KR100385788B1 - High strength cement composition comprising pozzolan as main material and manufacture device therefor - Google Patents
High strength cement composition comprising pozzolan as main material and manufacture device therefor Download PDFInfo
- Publication number
- KR100385788B1 KR100385788B1 KR10-2002-0007490A KR20020007490A KR100385788B1 KR 100385788 B1 KR100385788 B1 KR 100385788B1 KR 20020007490 A KR20020007490 A KR 20020007490A KR 100385788 B1 KR100385788 B1 KR 100385788B1
- Authority
- KR
- South Korea
- Prior art keywords
- fly ash
- weight
- powder
- mixed
- storage unit
- Prior art date
Abstract
본 발명은 상압의 증기양생 또는 일반 레미콘에 적용되는 고강도 시멘트 혼화재의 조성물과 그 제조장치로서, 특히 플라이 애쉬, 슬래그 미분말 등의 산업폐기물계 포졸란(pozzolan) 재료를 주재로 하고, 여기에 무수석고와 팽창제 및 유동화제를 일정량 함유시킴으로 포졸란의 조기 활성이 가능하고, 강도 및 내구성과 유동성의 증진은 물론 건조후의 수축 감소로 품질의 항상성이 유지되는 고품질의 2차 시멘트 제품 생산을 위한 포졸란 재료를 주재로 한 시멘트 혼화재 조성물과 그 제조장치인바, 이를 위하여 본 발명의 조성물은 4000∼6000㎠/g의 분말도를 유지하는 플라이 애쉬 83∼96중량%; 4000∼6000㎠/g의 분말도를 유지하는 슬래그 미분말 3∼6중량%; 4000∼5000㎠/g의 분말도를 유지하는 무수석고 0.1∼5중량%; 팽창제 0.5∼6중량%; 및 유동화제 0.5∼2중량%로 이루어짐과;The present invention is a composition of a high-strength cement admixture applied to normal pressure steam curing or general ready-mixed concrete, and a manufacturing apparatus thereof, which is mainly based on industrial waste-based pozzolan materials such as fly ash and slag fine powder. By containing a certain amount of swelling agent and fluidizing agent, it is possible to prematurely activate pozzolanic, and to improve the strength, durability and fluidity, and to reduce the shrinkage after drying, it is mainly based on pozzolanic material for producing high quality secondary cement products. One cement admixture composition and its manufacturing apparatus, for which the composition of the present invention is 83 to 96% by weight fly ash to maintain a powder degree of 4000 ~ 6000 cm 2 / g; 3 to 6% by weight of fine slag powder to maintain a powder degree of 4000 to 6000 cm 2 / g; 0.1-5% by weight of anhydrous gypsum having a powder degree of 4000-5000 cm 2 / g; 0.5-6% by weight of expanding agent; And 0.5 to 2% by weight of a fluidizing agent;
그 제조장치는 수집된 플라이 애쉬가 투입 저장된 채 임의의 배출양 조절이 가능한 제 1저장부; 배출된 플라이 애쉬를 수용하여 이를 4000㎠/g 이상의 고분말로 정제하기 위한 분급기; 정제된 플라이 애쉬가 이송되어 투입되는 원심분리기; 슬래그 미분말, 무수석고, 팽창제 및 유동화제 등의 부원료가 각기 별도로 저장된 채 적량 배출될 수 있도록 한 제 2저장부; 배출된 부원료의 투입량 산정을 위한 제 1계량기; 계량을 거친 부원료의 고른 혼합을 위한 제 1혼합기; 상기 혼합재료의 이송을 위한 제 1버킷 엘리베이터; 버킷 엘리베이터를 통해 이송된 혼합재료가 저장되는 제 3저장부; 상기 원심분리기를 거친 플라이 애쉬의 투입량 산정을 위한 제 2계량기; 상기 계량을 거친 플라이 애쉬와 제 3저장부를 거친 혼합재료가 일정 비율로 배합되는 제 2혼합기; 배합물의 이송을 위한 제 2버킷 엘리베이터; 배합물의 재 혼합을 위한 제 3혼합기; 재 혼합물의 저장을 위한 제 4저장부; 및 제 4저장부를 통해 완성된 저장물이 배출되어 출하될 수 있도록 배출슈트가 구비되어 이루어지는 것이다.The manufacturing apparatus includes a first storage unit capable of adjusting any discharge amount while the collected fly ash is input and stored; A classifier for accommodating the discharged fly ash and purifying it with a high powder of 4000 cm 2 / g or more; A centrifuge to which the purified fly ash is transferred and introduced; A