KR100384687B1 - mother-of-pearl ornament by screen printing and method for producing the same - Google Patents
mother-of-pearl ornament by screen printing and method for producing the same Download PDFInfo
- Publication number
- KR100384687B1 KR100384687B1 KR10-2000-0044481A KR20000044481A KR100384687B1 KR 100384687 B1 KR100384687 B1 KR 100384687B1 KR 20000044481 A KR20000044481 A KR 20000044481A KR 100384687 B1 KR100384687 B1 KR 100384687B1
- Authority
- KR
- South Korea
- Prior art keywords
- layer
- bare
- screen printing
- pattern layer
- pattern
- Prior art date
Abstract
본 발명은 스크린인쇄기법을 이용한 나전장식물 및 그의 제조방법에 관한 것으로, 이형지(1)가 부착된 기본층인 알루미늄박층(2), 상기 알루미늄박층(2) 위에 스크린 인쇄에 의해 형성된 문양층(3), 이들 위에 피복되는 에폭시수지층(5)으로 이루어지며, 상기 기본층인 알루미늄박층(2)과 이형지(1)를 접착하는 준비단계; 준비된 알루미늄 박층(2) 위에 스크린인쇄기법에 의해 문양층(3)을 형성하는 스크린인쇄단계; 문양층(3) 위에 나전조각을 접착하여 나전무늬층(4)을 형성하는 단계; 나전무 층(4)이 건조된 후, 상기 문양층(3)과 상기 나전무늬층(4) 위에 에폭시수지층(5)을 형성하는 에폭시수지피복단계; 70℃∼200℃온도하의 24시간동안 얻어진 나전장식물(A)의 열처리단계;와 실온에서의 건조단계;로 이루어지는 공정을 통하여 제조됨으로써, 내구성이 우수한 고품질의 나전칠기제품이 간단히 대량 생산에 의해 공급 가능하므로 나전 관광상품 및 전통상품과 장신구 및 가구류를 저렴하게 보급할 수 있다.The present invention relates to a barbed plant using a screen printing method and a manufacturing method thereof, an aluminum foil layer (2) which is a base layer to which a release paper (1) is attached, and a pattern layer (3) formed by screen printing on the aluminum foil layer (2). ), Consisting of an epoxy resin layer (5) coated on them, the preparing step of bonding the aluminum foil layer (2) and the release paper (1) which is the base layer; A screen printing step of forming a pattern layer 3 on the prepared aluminum thin layer 2 by a screen printing method; Bonding the bare pieces on the pattern layer 3 to form the bare pattern layer 4; An epoxy resin coating step of forming an epoxy resin layer (5) on the pattern layer (3) and the bare pattern layer (4) after the bare layer 4 is dried; By the heat treatment step of the bare electric plants (A) obtained for 24 hours at a temperature of 70 ℃ ~ 200 ℃; and drying at room temperature; is produced through a process consisting of, high-quality, high-precision lacquer lacquer products are simply supplied by mass production As a result, Najeon tourism products, traditional goods, jewelry and furniture can be distributed at low prices.
Description
본 발명은 스크린인쇄기법을 이용한 나전장식물 및 그의 제조방법에 관한 것으로, 보다 상세하게 말하면 나전장식물을 단기에 간단한 방식에 의해 대량으로 제조할 수 있는 스크린인쇄기법을 이용한 나전장식물 및 그의 제조방법에 대한 것이다.The present invention relates to a barbed plant using a screen printing method and a manufacturing method thereof, and more particularly, to a barbed plant using a screen printing method and a method for producing the barbed plant in large quantities by a simple method in a short time. will be.
예로부터 전통칠기중의 한 기법인 나전칠기는 대소형 가구를 비롯하여 각종 생활용품 및 장신구에 응용되어 오고 있는 우리의 전통적인 고급 공예이다.Najeon lacquer, a technique of traditional lacquer, has been applied to our traditional high-quality crafts that have been applied to various household items and ornaments, including small furniture.
그런데, 타 공예도 마찬가지지만 특히 나전칠기의 경우 기본 나무틀을 제작하는 백골(白骨)과 칠과정이 매우 복잡하여 손이 많이 가므로 장기간이 걸려야만 제작이 가능한 공예이다.By the way, in the case of other crafts as well, especially Najeon lacquer is a craft that can be produced only if it takes a long time because the white bone (白骨) and the painting process to produce a basic wooden frame is very complex and takes a lot of hands.
