KR100239507B1 - Compound for the spray type waterborn vibration reduction material - Google Patents
Compound for the spray type waterborn vibration reduction material Download PDFInfo
- Publication number
- KR100239507B1 KR100239507B1 KR1019970052510A KR19970052510A KR100239507B1 KR 100239507 B1 KR100239507 B1 KR 100239507B1 KR 1019970052510 A KR1019970052510 A KR 1019970052510A KR 19970052510 A KR19970052510 A KR 19970052510A KR 100239507 B1 KR100239507 B1 KR 100239507B1
- Authority
- KR
- South Korea
- Prior art keywords
- water
- soluble
- parts
- resin
- vibration damping
- Prior art date
Abstract
이 발명은 스프레이 타입 수용성 제진재(vibration reduction Material)를 제안하려는 것으로, 특히 환경 친화적으로 온도 의존성이 낮은 스프레이 타입 수용성 제진재 및 그 조성물이다. 이 발명은 수용성 폴리머 20~30부, 무기필러 30~35부, 접착성을 부여하기 위한 첨가제 수지류 10-20부, 경화제 0.5~1부, 물 20~30부, 탄성증가제 및 접착성 증가제를 믹서에 혼합 반응시켜 얻는 점도 10,000~100,000cpThe present invention intends to propose a spray type water-soluble vibration damping material, and in particular, a spray-type water-soluble damping material and composition thereof having low temperature dependence in an environmentally friendly manner. The present invention is 20-30 parts of water-soluble polymers, 30-35 parts of inorganic fillers, 10-20 parts of additive resins for imparting adhesiveness, 0.5-1 part of curing agent, 20-30 parts of water, elasticity increasing agent and increased adhesion 10,000 to 100,000 cps obtained by mixing and reacting agents in a mixer
s의 조성물을 피착제에 스프레이로 부여하고 가열 경화하여 얻는다. 이 발명의 물성은 제진계수(tan δ) 0.1~0.5 경도(shore A type) 90이상이다. 이 발명에 의하면 제진제 조성물이 수용성 이므로 그 적용공정이 환경친화적이고 가벼우며, 스프레이 타입 수용성 제진재로서 로봇에 의한 자동화 공정에서 이용할 수 있고; 피착재로서 금속, 도금강판, 알미늄, 마그네슘, 스테인레스스틸에서 강한 접착력을 가지며; 제진계수(tan δ) 0.1~0.5가 되는 것이다.The composition of s is obtained by spraying and adhering to the adherend. The physical properties of the present invention have a damping coefficient (tan δ) of 0.1 to 0.5 hardness (shore A type) of 90 or more. According to this invention, since the vibration damping agent composition is water-soluble, its application process is environmentally friendly and light, and can be used in an automated process by a robot as a spray-type water-soluble vibration damping material; As the adherend, it has strong adhesion in metal, plated steel, aluminum, magnesium and stainless steel; The damping coefficient (tan δ) is 0.1 to 0.5.
Description
이 발명은 스프레이 타입 수용성 제진재(Vibration reduction Material)를 제안하려는 것으로, 특히 환경 친화적이고 온도 의존성이 낮은 스프레이 타입 수용성 제진재 및 그 조성물에 관한 것이다.The present invention intends to propose a spray type water-soluble vibration damping material, and more particularly, relates to a spray-type water-soluble vibration damping material and its composition which are environmentally friendly and low in temperature dependence.
제진재는 성상에 따라 고체 타입(nonreactive type)와 액체 상태에서 고체로 변화하는 타입(reactive type)으로 분류 할 수 있으며, 특히 스프레이 타입의 액체상태 제진재 로서는 유용성(가소제, Solvent 매체)과 수용성(H2O를 매체로 하는 것을 포함)으로 나눌 수 있다.Vibration dampers can be classified into solid type (nonreactive type) and liquid type (reactive type) according to their properties. Especially, as a spray type liquid damping material, it is useful (plasticizer, solvent media) and water-soluble ( And H 2 O as a medium).