second storage unit configured to discharge a small amount of auxiliary materials such as fine slag powder, anhydrous gypsum, an expanding agent, and a fluidizing agent, respectively and stored separately; A first meter for calculating an input amount of the discharged subsidiary material; A first mixer for even mixing of the weighed minor ingredients; A first bucket elevator for conveying the mixed material; A third storage unit for storing the mixed material transferred through the bucket elevator; A second meter for estimating the input amount of the fly ash passed through the centrifuge; A second mixer in which the mixed ash that has passed through the weighing and the third storage portion have been mixed in a predetermined ratio; A second bucket elevator for conveying the formulation; A third mixer for remixing the blend; A fourth reservoir for storing the ash mixture; And a discharge chute provided so that the completed storage is discharged and shipped through the fourth storage unit.
Description
본 발명은 상압의 증기양생 또는 일반 레미콘에 적용되는 고강도 시멘트 혼화재의 조성물과 그 제조장치에 관한 것이다.The present invention relates to a composition of a high-strength cement admixture applied to steam curing at normal pressure or a general ready-mixed concrete and its manufacturing apparatus.
특히, 본 발명의 혼화재 조성물은 플라이 애쉬, 슬래그 미분말 등의 산업폐기물계 포졸란(pozzolan) 재료를 주재로 하고, 여기에 무수석고와 팽창제 및 유동화제를 일정량 함유시킴으로 포졸란의 조기 활성이 가능하고, 강도 및 내구성과 유동성의 증진은 물론 건조후의 수축 감소로 품질의 항상성이 유지되는 고품질의 2차 시멘트 제품 생산을 위한 포졸란 재료를 주재로 한 시멘트 혼화재 조성물과 그 제조장치이다.In particular, the admixture composition of the present invention is based on industrial waste-based pozzolan materials such as fly ash and slag fine powder, and contains an amount of anhydrous gypsum, a swelling agent, and a fluidizing agent, thereby enabling early activation of pozzolanic and strength. And cement admixture compositions based on pozzolanic materials for the production of high quality secondary cement products in which the homeostasis of quality is maintained by improving the durability and fluidity as well as reducing shrinkage after drying.
한편, 본 발명은 출원인에 의해 선 출원되어 등록된 대한민국 특허등록 제 300008호“포졸란 재료를 주성분으로 하는 레미콘 전용 시멘트 혼화재 조성물”에 후속되는 개량발명의 성격을 유지한다.On the other hand, the present invention maintains the characteristics of the improved invention followed by the Republic of Korea Patent Registration No. 300008 "Premixed Cement admixture composition based on pozzolan material" that is pre- filed by the applicant.
일반적으로, 시멘트 혼화재는 레미콘 등 2차 시멘트 제품의 성능향상을 위해 사용되는 것으로, 주로 시멘트의 사용량을 줄이면서 콘크리트의 고강도 발현, 화학 및 동결융해의 저항성 증대에 따른 내구성 향상, 수화열에 의한 콘크리트의 균열방지와 그에 따른 저발열성 콘크리트의 제조 등을 위해 제공된다.In general, cement admixtures are used to improve the performance of secondary cement products such as ready-mixed concrete. The cement admixture is mainly used for reducing the amount of cement and improving the durability by increasing the strength of concrete, resistance to chemical and freeze-thawing, and It is provided for the prevention of cracking and the production of low heat concrete accordingly.