그래서, 대량 제작이 불가능하므로 자연히 제품단가가 고가로 되므로 우리 일상생활에 다양하게 적용하고 싶어도 일반인은 쉽게 구입할 수 없는 비싼 제품이었다.Therefore, mass production is impossible, so the product price is naturally expensive, so even if you want to apply a variety of our daily life was an expensive product that can not be easily purchased.
본 발명자는 나전칠기공예분야에 오래 동안 종사해 오면서 이를 대량 생산하여 작품으로서가 아니라 산업공예로서 저렴한 가격에 일반인에게 공급하여 우리 일상용품으로 유용하게 적용할 수 있도록 하고자 예의 연구 개발하게 되었다.The present inventors have been engaged in the field of Najeon lacquer crafts for a long time, and have been intensively researching and developing to mass-produce them and supply them to the general public at low prices as industrial crafts rather than as works.
그 결과, 본 발명자는 현대적인 장신구제작기법을 나전칠기공법과 접목시킴으로써 나전칠기 공예를 산업화하여 대량생산할 수 있게 되어 나전을 적용한 각 지방 및 우리나라 고유의 관광용품 및 전통 민속용품, 각종 장신구, 가구류를 저렴한 가격에 제공할 수 있는 방안을 안출하게 되었다.As a result, the present inventor can industrialize the Najeon lacquer craft by mass-producing the modern jewelry making technique with Najeon lacquer making method, thereby producing tourism products, traditional folk goods, various ornaments, and furniture unique to Najeon. The plan was to come up with a low price.
도1은 본 발명에 따른 스크린인쇄기법을 이용한 나전장식물의 전체적인 사시도,1 is an overall perspective view of a bare plant using a screen printing method according to the present invention,
도2는 도1의 a-a선을 따른 횡단면도,2 is a cross-sectional view along the line a-a of FIG. 1;
도3은 도1의 나전장식물의 일 실시례로서 열쇠고리에 장착하였을 때의 사용상태도,3 is a state of use when mounted on the key ring as an embodiment of the barbed plant of FIG.
도4는 본 발명에 따른 스크린인쇄기법을 이용한 나전장식물의 제조공정도.Figure 4 is a manufacturing process of the barbed plants using the screen printing technique according to the present invention.
※도면의 주요부분에 대한 부호의 설명※ Explanation of symbols for main parts of drawing
A : 나전장식물A: Naeon Plant
1 : 이형지(離型紙)1: Release paper
2 : 알루미늄박(aluminium foil)층2: aluminum foil layer
3 : 문양층3: glyph layer
4 : 나전(螺鈿)무늬층4: Najeon pattern layer
5 : 에폭시수지(epoxy resin)층5: epoxy resin layer
6 : 장식부6: decoration
본 발명은 이형지가 부착된 기본층인 알루미늄박층, 이 알루미늄박층 위에 스크린 인쇄에 의해 도료 또는 잉크가 도포된 문양층, 이 문양층위에 부착되는 나전무늬층 및 상기 나전무늬층 위에 피복되는 에폭시수지층으로 이루어지는 스크린인쇄기법을 이용한 나전장식물을 제공하는 것을 특징으로 한다.The present invention is an aluminum foil layer which is a base layer to which a release paper is attached, a pattern layer coated with paint or ink by screen printing on the aluminum foil layer, a bare pattern layer attached on the pattern layer, and an epoxy resin layer coated on the bare layer. It is characterized by providing a bare plant using a screen printing technique consisting of.
본 발명에서는 상기 스크린인쇄기법을 이용한 나전장식물은 기본층인 알루미늄박층과 이형지를 접착하는 준비단계;In the present invention, the bare plant using the screen printing method is a step of preparing a bonding layer and the release paper aluminum base layer;
준비된 알루미늄박층 위에 스크린인쇄기법에 의해 잉크 내지 도료를 도포하여 문양층을 형성하는 스크린인쇄단계;A screen printing step of forming a pattern layer by coating ink or paint on the prepared aluminum foil layer by a screen printing method;
형성된 문양층위에 무늬에 맞게 나전조각을 접착하여 나전무늬층을 형성하는 단계;Forming a bare pattern layer by bonding a bare piece to a pattern on the formed pattern layer;
나전무늬층이 건조된 후 상기 문양층과 상기 나전무늬층 위에 전체적으로 에폭시수지를 코팅하는 에폭시수지피복단계;An epoxy resin coating step of coating the epoxy resin on the pattern layer and the bare pattern layer after the bare pattern layer is dried;
얻어진 나전장식물을 70℃∼200℃사이의 온도 하에서 24시간동안 열처리하는 단계;와Heat-treating the obtained bare field plants at a temperature between 70 ° C. and 200 ° C. for 24 hours; and
실온에서의 건조단계;에 의하여 제조됨으로써 일회에 동일물을 다량으로 제조할 수 있다.By drying at room temperature; the same can be prepared in large quantities at one time.
