of the structure. When applied below 5% by weight, strength by octyltrialkoxy silane And the structure filling effect is poor, there is no performance improvement function to obtain in the invention, it causes a decrease in the penetration performance by the addition, when added in excess of 20% by weight loses the waterproofing performance and protection from chemical penetration As a result, denser filling of the voids of the structure will only increase the strength.
B. 조성물의 제조방법B. Preparation of Composition
본 발명에 따른 침투성 물 흡수 방지제 조성물의 제조방법은 물 5-10중량%에 보호콜로이드제 0.1-1.5중량% 범위로 첨가 교반한 에멀션화제 0.05-0.5중량% 범위로 첨가하여 중속도로 교반하여 제1액상을 준비하는 제1단계와, 옥틸트리에톡시실란/실록산 35-50중량%에 에멀션화제를 0.05-0.5중량% 범위로 첨가하여 중속도로 교반하여 제2액상을 준비하는 제2단계와, 물 25-55중량%에 소디움계 실리케이트 5-20중량%를 교반하면서 첨가한 후 충분히 교반하여 균일한 제3액상을 제조하는 제3단계와, 상기 제1액상에 중속도로 교반하면서 제2액상을 천천히 드룹핑(Drooping)하여 제1수용화 액상을 준비하는 제4단계와, 상기 제1수용화 액상을 중속도로 교반하면서 상기 제3액상을 드룹핑하여 혼합하는 제5단계로 구성되어, W/O형의 수성형 침투성 물 흡수 방지제 조성물을 제조하는 것을 특징으로 한다.Method for producing a water-permeable water absorption composition according to the present invention is added to 5-10% by weight of water in the range of 0.1-1.5% by weight of the protective colloid agent stirred emulsifier added in the range of 0.05-0.5% by weight and stirred at a medium speed of the first A first step of preparing a liquid phase, a second step of preparing a second liquid phase by adding an emulsifier to a range of 0.05-0.5% by weight to 35-50% by weight of octyl triethoxysilane / siloxane and stirring at a medium speed; 5 to 20% by weight of sodium silicate was added to 25-55% by weight, followed by stirring to prepare a uniform third liquid phase, and slowly stirring the second liquid phase while stirring the medium to the first liquid phase. And a fifth step of drooping to prepare a first aqueous solution liquid, and a fifth step of mixing the third liquid phase by mixing the first aqueous solution liquid at a medium speed, thereby mixing W / O. To prepare a water-based penetrating water absorption inhibitor composition And that is characterized.
유화에 필요한 물의 사용량은 5-10 중량%를 적용하며, 5 중량% 미만 적용시에는 유화를 위한 수상 베이스의 최소값으로 설정된 것이다. 10 중량% 초과 적용시에는 적정한 유화 이상의 베이스를 가지므로써 얻고자하는 크림 형태에서 저점도 형태의 제조물을 얻게 된다.The amount of water required for emulsification is 5-10% by weight, and when less than 5% by weight is set to the minimum value of the aqueous base for emulsification. When applied in excess of 10% by weight, the base in the form of cream to obtain a low viscosity in the form of creams obtained by obtaining more than a suitable emulsification.
실리케이트 희석에 사용되는 물의 량은 25-55 중량%로 25중량% 미만 적용시 실리케이트 함량이 많아지게 되고 이로 인한 침투성능 저하를 수반하게 되고, 55 중량% 초과 적용되는 경우 얻고자 하는 크림형태의 조성물을 얻지 못하게 된다.The amount of water used for the silicate dilution is 25-55% by weight, the application of less than 25% by weight of the silicate content is increased, resulting in a decrease in permeation performance, if the application of more than 55% by weight of the cream form composition You won't get it.
이하에 상기한 조성물의 제조방법을 구체적인 예를들어 상세하게 설명한다.The manufacturing method of the said composition is demonstrated to a specific example below.
먼저 물 1,000g에 폴리비닐알콜 (예 PVA-224, Kuraray社) 17.17g을 첨가 후 2,000rpm 이상으로 교반한 다음 에멀션화제 (예 Span 80, ICI社) 4.21g을 첨가하여 1,500-2,000rpm으로 20 분간 교반하여 제1액상을 제조한다.First, 17.17 g of polyvinyl alcohol (e.g. PVA-224, Kuraray) was added to 1,000 g of water, followed by stirring at 2,000 rpm or more, and then 4.21 g of an emulsifier (e.g., Span 80, ICI) was added to 20 to 1,500-2,000 rpm. Stirring for minutes prepares the first liquid phase.
상기 배합순서는 물-폴리비닐알콜-에멀션화제 순서로 제조한다. 상세하게는 교반기에 물을 넣은 다음 저속교반(1000rpm)하면서 폴리비닐알콜 파우더를 소량씩 첨가하도록 한다. 과량 투입시 폴리비닐알콜의 뭉침 현상으로 용해하는 데 장시간이 필요하게 되며, 특히 유화 이후 응결 핵으로 작용하여 뭉침 현상이 발생하게 된다.The compounding sequence is prepared in the order of water-polyvinyl alcohol-emulsifier. Specifically, water is added to the stirrer, and then a small amount of polyvinyl alcohol powder is added while stirring at a low speed (1000 rpm). In case of excessive input, a long time is required to dissolve due to agglomeration of polyvinyl alcohol, and in particular, it acts as a coagulation nucleus after emulsification and causes agglomeration.
