KR0182764B1 - Pearl nucleus - Google Patents
Pearl nucleus Download PDFInfo
- Publication number
- KR0182764B1 KR0182764B1 KR1019970006977A KR19970006977A KR0182764B1 KR 0182764 B1 KR0182764 B1 KR 0182764B1 KR 1019970006977 A KR1019970006977 A KR 1019970006977A KR 19970006977 A KR19970006977 A KR 19970006977A KR 0182764 B1 KR0182764 B1 KR 0182764B1
- Authority
- KR
- South Korea
- Prior art keywords
- pearl
- cultured
- core
- oxide
- shell
- Prior art date
Abstract
본 발명은 진주조개를 모패(母貝)로 하여 양식진주를 양식하도록 하는 진주핵에 관한 것으로서, 더욱 상세하게는 진주(眞珠)와 유사한 성분을 가진 순백색(純白色)의 백운석(白雲石)을 가공하여 진주핵으로 이용함으로서, 직경이 4~25mm의 크기를 갖는 진주핵의 제조가 용이함은 물론이고 진주핵의 다량생산이 용이하도록 하기 위한 것이다.The present invention relates to a pearl nucleus for cultivating cultured pearls using a mother-of-pearl shell, and more particularly, a pure white dolomite with a similar composition to pearls. By using it as a pearl core, it is easy to manufacture a pearl core having a size of 4 ~ 25mm in diameter, as well as to facilitate the mass production of pearl core.
본 발명은 진주조개(10)의 조개살(3)에 형성된 진주주머니(4)에 삽입하여 이식되는 양식진주핵(5)에 있어서, 상기 양식진주핵(5)은 산화알미늄 0.002%, 산화철 0.01%, 산화칼륨 0.03%, 산화나트륨 0.09%, 이산화규소 0.17%, 산화칼슘 33.7%, 산화마그네슘 19.9%, 유기물 46,098%로 이루어지는 순백색의 백운석을 지름 4~25mm의 구(球)형태로 가공하여 진주조개(10)의 진주주머니(4)에 삽입이식하는 것을 특징으로 한다.In the present invention, the cultured pearl core (5) is inserted and implanted in the pearl bag (4) formed in the clam shell (3) of the pearl shell (10), the cultured pearl core (5) is 0.002% aluminum oxide, 0.01% iron oxide Pure white dolomite consisting of 0.03% of potassium oxide, 0.09% of sodium oxide, 0.17% of silicon dioxide, 33.7% of calcium oxide, 19.9% of magnesium oxide, and 46,098% of organic matter, is processed into a ball with a diameter of 4-25mm. (10) characterized in that the implant graft on the pearl bag (4).
Description
본 발명은 진주조개를 모패(母貝)로 하여 양식진주를 양식하도록 하는 진주핵에 관한 것으로서, 더욱 상세하게는 진주(眞珠)와 유사한 성분을 가진 순백색의 백운석(白雲石 : Dolomite)을 가공 형성하여 진주핵으로 사용함으로서, 크기가 큰 진주핵의 제조가 용이함은 물론이고 진주핵의 다량생산이 용이하도록 하기 위한 것이다.The present invention relates to a pearl nucleus for cultivating cultured pearls using a mother-of-pearl shell, and more particularly, processing a pure white dolomite having a component similar to that of a pearl. By forming and using as a pearl core, it is to facilitate the production of large pearl cores as well as to facilitate the mass production of pearl cores.
진주는 조개류 특히 판새류 조개의 체내에서 형성되는 구슬모양의 분비물 덩어리를 칭하며, 주로 탄산칼슘으로 이루어지는데, 약간의 유기물이 함유되며 은빛의 아름다운 광택을 내고 있어서 보석으로서의 가치가 높이 평가되어 널리 이용되고 있다.Pearls refer to clumps of marble-like secretions that form in the shells of shellfish, especially shellfish clams, and are mainly composed of calcium carbonate, which contains some organic matter and has a beautiful silvery luster, so its value as a jewel is widely used. have.
이러한 진주는 보석으로의 가치가 높고 가격도 고가이어서 양식에 의해 진주를 얻을 수 있도록 양식방법이 개발되었으며, 진주를 양식하는 일반적인 방법은 다음과 같다.Since these pearls are highly valuable as gems and expensive, culture methods have been developed to obtain pearls by farming.