본 발명에서 사용되는 상기 알루미늄박층은 기본층으로서 대략 0.005인치(약 0.127mm) 두께의 얇고 편평한 시이트 상태의 알루미늄으로 이루어지며 그 이면에 접착제에 의해 박리가능하도록 접착된 이형지가 구비되어 있다. 이 이형지는 폴리에스테르, 폴리에틸렌, 폴리프로필렌 등의 각종 합성수지로 이루어지는 통상의 얇고 투명한 시이트이다.The aluminum foil layer used in the present invention is made of thin, flat sheet aluminum having a thickness of approximately 0.005 inches (about 0.127 mm) as a base layer, and a release paper adhered to the back side thereof to be peeled off by an adhesive. This release paper is a normal thin and transparent sheet which consists of various synthetic resins, such as polyester, polyethylene, and a polypropylene.
상기 문양층은 통상의 실크스크린 등 각종 스크린 인쇄기법에 의해 형성되며, 이 문양층은 원하는 디자인에 따라 적어도 2이상 수회 인쇄되어 다양한 색상의 무늬를 형성하고 있다.The pattern layer is formed by various screen printing techniques such as a conventional silk screen, and the pattern layer is printed at least two or more times according to a desired design to form a pattern of various colors.
본 발명에서 사용되는 나전으로는 소라, 전복, 진주조개 등의 각종 조개껍질로서 고급 나전칠기작품에 사용되는 것과 동일한 방식으로 준비된다. 나전은 통상의 합성 접착제에 의해 접착되며, 예를 들면 액상의 페놀수지, 요소수지, 멜라민수지, 폴리 에스테르수지, 폴리 우레탄수지, 에폭시수지, 실리콘수지 등의 열경화성 수지와 폴리 아세트산비닐, 폴리 비닐알코올, 폴리 염화비닐, 폴리 비닐부티랄, 폴리 아크릴산에스테르, 니트로 셀룰로오스 등의 열가소성 수지 중에서 어느 하나 또는 둘이상 혼합된 것이 사용될 수 있으며, 이들 중 폴리 아세트산 비닐수지나 폴리 우레탄계수지가 보다 바람직하게 사용될 수 있다.Najeon used in the present invention is prepared in the same manner as used in high-quality najeon lacquer work as a variety of shells such as seashells, abalone, pearl shells. Najeon is bonded by a conventional synthetic adhesive, for example, a thermosetting resin such as a liquid phenol resin, urea resin, melamine resin, polyester resin, polyurethane resin, epoxy resin, silicone resin, polyvinyl acetate, polyvinyl alcohol , Polyvinyl chloride, polyvinyl butyral, polyacrylic acid ester, and any one or two or more of the thermoplastic resins such as nitrocellulose may be used, and among these, polyvinyl acetate resin or polyurethane resin may be more preferably used. .
또한, 상기 나전무늬층 위에 피복되는 상기 에폭시수지층은 요구되는 경도 및 강도에 합치할 수 있도록 적정한 점도의 에폭시수지와 경화제의 혼합물로 이루어진다.In addition, the epoxy resin layer coated on the bare pattern layer is composed of a mixture of epoxy resin and a curing agent of a suitable viscosity to match the required hardness and strength.
따라서, 본 발명에 의한 스크린인쇄기법을 이용한 나전장식물은 전통기법에 의한 나전장식물보다 더 견고하며 변형 및 변질이 없어 수명이 반영구적이다.Therefore, the barbed plant using the screen printing technique according to the present invention is more durable than the barbed plant according to the traditional technique, and life is long since there is no deformation and alteration.
