Abstract

PURPOSE: Nonwoven fabric emitting far infrared radiation obtained by treating a nonwoven fabric with a far infrared radiation emitting material such as loess, illite, charcoal and water vessel waves shielding material and then forming is provided which can be used as bedclothes, wallpaper or the like which has a deodorizing, air cleaning, bactericidal, blood circulation promoting and water vessel waves shielding function. CONSTITUTION: A nonwoven fabric is impregnated with a suitable amount of a mixture containing 45% by weight of loess, 40% by weight of illite, 14% by weight of charcoal and 1% by weight of water vessel waves shielding material, heated at 180deg.C under pressure and then formed in a shape of an uneven plate(embossing) or plate.

Description

Material of Far Infrared Textile Fabric

본발명은 원료소재로 잘알려진 황토, 일라이트, 목탄, 및 전자파 산파용, 소재를 원면 부직포에 함침, 특수가공 공정과 열처리 방법으로 압착, 영구적으로 자연 발생의 기를 방사하는 즉 악취를 흡착, 탈취하고 중금속등을 정화 촉진케하며, 인체에 유해한 병원균을 살균하고 인체에 접촉하면 혈액순환을 촉진시켜서 신진대사를 도우고 전자파 수맥파를 방산케하여 피로회복을 빠르게 하는등의 효과를 갖는 원적외선 섬유직포의 소재에 관한 것이다.The present invention is for use in loess, illite, charcoal, and electromagnetic wave scattering, which are well known as raw materials, impregnating the material into nonwoven fabrics, pressing them by special processing and heat treatment methods, and permanently radiating naturally occurring groups, that is, adsorbing and deodorizing odors. It promotes the purification of heavy metals, sterilizes pathogens harmful to the human body, and promotes blood circulation when it comes into contact with the human body, helping metabolism and dissipating electromagnetic water waves to speed up fatigue recovery. It is about material.

자연의 원적외선이 우리 인체에 주는 영향은 신비의 생명력을 주고 지구의 자력은 공기속에 있으며 기는 땅속에서 올라오고 인간이 호흡하며 피부에 모세혈관을 통해 덥고 찬 것을 느끼며 기운을 받아 들인다,그런데 현대 문화가 극도로 발달 되면서 모든 자연의 생활 공간은 파괴하여 편의주의로 생활 설계가 이루어져 시멘트 콘크리트로서 자연의 기를 차단하는 공간에서 잠을 자고 아스팔트나 시멘트 콘크리트 위를 걷고 거주하며 생활 하므로서 인체의 모든 기능은 약해지고 문화병이라는 성인병이 생기며 건강치 못한 생명이나마 수명을 단축시키는 불행을 초래케 하였던 것이다,The impact of nature's far-infrared rays on our human body gives the vitality of mystery, the earth's magnetic force is in the air, the creeping up from the ground, human breathing, feeling hot and cold through capillaries on the skin, but modern culture is extremely As it was developed into a living area, all natural living spaces are destroyed, and the design of life is made with convenience, so as to sleep in a space that blocks natural air, and to walk and live on asphalt or cement concrete, all the functions of the human body become weak and become cultural diseases. Adult disease, which leads to unhealthy life and shortened life,