즉, 제1도에서와 같이 민물조개의 껍질을 직경 5~9mm의 구(球)형태로 가공하여 양식진주핵(5)을 형성한 다음 제2도에서와 같이 진주조개(10)의 진주주머니(4)에 칼집을 내어 절개부를 형성한 후 상기 절개부를 통해 구형태로 가공된 하나 이상의 양식진주핵(5)을 절개부를 통해 진주주머니(4)에 삽입시킨다.That is, as shown in FIG. 1, the shell of the freshwater clam is processed into a sphere having a diameter of 5 to 9 mm to form a cultured
또한, 다른 진주조개의 외투막을 적정크기로 절단하여 외투막절편을 형성하고, 상기 다른 진주조개로 부터 얻은 외투막절편(6)을 진주주머니(4)에 삽입한 후 절개된 진주주머니(4)를 접합시킴으로서 상기 진주주머니(4)에 구형태의 양식진주핵(5)과 다른 진주조개로 부터 얻은 외투막절편(6)의 이식을 완료하게 된다.In addition, the outer membrane is cut to the appropriate size to form a coat membrane section, and the coat membrane section (6) obtained from the other pearl shell is inserted into the pearl bag (4) and then the cut pearl bag (4) is bonded By completing the implantation of the outer membrane membrane section (6) obtained from the spherical cultured pearl core (5) and other pearl shells in the pearl bag (4).
제4도는 진주조개에 양식진주핵을 이식하는 상태를 설명하는 흐름도이다.4 is a flow chart illustrating a state in which cultured pearl cores are implanted in pearl shells.
상기와 같은 과정을 통해 진주조개(4)의 진주주머니(4)에 양식진주핵(5)과 외투막절편(6)의 이식이 완료된 상태에서 진주조개(4)를 바다물속에 투입하면 다른 진주조개로 부터 이식된 외투막절편(6)과 진주주머니(4)간에 활착(活着)이 일어나게 되며, 이러한 과정에서 순수한 진주액이 분비되면서 양식진주핵(5)의 표면에 골고루 도포되며, 그 도포된 진주액이 응고됨에 따라 양식진주핵(5)의 외면에 진주막이 형성되는 한편, 상기 진주막이 적층응고 됨으로서 제3도에서와 같이 진주층(7)을 형성하게 되는 것이다.When the cultured pearl core (5) and the coat membrane section (6) is transplanted into the pearl bag (4) of the pearl shell (4) through the above process, when the pearl shell (4) is put into the sea water, the other pearl shell Activation occurs between the outer membrane membrane fragment (6) and the pearl bag (4) implanted from the, and during this process, pure pearl liquid is secreted and evenly applied to the surface of the cultured pearl core (5), and the coated pearl As the liquid solidifies, a nacre is formed on the outer surface of the cultured
그러므로 진주조개의 성장속도에 따라 약 1~2년이 경과하면 양식진주핵(5)에 약 1000겹 정도의 진주액이 적층되어 제3도에서와 같이 0.5~1.0mm 정도 두께의 진주층(7)이 형성되어 양식진주(8)를 채취할 수 있게 된다.Therefore, after about 1 ~ 2 years depending on the growth rate of the pearl shell, about 1,000 layers of pearl liquid is deposited on the cultured pearl core (5), and the pearl layer of 0.5 ~ 1.0mm thickness as shown in FIG. This is formed so that the cultured pearl 8 can be collected.
이와 같이 양식진주를 양식하기 위해서는 양식진주핵이 매우 중요한데, 상기 양식진주핵을 만들기 위한 민물조개 겁질은 백색 또는 얼룩이 포함되어 있으며, 두께는 7~12mm이고, 경도는 모스경도(Mohs hardness scale) 3.0도 내외이다.The cultured pearl core is very important in order to culture the cultured pearls. The freshwater clam scare to make the cultured pearl core contains white or stains, the thickness is 7 ~ 12mm, the hardness is Mohs hardness scale 3.0 Is also inside and outside.
이와같은 민물조개 겁질의 성분에 대하여 한국화학시험연구원(KSE)에서 화학적방법에 의한 성분내용에 대하여 기술하면 다음과 같다.The components of the freshwater clam are described below by the Chemical Method in Korea Chemical Testing Institute (KSE).