이때, 상기 혼화재로는 종래 실리카흄, 메타카올린, CSA계(Calcium Sulpho-Aluminate)의 클링커나 에트링자이트 및 Ca(OH)2의 팽창성 혼화재가 사용되었으나 제품의 단가상승과 팽창성분에 따라 수화 경화체의 조직 붕괴가 우려되어 요구되는 강도와 내구성의 저하를 수반한다는 문제점을 포함하고 있었다.At this time, as the admixture, a conventional silica fume, metakaolin, CSA (Calcium Sulpho-Aluminate) clinker or ettringite and Ca (OH) 2 expandable admixtures were used. The problem of tissue collapse is a concern, and it involves the problem of accompanied by a decrease in the required strength and durability.
따라서, 최근에는 상기 선출원 등록된 발명에서와 같이 포졸란계의 산업폐기물인 플라이 애쉬, 슬래그 미분말, 폐제올라이트 등을 혼화재로 사용하여 산업폐기물의 재활용을 도모하면서도 단가의 저감과 콘크리트 제품의 장기강도 및 내구성의 향상을 구현하기 위해 초기 강도의 상승과 시멘트의 치환량을 낮추기 위한 최적의 분말도를 산정하여 7000∼10000㎠/g의 분말도를 갖는 어느 1종의 포졸란 물질 10∼20중량%와, 3000∼4500㎠/g의 분말도를 갖는 플라이 애쉬 40∼50중량% 및 3000∼4500㎠/g의 분말도를 갖는 슬래그 미분말 40∼50중량%를 포함하는 시멘트 혼화재 조성물을 특정하여 제안한 바 있으나, 2차 시멘트 제품을 위한 상압의 증기양생에서 상기 포졸란계 재료의 압축강도가 낮아진다는 문제점이 표면화되었고, 이는 대한민국 공개특허번호 제2000-7099호에서 설명된 바와 같다.Therefore, in recent years, such as fly ash, slag fine powder, and waste zeolite, which are pozzolan-based industrial wastes as admixtures, as a mixed material, it is possible to reduce industrial costs and reduce long-term strength and durability of concrete products. 10-20% by weight of any one type of pozzolanic substance having a powder degree of 7000-10000 cm 2 / g, and 3000- Although a cement admixture composition comprising 40-50 wt% of fly ash having a powder degree of 4500 cm 2 / g and 40-50 wt% of slag fine powder having a powder degree of 3000-4500 cm 2 / g has been specifically proposed, the secondary The problem that the compressive strength of the pozzolanic material is lowered in the steam curing at atmospheric pressure for cement products has been surfaced, which is Korean Patent Publication No. 2000-7099. As described in
때문에, 상기의 표면화된 문제점을 해결하기 위한 방안으로 포졸란 재료에 에트린자이드 생성과 그에 따른 시멘트 경화제의 공극 충진으로 일정한 강도가 유지될 수 있도록 무수석고를 배합한 혼화재가 제안되었으며, 이러한 선행기술은 위 언급된 선출원 공개특허와 그 이전에 출원된 대한민국 공개특허번호 제1996-37607호를 통해 충분히 확인될 수 있다.Therefore, in order to solve the above-mentioned surface problem, admixtures containing anhydrous gypsum have been proposed to maintain constant strength due to the formation of ethrinzide and pore filling of cement hardener according to the pozzolanic material. It can be sufficiently confirmed through the above-mentioned prior application published patent and the Republic of Korea Patent Publication No. 1996-37607 filed previously.
그러나, 이와 같은 선행기술 역시 동/하절기의 기온 편차에 대한 적응성이 낮아 시공에 적지 않은 차질을 초래하였던 바 이는 각 구성물질의 분말도와 배합치의 부적정에 기인된 것임을 확인하였다.However, this prior art also has a low adaptability to the temperature fluctuations during the winter / summer season caused a lot of disruptions in construction, it was confirmed that this is due to the inadequateness of the powder and blending value of each component.
따라서, 본 발명은 포졸란 재료 중 특히 플라이 애쉬를 주 원료로 2차 시멘트 제품의 기능성 보장을 위해 마련되는 구성물질의 적절한 배합으로 품질의 항상성이 유지될 수 있는 혼화재 조성물을 제안한다.Accordingly, the present invention proposes a miscible composition in which the homeostasis of quality can be maintained by appropriate blending of pozzolan materials, in particular fly ash, as a main raw material, to ensure the functionality of the secondary cement product.