따라서 이를 극복하고자 각종 약품 운동요법, 식이요법, 건강을 위한 수맥파, 전자파 차단재, 황토방, 황토매트, 황토침대, 돌침대, 심지어는 원적외선 섬유는 물론 황토를 섬유사() 에 첨가해서 실을 만들어서 직조하여 사용케 하는 것 등이 다수 개발되고 상품화 되어서 범람하고 있는 것이다,그러나 이들은 한결같이 하나의 용도에 국한 되어서 이용되어 왔고 특히 박테리아균이나 인체에 유해한 병원균을 퇴치 시키거나 감소 시키지 못하였고 악취를 흡착 탈취 시키거나 분해시키지 못하였을 뿐 아니라 질병예방과 원적외선 방사에 의한 기를 받아서 피로회복 혈액순환 촉진등의 효과를 한꺼번에 기대할수 가 없었던 것이다,이와같은 종래의 제반문제점을 해결 및 보완하고자 하는 의미로서 일부나마 개선된 것으로서 국내 공개 실용신안 공보 97-13811호로 공개된 방사물질이 함유된 벽지와 또 외국에서는 일본국 특개평 10-292268호로 공개된 소취 포리에스텔 섬유구조물이 알려져 있으며, 전자는 물 5-15%, 바인더 15-20%, 황토 및 일라이트 10-20%, 맥반석 10-20%, 전분 4%, 소포제 0.1-0.5%, 분산제 1.05-0.1%, 중 탄산칼슘 30-45%, 로 조성된 방사물질을 배면지 표면에 적층도포하여 형성한 방사물질층의 상면에 상기 조성비로 혼합한 것에 염료 0.5-1.0%, 티탄 5-10%, 조서비로 구성한 잉크로서 문양을 인쇄한 샌드위치 형태의 벽지를 구성한 것으로서 조성물중 맥반석은 일반적으로 알려진 것 외에 인체에 유해한 독성물이 배출되는 경우가 있으며, 특히 이와 같이 구성된 벽지는 벽지로 사용하였을 경우 실내의 습도 온도등에 따라 변화되여 장기간 경과하면 방사물질층이 분산되고 표면의 인쇄층 역시 분산해체되여(부스러지는 현상등) 벽지로서의 기능을 상실하는 결점이 있었으며,또 후자의 소취 포리에스텔 섬유구조물은 폴리에스텔 섬유에 활성탄, 무기산화물 및 유기질소계 화합물이 수지 바인더(접합제)를 개입되게 고착하는 구성으로서 무기산화물은 Si, Zn, Ti, Fe, Al, Mg, Zr 중에서 선택한 산화물을 개입시켜서 소취 폴리에스텔 섬유의 구조물을 형성하는 것으로서 실내에 적용하여 전자의 벽지등의 용도와 같이 악취를 제거한다는 데에 목적을 두고 개발된 것이며,이것은 활성탄에 무기 산화물과 유기질소계 화합물을 주성분으로 함으로서 예를 들어 인체의 장신구 주변물품 신발깔창등에[서 사용할수 없는 결점이 있었던 것이다.Therefore, in order to overcome the various medicine exercise therapy, diet, health water wave, electromagnetic wave shielding material, ocher room, ocher mat, ocher bed, stone bed, even far-infrared fiber as well as ocher fiber yarn ( In addition to making yarns, weaving them, and making them available for use, are flooded with many developments and commercialization, but they have been consistently used for one purpose, especially to combat or reduce bacteria and pathogens harmful to humans. Not only did they fail to adsorb or deodorize or decompose odors, but also prevented disease and promoted blood recovery due to far-infrared radiation. As a result, the wallpaper containing the radioactive material disclosed in Korean Utility Model Publication No. 97-13811 and the deodorizing polyester fiber structure disclosed in Japanese Patent Application Laid-open No. Hei 10-292268 are known. 5-15% water, 15-20% binder, ocher and ella 10-20% of calcite, 10-20% of starch stone, 4% of starch, 0.1-0.5% of antifoam, 1.05-0.1% of dispersant, 30-45% of calcium bicarbonate, An ink composed of 0.5-1.0% of dye, 5-10% of titanium, and co-servo, which is mixed with the above composition on the upper surface of one emitting material layer, constituted a sandwich-shaped wallpaper printed with patterns. Toxic substances harmful to the human body may be emitted, and in particular, the wallpaper configured in this way is changed depending on the humidity temperature of the room, and when it is used for a long time, the radioactive material layer is dispersed and the printed layer on the surface is also disassembled. In the latter deodorant polyester fiber structure, activated carbon, inorganic oxides and organic nitrogen-based compounds were added to the resin binder (resin binder). The inorganic oxide is formed through the oxide selected from Si, Zn, Ti, Fe, Al, Mg, and Zr to form a structure of deodorized polyester fiber. It was developed with the purpose of eliminating odors, as in the use of carbon dioxide, which has a defect that cannot be used in, for example, shoe insoles, etc. .