상기 표 1과 같은 성분을 포함하는 조개겁질은 순백색이 적으며 두꺼운 부분이 일부에만 있어 사용가능한 부분이 적고, 두께가 두꺼운 조개겁질의 경우는 다년생 패각이라 조개겁질에 노쇄현상이 발생되며, 결이 형성되어 있어 가공연마하는 과정에서 와해 또는 금이 가는 현상이 발생하여 진주핵으로의 사용이 불가능한 관계로 사용할 수 있는 부분이 극히 적다.The clam scab containing the components as shown in Table 1 is less pure white and there are only a few parts of the thick part available, the thick clam scab is a perennial shell because it is a perennial shell, resulting in rusting phenomenon. Because it is formed, breakage or cracking occurs in the process of grinding, so there are very few parts that cannot be used as a pearl core.
따라서 상기와 같은 조개겁질의 제한적요소 때문에 종래의 진주핵은 직경이 최대 9mm 이하의 것으로서, 조개겁질 1000kg에서 7~15kg의 진주핵을 얻을 수 있어 최고 1.5% 미만의 저조한 수율을 나타내고 있다.Therefore, due to the limited elements of the clam pulp, the conventional pearl core has a diameter of up to 9 mm or less, and can obtain a pearl nucleus of 7 to 15 kg from clam pulp 1000 kg, indicating a low yield of less than 1.5%.
그러므로 상기와 같이 민물조개 겁질의 두께가 두껍지 않고 수율이 저조하기 때문에 크기가 10mm 이상의 큰 양식진주를 양식하기 위한 양식진주핵을 형성할 수가 없었을 뿐만 아니라, 양식진주핵의 크기와 그 양식진주핵이 삽입되어지는 진주모패의 크기가 적합하게 맞아야함으로 인한 양식진주핵을 다양한 크기로 형성할 수 없는 등 양식진주를 양식하는데 제약이 따르게되어 양식진주의 생산량이 소량일 수 밖에 없음은 물론 고품질의 진주를 생산하기에는 많은 문제점이 있는 것이다.Therefore, as mentioned above, since the thickness of the freshwater clam was not thick and the yield was low, it was not possible to form a cultured pearl core for growing a large culture pearl of more than 10 mm in size. The production of pearls is limited due to the inability to form pearls of different sizes due to the size of the mother-of-pearl inserts being inserted properly. There are many problems to produce.
본 발명은 상기와 같은 문제점을 해결하기 위한 것으로서, 본 발명의 목적은, 양식진주를 양식함에 있어서 가장 중요한 양식진주핵을 진주성분과 유사하고 가공이 용이한 순백색의 백운석을 사용함으로서 양식진주핵의 크기를 4~25mm로 형성 가능함에 따라 크기가 큰 양식진주를 양식할 수 있음은 물론이고, 이로인해 고가의 양식진주를 다량으로 생산할 수 있도록 하는 진주핵을 제공하기 위한 것이다.The present invention is to solve the above problems, an object of the present invention, the size of the cultured pearl core by using a pure white dolomite similar to the pearl component and easy to process in cultured pearls As it is possible to form 4 to 25mm, it is possible not only to grow a large sized pearl, but also to provide a pearl core that can produce a large amount of expensive pearls.
이와같은 목적을 실현하기 위한 본 발명은, 진주조개의 조개살에 형성된 진주주머니에 삽입하여 이식되는 양식진주핵에 있어서, 상기 양식진주핵은 산화알미늄 0.002%, 산화철 0.01%, 산화칼륨 0.03%, 산화나트륨 0.09%, 이산화규소 0.17%, 산화칼슘 33.7%, 산화마그네슘 19.9%, 유기물 46,098%로 이루어지는 순백색의 백운석을 지름 4~25mm의 구형태로 가공하여 진주조개의 진주주머니에 삽입이식하는 것에 특징이 있다.In order to achieve the above object, the present invention provides a cultured pearl core which is inserted and implanted in a pearl bag formed in a clam shell, wherein the cultured pearl core is made of aluminum oxide 0.002%, iron oxide 0.01%, potassium oxide 0.03%, and oxidation. Pure white dolomite consisting of 0.09% of sodium, 0.17% of silicon dioxide, 33.7% of calcium oxide, 19.9% of magnesium oxide, and 46,098% of organic matter is processed into a spherical shape of 4 ~ 25mm in diameter and inserted into a pearl shell of pearl shell. have.