주지하다시피, 플라이 애쉬는 상당량의 미연 탄소분과 철분을 포함하고 있어이를 시멘트 혼화재로 활용할 경우의 유용성은 매우 큰 것으로 이는 이미 검증된 사실이다.As is well known, fly ash contains significant amounts of unburned carbon and iron, which has proved to be very useful when used as a cement admixture.
상기의 제안에 따라 안출되는 본 발명의 목적으로는 본 출원인의 선 출원 발명의 목적인 혼화재의 단가상승 억제와 포졸란의 조기 활성을 가능케하고 동시에 혼화재의 시멘트 치환량에 대한 증가를 포함하면서 강도 및 내구성과 유동성의 증진을 기하고, 건조후의 수축 감소로 품질의 균일화와 항상성 유지를 통해 고품질의 2차 시멘트 제품을 제공하기 위함에 있다.The object of the present invention devised in accordance with the above proposal is to provide the strength and durability and fluidity of the present invention, including the increase in the amount of cement substitution of the admixture while at the same time enabling the suppression of unit cost rise of admixtures and the early activation of pozzolans. The purpose is to provide a high quality secondary cement product through uniformity of quality and maintenance of homeostasis by reducing shrinkage after drying.
도 1은 본 발명 제조장치의 전체적인 구성상태를 도시해 보인 예시도.1 is an exemplary view showing the overall configuration of the manufacturing apparatus of the present invention.
*주요부분에 대한 부호의 설명** Explanation of symbols for main parts *
1 : 제 1저장부 2 : 분급기1: first storage unit 2: classifier
3 : 원심분리기 4 : 제 2저장부3: centrifuge 4: second reservoir
5 : 제 1계량기 6 : 제 1혼합기5: 1st meter 6: 1st mixer
7 : 제 1버킷 엘리베이터 8 : 제 3저장부7: first bucket elevator 8: third storage
9 : 제 2계량기 10 : 제 2혼합기9: second meter 10: second mixer
11 : 제 2버킷 엘리베이터 12 : 제 3혼합기11: second bucket elevator 12: third mixer
13 : 제 4저장부 14 : 배출슈트13: 4th storage unit 14: discharge chute
상기의 목적 달성을 위한 본 발명의 시멘트 혼화재 조성물은 4000∼6000㎠/g의 분말도를 유지하는 플라이 애쉬 83∼96중량%; 4000∼6000㎠/g의 분말도를 유지하는 슬래그 미분말 3∼6중량%; 4000∼5000㎠/g의 분말도를 유지하는 무수석고 0.1∼5중량%; 팽창제 0.5∼6중량%; 및 유동화제 0.5∼2중량%로 이루어짐을 특징으로 한다.Cement admixture composition of the present invention for achieving the above object is 83 to 96% by weight fly ash to maintain a powder degree of 4000 ~ 6000 cm 2 / g; 3 to 6% by weight of fine slag powder to maintain a powder degree of 4000 to 6000 cm 2 / g; 0.1-5% by weight of anhydrous gypsum having a powder degree of 4000-5000 cm 2 / g; 0.5-6% by weight of expanding agent; And 0.5 to 2% by weight of a fluidizing agent.