완전히 용해한 다음 에멸션화제를 투입 한 다음 중속 교반(1,500-2,000rpm)으로 20분간 교반하여 균일한 액상을 제조한다. 에멀션화제 첨가 후 2,000rpm 이하의 경우 폴리비닐알콜의 불완전한 용해로 인하여 이후 에멀션화제의 효율적인 분산을 저해하여 보호콜로이드 효과와 유화안정성을 저해한다. 교반시간은 최소한의 제조 요소로 설정된 것이다.After dissolving completely, an emulsifier is added and then stirred for 20 minutes with medium speed stirring (1,500-2,000 rpm) to prepare a uniform liquid phase. In case of less than 2,000rpm after the emulsifier is added, due to incomplete dissolution of the polyvinyl alcohol, the effective dispersing of the emulsifier is inhibited, thereby inhibiting the protective colloid effect and the emulsion stability. The stirring time is set to the minimum manufacturing element.
또한, 다른 용기에 옥틸트리에톡시실란/실록산 (octyl-tri-ethoxy silan ; BS-1701 octyl-tri-ethoxy Silane/siloxane ; BS-275 =1:0.03 혼합액 Wacker社) 2,583.4g에 에멀션화제 4.21g을 첨가하여 1,500-2,000rpm으로 20분간 교반한 다음, 상기 액상에 1,700rpm속도로 교반하면서 천천히 드룹핑(속도 1.7 kg/min)하여 수용화 제2액상을 제조한다.Further, emulsifier 4.21 g in 2,583.4 g of octyl-tri-ethoxy silan (BS-1701 octyl-tri-ethoxy Silane / siloxane; BS-275 = 1: 0.03 mixed solution Wacker) in another container After stirring for 20 minutes at 1,500-2,000rpm, and then stirred at 1,700rpm speed to the liquid phase slowly drooping (speed 1.7kg / min) to prepare a water-soluble second liquid phase.
이 경우 실란/실록산에 저속교반(1000rpm) 하면서 에멀션화제를 투입한다. 투입 후 1,500rpm 이하의 경우 균일한 유화안정성을 얻을 수 없으며, 2,000rpm 이상의 경우 액상의 온도 상승으로 제조 후 냉각 시 에멀션화제가 석출되는 성질을 가지므로 유화 불안정성을 가지게 된다.In this case, the emulsifier is added to the silane / siloxane while stirring at a low speed (1000 rpm). If it is less than 1,500rpm after the addition, it is not possible to obtain a uniform emulsion stability, and if more than 2,000rpm has the property of emulsifier is precipitated during the cooling after manufacturing due to the rise of the temperature of the liquid phase has an emulsion instability.
드룹핑(속도 1.7 kg/min)시 교반 속도는 1,500~1,700 RPM으로 중속 교반으로 실시하며, 1,500RPM 이하인 경우 유상이 유화되지 않고 상부로 유적이 모이는 현상이 있으며, 1,700 RPM 이상인 경우 유화에 의한 온도 상승 현상이 발생하여 유화안정성 및 전상 상태가 이루어지지 않는다. 드룹핑 속도가 분당 2.0kg 이상의 경우 유상의 충분한 유화안정성 확보 전 과량 투입됨으로써 요구하는 액상을 만들 수 없으며, 1.5kg 이하의 경우 생산성이 저하되는 시점으로 작용한다.In the case of drooping (speed 1.7 kg / min), the stirring speed is 1,500 ~ 1,700 RPM and it is carried out by medium speed agitation.If it is less than 1,500RPM, the oil phase is not emulsified and the oil remains in the upper part. Synergy occurs and emulsion stability and phase state are not achieved. If the drooping speed is more than 2.0kg per minute, it can not make the required liquid phase because it is excessively charged before securing sufficient emulsion stability of the oil phase, and if it is less than 1.5kg, it acts as a point of decreasing productivity.
그후 상기 제2단계에 의해 제조된 유성 베이스의 액상을 제1단계에 의해 제조된 수성 베이스의 액상에 적하하는 방법(W/O형에서 O/W형으로 상전이하는 방법)을 적용하며, 반대로 O/W형에서 W/O형으로 전상(轉相:액상의 주 base가 전환되는 시점)하는 방법 적용하였을 경우 O/W 상의 유화상태로 장기적인 저장안정성이 부족한 액상을 얻게 된다. 장기적인 저장안정성은 에멀션화재를 적용하여 제조상태에서는 W/O 형에서 O/W형으로 전상(轉相)하도록 제조한 O/W형 수용화제가 가장 우수한 안정성을 가진다.Then, a method of dropping the liquid phase of the oily base prepared by the second step into the liquid phase of the aqueous base prepared by the first step (method of phase transition from the W / O type to the O / W type) is applied. In the case of applying the method of phase change from the / W type to the W / O type, the liquid phase lacking long-term storage stability is obtained in the emulsified state of the O / W phase. Long-term storage stability is the best stability of the O / W type solubilizer prepared by applying the emulsion fire from the W / O type to O / W phase in the manufacturing state.