본발명이 이와 같이 종래의 것들과는 달리 분말 원료를 부직포에 함침함에 있어서 단순히 접합제(Binder)나 접착제의 사용없이 성형후 분말 원료가 떨어지거나 분리되는 폐단이 없도록 하면서 용도에 따라서 침구류, 위생구, 벽지등 기타 강도와 두께를 조절, 성형하여 인체장신구, 인체의 주변 물품등에 사용토록 하여 생활공간을 신선하게 하고 인체에 원기를 회복시키며 건강을 유지시키는데에 본 발명이 이루고자 하는 과제이다,본원에서 일라이트 또는 크로라이트, 코디라이트 목탄 등에서는 원적외선이 89-91% 이상과 95%이상의 원적외선을 방사한다고 알려져 있고, 원적외선에 대해 살펴보면,첫째 : 진동수가 많은 순서에 따라 감마선, X선이 있고 이것은 투과성질이 있으며 그다음에 자외선, 가시광선으로 이어지나 그것은 반사의 성질을 갖이며 가시광선은 보라, 남, 파랑, 초록, 노랑, 주황, 빨강의 일곱가지 색으로서 인간의 눈에 보이는빛으로 빛가운데 전체의 약 7%에 해당한다,이 가시광선의 보라보다 짧은 빛을 보라의 밖에 있다고하여 자외선이라 부르며 가시광선중에서 가장 파장이 긴 빨강보다 긴쪽의 빛을 빨강밖에 있다고 하여 적외선이라 하며 빛가운데 약 80%을 차지하고 있으며 4마이크론을 기준으로 하여 짧은 쪽을 근적외선, 먼쪽을 원적외선이라 한다,빛의 분류와 원적외선(赤外線)) 의 위치를 살펴보면둘째 : 원적외선의 성질에 있어서는1) 열의 전달방식에는 대류, 전도, 방사의 세가지 형태가 있으며 적외선은 이 세가지중 방사(放射)로 열을 전달하는데 방사는 공기나 물등에 의하여 간접적으로 열을 전파하는 대류나 전도와는 달리 대상물에 직접열을 전달하는 방법으로 열효율이 대단히 좋다는 장점이 있고,2) 원적외선은 흡수광선이므로 상대에 흡수되여 체내에 에너지화 한다 원적외선은 열의 운반자이기도 하며 가하여진 열이 신속히 전파하며 근 적외선은 반사광선이고 원적외선은 흡수광선이다, 겨울에 부드럽고 따스한 느낌, 햇살이 쪼이는등 아련히 몸속에 느껴지는 따뜻한 온기, 몸에 기분좋게 흡수되는 빛, 그것이 원적외선의사열이라는 것이다,체온보다 낮은 온도에서는 몸표면에서 느낄수 없다면 왜 체온보다 낮은 30℃의 내려쪼이는 태양아래서 땀을 흘릴까 하는 의문에서 생각할 때 태양으로부터 열을 적외선이 운반하여 온다.3) 원적외선이 가지는 여러 가지 현상에서원적외선은 자기발열 현상과 물을 활성하는 현상물분자 결합을 강하게 하면 물은 활성화하며 특히 생체에 미치는 영향에서 원적외선 흡수광의 성질을 이용하는 것이므로 이 원적외선을 흡수하는 물질이 있기 때문에 가능하고 원적외선 흡수물질은 유기화합물질인데 이는 생물이고 생체(生體)로서 생명체라 부른다 생체내에는 당, 아미노산, 단백질, 홀몬등 여러물질이 복잡하게 만들어직 모두 탄소가 핵으로 되어 생체로부터 산출되는 것은 탄소화합물질이며 이를 총칭하여 유기화합물이라 하며 생명활동을 영위하고 있는 것은 유기화합물이며 이를 흡수하지 않으면 생명활동은 중지된다,이와 같은 원인에 의하여 생체의 80%를 차지하고 있는 수소, 원자가 원적외선 방사에 의한 운동으로 생체활동을 강화 하는데 필연적으로 연관성을 가지고 있으므로 본원에서는 이를 이용한 섬유직포의 소재에 이용한 것이다.Unlike the conventional ones, in the present invention, when impregnating a powder raw material into a nonwoven fabric, bedding and hygiene are not used depending on the purpose, so that the powder raw material does not fall or separate after molding without the use of a binder or an adhesive. It is an object of the present invention to maintain the freshness of the living space, to rejuvenate the human body, and to maintain health by adjusting and molding other strengths and thicknesses such as spheres, wallpaper, and the like to be used for human ornaments and surrounding objects of the human body. In illite, chromite, cordierite charcoal, etc., far infrared rays are known to emit more than 89-91% and more than 95% of far infrared rays. When looking at far infrared rays, firstly, there are gamma rays and X rays in order of high frequency. It is transparent and then leads to ultraviolet rays and visible light, but it is reflective and visible The line consists of seven colors: purple, blue, green, yellow, orange, and red, which are about 7% of the total light visible to the human eye. It is called ultraviolet rays and the longest light out of the visible light is called red, and it is called infrared, and it occupies about 80% of the light. The short side is called near-infrared and the far infrared is far-infrared based on 4 microns. Classification and far infrared ( If you look at the location of 赤外線)) Secondly, in the nature of far-infrared rays, there are three types of heat transfer methods: convection, conduction, and radiation. Infrared radiation transmits heat in three kinds of radiation, which radiates heat indirectly by air or water. Unlike convection or conduction, it has the advantage that thermal efficiency is very good by transferring heat directly to the object.2) Since far infrared rays are absorbed rays, they are absorbed by the partner and energized in the body. Far infrared rays are also carriers of heat and heat applied quickly Near-infrared rays are reflected rays and far-infrared rays are absorbed rays. Warm warmth felt in the body, such as soft and warm feelings in the winter, and the sun shining, pleasant light absorbed by the body, it is far infrared rays, lower than body temperature If you can't feel it at the body surface at the temperature In the question of sweating from below, infrared light carries heat from the sun. 3) In various phenomena of far infrared, far infrared rays activate water by strengthening the self-heating phenomenon and the activation of water molecules. In particular, the effect on the living body uses the properties of the far-infrared absorbing light, which is possible because there is a material that absorbs the far-infrared light. The far-infrared absorbing material is an organic compound, which is a living organism, and is called a living organism. Carbon, nucleus, and various substances such as proteins, and holmone are all complex, and carbon is the nucleus and is produced from living organisms. Carbon compounds are collectively called organic compounds. Is stopped, living by such a cause To enhance the biological activity of exercise by hydrogen atoms far-infrared radiation, which account for 80%, so inevitably have relevance in the present application will be used for the material of the fiber woven fabric using the same.