제1도는 진주조개에 삽입 이식되는 양식진주핵의 단면도.1 is a cross-sectional view of a cultured pearl core implanted in a pearl clam.
제2도는 진주조개의 일측 겁질을 분리시켜서 진주조개의 내부를 나타내는 도면.2 is a view showing the inside of the pearl shell by separating one side of the pearl shell.
제3도는 양식진주핵에 진주층이 적층된 상태를 나타내는 단면도.3 is a cross-sectional view showing a state in which a nacre layer is stacked on a cultured pearl core.
제4도는 진주조개에 양식진주핵을 이식하는 상태를 설명하는 흐름도이다.4 is a flow chart illustrating a state in which cultured pearl cores are implanted in pearl shells.
* 도면의 주요부분에 대한 부호의 설명* Explanation of symbols for main parts of the drawings
1 : 진주모패(母貝) 2 : 외투막1: mother-of-pearl cover 2: coat
3 : 조개살 4 : 진주주머니3: clam meat 4: pearl bag
5 : 양식진주핵 6 : 외투막절편5: cultured pearl core 6: mantle membrane slice
7 : 진주층 8 : 양식진주7: mother of pearl 8: cultured pearls
10 : 진주조개10: pearl shell
이하, 본 발명의 바람직한 실시예를 첨부된 도면에 따라 상세하게 설명하면 다음과 같다.Hereinafter, preferred embodiments of the present invention will be described in detail with reference to the accompanying drawings.
먼저, 양식진주핵(5)은 진주와 유사한 성분인 산화알미늄 0.002%, 산화철 0.01%, 산화칼륨 0.03%, 산화나트륨 0.09%, 이산화규소 0.17%, 산화칼슘 33.7%, 산화마그네슘 19.9%, 유기물 46.098%로 이루어지는 순백색의 백운석을 제1도에서와 같이 구(球)형태로 가공하여 양식진주핵(5)을 형성하고, 이때 가공되는 양식진주핵(5)의 직경은 4~25mm 범위내에서 작은 것에서 부터 큰 것까지 다양한 크기로 가공한다.First, the cultured pearl core (5) is composed of pearl-like components: aluminum oxide 0.002%, iron oxide 0.01%, potassium oxide 0.03%, sodium oxide 0.09%, silicon dioxide 0.17%, calcium oxide 33.7%, magnesium oxide 19.9%, organic matter 46.098 The pure white dolomite made of% is processed into a spherical shape as shown in FIG. 1 to form a cultured
상기와 같이 순백색의 백운석을 가공하여 직경 4~25mm의 크기를 갖는 구형태의 양식진주핵(5)을 형성한 후에는 제2도에서와 같이 진주조개(4)의 진주주머니(4)에 칼집을 내어 절개부를 형성한 후, 상기 절개부를 통해 상기 순백색의 백운석인 구형태로 가공된 하나 이상의 양식진주핵(5)을 절개부를 통해 진주주머니(4)에 삽입시킨다.After processing the pure white dolomite as described above to form a spherical cultured pearl core (5) having a diameter of 4 to 25mm, sheathed the pearl bag (4) of the pearl shell (4) as shown in FIG. After forming the cut out portion, the one or more cultured pearl cores (5) processed in the form of the pure white dolomite sphere through the cut portion is inserted into the pearl bag (4) through the cut.
이와 동시에 다른 진주조개의 외투막을 적정크기로 절단하여 외투막절편을 형성하고, 상기 다른 진주조개로 부터 얻은 외투막절편(6)을 진주주머니(4)의 내벽과 양식진주핵(5) 사이에 삽입한 후 절개된 진주주머니(4)를 접합시킴으로서 상기 진주주머니(4)에 구형태로 형성된 순백색의 백운석인 양식진주핵(5)과 다른 진주조개로 부터 얻은 외투막절편(6)의 이식을 완료하게 된다.At the same time, the outer membrane is cut to an appropriate size to form a coat membrane section, and a coat membrane section (6) obtained from the other pearl shell is inserted between the inner wall of the pearl bag (4) and the cultured pearl core (5). After grafting the incision pearl bag (4) to complete the implantation of the outer membrane membrane section (6) obtained from the cultured pearl core (5), which is a pure white dolomite formed in a spherical shape on the pearl bag (4) and other pearl shells .