이어서, 다른 용기에 물 2549.1g 에 소듀움계 실리케이트(고형분 40%) 849.7g을 교반하면서 첨가한 후 30분 이상 교반하여 균일한 제3액상을 제조한다.Subsequently, 849.7 g of sodium silicate (solid content 40%) was added to 2549.1 g of water in another container with stirring, followed by stirring for 30 minutes or more to prepare a uniform third liquid phase.
소듀움계 실리케이트의 경우는 반드시 물에 교반하면서 실리케이트를 첨가하는 방법으로 제조하도록 한다. 이것은 고밀도 점조성의 액상을 물로 희석하는 경우 균일한 액상 제조가 어려우며, 희석 용해되지 않은 상태가 존재하게 된다.In the case of sodium silicate, the silicate should be prepared by adding silicate while stirring in water. It is difficult to prepare a uniform liquid when the liquid of high density viscous liquid is diluted with water, and the diluted undissolved state exists.
상기 수용화 제2액상을 1,500~1700rpm속도로 교반하면서 천천히 상기 제3액상을 드룹핑(속도 1.7 kg/min) 하여 혼합하여 본 발명에서 얻고자하는 W/O형의 수성형 표면 처리재를 얻는다.While stirring the second liquid phase at 1,500 to 1700 rpm, the third liquid phase is slowly drooped (rate 1.7 kg / min) and mixed to obtain a W / O type aqueous surface treatment material to be obtained in the present invention. .
상기 방법으로 희석한 다음 제2 및 제3단계에 의해 제조된 유화 액상은 높은 PH 조건에서는 불안정화되므로 반드시 희석 후 소량씩(1/4정도) 교반하면서 첨가하여 균일한 액상을 얻도록 한다.After dilution by the above method, the emulsion liquid prepared by the second and third steps is destabilized under high PH conditions, so it must be added with a small amount of stirring (about 1/4) after dilution to obtain a uniform liquid phase.
교반시간 : 제조상의 최적 조건을 얻기 위한 최소한의 시간.Stirring Time: The minimum time for obtaining optimum manufacturing conditions.
교반속도 : 제조 안정성상 가장 최적의 교반 효율을 얻을 수 있는 속도.Stirring Speed: The speed at which the most optimal stirring efficiency can be obtained in terms of manufacturing stability.
교반온도 : 상온에서 실시하는 것으로 온도 상승에 대한 특별한 냉각요소가 없다.Stirring temperature: It is conducted at room temperature and there is no special cooling element for temperature rise.
드룹핑 : 바람직하게는 1.7 kg/min 적하 속도로 한다.Drooping: Preferably it is 1.7 kg / min dripping speed.
C. 복합 방수시공방법C. Composite waterproof construction method
본 발명의 복합 방수시공방법은 상기한 콘크리트 표면 보호용 실리콘계 수성형 침투성 물 흡수 방지제와 도막 방수제를 사용한 복합 방수시공방법이다.The composite waterproof construction method of the present invention is a composite waterproof construction method using the above-described silicone-based aqueous permeable water absorption preventing agent and coating waterproofing agent for concrete surface protection.
특히 본 발명은 기존에 사용되던 방수 시공방법과 비교해보면 외적인 부분에서는 프라이머 시공후 도막방수제 시공이라는 시공법과 침투성 물 흡수 방지제 도포로 거의 유사하나, 본 발명의 가장 큰 특징인 침투성 물 흡수 방지제의 도포로 콘크리트 구조물에 방수, 방식 성능을 부여하여 모체 콘크리트의 내구연한을 향상시키며 구조물 크랙에 대한 추종성을 위하여 탄성도막방수층을 도포한 기능성 복합도막방수시공법을 제시하는데 있다.In particular, the present invention is almost similar to the coating method of coating film waterproofing agent and the coating of permeable water absorption inhibitor after the primer construction in the external part, compared with the conventional waterproofing method, which is the most characteristic of the present invention. To provide durability and anticorrosive performance to concrete structures to improve the durability of the parent concrete and to present a functional composite coating waterproofing method with an elastic coating waterproof layer applied for the track cracking.
2차 도막 방수제의 구성 성분은 바람직하게는 침투형 도포 방수제로 합성고분자 수지 에멀젼과 시멘트계 특수 조합 골재를 주원료로 이루어진 건축물 지하 토목용 제품을 사용하며, 따라서 이 경우 콘크리트 모체에 대한 우수한 접착력, 내후성, 내약품성, 내알카리성, 내열성, 내한성, 염소와 오존에 의한 내부식성, 내균열성, 내구성이 우수하며, 수용성이므로 환경 친화적이며 우수한 시공성을 가지고 있다.The component of the secondary coating waterproofing agent is preferably a penetration coating waterproofing agent, which is a building underground civil engineering product composed of synthetic polymer resin emulsion and cement-based special combination aggregate, and in this case, therefore, excellent adhesion, weather resistance, It has excellent chemical resistance, alkali resistance, heat resistance, cold resistance, corrosion resistance by chlorine and ozone, crack resistance and durability, and is water-soluble, so it is environmentally friendly and has excellent workability.