직조하지 않은 섬유 부직포에 원적외선의 기를 방사하고 박테리아 병원균을 퇴치 및 감소시키며 질병예방과 수맥파 전자파등을 방사시켜서 피로회복, 혈액순환 각종 냄새의 흡착탈취 및 주변 공기의 정화작용을 갖도록 하는 황토 약 45%, 일라이트 또는 크로라이트 약40%, 목탄 약 14%, 수맥 및 전자파 산파용 소재는 동분말 55%와 아연분말 45%로 구성된 소재 1%를 물에 혼합하는데 황토, 일라이트, 목분, 산파용소재를 혼합한 100%에 대하여 70%와 물30% 비율로 혼합하여 이를 부직포에 함침(침적)시켜서된 부직포를 2중으로 겹쳐서 적정의 고열(160-200 ℃)로 가열 압착 성형한다. 즉암수의요철을로서 표면에 구성하거나 암수의 요철이 없는 한쌍의 로울러를 통과시켜서 성형하는 것이다 수맥파산파용 소재로서,동과 아연은 수맥이나 파장을 차단내지 산파하는 역할을 하며 부직포는 용도에 따라 합성수지재 또는 면화로 구성되는 편직 내지 직조되 않은 것을 사용하는데 일반적으로 잘알려져 있고 시중에 상품화 되고 있는 것을 사용하고,수맥파 및 전자파 산파용 소재에는 두가지가 있는데, 첫째 : 일반적으로 알려진 구리 및 아연분말을 사용해오고 있고, 둘째 : 장석, 남석, 도석을 1200-1300 ℃로 1차 가열후 250메쉬로 분쇄한 30%를 물70%에 혼합하여 발효조에 넣어 게르마늄 등 다수종을 첨가하여 36 ℃에서 7일간 발효후 견운모, 점토, 고령토, 백남석, 황토, 규석, 운석등을 분쇄한 것등을 혼합하여 숫성시켜서 1200-1300 ℃로 18시간이상 가열후 덩어리진 것을 분말화한 소재가 상품화되고 있는데 이들중 어느것을 수맥파나 전자파의 산파용 소재로 사용해도 효과는 비슷하다, 그러나 이들 수맥파 및 전자파산파용 소재는 예를 들어 신발깔창의 경우에는 전자의 소재가 적합하고 메트용이거나 실내의 장치 벽지등에는 후자의 소재를 사용해도 무방하다 이외에도 몇가지 더 있으나 어느것을 사용해도 효과에는 큰 차이가 없다About 45% of yellow soil to radiate far-infrared rays to non-woven textile non-woven fabrics, fight and reduce bacterial pathogens, and prevent disease and water wave electromagnetic radiation to recover from fatigue, adsorption deodorization of various circulating odors, and purification of surrounding air. , About 40% for illite or chromite, about 14% for charcoal, and for water vein and electromagnetic wave spreading material, 1% material composed of 55% copper powder and 45% zinc powder is mixed with water. 70% and 30% of water is mixed with 100% of the mixed material, and the nonwoven fabric is impregnated (precipitated) in a nonwoven fabric, and the resulting nonwoven fabric is piled up in duplicate to be heat-compression molded at an appropriate high temperature (160-200 ° C). In other words, it is formed by forming unevenness of male and female on the surface or by passing through a pair of rollers without male and female unevenness. As a material for water-wave rupture, copper and zinc block or scatter water vein or wavelength. Knitting or non-woven materials consisting of synthetic resins or cotton are used, which are generally known and commercially available, and there are two kinds of materials for water wave and electromagnetic wave scattering. Firstly, copper and zinc powders are generally known. Secondly: 30% of feldspar, namseok, and pottery were first heated to 1200-1300 ℃ and then mixed with 30% of crushed 250mesh in 70% of water. After fermentation, mixed with crushed mica, clay, kaolin, dolomite, loess, quartz, meteorite, etc. Powdered materials are commercialized after heating, and any of these materials can be used as midwave or electromagnetic wave midwave material. However, these water wave and electromagnetic wave wave materials are used for example in the case of shoe insole. Material is suitable, and the latter material may be used for mat or indoor device wallpaper, but there are some more but there is no big difference in effect