이하, 본 발명을 첨부된 도면을 참조하여 보다 상세히 설명하면 다음과 같다.Hereinafter, the present invention will be described in more detail with reference to the accompanying drawings.
전체적인 구조를 보여주는 사시도의 도1 및 그 횡단면도인 도2에 나타낸 바와 같이 본 발명에 따른 스크린인쇄기법을 이용한 나전장식물(A)은 여러 층으로 이루어진다.As shown in Fig. 1 and a cross-sectional view of Fig. 1 of a perspective view showing the overall structure, the barbed plant (A) using the screen printing method according to the present invention consists of several layers.
도3은 일 적용례로서 본 발명에 따른 스크린인쇄기법을 이용한 나전장식물(A)을 열쇠고리에 적용한 것을 나타내고 있다.Figure 3 shows the application of the barbed plant (A) using the screen printing technique according to the present invention to the key ring as an application example.
본 발명에 따른 스크린인쇄기법을 이용한 나전장식물(A)의 알루미늄박층(2)은 그 이면에 박리가능하게 접착된 이형지(1)와 함께 기본층으로서의 역할을 한다.The aluminum foil layer 2 of the bare electric field plant A using the screen printing method according to the present invention serves as a base layer together with the release paper 1 detachably adhered to the back surface thereof.
또한, 본 발명에서는 기본층으로서 상기 알루미늄박층(2)대신에 목재나 금속판이 필요에 따라 상기와 동일한 방식으로 적용될 수도 있다.In the present invention, instead of the aluminum foil layer 2 as the base layer, wood or a metal plate may be applied in the same manner as above.
상기 알루미늄박층(2)의 표면은 스크린 인쇄에 적당하도록 형성되며 그 위에 실크스크린 등의 통상 방식에 의하여 도료 또는 잉크가 도포된다. 원하는 디자인에 맞게 수차 도료 내지 잉크가 도포되고 건조되어 문양층(3)이 구비된다. 이 문양층(3) 위에 미리 디자인된 문양에 따라 다양한 색상의 나전조각이 부분적으로 또는 전체적으로 접착되어 나전무늬층(4)이 형성된다.The surface of the aluminum foil layer 2 is formed to be suitable for screen printing, and paint or ink is applied thereon by a conventional method such as silk screen. According to the desired design, the aberration paint or ink is applied and dried to provide a pattern layer 3. According to the pattern previously designed on the pattern layer 3, the bare pieces of various colors are partially or totally bonded to form the bare pattern layer 4.
또한, 문양층(3) 및 나전무늬층(4) 위에는 에폭시수지층(5)이 코팅되어 있다.In addition, the epoxy resin layer 5 is coated on the pattern layer 3 and the bare pattern layer 4.
이러한 구조의 본 발명에 따른 스크린인쇄기법을 이용한 나전장식물(A)은 상기 문양층(3)을 형성하기 위하여, 먼저 기본층인 알루미늄박층(2)과 이형지(1)를 접착한다.The bare plant (A) using the screen printing method according to the present invention of such a structure, first to bond the base layer aluminum foil layer 2 and the release paper (1) to form the pattern layer (3).
그 후 준비된 알루미늄박층(2) 위에 스크린인쇄기법에 의해 도료 내지 잉크를 도포하여 문양층(3)을 형성한다. 상기 스크린인쇄기법으로는 실크스크린이 주로 적용되며 통상의 방식과 마찬가지로 컴퓨터 그래픽에 의한 도안 후 필름을 제작 출력, 알루미늄 프레임 제작 및 스크린인쇄, 그리고 스퀴징의 순으로 작업함으로써 상기 알루미늄박층(2) 위에 다양한 색상의 도료 또는 유·수성의 스크린잉크가 수회 도포된다. 도포된 잉크 또는 도료의 건조 후 형성된 문양층(3)위에 무늬에 맞는 나전조각을 그 이면에 접착제를 골고루 잘 바른 후 해당 무늬부분에 접착하여 나전무늬층(4)을 형성한다.Thereafter, the paint or ink is applied onto the prepared aluminum foil layer 2 by a screen printing method to form a pattern layer 3. Silk screen is mainly applied to the screen printing technique, and the film is printed on the aluminum foil layer 2 by working in the order of fabrication output, aluminum frame fabrication and screen printing, and squeegeeing in the same manner as usual. Various colors of paint or oil-based screen ink are applied several times. Apply the adhesive evenly on the back surface of the bare pieces suited to the pattern on the pattern layer (3) formed after drying of the applied ink or paint, and then adhere to the patterned part to form the bare pattern layer (4).