또한 본 복합 공법에 적용되는 상부 2차 방수층은 다양한 재료 적용성을 가지고 있으므로, 무기질계 탄성 도막방수제, 시멘트 혼입 폴리머계, 수용성 1액형 도막재, 수용성 우레탄계 도막방수제, 수용성 에폭시계 방식, 방청 도막재 등의 다양한 적용이 가능하다.In addition, the upper secondary waterproof layer applied in the present composite method has a variety of material applicability, so the inorganic elastic coating waterproofing agent, cement mixed polymer type, water-soluble one-part coating material, water-soluble urethane coating film waterproofing agent, water-soluble epoxy method, rustproof coating material Various applications are possible.
상기 2차 방수층은 규산질계 도포방수제, 침투성 도포방수제, 슬러리형 방수제, 수용성 우레탄, 수용성 에폭시, 아크릴 고무계, 우레탄 고무계, 클로로프렌 고무계, 고무 아스팔트계, 실리콘 고무계 중 어느 하나 또는 아스팔트 시트, 개량 아스팔트 시트, 합성고분자 시트, EPDM 시트 중 어느 하나를 사용하는 것도 가능하다.The secondary waterproof layer is a siliceous coating waterproofing agent, permeable coating waterproofing agent, slurry type waterproofing agent, water-soluble urethane, water-soluble epoxy, acrylic rubber-based, urethane rubber-based, chloroprene rubber-based, rubber asphalt-based, silicon rubber-based or asphalt sheet, improved asphalt sheet, It is also possible to use either synthetic polymer sheet or EPDM sheet.
상기에서 언급한 것처럼 본 발명의 침투성 물 흡수 방지제를 사용한 복합도막방수 시공방법은 먼저 모체 콘크리트에 도포하여 콘크리트 표면으로부터 깊이 침투하여 방수효과를 발휘하며 수증기 투과성이 있어 모체의 내구성을 향상시키고 콘크리트 구조물의 수명을 좌우하는 내부의 철근의 부식을 방지하여 모체 구조물의 강도 유지를 통한 내구성 향상과 시멘트계 도막재를 적용함으로써 방수성능과 구조체 안정화, 내구년한 향상을 도모할 수 있다.As mentioned above, the composite coating waterproofing method using the permeable water absorption preventing agent of the present invention is first applied to the mother concrete to penetrate deeply from the concrete surface to exhibit a waterproofing effect, and the water vapor permeability improves the durability of the mother body and improves the durability of the concrete structure. By preventing the corrosion of the internal reinforcing steel, which affects the service life, it is possible to improve the durability by maintaining the strength of the parent structure and to apply the cement-based coating material to achieve the waterproof performance, the structure stabilization, and the durability improvement.
(실시예)(Example)
이하에 상기한 본 발명을 바람직한 실시예를 참고하여 더욱 상세하게 설명한다.Hereinafter, the present invention will be described in more detail with reference to preferred embodiments.
제조예Production Example
물 1,000g에 폴리비닐알콜 (예 PVA-224, Kuraray社) 17.17g을 첨가 후 3000rpm으로 교반한 다음 에멀션화제 (예 Span 80, ICI社) 4.21g 을 첨가하여 2,000rpm으로 20분간 교반하여 제1액상을 준비한다.17.17 g of polyvinyl alcohol (eg PVA-224, Kuraray) was added to 1,000 g of water, followed by stirring at 3000 rpm, followed by addition of 4.21 g of emulsifier (eg Span 80, ICI) for 20 minutes at 2,000 rpm. Prepare the liquid.
이어서, 다른 용기에 옥틸트리에톡시실란/실록산(octyl-tri-ethoxy silan/siloxane ; 예 Wacker社) 2,583.4g에 에멀션화제 4.21g 을 첨가하여 2,000rpm으로 20분간 교반하여 제2액상을 준비한 다음, 상기 제1액상에 1700rpm속도로 교반하면서 천천히 드룹핑하여 수용화 제3액상을 제조한다.Subsequently, 4.21 g of an emulsifier was added to 2,583.4 g of octyl-tri-ethoxy silan / siloxane (e.g. Wacker) in another vessel, and stirred at 2,000 rpm for 20 minutes to prepare a second liquid phase. The first liquid phase was dripped slowly while stirring at a speed of 1700 rpm to prepare a solubilized third liquid phase.
그후 다른 용기에 물 2549.1g 에 Sodium계 Silicate (고형분 40%) 849.7g을30분 이상 교반하여 균일한 제4액상을 제조한다. 상기 수용화 제3액상을 1700rpm속도로 교반하면서 천천히 상기 제4액상을 드룹핑(Drooping)하여 혼합하여 본 발명에서 얻고자 하는 1차 표면 처리재를 얻는다.Thereafter, 849.7 g of sodium Silicate (40% solids) in 2549.1 g of water was stirred in another container for 30 minutes or more to prepare a uniform fourth liquid phase. The aqueous third liquid phase is dripped at the rate of 1700 rpm and slowly mixed with the fourth liquid phase to obtain a primary surface treatment material to be obtained in the present invention.