전자의 산파용 소재인 구리 및 아연분말을 각각 사용하였던 것에서 본발명의 산파용 소재로서는 구리분말 55%와 아연분말 45%를 혼합한 것을 산파용소재로 이용하였다,부직포에 함침시키는 분말원료인 황토, 일라이트 목탄분말 산파용소재등은 250매쉬정도 이하로 미세하게 분쇄한 것을 사용하는데 황토의 경우에는 미세하게 걸러주는 망목(일명; 체)으로 걸러서 사용하며 혼합물을 70%와 물 30%의 비율로 혼합하여 부직포를 침적시켜서 약 20분이상 경과하면 물과 혼합된 혼합물이 부직포에 침투되면 건져서 자연탈수후 160-200℃의 온돌로 가열된 압축로울러에 통과시켜 압축하면 1차 성형품이 성형되며, 1차 성형된 제품은 얇은 벽지, 메트커버 등으로 사용되며 다시 중첩하여 2차성형하면 신발깔창등으로 사용하는 판상의 제품이 제조된다,The former midwife materials copper and zinc powders were used, respectively. As the midwife materials of the present invention, a mixture of 55% copper powder and 45% zinc powder was used as a midwife material, ocher, a powder raw material impregnated into a nonwoven fabric. In the case of loess, the fine charcoal powder is used for the pulverization of less than 250 mesh. In the case of loess, it is used to filter out finely filtered mesh (aka sieve). After about 20 minutes of depositing the nonwoven fabric by mixing with water, the mixture mixed with water penetrates into the nonwoven fabric, is dried and passed through a compression roller heated by ondol of 160-200 ℃ after natural dehydration. The first molded product is used as a thin wallpaper, a mat cover, etc., and when the second molding is overlaid again, a plate-like product used as a shoe insole is manufactured.

이때에 성형로울러 표면에 암수 요철을 구성할 경우 1차나, 2차 성형제품이 요철상(일명; 엠보싱)의 형태로 제조된다,가열압착하는 방법, 맞물려서 회전하는 로울러에 160-200℃의 온도로 가열하여 합성수지 부직포의 경우에는 압축통과하는 과정에서 혼합물을 함침한 상태에서 용착되며, 로울러의 대향되는 쪽에 다수의 암수 요철이 구성되게 하여 맞물려서 압출하면 로울러를 통과하는 과저에서 암수 요철에 의해 섬유직포의 소재가 성형되면 엠보싱 상태의 요철면이 구성된다,At this time, when the male and female irregularities are formed on the surface of the molding roller, the primary and secondary molded products are manufactured in the form of the irregularities (aka embossing), the method of heat pressing, the interlocking roller at a temperature of 160-200 ° C. In the case of synthetic resin nonwoven fabric by heating, it is welded in the state of impregnating the mixture in the passage of compression, and the number of male and female irregularities are formed on the opposite side of the roller. When the material is molded, the uneven surface of the embossed state is formed.