또한, 상기 혼화재의 시멘트 치환량을 증가시키기 위해 플라이 애쉬를 정제 및 혼화하는 제조장치로서의 본 발명은 수집된 플라이 애쉬가 투입 저장된 채 임의의 배출양 조절이 가능한 제 1저장부; 배출된 플라이 애쉬를 수용하여 이를 4000㎠/g 이상의 고분말로 정제하기 위한 분급기; 정제된 플라이 애쉬가 이송되어 투입되는 원심분리기; 슬래그 미분말, 무수석고, 팽창제 및 유동화제 등의 부원료가 각기 별도로 저장된 채 적량 배출될 수 있도록 한 제 2저장부; 배출된 부원료의투입량 산정을 위한 제 1계량기; 계량을 거친 부원료의 고른 혼합을 위한 제 1혼합기; 상기 혼합재료의 이송을 위한 제 1버킷 엘리베이터; 버킷 엘리베이터를 통해 이송된 혼합재료가 저장되는 제 3저장부; 상기 원심분리기를 거친 플라이 애쉬의 투입량 산정을 위한 제 2계량기; 상기 계량을 거친 플라이 애쉬와 제 3저장부를 거친 혼합재료가 일정 비율로 배합되는 제 2혼합기; 배합물의 이송을 위한 제 2버킷 엘리베이터; 배합물의 재 혼합을 위한 제 3혼합기; 재 혼합물의 저장을 위한 제 4저장부; 및 제 4저장부를 통해 완성된 저장물이 배출되어 출하될 수 있도록 배출슈트가 구비됨을 그 기술적 사상의 특징으로 한다.In addition, the present invention as a manufacturing apparatus for refining and admixing fly ash to increase the amount of cement substitution of the admixture, the present invention comprises: a first storage unit capable of adjusting any discharge amount while the collected fly ash is stored and stored; A classifier for accommodating the discharged fly ash and purifying it with a high powder of 4000 cm 2 / g or more; A centrifuge to which the purified fly ash is transferred and introduced; A second storage unit configured to discharge a small amount of auxiliary materials such as fine slag powder, anhydrous gypsum, an expanding agent, and a fluidizing agent, respectively and stored separately; A first meter for calculating an input amount of the discharged subsidiary material; A first mixer for even mixing of the weighed minor ingredients; A first bucket elevator for conveying the mixed material; A third storage unit for storing the mixed material transferred through the bucket elevator; A second meter for estimating the input amount of the fly ash passed through the centrifuge; A second mixer in which the mixed ash that has passed through the weighing and the third storage portion have been mixed in a predetermined ratio; A second bucket elevator for conveying the formulation; A third mixer for remixing the blend; A fourth reservoir for storing the ash mixture; And a discharge chute provided so that the completed storage can be discharged and shipped through the fourth storage unit.
본 발명의 시멘트 혼화재 조성물과 그 제조장치는 이하의 구체적인 설명을 통해 보다 명확하게 재현될 수 있을 것이다.Cement admixture composition of the present invention and its manufacturing apparatus will be more clearly reproduced through the following detailed description.
먼저, 본 발명에 의한 혼화재 조성물은 산업폐기물계로 저가의 포졸란 재료인 플라이 애쉬를 수집하여 이를 주재로 한 채 슬래그 미분말과 여기에 포졸란 재료의 조기 활성을 위한 목적의 일환으로 적량의 무수석고가 혼합되고, 각기 소량으로 2차 시멘트 제품인 레미콘 등의 무수축성을 위한 CSA계 팽창제 및 수밀성과 유동성 증진을 위한 리그닌계 유동화제인 리그닌 설폰산염이 혼합된다.First, in the admixture composition according to the present invention, a small amount of anhydrous gypsum is mixed as part of the purpose of premature activation of the pozzolanic material with the slag powder while collecting fly ash, which is a low-cost pozzolanic material, as an industrial waste system. In each case, a small amount of CSA-based swelling agent, such as a ready-mixed concrete, such as ready-mixed concrete, is mixed with lignin sulfonate, which is a lignin-based fluidizing agent for enhancing water tightness and fluidity.