상기와 같은 과정을 통해 진주조개(10)의 진주주머니(4)에 순백색의 백운석인 양식진주핵(5)과 외투막절편(6)의 이식이 완료된 상태에서 진주조개(10)를 바다물속에 투입하면 다른 진주조개로 부터 이식된 외투막절편(6)과 진주주머니(4)간에 활착(活着)이 일어나게 되며, 이러한 과정에서 순수한 진주액이 분비되면서 양식진주핵(5)의 표면에 골고루 도포되며, 그 도포된 진주액이 응고됨에 따라 양식진주핵(5)의 외면에 진주막이 형성되는 한편, 상기 진주막이 적층응고 됨으로서 제3도에서와 같이 진주층(7)을 형성하게 되는 것이다.Through the above process, the pearl shell (10) is introduced into the seawater in the state of completion of the transplantation of the cultured pearl core (5) and the outer membrane fragment (6), which are pure white dolomite, into the pearl bag (4) of the pearl shell (10). If this occurs between the outer membrane membrane (6) and the pearl bag (4) transplanted from the other pearl clam, and the active pearl is secreted in this process, evenly applied to the surface of the cultured pearl core (5), As the applied pearl solution solidifies, a nacre is formed on the outer surface of the cultured
그러므로 진주조개의 성장속도에 따라 약 1~2년이 경과하면 양식진주핵(5)에 약 1000겹 정도의 진주액이 적층되어 제3도에서와 같이 0.5~1.0mm 정도 두께의 진주층(7)이 형성되어 양식진주(8)를 채취할 수 있게 되며, 이렇게 1000겹 정도로 적층 도포된 진주층에 빛이 침투되면 1000겹 정도의 진주층에서 빛의 굴절과 산란작용에 의해 영롱한 광채를 발하게 되는 것이다.Therefore, after about 1 ~ 2 years depending on the growth rate of the pearl shell, about 1,000 layers of pearl liquid is deposited on the cultured pearl core (5), and the pearl layer of 0.5 ~ 1.0mm thickness as shown in FIG. This form is able to collect the cultured pearl (8), and when light penetrates the layer of nacres coated with 1000 layers in this way is to emit a brilliant brilliance by the refraction and scattering of light in the nacres of 1000 layers.
즉, 양식진주핵(5)의 순백색인 백운석과 상기 양식진주핵(5)의 표면에 적층되는 진주층(7) 형성에 미치는 영향과 진주광채의 상호관계를 살펴보면, 첫째는 진주층(7)의 외부에서 침투하는 빛의 굴절과 반사에 의한 물리적 작용이며, 둘째는 진주층(7) 내부에 함유된 진주조개겁질인 진주모채(1)의 유전자 영향을 받은 색소가 겹쳐짐으로서 특정한 색체를 나타내게 된다.In other words, the influence of the pure white dolomite of the cultured pearl core (5) on the formation of the pearl layer (7) stacked on the surface of the cultured pearl core (5) and the relationship between the pearl sheen and the first, the outside of the pearl layer (7) It is a physical action by the refraction and reflection of the light penetrating in, and the second is a specific color by overlapping the genetically-pigmented pigments of the pearl shell (1), the pearl shell of the pearl shell contained in the nacre (7).
따라서 상기와 같은 작용에 의해 특정한 색체를 나타내게 되나, 진주자체의 현란한 빛깔은 극히 얇은 탄산칼슘결정판인 진주막이 수없이 적층되는 과정에서 규칙정연하게 빛이 순백색 백운석인 양식진주핵(5) 까지 침투할 때 백운석의 양식진주핵(5)에 반사되어 되돌아 나오면서 가장 이상적인 빛깔, 즉 무지개색의 찬란한 진주의 색채가 나타나게 되는 것이다.Therefore, a specific color is expressed by the above-mentioned action, but the brilliant color of the pearl itself penetrates to the cultured pearl core (5), which is light and pure white dolomite, in the process of laminating numerous pearl membranes which are extremely thin calcium carbonate crystal plates. When reflected back to the cultured pearl core (5) of dolomite, the most ideal color, that is, the color of the rainbow-colored brilliant pearl appears.