또한 황토, 일라이트, 목탄, 산파소재의 성분이 각기 상이하고 비중 역시 각기 상이하지만 극 미세한 상태의 입자로 분쇄된 분말이 혼합될 때 많은량의 물로서 혼합하지 않으므로 각기 성분데로 분리되지 않으며 경우에 따라서는 식물성의 접합체를 약간 (10%미만) 첨가하여 침적 시키면 부직포에 침적 침투가 용이하고 흡착이 빠르나 접합제는 크게 필요한 경우는 없다,특히 황토, 일라이트, 목탄, 산파소재의 수치를 한정하는 것은 한정된 범위를 약간씩 초과 하거나 미달하여도 제조와 성형후의 효과는 거의 유사하나 황토 45%, 일라이트 40%, 목분 14%, 산파용소재 1%로 수치를 한정 하는 것은 수차례의 실험결과 혼합 조성물의 혼합상태와 부직포에 침투 흡착정도가 가장 우수하다는 점에 있고 각기 성분과 비중이 다른 이들의 혼합, 침투에 적당하기 때문이다,In addition, when the components of ocher, illite, charcoal, and midwife materials are different and their specific gravity are different, but the powders pulverized into extremely fine particles are not mixed as a large amount of water, they are not separated into each component. Therefore, when a small amount (less than 10%) of the vegetable conjugate is added and deposited, it is easy to infiltrate into the nonwoven fabric and the adsorption is fast, but the binder is not required very much, especially in the case of limiting the values of ocher, illite, charcoal, and midwife materials. Although the effect after manufacture and molding is almost similar even though it slightly exceeds or falls short of the limited range, limiting the value to 45% of ocher, 40% of illite, 14% of wood flour, and 1% of midwife material is mixed several times. This is because it has the best penetration and penetration rate in the mixed state of the composition and the nonwoven fabric, and is suitable for mixing and penetrating the different components and specific gravity. Everything,

다음에 이중으로 겹쳐서 가열압착한 것을 용도에 따라서 다르지만 침구메트나 방석등에 사용하는 소재일 경우에는 요철형테를 크게하여 제작한 금형로울러에 통과 시켜서 표면과 이면의 전체가 요철형상인 유연성 판재(板材)로 제작된다,이것을 임의의 싸이즈로 필요에 따라 절단 사용케하며 예를 들어 신발의 내부 깔창의 경우에는 두께를 극히 얇게 성형하여 요철형상이 극히 작도록 성형하여서 발바닥에 지압을 겸하여 악취제거와 병원균인 박테리아균을 살균케하여 장시간 신발을 착용하는 사람에게 상당한 혈액순환과 피로회복에 도움을 주도록 하게된다,또 성형하지 않고 실내의 벽지로 사용케 하는경우에는 아주 얇게 성형하여 초배지로 사용하면 실내에 거주하는 사람에게 혈액순환 촉진 피로회복은 물론 공기의 정화에 효과가 있고 인체에 유해한 전자파, 및 수맥파를 방산시키고 냄새와 병원균을 퇴치 및 감소 시키므로서 쾌적한 실내공간을 만들수가 있게된다,Next, overlapping and heating and pressing the material according to the use differs depending on the use, but in the case of materials used for bedding mats or cushions, a flexible plate having a concave-convex shape of the surface and the back surface is passed through a mold roller made with a large concave-convex frame. This can be cut to any size and used as needed.For example, in the case of the shoe's inner insole, the thickness is extremely thin and the irregularities are formed to be extremely small. It sterilizes bacteria and helps people who wear shoes for a long time to help blood circulation and relieve fatigue.In addition, if they are used as wallpaper in the room without molding, they are molded very thin and used as super medium. It is effective in purifying the circulation of blood and of purifying air, To dissipate the electromagnetic wave, and sumaekpa and thereby create a comfortable indoor space standing because combating and reducing odor and pathogens,