이때, 플라이 애쉬는 대게 4000∼6000㎠/g의 정제된 분말도를 유지하면서 83∼96중량%, 바람직하게는 95중량%로 투입되고, 부원료인 슬래그 미분말과 무수석고 및 팽창제, 유동화제는 부원료만의 혼합과정을 거친 후 플라이 애쉬와 혼합되는데, 슬래그 미분말은 4000∼6000㎠/g의 분말도를 유지하면서 공급되어 3∼6중량%으로 투입하되, 특히 4중량%의 범위를 유지하는 것이 요망되는 것이라 하겠으며, 무수석고는 4000∼5000㎠/g의 분말도로 0.1∼5중량%의 범위를 유지하되, 최적의 혼화재 기능을 구현하기 위해서는 1중량%가 산정된다.In this case, the fly ash is usually added at 83 to 96% by weight, preferably 95% by weight, while maintaining a refined powder of 4000 to 6000 cm 2 / g, and the slag fine powder, anhydrous gypsum and swelling agent, and the fluidizing agent are secondary raw materials. After the mixing process, it is mixed with fly ash. Slag fine powder is supplied while maintaining the powder level of 4000∼6000㎠ / g, and 3 ~ 6% by weight, especially it is desirable to maintain the range of 4% by weight. Anhydrous gypsum is maintained in the range of 0.1 to 5% by weight with a powder of 4000 to 5000 cm 2 / g, but 1% by weight is calculated to realize the optimum admixture function.
한편, 전술한 바의 목적으로 사용되는 팽창제와 유동화제는 2차 시멘트 제품의 용도에 따른 적용성을 높이기 위해 선택되는 것으로 각기 팽창제 0.5∼6중량%와 리그닌계 유동화제 0.5∼2중량%로 투입되어 혼합됨이 바람직하다.Meanwhile, the swelling agent and the fluidizing agent used for the above-mentioned purposes are selected to increase the applicability according to the use of the secondary cement product, and each of the swelling agent is added in an amount of 0.5 to 6% by weight and lignin-based fluidizing agent, respectively. And preferably mixed.
이러한 각 원료의 투입량 계량은 임펙트 플로우 메터와 스케일 호퍼를 통해 이루어지며, 플라이 애쉬와 부원료와의 혼합은 2차에 걸친 혼합공정을 통해 완성된 조성물로서 제품사일로에 투입저장된다.The metering of each raw material is carried out through an impact flow meter and a scale hopper, and the mixing of the fly ash and the subsidiary material is stored and stored in the product silo as a completed composition through a second mixing process.
이와 같은 본 발명의 혼화재 조성물에 대한 물성평가는 다음과 같다.Such physical property evaluation of the admixture composition of the present invention is as follows.
이러한 본 발명의 혼화재 조성물에 따르면, 시멘트의 치환량을 시멘트 중량 대비 10∼50%만큼 확대 적용하여도 콘크리트에서 우려될 만한 팽창 현상은 발생되지 아니하였다.According to the admixture composition of the present invention, even if the substitution amount of cement is increased by 10 to 50% relative to the weight of the cement, there was no swellable phenomenon in the concrete.
한편, 본 발명의 시멘트 혼화재 조성물의 제조를 위해 마련되는 장치 구성물을 보다 상세하게 설명하면, 먼저 화력발전소 등에서 발생되는 폐기물로서 타지않은 석탄분인 플라이 애쉬를 수집하여 이를 벌크 트럭 등의 운송수단을 통해 사일로우 형식의 제 1저장부(1)에 투입 저장한 후 이를 분말도(BLAINE) 4000㎠/g 이상의고분말로 정제하기 위한 분급기(2)로 투입될 수 있게 하되, 작업자에 의한 임의의 투입량 조절이 가능할 수 있게 한다.On the other hand, the device components provided for the production of the cement admixture composition of the present invention in more detail, first to collect the fly ash, which is unburned coal powder as waste generated from a thermal power plant, and the like through a transport such as a bulk truck After being put into the first storage part 1 of the silo type and storing it, it can be put into the classifier 2 for refining with a high powder of BLAINE 4000 cm 2 / g or more, but any input amount by the operator Make the adjustment possible.