나전무늬층(4)이 완전 건조된 후, 이 나전무늬층(4)과 문양층(3) 위에 전체적으로 에폭시수지를 소정 두께로 코팅한 다음 얻어진 장식물을 70℃∼200℃사이의 온도에서 24시간동안 열처리하여 건조함으로써 나전장식물(A)이 얻어진다.After the bare pattern layer 4 is completely dried, the epoxy resin is coated on the bare layer pattern 4 and the pattern layer 3 to a predetermined thickness as a whole, and the obtained decoration is then heated at a temperature between 70 ° C. and 200 ° C. for 24 hours. The heat-treated and dried to obtain a bare field (A).
이렇게 제조된 나전장식물(A)을 도3에 나타낸 바와 같이, 일례로 열쇠고리에 적용할 경우 맨 하부의 이형지(1)를 박리한 후 상기 나전장식물(A)의 크기에 맞게 성형 내지 금형 제작된 장식부(6)에 위치시키기만 하면 간단히 제 위치에 확고하게 부착되어 열쇠고리가 완성된다.As shown in Fig. 3, when the barbed plant A thus prepared is applied to the key ring, the release paper 1 is peeled off at the bottom, and then molded or molded into the size of the barbed plant A. Simply place it in the decorative part 6, it is simply firmly attached in place to complete the key ring.
그러므로, 본 발명에 따르면 전통 나전칠기의 공예작품과 같은 우아한 멋은 다소 떨어지나 오히려 현대감각에 맞게 분위기를 연출할 수 있으며 전통나전칠기와는 달리 나전부분이 외부에 직접 노출되지 않으므로 나전이 들뜨거나 훼손되지 않고 변형 및 변질이 없어 내구성이 뛰어난 나전장식물(A)을 위와 같은 제조공정을 통하여 일회에 다량으로 간단히 제조할 수 있게 된다.Therefore, according to the present invention, the elegant fashion, such as the craft of traditional Najeon lacquer wares are somewhat inferior, but can produce an atmosphere according to the modern sense. Without deformation and deterioration, the highly durable barley plant (A) can be easily produced in a large amount through the above manufacturing process.
본 발명의 특징을 보다 더 용이하게 이해할 수 있도록 하기 위하여 다음에 일 실시례를 들어 기술하나 본 발명은 이에 한정되지 않고 그 범주 및 첨부된 특허청구의 범위 내에서 정정 및 변경이 가능하다는 것을 본 분야에 숙지된 자라면 쉽게 이해할 수 있을 것이다.In order to more easily understand the features of the present invention, the following examples will be described, but the present invention is not limited thereto, and it is possible to make modifications and changes within the scope and scope of the appended claims. If you are familiar with it, you will easily understand it.
(실시례)(Example)
먼저, 각기 직경 3㎝정도의 원형문양의 6가지 색상으로 된 디자인을 도안하고 이를 실크스크린으로 일시에 50개 인쇄할 수 있도록 프레임 및 기타 작업 준비를 하였다.First, designs of six colors of circular patterns each about 3cm in diameter were designed, and frames and other work preparations were made to print 50 on a silk screen at a time.
그리고, 시이트상의 알루미늄박에 폴리 에틸렌수지필름을 이형지로서 박리 가능하도록 접착하였다.And the polyethylene resin film was adhere | attached on the sheet-like aluminum foil so that peeling was possible as a release paper.
상기 준비된 알루미늄박 위에 원하는 디자인을 실크스크린에 의해 인쇄하고 옅은 색 순으로 단계적으로 유성잉크를 사용하여 5도의 잉크를 각기 도포한 후 건조하여 알루미늄박 위에 동일한 문양을 50개 형성하였다.The desired design was printed on the prepared aluminum foil by silkscreen, and each ink was applied by 5 degrees using oil-based ink in the order of light colors, and then dried to form 50 identical patterns on the aluminum foil.