실시예 1-5 및 비교예 1-4Example 1-5 and Comparative Example 1-4
제조예와 같은 방법으로 실시예 1,2,3,4,5와 비교예 1,2,3,4를 하기 표 1과 같이 제조하여 하기 표 2와 같이 시험을 실시하였다.In the same manner as in Preparation Example 1, 2, 3, 4, 5 and Comparative Examples 1, 2, 3, 4 were prepared as shown in Table 1 and tested as shown in Table 2 below.
실시예 및 비교예 적용을 위한 제조시 비교예 1의 경우는 유화 불균형에 의해, 표면 유분 부유현상이 발생하여 추가적인 시험을 실시하지 않았다.In the case of Comparative Example 1 in the preparation for the application of Examples and Comparative Examples, surface oil flotation occurred due to emulsion imbalance, and no further tests were performed.
시험방법Test Methods
① 유화상태 육안 검사방법으로 유화제조후 100g의 물에 제조액상을 2-3 방울 적하(滴下)하여 물에 퍼지는 상태 확인하여 판정하였다.① Emulsification state After visual inspection method, 2-3 drops of the manufacturing liquid phase was added dropwise to 100 g of water after emulsification, and it was determined by checking the state of spreading in water.
② 저장안정성은 상온에서의 6개월 저장안정성과 항온항습설비내 온도 60℃에서 8시간 20℃에서 16시간을 1 사이클(cycle)로 설정하여 30 사이클 이후 표면 및 내부 저장상태를 확인하여 판정하였다.② Storage stability was determined by checking the surface and internal storage condition after 30 cycles by setting 6 months storage stability at room temperature and 16 hours at 60 ℃ for 8 hours at 20 ℃ and 16 hours at constant temperature and humidity.
③ 침투깊이는 "침투성 흡수 방지재의 시험방법(안)" 중 침투 깊이 시험방법 <일본 공업 기술 진흥 협회(Polymers in concrete) 위원회>를 적용하여 시험체 도포 양생 후 시험체를 2분할하고, 그 단면에 물을 분무하여 물이 침투하지 않는 부분의 깊이를 버니어 캘리퍼스로 측정한다. 측정은 3개 시험체에 대하여 3개소에서 실시하여 이들의 평균값을 침투 깊이로 한다.③ The penetration depth is the penetration depth test method of "Test Method of Penetrable Absorption Absorption Material". <Polymers in Concrete Committee> is applied, and the test body is divided into two parts after curing of the test object. Spray the water and measure the depth of the part where water does not penetrate with a vernier caliper. The measurement is carried out at three places on three test specimens and their average value is defined as penetration depth.
④ 흡수비, 투수비 시험은 KS F 2451 건축용 시멘트 방수제 시험방법에 준하여 실시하였다.④ Absorption ratio and permeability ratio test were conducted in accordance with KS F 2451 building cement waterproofing test method.
⑤ 압축강도비 시험은 KS F 2477 폴리머 시멘트 모르타르의 강도시험 방법에 준하여 실시하였다.⑤ Compressive strength ratio test was conducted according to the strength test method of KS F 2477 polymer cement mortar.
⑥ 부착강도시험은 현장 부착력 시험기계인 건연식 부착력 시험기를 사용하여 도막재 도포 양생 후 막간 부착력을 측정하였다.⑥ The bond strength test was carried out using a dry adhesion tester, a field adhesion test machine, to measure the interlayer adhesion force after coating film curing.
시험실시결과Test result
실시예 조건에 만족하는 경우에 상기 표 2와 같이 본 발명에서 얻고자하는 물성값을 제시하고 있다. 가장 중요한 특성으로는 제품의 저장안정성부분으로 결과에서처럼 모든 예에서 정도의 차이는 있으나 단일재료보다 향상된 성능을 나타내고 있으나, 제품의 적용 특성상 저장안정성능이 우선적으로 검토되어야할 사항이다. 저장안정성의 경우는 장기적 안정성과 촉진 안정성을 확인한 결과 실시예 1,2,3,4,5의 경우는 안정한 상태로 유지하였으나 비교예의 경우 특성 평가를 위한 재료 첨가량 설정으로 안정성이 부족한 것으로 나타났다.In the case of satisfying the Example conditions, the physical properties to be obtained in the present invention are presented as shown in Table 2 above. The most important characteristic is the storage stability of the product. As shown in the results, although there is a difference in the degree in all examples, it shows the improved performance over the single material, but the storage stability performance should be considered first because of the application characteristics of the product. In the case of storage stability, as a result of confirming long-term stability and promotion stability, in Examples 1, 2, 3, 4 and 5, it was maintained in a stable state, but in case of Comparative Example, it was found that the stability was insufficient due to the amount of material added for evaluation of properties.