탄소로 이루어진 목탄은 전자를 공급하는 성질과 환원작용이 있으며 산화를 방지하고 악취제거, 불순물여과, 등의 효과가 있는데 일반적으로 땔감 또는 정수기의 물을 여과하는 것에 이용되어 왔고 숯의 특성은첫째 : 탄소로 이루어져 있어서 주변에 전자를 공급하는 성질을 가지고 환원작용을 하며 산화를 방지하는 능력이 있고 산화의 원인은 물질을 이루고 있는 원소가 전자를 상실하는 것이 원인이며, 탄소는 주변에 활발한 전자를 포함하고 있어, 물질이 잃어버린 전자를 공급하는 작용을 하므로 산화작용이 일어나지 않게 된다, 즉 방부제의 효과가 있다.둘째 : 공기중에 양이온 음이온의 발란서를 맞추어서 이온화현상으로 바꾸는 작용도 하여 공기를 맑게하는 작용도 하고,셋째 : 목탄은 기준치의 98% 정도의 원적외선이 발산되고 있는데 원적외선은 인체의 혈행을 좋게하고 살균작용 정기작용 수질개선작용 등이 있고 특히 전자파와 수맥파의 차폐에도 효과가 있으며 전도성이 높아서 낙뇌 방지용에도 이용되며 또한 공기중 양이온이 많을 경우 공기가 급속히 오염되는데 목탄은 음이온을 방사하여 양이온을 흡수하는 이온화 현상으로 냄새를 흡착시킨다, 전자파 및 수맥파 산파용 소재는 인체에 유해한 주변환경으로부터 파생되는 각종 전자파와 수맥파가 비켜가서 산파하도록 인체에 유해함을 방지하고, 황토(loess)은 일반적으로 알려지기에는 가루모양의 산화철로서 보통 점토(粘土)에 혼합되어 있고, 안료, 도료, 리놀륨(linolium) 또는 제지의 원료등에 쓰이고 있는 누르고 거므스름한 흙으로 알려져 있으나 황토에는 기를 방사하고 박테리아 병원균을 퇴치 감소시켜서 질병예방과 수맥파, 전자파 등을 방산시켜서 피로회복, 혈액순환촉진, 각종냄새의 흡착, 탈취 및 주변공기의 정화작용을 하는 것으로 새롭게 대두되고 있다, 본발명은 이들 크로라이드 또는 일라이트(또는 코디라이트) 목탄, 황토등을 이용하여 인간생활에 유익한 소재를 개발한 것이다, 일라이트, 크로라이트 및 코디라이트는 광물학적인 구조가 인편상(운모) 삼층구조를 갖고 있어, 흡수하면 층간 간격이 1.8A정도로 확장되며 2(-)가 전하를 갖는 관계로 용수중 양이온의 부유 미립자와 전기적인 중화로 응집 침전을 유발하여 탁도를 매우향상 시키며 자체 함수기능으로 보습효과가 크고 직사광선을 방지하며 활도가 높다,그리고 일라이트는 상온에서 2∼25마이크로 파장의 원적외선 80%이상 방출하며 흡착력과 원적외선의 이중작용으로 탈취능력이 우수하다,일라이트는 결정구조 특성의 흡착력과 원적외선 방사의 복합상승이 높으며 인체에 무해하고 원적외선 방사로서 산업폐수의 정수제, 상수도 처리시 청동제, 피부보습제, 탈취, 탈색등으로 이용되며 독소 배양억제와 정균작용으로 신선도 유지 생물의 생육촉진 혈액순환 수질의 정수조절 작용의 효과가 있으며, 일라이트(lilite)는 접촉열 수변성 점토질광물로서 몇가지로 나눌 수 있는데첫째 ; 광물학적 구조가 삼층인 편상구조를 갖이며 주성분은 SiO2, Al2O3, K2O, 광물질의 분자식은 Kal4,(Alsi7 O2O) (OH)4 이며 황백색의 합성물질인데 상온에서 3-25마이크로 파장의 원적외선을 89-92%방사한다, 여기서 코디라이트(2MSO,2Al₂O₃,5SiO₂)가 원적외선 방사는 일라이트에 비하여 다소 높은 것으로 알려져 있어 일라이트 대신에 크로라이트 또는 코디라이트 사용이 더욱 효율적이다,둘째 : 일라이트는 98%의 탈취력이 있고 강력한 기를 발산하며 수중에서는 물분자를 활성화 시켜 용존산소를 3배이상 확보하고 산소응집력이 강하며 용수중에 양이온 유기질이온을 흡착하고,셋째 : 직사광선을 방지하며 산소, 원적외선, 음이온, 기등에 의하여 토양의 지력을 향상시키며 강력한 음이온을 발산한다,넷째 : 이와 같은 일라이트 또는 크로라이트나 코디라이트를 섬유 부직포 및 직포의 소재로 이용케함으로서 악취제거, 피부보호, 충균방지, 피로회복, 수맥파의 차단등의 효과를 얻고자 하는 것이다.Charcoal made of carbon has the property of supplying electrons and reducing effect, prevents oxidation, removes odor, impurity filtration, etc. It is generally used to filter fire or water of water purifier. It is composed of carbon and has the property of supplying electrons to the surroundings, it has a reductive action and ability to prevent oxidation, and the cause of oxidation is caused by the loss of electrons by the elements in the material, and carbon contains active electrons in the surroundings. As the substance acts to supply the lost electrons, the oxidation does not occur, that is, it has the effect of preservatives. Second: It acts to change the ionization phenomena by matching the balance of cation anion in the air and to clean the air. And third: charcoal emits far infrared rays about 98% of the standard value. It improves blood circulation of the human body, sterilization, regular action, water quality improvement, and especially, it is effective for shielding electromagnetic and water waves, and it is used for prevention of falling brain due to its high conductivity. Also, if there are a lot of cations in the air, air is rapidly polluted. It absorbs odors by ionizing phenomenon that absorbs cations and absorbs cations. Electromagnetic wave and water wave material for midwife prevents harmful to human body so that various electromagnetic waves and water wave derived from surrounding environment harmful to human body deviate and spread, and loess ) Is generally known as powdery iron oxide, usually mixed with clay, and known as dark reddish soil used for pigments, paints, linolium, or raw materials for papermaking. To reduce bacterial pathogens and prevent disease It is newly emerging as a method of recovering fatigue, promoting blood circulation, adsorbing various odors, deodorizing, and purifying ambient air. The present invention is directed to these chromides, illite (or cordierite) charcoal, loess, etc. It has developed materials that are beneficial to human life.Ilite, chromite and cordierite have a mineral layer of flaky (mica) three-layer structure, and when absorbed, the interlayer spacing is extended to 1.8A and 2 (-). Due to its electric charge, suspended particles of cations in the water and electrical neutralization cause coagulation precipitation, which greatly improves turbidity.Its self-hydrating function has a great moisturizing effect, prevents direct sunlight, and has high activity. It emits more than 80% of far infrared rays with a wavelength of ～ 25 microns and has excellent deodorizing ability due to the double action of adsorption power and far infrared rays. It has high compound adsorption capacity and far-infrared radiation, and it is harmless to human body. It is far-infrared radiation and used as water purification agent of industrial wastewater, bronze agent, water moisturizer, deodorization, decolorization, etc. It has the effect of purifying blood circulation water purification, and illite (lilite) can be divided into several kinds as contact heat-modified clay minerals. It has a three-layered mineralogy structure, and its main component is SiO2, Al2O3, K2O, and the molecular formula of Kal4, (Alsi7 O2O) (OH) 4 is a yellowish white synthetic material, which is 3-25 microwave far-infrared at room temperature. -92%, where the far-infrared radiation of cordierite (2MSO, 2Al ₂ O ₃ , 5SiO ₂ ) is known to be somewhat higher than that of elite, making it more efficient to use chromite or cordierite instead of elite. Ilite has 98% deodorizing power and emits strong groups, activating water molecules in water to secure dissolved oxygen more than three times, oxygen aggregation ability is strong, adsorbing cationic organic ions in water, and third: preventing direct sunlight, oxygen, The far infrared rays, anions, and the like improve the soil's intellect and emit strong anions. Port and by Cain used as the material of the woven fabric to obtain the effects such as odor removal, skin protection, anti chunggyun, fatigue, blocked sumaekpa.