스프레이 가능한 액상타입 제제는 유기 용매에서 발생하는 VOC의 문제, 오존파괴 문제 등 생태계에 미치는 영향이 심각하므로 환경 친화적 수용성 스프레이 제제의 형태로 전환되어 가고 있다.Sprayable liquid-type preparations are being converted to environmentally friendly water-soluble spray preparations because of their serious impact on the ecosystem, such as VOC problems and ozone depletion problems.
자동차 산업은 차체의 경량화, 엔진의 고출력화에서 소음과 진동 문제가 핫이슈로 되어 있다. 이에 대한 방음, 제진재의 개발이 급속이 진전되고 있다.In the automobile industry, noise and vibration problems are hot issues in light weight of the vehicle body and high engine power. The development of soundproofing and damping materials is progressing rapidly.
방음, 제진재 중에서 대표적인 아스팔트 시트는 1960년대 후반부터 자동차의 차상(floor)에 사용되어 지금까지 제진재의 주류를 이루고 있다. 사용량은 승용차 1대에 10~20kg 정도로서 차체에 사용되는 비금속 재료 사용량 가운데 가장 큰 비중을 차지하고 있다. 아스팔트는 유용성이고 열경화시켜 사용되므로 가열 경화시 발생하는 VOC의 문제, 냄새(악취)등 환경 파괴적 요소와 차량의 화재시에 매연 발생과 함께 인명 피해의 위험을 내포하고 있으며, 제진재 부여 공정에 인력 배치가 크게 되는 문제점이 있는 것이다. 또한 제진 성능을 보더라도 낮은 온도(20℃)에서의 제진 성능은 양호하나(도1 그래프 참조) 높은 온도(40℃, 60℃)에서 제진성능이 급격히 감소하는 치명적인 결점을 가지고 있는 것이다.Asphalt sheets, which are representative of soundproofing and vibration damping materials, have been used in automobile floors since the late 1960s and have been the mainstream of vibration damping materials. The amount used is about 10-20kg per passenger car, accounting for the largest share of nonmetallic materials used in the car body. As asphalt is useful and thermally cured, it contains environmental destructive elements such as VOC problems, odors (odors) generated during heat curing, and smoke in the event of a vehicle fire. There is a problem that the manpower deployment is large. In addition, the vibration damping performance is good even at low temperatures (20 ℃) (see Fig. 1 graph), but at a high temperature (40 ℃, 60 ℃) has a fatal defect that the sharp reduction in vibration performance.
위와 같은 환경파괴 요소와 화재시의 위험성을 내포하고 있는 아스팔트 제진재는 자동차 산업 분야에서 대량으로 사용되고 있어 대체용 제진재가 요구되고 있으며, 자동차 외의 산업분야에서도 환경친화적이고 위험성이 없는 대체 제진재가 요구되고 있다.Asphalt vibration damping materials, which contain such environmental destructive elements and fire hazards, are being used in large quantities in the automotive industry, requiring replacement of vibration damping materials. It is required.
이 발명의 목적은 환경 파괴적이고 제진기능에서 온도 의존성이 큰 아스팔트 고체 타입 제진재에 대체하여 사용 할 수 있는 제진재로서 환경 친화적이고 온도 의존성이 낮은 스프레이 타입 수용성(수 분산성을 포함한다) 제진재 조성물 및 제진재를 제안함에 있다.An object of the present invention is to use an environmentally friendly and low temperature dependent spray type water-soluble (including water dispersibility) vibration damping material that can be used as an alternative to asphalt solid type vibration damping materials having high environmental dependence and vibration damping function. A composition and vibration damper are proposed.
이 발명의 다른 목적은 피착물의 하중을 줄일 수 있는 경량화 제진재를 제공함에 있다.Another object of the present invention is to provide a light weight vibration damper that can reduce the load of the adherend.
이 발명의 다른 목적은 제진재를 부여하는 공정에서 스프레이 할 수 있게 하므로 로봇에 의한 자동차 시공을 가능하게 하는 스프레이 타입 수용성 제진재 조성물을 제공함에 있다.Another object of the present invention is to provide a spray-type water-soluble vibration damper composition which enables spraying in a process of imparting a vibration damping material, thereby enabling automobile construction by a robot.