그러므로 본 발명에 적용되는 순백색 백운석의 양식진주핵(5)은 진주층(7)이 형성되기에는 매우 적합하여 기존의 조개겁질을 사용한 양식진주핵 보다 진주층(7)의 형성이 보다 많이 이루어지고, 진주의 광체 역시 매우 월등한 것으로 나타났다.Therefore, the cultured pearl core (5) of the pure white dolomite applied to the present invention is very suitable for the formation of the nacre (7), the pearl layer (7) is formed more than the cultured pearl core using the conventional clam, pearl The ore was also very superior.
또한, 상기 양식진주를 양식함에 있어서 가장 중요한 요소인 양식진주핵은 진주와 유사한 성분의 것이어야 하는데, 본 발명에서 사용되는 순백색의 백운석에는 진주와 가장 유사한 성분 즉, 산화알미늄, 산화철, 산화칼륨, 산화나트륨, 이산화규소, 산화칼슘, 산화마그네슘, 기타 유기물을 지니고 있으며 모스경도가 3.5로 진주경도와 거의 동일하므로 순백색의 백운석으로 형성된 양식진주핵에 적층되는 진주층이 적층된 양식진주는 보석으로서의 가치가 높을 뿐만 아니라 구멍형성 등 가공처리가 용이하며, 비중이 2.8~2.9로 진주와 유사하여 휴대 및 착용이 용이하다.In addition, the cultured pearl core, which is the most important element in cultured pearls, should be one of pearl-like components. The pure white dolomite used in the present invention includes the most similar components to pearls, namely aluminum oxide, iron oxide, potassium oxide, It has sodium oxide, silicon dioxide, calcium oxide, magnesium oxide, and other organic matters, and its moss hardness is 3.5, which is almost the same as pearl hardness, so that pearl cultured with a pearl layer stacked on a cultured pearl core formed of pure white dolomite is valuable as a jewel. It is not only high, but also easy to process such as hole formation, and its specific gravity is 2.8 ~ 2.9, so it is easy to carry and wear.
또한, 순백색의 백운석 1000kg을 가공하면 150~200kg 이상의 진주핵을 얻을 수 있어 수율이 약 15%~20% 이상이고, 진주핵을 소형에서 대형까지 필요에 의해 크기조절은 얼마든지 가능할 뿐만아니라 순백색의 백운석에는 결이 없어서 와해율이 낮음으로써 생산 수율이 높아 다량생산이 가능한 것이다.In addition, if you process 1000kg of pure white dolomite, you can get more than 150 ~ 200kg of pearl cores, and the yield is about 15% ~ 20% or more, and you can adjust the size of pearl cores from small to large size. Dolomite has no grains, so the disintegration rate is low.
상기 순백색 백운석의 성분에 대하여 한국화학시험연구원(KSE)에서 화학적방법에 의한 성분내용에 대하여 기술하면 다음과 같다.The components of the pure white dolomite will be described in detail by the chemical method in Korea Chemical Testing Institute (KSE) as follows.
이상에서 살펴본 바와 같은 본 발명에 의한 진주핵은, 진주에 포함되어 있는 성분과 유사한 성분을 포함하고 있는 순백색의 백운석으로 양식진주핵을 가공 형성하여 진주핵으로 활용함으로서, 양식진주핵의 크기를 진주모패의 크기에 맞추어 4~25mm 범위내에서 얼마든지 크게, 또는 작게 가공 형성할 수 있어서 대형의 양식진주를 양식할 수 있음은 물론이고, 다량의 양식진주를 용이하게 양식할 수 있는 매우 유용한 효과가 있는 것이다.As described above, the pearl core according to the present invention is formed by processing a cultured pearl core into a pure white dolomite containing a component similar to that contained in pearls, and utilizing the pearl as a pearl core. According to the size of the mother hat can be processed to any large or small within the range of 4 ~ 25mm to form a large cultured pearl, as well as a very useful effect that can easily grow a large number of cultured pearls It is.
Claims (1)