KR100204107B1 - Pattern board for interior decoration and making method thereof - Google Patents

Pattern board for interior decoration and making method thereof Download PDF

Info

Publication number
KR100204107B1
KR100204107B1 KR1019970003537A KR19970003537A KR100204107B1 KR 100204107 B1 KR100204107 B1 KR 100204107B1 KR 1019970003537 A KR1019970003537 A KR 1019970003537A KR 19970003537 A KR19970003537 A KR 19970003537A KR 100204107 B1 KR100204107 B1 KR 100204107B1
Authority
KR
South Korea
Prior art keywords
plate
paper
night light
resin impregnated
pattern
Prior art date
Application number
KR1019970003537A
Other languages
Korean (ko)
Other versions
KR970020422A (en
Inventor
심응문
Original Assignee
심응문
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 심응문 filed Critical 심응문
Priority to KR1019970003537A priority Critical patent/KR100204107B1/en
Publication of KR970020422A publication Critical patent/KR970020422A/en
Application granted granted Critical
Publication of KR100204107B1 publication Critical patent/KR100204107B1/en

Abstract

본 발명은 밤라이트 판의 표면에 표면재가 형성되도록 한 것으로서, 특히, 밤라이트 판의 표면에 페놀수지 함침지 및 멜라민수지 함침무늬지가 적층, 압착되어 선택된 무늬에 의해서 미감을 느낄 수 있음은 물론, 고품질의 제품을 얻을 수 있도록 구성된 밤라이트 무늬판 및 그 제조방법에 관한 것이다.According to the present invention, the surface material is formed on the surface of the chestnut plate, and in particular, the phenolic resin-impregnated paper and the melamine resin-impregnated paper are laminated and pressed on the surface of the chestnut plate, so that the aesthetics may be felt by the selected pattern. It relates to a night light patterned plate configured to obtain a high quality product and a manufacturing method thereof.

하측으로부터 페놀수지함침지(1b), 밤라이트판(1c), 페놀수지 함침지(1b), 멜라민수지 함침무늬지(1a)의 순서로 적층된 상태에서 130° - 190℃의 온도와 50-90kg/cm2의 압력으로 15 ~ 30분간 동시에 프레싱 작동을 실시한 후, 50 ~ 70℃의 온도로 냉각하여 밤라이트 무늬판(1)을 제조하는 것을 특징으로 하고 있으며, 대량생산을 할 수 있게 되어 생산성 향상 및 원가절감이 됨은 물론 무늬들이 형성되어 있는 고품질의 제품을 얻을 수 있게 되며, 장구히 사용할 수 있는 효과가 있다.Temperature of 130 ° -190 ° C and 50- in a state of being laminated from the lower side in the order of phenol resin impregnated paper (1b), night light plate (1c), phenol resin impregnated paper (1b), and melamine resin impregnated pattern paper (1a). Pressing at the same time for 15 to 30 minutes at a pressure of 90kg / cm 2 , and then cooled to a temperature of 50 ~ 70 ℃ to produce a night light pattern plate (1), it is possible to mass production In addition to improving productivity and reducing costs, it is possible to obtain a high quality product in which patterns are formed, and can be used for a long time.

Description

밤라이트 무늬판 및 그 제조방법Night light pattern plate and manufacturing method

제1도는 본 발명의 밤라이트 무늬판의 동단면도이다.1 is a cross-sectional view of the night light pattern plate of the present invention.