이 발명은 수용성 폴리머인 아크릴계 폴리머와 수 분산성 폴리머인 아크릴코폴리머 에멀젼, EVA(에틸렌-비닐아세테이트 공중합물), EVA 터폴리머 에멀젼, 천연고무(라텍스), 합성고무(라텍스)등을 이용한 합성물을 제공함을 특징로 한다.The present invention is a composite using an acrylic polymer which is a water-soluble polymer and an acrylic copolymer emulsion which is a water dispersible polymer, EVA (ethylene-vinylacetate copolymer), EVA terpolymer emulsion, natural rubber (latex), synthetic rubber (latex), etc. It is characterized by providing.
이 발명의 제진재는 금속, 도금강판, 알미늄, 마그네슘, 스테인레스스틸에 대한 강한 접착력을 가지며, 제진계수(tan δ)가 0.1~0.5이고, 제진성능은 온도 의존성이 적고, 자동화 공정에서 로봇에 의한 스프레이 시공을 할 수 있는 열경화성제진재이다.The vibration damping material of the present invention has strong adhesion to metal, plated steel, aluminum, magnesium, and stainless steel, has a vibration damping coefficient (tan δ) of 0.1 to 0.5, and the vibration damping performance is less temperature dependent, It is a thermosetting vibration damper that can be sprayed.
제1도는 아스팔트시트와 스프레이 타입 수용성 제진재의 성능을 비교한 그래프.1 is a graph comparing the performance of the asphalt sheet and spray type water-soluble vibration damper.
이 발명은 수용성 폴리머인 폴리아크릴산소다 또는 폴리아크릴산아마이드나, 수 분산성 폴리머인 아크릴 코폴리머 에멀젼, EVA(에틸렌-비닐아세테이트 공중합물), EVA 터폴리머 에멀젼, 천연고무(라텍), 합성고무(라텍스) 등을 포함하는 수용성 폴리머를 포함하는 조성물로 구성한다. 이 발명에서, 수용성 폴리머라 함은 물에 용해하는 폴리머는 물론이고 물에 용해되지 않고 분산 상태를 유지하는 수분산성 폴리머를 포함한다.The present invention relates to polyacrylic acid or polyacrylamide as a water-soluble polymer, acrylic copolymer emulsion as a water dispersible polymer, EVA (ethylene-vinylacetate copolymer), EVA terpolymer emulsion, natural rubber (latec), synthetic rubber (latex). It consists of the composition containing the water-soluble polymer containing). In this invention, the water-soluble polymer includes not only a polymer which dissolves in water but also a water-dispersible polymer which does not dissolve in water and maintains a dispersed state.
이 발명 스프레이 타입 수용성 제진재의 제조방법은 다음과 같다.The manufacturing method of this invention spray type water-soluble vibration damper is as follows.
조성물 중량부수 비고Weight by Composition Remarks
수용성폴리머 20~30 물과 함께 에멀젼으로 제조함Water Soluble Polymer 20 ~ 30 Prepared in emulsion with water
무기충진재(Filler) 30~40Inorganic Filler (Filler) 30 ~ 40
수지첨가제(additive) 9.5~20 접착성을 부여하기위한 수지류Additives 9.5 ~ 20 Resins for imparting adhesion
경화제(Curing agent) 0.5~1Curing agent 0.5 ~ 1
물(H2O) 20~30Water (H 2 O) 20 ~ 30
이 발명에 사용하는 수용성 폴리머로서는 폴리아크릴산소다 및 폴리아크릴산아마이드가 있으며, 수 분산성 폴리머로서는 아크릴 코폴리머, 에틸렌-비닐아세테이트 공중합물(EVA), EVA 터폴리머, 천연고무 및 합성고무 라텍스를 포함하는 폴리머 중에서 하나 이상을 선택하여 사용할 수 있다.Water-soluble polymers used in this invention include polyacrylic acid sodium and polyacrylamide amide, and water dispersible polymers include acrylic copolymer, ethylene-vinylacetate copolymer (EVA), EVA terpolymer, natural rubber and synthetic rubber latex. One or more polymers can be selected and used.