침투깊이 시험결과 실시예의 경우 도 1과 같이 최소 2.3mm 이상의 침투깊이를 균일한 형태를 가지고 있는 반면, 비교예의 경우 최대 2.4mm 이하의 침투력을 보이고 있다. 이것은 옥틸트리에톡시실란/실록산의 함량에 따른 영향도 있으나 비교 실시예 결과 적정 유화제 이외의 경우와 과도한 함량의 강도보호재를 첨가함으로써 옥틸트리에톡시실란/실록산의 침투력을 저하시킨 결과로 판단이 된다.Penetration depth test results In the case of the embodiment has a uniform depth of at least 2.3mm or more as shown in Fig. 1, while the comparative example shows a maximum penetration of 2.4mm or less. This may have an effect depending on the content of octyl triethoxysilane / siloxane, but it is judged that the result of lowering the penetration of octyl triethoxysilane / siloxane by the addition of an excessive amount of strength protective material and the case other than the appropriate emulsifier as a result of the comparative example .
특히, 강도 보호재의 함량은 강도 향상을 위한 실리케이트 재료로서 옥틸트리에톡시실란/실록산보다 우수한 침투력을 가진 것으로 일반적으로 알려져 있으나 일정 비율 혼합해서 사용하는 경우 침투력의 저하를 수반하는 것으로 나타났다. 일반적으로 공극 충진형 강도 향상제 적용시 겔화를 통하여 진행되므로 옥틸트리에톡시실란/실록산의 침투력을 저해함을 알 수 있다.In particular, the content of the strength protective material is generally known to have better penetration than octyltriethoxysilane / siloxane as a silicate material for improving the strength. In general, it can be seen that the application of the pore-filling strength enhancer inhibits the penetration of octyltriethoxysilane / siloxane because it proceeds through gelation.
침투 깊이는 도포되는 량에 의해 영향을 받고 있으며, 특히, 동일한 량을 2-3회 적정 횟수를 도포하는 것이 침투력 향상에 영향을 주는 것으로 나타났다.The penetration depth is influenced by the amount applied, and in particular, applying the same amount 2-3 times has been shown to affect the penetration.
압축강도의 경향은 실리케이트의 함량이 증가함에 따라 상승하는 경향이 있으며, 크림타입에 대한 시험결과 최대 105% 최소 101%로 나타났다.The compressive strength tends to increase as the silicate content increases, with a maximum of 105% and a minimum of 101% for the cream type test.
압축강도의 경우 기존 콘크리트 또는 구조체에 침투성 물 흡수 방지제 도포시 강도저하 현상은 없으며, 실리케이트의 함량 증가에 따른 강도 상승 효과를 부분적으로 부여할 수 있다.In the case of the compressive strength, there is no decrease in strength when the permeable water absorption inhibitor is applied to the existing concrete or the structure, and the strength increase effect may be partially provided by increasing the content of silicate.
기존 시판되고 있는 제품의 유형별 물성 시험결과를 보면 다음 표 5와 같다.The results of the physical property test by type of existing commercial products are shown in Table 5 below.
시험체 : 본 발명의 침투성 물 흡수 방지제 도포후 각종 방수제 도포Test body: Applying various waterproofing agent after applying the permeable water absorption preventing agent of the present invention
시험항목 : 부착성능Test Item: Attachment Performance
시험방법 : KS F 4715의 5.8 부착강도시험방법에 준한다.Test method: According to 5.8 Bond strength test method of KS F 4715.
본 발명의 방수제 도포 후 부착성능은 도포전의 상태보다 최소 25%, 최대33% 향상된 성능을 나타내고 있다. 이것은 기존 방수재료도포시 계면 접착력 저하에 따른 다음 공정 진행 여부 및 이후 공정에 의한 상부1차 방수층의 이탈현상에 의한 방수성능 저하가 없다는 것을 의미하며, 바탕면 하부에 작용하는 수압에 의한 저항성을 판단하는 투수비의 경우 기존 재료 대비 33% 정도 낮으므로써 외부 수압 및 계면 부착력의 성능상 기존 재료보다 우수한 것으로 나타났다.The adhesion performance after applying the waterproofing agent of the present invention is at least 25%, up to 33% improved performance than the state before application. This means that there is no deterioration in the waterproofing performance due to the separation of the upper primary waterproofing layer by the subsequent process and the subsequent process due to the decrease of the interfacial adhesive force when the existing waterproofing material is applied. The permeability ratio is about 33% lower than that of existing materials, which is superior to existing materials in terms of external hydraulic pressure and interface adhesion.
시험항목 : 흡수비Test Item: Absorption Ratio
시험방법 : KS F 2451 흡수성시험방법(28일 양생)Test Method: KS F 2451 Absorption Test Method (28 days curing)
시험항목 : 투수비Test item: pitching cost
시험방법 : KS F 2451 투수성시험방법Test Method: KS F 2451 Permeability Test Method
흡수비가 매우 우수하여 수압을 받지 않는 곳에서는 방수 성능이 우수하게 나타나고 있으며, 투수비는 흡수비에 비하여 상대적으로 떨어지나 다른 방수제에 비하여 우수하여 지하나 토목 구조물에 사용이 적합한 특징을 가지고 있다. 매우우수한 침투깊이를 가지므로 콘크리트 내부의 철근을 부식으로부터 막아주며 결과적으로 구조물의 수명을 연장시켜 방수 품질을 극대화시킨다.Absorption ratio is very good and waterproof performance is excellent in places without receiving water pressure. Permeability ratio is relatively lower than absorption ratio, but it is superior to other waterproofing agents, and it is suitable for use in underground or civil engineering structures. It has a very good penetration depth to prevent reinforcing bars in concrete from corrosion and consequently extends the life of the structure to maximize waterproof quality.