* 도면의 주요부분에 대한 부호의 설명* Explanation of symbols for main parts of the drawings

1 : 밤라이트 무늬판 1a : 멜리민수지 함침무늬지1: night light pattern 1a: melamine resin impregnated pattern paper

1b : 페놀수지 함침지 1c : 밤라이트 판1b: phenol resin impregnated paper 1c: night light plate

[기술분야][Technical Field]

본발명은 밤라이트 판의 표면에 표면재가 가열 압착되어서 형성되도록 한 것으로서, 특히, 밤라이트 판의 표면에 멜라민수지 함침무늬지 및 페놀수지 함침지가 적층, 압착되어 선택된 무늬에 의해서 미감을 느낄 수 있음은 물론, 고품질의 제품을 얻을 수 있도록 구성된 밤라이트 무늬판 및 그 제조 방법에 관한 것이다.According to the present invention, the surface material is formed by heating and compressing the surface of the nightlight plate, and in particular, the surface of the nightlight plate may be aesthetically sensitized by the selected pattern by laminating and pressing the melamine resin-impregnated pattern paper and the phenol resin-impregnated paper. Of course, it relates to a night light patterned plate and a manufacturing method thereof configured to obtain a high quality product.

[발명의 배경][Background of invention]

일반적으로 빌딩, 사무실, 호텔, 점포, 아파트, 주택 등의 간막이 벽 및 천정의 마감용 미장재로서 불연내장재인 밤라이트 판이 사용되고 있다. 종래에 사용되었던 밤라이트 판은 그 재질의 특성으로 인하여 밤라이트판 자체에 무늬를 형성하기 곤란하여 밤라이트 판에 수성 또는 유성 페인트를 도포하여서 사용하는 것으로서, 이와같은 밤라이트 판은 밤라이트 판자체내에서 분진이 발생하여 인체에 해로우며, 필요시마다 세척을 해야하고, 표면강도가 약한 문제점이 있었고, 다른 일례로서, 밤라이트 판에 벽지 등 얇은 종이를 부착시켜서 사용하는 방법이 있었으나 이는 종이가 베껴지는 탈피현상이 발생되었으며, 또 다른 일례로서, 밤라이트 판에 부착되는 얇은 종이에 투명도료를 도포하는 방법도 상기와 마찬가지로 탈피현상이 발생하는 등 내화학약품성, 내오염성, 내열수(熱水)성 및 내굻힘성이 약한 문제점이 있었다.In general, a non-combustible night light plate is used as a plaster for finishing walls and ceilings of buildings, offices, hotels, stores, apartments, houses, and the like. Conventionally, the nightlight plate is difficult to form a pattern on the nightlight plate itself due to the characteristics of the material, and is used by applying an aqueous or oil paint to the nightlight plate. Dust is harmful to the human body due to the occurrence of dust, the need to wash whenever necessary, the surface strength was weak problem, as another example, there was a method to use a thin paper such as wallpaper attached to the night light plate, but this is a paper copy Peeling phenomenon has occurred, and as another example, the method of applying a transparent paint to the thin paper attached to the night light plate, such as the peeling phenomenon occurs, such as chemical resistance, fouling resistance, hot water resistance And there was a problem of weak resistance to resistance.

또한, 밤라이트 판 위에 멜라민판을 접착해서 사용하는 방법은 내접착성, 내열수성이 약하고, 표면이 균일하지 못한 문제점이 있었다.In addition, the method of adhering and using the melamine plate on the chestnut plate has a problem of poor adhesion and hot water resistance and uneven surface.

[발명의 목적][Purpose of invention]

본 발명은 상기 종래 밤라이트 판의 문제점을 해소하기 위해서 밤라이트 판의 표면과 이면에 표면재가 적층, 압착되도록 함으로서, 내화학약품성, 내오염성, 내열수성, 내굻힘성, 내접착성이 강하고, 표면이 균일한 명이 이루어질 수 있게 하면서 표면에 무늬도 나타낼 수 있도록 한 밤라이트 무늬판 및 그 제조방법을 제공하는데 그 목적이 있다.The present invention is to solve the problems of the conventional nightlight plate by laminating and compressing the surface material on the surface and the back surface of the nightlight plate, chemical resistance, fouling resistance, hot water resistance, crush resistance, adhesion resistance is strong, the surface It is an object of the present invention to provide a night-light patterned plate and a method of manufacturing the same to enable the uniform name to be formed on the surface.