필러로서는 탄산칼슘(CaCO3), 탄산마그네슘(MgCO3), 탈크(talc), 운모(Mica), 고령토(Kaoline), 흑연(Graphite), 황화몰리브덴(MoS2) 및 산화규소(SiO2)를 포함하는 무기필러 중에서 하나 이상을 선택하여 사용한다.The fillers include calcium carbonate (CaCO 3 ), magnesium carbonate (MgCO 3 ), talc, mica (Mica), kaolin, graphite (Graphite), molybdenum sulfide (MoS 2 ) and silicon oxide (SiO 2 ). Select one or more of the inorganic fillers included.
접착성을 부여하는 첨가제(Additive)수지로는 테르펜 페놀 수지, 수첨 로진, 석유수지, 크실렌수지 및 쿠마론(Cumarone)수지를 포함하는 접착성 수지 중에서 하나 이상 선택하여 사용한다.As an additive resin for imparting adhesiveness, one or more of an adhesive resin including terpene phenol resin, hydrogenated rosin, petroleum resin, xylene resin, and coumarone resin is used.
상기 수지첨가제에 탄성증가제로서 피부이시 페스트레진(중합도 560~1300)을 포함시킬 수 있다.The resin additive may include skin-ish pest resin (polymerization degree 560-1300) as an elasticity increasing agent.
상기 수지첨가제에 저온에서 제진성능의 향상하기 위하여 자체결합(selfcrosslinked) 에틸비닐아세테이트와 같은 부분가교 타입 및 Tg가 높은 EVA수지를 포함시킬 수 있다.In order to improve the vibration damping performance at low temperature, the resin additive may include a partially crosslinked type such as self-crosslinked ethyl vinyl acetate and a high Tg EVA resin.
경화제는 메탈릭 아크릴레이트, 트리메틸롤프로판메타크릴레이트(TMPTMA), 아미드 등을 사용 한다.Curing agents include metallic acrylate, trimethylolpropane methacrylate (TMPTMA), amide and the like.
상기 수지첨가제에 제진성능 및 피착재 금속, 알미늄, 마그네슘, 스테인레스스틸에 대한 접착력 향상을 위하여 아크릴레이트 및 알릴레이트를 포함하는 메탈릭코에이젠트 하나 이상을 경화(가교)성분으로 수지첨가물에 포함시킬 수 있다.One or more metallic coagents including acrylate and allylate may be included in the resin additive as a hardening (crosslinking) component in order to improve the damping performance and adhesion to the metal, aluminum, magnesium, and stainless steel in the resin additive. have.
상기 배합물을 혼합기(Kneader, 디졸바, 기타믹서)에 투입하여 상온(20~25℃)에서 24시간 전후로 교반하여 점도10,000~100,000cps(Brookfield/Viscometer)의 피이스트상 콤파운드로 제조한다.The mixture is added to a mixer (Kneader, dissolva, other mixers) and stirred at room temperature (20-25 ° C.) for about 24 hours to prepare a pist phase compound having a viscosity of 10,000 to 100,000 cps (Brookfield / Viscometer).
제조된 콤파운드는 피착재에 도포하고 열원(적외선, 전열)을 이용하여 140~200℃에서 10~60분정도 가열처리 하면 경화되어 제진재로서의 성능을 발휘 하게 된다(자동차 산업의 경우 페인트 라인의 열원에 의존한다).The prepared compound is applied to the adherend and heat-treated at 140 ~ 200 ℃ for 10 ~ 60 minutes using a heat source (infrared rays, heat transfer) to harden and show its performance as a vibration damper. Depends on).
이 발명 스프레이 타입 수용성 제진재와 아스팔트시트의 제진 성능을 그라프로 비교하면 도1과 같다. 도1에서 아스팔트시트는 상온에서 초기제진계수가 40℃와 60℃에서 급격히 낮아지고 있으나 이 발명 제진재는 40℃에서 제진성능이 초기성능의 2배이상이 되고 60℃에서도 초기 제진 성능을 능가 하였다.When the dust removal performance of this invention spray type water-soluble vibration damper and an asphalt sheet is compared with a graph, it is as FIG. As shown in Fig. 1, the initial damping coefficient of the asphalt sheet is rapidly decreased at 40 ° C. and 60 ° C. at room temperature. .