소정의 문양이 형성된 알루미늄박 위에 무늬에 맞게 오려진 나전조각을 폴리 아세트산 비닐계의 흔히 201오공본드라고 불리는 상품명의 국내산 접착제를 도포하여 디자인상의 문양 중 해당 나전조각부착부분에 부착하여 나전무늬층을 형성하였다.Applying a domestic adhesive of a brand name commonly referred to as 201 pore bond of polyvinyl acetate, and attaching the bare slice cut to the pattern on the aluminum foil on which the predetermined pattern is formed, and affixing the bare pattern layer to the corresponding bare portion of the design pattern. Formed.
형성된 50개의 중간 제작물위에 소량의 아민류 경화제가 첨가된 에폭시수지를 피복하여 180℃온도의 오븐에 투입한 다음 24시간동안 열처리하여 열고정시켰다.Epoxy resin to which a small amount of amine curing agent was added was coated on the formed 50 intermediate products, and the resultant was placed in an oven at 180 ° C. and heat-set by heat treatment for 24 hours.
열처리 후 실온에서 서서히 식히면서 건조하여 나전장식물 50개를 동시에 완성하였다.After heat treatment, the mixture was slowly cooled to room temperature and dried to complete 50 bare plants at the same time.
완성된 나전장식물의 하나를 열쇠고리의 장식부에 부착함으로써 현대적 감각에 전통 나전칠기법에 의한 멋이 가미된 독특한 분위기를 나타내는 나전장식물을 간단히 약 2일만에 얻었다.By attaching one of the completed Najeon plants to the decorative part of the key ring, Na Na plants were presented in about two days, giving a unique atmosphere with a modern touch and a traditional Najeon lacquer technique.
이상과 같이 본 발명에 따른 스크린인쇄기법을 이용한 나전장식물 및 그의 제조방법에 의하면 오직 수작업에만 의존하던 전통 나전칠기제품을 대량생산이 가능하도록 산업공예화 할 수 있어 고가의 나전칠기제품을 저가로 보급할 수 있다.As described above, according to the present invention and the manufacturing method of the najeonjeon plants using the screen printing method according to the present invention can be industrialized to enable the mass production of traditional najeon lacquer products that only depended on manual labor to supply expensive najeon lacquer products at low prices can do.
즉, 예전의 전통 나전칠기공법과는 달리 본 발명에 의하면 제작공법이 간단하고 다수개의 내구성이 우수한 나전장식물을 일시에 얻을 수 있어 가격을 상당히 낮출 수 있으므로 대중화가 가능하여 일반 다수인이 손쉽게 나전칠기제품을 이용할 수 있다.In other words, unlike the traditional traditional Najeon lacquer method according to the present invention, the production method is simple and can obtain a large number of durable Najeon plants at one time, so that the price can be considerably lowered, so that many people can easily popularize Najeon Lacquerware. Product is available.
또한, 본 발명에서는 고품질의 나전칠기제품을 저가로 생산할 수 있으므로 우리나라 고유의 관광상품 및 전통상품에 나전을 적용하여 상품을 보다 고부가가치화할 수 있음과 아울러 다량 보급할 수 있어 문화민족으로서의 긍지를 드높일 수 있으며 수출 및 관광상품의 판매량 증가로 수익을 크게 올릴 수 있다.In addition, the present invention can produce high-quality Najeon Lacquerware at low price, so that it is possible to apply Najeon to Korea's unique tourism products and traditional products, and to increase the value of the products. In addition, profits can be greatly increased by increasing sales volume of exports and tourism products.
본 발명에 따른 스크린인쇄기법을 이용한 나전장식물은 경도 및 강도가 우수하여 변질 및 변형 없이 거의 반영구적으로 사용할 수 있으며 열쇠고리, 넥타이핀 등의 소품뿐만 아니라 반지, 목걸이의 보석장신구 및 거울, 장롱, 서랍의 가구류에도 적용할 수 있고, 기타 칠보세공 등의 각종 공예와 함께 접목하여 제작이 가능하므로 색다른 느낌을 부여하는 현대적 감각의 각종 장식물에도 적용 가능하다.Bare plants using the screen printing method according to the present invention is excellent in hardness and strength can be used almost semi-permanently without alteration and deformation, as well as accessories such as key chains, tie pins, rings, necklaces jewelry ornaments and mirrors, dressers, drawers It can be applied to furniture, and it can be combined with various crafts such as cloisonne, so it can be applied to various kinds of decorations with a modern sense.
Claims (2)