시험항목 : 압축강도비Test item: Compressive strength ratio
시험방법 : KS F 2477Test Method: KS F 2477
압축강도시험결과 기존의 재료가 적용된 경우 적용 전에 비해 전반적으로 약 10% 이상 저하를 수반하고 있으나 본 발명 적용재료의 경우 기존의 강도 이상을 유지하면서 흡수 방지성능을 가진 것으로 판단할 수 있다.As a result of the compressive strength test, when the existing material is applied, the overall material is about 10% or more lower than before application. However, the applied material of the present invention can be judged to have an absorption preventing performance while maintaining the existing strength or more.
시험항목 : 침투깊이시험Test item: Penetration depth test
시험 방법 : "침투성 흡수 방지재의 시험방법(안)" 중 침투 깊이 시험방법Test method: Penetration depth test method in "Test method of penetrable absorption prevention material"
일본 공업 기술 진흥 협회(Polymers in concrete 위원회)Japan Industrial Technology Association (Polymers in concrete committee)
침투 깊이 시험은 시료를 도포한 시험체를 2분할하고, 그 단면에 물을 분무하여 물이 침투하지 않는 부분의 깊이를 버니어 캘리퍼스로 측정한다.The penetration depth test divides the test object which apply | coated the sample into 2 parts, and sprays water on the cross section, and measures the depth of the part which water does not penetrate with a vernier caliper.
측정은 3개 시험체에 대하여 3개소에서 실시하여 이들의 평균값을 침투 깊이로 한다.The measurement is carried out at three places on three test specimens and their average value is defined as penetration depth.
침투깊이의 경우 기존 재료의 경우는 시각적인 판단이 상당히 어려우며, 전자주사현미경등의 장비를 사용하여야 구조체에 침투된 경향을 파악할 수 있는 반면, 본 발명의 경우는 물에 침적하는 간단한 실험을 통하여 침투된 정도를 확인할 수 있는 장점이 있으며, 시험결과를 보면 최소 2 mm 이상의 침투성능을 가지고 있으므로 우수한 방수 및 수밀 특성을 가지고 있다고 판단할 수 있다.In the case of the depth of penetration, it is difficult to visually judge the existing materials, and it is possible to identify the tendency to penetrate the structure only by using equipment such as an electron scanning microscope, whereas in the case of the present invention, the penetration is carried out through a simple experiment in which water is deposited. It has the advantage of confirming the degree to which it is made, and from the test results, it can be judged that it has excellent waterproof and watertight characteristics because it has a penetration performance of at least 2 mm.
상기 표 5 내지 표 9에서 본 발명과 대비되는 종래기술의 측정 데이터의 제시예 1)은 방수제 표준화 연구(Ⅳ) 2000.10 산업자원부기술표준원 발행자료이고, 제시예 2)는 규산질계 분말형 도포방수재의 방수특성과 성능에 관한 연구 서울산업대학교 산업대학원 건축공학과 1998년도 공학석사 학위 논문집이다.In Table 5 to Table 9, Example 1 of the measurement data of the related art compared with the present invention is a standard for waterproofing agent standardization (IV) 2000.10, published by the Ministry of Commerce, Industry and Energy, and Standard 2, and Example 2) of the siliceous-based powder coating waterproofing material. A Study on the Waterproof Characteristics and Performance This is a 1998 dissertation of the Master of Engineering, Seoul National University of Technology.
시공 방법Construction method
상기 제조된 조성물에 의한 1차 처리 후 시멘트계 도막방수제의 2차 처리 방법은 다음에 준한다.The secondary treatment method of the cement-based coating waterproofing agent after the primary treatment by the prepared composition is as follows.
a. 바탕면 청소-이물질, 레이턴스( Laitance ) 제거a. Substrate Cleaning-Remove Foreign Matter, Laitance
b. 바탕면 충분히 건조시킨 후 ( 20 % 내외 함수율 가능) 본 발명 조성물 도포 (2회)b. After the base surface is sufficiently dried (water content of about 20% is possible), the composition of the present invention is applied (twice)
c. 도막방수재 도포c. Coating waterproofing material
본 발명은 1차 구조물의 안전화 및 내구성 향상을 목적으로 침투성 물 흡수 방지제를 도포하여 내부적인 방수하자 요인으로 받아드려지고 있는 수분 침투와 동결융해 작용에 의한 구조체의 손상, 지속적인 구조체의 움직임과 내부 수분의 수층 팽창 등으로 방수층의 부풀음, 파단으로 이어지는 2차 방수층 하자로 이어지는 원인을 도막방수층을 도포함으로써 제거하였다.The present invention applies a permeable water absorption inhibitor for the purpose of improving the safety and durability of the primary structure, damage to the structure due to moisture infiltration and freeze-thawing action, which are accepted as internal waterproof defect factors, continuous movement of the structure and internal moisture The cause of the secondary waterproof layer defect leading to swelling and breakage of the waterproof layer due to expansion of the aqueous layer and the like was eliminated by applying the coating waterproof layer.