[실시예 1]Example 1
금속과의 접착력 증대를 위하여 EVA 및 EVA-스티렌 터폴리머를 첨가한 스프레이 타입 수용성 제진재 조성물Spray type water-soluble vibration damper composition containing EVA and EVA-styrene terpolymer to increase adhesion to metal
조성물 중량비 비고Composition weight ratio Remarks
에틸비닐아세테이트코폴리머 20 터폴리머 사용가능Ethyl Vinyl Acetate Copolymer 20 Terpolymer Available
테르펜 페놀수지 2~5Terpene Phenolic Resin 2 ~ 5
운모 20Mica 20
탄산칼슘(CaCO3) 20Calcium Carbonate (CaCO 3 ) 20
TMPTMA 0.5~1 제진성능 및 금속 접착력 향상TMPTMA 0.5 ~ 1 Dust Removal Performance and Metal Adhesion Improvement
물 45Water 45
발포제 0.5Blowing Agent 0.5
상기 배합물을 혼합기에 투입하고 상온(20~25℃)에서 24시간 교반시켜 스프레이 가능한 수용성 제진재 조성물을 얻었다.The compound was added to a mixer and stirred at room temperature (20-25 ° C.) for 24 hours to obtain a sprayable water-soluble vibration damping composition.
실시예 1의 스프레이 타입 제진재의 성능은 다음과 같다.The performance of the spray type vibration damper of Example 1 is as follows.
도막무게(젖은상태) ; 17gCoating weight (wet state); 17 g
도막무게(마른상태) ; 10.5gCoating weight (dry); 10.5 g
도막두께 ; 4.1mmFilm thickness; 4.1mm
점도(cps, brook field) ; 40,000~50,000Viscosity (cps, brook field); 40,000 ~ 50,000
손실계수의 측정Loss Factor Measurement
측정방법How to measure
측정 ; Dual-ch spectrum averagingMeasure ; Dual-ch spectrum averaging
주파수 ; 16KHzfrequency ; 16KHz
Δf ; 2HzΔf; 2 Hz
T ; 500msT; 500 ms
Δt ; 244μsΔt; 244 μs
측정결과Measurement result
손실계수(tan δ) 20℃ ; 0.15이상Loss factor (tan δ) 20 ° C .; 0.15 or more
손실계수(tan δ) 40℃ ; 0.20이상Loss factor (tan δ) 40 ° C .; 0.20 or more
손실계수(tan δ) 60℃ ; 0.12이상Loss factor (tan δ) 60 ° C .; 0.12 or more
표면경도(KS M6518 shore A type) ; 90이상Surface hardness (KS M6518 shore A type); over 90
금속과의 접착력 ; 응집파괴Adhesion to metal; Cohesive failure
[실시예 2]Example 2
저온에서 제진성능 향상을 위해 부분가교 타입 및 Tg가 높은 EVA사용한 스프레이 타입 수용성 제진재 조성물Spray type water-soluble vibration damper composition using partial crosslinking type and high Tg EVA to improve vibration damping performance at low temperature
조성물 중량비 비고Composition weight ratio Remarks
EVA 코폴리머 13.5EVA copolymer 13.5
자체결합 에틸비닐아세테이트 10 저온 제진성능개선Self-bonding ethyl vinyl acetate 10 improved low temperature vibration damping performance
테르펜 페놀 수지 2~5Terpene Phenolic Resin 2 ~ 5
운모 40
TMPTMA 0.5 접착성 개선Improved TMPTMA 0.5 adhesion
발포제 0.5Blowing Agent 0.5
물 50Water 50
제조법은 실시예 1과 같다.The manufacturing method is the same as in Example 1.
실시예 2의 스프레이 타입 제진재의 성능은 다음과 같다.The performance of the spray type vibration damper of Example 2 is as follows.