[발명의 요약][Summary of invention]

본 발명의 밤라이트 무늬판 및 그 제조방법은 하측으로부터 페놀수지함침지, 밤라이트 판, 페놀수지 함침지, 멜라민수지 함침무늬지의 순서로 적층된 상태에서 130 - 190℃의 온도와 50 ~ 90kg/㎠의 압력으로 약 15 ~ 30분간동시에 가열, 압착성형 한 후 50°~ 70℃의 온도로 내려서 밤라이트 무늬판을 제조하는 것을 특징으로 하고 있다.The night light patterned plate of the present invention and a method for producing the same are laminated in the order of phenolic resin impregnated paper, night light plate, phenolic resin impregnated paper, melamine resin impregnated patterned paper from the lower side and a temperature of 130 to 190 ° C. and 50 to 90 kg / After heating and pressing at the same time for about 15 to 30 minutes at a pressure of cm 2, it is characterized in that the night light pattern plate is manufactured by lowering to a temperature of 50 ° to 70 ° C.

[발명의 구체적 실시예에 대한 설명][Description of Specific Embodiment of the Invention]

본 발명의 밤라이트 무늬판 및 그 제조방법을 제조공정별로 상세히 설명하면 다음과 같다.The night light patterned plate of the present invention and a manufacturing method thereof will be described in detail for each manufacturing process as follows.

[제조공정][Manufacture process]

제1공정(멜라민수지 함침무늬지 준비공정)First step (melamine resin impregnated pattern paper preparation process)

각 종이마다 서로 다른 무늬가 그라비어 인쇄되어진 인쇄지들을 멜라민 수지에 합침시킨 후 건조시켜서 된 멜라민수지 함침무늬지(la)를 준비한다.Melamine resin impregnated pattern paper (la) is prepared by incorporating gravure-printed printing papers with different patterns for each paper and then drying them with melamine resin.

제2공정(페놀수지 함침지 준비공정)2nd process (Phenol resin impregnation paper preparation process)

종이를 페놀 수지에 함침시킨 후 건조시켜서 된 페놀수지 함침지(1b)를 준비한다.The phenol resin impregnated paper 1b was prepared by impregnating paper with a phenol resin and drying.

제3공정(가열 압착 프레스 가공 공정)3rd process (heat press press process)

하측으로부터 페놀수지 함침지(1b), 밤라이트 판(1c), 페놀수지 함침지(1b), 멜라민수지 함침무늬지(1a)의 순서로 적층된 상태에서 130° - 190℃의 온도와 50-90kg/cm2의 압력으로 약 15-30분간 동시에 프레싱 작동을 실시한 후 50 -70℃의 온도로 내리면 밤라이트 무늬판(1)의 제조가 완료된다. 상기와 같은 제조공정에 의해 제조되는 본 발명에 의한 밤라이트 무늬판(1)은 밤라이트 판(1c)표면과 이면에 멜라민수지 함침무늬지(1a)및 페놀수지 함침지(1b)가 적층하여 형성되어진 것으로서, 빌딩, 사무실, 호텔, 점포, 아파트, 주택 등의 내장재로 밤라이트 무늬판(1)이 유용하게 사용됨은 물론, 탁자, 도어 및 가구 표면재로도 사용할 수 있게 되며, 사용되는 밤라이트 무늬판에서 분진이 전혀 발생되지 않게 되고, 일일이 세척할 필요가 없으며, 표면강도가 강하고, 가열 압착한 것이므로 표면재인 멜리민수지 함침무늬지(1a)및 페놀수지 함침지(1b)가 가 탈피될 우려가 없으며 일일이 도료를 도포할 필요가 없게 되고, 멜라민수지 및 페놀수지의 특성에 의하여 내화학약품성, 내오염성, 내열수성, 내굻힘성, 및 내 접착성이 강한것이며, 표면이 균일하게 될 수 있게 된다. 전술한 바와 같이 본 발명의 밤라이트 무늬판(1)은 대량생산을 할 수 있게 되어 생산성 향상 및 원가절감이 됨은 물론, 미려한 무늬들이 형성되어 있는 고품질의 제품을 얻을 수 있게 되며, 장구히 사용할 수 있는 효과가 있게 된다.Temperature of 130 ° -190 ° C and 50- in a state of being laminated from the lower side in the order of phenol resin impregnated paper (1b), bamite plate (1c), phenol resin impregnated paper (1b), and melamine resin impregnated pattern paper (1a). Pressing at the same time for about 15-30 minutes at a pressure of 90kg / cm2 and then to the temperature of 50 -70 ℃ to complete the manufacture of the night light pattern plate (1). The night light pattern plate 1 according to the present invention manufactured by the above manufacturing process is laminated with melamine resin impregnated pattern paper 1a and phenolic resin impregnated paper 1b on the surface and the back of the night light plate 1c. As formed, the night light pattern plate (1) is useful as interior materials of buildings, offices, hotels, stores, apartments, houses, etc., as well as table, doors, and furniture surface materials. Since no dust is generated in the pattern plate, it does not need to be cleaned one by one, and the surface strength is strong and heat-compressed, so that the surface-impregnated melamine resin-impregnated pattern paper (1a) and phenolic resin-impregnated paper (1b) are peeled off. There is no concern, and there is no need to apply paints one by one, and because of the properties of melamine resin and phenol resin, chemical resistance, pollution resistance, hot water resistance, resistance to abrasion, and adhesion resistance are strong, and the surface becomes uniform. It becomes possible. As described above, the night light pattern plate 1 of the present invention can be mass-produced to improve productivity and reduce costs, as well as to obtain a high quality product in which beautiful patterns are formed, and can be used for a long time. It is effective.