상기와 같이 분급기(2)를 통해 정제된 플라이 애쉬는 이송로를 통해 원심분리기(3)로 투입되고, 이러한 플라이 애쉬의 주재와는 별도로 슬래그 미분말, 무수석고, 팽창제 및 유동화제 등의 부원료는 역시 사일로우 형식의 제 2저장부(4)를 통해 투입 공급되어져 각기 별도로 저장된 채 적량 배출될 수 있도록 하는데, 배출된 부원료의 투입량 산정은 스케일 호퍼로 마련되는 제 1계량기(5)를 통해 계량된 후 고른 혼합을 위해 고효율의 제 1혼합기(6)로 넘겨져 혼합 처리된다.The fly ash purified through the classifier (2) as described above is introduced into the centrifuge (3) through a transfer path, and separate raw materials such as fine slag powder, anhydrous gypsum, swelling agent and fluidizing agent, apart from the main body of the fly ash, Also, it is supplied through the second storage part 4 of the silo type so that each of the separately stored quantities can be discharged, and the input amount of the discharged subsidiary material is measured through the first meter 5 provided with the scale hopper. It is then passed to the high efficiency first mixer 6 for even mixing, and then mixed.
이후, 상기 제 1혼합기(6)를 통한 혼합재료는 이송수단인 제 1버킷 엘리베이터(7)를 통해 운반되어 제 3저장부(8)에 저장된 채 대기된다.Thereafter, the mixed material through the first mixer 6 is transported through the first bucket elevator 7, which is a conveying means, and waits while being stored in the third storage 8.
한편, 상기 원심분리기(3)를 거친 플라이 애쉬는 그 투입량 산정을 위해 마련되는 임펙트 플로우 메터인 제 2계량기(9)를 통해 계량된 후 대기하고 있던 전술한 제 3저장부(8)를 거친 혼합재료가 계량과정을 거쳐 상호 일정한 비율로 고루 배합될 수 있게 제 2혼합기(10)를 통과하게 되고, 이러한 배합물은 이송수단인 제 2버킷 엘리베이터(11)를 통해 운반되어져 배합물의 재 혼합을 위해 스크류 방식을 채택하고 있는 제 3혼합기(12)로 투여된 후 완성된 조성물로서 배출되는 것으로, 이와 같이 조성되는 본 발명의 조성물은 제 4저장부(13)로 이송되어 대기하면서 배출슈트(14)를 통해 적절히 외부로 출하될 수 있도록 배려되는 것이다.On the other hand, the fly ash that passed through the centrifuge (3) is mixed through the above-described third storage section (8), which was measured after waiting through the second meter (9), which is an impact flow meter provided for the calculation of the input amount. The material is passed through the second mixer 10 so that the material is evenly blended at a constant rate through the weighing process, and the compound is conveyed through the second bucket elevator 11, which is a conveying means, to remix the compound. It is discharged as a finished composition after being administered to the third mixer 12 employing the method, the composition of the present invention is thus transferred to the fourth storage unit 13 while waiting for the discharge chute 14 It will be considered to be properly shipped to the outside.
이와 같은 조성물 및 장치를 갖는 본 발명에 따르면, 혼화재의 단가상승 억제를 통한 경제성 도모와 경쟁력 강화가 구현되며, 포졸란의 조기 활성을 가능케 함과 동시에 혼화재의 시멘트 치환량에 대한 증가를 포함하여 폐자원의 재활용에 따른 혼화재로서의 유용함을 도모할 수 있다는 것이고, 강도 및 내구성과 유동성의 증진 그리고 건조후의 수축 감소에 따른 품질의 균일화와 항상성으로 고품질의 2차 시멘트 제품 생산이 가능하다는 충분한 실시상의 가치를 갖게 된다.According to the present invention having such a composition and apparatus, it is possible to achieve economic feasibility and competitiveness by suppressing the cost increase of the admixture, and to enable the early activation of pozzolanic and at the same time increase the amount of cement replacement of the admixture. It can be useful as a mixed material by recycling, and it has sufficient practical value that it is possible to produce high-quality secondary cement products with uniformity and homeostasis of quality due to enhancement of strength, durability, flowability, and shrinkage after drying. .
한편, 본 발명은 그에 관한 최선의 실시예만을 언급하였으나, 굳이 이에 한정되지 않으며 본 발명의 목적범위내에서 청구범위를 벗어나지 않고 실시될 수 있다면 본 발명의 권리범위에 속할 것임은 자명하다.On the other hand, the present invention has been referred to only the best embodiments thereof, but it is obviously not limited to this, it will be obvious that it can be carried out without departing from the scope of the claims within the scope of the present invention.
Claims (4)