도막무게(젖은상태) ; 20.7gCoating weight (wet state); 20.7 g
도막무게(마른상태) ; 11.99gCoating weight (dry); 11.99 g
도막두께 ; 3.9.1mmFilm thickness; 3.9.1mm
점도(cps, brook field) ; 40,000~50,000Viscosity (cps, brook field); 40,000 ~ 50,000
손실계수(측정방법 실시예1과 동일함)Loss Factor (Same as Measurement Method Example 1)
손실계수(tan δ) 20℃ ; 0.18이상Loss factor (tan δ) 20 ° C .; 0.18 or more
손실계수(tan δ) 40℃ ; 0.25이상Loss factor (tan δ) 40 ° C .; 0.25 or more
손실계수(tan δ) 60℃ ; 0.15이상Loss factor (tan δ) 60 ° C .; 0.15 or more
표면경도(KS M6518 shore A type) ; 90이상Surface hardness (KS M6518 shore A type); over 90
금속과의 접착력 ; 응집파괴Adhesion to metal; Cohesive failure
[실시예 3]Example 3
표면경도의 극대화로 손실계수 및 접착력의 향상하고 있는 스프레이 타입 제진재 조성물Spray type vibration damper composition improves loss factor and adhesion by maximizing surface hardness
조성물 중량비 비고Composition weight ratio Remarks
EVA 20EVA 20
테르펜 페놀 수지 2~5Terpene Phenolic Resin 2 ~ 5
운모 20Mica 20
CaCO320CaCO 3 20
피부이시 페스트레진 10 중합도 560~1300(탄성증가재)Dermatitis Pastresin 10 Polymerization Degree 560 ~ 1300
TMPTMA 0.5TMPTMA 0.5
발표제 0.5Presentation 0.5
물 42Water 42
제조법은 실시예 1과 같다.The manufacturing method is the same as in Example 1.
실시예 3의 스프레이 타입 제진재의 성능은 다음과 같다.The performance of the spray type vibration damper of Example 3 is as follows.
도막무게(젖은상태) ; 19gCoating weight (wet state); 19 g
도막무게(마른상태) ; 12gCoating weight (dry); 12g
도막두께 ; 4.3mmFilm thickness; 4.3mm
점도(cps, brook field) ; 40,000~50,000Viscosity (cps, brook field); 40,000 ~ 50,000
손실계수(측정방법 실시예 1과 동일함)Loss Factor (Same as Measurement Method Example 1)
손실계수(tan δ) 20℃ ; 0.18이상Loss factor (tan δ) 20 ° C .; 0.18 or more
손실계수(tan δ) 40℃ ; 0.25이상Loss factor (tan δ) 40 ° C .; 0.25 or more
손실계수(tan δ) 60℃ ; 0.16이상Loss factor (tan δ) 60 ° C .; 0.16 or more
표면경도(KS M6518 shore A type) ; 95이상Surface hardness (KS M6518 shore A type); 95 or more
금속과의 접착력(자사방법) ; 응집파괴Adhesion to metal (own method); Cohesive failure
상기와 같이 이 발명은 수용성 폴리머로서 아크릴, 수 분산성 폴리머로서 아크릴 코폴리머 에멀젼, EVA, EVA 터폴리머 에멀젼, 천연고무, 합성고무를 사용한 수용성 합성물로서 그 적용공정이 환경 친화적이며; 가볍고; 스프레이 타입 수용성 제진재로서 로봇에 의한 자동화 공정에서 이용할 수 있고; 피착재로서 금속, 도금강판, 알미늄, 마그네슘, 스테인레스스틸에서 강한 접착력을 가지며; 제진계수(tan δ) 0.1-0.5이고; 제진성능은 온도 의존성이 적은 스프레이 타입 수용성 제진재를 제공하는 것이다.As described above, the present invention is an aqueous process using acrylic as water-soluble polymer, acrylic copolymer emulsion as water-dispersible polymer, EVA, EVA terpolymer emulsion, natural rubber, synthetic rubber, and its application process is environmentally friendly; Light; It can be used in the automated process by a robot as a spray type water-soluble vibration damper; As the adherend, it has strong adhesion in metal, plated steel, aluminum, magnesium and stainless steel; Damping coefficient (tan δ) of 0.1-0.5; The vibration damping performance is to provide a spray type water-soluble vibration damping material with little temperature dependence.
Claims (4)