본 발명에서 1차 구조물의 안전화 및 내구성을 확보하여 구조체 자체의 노화 및 열화요인으로부터 최대한 보호하여 구조물에 의한 방수의 근본적인 문제점을 해결할 수 있는 개념을 바탕으로 하고 있으므로, 기존 방수재료의 한계점으로 인식되고 있는 구조체 하자에 의한 방수 성능의 저하를 침투성 물 흡수 방지제를 도포함으로써 방지할 수 있게 되었다.In the present invention, it is recognized as a limitation of the existing waterproofing material because it is based on the concept of solving the fundamental problem of waterproofing by the structure by securing the safety and durability of the primary structure to the maximum protection from the aging and deterioration factors of the structure itself. The fall of the waterproof performance by the defective structure of the present structure can be prevented by applying a permeable water absorption inhibitor.
더욱이 기존 침투성 방수재료의 특성상 침투부분에 대한 명확한 판정 및 검증이 어려운 부분들을 본 발명에서는 방수 품질 관리 차원에서 정밀한 장비 없이 간단히 확인할 수 있는 실용성을 가지고 있으며, 기존의 침투성 방수제와는 차별화될 수 있는 부분으로 유용성 재료의 특성을 가지면서 동시에 수용화 기술을 개발함으로서 최근 확산되고 있는 환경 친화적 경향에 적극적으로 대처하는 경제성을 포함한 재료적용으로 시공성에서 보다 안전한 재료로 적용이 가능하다.Furthermore, in the present invention, the parts that are difficult to clearly determine and verify the permeated part due to the characteristics of the existing permeable waterproof material have practicality that can be easily identified without precise equipment in terms of waterproof quality control, and can be differentiated from the existing permeable waterproofing agent. In addition, it is possible to apply it as a safer material in constructability by applying materials including economics that actively cope with the recently spreading environmentally friendly tendency by having the characteristics of useful materials and developing an acceptance technology.
본 발명은 1차 침투성 물 흡수 방지제와 2차 시멘트계 도막방수층을 형성시킴으로서 각 재료의 단점인 크랙에 대한 추종성 부족, 바탕면의 상태에 따른 다양한 하자 요인들을 동시에 대처할 수 있어 방수성능 및 기술개발에 촉진제 역활을 할 것으로 판단된다.The present invention forms the primary permeable water absorption inhibitor and the secondary cement-based waterproofing layer to cope with various defects depending on the condition of the ground, the lack of trackability for cracks, which are the disadvantages of each material, and the accelerator for waterproofing performance and technology development. It is expected to play a role.
본 발명의 침투성 물 흡수 방지제는 다음과 같은 특성을 가지고 있다.The permeable water absorption inhibitor of the present invention has the following characteristics.
① 강력한 침투성능.① Strong penetration performance.
② 실란/실록산에 의한 견고한 실리콘 레진 네트웍(망상구조) 형성으로 알칼리 저항성, 흡수방지성능 우수.② Excellent alkali resistance and absorption prevention performance by forming solid silicone resin network (network structure) by silane / siloxane.
③ 우수한 수증기 투과성능.③ Excellent water vapor transmission performance.
④ 결빙(동해)/제설제 염에 대한 저항성 우수.④ Excellent resistance to freezing (Donghae) / snow removing salt.
⑤ 수용성의 환경 친화적인 적용성.⑤ Environmentally friendly applicability of water soluble.
⑥ 크림형태의 경우 요변성의 고유동화 특성으로 작업에 따라 손실량 절감효과.⑥ In the case of cream type, it has a thixotropic high liquefaction characteristic, which reduces the amount of loss according to work.
⑦ 우수한 부착력.⑦ Excellent adhesion.
⑧ 낮은 휘발성에 의한 방수층의 들뜸 현상 방지.⑧ Prevent the floating layer from rising due to low volatility.
⑨ 화학적 부식 환경에 대한 저항성(방식성)을 부여하여 구조물의 내구성 향상.⑨ It improves the durability of the structure by giving resistance to corrosion environment (corrosion).
이상에서는 본 발명을 특정의 바람직한 실시예를 예를 들어 도시하고 설명하였으나, 본 발명은 상기한 실시예에 한정되지 아니하며 본 발명의 정신을 벗어나지 않는 범위내에서 당해 발명이 속하는 기술분야에서 통상의 지식을 가진 자에 의해 다양한 변경과 수정이 가능할 것이다.In the above, the present invention has been illustrated and described with reference to specific preferred embodiments, but the present invention is not limited to the above-described embodiments, and the present invention is not limited to the spirit of the present invention. Various changes and modifications will be possible by those who have the same.
Claims (6)