이와 같이 본발명이 섬유부직포의 소재는 침구용메트 방석은 물론 베개커버등에 사용할 경우에는 요철상으로 성형하여 지압효과를 겸하고 신발깔창, 벽지등으로 사용할 경우에는 두께를 조절하여 판상으로 성형하여 용도에 따라서 사용하면 공기정화, 냄세제거, 박테리아병원균 퇴치는 물론 원적외선 발생으로 피로회복, 혈액순환 촉진은 물론 전자파와 수맥파까지 산파케 함으로서 각종 인체주변 물품에 이용할수 있는 효과적인 것이다.In this way, the material of the textile nonwoven fabric of the present invention is formed into an uneven shape when used for a pillow cover, as well as a mat mat for bedding, and serves as an acupressure effect, and when used as a shoe insole or a wallpaper, it is molded into a plate shape by controlling the thickness. Therefore, when used, it is effective to be used for various objects around the human body by removing air path, removing odors, eradicating bacterial pathogens, recovering fatigue, promoting blood circulation, and scattering electromagnetic waves and water waves as well as generating far infrared rays.

Claims

A fibrous nonwoven fabric of appropriate thickness is added by mixing 45% ocher, 40% illite, 14% charcoal, and 1% suede midwife material in an appropriate amount of water, impregnating and adsorbing it on a nonwoven fabric, and compressing it by heating. A material of far-infrared textile woven fabric, characterized in that it is heated and pressed at high temperature to be formed into an uneven plate or plate.