[실시예]EXAMPLE

하측으로부터 페놀수지 함침지(1b), 밤라이트 판(1c), 페놀수지 함침지(1b), 멜라민수지 함침무늬지(1a)의 순서로 적층시킨 상태에서 160℃의 온도 와 70kg/cm2의 압력으로 22분간 동시에 프레싱 작동을 실시하여 완성품인 밤라이트 무늬판(1)을 얻게 되었다.The temperature of 160 ° C. and 70 kg / cm 2 were laminated from the lower side in the order of phenol resin impregnated paper 1b, bamite plate 1c, phenol resin impregnated paper 1b, and melamine resin impregnated pattern paper 1a. Pressing operation was simultaneously performed for 22 minutes under pressure to obtain a finished night light pattern plate (1).

Claims (1)

내장재인 밤라이트판에 있어서, 하측으로부터 페놀수지 함침지(1b), 밤라이트 판(1c), 페놀수지 함침지(1b), 멜라민수지 함침무늬지(1a)의 순서로 적층된 상태에서 가열, 압착되어서 형성된 것을 특징으로 하는 밤라이트 무늬판.In the night light plate which is an interior material, it heats in the state laminated | stacked in order of the phenol resin impregnated paper 1b, the night light plate 1c, the phenol resin impregnated paper 1b, and the melamine resin impregnated pattern paper 1a from the lower side, Night light patterned plate, characterized in that formed by pressing. 하측으로부터 페놀수지 함침지(1b), 밤라이트 판(1c), 페놀수지 함침지(1b), 멜라민수지 함침무늬지(1a)의 순서로 적층된 상태에서 130° - 190℃의 온도와 50-90kg/cm2의 압력으로 15-30분간 동시에 프레싱 작동을 실시한 후, 50 ~ 70℃의 온도로 내려서 제조하는 것을 특징으로 하는 밤라이트 무늬판의 제조방법.Temperature of 130 ° -190 ° C and 50- in a state of being laminated from the lower side in the order of phenol resin impregnated paper (1b), bamite plate (1c), phenol resin impregnated paper (1b), and melamine resin impregnated pattern paper (1a). Method of producing a night-light patterned plate, characterized in that by pressing at the same time for 15-30 minutes at a pressure of 90kg / cm 2 , the temperature is lowered to 50 ~ 70 ℃.
KR1019970003537A 1997-02-05 1997-02-05 Pattern board for interior decoration and making method thereof KR100204107B1 (en)